The present invention discloses a polyimide-based composite carbon film with high thermal conductivity and a preparation method therefor. The preparation method includes: uniformly coating the surface of a polyimide-based carbon film with an aqueous graphene oxide solution, and then covering the same with another polyimide-based carbon film uniformly coated with an aqueous graphene oxide solution; repeating such operation; after the polyimide-based carbon films are dried, bonding the polyimide-based carbon films by means of graphene oxide so as to form a thick film; bonding the polyimide-based carbon films more tightly by means of further low-temperature hot pressing; and finally, obtaining a thick polyimide-based carbon film with high thermal conductivity by repairing defects by means of low-temperature heating pre-reduction and high-temperature and high-pressure thermal treatment. The thick polyimide-based carbon film with high thermal conductivity has a thickness greater than 100 μm and an in-plane thermal conductivity of even reaching 1700 W/mK or above.

A paramagnetic garnet-type transparent ceramic is a sintered body of complex oxide represented by the following formula (1), comprising SiO.sub.2 as a sintering aid in an amount of more than 0% by weight to 0.1% by weight or less, and has a linear transmittance of 83.5% or more at the wavelength of 1,064 nm for an optical path length of 25 mm:
(Tb.sub.1-x-yY.sub.xSc.sub.y).sub.3(Al.sub.1-zSc.sub.z).sub.5O.sub.12  (1)
wherein 0.05≤x<0.45, 0<y<0.1, 0.5<1−x−y<0.95, and 0.004<z<0.2.

A dielectric composition includes a main ingredient having a perovskite structure represented by ABO.sub.3, where A is at least one of Ba, Sr, and Ca and B is at least one of Ti, Zr, and Hf, and a first accessory ingredient. The first accessory ingredient comprises 0.1 mole or more of a rare earth element, 0.02 mole or more of Nb, and 0.25 mole or more and 0.9 mole or less of Mg, a sum of contents of the rare earth element and Nb is 1.5 mole or less.

A sintered body includes a solid solution containing cobalt and iron, with the balance being zirconia. The total content of cobalt in terms of CoO and iron in terms of Fe.sub.2O.sub.3 is more than 0.1 wt % and less than 3.0 wt %, and the proportion of cobalt regions larger than 5.5 μm.sup.2 in an elemental map obtained using an electron probe microanalyzer is 25% or less.

The present invention provides a method of preparing bulk BSCCO-based material, the method comprising: mixing a first solution with a second solution at a pre-determined temperature to form a gel, wherein the first solution comprises salts of at least bismuth, strontium, calcium and copper and the second solution comprises a precipitating agent; drying the gel to form a xerogel; grinding the xerogel to form a homogeneous metalorganic precursor; and calcining the homogeneous metalorganic precursor to form bulk BSCCO-based materials. Further steps may enable preparation of 2D BSCCO flakes.

The present invention relates to a method for preparing a fully ceramic capsulated nuclear fuel material containing three-layer-structured isotropic nuclear fuel particles coated with a ceramic having a composition which has a higher shrinkage than a matrix in order to prevent cracking of ceramic nuclear fuel, wherein the three-layer-structured nuclear fuel particles before coating is included in the range of between 5 and 40 fractions by volume based on after sintering. More specifically, the present invention provides a composition for preparing a fully ceramic capsulated nuclear fuel containing three-layer-structured isotropic particles coated with the substance which includes, as a main ingredient, a silicon carbine derived from a precursor of the silicon carbide wherein a condition of ΔL.sub.c>ΔL.sub.m at normal pressure sintering is created, where the sintering shrinkage of the coating layer of the three-layer-structured isotropic nuclear fuel particles is ΔL.sub.c and the sintering shrinkage of the silicon carbide matrix is ΔL.sub.m; material produced therefrom; and a method for manufacturing the material. The residual porosity of the fully ceramic capsulated nuclear fuel material is 4% or less.

A Li ion conductor having a composition different from a conventional composition is provided. The Li ion conductor contains at least one selected from a group Q consisting of Ga, V, and Al, Li, La and O. A part of an Li site is optionally substituted with a metal element D, a part of an La site is optionally substituted with a metal element E, and parts of Ga, V and Al sites are optionally substituted with a metal element J. A mole ratio of an amount of Li to a total amount of La, the element E, Ga, V, Al, and the element J is not lower than 8.1/5 and not higher than 9.5/5. A mole ratio of a total amount of Ga, V, and Al to a total amount of La and the element E is not lower than 1.1/3 and not higher than 2/3.

The present invention relates to a suspension comprising 50-95% by weight of the total suspension (w/w) of at least one metallic material and/or ceramic material and/or polymeric material and/or solid carbon containing material; and at least 5% by weight of the total suspension of one or more fatty acids or derivatives thereof. In addition, the invention relates to uses of such suspension in 3D printing processes.

An example method includes combining an interlayer and a carbon fiber fabric, wherein the interlayer comprises a highly oriented milled carbon fiber ply comprising a plurality of out-of-plane carbon fibers. The method further includes winding the interlayer and the carbon fiber fabric around a core to form a composite fiber preform comprising a plurality of layers defining an annulus extending along a central axis. The method further includes densifying the composite fiber preform.

A method includes molding a raw material powder containing a ceramic powder and a thermoplastic resin having a glass transition temperature higher than room temperature into a shape by isostatic pressing and in which a raw material powder slurry is prepared by adding the ceramic powder and the thermoplastic resin to a solvent so that the thermoplastic resin is 2% by weight or more and 40% by weight or less with respect to a total weight of the ceramic powder and the thermoplastic resin, a cast-molded body is to formed by wet-casting the raw material powder slurry into a shape, dried, and subjected to first-stage isostatic press molding at a temperature lower than the glass transition temperature of the thermoplastic resin, then this first-stage press-molded body is heated to the glass transition temperature of the thermoplastic resin or above, and warm isostatic press (WIP) molding is performed.