Elastic Parylene films produced via chemical vapor deposition polymerization (CVDP) on a substrate are disclosed.

An allyl-containing resin is provided. The allyl-containing resin comprises a repeating unit comprising a structural unit represented by the following formula (I): ##STR00001## wherein, R.sub.1 to R.sub.3 in formula (I) are as defined in the specification; the Fourier transform infrared spectrum of the allyl-containing resin has a signal intensity “a” from 1650 cm.sup.−1 to 1630 cm.sup.−1 and a signal intensity “b” from 1620 cm.sup.−1 to 1560 cm.sup.−1, and 0<a/b≤1.20; and the quantitative .sup.1H-NMR spectrum of the allyl-containing resin has a signal intensity “c” from 3.2 ppm to 6.2 ppm and a signal intensity “d” from 6.6 ppm to 7.4 ppm, and 0<c/d≤1.20.

A frontally polymerized polymeric body includes, according to a first embodiment, a deformable polymer comprising polydicyclopentadiene (pDCPD) and/or poly(5-ethylidene-2-norbornene) (pENB), where the deformable polymer has a fracture strain of at least about 0.5 mm mm.sup.−1. According to a second embodiment, the frontally polymerized polymeric body includes a first polymer comprising pDCPD and/or pENB, and a second polymer adjacent to the first polymer also comprising the pDCPD and/or the pENB. The second polymer is more or less deformable than the first polymer. Thus, the frontally polymerized polymeric body exhibits spatially varying mechanical and/or other properties.

A liquid cyclopentene ring-opened copolymer includes a monomer unit derived from cyclopentene and a monomer unit derived from a norbornene compound, the monomer unit derived from cyclopentene being present in an amount of 60 to 95 wt %, the liquid cyclopentene ring-opened copolymer having a hydroxyl group-terminated copolymer chain and having a melt viscosity at 25° C. of less than 500 Pa.Math.s, which is measured using a B-type viscometer.

A layered film includes first, second, and third layers formed of first, second, and third resins, respectively, and provided in this order. The second resin contains an alkoxysilyl group-modified product of a hydrogenated product of a block copolymer; has 0.020% by weight or less of a moisture content as measured by the Karl-Fischer method after immersed in water at 37° C. for 24 hours and then allowed to stand at 23° C. and a humidity of 70% for 24 hours; and has a flexural modulus lower than flexural moduli of the first and third resins. One or both of the first and third resins contain a polymer containing an alicyclic structure. The first resin has a specific water vapor transmission rate. A ratio of a sum of thicknesses of the first and third layers relative to a thickness of the second layer is in a specific range.

A phase difference film formed of a resin containing a polymer having crystallizability, wherein: an NZ factor thereof is less than 1.0; and a haze thereof is less than 1.0%.

Elastic Parylene films produced via chemical vapor deposition polymerization (CVDP) on a substrate are disclosed.

A cyclic olefin copolymer for a medical instrument has an aromatic ring and contains at least one structural unit (A) of the specific formulas (Ia), (II), and (III).

Gas separation membranes are provided and more particularly, a series of addition-type and ROMP type polynorbornenes with substituents derived from Mizoroki-Heck reactions are provided and have particular utility as gas separation membranes for natural gas upgrading.

Provided is a shaping material with which a shaped product having excellent flame retardancy can be formed. The shaping material contains a hydrogenated cycloolefin ring-opened polymer and an organophosphinate flame retardant. The organophosphinate flame retardant is either or both of a compound indicated by the following formula (I) and a compound indicated by the following formula (II). Moreover, the organophosphinate flame retardant has an average dispersion diameter of 10 μm or less.

##STR00001##