Provided is a ceramic coating intended to be applied on a metal support and having the form of at least a continuous film having a thickness between 2 and 100 μm, this coating comprising a matrix including at least a metal polyalkoxide and wherein are dispersed particles whereof the diameter ranges between 0.01 and 50 μm, said particles being from a material having a thermal conductivity equal to or higher than 10 W.Math.m.sup.−1.Math.K.sup.−1 and a bulk density of at the most 3.9 g/cm.sup.3. Also provided is an article, for example culinary, comprising such a coating and its method of manufacture.

A strengthened glass container or vessel such as, but not limited to, vials for holding pharmaceutical products or vaccines in a hermetic and/or sterile state. The strengthened glass container undergoes a strengthening process that produces compression at the surface and tension within the container wall. The strengthening process is designed such that the tension within the wall is great enough to ensure catastrophic failure of the container, thus rendering the product unusable, should sterility be compromised by a through-wall crack. The tension is greater than a threshold central tension, above which catastrophic failure of the container is guaranteed, thus eliminating any potential for violation of pharmaceutical integrity.

The embodiments described herein relate to chemically and mechanically durable glass compositions and glass articles formed from the same. In an embodiment the glass composition may include from about 67 mol. % to about 80 mol. % SiO.sub.2; from about 3 mol. % to about 13 mol. % alkaline earth oxide; from about 2 mol. % to about 10 mol. % Al.sub.2O.sub.3; from about 2 mol. % to about 18 mol. % alkali oxide, wherein the alkali oxide comprises non-zero amounts of Na.sub.2O; from 0 mol. % to about 4 mol. % B.sub.2O.sub.3; and from about 0.01 mol. % to about 1 mol. % of a fining agent.

A multi-layered balloon is provided where each layer is formed such that each layer is made from tubing that optimizes the inner wall stretch thus providing maximum balloon strength. The high pressure, multi-layer balloon is provided with layers that allow for slipping, such that the balloon has a very high pressure rating and toughness, yet excellent folding characteristics. Methods for producing such multi-layer balloons using existing balloon forming equipment are also provided. The multi-layer balloons can have alternating structural and lubricating layers, or layers with low-friction surfaces. The multi-layer balloons are preferably manufactured using a variety of methods including nesting, co-extrusion, or a combination of nesting and co-extrusion. The multi-layer balloons have balloon layers having substantially similar, or the same, high degree of biaxial orientation of their polymer molecules such that each balloon layer of the multi-layer balloon will fail at approximately the same applied pressure.

A label for a bottle where the label is comprised of a laminate where an outer layer (3) is a material susceptible to losing opaqueness when made wet, and an inner layer (5) behind this first layer which is a material that is opaque, and such that it will maintain such opaqueness when wet.

A strengthened glass container or vessel such as, but not limited to, vials for holding pharmaceutical products or vaccines in a hermetic and/or sterile state. The strengthened glass container undergoes a strengthening process that produces compression at the surface and tension within the container wall. The strengthening process is designed such that the tension within the wall is great enough to ensure catastrophic failure of the container, thus rendering the product unusable, should sterility be compromised by a through-wall crack. The tension is greater than a threshold central tension, above which catastrophic failure of the container is guaranteed, thus eliminating any potential for violation of pharmaceutical integrity.

A fire insulation precursor material formed of cement, in an amount of between 10-30% w/w; and an aluminium or magnesium hydroxide, huntite or hydromagnesite in an amount of between 60-90% w/w/. A fire insulation material is provided including the previously mentioned precursor material. Further described are methods of forming a fire insulation material and applications for such material in sheaths, duct coatings, cable trays and other elongate components.

A method includes casting a metallic material (56) in a mold (20) containing a core, the core having a substrate (40, 44) coated with a coating (42). A removing of the metallic material from the mold and decoring leaves a casting having a layer formed by the coating. The coating has a ceramic having a porosity in a zone (50) near the substrate less than a porosity in a zone (52) away from the substrate.

A component for a processing chamber includes a ceramic body having at least one surface with a first average surface roughness. The component further includes a conformal protective layer on at least one surface of the ceramic body, wherein the conformal protective layer is a plasma resistant rare earth oxide film having a substantially uniform thickness of less than 300 μm over the at least one surface and having a second average surface roughness that is less than the first average surface roughness.

The embodiments described herein relate to chemically and mechanically durable glass compositions and glass articles formed from the same. In embodiments, the glass composition may include 74-78 mol. % SiO.sub.2; X mol. % Al.sub.2O.sub.3, wherein X is 5-7; alkaline earth oxide comprising MgO and CaO, wherein: CaO is 0.1-1.0 mol. %; MgO is 4-7 mol. %; and a ratio (CaO (mol. %)/(CaO (mol. %)+MgO (mol. %)) is less than or equal to 0.5. The glass composition may further include Y mol. % alkali oxide, wherein the alkali oxide comprises 9-13 mol. % Na.sub.2O and less than or equal to 0.4 mol. % of a fining agent. The glass composition may be free of boron and compounds of boron.