The present disclosure aims to provide a bonded magnet having good magnetic properties and a method of preparing the bonded magnet. The present disclosure provides a method of preparing a bonded magnet, including: a first compression step of compressing a magnetic powder having an average particle size of 10 μm or less while magnetically orienting it to obtain a first molded article; a second compression step of bringing the first molded article into contact with a thermosetting resin having a viscosity of 200 mPa.Math.s or less, followed by compression to obtain a second molded article; and a heat treatment step of heat treating the second molded article.

The present disclosure aims to provide a bonded magnet having good magnetic properties and a method of preparing the bonded magnet. The present disclosure provides a method of preparing a bonded magnet, including: a first compression step of compressing a magnetic powder having an average particle size of 10 μm or less while magnetically orienting it to obtain a first molded article; a second compression step of bringing the first molded article into contact with a thermosetting resin having a viscosity of 200 mPa.Math.s or less, followed by compression to obtain a second molded article; and a heat treatment step of heat treating the second molded article.

A method of producing a SmFeN-based anisotropic magnetic powder is provided, the method including preparing a SmFeN-based anisotropic magnetic powder before dispersing comprising Sm, Fe, W, and N, and dispersing the SmFeN-based anisotropic magnetic powder before dispersing using a resin-coated metal media or a resin-coated ceramic media to obtain a SmFeN-based anisotropic magnetic powder. Also provided is a SmFeN-based anisotropic magnetic powder comprising Sm, Fe, W, and N and having an average particle size of less than 2.5 μm, a residual magnetization σr of not less than 130 emu/g, and an oxygen content of not higher than 0.75% by mass.

A method of producing a SmFeN-based anisotropic magnetic powder is provided, the method including preparing a SmFeN-based anisotropic magnetic powder before dispersing comprising Sm, Fe, W, and N, and dispersing the SmFeN-based anisotropic magnetic powder before dispersing using a resin-coated metal media or a resin-coated ceramic media to obtain a SmFeN-based anisotropic magnetic powder. Also provided is a SmFeN-based anisotropic magnetic powder comprising Sm, Fe, W, and N and having an average particle size of less than 2.5 μm, a residual magnetization σr of not less than 130 emu/g, and an oxygen content of not higher than 0.75% by mass.

A method of producing a SmFeN-based rare earth magnet, the method including: dispersing a SmFeN-based anisotropic magnetic powder comprising Sm, Fe, and N using a resin-coated metal media or a resin-coated ceramic media to obtain a dispersed SmFeN-based anisotropic magnetic powder; mixing the dispersed SmFeN-based anisotropic magnetic powder with a modifier powder to obtain a powder mixture; compacting the powder mixture in a magnetic field to obtain a magnetic field compact; pressure-sintering the magnetic field compact to obtain a sintered compact; and heat treating the sintered compact.

The present invention discloses a high-resistivity sintered samarium-cobalt magnet and a preparation method thereof. According to the present invention, considering the specialty of sintered samarium-cobalt magnetic powder, fluoride or oxide is firstly prepared into nano-powder using high-energy ball milling, and the samarium-cobalt magnetic powder is prepared separately by rolling ball milling or high-speed jet milling, and then a certain electric field is applied in a fluoride suspension to drive the fluoride nano-powder to evenly cover a surface of the samarium-cobalt magnetic powder. The present invention breaks through the technical bottleneck that fluoride/oxide can improve the resistivity of a samarium-cobalt magnet but result in deterioration of the magnetic properties.

The present invention discloses a high-resistivity sintered samarium-cobalt magnet and a preparation method thereof. According to the present invention, considering the specialty of sintered samarium-cobalt magnetic powder, fluoride or oxide is firstly prepared into nano-powder using high-energy ball milling, and the samarium-cobalt magnetic powder is prepared separately by rolling ball milling or high-speed jet milling, and then a certain electric field is applied in a fluoride suspension to drive the fluoride nano-powder to evenly cover a surface of the samarium-cobalt magnetic powder. The present invention breaks through the technical bottleneck that fluoride/oxide can improve the resistivity of a samarium-cobalt magnet but result in deterioration of the magnetic properties.

A sintered magnet contains Sm—Fe—N-based crystal grains and has high coercivity; and a magnetic powder is capable of forming a sintered magnet without lowering the coercivity even if heat is generated in association with the sintering. A sintered magnet comprises a crystal phase composed of a plurality of Sm—Fe—N-based crystal grains and a nonmagnetic metal phase present between the Sm—Fe—N crystal grains adjacent to each other, wherein a ratio of Fe peak intensity I.sub.Fe to SmFeN peak intensity I.sub.SmFeN measured by an X-ray diffraction method is 0.2 or less. A magnetic powder comprises Sm—Fe—N-based crystal particles and a nonmagnetic metal layer covering surfaces of the Sm—Fe—N crystal particles.

A sintered magnet contains Sm—Fe—N-based crystal grains and has high coercivity; and a magnetic powder is capable of forming a sintered magnet without lowering the coercivity even if heat is generated in association with the sintering. A sintered magnet comprises a crystal phase composed of a plurality of Sm—Fe—N-based crystal grains and a nonmagnetic metal phase present between the Sm—Fe—N crystal grains adjacent to each other, wherein a ratio of Fe peak intensity I.sub.Fe to SmFeN peak intensity I.sub.SmFeN measured by an X-ray diffraction method is 0.2 or less. A magnetic powder comprises Sm—Fe—N-based crystal particles and a nonmagnetic metal layer covering surfaces of the Sm—Fe—N crystal particles.

The present disclosure discloses an yttrium (Y)-added rare-earth permanent magnetic material and a preparation method thereof. A chemical formula of the material expressed in atomic percentage is (YxRE1-x)aFebalMbNc, wherein 0.05≤x≤0.4, 7≤a≤13, 0≤b≤3, 5≤c≤20, and the balance is Fe, namely, bal=100-a-b-c; RE represents a rare-earth element Sm, or a combination of the rare-earth element Sm and any one or more elements of Zr, Nd and Pr; M represents Co and/or Nb; and N represents nitrogen. In the preparation method, the rare-earth element Y is utilized to replace the element Sm of a samarium-iron-nitrogen material. By regulating a ratio of the element Sm to the element Y, viscosity of an alloy liquid can be reduced, and an amorphous forming ability of the material is enhanced.