A method for producing an electrically-conductive pellet includes reducing a size of a first material. The method also includes wetting the first material to produce a first slurry. The method also includes introducing the first slurry into a fluidizer to produce a first pellet. The method also includes reducing a size of a second material. The second material is an electrically-conductive material. The method also includes wetting the second material to produce a second slurry. The method also includes applying the second slurry to the first pellet.

A method for producing a lithium-transition metal composite oxide, including steps of: preparing a mixture including a lithium-containing compound and a transition metal compound; obtaining a molded body of the mixture; and sintering the molded bodies in a container having at least one vent hole, to obtain sintered bodies.

The present disclosure relates to the technical field of ceramic powder preparation, and discloses a zirconia/titania/cerium oxide doped rare earth tantalum/niobate RETa/NbO.sub.4 ceramic powder and a preparation method thereof. A general chemical formula of the ceramic powder is RE.sub.1-x(Ta/Nb).sub.1-x(Zr/Ce/Ti).sub.2xO.sub.4, 0<x<1, the crystal structure of the ceramic powder is orthorhombic, the lattice space group of the ceramic powder is C222.sub.1, the particle size of the ceramic powder ranges from 10 to 70 μm, and particles of the ceramic powder are spherical. During preparation, the raw materials are ball-milled before a high temperature solid phase reaction, then mixed with a solvent and an organic binder to obtain a slurry C, then centrifuged and atomized to obtain dry pellets, and finally sintered to obtain a zirconia/titanium oxide/cerium oxide doped rare earth tantalum/niobate RETa/NbO.sub.4 ceramic powder, which satisfies the requirements of APS technology for ceramic powders.

A dielectric ceramic composition includes a barium titanate (BaTiO.sub.3)-based base material main ingredient and an accessory ingredient, the accessory ingredient including dysprosium (Dy) and praseodymium (Pr) as first accessory ingredients. A content of the Pr satisfies 0.233 mol≤Pr≤0.699 mol, based on 100 mol of the barium titanate base material main ingredient.

A dielectric ceramic composition includes a barium titanate (BaTiO.sub.3)-based base material main ingredient and an accessory ingredient, the accessory ingredient including dysprosium (Dy) and praseodymium (Pr) as first accessory ingredients. A content of the Pr satisfies 0.233 mol≤Pr≤0.699 mol, based on 100 mol of the barium titanate base material main ingredient.

A method for producing a ceramic composite includes: preparing a sintered body in a plate form containing a fluorescent material having a composition of a rare earth aluminate, and aluminum oxide; and eluting the aluminum oxide from the sintered body by contacting the sintered body with a basic substance, for example, contained in an alkali aqueous solution, and the dissolution amount of the fluorescent material eluted from the sintered body in the step of eluting the aluminum oxide is 0.5% by mass or less based on an amount of the fluorescent material contained in the sintered body as 100% by mass.

A glassy carbon compact according to the present invention has a maximum inscribed sphere diameter of 5 mm or greater, comprises pores having diameters of 500 nm or less dispersed throughout the glassy carbon compact, and has a density of 1.1 g/cm.sup.3 or greater.

A method includes molding a raw material powder containing a ceramic powder and a thermoplastic resin having a glass transition temperature higher than room temperature into a shape by isostatic pressing and in which a raw material powder slurry is prepared by adding the ceramic powder and the thermoplastic resin to a solvent so that the thermoplastic resin is 2% by weight or more and 40% by weight or less with respect to a total weight of the ceramic powder and the thermoplastic resin, a cast-molded body is to formed by wet-casting the raw material powder slurry into a shape, dried, and subjected to first-stage isostatic press molding at a temperature lower than the glass transition temperature of the thermoplastic resin, then this first-stage press-molded body is heated to the glass transition temperature of the thermoplastic resin or above, and warm isostatic press (WIP) molding is performed.

A method for molding a ceramic material includes: mixing a ceramic powder, a resin, a curing agent and a solvent to obtain a raw material slurry for a ceramic material; injecting the raw material slurry into an elastic container; curing the resin in the raw material slurry injected into the elastic container to form a molded body having a desired shape; and demolding the molded body from the elastic container.

An antiballistic armor-plating component, includes a ceramic body made of a material comprising, as percentages by volume, between 35% and 55% of silicon carbide, between 20% and 50% of boron carbide, between 15% and 35% of a metallic silicon phase or of a metallic phase including silicon.