The present invention relates to use of optionally monosubstituted 2,2-di(tetrahydrofuryl)methanes, as internal donors in Ziegler-Natta catalysts to obtain polymers with desirable properties. The present disclosure further concerns Ziegler-Natta catalyst components comprising said optionally monosubstituted 2,2-di(tetrahydrofuryl)methanes and Ziegler-Natta catalysts for olefin polymerization comprising said Ziegler-Natta catalyst components as well as a method for preparing the same and their use in providing polyolefins.

The present invention relates to use of optionally monosubstituted 2,2-di(tetrahydrofuryl)methanes, as internal donors in Ziegler-Natta catalysts to obtain polymers with desirable properties. The present disclosure further concerns Ziegler-Natta catalyst components comprising said optionally monosubstituted 2,2-di(tetrahydrofuryl)methanes and Ziegler-Natta catalysts for olefin polymerization comprising said Ziegler-Natta catalyst components as well as a method for preparing the same and their use in providing polyolefins.

To provide a semi-aromatic polyamide resin composition having excellent good plating properties, low water absorption properties, and solder reflow resistance. A semi-aromatic polyamide resin composition of the present invention comprises: 10 to 200 parts by mass of an inorganic filler (B) and 2 to 30 parts by mass of a toughness improver (C) based on 100 parts by mass of a semi-aromatic polyamide (A), wherein the semi-aromatic polyamide resin (A) satisfies the following (a) and (b): (a) a melting point (Tm) measured by differential scanning calorimetry (DSC) is 280° C. or higher; and (b) an equilibrium water absorption rate at 80° C. and 95% RH is 3.5% or less.

To provide a semi-aromatic polyamide resin composition having excellent good plating properties, low water absorption properties, and solder reflow resistance. A semi-aromatic polyamide resin composition of the present invention comprises: 10 to 200 parts by mass of an inorganic filler (B) and 2 to 30 parts by mass of a toughness improver (C) based on 100 parts by mass of a semi-aromatic polyamide (A), wherein the semi-aromatic polyamide resin (A) satisfies the following (a) and (b): (a) a melting point (Tm) measured by differential scanning calorimetry (DSC) is 280° C. or higher; and (b) an equilibrium water absorption rate at 80° C. and 95% RH is 3.5% or less.

The present invention relates to an olefin-based polymer satisfying requirements: (1) a melt index (MI, 190° C., 2.16 kg load conditions) ranging from 1.0 to 10.0 g/10 min; (2) a density (d) ranging from 0.875 to 0.895 g/cc; (3) 0.5 J/g≤dH(100)≤3.0 J/g and 1.0 J/g≤dH(90)≤6.0 J/g as measured by successive self-nucleation/annealing (SSA) using a differential scanning calorimeter (DSC); (4) 15≤T(90)−T(50)≤30 and 50° C.≤T(50)≤75° C. as measured by SSA using a DSC; and (5) a melting point (Tm) of 55° C.≤Tm≤80° C. as measured using a DSC. The olefin-based polymer according to the present invention is a low-density olefin-based polymer and has a highly crystalline region introduced therein, thereby exhibiting high mechanical stiffness.

The present invention relates to an olefin-based polymer satisfying requirements: (1) a melt index (MI, 190° C., 2.16 kg load conditions) ranging from 1.0 to 10.0 g/10 min; (2) a density (d) ranging from 0.875 to 0.895 g/cc; (3) 0.5 J/g≤dH(100)≤3.0 J/g and 1.0 J/g≤dH(90)≤6.0 J/g as measured by successive self-nucleation/annealing (SSA) using a differential scanning calorimeter (DSC); (4) 15≤T(90)−T(50)≤30 and 50° C.≤T(50)≤75° C. as measured by SSA using a DSC; and (5) a melting point (Tm) of 55° C.≤Tm≤80° C. as measured using a DSC. The olefin-based polymer according to the present invention is a low-density olefin-based polymer and has a highly crystalline region introduced therein, thereby exhibiting high mechanical stiffness.

The present disclosure relates to a polyethylene composition capable of producing a molded product having excellent environmental stress crack resistance, and improving total volatile organic compound (TVOC) properties that can be generated by a low molecular weight polymer, and a method for preparing the same.

The present disclosure relates to a polyethylene composition capable of producing a molded product having excellent environmental stress crack resistance, and improving total volatile organic compound (TVOC) properties that can be generated by a low molecular weight polymer, and a method for preparing the same.

The present invention relates to optionally substituted 1,3-dimethoxypropanes and 3-methoxypropylamines, and more particularly to their use as internal donors in Ziegler-Natta catalysts to obtain polymers with desirable properties. The present disclosure further concerns Ziegler-Natta catalyst components comprising said optionally substituted 1,3-dimethoxypropanes and 3-methoxypropylamines, and Ziegler-Natta catalysts for olefin polymerization comprising said Ziegler-Natta catalyst components, as well as a method for preparing the same and their use in providing polyolefins.

The present invention relates to optionally substituted 1,3-dimethoxypropanes and 3-methoxypropylamines, and more particularly to their use as internal donors in Ziegler-Natta catalysts to obtain polymers with desirable properties. The present disclosure further concerns Ziegler-Natta catalyst components comprising said optionally substituted 1,3-dimethoxypropanes and 3-methoxypropylamines, and Ziegler-Natta catalysts for olefin polymerization comprising said Ziegler-Natta catalyst components, as well as a method for preparing the same and their use in providing polyolefins.