Supported chromium catalysts containing a solid oxide and 0.1 to 15 wt. % chromium, in which the solid oxide or the supported chromium catalyst has a particle size span from 0.5 to 1.4, less than 3 wt. % has a particle size greater than 100 μm, and less than 10 wt. % has a particle size less than 10 μm, can be contacted with an olefin monomer in a loop slurry reactor to produce an olefin polymer. Representative ethylene-based polymers produced using the chromium catalysts have a HLMI of 4 to 70 g/10 min, a density from 0.93 to 0.96 g/cm.sup.3, from 150 to 680 ppm solid oxide (such as silica), from 1.5 to 6.8 ppm chromium, and a film gel count of less than 15 catalyst particle gels per ft.sup.2 of 25 micron thick film and/or a gel count of less than or equal to 50 catalyst particles of greater than 100 μm per five grams of the ethylene polymer.

Supported chromium catalysts containing a solid oxide and 0.1 to 15 wt. % chromium, in which the solid oxide or the supported chromium catalyst has a particle size span from 0.5 to 1.4, less than 3 wt. % has a particle size greater than 100 μm, and less than 10 wt. % has a particle size less than 10 μm, can be contacted with an olefin monomer in a loop slurry reactor to produce an olefin polymer. Representative ethylene-based polymers produced using the chromium catalysts have a HLMI of 4 to 70 g/10 min, a density from 0.93 to 0.96 g/cm.sup.3, from 150 to 680 ppm solid oxide (such as silica), from 1.5 to 6.8 ppm chromium, and a film gel count of less than 15 catalyst particle gels per ft.sup.2 of 25 micron thick film and/or a gel count of less than or equal to 50 catalyst particles of greater than 100 μm per five grams of the ethylene polymer.

Supported chromium catalysts containing a solid oxide and 0.1 to 15 wt. % chromium, in which the solid oxide or the supported chromium catalyst has a particle size span from 0.5 to 1.4, less than 3 wt. % has a particle size greater than 100 μm, and less than 10 wt. % has a particle size less than 10 μm, can be contacted with an olefin monomer in a loop slurry reactor to produce an olefin polymer. Representative ethylene-based polymers produced using the chromium catalysts have a HLMI of 4 to 70 g/10 min, a density from 0.93 to 0.96 g/cm.sup.3, from 150 to 680 ppm solid oxide (such as silica), from 1.5 to 6.8 ppm chromium, and a film gel count of less than 15 catalyst particle gels per ft.sup.2 of 25 micron thick film and/or a gel count of less than or equal to 50 catalyst particles of greater than 100 μm per five grams of the ethylene polymer.

Supported chromium catalysts containing a solid oxide and 0.1 to 15 wt. % chromium, in which the solid oxide or the supported chromium catalyst has a particle size span from 0.5 to 1.4, less than 3 wt. % has a particle size greater than 100 μm, and less than 10 wt. % has a particle size less than 10 μm, can be contacted with an olefin monomer in a loop slurry reactor to produce an olefin polymer. Representative ethylene-based polymers produced using the chromium catalysts have a HLMI of 4 to 70 g/10 min, a density from 0.93 to 0.96 g/cm.sup.3, from 150 to 680 ppm solid oxide (such as silica), from 1.5 to 6.8 ppm chromium, and a film gel count of less than 15 catalyst particle gels per ft.sup.2 of 25 micron thick film and/or a gel count of less than or equal to 50 catalyst particles of greater than 100 μm per five grams of the ethylene polymer.

The present invention relates to a process for the preparation of a polyethylene wax, the process comprising the steps of providing a catalyst solution, wherein the catalyst solution comprises at least one activating compound, an alkylaluminoxane and a me-tallocene complex, wherein the molar ratio of the activating compound to aluminum comprised in the alkylaluminoxane is from 0.0005 to 0.20; and polymerizing ethylene, by contacting the ethylene and the catalyst solution.

The present invention relates to a process for the preparation of a polyethylene wax, the process comprising the steps of providing a catalyst solution, wherein the catalyst solution comprises at least one activating compound, an alkylaluminoxane and a me-tallocene complex, wherein the molar ratio of the activating compound to aluminum comprised in the alkylaluminoxane is from 0.0005 to 0.20; and polymerizing ethylene, by contacting the ethylene and the catalyst solution.

Supported chromium catalysts containing a solid oxide and 0.1 to 15 wt. % chromium, in which the solid oxide or the supported chromium catalyst has a particle size span from 0.5 to 1.4, less than 3 wt. % has a particle size greater than 100 ?m, and less than 10 wt. % has a particle size less than 10 ?m, can be contacted with an olefin monomer in a loop slurry reactor to produce an olefin polymer. Representative ethylene-based polymers produced using the chromium catalysts have a HLMI of 4 to 70 g/10 min, a density from 0.93 to 0.96 g/cm.sup.3, from 150 to 680 ppm solid oxide (such as silica), from 1.5 to 6.8 ppm chromium, and a film gel count of less than 15 catalyst particle gels per ft.sup.2 of 25 micron thick film and/or a gel count of less than or equal to 50 catalyst particles of greater than 100 ?m per five grams of the ethylene polymer.

Supported chromium catalysts containing a solid oxide and 0.1 to 15 wt. % chromium, in which the solid oxide or the supported chromium catalyst has a particle size span from 0.5 to 1.4, less than 3 wt. % has a particle size greater than 100 ?m, and less than 10 wt. % has a particle size less than 10 ?m, can be contacted with an olefin monomer in a loop slurry reactor to produce an olefin polymer. Representative ethylene-based polymers produced using the chromium catalysts have a HLMI of 4 to 70 g/10 min, a density from 0.93 to 0.96 g/cm.sup.3, from 150 to 680 ppm solid oxide (such as silica), from 1.5 to 6.8 ppm chromium, and a film gel count of less than 15 catalyst particle gels per ft.sup.2 of 25 micron thick film and/or a gel count of less than or equal to 50 catalyst particles of greater than 100 ?m per five grams of the ethylene polymer.

A process may include contacting ethylene monomer with Ziegler-Natta catalyst to form polyethylene. The Ziegler-Natta catalyst may be formed by contacting an alkyl magnesium compound with an alcohol and a metal reagent to form a blend, and contacting the blend with a first agent to form a solution of reaction product A. The solution of reaction product A may be contacted with a second agent to form a solid reaction product B, and the solid reaction product B may be contacted with a third agent to form a solid reaction product C. The solid reaction product C may be contacted with a fourth agent to form a solid reaction product D, and the solid reaction product D may be contacted with a fifth agent to form a catalyst component.

A process may include contacting ethylene monomer with Ziegler-Natta catalyst to form polyethylene. The Ziegler-Natta catalyst may be formed by contacting an alkyl magnesium compound with an alcohol and a metal reagent to form a blend, and contacting the blend with a first agent to form a solution of reaction product A. The solution of reaction product A may be contacted with a second agent to form a solid reaction product B, and the solid reaction product B may be contacted with a third agent to form a solid reaction product C. The solid reaction product C may be contacted with a fourth agent to form a solid reaction product D, and the solid reaction product D may be contacted with a fifth agent to form a catalyst component.