Disclosed are a composite oxide which is capable of maintaining a large volume of pores even used in a high temperature environment, and which has excellent heat resistance and catalytic activity, as well as a method for producing the composite oxide and a catalyst for exhaust gas purification employing the composite oxide. The composite oxide contains cerium and at least one element selected from aluminum, silicon, or rare earth metals other than cerium and including yttrium, at a mass ratio of 85:15 to 99:1 in terms oxides, and has a property of exhibiting a not less than 0.30 cm.sup.3/g, preferably not less than 0.40 cm.sup.3/g volume of pores with a diameter of not larger than 200 nm, after calcination at 900° C. for 5 hours, and is suitable for a co-catalyst in a catalyst for vehicle exhaust gas purification.

The invention provides a method for the production of a supported nickel catalyst, in which an aqueous mixture comprising an alkali metal salt plus other metal salts is sintered to form a support material. A supported nickel catalyst comprising potassium β-alumina is also provided.

An object of the present invention is to provide ferrite particles for supporting a catalyst having a small apparent density, various properties are maintained in a controllable state and a specified volume is filled with a small weight, and a catalyst using the ferrite particles for supporting a catalyst. To achieve the object, ferrite particles for supporting a catalyst provided with an outer shell structure containing Ti oxide, a catalyst using the ferrite particles for supporting a catalyst are employed.

The present invention relates to a mixed oxide of aluminium, of zirconium, of cerium, of lanthanum and optionally of at least one rare-earth metal other than cerium and lanthanum that makes it possible to repair a catalyst that retains, after severe ageing, a good thermal stability and a good catalytic activity. The invention also relates to the process for preparing this mixed oxide and also to a process for treating exhaust gases from internal combustion engines using a catalyst prepared from this mixed oxide.

A process for preparing C2 to C3 hydrocarbons may include introducing a feed stream including hydrogen gas and a carbon-containing gas comprising carbon monoxide, carbon dioxide, and mixtures thereof into a reaction zone of a reactor, and converting the feed stream into a product stream comprising C2 to C3 hydrocarbons in the reaction zone in the presence of a hybrid catalyst. The hybrid catalyst may include a metal oxide catalyst component and a microporous catalyst component comprising 8-MR pore openings less than or equal to 5.1 A and a cage defining ring size less than or equal to 7.45 A, where a C2/C3 carbon molar ratio of the product stream is greater than or equal to 0.7.

The invention provides for a method to prepare an alumina catalyst support comprising bismuth for emission control applications, to an alumina catalyst support prepared according to the method of the invention and to an alumina catalyst support comprising bismuth and having a specific crystallinity value that leads to improved technical effects.

The present invention provides a catalyst, comprising molybdenum; one or more first elements selected from a Group V, VI, VII, VIII, IX, X, and XI metal (e.g., silver, cobalt, nickel, copper, rhodium, ruthenium, iridium, palladium, niobium, and manganese); one or more second elements selected from sulfur, carbon, oxygen, phosphorus, nitrogen, and selenium; and optionally, one or more Group IA metals, wherein the molybdenum is present in an amount of 10-50 wt. % of the total amount of the one or more first elements, the molybdenum, the one or more second elements, and the Group IA metal, and methods of using said catalyst in the production of ethanol from carbon dioxide.

Disclosed are a spherelike supermacroporous mesoporous material, a polyolefin catalyst, and a preparation method therefor and an olefin polymerization process. The spherelike supermacroporous mesoporous material has a twodimensional hexagonal ordered pore channel structures. The mesoporous material has an average pore size of 10 nm to 15 nm, a specific surface area of 300 m.sup.2/g to 400 m.sup.2/g, and an average particle size of 1 .Math.m to 3 .Math.m, based on the total mass of the mesoporous material. The mass content of water in the mesoporous material is < 1 ppm. The mass content of oxygen in the mesoporous material is < 1 ppm. When a polyolefin catalyst prepared with the mesoporous material as a carrier is used for an olefin polymerization reaction, the a polyolefin product with a narrow molecular weight distribution and a good melt index can be obtained.

Described herein are reusable, mesh-based catalysts with superior mechanical stability and magnetic separability wherein the mesh may be formed in a variety of shapes and can be easily separated from a process stream and in combination with biomass torrefaction, reduces toxic emissions and produce hydrogen gas, which can be burned at the facility to generate heat or electricity.

The present invention relates to a catalyst to be applied to the process of gasification of coke or coal, individually or in mixture, and to the process of preparing said catalyst, which is useful in obtaining higher levels of hydrogen and carbon monoxide, which allows the conversion of coke into by-products of higher added value (hydrogen-rich syngas). The present invention also addresses to a process for converting petroleum coke by using a catalyst according to the present invention.