The present invention is concerned with expanded beads that are olefin-based thermoplastic elastomer expanded beads containing a coloring agent, wherein an apparent density of the expanded beads is 40 to 300 g/L, and an average surface layer membrane thickness (a) is 3 to 25 μm, and a molded article thereof, and is able to provide expanded beads capable of producing an expanded beads molded article which is excellent in in-mold moldability and excellent in tensile characteristics and an expanded beads molded article using the expanded beads.

Described herein is a Low TVOC flame-retardant polyurethane spray foam system, including at least one isocyanate as isocyanate component, and at least one substance reactive toward isocyanate, chain extender and/or crosslinking agent, flame retardant, blowing agent, catalysts, and additives and/or auxiliaries, as resin components, where the flame retardant includes expandable graphite and melamine, the amount of expandable graphite is in the range of from 5 wt % to less than 30 wt %, and the amount of melamine is in the range of from greater than 5 wt % to 30 wt %, each based on the total weight of the resin components. Also described herein are a polyurethane spray foam produced therefrom, the preparation thereof, and a method of use thereof in the application of heat insulation, sound insulation, cavity filling and damping packing.

A method of foam production is described. The method includes providing a foam precursor including one or more components, the one or more components including at least one of chitin, chitosan, or chitosan oligosaccharide and a solvent. The method further comprises exposing the foam precursor to radiation. The radiation is of a wavelength to heat the foam precursor. A system for foam produced is described, the system including a mixer configured to output a foam precursor including one or more components. The one or more components include at least one of chitin, chitosan, or chitosan oligosaccharide. The system further includes a radiation emitting system positioned to receive the foam precursor from the mixer and expose the foam precursor to radiation to heat the foam precursor to form a solid foam.

The thermoplastic elastomer composition contains a thermoplastic elastomer and a pigment.

This invention relates to a foaming composition, comprising at least one ethylene-vinyl acetate (EVA) copolymer; at least one foaming agent; at least one peroxide compound; at least one polyamine; at least one crosslinking enhancer; at least one primary antioxidant; and at least one secondary antioxidant; the content of the crosslinking enhancer is from 0.1 to 3% by weight based on the total weight of the composition. A foaming article cured from the foaming composition under the temperature range of 80 to 120° C. according to the present invention exhibits high initial volume expansion ratio at the baking window from 130 to 200° C. and shows excellent stability after storage.

A porous film includes at least one porous polyimide film that includes a polyimide resin, an organic amine compound and a resin other than a polyimide resin, and that does not include a polar aprotic solvent, wherein a content of the organic amine compound is 0.001% by weight or higher with respect to a total weight of the porous polyimide film.

An insulation material formed of a composition, and a method of making an insulation material is provided. The composition forming the insulation material includes magnesium oxide; at least one of magnesium chloride, magnesium sulfate, and hydrates thereof; water; a foaming agent; a thickener; and a foam stabilizer. The composition is foamed to promote aeration of the composition to reduce density of the insulation material formed from the composition.

Expanded polyethylene resin particles include an antistatic agent and a base resin. The expanded polyethylene resin particles are obtained by expanding polyethylene resin particles including the antistatic agent and the base resin, the polyethylene resin particles having a storage modulus of elasticity of 900 to 5000 Pa at an angular frequency of 1 rad/sec in dynamic viscoelastic behavior measurement at 190° C. and a storage modulus of elasticity of 100000 Pa or less at an angular frequency of 100 rad/sec in dynamic viscoelastic behavior measurement at 190° C. The expanded polyethylene resin particles have a low temperature side melting peak and a high temperature side melting peak on a differential scanning calorimetry (DSC) curve obtained when a temperature of the expanded polyethylene resin particles is increased from 20° C. to 220° C. at a heating rate of 10° C./min.

A method of producing a polyethylene resin expanded molded product includes filling a mold with expanded polyethylene resin particles, wherein an internal pressure of 0.12 to 0.16 MPa is applied to the expanded polyethylene resin particles in the mold, and forming the polyethylene resin expanded molded product by heating the expanded polyethylene resin particles and fusing the expanded polyethylene resin particles. The expanded polyethylene resin particles includes 100 parts by weight of a polyethylene resin, 0.08 to 0.25 parts by weight of a cell nucleating agent, 0.3 to 0.8 parts by weight of a polyhydric alcohol fatty acid ester, and 0.01 to 10 parts by weight of a hydrophilic compound, each of the expanded polyethylene resin particles having a weight of 2.5 to 3.5 mg. The polyethylene resin expanded molded product has a density of 0.017 to 0.021 g/cm.sup.3 and a thickness of 10 to 40 mm.

An expanded polyolefin resin particle is obtained by expanding a polyolefin resin particle using water and/or an inorganic gas as a foaming agent. The polyolefin resin particle includes a polyolefin resin, a product obtained by heating and kneading a mixture, and a water absorbing substance, wherein the mixture includes a first polypropylene resin, a polypropylene wax, a polyorganosiloxane including at least one silicon-atom-bound radical polymerizable functional group per molecule, and an organic peroxide.