A fire retardant molding contains a thermoplastic compound and an inorganic flameproof agent that is mixed with the thermoplastic compound and which acts by separating from water, having a proportion in the range of 10 wt % to 90 wt %. The fire retardant molding is produced by mixing the thermoplastic material with an inorganic flame-proofing agent, the flame-proofing agent having a proportion in the range of 20 wt % to 80 wt %, and by outputting the compound obtained by mixing, in particular as a flat product. The fire retardant molding is advantageously used, for example, in or on land-based vehicles, water-based vehicles, aircraft and buildings.

Water-resistant gypsum products may be produced using a novel catalyst that includes calcium aluminate cement and/or calcium sulfoaluminate cement. For example, a water-resistant gypsum panel may have a core comprising: interwoven matrices of calcium sulfate dihydrate crystals and a silicone resin, wherein the interwoven matrices have dispersed throughout them a siloxane polymerization catalyst comprising (a) 55 wt % to 100 wt % calcium aluminate cement and/or calcium aluminate cement and (b) 0 wt % to 45 wt % and magnesium oxide, wherein the weight ratio of the siloxane polymerization catalyst to the calcium sulfate dihydrate is 0.01-5:100. The water-resistant gypsum panel may have an absence of one or more of: Portland cement, limestone, aragonite, calcite, dolomite, and slaked lime.

Water-resistant gypsum products may be produced using a novel catalyst that includes calcium aluminate cement and/or calcium sulfoaluminate cement. For example, a water-resistant gypsum panel may have a core comprising: interwoven matrices of calcium sulfate dihydrate crystals and a silicone resin, wherein the interwoven matrices have dispersed throughout them a siloxane polymerization catalyst comprising (a) 55 wt % to 100 wt % calcium aluminate cement and/or calcium aluminate cement and (b) 0 wt % to 45 wt % and magnesium oxide, wherein the weight ratio of the siloxane polymerization catalyst to the calcium sulfate dihydrate is 0.01-5:100. The water-resistant gypsum panel may have an absence of one or more of: Portland cement, limestone, aragonite, calcite, dolomite, and slaked lime.

Particulate high-emissivity (high-ε) refractory products include a mixture of (a) a particulate refractory base material which includes at least one particulate binder material, at least one particulate refractory raw material filler material and optionally at least one refractory additive; and (b) a high-ε pigment in an amount sufficient to impart high-ε properties to the refractory product when cured of at least 0.80. The high-ε pigment is homogenously dispersed throughout the particulate refractory base material and is thereby less susceptible to loss of high-ε properties over time. The particulate high-ε products may be formed into an castable wet mix, an aqueous slurry or an insulating aqueous foam and cured so as to provide a component part of a high temperature refractory structure (e.g., the walls or ceiling of a refractory furnace) having high-ε properties.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.

There is provided a composition comprising a slurry of capsules, the capsules having shells comprising silica and said shells encapsulating phase change materials (PCM); and a cementitious binder. There is also provided a method for preparing said composition.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.