Provided is a method of producing a toner including the steps of: mixing a resin solution comprising a resin R, a colorant, and an organic solvent, a resin fine particle comprising a resin S containing an element α, and carbon dioxide to form a droplet having a surface covered with the resin fine particle; introducing carbon dioxide in a liquid state and pressurizing to extract the organic solvent in the droplet; and removing the extracted organic solvent together with the carbon dioxide to provide a toner particle. In the method of producing a toner, when the resin fine particle is treated with the carbon dioxide in a liquid state, a change in amount of the element α on the surface of the resin fine particle after the treatment as compared to the amount before the treatment falls within a specific range.

Provided are rapidly cross-linkable silicone foam compositions, kits, and methods for filling implanted medical devices in situ or in vivo, the implanted medical devices, including for example, body implants and tissue expanders, the compositions including a platinum divinyl disiloxane complex; a low viscosity vinyl terminated polydimethylsiloxane; a low viscosity hydride terminated polydimethylsiloxane; a silicone cross-linker; and a gas and/or gas-filled microcapsules, where the rapidly cross-linkable silicone foam composition has a viscosity of ≤150 cPs for ≥1 min. post-preparation and ≤300 cPs≤5 min. post-preparation, at ambient temperature.

A thermoplastic elastomer composition comprising a blend of (A) a thermoplastic organic polyether block amide copolymer, (B) a silicone composition comprising (B1) a silicone base comprising (B1a) a diorganopolysiloxane polymer having a viscosity of at least 1000000 mPa.Math.s at 25° C. and an average of at least 2 alkenyl groups per molecule and (B1b) a reinforcing filler in an amount of from 1 to 50% by weight based on the weight of (B1a), (B2) an organohydrido silicone compound which contains an average of at least 2 silicon-bonded hydrogen groups per molecule, (C) a hydrosilylation catalyst, and optionally: one or more additives component (D), wherein the weight ratio of thermoplastic organic polyether block amide copolymer (A) to the silicone composition (B) is in the range 50:50 to 95:5, and wherein component (B2) and (C) are present in an amount sufficient to cure said silicone composition (B1).

A method for nano-depth surface activation of a PTFE-based membrane and relates to the technical field of polymer composites is disclosed. The method comprises the following steps: covering a functional surface of a PTFE-based nano functional composite membrane, performing surface activation treatment on a single surface of the membrane to which a bonding adhesive is applied, and migrating and complexing a high-toughness cold bonding adhesive tape on the membrane surface, with an activated structure layer, of the PTFE-based nano functional composite membrane through a mechanical adhesive applying device to form an adhesive-membrane complex. An extremely strong affinity and a high-strength bonding performance are generated between the membrane and the adhesive, and the adhesive-membrane complex is formed. Integration of membrane/adhesive bonding complexing, membrane/membrane bonding complexing and membrane/adhesive layer bonding is realized.

A crosslinked polyolefin separator which has gels with a longer side length of 50 μm or more in a number ranging from 0 to 3 per 1 m.sup.2 of the separator, and shows a standard deviation of absorbance ratio between the center of the separator and the side thereof ranging from 0.01 to 0.5 is provided. A method for manufacturing the crosslinked polyolefin separator is also provided. The method includes (S1) preparing a polyolefin porous membranes, and (S2) applying a coating solution containing an initiator and alkoxy group-containing vinylsilane onto at least one surface of the porous membrane. The coating solution can permeate even to the inside of exposed pores. Thus, it is possible to provide a crosslinked polyolefin separator in which silane crosslinking occurs uniformly even inside of the pores.

Expandable polystyrene-based resin particles may include a styrene-based monomer, a polysiloxane-containing macro monomer, and a coating composition having a melting point of 40° C. or greater. A coefficient of static friction of a foamed molded product, obtained by pre-expanding the expandable polystyrene-based resin particles and molding the pre-expanded expandable polystyrene-based resin particles, may be 4.0 or less. The expandable polystyrene-based resin particles may have a surface layer part that contains polysiloxane as a main component.

A plastic substrate includes: a transparent plastic support member; a first inorganic layer on a surface of the plastic support member; and a first organic-inorganic hybrid layer on the first inorganic layer. A display device includes a display panel and a window on the display panel, the window including the plastic substrate.

An addition reaction-curable silicone emulsion composition containing a water-soluble silane coupling agent (I) and an organopolysiloxane (II) having at least two alkenyl groups in one molecule thereof, where the water-soluble silane coupling agent (I) has at least one group selected from among a succinic anhydride group, a quaternary ammonium group, and a ureido group, and 1 part by mass or more of the water-soluble silane coupling agent (I) is contained relative to 100 parts by mass of the organopolysiloxane (II). This provides: a silicone emulsion composition that gives a cured film adhering well to plastic film substrates regardless of the type, while having suitable release properties regarding adhesives; and a delamination film made by forming a cured film of the silicone emulsion composition.

A rigid polyurethane foam formulation comprising a polyol composition comprising, by weight based on the weight of the polyol composition, more than 70% of at least one polyester polyol having an average hydroxyl number of from 150 to less than 300 mg KOH/g and an average functionality of at least 2; a blowing agent comprising water and an auxiliary blowing agent; a silicone copolymer surfactant; from 1% to 5% by weight based on the weight of the polyol composition, of a cyclic siloxane having a surface tension less than 21 dynes/cm at 25° C., wherein the weight ratio of the cyclic siloxane to the silicone copolymer surfactant is from 0.6 to less than 2.27; a catalyst, and optionally a flame retardant; and a polyisocyanate; such that the isocyanate index is in the range of from 180 to 500; a rigid polyurethane foam formed from the foam formulation; and a method of forming a rigid polyurethane foam.

A crosslinked polyolefin separator which has gels with a longer side length of 50 μm or more in a number ranging from 0 to 3 per 1 m.sup.2 of the separator, and shows a standard deviation of absorbance ratio between the center of the separator and the side thereof ranging from 0.01 to 0.5 is provided. A method for manufacturing the crosslinked polyolefin separator is also provided. The method includes (S1) preparing a polyolefin porous membrane, and (S2) applying a coating solution containing an initiator and alkoxy group-containing vinylsilane onto at least one surface of the porous membrane. The coating solution can permeate even to the inside of exposed pores. Thus, it is possible to provide a crosslinked polyolefin separator in which silane crosslinking occurs uniformly even inside of the pores.