An aspect of the present invention relates to a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4≤0.4*Cr+Si≤3.2 (wherein element symbols denote measurements of respective element contents by weight %).

An aspect of the present invention relates to a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4≤0.4*Cr+Si≤3.2 (wherein element symbols denote measurements of respective element contents by weight %).

This steel sheet has a specific chemical composition, the tensile strength is 1300 MPa or more, the ratio (R/t) of the limit bend radius to the sheet thickness is less than 3.5, when a depth position of 30 μm from the surface in the sheet thickness direction is defined as a position A and a depth position of ¼ of the sheet thickness from the surface in the sheet thickness direction is defined as a position B, the number density of AIN at the position A is 3000 pieces/mm.sup.2 or more and 6000 pieces/mm.sup.2 or less, a metallographic structure at the position B includes 90% or more of martensite by volume percentage, and the hardness at the position A is 1.20 times or higher than the hardness at the position B.

This steel sheet has a specific chemical composition, the tensile strength is 1300 MPa or more, the ratio (R/t) of the limit bend radius to the sheet thickness is less than 3.5, when a depth position of 30 μm from the surface in the sheet thickness direction is defined as a position A and a depth position of ¼ of the sheet thickness from the surface in the sheet thickness direction is defined as a position B, the number density of AIN at the position A is 3000 pieces/mm.sup.2 or more and 6000 pieces/mm.sup.2 or less, a metallographic structure at the position B includes 90% or more of martensite by volume percentage, and the hardness at the position A is 1.20 times or higher than the hardness at the position B.

Provided according to one preferred aspect of the present invention are austenitic steel material having superb abrasion resistance and toughness, and a method for producing the austenite steel material. The austenitic steel material having superb abrasion resistance and toughness according to one preferred aspect of the present invention comprises, in wt %, 0.6-1.9% carbon (C); 12-22% manganese (Mn); 5% or lower (excluding 0%) chromium (Cr); 5% or lower (excluding 0%) copper (Cu); 0.5% or lower (excluding 0%) aluminum (Al); 1.0% or lower (excluding 0%) silicon (Si); 0.1% or lower (including 0%) phosphorous (P); 0.02% or lower (including 0%) sulfur (S); and the rest in Fe and unavoidable impurities, and has the microstructure comprising, by surface area fraction, 97% or higher (including 100%) austenite and 3% or lower (including 0%) carbide.

Provided according to one preferred aspect of the present invention are austenitic steel material having superb abrasion resistance and toughness, and a method for producing the austenite steel material. The austenitic steel material having superb abrasion resistance and toughness according to one preferred aspect of the present invention comprises, in wt %, 0.6-1.9% carbon (C); 12-22% manganese (Mn); 5% or lower (excluding 0%) chromium (Cr); 5% or lower (excluding 0%) copper (Cu); 0.5% or lower (excluding 0%) aluminum (Al); 1.0% or lower (excluding 0%) silicon (Si); 0.1% or lower (including 0%) phosphorous (P); 0.02% or lower (including 0%) sulfur (S); and the rest in Fe and unavoidable impurities, and has the microstructure comprising, by surface area fraction, 97% or higher (including 100%) austenite and 3% or lower (including 0%) carbide.

Provided is a rail that is effective in improving wear resistance and rolling contact fatigue (RCF) resistance. The rail has a metallic structure including a pearlitic structure and a structure other than the pearlitic structure in a surface layer from a surface of a rail head to a depth of at least 0.5 mm, where the pearlitic structure has Vickers hardness of 420 HV or more and 520 HV or less, and the structure other than the pearlitic structure has Vickers hardness of 350 HV or more and 420 HV or less.

There is provided a hot-stamped member or a steel sheet for hot stamping having a chemical composition including, in mass %, C: 0.25% or more and 0.55% or less, Si: 0.001% or more and 2.0% or less, Mn: 0.3% or more and 3.0% or less, P: 0.02% or less, S: 0.003% or less, Al: 0.005% or more and 1.0% or less, Cr: 0% or more and 1.0% or less, Mo: 0% or more and 1.0% or less, N: 0.02% or less, Ca: 0% or more and 0.0010% or less, B: 0.0005% or more and 0.01% or less, one or two or more selected from the group consisting of Ti: 0.005% or more and 0.5% or less, Nb: 0.005% or more and 0.5% or less, V: 0.005% or more and 0.5% or less, and Zr: 0.005% or more and 0.5% or less, and Ni+Cu+Sn: 0% or more and 2% or less, and a remainder consisting of Fe and impurities.

Provided is a steel sheet and a method for manufacturing same, the steel sheet which can be used for automobile parts and the like, having excellent bending workability, and excellent balance of strength and ductility and of strength and hole expansibility.

Provided is a steel sheet and a method for manufacturing same, the steel sheet which can be used for automobile parts and the like, having excellent bending workability, and excellent balance of strength and ductility and of strength and hole expansibility.