A bimodal polymer composition comprising a lower molecular weight homopolymer and a higher molecular weight copolymer wherein the bimodal polymer composition has a density of from about 0.930 gram per cubic centimeter (g/cc) to about 0.970 g/cc, a ratio of high load melt index:melt index of from about 10 to about 150 and an Environmental Stress Crack Resistance (ESCR) of from about 25 hours to about 300 hours when measured in accordance with ASTM D1693 or ASTM D2561. A chromium-catalyzed polymer composition comprising (i) a lower molecular weight homopolymer and (ii) a higher molecular weight copolymer, wherein the bimodal polymer composition has an Environmental Stress Crack Resistance (ESCR) of from about 25 hours to about 300 hours when measured in accordance with ASTM D1693 or ASTM D2561.

In some embodiments, a polyethylene composition includes has 80 wt % to 99.9 wt % ethylene content and 20 wt % to 0.1 wt % a C3 to C40 α-olefin comonomer content, based on ethylene content plus comonomer content. The composition has a Mw/Mn of 15 to 45, a density of 0.93 g/cm.sup.3 to 0.97 g/cm.sup.3, a complex viscosity (at 628 rad/s, 190° C.) of 600 Pa*s or less, a zero shear viscosity by Cross model of 150,000 Pa*s to 350,000 Pa*s. It may also have a V index of less than 7. In some embodiments, an article includes the polyethylene composition. In some embodiments, the article is a pipe.

In some embodiments, a polyethylene composition includes has 80 wt % to 99.9 wt % ethylene content and 20 wt % to 0.1 wt % a C3 to C40 α-olefin comonomer content, based on ethylene content plus comonomer content. The composition has a Mw/Mn of 15 to 45, a density of 0.93 g/cm.sup.3 to 0.97 g/cm.sup.3, a complex viscosity (at 628 rad/s, 190° C.) of 600 Pa*s or less, a zero shear viscosity by Cross model of 150,000 Pa*s to 350,000 Pa*s. It may also have a V index of less than 7. In some embodiments, an article includes the polyethylene composition. In some embodiments, the article is a pipe.

A method for evaluating long-term durability of a resin for piping is provided. Unlike the conventional FNCT evaluation method requiring a long period of time, the method disclosed herein is capable of predicting long-term durability of a resin for piping in a short time, by a simple calculation using a content of tie molecules, an entanglement molecular weight (M.sub.e) and a content of ultrahigh molecular weight components. In addition, the olefinic polymer is configured to have a predetermined relationship in relation to the content of tie molecules, the entanglement molecular weight (M.sub.e) and the content of ultrahigh molecular weight components, whereby the polymer of the present application can be used in the manufacture of a heating pipe requiring excellent long-term durability.

A method for evaluating long-term durability of a resin for piping is provided. Unlike the conventional FNCT evaluation method requiring a long period of time, the method disclosed herein is capable of predicting long-term durability of a resin for piping in a short time, by a simple calculation using a content of tie molecules, an entanglement molecular weight (M.sub.e) and a content of ultrahigh molecular weight components. In addition, the olefinic polymer is configured to have a predetermined relationship in relation to the content of tie molecules, the entanglement molecular weight (M.sub.e) and the content of ultrahigh molecular weight components, whereby the polymer of the present application can be used in the manufacture of a heating pipe requiring excellent long-term durability.

The present disclosure relates to a polyethylene composition capable of producing a molded product having excellent environmental stress crack resistance, and improving total volatile organic compound (TVOC) properties that can be generated by a low molecular weight polymer, and a method for preparing the same.

The present disclosure relates to a polyethylene composition capable of producing a molded product having excellent environmental stress crack resistance, and improving total volatile organic compound (TVOC) properties that can be generated by a low molecular weight polymer, and a method for preparing the same.

An interpolymer product comprising: a first ethylene interpolymer comprising ethylene and an α-olefin having a weight-average molecular weight (M.sub.w) of greater than 250,000 and a density of less than 0.930 g/cm.sup.3, and a second ethylene interpolymer comprising ethylene and an α-olefin wherein the second ethylene interpolymer comprises a M.sub.w of less than 70,000 and a density of greater than 0.930 g/cm.sup.3; and wherein the interpolymer product comprises an environmental stress crack resistance (ESCR), measured according to ASTM D1693, Condition B, 10% IGEPAL CO-630, of greater than 90 hours. The interpolymer product may be manufactured in a continuous solution polymerization process utilizing at least two reactors employing at least one single site catalyst formulation and at least one heterogeneous catalyst formulation.

An interpolymer product comprising: a first ethylene interpolymer comprising ethylene and an α-olefin having a weight-average molecular weight (M.sub.w) of greater than 250,000 and a density of less than 0.930 g/cm.sup.3, and a second ethylene interpolymer comprising ethylene and an α-olefin wherein the second ethylene interpolymer comprises a M.sub.w of less than 70,000 and a density of greater than 0.930 g/cm.sup.3; and wherein the interpolymer product comprises an environmental stress crack resistance (ESCR), measured according to ASTM D1693, Condition B, 10% IGEPAL CO-630, of greater than 90 hours. The interpolymer product may be manufactured in a continuous solution polymerization process utilizing at least two reactors employing at least one single site catalyst formulation and at least one heterogeneous catalyst formulation.

What is disclosed is a Ziegler-Natta catalyzed ethylene and alpha-olefin LLDPE copolymer having a unique composition distribution and long chain-branching. The polymers of the present invention inherently exhibit outstanding melt strength with great bubble stability, sufficient flexibility, excellent gel performance, as well as desirable mechanical properties such as balanced toughness and stiffness, which are desirable properties for thick gauge film applications. Specifically, the polymers of the present invention.