A mixed ionic and electronic conductor represented by Formula 1:
T.sub.xVa.sub.yA.sub.1-x-yM.sub.zO.sub.3-δ,
wherein T includes at least one monovalent cation, A includes at least one of a monovalent cation, a divalent cation, and a trivalent cation, M includes at least one of a trivalent cation, a tetravalent cation, and a pentavalent cation, M is an element other than Ti and Zr, Va is a vacancy, δ is an oxygen vacancy, 0<x, y≤0.25, 0<z<1, and 0≤δ≤1.

An apparatus for solid state energy harvesting includes a complex oxide based pyrochlores having a chemical formula of A2 B2 O7 configured to directly convert heat into electricity and operate and function at a higher temperature without oxidizing in air. The complex oxide based pyrochlores are mixed with cation at B-site.

Provided is a method of producing a metal nanoparticle-oxide support complex structure, in which metal nanoparticles uniform in size are evenly distributed on the surface of oxide supports. A gas sensor with improved gas sensing ability and durability may be provided by using the same.

Provided is a crystalline oxide film including: a plane tilted from a c-plane as a principal plane; gallium; and a metal in Group 9 of the periodic table, the metal in Group 9 of the periodic table among all metallic elements in the film having an atomic ratio of equal to or less than 23%.

A cathode configured to use oxygen as a cathode active material includes: a porous film including a metal oxide, where a porosity of the porous film is about 50 volume percent to about 95 volume percent, based on a total volume of the porous film, and an amount of an organic component in the porous film is 0 to about 2 weight percent, based on a total weight of the porous film.

Disclosed are a perovskite compound, a method for producing the perovskite compound, a catalyst for a fuel cell including the perovskite compound, and a method for producing the catalyst. The perovskite compound overcomes the low stability of palladium due to its perovskite structural properties. Therefore, the perovskite compound can be used as a catalyst material for a fuel cell. In addition, the use of palladium in the catalyst instead of expensive platinum leads to an improvement in the price competitiveness of fuel cells. The catalyst is highly durable and catalytically active due to its perovskite structure.

A solid electrolyte having high electrical conductivity even in a low-temperature region is provided. A solid electrolyte containing a hexagonal perovskite-related compound, in which the compound is a compound represented by the following general formula (1), and an electrolyte layer and a battery using the solid electrolyte are disclosed. Ba.sub.7-αNb.sub.(4−x-y)Mo.sub.(1+x)M.sub.yO.sub.(20+z) (1), in the formula (1), M is a cation of at least one element; a represents a Ba deficiency amount and represents a value of 0 or more and 0.5 or less, x represents a value of −1.1 or more and 1.1 or less, y represents a value of 0 or more and 1.1 or less, and z represents an oxygen non-stoichiometry and represents a value of −2.0 or more and 2.0 or less, provided that in the formula (1), |x|+y≥0.01 is satisfied.

Provided are: an oxygen catalyst that uses an alkaline aqueous solution as an electrolyte and has high catalytic activity; and an electrode. The oxygen catalyst according to the present invention is an oxygen catalyst in which an alkaline aqueous solution is used as an electrolyte, the oxygen catalyst being characterized by having a pyrochlore oxide structure including bismuth on an A-site and ruthenium on a B-site, and containing manganese as well as bismuth and ruthenium. The electrode according to the present invention is characterized by using the oxygen catalyst according to the present invention.

A method of forming a metal oxide material having a rod shape or polyhedral nanostructure includes preparing a first reverse micro-emulsion system comprising an aqueous precipitating agent dispersion and a second reverse micro-emulsion system containing an aqueous metal salt dispersion; combining the micro-emulsions together to initiate a reaction; allowing the reaction to continue to form a product mixture comprising a metal oxide gel and aqueous media; separating the metal oxide gel from the aqueous media; collecting the metal oxide gel; and calcining the metal oxide gel to form the metal oxide material. The metal oxide material corresponds to the chemical formula of La.sub.2M.sub.xNi.sub.1-xO.sub.4, Pr.sub.2-yA.sub.yNiO.sub.4, or La.sub.2-zD.sub.zNiO.sub.4, wherein M is copper, cobalt, iron, manganese, chromium, aluminum, or platinum; A is lanthanum or neodymium; D is calcium, barium or strontium; x ranges from 0 to 1; y ranges from 0 to 2; and z ranges from 0 to 0.25.

A cathode configured to use oxygen as a cathode active material includes: a porous film including a metal oxide, where a porosity of the porous film is about 50 volume percent to about 95 volume percent, based on a total volume of the porous film, and an amount of an organic component in the porous film is 0 to about 2 weight percent, based on a total weight of the porous film.