The present invention provides a method for producing a zirconia particle-containing powder that enables easy production of a zirconia sintered body having both high translucency and high strength. The present invention relates to a method for producing a zirconia particle-containing powder, comprising a drying step of spray drying a slurry containing zirconia particles, wherein the zirconia particles have an average primary particle diameter of 30 nm or less, and the slurry comprises a dispersion medium containing a liquid having a surface tension at 25° C. of 50 mN/m or less. Preferably, the zirconia particles comprise 2.0 to 9.0 mol % yttria. Preferably, wherein the content of the liquid in the dispersion medium is 50 mass % or more.

[Problem]

A technique for improving translucency in order to prepare a zirconia sintered body having high translucency without using special equipment, has been required.

[Solution]

To provide A sintering method for a dental zirconia calcined body containing 5.5 mol % to 7.0 mol % of a stabilizer, wherein the method satisfies the following (a) to (c). (a) an average rate of temperature increase in the section from room temperature to 1300° C. is 9° C./min or more. (b) an average rate of temperature increase in the section from 1300° C. to 1400° C. is 0.6° C./min or more and 3° C./min or less. (c) an average rate of temperature increase in the section from 1400° C. to the maximum temperature of the sintering process is 0.5° C./min or more and 2.5° C./min or less.

A zirconia sintered body is provided and includes yttria and zirconia, containing yttria by a content ranging from 4.5 mol % or more to 6.5 mol % or less and zirconia as the remainder, the total light transmittance of a 1-mm thick sample measured in compliance with JIS K 7361-1 being 46.5% or higher, the three-point bending strength being 700 MPa or higher, and a ratio of an integrated value for the total light transmittance to an integrated value for the parallel light transmittance of a 1-mm thick sample measured at the measurement wavelength ranging from 400 to 700 nm being 1.3% or less.

A paramagnetic garnet-type transparent ceramic characterized by being a sintered body of a terbium-containing composite oxide represented by formula (1) in which the linear transmittance at a wavelength of 1,064 nm at an optical path length of 15 mm is 83% or higher.
(Tb.sub.1-x-ySc.sub.xCe.sub.y).sub.3(Al.sub.1-zSc.sub.z).sub.5O.sub.12  (1)
(In the formula, 0<x<0.08, 0≤y≤0.01, 0.004<z<0.16.)

An exemplary embodiment of the present disclosure provides a method for manufacturing a transparent ceramic material. The method comprises providing a compact comprising a metal oxide and, during sintering, exposing the compact to a vapor comprising one of or both fluorine ions and lithium ions to form a transparent ceramic material comprising at least 90% of a theoretical transparency.

The present invention aims to provide a scintillator which has a short fluorescence decay time, whose fluorescence intensity after a period of time following radiation irradiation is low, and which shows largely improved light-transmittance. A scintillator represented by the following General Formula (1), the scintillator including Zr, having a Zr content of not less than 1500 ppm by mass therein, and being a block of a sintered body. Q.sub.xM.sub.yO.sub.3z:A . . . (1) (wherein in General Formula (1), Q includes at least one or more kinds of divalent metallic elements; M includes at least Hf; and x, y, and z independently satisfy 0.5≤x≤1.5, 0.5≤y≤1.5, and 0.7≤z≤1.5, respectively).

A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

The present disclosure relates to a dental cutting zirconia blank having high relative density for preparing a dental restoration. More specifically, the present disclosure relates to a dental cutting zirconia blank which consists of a zirconia ceramics used for the cutting with the CAD/CAM system in the dental field, a semi-sinter zirconia blank (pre-sintered body) of which has high relative density, and which can provide a prosthesis device having high aesthetics after sintering. There is provided a dental cutting zirconia blank wherein the dental cutting zirconia blank has at least one layer consisting of zirconia powder containing 4 to 15 mol % of yttria or erbium oxide as a stabilizer, a relationship among pre-sintering density, final-sintering density and relative density satisfies the following relation:
54≤Relative density(%)={(Pre-sintering density)/(Perfect-sintering density)}×100≤70.

A zirconia sintered body comprises zirconia and multiple different areas, including at least one upper area and at least one lower area having a different chemical composition and a different strength. The sintered body has a translucency and a strength with an inverse relationship. The translucency increases in one direction across the multiple different areas and the strength decreasing in the same direction across the multiple different areas. At least part of the sintered body has a total light transmittance of at least 35% and less than 53% to light with a wavelength at least at a point between 400 nm and 600 nm, and at least 51% and less than 57% to light with a wavelength at least at a point between 600 nm and 800 nm, at a thickness of 0.6 mm. At least a part of the sintered body has a strength of at least 925 Mpa.

A three-dimensional shaped article production method for producing a three-dimensional shaped article by stacking layers to form a stacked body includes a first layer formation step of forming a first layer on a support by supplying a first composition containing first particles and a binder, a second layer formation step of forming a second layer composed of one layer or a plurality of layers on the first layer by supplying a second composition containing second particles and a binder, and a separation step of separating the second layer from the support through the first layer, wherein after the separation step, a sintering step of sintering the second layer is performed.