A balance for timepieces includes a rim, a hub, and at least one arm connecting the hub to the rim. At least one portion of the balance is made of an at least partially amorphous metal alloy. The at least partially amorphous metal alloy is based on an element chosen from the group consisting of platinum, zirconium and titanium, and has a coefficient of thermal expansion comprised between 7 ppm/° C. and 12 ppm/° C. The balance can be manufactured by moulding. A resonator can include such a balance and a monocrystalline quartz balance spring.

A spiral spring intended to equip a balance of a horological movement, wherein the spiral spring is made of an alloy consisting of Nb, Ti and at least one element selected from Zr and Hf, optionally at least one element selected from W and Mo, possible traces of other elements selected from O, H, Ta, C, Fe, N, Ni, Si, Cu, Al, with the following weight percentages: a content of Nb comprised between 40 and 84%, a total content of Ti, Zr and Hf comprised between 16 and 55%, a content for W and Mo respectively comprised between 0 and 2.5%, a content for each of said elements selected from O, H, Ta, C, Fe, N, Ni, Si, Cu, Al comprised between 0 and 1600 ppm with the sum of said traces less than or equal to 0.3% by weight. The method for manufacturing the spiral spring is also disclosed.

A spiral spring is configured to equip a balance of a horological movement. The spiral spring is made of an alloy consisting of: Nb, Ti and at least one element selected from V and Ta, optionally at least one element selected from Zr and Hf, optionally at least one element selected from W and Mo, possible traces of other elements selected from O, H, C, Fe, N, Ni, Si, Cu, Al, with the following weight percentages: a total content of Nb, V and Ta comprised between 40 and 85%, a total content of Ti, Zr and Hf comprised between 15 and 55%, a content for W and Mo respectively comprised between 0 and 2.5%, a content for each of the elements selected from 0, H, C, Fe, N, Ni, Si, Cu, Al between 0 and 1600 ppm with the sum of the traces less than or equal to 0.3% by weight.

A process for producing a metal alloy balance wheel by molding includes a) making a mold in the negative shape of the balance wheel; b) obtaining a metal alloy that has a thermal expansion coefficient of less than 25 ppm/° C. and is able to be in an at least partly amorphous state when it is heated to a temperature between its glass transition temperature and its crystallization temperature; c) putting the metal alloy into the mold, the metal alloy being heated to a temperature between its glass transition temperature and its crystallization temperature so as to be hot-molded and to form a balance wheel; d) cooling the metal alloy to obtain a balance wheel made of the metal alloy; and e) releasing the balance wheel obtained in step d) from its mold. The process also includes a step for over-molding flexible centering components in the hub.

A process for fabricating a hairspring having a final stiffness includes the steps of fabricating a hairspring to thickened dimensions, and determining the initial stiffness of the hairspring formed in order to remove the volume of material to obtain the hairspring having the dimensions required for said final stiffness.

A balance spring for a balance with a blank containing: niobium: the remainder to 100 wt %, titanium: between 40 and 60 wt %, traces of elements selected from the group formed of O, H, C, Fe, Ta, N, Ni, Si, Cu, Al, between 0 and 1600 ppm by weight individually, and less than 0.3 wt % combined, a step of β-quenching the blank with a given diameter, such that the titanium of the alloy is essentially in solid solution form with β-phase niobium, the α-phase titanium content being less than or equal to 5% by volume, at least one deformation step of the alloy alternated with at least one heat treatment step such that the niobium and titanium alloy obtained has an elastic limit higher than or equal to 600 MPa and a modulus of elasticity lower than or equal to 100 GPa, a winding step to form the balance spring being performed prior to the final heat treatment step, prior to the deformation step, a step of depositing, on the alloy blank, a surface layer of a ductile material such as copper, the surface layer of ductile material being retained on the balance spring, the thermoelastic coefficient of the niobium and titanium alloy being adapted accordingly.

A balance for timepieces includes a rim, a hub, and at least one arm connecting the hub to the rim. At least one portion of the balance is made of an at least partially amorphous metal alloy. The at least partially amorphous metal alloy is based on an element chosen from the group consisting of platinum, zirconium and titanium, and has a coefficient of thermal expansion comprised between 7 ppm/° C. and 12 ppm/° C. The balance can be manufactured by moulding. A resonator can include such a balance and a monocrystalline quartz balance spring.

A balance-spring intended to equip a balance of an horological movement, comprising a core made of Nb—Ti made from an alloy consisting of: niobium: balance to 100% by weight, titanium: between 5 and 95% by weight, traces of elements chosen from the group consisting of O, H, C, Fe, Ta, N, Ni, Si, Cu, Al, each of said elements being present in a quantity between 0 and 1600 ppm by weight, the total quantity formed by all of said elements being between 0% and 0.3% by weight, wherein the core made of Nb—Ti is coated with a layer of niobium, said layer of niobium having a thickness between 20 nm and 10 μm.

A bimetallic device, the difference in expansion coefficient of which is between 10 and 30 10.sup.−6 K.sup.−1, for providing a resonator with thermal compensation via the balance wheel.

A method for manufacturing a micromechanical component made of a first material, the first material being a material that can become at least partially amorphous, the method including: a) providing a mold made of a second material, the mold including a cavity forming the negative of the micromechanical component; b) providing the first material and forming the first material in the cavity of the mold, the first material having undergone, at a latest at a time of the forming, treatment allowing the first material to become at least partially amorphous; c) separating the micromechanical component thus formed from the mold.