Provided are pre-sintered and sintered zirconia dental ceramic materials. The materials have a gradient in yttria content. The materials may have a gradient in one or more physical/mechanical property and/or one or more optical property. The materials may be made by mixing at least two zirconia ceramic powders having different yttria content. A sintered zirconia dental ceramic material may be in the form of a dental article.

The present invention provides a ferrite sintered magnet comprising ferrite crystal grains having a hexagonal structure, wherein the ferrite sintered magnet comprises metallic elements at an atomic ratio represented by formula (1). In formula (1), R is at least one element selected from the group consisting of Bi and rare-earth elements, and R comprises at least La. In formula (1), w, x, z and m satisfy formulae (2) to (5). The above-mentioned ferrite sintered magnet further has a coefficient of variation of a size of the crystal grains in a section parallel to a c axis of less than 45%.
Ca.sub.1-w-xR.sub.wSr.sub.xFe.sub.zCo.sub.m  (1)
0.360≤w≤0.420  (2)
0.110≤x≤0.173  (3)
8.51≤z≤9.71  (4)
0.208≤m≤0.269  (5)

This disclosure relates to a polycrystalline cubic boron nitride, PCBN, composite material comprising cubic boron nitride, cBN, particles and a binder matrix material in which the cBN particles are dispersed. The binder matrix material comprises one or more superalloys.

A member for a plasma processing apparatus configured of a tubular body composed of a ceramic having a rare earth element oxide, aluminum oxide, or a rare earth element aluminum composite oxide as a main constituent and including a through hole in an axial direction, in which a number of recessed portions having a depth of from 10 μm to 20 μm, the depth starting from a ridge located between an inner peripheral surface of the tubular body and a target observation surface obtained by polishing from an outer peripheral surface of the tubular body toward an axis, is 2 or less per 1 mm of the ridge.

A hard lead zirconate titanate (PZT) ceramic has an ABO.sub.3 structure with A sites and B sites. The PZT ceramic is doped with Mn and with Nb on the B sites and the ratio Nb/Mn is <2. A piezoelectric multilayer component having such a PZT ceramic and also a method for producing a piezoelectric multilayer component are also disclosed.

The present invention provides a method for producing a zirconia particle-containing powder that enables easy production of a zirconia sintered body having both high translucency and high strength. The present invention relates to a method for producing a zirconia particle-containing powder, comprising a drying step of spray drying a slurry containing zirconia particles, wherein the zirconia particles have an average primary particle diameter of 30 nm or less, and the slurry comprises a dispersion medium containing a liquid having a surface tension at 25° C. of 50 mN/m or less. Preferably, the zirconia particles comprise 2.0 to 9.0 mol % yttria. Preferably, wherein the content of the liquid in the dispersion medium is 50 mass % or more.

A silicon nitride sintered body includes at least one black portion with a major axis of 10 μm or more in a field of view with a unit area of 5 mm×5 mm, when observing an arbitrary cross-section of the silicon nitride sintered body using a metallurgical microscope. A major axis of the black portion is Preferably 500 μm or less. The number of the black portion within the field of view with a unit area of 5 mm×5 mm is preferably 2 or more and 10 or less. A segregation portion of Fe is preferably included in the black portion.

Disclosed herein are embodiments of low temperature co-fireable barium tungstate materials which can be used in combination with high dielectric materials, such as nickel zinc ferrite, to form composite structures, in particular for isolators and circulators for radiofrequency components. Embodiments of the material can include flux, such as bismuth vanadate, to reduce co-firing temperatures.

Provided is an aluminum nitride structure that includes a plurality of aluminum nitride particles, wherein aluminum nitride particles that are adjacent are bound to each other through a boehmite phase containing boehmite, and the porosity is 30% or less. Also provided is a method for producing an aluminum nitride structure that includes: obtaining a mixture by mixing an aluminum nitride powder with a solvent containing water; and pressurizing and heating the mixture under conditions of a pressure of 10 to 600 MPa and a temperature of 50 to 300° C.

A method for forming a ceramic-based material comprises depositing a ceramic-precursor composition comprising nanoparticles having at least one dimension less than 100 nm and an aspect ratio of 1.5 or greater, and a carrier fluid on a surface of a substrate to form an as-deposited layer of the ceramic precursor composition; and sintering the as-deposited layer of the ceramic precursor composition at a sintering temperature to form a ceramic-based material.