A sintered magnet contains Sm—Fe—N-based crystal grains and has high coercivity; and a magnetic powder is capable of forming a sintered magnet without lowering the coercivity even if heat is generated in association with the sintering. A sintered magnet comprises a crystal phase composed of a plurality of Sm—Fe—N-based crystal grains and a nonmagnetic metal phase present between the Sm—Fe—N crystal grains adjacent to each other, wherein a ratio of Fe peak intensity I.sub.Fe to SmFeN peak intensity I.sub.SmFeN measured by an X-ray diffraction method is 0.2 or less. A magnetic powder comprises Sm—Fe—N-based crystal particles and a nonmagnetic metal layer covering surfaces of the Sm—Fe—N crystal particles.

To provide novel low-temperature sinterable copper particles that can be sintered even at a low temperature of, for example, around 100° C. or less, and a method for producing a sintered body by using the same. The low-temperature sinterable copper particles according to the present invention are coated with a carboxylic acid, and a surface of the copper particle is oxidized so as to have a cuprous oxide fraction (Cu.sub.2O/(Cu+Cu.sub.2O)) in the copper particle of 4% by mass or less or so as to have an average coating thickness of cuprous oxide of 10 nm or less. The low-temperature sinterable copper particles are subjected to low-temperature firing in an atmosphere of 0.01 Pa or less.

To provide novel low-temperature sinterable copper particles that can be sintered even at a low temperature of, for example, around 100° C. or less, and a method for producing a sintered body by using the same. The low-temperature sinterable copper particles according to the present invention are coated with a carboxylic acid, and a surface of the copper particle is oxidized so as to have a cuprous oxide fraction (Cu.sub.2O/(Cu+Cu.sub.2O)) in the copper particle of 4% by mass or less or so as to have an average coating thickness of cuprous oxide of 10 nm or less. The low-temperature sinterable copper particles are subjected to low-temperature firing in an atmosphere of 0.01 Pa or less.

A process for manufacturing a multi-material part by additive manufacturing, includes the following steps: a) a step of providing a pre-treated metal powder comprising grains and an oxidized and porous layer on a surface of the grains; b) a selective laser powder-bed fusion step comprising implementation of steps i) and ii) as follows: i) a step of forming a layer from the pre-treated metal powder; ii) a step of melting by laser the layer, the melting step being carried out under a reactive atmosphere and comprising changing parameters of application of the laser so that at least a first region of the layer is converted so as to lower the electrical conductivity thereof, thus forming a dielectric, and so that at least a second region of the layer is densified without converting it, the at least a first region being formed when the parameters of application of the laser allow a first energy density to be applied to the first region and/or the laser beam to be kept for a first dwell time on the first region, the at least a second region being formed when the parameters of application of the laser allow a second energy density to be applied to the second region and/or the laser beam to be kept for a second dwell time on the second region, and the first energy density being higher than the second energy density and/or the first dwell time being longer than the second dwell time. A part obtained using the process is also provided.

A process for manufacturing a multi-material part by additive manufacturing, includes the following steps: a) a step of providing a pre-treated metal powder comprising grains and an oxidized and porous layer on a surface of the grains; b) a selective laser powder-bed fusion step comprising implementation of steps i) and ii) as follows: i) a step of forming a layer from the pre-treated metal powder; ii) a step of melting by laser the layer, the melting step being carried out under a reactive atmosphere and comprising changing parameters of application of the laser so that at least a first region of the layer is converted so as to lower the electrical conductivity thereof, thus forming a dielectric, and so that at least a second region of the layer is densified without converting it, the at least a first region being formed when the parameters of application of the laser allow a first energy density to be applied to the first region and/or the laser beam to be kept for a first dwell time on the first region, the at least a second region being formed when the parameters of application of the laser allow a second energy density to be applied to the second region and/or the laser beam to be kept for a second dwell time on the second region, and the first energy density being higher than the second energy density and/or the first dwell time being longer than the second dwell time. A part obtained using the process is also provided.

An R-T-B series permanent magnet material, a raw material composition, a preparation method, and an application. The R-T-B series permanent magnet material comprises the following components: R: 29-31.0 wt. %, RH is greater than 1 wt. %, B: 0.905-0.945 wt. %, C: 0.04-0.15 wt. %, N: 0.1-0.4 wt. %, and Fe: 67-69 wt. %, wherein R comprises RL and RH, RL is a light rare earth element, RL comprises Nd, RH is a heavy rare earth element, a (RL.sub.1-yRH.sub.y).sub.2T.sub.17C.sub.x phase is present at the grain boundary of the R-T-B series permanent magnet material, x: 2-3, y: 0.15-0.35, and T must comprise Fe, and also comprises one or more among Co, Ti and N. The permanent magnet material retains relative high Br and Hcj under different heat treatment temperatures.

A method for manufacturing a porous metal body according to the present invention includes: a surface oxidizing step of heating a titanium-containing powder in an atmosphere containing oxygen at a temperature of 250° C. or more for 30 minutes or more to provide a surface-oxidized powder; and a sintering step of depositing the surface-oxidized powder in a dry process, and sintering the surface-oxidized powder by heating it in a reduced pressure atmosphere or an inert atmosphere at a temperature of 950° C. or more.

A method for manufacturing a porous metal body according to the present invention includes: a surface oxidizing step of heating a titanium-containing powder in an atmosphere containing oxygen at a temperature of 250° C. or more for 30 minutes or more to provide a surface-oxidized powder; and a sintering step of depositing the surface-oxidized powder in a dry process, and sintering the surface-oxidized powder by heating it in a reduced pressure atmosphere or an inert atmosphere at a temperature of 950° C. or more.

The invention provides a powder magnetic core and a method for manufacturing a powder magnetic core through simple compression molding and capable of manufacturing a complicatedly shaped powder magnetic core with reliable high strength and insulating properties. A method for manufacturing a powder magnetic core with a metallic soft magnetic material powder includes: a first step including mixing a soft magnetic material powder and a binder; a second step including compression molding the mixture obtained after the first step; a third step including performing at least one of grinding and cutting on the compact obtained after the second step; and a fourth step including heat-treating the compact after the third step, wherein in the fourth step, the compact is heat-treated so that an oxide layer containing an element constituting the soft magnetic material powder is formed on the surface of the soft magnetic material powder.

The invention provides a powder magnetic core and a method for manufacturing a powder magnetic core through simple compression molding and capable of manufacturing a complicatedly shaped powder magnetic core with reliable high strength and insulating properties. A method for manufacturing a powder magnetic core with a metallic soft magnetic material powder includes: a first step including mixing a soft magnetic material powder and a binder; a second step including compression molding the mixture obtained after the first step; a third step including performing at least one of grinding and cutting on the compact obtained after the second step; and a fourth step including heat-treating the compact after the third step, wherein in the fourth step, the compact is heat-treated so that an oxide layer containing an element constituting the soft magnetic material powder is formed on the surface of the soft magnetic material powder.