ZR-based amorphous alloy

Abstract

A Zr-based amorphous alloy is provided; the formula of the Zr-based amorphous alloy is (Zr, Hf, Nb).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e, where a, b, c, d, and e are corresponding atomic percent content of elements in the Zr-based amorphous alloy, 45≦a≦65, 15≦b≦40, 0.1≦c≦15, 5≦d≦15, 0.05≦e≦5, a+b+c+d+e≦100, and Re is one of or any combination of elements La, Ce, Po, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Po, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu.

Claims

1. A zirconium-based (Zr-based) amorphous alloy, wherein the Zr-based amorphous alloy comprises one of the following formulas:
Zr.sub.57Cu.sub.29Ni.sub.3Al.sub.9Gd.sub.2,
Zr.sub.63Cu.sub.17.5Ni.sub.10Al.sub.7.5Er.sub.2,
Zr.sub.60.05Cu.sub.25Ni.sub.2Al.sub.12Er.sub.0.5, or
Zr.sub.60Cu.sub.22Ni.sub.5Al.sub.12Dy.sub.1.

2. A zirconium-based (Zr-based) amorphous alloy, wherein the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.46.9Cu.sub.36Ni.sub.8Al.sub.8Er.sub.0.1Y.sub.1,
Zr.sub.54.5Cu.sub.30Ni.sub.5Al.sub.10Tm.sub.0.5, or
Zr.sub.50Cu.sub.35Ni.sub.4Al.sub.10Yb.sub.1.

3. A zirconium-based (Zr-based) amorphous alloy, wherein the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.59.5Hf.sub.2Ni.sub.10Cu.sub.19Al.sub.8Er.sub.0.5Tm.sub.0.5Y.sub.0.5,
Zr.sub.60.5Hf.sub.2Cu.sub.19Ni.sub.10Al.sub.8Er.sub.0.5,
Zr.sub.60.5Ni.sub.2Cu.sub.25Al.sub.12Tm.sub.0.5,
Zr.sub.63Hf.sub.1.5Cu.sub.18Ni.sub.10Al.sub.7Yb.sub.0.5, or
Zr.sub.60.5Hf.sub.2Cu.sub.19Ni.sub.10Al.sub.8Nd.sub.0.5.

4. A zirconium-based (Zr-based) amorphous alloy, wherein the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.53.5Hf.sub.1Cu.sub.30Ni.sub.5Al.sub.10(Y, Er).sub.0.5,
Zr.sub.52.8Hf.sub.2Cu.sub.30Ni.sub.5Al.sub.10La.sub.0.2,
Zr.sub.53Hf.sub.1Ni.sub.5Cu.sub.30Al.sub.10Ce.sub.1, or
Zr.sub.51Hf.sub.1Cu.sub.30Al.sub.10Ni.sub.7Tm.sub.1.

5. A zirconium-based (Zr-based) amorphous alloy, wherein the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.62Nb.sub.1Cu.sub.17Al.sub.8Ni.sub.10Er.sub.2,
Zr.sub.60Cu.sub.18Ni.sub.10Al.sub.8Nb.sub.2Er.sub.2,
Zr.sub.53Nb.sub.1Cu.sub.30Al.sub.10Ni.sub.5Tm.sub.1, or
Zr.sub.59Nb.sub.2Cu.sub.19Al.sub.8Ni.sub.10Yb.sub.2.

6. A method for manufacturing a zirconium-based (Zr-based) amorphous alloy, comprising: melting metal raw materials within a protection atmosphere or vacuum condition, and then performing casting, cooling, and molding to form a Zr-based amorphous alloy, wherein the metal raw materials comprise a purity of less than 99.9%, wherein in the melting process, the raw materials are subjected to a vacuum degree of 6-9×10.sup.−1 Pa and with charged argon protection gas from 0.03 to 0.08 MPa, and wherein the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.57Cu.sub.29Ni.sub.3Al.sub.9Gd.sub.2,
Zr.sub.63Cu.sub.17.5Ni.sub.10Al.sub.7.5Er.sub.2,
Zr.sub.60.5Cu.sub.25Ni.sub.2Al.sub.12Er.sub.0.5, or
Zr.sub.60Cu.sub.22Ni.sub.5Al.sub.12Dy.sub.1.

7. The manufacturing method according to claim 6, wherein in the melting process, a vacuum degree is 8×10.sup.−1 Pa, and a charged argon protection gas is of 0.05 MPa.

8. An electronic device, comprising: a casing and electronic components placed in the casing, wherein the casing comprises a zirconium-based (Zr-based) amorphous alloy, and the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.57Cu.sub.29Ni.sub.3Al.sub.9Gd.sub.2,
Zr.sub.63Cu.sub.17.5Ni.sub.10Al.sub.7.5Er.sub.2,
Zr.sub.60.5Cu.sub.25Ni.sub.2Al.sub.12Er.sub.0.5, or
Zr.sub.60Cu.sub.22Ni.sub.5Al.sub.12Dy.sub.1.

9. An electronic device comprising a Zr-based amorphous alloy that has one of the following formulas:
Zr.sub.46.9Cu.sub.36Ni.sub.8Al.sub.8Er.sub.0.1Y.sub.1,
Zr.sub.54.5Cu.sub.30Ni.sub.5Al.sub.10Tm.sub.0.5, or
Zr.sub.50Cu.sub.35Ni.sub.4Al.sub.10Yb.sub.1.

10. An electronic device comprising: a casing and electronic components placed in the casing, wherein the casing comprises a zirconium-based (Zr-based) amorphous alloy, and the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.59.5Hf.sub.2Ni.sub.10Cu.sub.19Al.sub.8Er.sub.0.5Tm.sub.0.5Y.sub.0.5,
Zr.sub.60.5Hf.sub.2Cu.sub.19Ni.sub.10Al.sub.8Er.sub.0.5,
Zr.sub.60.5Ni.sub.2Cu.sub.25Al.sub.12Tm.sub.0.5,
Zr.sub.63Hf.sub.1.5Cu.sub.18Ni.sub.10Al.sub.7Yb.sub.0.5, or
Zr.sub.60.5Hf.sub.2Cu.sub.19Ni.sub.10Al.sub.8Nd.sub.0.5.

11. An electronic device comprising: a casing and electronic components placed in the casing, wherein the casing comprises a zirconium-based (Zr-based) amorphous alloy, and the Zr-based amorphous alloy has one of the following formulas:
Zr.sub.53.5Hf.sub.1Cu.sub.30Ni.sub.5Al.sub.10(Y, Er).sub.0.5,
Zr.sub.52.8Hf.sub.2Cu.sub.30Ni.sub.5Al.sub.10La.sub.0.2,
Zr.sub.53Hf.sub.1Ni.sub.5Cu.sub.30Al.sub.10Ce.sub.1, or
Zr.sub.51Hf.sub.1Cu.sub.30Al.sub.10Ni.sub.7Tm.sub.1.

12. An electronic device comprising a Zr-based amorphous alloy that has one of the following formulas:
Zr.sub.62Nb.sub.1Cu.sub.17Al.sub.8Ni.sub.10Er.sub.2,
Zr.sub.60Cu.sub.18Ni.sub.10Al.sub.8Nb.sub.2Er.sub.2,
Zr.sub.53Nb.sub.1Cu.sub.30Al.sub.10Ni.sub.5Tm.sub.1, or
Zr.sub.59Nb.sub.2Cu.sub.19Al.sub.8Ni.sub.10Yb.sub.2.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) To illustrate the technical solutions in the embodiments of the present invention more clearly, the following briefly introduces the accompanying drawings required for describing the embodiments. Apparently, the accompanying drawings in the following description show merely some embodiments of the present invention, and a person of ordinary skill in the art may still derive other drawings from these accompanying drawings without creative efforts.

(2) FIG. 1 is an XRD diffraction analysis result diagram of a Zr-based amorphous alloy of two components according to an embodiment of the present invention; and

(3) FIG. 2 is a schematic diagram of an electronic device according to Embodiment 8 of the present invention.

DESCRIPTION OF EMBODIMENTS

(4) The following clearly describes the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Apparently, the described embodiments are merely a part rather than all of the embodiments of the present invention. All other embodiments obtained by a person of ordinary skill in the art based on the embodiments of the present invention without creative efforts shall fall within the protection scope of the present invention.

(5) The present invention provides an easily formable Zr-based amorphous alloy, where the Zr-based amorphous alloy of an amorphous structure maybe subjected to an ordinary copper mold casting method or a conventional parts casting method to generate amorphous bulk materials or parts of an amorphous structure. The Zr-based amorphous alloy includes Zr, Ni, Cu, Al, and one or more elements of rare earth, in which Zr may be partly replaced with Hf and Nb. An atomic percent of each element in the final amorphous alloy fulfills the following general formula:
(Zr,Hf,Nb).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(6) where a, b, c, d, and e are corresponding atomic percent content of elements in the Zr-based amorphous alloy, 45≦a≦65, 15≦b≦40, 0.1≦c≦15, 5≦d≦15, 0.05≦e≦5, a+b+c +d+e≦100, and Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. The Re element group may be obtained by adding misch metal (Misch Metal, expressed by MM in the molecular formula). In some embodiments, the Re is preferably one of or any combination of elements La, Nd, Dy, Er, Tm, and Yb.

(7) For example, in some embodiments, the Zr-based amorphous alloy may include the following components: Zr63Ni10Cu17.5Al7.5Er2, Zr46.9Ni8Cu36Al8Er0.1Y1, Zr54.5Cu30Al10Ni5Tm0.5, Zr63Hf1.5Cu18Ni10Al7Yb0.5, Zr53.5Hf1Cu30Ni5Al10(Y, Er)0.5, Zr60.5Hf2Cu19Ni10Al8Nd0.5, Zr50Cu35Al10Ni4Yb1, Zr47Hf0.5Cu36Ni8Al8Er0.5, and the like.

(8) With the Zr-based amorphous alloy in the foregoing range of components, an alloy ingot of a bar shape, granule shape, or strip shape maybe obtained first through arc melting or induction melting by using low-purity raw materials at a low vacuum degree (lower than 1×10.sup.−2 Pa), and then the alloy ingot is re-melted or cast at a low vacuum degree (lower than 1×10.sup.−2 Pa) to obtain an amorphous bar or amorphous part of a relatively large size.

(9) The present invention provides a method for manufacturing a Zr-based amorphous alloy of the foregoing molecular formula. The method includes: setting corresponding atomic percent content of elements of a Zr-based amorphous alloy of the foregoing (Zr, Hf, Nb).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e in the Zr-based amorphous alloy to 45≦a≦65, 15≦b≦40, 0.1≦c≦15, 5≦d≦15, 0.05≦e≦5, and a+b+c+d+e≦100 respectively; melting such components into a master alloy until they are fully blended homogeneously; and performing casting and cooling for the master alloy to obtain an amorphous bar or a part of another shape that is formed by the Zr-based amorphous alloy. The casting may be pouring, suction casting, spray casting, or die casting. For example, the Zr-based amorphous alloy in the present invention may have any one of the combination of components listed in Table 1:

(10) TABLE-US-00001 TABLE 1 Serial Number Alloy components 1 Zr57Ni3Cu29Al9Gd2 2 Zr63Ni10Cu17.5Al7.5Er2 3 Zr60.5Ni2Cu25Al12Er0.5 4 Zr60Ni5Cu22Al12Dy1 5 Zr54Cu30Al10Ni5Er1 6 Zr46.9Ni8Cu36Al8Er0.1Y1 7 Zr54.5Cu30Al10Ni5Tm0.5 8 Zr50Cu35Al10Ni4Yb1 9 Zr59.5Hf2Ni10Cu19Al8Er0.5Tm0.5Y0.5 10 Zr60.5Hf2Cu19Ni10Al8Er0.5 11 Zr60.5Ni2Cu25Al12Tm0.5 12 Zr63Hf1.5Cu18Ni10Al7Yb0.5 13 Zr60.5Hf2Cu19Ni10Al8Nd0.5 14 Zr51Cu23Al10Ni15Er1 15 Zr53.5Hf1Cu30Ni5Al10(Y,Er)0.5 16 Zr52.8Hf2Cu30Ni5Al10La0.2 17 Zr53Hf1Ni5Cu30Al10Ce1 18 Zr47Hf0.5Cu36Ni8Al8Er0.5 19 Zr51Hf1Cu30Al10Ni7Tm1 20 Zr62Nb1Cu17Al8Ni10Er2 21 Zr64Nb0.5Cu30Ni5Al10Er0.5 22 Zr60Cu18Ni10Al8Nb2Er2 23 Zr53Nb1Cu30Al10Ni5Tm1 24 Zr59Nb2Cu19Al8Ni10Yb2

(11) The method for manufacturing a Zr-based amorphous alloy may include the following steps:

(12) Step 1: Components preparation

(13) Components are prepared within the range of the formula at a specific atomic percent. For example, components are prepared according to each component and a specific atomic percent in Table 1.

(14) In the preparation process, components of the alloy may be prepared according to the components and atomic percents in Table 1 by using materials such as metal rods, blocks, ingots and plates made of elements Zr, Hf, Nb, Ni, Cu, Al, Er, and the like, with a purity of 99.5%.

(15) Step 2: Melting

(16) The prepared raw materials are melted under a protection atmosphere or vacuum condition to achieve homogeneous fusion of all components.

(17) The melting method is not limited. Any melting method is appropriate so long as metals of various components are thoroughly melted and fused. A melting device may also be any type of conventional melting device. In the embodiments of the present invention, the melting device is preferably an arc melting furnace or an induction melting furnace. That is, the prepared raw materials are placed into an arc furnace water-cooled copper crucible or an induction melting crucible and vacuum-pumped to 6-9×10.sup.−1 Pa, and charged with argon of from 0.03 to 0.08 MPa as protection gas. Heating is applied until the materials are melted to form an alloy material whose components are completely homogeneous. The vacuum degree is preferably 8×10.sup.−1 Pa, and the argon protection gas is preferably of 0.05 MPa.

(18) Step 3: Casting and cooling to form an amorphous alloy

(19) The melted alloy material is cast into a mold to cool down, so as to obtain the Zr-based amorphous alloy of the foregoing molecular formula according to the corresponding components.

(20) The detailed steps maybe as follows: Place a specific amount of prepared master alloy into a high-frequency induction furnace graphite crucible; create a vacuum below 0.1 Pa, and charge argon of 0.05 MPa into the vacuum; heat the graphite crucible until the temperature is higher than the melting point of the alloy material so that the alloy material is completely melted down; turn over the graphite crucible and pour the melt into a copper mold to form amorphous rods; or, by using a die-casting method, lead the alloy into a feeding pool of a die-casting device, and use a die-casting mold to form parts of complex dimensions.

(21) The cooling speed of the cooling processing is 1 to 10 K/second, so as to suppress crystallization and form a cylinder-shaped fully amorphous alloy of a 10 mm critical size.

(22) FIG. 1 is an X ray diffraction (XRD) analysis result diagram of two formulas sampled randomly in the table. The XRD spectrum is a typical amorphous diffuse peak, without a diffraction peak of a crystal phase, indicating that the entire cast bar is a single amorphous phase. In the figure, 1# and 2# represent two sampled formulas Zr63Ni10Cu17.5Al7.5Er2 (2#) and Zr54Cu30Al10Ni5Er1 (5#), where the X coordinate represents an XRD diffraction angle (2θ), and the Y coordinate represents relative diffraction intensity.

(23) In the embodiments of the present invention, trace quantities of rare earth elements (0.05-5 atomic percent) are added into an alloy to suppress a crystallization trend and improve melt stability; the rare earth elements can absorb oxygen in the alloy, adjust oxygen content of the alloy, suppress heterogeneous nucleation, avoid crystallization of liquid metal in a cooling process, enhance glass forming ability of the alloy, thereby widening the choice range of raw materials required for manufacturing an amorphous alloy. Moreover, a product of a high glass forming ability can be manufactured without using high-purity raw materials, and we can further reduce process requirements such as vacuum degree, which slashes production costs.

Embodiment 1

(24) Embodiment 1 of the present invention provides a Zr-based amorphous alloy, whose components and atomic percents fulfill the following general formula:
Zr.sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(25) where a, b, c, d, and e are corresponding atomic percent content of elements in the amorphous alloy, and fulfill 56≦a≦65, 15≦b≦32, 2≦c≦15, 7≦d≦13, and 0.05≦e≦2 respectively. Re is one or more elements of rare earth, that is, Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. The Re element group may be obtained by adding mishch metal (Misch Metal).

(26) Component preparation, melting, casting and cooling are performed according to the general formula and the method for manufacturing a Zr-based amorphous alloy, so as to form a Zr-based amorphous alloy expressed by the general formula.

(27) In this embodiment, Re is preferably one of or any combination of Gd, Er, and Dy. For example, the Zr-based amorphous alloy expressed by the general formula specifically includes Zr57Ni3Cu29Al9Gd2, Zr63Ni10Cu17.5Al7.5Er2,Zr60.5Ni2Cu25Al12Er0.5, r60Ni5Cu22Al12Dy1, and the like.

Embodiment 2

(28) Embodiment 2 of the present invention provides a Zr-based amorphous alloy, whose components and atomic percents fulfill the following general formula:
Zr.sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(29) where a, b, c, d, and e are corresponding atomic percent content of elements in the amorphous alloy, and fulfill 45≦a≦55, 25≦b≦38, 2≦c≦15, 7≦d≦13, and 0.05≦e≦2 respectively, and Re is one or more elements of rare earth, that is, Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. The Re element group may be obtained by adding mishch metal (Misch Metal).

(30) Component preparation, melting, casting and cooling are performed according to the general formula and the method for manufacturing a Zr-based amorphous alloy, so as to form a Zr-based amorphous alloy expressed by the general formula.

(31) In this embodiment, preferably, Re is Er and Y, or is one of or any combination of Er, Tm, and Yb. For example, the Zr-based amorphous alloy expressed by the general formula specifically includes Zr54Cu30Al10Ni5Er1, Zr46.9Ni8Cu36Al8Er0.1Y1, Zr54.5Cu30Al10Ni5Tm0.5, Zr50Cu35Al10Ni4Yb1, and the like.

Embodiment 3

(32) Embodiment 3 of the present invention provides a Zr-based amorphous alloy, whose components and atomic percents fulfill the following general formula:
(Zr,Hf).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(33) where a, b, c, d, and e are corresponding atomic percent content of elements in the amorphous alloy, and fulfill 58≦a≦65, 15≦b≦32, 2≦c≦15, 7≦d≦13, and 0.05≦e≦2 respectively, and Re is one or more elements of rare earth, that is, Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. The Re element group may be obtained by adding mishch metal (Misch Metal).

(34) Component preparation, melting, casting and cooling are performed according to the general formula and the method for manufacturing a Zr-based amorphous alloy, so as to form a Zr-based amorphous alloy expressed by the general formula.

(35) In this embodiment, Re is preferably one of or any combination of Er, Yb, Nd, and Tm; the percent content of Hf in (Zr, Hf) is from 0 to 8. For example, the Zr-based amorphous alloy expressed by the general formula specifically includes Zr59.5Hf2Ni10Cu19Al8Er0.5Tm0.5Y0.5, Zr60.5Hf2Cu19Ni10Al8Er0.5, Zr60.5Ni2Cu25Al12Tm0.5, Zr63Hf1.5Cu18Ni10Al7Yb0.5, Zr60.5Hf2Cu19Ni10Al8Nd0.5, and the like.

Embodiment 4

(36) Embodiment 4 of the present invention provides a Zr-based amorphous alloy, whose components and atomic percents fulfill the following general formula:
(Zr,Hf).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(37) where a, b, c, d, and e are corresponding atomic percent content of elements in the amorphous alloy, and fulfill 48≦a≦55, 25≦b≦38, 2≦c≦15, 7≦d≦13, and 0.05≦e≦2 respectively, and Re is one or more elements of rare earth, that is, Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. The Re element group may be obtained by adding mishch metal (Misch Metal).

(38) Component preparation, melting, casting and cooling are performed according to the general formula and the method for manufacturing a Zr-based amorphous alloy, so as to form a Zr-based amorphous alloy expressed by the general formula.

(39) In this embodiment, preferably, Re is Er and Y, or is one of or any combination of Er, La, Tm, and Ce; the percent content of Hf in (Zr, Hf) is from 0 to 8. For example, the Zr-based amorphous alloy expressed by the general formula specifically includes Zr51Cu23Al10Ni15Er1, Zr53.5Hf1Cu30Ni5Al10(Y, Er)0.5, Zr52.8Hf2Cu30Ni5Al10La0.2, Zr53Hf1Ni5Cu30Al10Ce1, Zr47Hf0.5Cu36Ni8Al8Er0.5, Zr51Hf1Cu30Al10Ni7Tm1, and the like.

Embodiment 5

(40) Embodiment 5 of the present invention provides a Zr-based amorphous alloy, whose components and atomic percents fulfill the following general formula:
(Zr,Nb).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(41) where a, b, c, d, and e are corresponding atomic percent content of elements in the amorphous alloy, and fulfill 48≦a≦65, 15≦b≦38, 2≦c≦15, 7≦d≦13, and 0.05≦e≦2 respectively, and Re is one or more elements of rare earth, that is, Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. The Re element group may be obtained by adding mishch metal (Misch Metal).

(42) Component preparation, melting, casting and cooling are performed according to the general formula and the method for manufacturing a Zr-based amorphous alloy, so as to form a Zr-based amorphous alloy expressed by the general formula.

(43) In this embodiment, Re is preferably one of or any combination of Er, Tm, and Yb; the percent content of Nb in (Zr,Nb) is from 0 to 2. For example, the Zr-based amorphous alloy expressed by the general formula specifically includes Zr62Nb1Cu17Al8Ni10Er2, Zr64Nb0.5Cu30Ni5Al10Er0.5, Zr60Cu18Ni10Al8Nb2Er2, Zr53Nb1Cu30Al10Ni5Tm1, Zr59Nb2Cu19Al8Ni10Yb2, and the like.

Embodiment 6

(44) As shown in FIG. 2, Embodiment 9 of the present invention provides an electronic device, where the electronic device includes a casing 100 and electronic components 200 placed in the casing. The casing 100 is made of the foregoing Zr-based amorphous alloy. For example, the Zr-based amorphous alloy used for manufacturing the casing 100 includes Zr, Ni, Cu, Al, and one or more elements of rare earth, in which Zr maybe partly replaced with Hf or/and Nb. An atomic percent of each element in the final amorphous alloy fulfills the following general formula:
(Zr,Hf,Nb).sub.aCu.sub.bNi.sub.cAl.sub.dRe.sub.e,

(45) where a, b, c, d, and e are corresponding atomic percent content of elements in the Zr-based amorphous alloy, 45≦a≦65, 15≦b≦40, 0.1≦c≦15, 5≦d≦15, 0.05≦e≦5, a+b+c+d+e≦100, and Re is one or more elements of rare earth, that is, Re is one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu, or Re is combined with Y and one of or any combination of elements La, Ce, Pm, Ho, Er, Nd, Gd, Dy, Sc, Eu, Tm, Tb, Pr, Sm, Yb, and Lu. In some embodiments, the Re is preferably one of or any combination of elements La, Nd, Dy, Er, Tm, and Yb. The Re element group may be obtained by adding mishch metal (Misch Metal).

(46) The casing 100 may be made of the Zr-based amorphous alloy described in any one of Embodiments 1 to 8.

(47) The casing 100 made of the Zr-based amorphous alloy provides high mechanical performance, such as high rigidity, high intensity, and high resilience, and has merits such as low difficulty in making the Zr-based amorphous alloy and relatively low costs.

(48) It should be noted that the components described in the embodiments of the present invention do not involve non-metal components such as oxygen and nitrogen, but those skilled in the art know that a certain content of non-metal elements such as oxygen and nitrogen is inevitable in an alloy. For example, in the process of melting a Zr-based amorphous alloy in the embodiments of the present invention, oxidation may occur and introduce certain oxygen content, which is inevitable in the current manufacturing process. Therefore, amorphous alloys of homogeneous metal components combined with certain non-metal components shall fall within the protection scope of the present invention.

(49) Persons of ordinary skill in the art should understand that all or a part of the processes of the method in the embodiments may be implemented by a computer program instructing relevant hardware. The program may be stored in a computer readable storage medium. When the program is run, the processes of the method in the embodiments are performed. The storage medium may be a magnetic disk, an optical disk, a read-only memory (Read-Only Memory, ROM), a random access memory (Read-Only Memory, RAM), or the like.

(50) Finally, the foregoing embodiments are merely intended for describing the technical solutions of the embodiments of the present invention rather than limiting the present invention. Although the embodiments of the present invention are described in detail with reference to preferred embodiments, persons of ordinary skill in the art should understand that they may still make modifications to the technical solutions described in the embodiments of the present invention or make equivalent replacements to some technical features thereof, without departing from the spirit and scope of the technical solutions of the embodiments of the present invention.