The present invention relates to a carbonaceous material for an electrochemical device, having an average particle size D.sub.50 of 30 μm or larger as measured by a laser scattering method, and a basic flowability energy BFE of 270 mJ to 1,100 mJ as measured using a powder flowability analyzer equipped with a measuring vessel of 50 mm in diameter and 160 mL in volume under the conditions of a blade tip speed of 100 mm/sec and a powder sample filling capacity of 120 mL and calculated by the following formula: BFE=T/(R tan α)+F (wherein, R=48 mm, α=5°, T represents a numerical value of the rotational torque measured by the analyzer, and F represents a numerical value of the normal stress measured by the analyzer).

A non-spray-drying, dry-granulation process for making a ceramic particulate mixture including from 4 wt % to 9 wt % water. At least 90 wt % of the particles have a particle size of from 80 μm to 600 μm. The process includes the steps of: (a) forming a precursor material; (b) subjecting the precursor material to a compaction step to form a compacted precursor material; (c) subjecting the compacted precursor material to a crushing step to form a crushed precursor material; and (d) subjecting the crushed precursor material to at least two air classification steps. One air classification step removes at least a portion of the particles having a particle size of greater than 600 μm from the crushed precursor material, and the other air classification step removes at least a portion of the particles having a particle size of less than 80 μm from the crushed precursor material.

The present invention is a method for manufacturing a high-performance composite active material of zinc oxide powder, which is a method for manufacturing a high-performance composite active zinc oxide material powder as an aid for an operation of shaping and vulcanization of rubber/plastic materials, generally carried out by mixing an alkali solution and a calcium compound, in combination with addition of a zinc salt to directly carry out a chemical reaction therewith through mixture so as to obtain a precipitation solution of a predetermined pH value, following a process of filtering to remove water to form an intermediate powder material, which is subjected to drying to form zinc oxide long crystal material exhibiting nanometer scale high performance composite activity, helping achieve a purpose of diversification of application of zinc oxide power in industry.

Polarizable diamond materials and methods for obtaining nuclear magnetic resonance spectra of samples external to the diamond materials are described. The diamond materials can include .sup.12C, .sup.13C, substitutional nitrogen, and nitrogen vacancy defects in a crystalline lattice, wherein the substitutional nitrogen concentration is between 10 ppm and 200 ppm, the nitrogen vacancy concentration is between 10 ppb and 10 ppm, and the .sup.13C concentration is greater than 1.1% and not more than 25%. Methods for obtaining nuclear magnetic resonance spectra can include optically pumping a diamond material to generate electron spin hyperpolarization in nitrogen vacancy centers, transferring the electron spin hyperpolarization to nuclei of the sample, and generating a nuclear magnetic resonance spectrum by applying a magnetic field to the sample, exciting the sample with a radio frequency pulse, and detecting a nuclear magnetic resonance response from the sample.

The present invention relates to a method for producing a highly porous fine powdery slaked lime composition, comprising a fluidification step for forming said highly porous fine powdery slaked lime composition having an Alpine fluidity greater than 50% and which is carried out in a dryer/grinder chosen from the group consisting of a pin-type dryer/grinder, a cage-type dryer/grinder, an instantaneous dryer/disagglomerator and a combination of these until the powdery slaked lime composition has a non-solid residual-phase content of less than or equal to 3.5% by weight and greater than or equal to 0.3% by weight, as well as the product obtained therefrom.

A method is useful for reducing the caking tendency of potassium chloride during storage thereof, wherein caking of the potassium chloride grains is induced in the potassium chloride, the caked potassium chloride is passed to grinding, and the ground potassium chloride is subsequently put into storage.

A hexagonal boron nitride powder whose maximum absorption peak within the range of 3,100 to 3,800 cm.sup.1 of the diffuse reflectance fourier transform infrared spectrum is existent at 3,530 to 3,590 cm.sup.1 and which is able to provide high heat conductivity, dielectric strength and copper foil peel strength to a resin composition obtained by filling the powder into a resin, and a process for producing the above boron nitride powder by mixing together an oxygen-containing boron compound, a carbon source having a sulfur concentration of 1,000 to 10,000 ppm and an oxygen-containing calcium compound in a specific ratio and reduction nitriding the mixture.

The present invention is a method for manufacturing a high-performance composite active material of zinc oxide powder, which is a method for manufacturing a high-performance composite active zinc oxide material powder as an aid for an operation of shaping and vulcanization of rubber/plastic materials, generally carried out by mixing an alkali solution and a calcium compound, in combination with addition of a zinc salt to directly carry out a chemical reaction therewith through mixture so as to obtain a precipitation solution of a predetermined pH value, following a process of filtering to remove water to form an intermediate powder material, which is subjected to drying to form zinc oxide long crystal material exhibiting nanometer scale high performance composite activity, helping achieve a purpose of diversification of application of zinc oxide power in industry.

The present invention relates to: an alumina powder wherein a ratio (TBD/LBD) of a tapped bulk density (TBD) to a loose bulk density (LBD) is 1.5 or more; an alumina slurry containing the same; an alumina-containing coating layer; a multilayer separation membrane; and a secondary battery.

An infrared absorbing fine particle dispersed powder, dispersion liquid containing infrared absorbing fine particle dispersed powder, ink containing infrared absorbing fine particle dispersed powder, and anti-counterfeit ink and anti-counterfeit printed matter, which are transparent in a visible light region, have excellent infrared absorption properties, and are also excellent in chemical resistance, and an infrared absorbing fine particle dispersed powder containing particles made of solid media and having an average particle size of 1 m or more and having infrared absorbing fine particles dispersed inside.