A method may include introducing a resin treatment fluid into a wellbore, the resin treatment fluid including a resin, a hardening agent, and a neutron contrasting agent; and allowing the resin treatment fluid to set to form a hardened mass.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350° C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350° C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

The present disclosure concerns a cement dispersant for cement compositions wherein the cement dispersant is a polynaphthalene sulfonate salt having a weight average molecular weight of from 2500 g/mol to 3000 g/mol. The cement compositions are of from 10 weight percent to 70 weight percent of a cement precursor based on the total weight of the cement composition, from 5 weight percent to 70 weight percent water based on the total weight of the cement composition, and from 0.001 percent by weight of cement (BWOC) to 1.0 percent BWOC the cement dispersant. The cement dispersant provides improved rheological properties, allowing for good cement dispensing and increased presence of weighting agents.

A method of pumping a fluid and reactive solid into a mineral formation includes the fluid reacting with the mineral formation to produce a nucleation product. The method may be used in shale formations to seal fissures and prevent leakage. The fluid used in this method may comprise CO.sub.2 and the nucleation products may be the products of carbonation reactions. A cement formed by reacting CO.sub.2 with a reactive solid under deep geological formation conditions is also disclosed.

A method of cementing may include preparing a cement composition comprising: cementitious components comprising: a cement; a supplementary cementitious material; and nanoparticulate boehmite; and water; and introducing the cement composition into a subterranean formation.

A method of cementing may include preparing a cement composition comprising: cementitious components comprising: a cement; a supplementary cementitious material; and nanoparticulate boehmite; and water; and introducing the cement composition into a subterranean formation.

The effectiveness of expansive cement systems may be diluted when, during a well cementing operation, commingling takes place between the cement slurry and a spacer fluid, a drilling fluid, or both. Incorporating expansive agents in the spacer fluid or drilling fluid may reduce or negate the loss of expansion at the cement slurry/spacer interface or the cement slurry/drilling fluid interface, thereby promoting zonal isolation throughout the cemented interval.

The effectiveness of expansive cement systems may be diluted when, during a well cementing operation, commingling takes place between the cement slurry and a spacer fluid, a drilling fluid, or both. Incorporating expansive agents in the spacer fluid or drilling fluid may reduce or negate the loss of expansion at the cement slurry/spacer interface or the cement slurry/drilling fluid interface, thereby promoting zonal isolation throughout the cemented interval.

The effectiveness of expansive cement systems may be diluted when, during a well cementing operation, commingling takes place between the cement slurry and a spacer fluid, a drilling fluid, or both. Incorporating expansive agents in the spacer fluid or drilling fluid may reduce or negate the loss of expansion at the cement slurry/spacer interface or the cement slurry/drilling fluid interface, thereby promoting zonal isolation throughout the cemented interval.