A synthesis method for producing a refractory oxide-ceramic material of CaZrO.sub.3, in particular in the form of a refractory granular material that is preferably mechanically comminuted, in particular crushed and/or ground, as well as to a batch and a coarse ceramic, shaped or unshaped, refractory product containing at least one pre-synthesized refractory calcium zirconate-containing granular material.

Provided is an aluminum nitride structure that includes a plurality of aluminum nitride particles, wherein aluminum nitride particles that are adjacent are bound to each other through a boehmite phase containing boehmite, and the porosity is 30% or less. Also provided is a method for producing an aluminum nitride structure that includes: obtaining a mixture by mixing an aluminum nitride powder with a solvent containing water; and pressurizing and heating the mixture under conditions of a pressure of 10 to 600 MPa and a temperature of 50 to 300° C.

Provided is a piezoelectric ceramic composition including a potassium sodium niobate-based perovskite type complex oxide represented by Compositional Formula ABO.sub.3, as a main component. Further, the piezoelectric ceramic composition contains Bi in an A site and Zr in a B site. Further, the piezoelectric ceramic composition includes a segregation portion positioned in a crystal grain. At least one of Zr or Bi is localized in the segregation portion.

A preform for making a component of a braking system having a fibre-reinforced ceramic composite material, obtained by forming and subsequent pyrolysis of a pre-preg is described. Also described is a component of a braking system made wholly or in part from the preform, and a method for making a preform in a fibre-reinforced ceramic composite material.

A paramagnetic garnet-type transparent ceramic characterized by being a sintered body of a terbium-containing composite oxide represented by formula (1) in which the linear transmittance at a wavelength of 1,064 nm at an optical path length of 15 mm is 83% or higher.
(Tb.sub.1-x-ySc.sub.xCe.sub.y).sub.3(Al.sub.1-zSc.sub.z).sub.5O.sub.12  (1)
(In the formula, 0<x<0.08, 0≤y≤0.01, 0.004<z<0.16.)

A method of manufacturing a dielectric for a capacitor and a dielectric for a capacitor manufactured thereby are provided. A dielectric for a capacitor is prepared by calcining a precursor mixture containing lead, lanthanum, zirconium, and titanium to produce calcined powder, adding additives including sodium, potassium, and the like to the powder, and sintering the mixture at a low temperature, whereby the dielectric has a high density and a large dielectric constant.

An exemplary embodiment of the present disclosure provides a method for manufacturing a transparent ceramic material. The method comprises providing a compact comprising a metal oxide and, during sintering, exposing the compact to a vapor comprising one of or both fluorine ions and lithium ions to form a transparent ceramic material comprising at least 90% of a theoretical transparency.

A dielectric material which satisfies X9M characteristics and ensures operations over an extended period of time at 200° C. is provided.

A ferrite sintered magnet including ferrite grains having a hexagonal crystal structure. The ferrite grains satisfy 0.56≤W≤0.68 where W is an average value of circularities of the ferrite grains in a cross section parallel to an axis of easy magnetization.

Embodiments of synthetic garnet materials having advantageous properties, especially for below resonance frequency applications, are disclosed herein. In particular, embodiments of the synthetic garnet materials can have high Curie temperatures and dielectric constants while maintaining low magnetization. These materials can be incorporated into isolators and circulators, such as for use in telecommunication base stations.