A process for providing a fiber cement product is provided the process comprising the steps of: —providing an uncured fiber cement product; —curing said uncured fiber cement product; —drying said cured fiber cement product to obtain a humidity of said cured fiber cement product being less than or equal to about 8% w; —abrasive blasting at least part of the surface of said dried fiber cement product.

[Object] To provide a building material having excellent durability.

[Solution] A building material has a convex part formed on a surface thereof, the convex part including a first lateral surface part and a second lateral surface part corresponding to the first lateral surface part. The building material is formed from a mixture containing a hydraulic material, an admixture, and a plant-based reinforcing material, and the plant-based reinforcing material at least in the convex part is distributed in the mixture with the hydraulic material and the admixture attached to the plant-based reinforcing material. A distribution of the plant-based reinforcing material in the first lateral surface part and a distribution of the plant-based reinforcing material in the second lateral surface part are substantially the same. Desirably, the convex part includes a first edge part that is an edge part of the first lateral surface part and a second edge part that is an edge part of the second lateral surface part and that corresponds to the first edge part, and a distribution of holes formed in the first edge part and a distribution of holes formed in the second edge part are substantially the same.

[Object] To provide a building material having excellent durability.

[Solution] A building material has a convex part formed on a surface thereof, the convex part including a first lateral surface part and a second lateral surface part corresponding to the first lateral surface part. The building material is formed from a mixture containing a hydraulic material, an admixture, and a plant-based reinforcing material, and the plant-based reinforcing material at least in the convex part is distributed in the mixture with the hydraulic material and the admixture attached to the plant-based reinforcing material. A distribution of the plant-based reinforcing material in the first lateral surface part and a distribution of the plant-based reinforcing material in the second lateral surface part are substantially the same. Desirably, the convex part includes a first edge part that is an edge part of the first lateral surface part and a second edge part that is an edge part of the second lateral surface part and that corresponds to the first edge part, and a distribution of holes formed in the first edge part and a distribution of holes formed in the second edge part are substantially the same.

An inorganic fiber toughened inorganic composite artificial stone panel and a preparation method thereof are disclosed. The panel includes a surface layer and a toughened base layer. The surface layer includes the the following components in parts by weight: 40-70 parts of quartz sand, 10-30 parts of quartz powder, 20-45 parts of inorganic active powder, 0.5-4 parts of pigment, 0.3-1 parts of water reducing agent and 3-10 parts of water. The toughened base layer includes the following components in parts by weight: 40-60 parts of inorganic active powder, 45-65 parts of sand, 0.8-1.5 parts of water reducing agent, 6-14 parts of water, 0.4-2 parts of inorganic fiber and 0.8-2.5 parts of toughener.

The present invention relates to fiber cement products comprising an inner core material, which inner core material is covered by at least one outer surface layer, characterized in that: —said inner core material has a density of between about 0.4 and about 0.9 g/cm.sup.3 inclusive, and at least comprises cement and between 1 wt % and 70 wt % (with respect to the total dry weight of said inner core material) of a lightweight filler, and—said at least one outer surface layer has a density of between about 0.9 and about 1.4 g/cm.sup.3 inclusive, and at least comprises fibers and cement.

A method for making a carbonated precast concrete product includes: obtaining a mixture including at least one binder material, an aggregate, and water; molding the mixture into a molded intermediate; demolding the molded intermediate to obtain a demolded intermediate, the demolded intermediate having a first water-to-binder ratio; conditioning the demolded intermediate to provide a conditioned article having a second water-to-binder ratio less than the first water-to-binder ratio of the demolded intermediate; moisturizing at least one surface of the conditioned article with an aqueous medium, thereby causing a weight gain of the conditioned article and providing a moisturized product, a first portion of the moisturized product having a third water-to-binder ratio greater than a fourth water-to-binder ratio of a remainder of the moisturized product; and curing the moisturized product with carbon dioxide to obtain the carbonated precast concrete product.

A method for making a carbonated precast concrete product includes: obtaining a mixture including at least one binder material, an aggregate, and water; molding the mixture into a molded intermediate; demolding the molded intermediate to obtain a demolded intermediate, the demolded intermediate having a first water-to-binder ratio; conditioning the demolded intermediate to provide a conditioned article having a second water-to-binder ratio less than the first water-to-binder ratio of the demolded intermediate; moisturizing at least one surface of the conditioned article with an aqueous medium, thereby causing a weight gain of the conditioned article and providing a moisturized product, a first portion of the moisturized product having a third water-to-binder ratio greater than a fourth water-to-binder ratio of a remainder of the moisturized product; and curing the moisturized product with carbon dioxide to obtain the carbonated precast concrete product.

Method for producing a friction material, including the following steps in sequence: mixing an aluminosilicate source with an alkaline silicate solution to form a geopolymer, adding a friction mix to the geopolymer solution of the previous step to obtain a slurry, casting the slurry in a mold at temperature between room temperature and 120° C. and for between 5 min and 2 h and demolding to obtain a pad, attaching a backplate to the pad, curing for a time between X and Y hours at a temperature of between X and Y. The friction material obtained with the method is for the manufacture of friction layers/blocks for friction elements such as braking elements, including vehicle brake pads or blocks, and/or friction discs.

Method for producing a friction material, including the following steps in sequence: mixing an aluminosilicate source with an alkaline silicate solution to form a geopolymer, adding a friction mix to the geopolymer solution of the previous step to obtain a slurry, casting the slurry in a mold at temperature between room temperature and 120° C. and for between 5 min and 2 h and demolding to obtain a pad, attaching a backplate to the pad, curing for a time between X and Y hours at a temperature of between X and Y. The friction material obtained with the method is for the manufacture of friction layers/blocks for friction elements such as braking elements, including vehicle brake pads or blocks, and/or friction discs.

A method for injecting a loaded suspension into a fibrous texture having a three-dimensional or multilayer weaving includes the injection of a suspension containing a powder of solid particles into the volume of the fibrous texture. The injection of the loaded suspension is carried out by at least one hollow needle in communication with a loaded suspension supply device, each needle being movable in at least one direction extending between a first face and a second opposite face of the fibrous texture so as to inject the loaded suspension at one or more determined depths in the fibrous texture.