OSSEOINTEGRATIVE SURGICAL IMPLANT AND IMPLANT SURGICAL KIT
20220031429 · 2022-02-03
Inventors
Cpc classification
A61C8/0012
HUMAN NECESSITIES
A61C8/006
HUMAN NECESSITIES
A61C13/0003
HUMAN NECESSITIES
A61C8/0053
HUMAN NECESSITIES
A61C2008/0046
HUMAN NECESSITIES
A61C8/0075
HUMAN NECESSITIES
A61C8/0087
HUMAN NECESSITIES
International classification
A61C8/00
HUMAN NECESSITIES
B28B11/24
PERFORMING OPERATIONS; TRANSPORTING
Abstract
Embodiments of the present invention provide an osseointegrative implant and related tools, components and fabrication techniques for surgical bone fixation and dental restoration purposes. In one embodiment an all-ceramic single-stage threaded or press-fit implant is provided having finely detailed surface features formed by ceramic injection molding and/or spark plasma sintering of a powder compact or green body comprising finely powdered zirconia. In another embodiment a two-stage threaded implant is provided having an exterior shell or body formed substantially entirely of ceramic and/or CNT-reinforced ceramic composite material. The implant may include one or more frictionally anisotropic bone-engaging surfaces. In another embodiment a densely sintered ceramic implant is provided wherein, prior to sintering, the porous debound green body is exposed to ions and/or particles of silver, gold, titanium, zirconia, YSZ, α-tricalcium phosphate, hydroxyapatite, carbon, carbon nanotubes, and/or other particles which remain lodged in the implant surface after sintering. Optionally, at least the supragingival portions of an all-ceramic implant are configured to have high translucence in the visible light range. Optionally, at least the bone-engaging portions of an all-ceramic implant are coated with a fused layer of titanium oxide.
Claims
1-49. (canceled)
50. A single stage press-fit dental implant comprising: an anchoring portion configured to be inserted subgingivally into an unthreaded osteotomy formed within the alveolar bone of a patient, said anchoring portion being generally cylindrical in shape and comprising a plurality of gripping edges configured to provide frictional anisotropy facilitating locomotion in the insertion direction of said anchoring portion; and an abutment portion integrally formed with said anchoring portion, said abutment portion comprising a transgingival portion configured to emerge from said anchoring portion through the gingiva at a predetermined emergence angle relative to a longitudinal axis of the anchoring portion, and a supragingival portion configured to extend into the oral cavity to receive and support a prosthetic tooth or other restorative structure.
51. The single stage press-fit dental implant of claim 50 wherein said anchoring portion has an anisotropic portion with a coefficient of sliding friction that is at least 25% less in the insertion direction than in the opposite direction.
52. The single stage press-fit dental implant of claim 50 wherein said anchoring portion comprises a soft-bone-engaging lower anchoring portion and a hard-bone-engaging upper anchoring portion, and wherein said upper anchoring portion is larger in diameter than said lower anchoring portion and wherein said lower anchoring portion reduces in diameter as it extends from said upper anchoring portion.
53. The single stage press-fit dental implant of claim 52 wherein said lower anchoring portion comprises a plurality of dimples arranged in a spaced pattern with a surface packing density greater than 0.75.
54. The single stage press-fit dental implant of claim 1 manufactured by: (1) injecting a feedstock into a mold cavity comprising a reverse of the geometry of said implant, said feedstock comprising a powder suspended in a liquid binder; (2) causing or allowing said injected feedstock to cool in said mold cavity until it forms a substantially solid green body having sufficient strength for demolding, the green body comprising the geometry of said implant; (3) debinding said green body to remove said binder; and (4) sintering said debound green body to form said single stage press-fit dental implant.
55. An implant surgical kit comprising a variety of single stage press-fit dental implants as recited in claim 50 and corresponding implant analogues, each dental implant comprising a predetermined emergence angle relative to a longitudinal axis of said anchoring portion.
56. The implant surgical kit of claim 55 wherein each single stage press-fit dental implant comprises a single integral ceramic structure and wherein each corresponding implant analogue is formed from stainless steel.
57. A press-fit osseointegrative dental implant comprising: an anchoring portion configured to be inserted subgingivally into an unthreaded osteotomy formed within the alveolar bone of a patient, said anchoring portion being generally cylindrical in shape and comprising a hard-bone-engaging upper anchoring portion and a soft-bone-engaging lower anchoring portion that reduces in diameter as it extends from said upper anchoring portion, and wherein at least said upper anchoring portion comprises a plurality of bone engaging edges configured to provide frictional anisotropy relative to the insertion direction of said anchoring portion; and an abutment portion comprising a transgingival portion configured to emerge from said upper anchoring portion through the gingiva at a predetermined emergence angle relative to a longitudinal axis of said anchoring portion, and a supragingival portion configured to extend from said transgingival portion into the oral cavity to receive and support a prosthetic tooth or other restorative structure.
58. The press-fit osseointegrative dental implant of claim 57 wherein said anchoring portion has an anisotropic portion with a coefficient of sliding friction that is at least 25% less in the insertion direction than in the opposite direction.
59. The press-fit osseointegrative dental implant of claim 57 wherein at least said upper anchoring portion or said lower anchoring portion has a a peak-to-peak surface roughness (SZ) of between 23.91 μm and 36.27 μm.
60. The press-fit osseointegrative dental implant of claim 57 wherein said lower anchoring portion comprises a plurality of dimples arranged in a spaced pattern with a surface packing density greater than 0.75.
61. The press-fit osseointegrative dental implant of claim 57 manufactured by: (1) injecting a feedstock into a mold cavity comprising a reverse of the geometry of said implant, said feedstock comprising a powder suspended in a liquid binder; (2) causing or allowing said injected feedstock to cool in said mold cavity until it forms a substantially solid green body having sufficient strength for demolding, the green body comprising the geometry of said implant; (3) debinding said green body to remove said binder; and (4) sintering said debound green body to form said press-fit osseointegrative dental implant.
62. An implant surgical kit comprising a variety of press-fit osseointegrative dental implants as recited in claim 57 and corresponding implant analogues, each press-fit osseointegrative dental implant comprising a predetermined emergence angle relative to a longitudinal axis of said anchoring portion.
63. The implant surgical kit of claim 62 wherein each press-fit osseointegrative implant comprises a single integral ceramic structure and wherein each corresponding implant analogue is formed from stainless steel.
64. A dental implant surgical kit comprising a plurality of osseointegrative single stage press-fit dental implants and a corresponding plurality of non-osseointegrative implant analogues, each of said osseointegrative single stage press-fit dental implants comprising: an anchoring portion configured to be inserted subgingivally into an unthreaded osteotomy formed within the alveolar bone of a patient, said anchoring portion being generally cylindrical in shape and comprising a hard-bone-engaging upper anchoring portion and a soft-bone-engaging lower anchoring portion that reduces in diameter as it extends from said upper anchoring portion, and wherein at least said upper anchoring portion comprises a plurality of bone engaging edges configured to provide frictional anisotropy relative to the insertion direction of said anchoring portion; and an abutment portion comprising a transgingival portion configured to emerge from said upper anchoring portion through the gingiva at a predetermined emergence angle relative to a longitudinal axis of said anchoring portion, and a supragingival portion configured to extend from said transgingival portion into the oral cavity to receive and support a prosthetic tooth or other restorative structure.
65. The dental implant surgical kit of claim 64 wherein said anchoring portion of at least one of said osseointegrative single stage press-fit dental implants has an anisotropic portion with a coefficient of sliding friction that is at least 25% less in the insertion direction than in the opposite direction.
66. The dental implant surgical kit of claim 64 wherein said upper anchoring portion or said lower anchoring portion of at least one of said osseointegrative single stage press-fit dental implants has a peak-to-peak surface roughness (SZ) of between 23.91 μm and 36.27 μm.
67. The dental implant surgical kit of claim 64 wherein said lower anchoring portion of at least one of said osseointegrative single stage press-fit dental implants comprises a plurality of dimples arranged in a spaced pattern with a surface packing density greater than 0.75.
68. The dental implant surgical kit of claim 64 wherein at least one of said osseointegrative single stage press-fit dental implants is manufactured by: (1) injecting a feedstock into a mold cavity comprising a reverse of the geometry of said implant, said feedstock comprising a powder suspended in a liquid binder; (2) causing or allowing said injected feedstock to cool in said mold cavity until it forms a substantially solid green body having sufficient strength for demolding, the green body comprising the geometry of said implant; (3) debinding said green body to remove said binder; and (4) sintering said debound green body to form said press-fit osseointegrative dental implant.
69. The dental implant surgical kit of claim 64 wherein said plurality of osseointegrative single stage press-fit dental implants comprise transgingival portions emerging at a variety of predetermined emergence angles and wherein said non-osseointegrative implant analogues comprise analogue transgingival portions emerging at a corresponding variety of predetermined emergence angles.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0031] Having thus summarized the general nature of the invention and its essential features and advantages, certain preferred embodiments and obvious modifications thereof will become apparent to those skilled in the art from the detailed description herein having reference to the figures that follow, of which:
[0032]
[0033]
[0034]
[0035]
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
[0056]
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
[0068]
[0069]
[0070]
[0071]
[0072]
[0073]
[0074]
[0075]
[0076]
[0077]
[0078]
[0079]
[0080]
[0081]
[0082]
[0083]
[0084]
[0085]
[0086]
[0087] For convenience of description and for better clarity and understanding of the invention, similar elements in different figures may be identified with similar or even identical reference numerals. However, not all such elements in all embodiments are necessarily identical as there may be differences that become clear to persons skilled in the art when read and understood in the context of each particular disclosed preferred embodiment.
DETAILED DESCRIPTION
[0088] The attached figures and accompanying disclosure illustrate and describe multiple embodiments of various surgical implants and associated tools, components and fabrication techniques having features and advantages of the invention as more-fully described herein. All of these embodiments are intended to be within the scope of the invention herein disclosed. These and other embodiments and obvious variations of the present invention will become readily apparent to those skilled in the art from the following detailed description of the preferred embodiments having reference to the attached figures, the invention not being limited to any particular preferred embodiment(s) disclosed.
Definitions
[0089] The following terms as used herein in the specification and in the claims shall be defined and understood as follows, regardless of any other ordinary or understood meanings, dictionary definitions, definitions in documents incorporated by reference, or other possible meanings of the defined terms:
[0090] The indefinite articles “a” and “an” should be understood to mean at least one.
[0091] The conjunctive phrase “and/or” should be understood to mean “either or both” of the elements so conjoined, i.e., elements that are conjunctively present in some cases and disjunctively present in other cases. Multiple elements listed with “and/or” should be construed in the same fashion, i.e., “one or more” of the elements so conjoined. Other elements may optionally be present other than the elements specifically identified by the “and/or” clause, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, a reference to “A and/or B”, when used in conjunction with open-ended language such as “comprising” can refer, in one embodiment, to A only (optionally including elements other than B); in another embodiment, to B only (optionally including elements other than A); in yet another embodiment, to both A and B (optionally including other elements); etc.
[0092] The phrase “at least one,” in reference to a list of one or more elements, should be understood to mean at least one element selected from any one or more of the elements in the list of elements, but not necessarily including at least one of each and every element specifically listed within the list of elements and not excluding any combinations of elements in the list of elements. This definition also allows that elements may optionally be present other than the elements specifically identified within the list of elements to which the phrase “at least one” refers, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, “at least one of A and B” (or, equivalently, “at least one of A or B,” or, equivalently “at least one of A and/or B”) can refer, in one embodiment, to at least one, optionally including more than one, A, with no B present (and optionally including elements other than B); in another embodiment, to at least one, optionally including more than one, B, with no A present (and optionally including elements other than A); in yet another embodiment, to at least one, optionally including more than one, A, and at least one, optionally including more than one, B (and optionally including other elements); etc.
[0093] The phrase “communicatively coupled” or “communicative coupling” means that there is a path or channel of communication from one component to another, whether the path is direct or indirect and whether such path includes a path through one or more intervening component.
[0094] The conjunctive article “or” should be understood to have the same meaning as “and/or” as defined above. For example, when separating items in a list, “or” or “and/or” shall be interpreted as being inclusive, i.e., the inclusion of at least one, but also including more than one, of a number or list of elements, and, optionally, additional unlisted items. Only terms clearly indicated to the contrary, such as “only one of” or “exactly one of,” or, when used in the claims, “consisting of,” will refer to the inclusion of exactly one element of a number or list of elements. In general, the term “or” as used herein shall only be interpreted as indicating exclusive alternatives (i.e. “one or the other but not both”) when preceded by terms of exclusivity, such as “either,” “one of,” “only one of,” or “exactly one of.” When a range of “about X to Y” or “between about X and Y” is stated, the range includes from about X to about Y or between about X and about Y.
Acronyms
[0095] For the convenience of the reader certain acronyms and abbreviations used herein in the specification and claims are listed below:
[0096] BET Brunauer, Emmett and Teller technique
[0097] CIP cold isostatic pressing
[0098] CL conductive layer
[0099] CNT carbon nanotube
[0100] CT computed tomography
[0101] CTE coefficient of thermal expansion
[0102] DI dionized water
[0103] DLC diamond-like carbon
[0104] EDC electric discharge coating
[0105] EDM electrical discharge machining
[0106] FAST field-assisted sintering technique
[0107] FDA Food and Drug Administration
[0108] FESEM field emission scanning electron microscope
[0109] HIP Hot isostatic pressing
[0110] LTCC low-temperature co-fired ceramic
[0111] MWCNT multi-walled carbon nanotube
[0112] MWS Microwave sintering
[0113] NEMS nano-electro-mechanical system
[0114] PECS pulsed electric current sintering
[0115] PEG polyethylene glycol
[0116] PMEDC powder mixed electric discharge coating
[0117] PMMA polymethylmethacrylate
[0118] POM Polyoxymethylene
[0119] PVB polyvinyl butyral
[0120] SA stearic acid
[0121] SEM scanning electron microscope
[0122] SPS spark plasma sintering
[0123] SWCNT single-walled carbon nanotube
[0124] YSZ yttrium-stabilized zirconia
[0125] Single Stage Threaded Implant
[0126]
[0127] As illustrated in
[0128] Referring again to
[0129] Preferably, the lower anchoring portion 126 is formed with a single continuous clockwise thread 127 that extends helically and/or spirally from the proximal end 126a to the distal end 126b thereof. Preferably the thread 127 has a pitch of between about 0.4 mm to 0.8 mm or about 15%-25% of the major thread diameter Dt at or near the proximal end 126a and, more preferably, about 18% of the major thread diameter Dt at or near the proximal end 126a (See
[0130] The preferred thread profile is a truncated 30° saw tooth shape having a neutral or slightly positive (e.g., 3° to 5°) rake angle relative to the pull-out direction of the implant 100, as illustrated in more detail in
[0131] As illustrated in more detail in
[0132] If desired, one or more cutting edges may also be formed or provided on the thread 127 at or near the distal end 126b of the lower anchoring portion 126 and/or between the distal end 126B and the inflexion point 126c so as to provide a self-tapping and/or self-drilling capability in accordance with any one of a number of well-known self-tapping and/or self-drilling thread designs. Preferably, saw-tooth-like cutting edges are formed in the thread 127 between the distal end 126B and the inflexion point 126c so as to provide a self-tapping capability wherein mating threads are cut into the surrounding bone tissue as the implant 100 is threaded into an unthreaded or partially-threaded osteotomy. If desired, the spacing, depth and/or rake angle of the cutting edges may be varied from the distal end 126b to the inflexion point 126c so as to minimize friction and cutting forces and/or to maximize fracture resistance. Preferably, any cutting edges formed in thread 127 are substantially evenly spaced along the crest of the thread and increase in depth from the distal end 126b to the inflexion point 126c. Preferably, such cutting edges have associated rake angles that gradually decrease from neutral or slightly positive (e.g., 0° to 5°) at the distal end 126b to substantially negative (e.g., −30° to −45° at or near the inflexion point 126c. If desired, any one or more of the cutting edges may be formed with an oblique rake angle so as to reduce friction and associated cutting forces. Optionally, the cutting edges may be formed with alternating positive and negative rake angles and/or alternating oblique rake angles, as desired.
[0133] As illustrated in more detail in
[0134] Preferably, these and/or other similar raised or sunken features are formed with a maximum height or depth relative to the implant surface of less than about 0.15 mm or about 4% of the local diameter of the implant 100 and, more preferably, less than about 0.05 mm or about 1% of the local diameter of the implant 100. Advantageously, the combination of these and/or similar raised and/or sunken surface features, such as dimples, bumps and ridges, increases mechanical engagement and promotes in-growth and adhesion of live bone tissue, thereby improving primary stability and promoting healing and osseointegration. The tie rods 129 also increase the torsional strength of the lower anchoring portion 126 thereby increasing its torsional fracture resistance. The tie rods 129 and/or similar structures may also advantageously help remove and/or transport bone debris away from the hard cortical bone 160 during insertion of the implant 100 into a threaded or unthreaded osteotomy. Preferably, the tie rods 129 have a height of about 0.15 mm, a width of about 0.3 mm and a length of about 0.32 mm. Dimples 133 preferably have an average diameter of about 0.130 mm and an average depth of about 0.065 mm. Alternatively, the size and/or depth of the dimples 133 may be varied in a regular or irregular (e.g., random) pattern, if desired, so as to provide a surface that promotes mechanical engagement, adhesion and in-growth of live bone tissue. Alternatively, some or all of the dimples 133 may be replaced with similarly-sized bumps or alternating and/or varying combinations of dimples, bumps and/or other desired surface features as desired.
[0135] The upper anchoring portion 128 is designed to engage the hard/dense cortical bone 160 (e.g., see
[0136] Preferably, the outer bone-engaging surface of one or both of the first and second portions 128a, 128b are densely covered with multiple raised and/or sunken surface features, such as dimples, bumps or ridges, arranged in a regular or irregular spaced pattern (e.g., dimples 143 shown in
[0137] Preferably, these and/or other similar raised and/or sunken features are formed with a maximum height or depth relative to the implant surface equal to or less than about 0.15 mm or about 4% of the local diameter of the implant 100. In an alternative embodiment, these and/or other similar raised and/or sunken features are formed with a maximum height or depth relative to the implant surface equal to or less than about 0.05 mm or about 1% of the local diameter of the implant 100. Advantageously, the combination of these and similar raised and/or sunken surface features, such as dimples, bumps and ridges, increases the surface area and mechanical engagement of the implant and encourages in-growth and adhesion of live bone tissue, thereby improving primary stability and promoting healing and osseointegration. Dimples 143 preferably have an average diameter of about 0.130 mm, an average depth of about 0.065 mm and are preferably spaced apart between 0.13 mm and 0.18 mm from center to center and, more preferably about 0.15 mm from center to center, in a square packing or hexagonal packing arrangement. Alternatively, the size and/or depth of the dimples 143 may be varied in a regular or irregular (e.g., random or fractal) pattern, if desired, so as to provide an improved bone-engaging surface that increases mechanical engagement and promotes in-growth and adhesion of live bone tissue. Optionally, some or all of the dimples 143 may be replaced with raised bumps, studs, spurs, spikes, knurling and/or similar raised surface features for providing enhanced gripping, frictional anisotropy, resistance to rotation and/or additional desired bone engagement and increased primary stability. If present, these raised features create limited localized residual stresses at the point where each bump or other raised surface feature presses into the surrounding hard cortical bone tissue 160.
[0138] Referring again to
[0139] The supragingival portion 130 preferably comprises a post-like structure having a tapered anti-rotational cross-section (e.g., hex, square, star, and/or the like) configured to extend into the oral cavity to receive and support a porcelain crown or other restorative device or structure. This may be bonded or cemented directly to the supragingival portion 130 using a suitable bonding agent such as zinc phosphate or polycarboxylate. Preferably, a torque driver or similar tool (see, e.g.,
[0140]
[0141] As noted above, preferably the lower anchoring portion 126 is formed with a single continuous clockwise thread 127 that extends helically and/or spirally from the proximal end 126a to the distal end 126b thereof. Preferably the thread 127 has a pitch of 0.775 mm or about 19% of the major thread diameter Dt at or near the proximal end 126a (see, e.g.,
[0142] The preferred thread profile is a truncated 30° saw tooth shape having a substantially square gripping edge 335 formed with neutral rake angle (i.e., orthogonal) relative to the pull-out direction of the implant 100, as illustrated in more detail in
[0143] The thread 127 is preferably continuous for the first 2 thread revolutions 127a starting from the proximal end 126a and then transitioning to a notched or serrated thread 127b for the remaining portions thereof to the distal end 126b. Preferably, the thread 127 is notched with truncated V-notches 132, as best illustrated in
[0144] Multiple tie rods 129 are preferably provided between each adjacent thread 127 in a regular spaced pattern. Tie rods 129 are preferably raised surface features which are directly molded and integrally formed with the lower anchoring portion 126 of the implant body between adjacent threads 127, as illustrated in more detail in
[0145] The upper anchoring portion 128 is generally formed as a short cylinder having a total length of between about 0.75 and 1.0 mm, more preferably, about 0.875 mm. Preferably, the outer bone-engaging surface of the upper anchoring portion 128 is densely covered with 3-4 equally spaced rows of hemispherical dimples 143 having a radius of 0.125 mm and arranged in a square or hexagonal packing pattern with an average center-to-center spacing S1 of 0.280 mm (see
[0146] As illustrated in
[0147] As with the other embodiments described above, the supragingival portion 130 of the implant 100 preferably comprises a tapered post 130 having a generally square or quad-lobed cross-section (e.g.,
[0148] Preferably, the entire implant 100, including substantially all finely detailed surface features and surface texturing described herein, is injection molded and sintered to substantially its final geometry (the mold being slightly oversized to account for shrinkage during subsequent sintering). The post-sintered dental implant advantageously requires substantially no additional grinding, machining or chemical etching operations prior to final sterilization and packaging. Optionally, some additional machining operations or resurfacing (e.g., deburring, polishing, etching, or sharpening) may be performed either before or after final sintering.
[0149]
[0150]
[0151] The preferred thread profile is a truncated 30° saw tooth shape having a substantially square gripping edge formed with neutral rake angle (i.e., orthogonal) relative to the pull-out direction of the implant 100, as illustrated in more detail in
[0152] The thread 127 is preferably continuous for the first 2-3 thread revolutions 127a starting from the proximal end 126a and then transitioning to a notched or serrated thread 127b for the remaining portions thereof to the distal end 126b. Preferably, the thread 127 is notched with V-notches 132, as best illustrated in
[0153] Multiple tie rods 129 are preferably provided between each adjacent thread 127 in a regular spaced pattern. Tie rods 129 are preferably raised surface features which are directly molded, machined or otherwise integrally formed with the lower anchoring portion 126 of the implant body between adjacent threads 127, as illustrated in more detail in
[0154] The upper anchoring portion 128 is generally formed as a stepped cylinder having a first portion 128a configured to engage the hardest/densest part of the cortical bone near the surface thereof, and a second portion 128b configured to engage the less hard/dense part of the cortical bone located 1-2 mm below the surface thereof and/or the transition region between the cortical bone and the softer cancellous bone. The upper anchoring portion 128 is preferably about 1.5 mm to 2 mm in total length, and wherein the first portion 128a comprises about three-fourths and the second portion 128b comprises about one-fourth of this total length. Preferably, the first portion 128a has a first diameter D1 that is about 4% to 5% larger than the second diameter D2 of the second portion 128b. The stepped transition 137 between the first and second portions 128a, 128b (see, e.g.,
[0155] Preferably, the outer bone-engaging surface of the first portion 128a is densely covered with 8 circumferential rows of hemispherical dimples 143 having a radius of 0.064 mm and arranged in a square or hexagonal packing pattern with a center-to-center spacing S1 of 0.152 mm (see
[0156] For example, 5% to 50% and, more preferably, about 15% of the dimples 143 and/or 153 may be replaced with small bumps that protrude less than about 0.03 to 0.10 mm and, more preferably, about 0.065 mm from the bone-engaging surface 128a into the surrounding hard cortical bone tissue. These bumps and/or similar raised surface features may be arranged in a regular or irregular (e.g., random) pattern and/or they may be arranged, for example, in a helical pattern matching that of the thread 127, if desired. Alternatively, an alternating pattern of round dimples and raised spikes may be provided in a regular or irregular spaced pattern in order to provide precisely controlled amounts of mechanical engagement with the hard cortical bone tissue. Advantageously, the combination of these raised and/or sunken surface features produce precisely controllable amounts of localized stress and stress relief distributed over one or more desired areas of the implant site, resulting in increased mechanical engagement and interlocking of the implant 100 with the surrounding hard bone tissue and improved primary stability, while reducing or limiting the possibility of stress-induced bone necrosis and other bone injuries. Of course, those skilled in the art will readily appreciate that a wide variety of similar raised and/or sunken surface features may be provided in various shapes, sizes, combinations and patterns in order to achieve these and similar advantages as described herein.
[0157] As illustrated in
[0158] As with the other embodiments described above, the supragingival portion 130 of the implant 100 preferably comprises a tapered post 130 having a hex or star-like cross-section (e.g.,
[0159]
[0160] Those skilled in the art will appreciate that a wide variety of similar raised and/or sunken surface features and combinations of surface features may be provided or formed on one or more bone-engaging surfaces of a threaded or unthreaded implant in accordance with one or more alternative embodiments of the present invention. These surface features may be provided, for example, on the crest or other bone-engaging portions of one or more threads 127, 157, between adjacent threads 127, on the upper anchoring portion 128, and/or on the lower anchoring portion 126 of a threaded or unthreaded implant. Preferably, these and/or other similar raised or sunken features are formed with a maximum height or depth relative to the implant surface of less than about 0.15 mm or about 4% of the local diameter of the implant. In an alternative embodiment, these and/or other similar raised and/or sunken features are formed with a maximum height or depth relative to the implant surface equal to or less than about 0.05 mm or about 1% of the local diameter of the implant. Advantageously, the combination of these and/or similar raised and/or sunken surface features, such as dimples, bumps and ridges, increases mechanical engagement of the implant and promotes in-growth and adhesion of live bone tissue, thereby improving primary stability and promoting long-term healing and osseointegration.
[0161] Some of these surface features may also provide desired gripping, abrading, scraping or cutting action. Yet other surface features may help remove, transport or accommodate bone and other tissue debris that may be formed during insertion of the implant into a threaded or unthreaded osteotomy. Some or all of these surface features may be frictionally isotropic (e.g., see
[0162] For purposes of practicing the claimed invention, frictionally anisotropic surfaces preferably have a directionally-dependent coefficient of sliding friction that is at least 10% less, more preferably at least 25% less, and most preferably at least 50% less, in one direction (e.g., the insertion direction) than in another direction (e.g., the extraction direction). Such frictionally anisotropic surfaces are particularly preferred where it is desired to: i) minimize the insertion force or torque required to drive an implant, ii) maximize the retention or extraction force or torque required to remove an implant, and/or iii) impart desired locomotion to the implant during insertion or extraction thereof (e.g., urging a threaded or unthreaded implant deeper into an osteotomy as it is wiggled, vibrated and/or rotated). Note that for a threaded implant, the “insertion” direction generally refers to clockwise rotation of the implant (assuming a right-handed thread) while the “extraction” direction generally refers to counter-clockwise rotation. For a press-fit implant (described in more detail later) the “insertion” direction generally refers to the pressing-in direction while the “extraction” direction generally refers to the pulling-out direction.
[0163]
[0164] Preferably, all of the described geometries and surface features illustrated and discussed above in connection with
[0165] Two Stage Threaded Implant
[0166] In each of the single-stage threaded implant designs described above, preferably, the subgingival anchoring portion 110 and the supragingival abutment portion 120 are formed as a single integrated structure 100, as will be described in more detail herein. However, in an alternative embodiment the implant 100 may be formed in two or more mating pieces so as to provide greater restorative flexibility. For example, separate mating pieces may be formed as a threaded portion 126, a non-threaded portion 128, a subgingival portion 110, a transgingival portion 123 and/or a supragingival portion 120. Those skilled in the art will appreciate that any two or more of these mating pieces and combinations thereof may be permanently and/or removably secured to one another either before, during or after use in one or more surgical procedures. This may be accomplished, for example, using one or more mating screws or fasteners, or using a suitable cement or bonding agent such as zinc phosphate or polycarboxylate.
[0167]
[0168] Preferably, the abutment 220 and the outer shell 261 of the anchoring portion 210 are formed from a suitable ceramic material such as yttrium-stabilized zirconia which is preferably densely sintered and molded to a final desired geometry, as will be described in more detail later. Alternatively, the abutment 220 and the outer shell 261 may be formed as densely sintered ceramic blanks which are molded to near-final geometry and then machined to their final desired geometry by grinding and/or other machining steps. Alternatively, one or both of the abutment 220 and the outer shell 261 may be formed from blanks of pure titanium, titanium alloy, or other suitable material by molding, casting, rolling, forging, grinding and/or other machining operations.
[0169] Referring again to
[0170] Preferably, the lower anchoring portion 226 is formed with a single continuous clockwise thread 227 that extends helically and/or spirally from the proximal end 226a to the distal end 226b thereof. Preferably the thread 227 has a pitch of between about 0.4 mm to 0.8 mm or about 15%-25% of the major thread diameter Dt at or near the proximal end 226a and, more preferably, about 18% of the major thread diameter at or near the proximal end 226a (see
[0171] The preferred thread profile is a truncated 30° saw tooth shape having a neutral or slightly positive rake angle. The root or spacing between adjacent threads is preferably about 40%-60% of the thread pitch and, more preferably, about 50% of the thread pitch. A flattened crest is preferably formed at the outer-most edge of the thread 227 and preferably has a width of 0.102 mm or about 16% of the thread pitch at the proximal end 226a gradually widening to about 0.22 mm or about 35% of the thread pitch at or near the distal end 226b. Preferably, the thread pitch and the saw tooth profile remain substantially constant from the proximal end 226a to the distal end 226b. Preferably the thread profile and thread depth remain substantially constant from the proximal end 226a to an inflexion point 226c located approximately one-third of the distance from the proximal end 226a to the distal end 226b. From the inflexion point 226c to the distal end 226b preferably the thread depth decreases at a constant and/or accelerating rate, reducing from about 8% of the major thread diameter at or near the inflexion point 226c to less than about 1-2% of the major thread diameter at or near the distal end 226b.
[0172] Optionally, the thread 227 may be notched or serrated along at least a portion of its length, as illustrated in
[0173] As described above in connection with
[0174] Preferably, these and/or other similar raised or sunken features are formed with a maximum height or depth relative to the implant surface of less than about 0.15 mm or about 4% of the local diameter of the implant 200. In an alternative embodiment, these and/or other similar raised and/or sunken features are formed with a maximum height or depth relative to the implant surface equal to or less than about 0.05 mm or about 1% of the local diameter of the implant 200. Preferably, the tie rods 229 have a height of about 0.15 mm, a width of about 0.3 mm and a length of about 0.32 mm. Dimples 233 preferably have an average diameter of about 0.130 mm and an average depth of about 0.065 mm. Alternatively, the size and/or depth of the dimples 233 may be varied in a regular or irregular (e.g., random) pattern, if desired, so as to provide a surface that promotes mechanical engagement, adhesion and in-growth of live bone tissue. Alternatively, some or all of the dimples 233 may be replaced with similarly-sized bumps or alternating and/or varying combinations of dimples, bumps and/or other similar surface features as desired.
[0175] The upper anchoring portion 228 is designed to engage the hard/dense cortical bone in a manner that optimally achieves both primary stability and long-term osseointegration. The upper anchoring portion 228 is preferably formed as an inverted truncated cone having an emergence profile that preferably substantially matches the emergence profile of the transgingival portion 223 of the abutment 220, as illustrated in
[0176] The abutment 220 preferably comprises a smoothly tapered transgingival portion 223 configured to emerge from the anchoring portion 210 through the gingiva in a desired emergence profile, and a supragingival portion 230 comprising a post-like structure configured to extend into the oral cavity to receive and support a prosthetic tooth or other restorative structure such as an anatomically-functional aesthetic porcelain crown. Preferably, the transgingival portion 223 has a machined or polished biologically inert surface that provides a good sealing interface with the surrounding soft gum tissues and prevents or resists the accumulation of plaque and calculus thereon. If desired, the transgingival portion 223 may be shaped and contoured in accordance with any number of tooth emergence profiles as may be desired. Suitable emergence profiles may include, for example, simple rotationally symmetric shapes (e.g., round or conical), bilaterally symmetric shapes (e.g., ovular), radially symmetric shapes (e.g., triangular or hexagonal), compound curves, complex curves, or other arbitrary or asymmetric shapes (e.g., shapes mimicking or approximating the emergence profile of a natural tooth being replaced). In one embodiment, a suitable emergence profile is formed as an outwardly-opening flattened or ovular-shaped truncated cone that is substantially circular at the narrower end and substantially ovular at the wider end (see, e.g.,
[0177]
[0178] Once the lower inner sleeve 263 is in place within the inner cavity 281 of the outer shell 261, the upper inner sleeve 273 is pressed in through the opening 281 and engages the flexible fingers 279 of the lower sleeve 263. When the retention screw 271 is inserted and tightened, the lower sleeve 263 is pulled upward toward the upper sleeve 273 causing the flexible fingers 279 to ride up the sloped surface of the upper sleeve 273 and resiliently expand as illustrated in
[0179] Preferably, torque-transmitting anti-rotational features 283 are provided on the upper sleeve 273 (e.g.,
[0180] Single Stage Press-Fit Implant
[0181]
[0182] As illustrated in
[0183] The angle of emergence and the particular emergence profile of the abutment portion 320 relative to the anchoring portion 310 may be varied, as desired, such as illustrated in
[0184] Preferably, the transgingival portion 323 of the implant 300 has smooth biologically inert surface that provides a good sealing interface with the surrounding soft gum tissues and prevents or resists the accumulation of plaque and calculus thereon. A suitably smooth surface may be formed, for example, by molding, machining and/or polishing. The transgingival portion 323 is also preferably molded, shaped and/or contoured in accordance with any number of tooth emergence profiles as may be desired. Suitable emergence profiles may include, for example, simple rotationally symmetric shapes (e.g., round or conical), bilaterally symmetric shapes (e.g., ovular), radially symmetric shapes (e.g., triangular or hexagonal), compound curves, complex curves, or other arbitrary or asymmetric shapes (e.g., shapes mimicking or approximating the emergence profile of a natural tooth being replaced). In one embodiment, a suitable emergence profile is formed as an outwardly-opening flattened or ovular-shaped truncated cone that is substantially circular at the narrower end and substantially ovular at the wider end. The outer edge 324 of the transgingival portion 323 may also be contoured or shaped as desired. For example, the buccal and lingual sides of the transgingival portion 323 may be shaved down or undercut, as illustrated in
[0185] The supragingival portion 330 preferably comprises a post-like structure having a tapered anti-rotational cross-section (e.g., hex, square, star, and/or the like) configured to extend into the oral cavity to receive and support a porcelain crown or other restorative device or structure. The crown or other restorative device may be bonded or cemented directly to the supragingival portion 330 using a suitable bonding agent such as zinc phosphate or polycarboxylate. Preferably, a torque driver or similar tool (see, e.g.,
[0186] The anchoring portion 310 generally comprises a soft-bone-engaging lower anchoring portion 326 and a hard-bone-engaging upper anchoring portion 328. The lower anchoring portion 326 comprises a generally round or cylinder-like body, as illustrated, which may either be tapered or untapered, as desired. Preferably, the lower anchoring portion 326 is untapered or only slightly tapered (e.g., less than 1° or 2°) along all or a selected portion of its length from the proximal end (closest to the oral cavity) to the distal end thereof (furthest from the oral cavity). If tapered, the lower anchoring portion 326 is preferably widest at the proximal end and smallest at the distal end and may have a constant or variable (e.g., accelerating or decelerating) rate of taper from the proximal to the distal end. In one embodiment the lower anchoring portion 326 may be 5% to 10% smaller in diameter at the distal end than at the proximal end thereof. If desired, the distal end of the implant may terminate in a single-reducing or double-reducing chamfer 331, as illustrated in
[0187] Preferably, the outer bone-engaging surface of the lower anchoring portion 326 is densely covered with multiple raised and/or sunken surface features, such as dimples, bumps or ridges, arranged in a regular or irregular spaced pattern. See, for example,
[0188] Preferably, these and/or other similar raised and/or sunken features are formed with a maximum height or depth relative to the implant surface equal to or less than about 0.15 mm or about 4% of the local diameter of the implant 300. In an alternative embodiment, these and/or other similar raised and/or sunken features are formed with a maximum height or depth relative to the implant surface equal to or less than about 0.05 mm or about 1% of the local diameter of the implant 300. However, some larger features may also be used, as desired. Advantageously, the combination of these and other raised and/or sunken surface features, such as dimples, bumps and ridges, increases mechanical engagement of the implant and encourages in-growth and adhesion of live bone tissue, thereby improving primary stability and promoting healing and osseointegration of the implant 300. Dimples preferably have an average diameter of about 0.130 mm, an average depth of about 0.065 mm and are preferably spaced apart between 0.13 mm and 0.18 mm from center to center and, more preferably about 0.15 mm from center to center, in a square packing or hexagonal packing arrangement. Alternatively, the size and/or depth of the dimples may be varied in a regular or irregular (e.g., random) pattern, if desired, so as to provide an improved bone-engaging surface that increases mechanical engagement and promotes in-growth and adhesion of live bone tissue. Optionally, some or all of the dimples may be replaced with raised bumps, studs, spurs, spikes, knurling and/or similar raised surface features for providing enhanced gripping, frictional anisotropy, resistance to rotation and/or additional desired bone engagement and increased primary stability. If present, these raised features create limited localized residual stresses at the point where each bump or other raised surface feature presses into the surrounding soft cancellous bone tissue 170 (see
[0189] For example, 25% to 75% and, more preferably, about 50% of the dimples may be replaced with small bumps that protrude less than about 0.03 to 0.10 mm and, more preferably, less than about 0.065 mm from the bone-engaging surface 326 into the surrounding soft cancellous bone tissue. These bumps and/or similar raised surface features may be arranged in a regular or irregular (e.g., random) pattern, as desired. Alternatively, an alternating pattern of round dimples and raised spikes may be provided in a regular or irregular spaced pattern in order to provide precisely controlled amounts of mechanical engagement with the soft cancellous bone tissue. Advantageously, the combination of these raised and/or sunken surface features produce precisely controllable amounts of localized stress and stress relief distributed over one or more desired areas of the implant site, resulting in increased mechanical engagement and interlocking of the implant 300 within the surrounding bone tissue and improved primary stability, while reducing or limiting the possibility of stress-induced bone necrosis and/or other bone injuries. Of course, those skilled in the art will readily appreciate that a wide variety of similar raised and/or sunken finely detailed surface features may be provided in various shapes, sizes, combinations and patterns in order to achieve these and similar advantages as described herein.
[0190] Alternatively, or in addition, larger raised features, such as large bumps (e.g., having diameters greater than about 0.25 mm), gripping edges, thread-like features, and/or the like, may be added in order to provide additional desired functionality. For example, hemispherical bumps 333 having a diameter between 0.25 mm to 0.5 mm may be arranged on the lower anchoring portion 326, as illustrated in the alternative embodiment shown in
[0191] In another possible alternative embodiment illustrated in
[0192] Referring again to
[0193] Preferably, all of the described geometries and surface features illustrated and discussed above in connection with
[0194] Clinical Techniques and Tools
[0195] In the clinical procedure for inserting each of the implant embodiments described above, an oral surgeon first prepares the implant site by exposing and forming an osteotomy within the alveolar bone (either the maxilla or the mandible) of a patient. The size, shape, depth and orientation of the osteotomy is carefully planned using X-ray imaging and/or CT scanning of the patient's teeth, mouth and surrounding tissues to ensure there is sufficient bone integrity, thickness and depth to accommodate the implant. If the available bone structure is insufficient to support the implant, various bone grafting techniques may be used to augment, build up and/or repair the target implant site. A drill guide is preferably used to ensure the precise location and desired orientation of the osteotomy. Progress may be confirmed using X-ray imaging and/or CT scanning as the procedure progresses.
[0196] Once the osteotomy is formed to a desired depth a reamer and/or other similar tools may be used to expand and/or more precisely shape the opening of the osteotomy in accordance with a desired bone emergence profile of a particular implant selected to be inserted. For example, a dual-diameter stepped cylindrical reamer may be used to precisely shape the opening of the osteotomy to match the stepped cylindrical profile of the upper anchoring portion 128 of the threaded implant 100 illustrated and described above in connection with
[0197] Once the osteotomy is formed and suitably shaped and/or threaded, a precision torque driver is preferably used to drive or maneuver the implant to its final seated position. The torque driver is preferably configured to limit the amount of insertion torque to no more than the maximum design torque threshold for the particular associated implant (up to about 45 N-cm for a titanium implant and about 15-30 N-cm for a Zirconia implant). If the torque required to seat the implant exceeds the design threshold, the surgeon must remove the implant and use one or more of the above-described tools (e.g., drills, reamers, taps) to clean and/or enlarge the osteotomy. The torque driver and/or any one or more of the other tools described herein may be packaged and sold with the implant as a sterile single-use implant surgical kit, or the tools may be packaged and sold separately from the implant, as desired or expedient.
[0198]
[0199] The torque-limiting transfer coupling 407 comprises multiple (preferably 5) ball bearings 415 (e.g., stainless steel or ceramic bearings) that are generally configured to roll within a bearing race formed between a first component comprising a flexible cage 417 which forms an upper race 418 and a second component comprising a bearing support 419 forming a lower race 420. Alternatively, other rolling or sliding bearing types may be used with efficacy, including spherical-, cylindrical-, needle-, tapered-, barrel-, or slip-type bearings. The flexible cage 417 generally comprises a hollow cylinder having an upper portion 417a, a lower portion 417b and a middle portion 417c having a plurality of flexible fingers 422. The fingers 422 may be straight or slanted, as desired, or expedient. Preferably the fingers 422 are slanted or twisted by 5° to 10° as illustrated. Those skilled in the art will appreciate that at least the upper portion 417a of the flexible cage is rigidly coupled to the input shaft 403 while the second component 419 forming the lower race 420 is rigidly coupled to the output shaft 405. The flexible cage 417 and the second component 419 are both mounted within a housing comprising a main enclosure 421 and a threaded cap 423 which threads onto the end of the main enclosure 421. Those skilled in the art will appreciate that the housing may be fixed relative to the output shaft 405 and the second component 419, or it may be fixed relative to the input shaft 403 and the flexible cage 417, as desired or expedient.
[0200] When the torque-limiting transfer coupling 407 is assembled as illustrated in
[0201] Implant Fabrication
[0202] Conventional titanium implants are typically individually machined from a solid cylinder of titanium material and then acid etched to produce a finished implant having the final desired geometry and surface texture. The machining and acid etching (or other surface treatment) processes introduce oils, chemicals and other impurities to the surface of the work piece which must be removed by extensive post-fabrication cleaning and sterilization. Conventional titanium implant fabrication is also slow, requiring several days or even weeks to complete a single finished implant. It is also highly capital intensive, typically requiring multiple six-axis grinding machines and other sophisticated production equipment.
[0203] Conventional ceramic implants are typically fabricated in a similar fashion by grinding green-stage blanks to an initial desired geometry (e.g., forming threads and other macro features), sintering in an oven for several hours and then further grinding, sandblasting or acid etching the resulting hard smooth surface of the sintered implant to produce a finished implant having the final desired geometry and surface texture. The green-stage grinding process alone typically leads to production losses of 10-15% due to discoloration, fracturing and chipping. Additional expense and production losses are incurred in the post-sintering machining operations due to the inherent difficulties in machining hard, brittle ceramic materials. It is well known that post-sintering grinding and other ablative machining, sandblasting and chemical etching steps can leave machining marks, micro-cracks, fissures and other defects in the finished ceramic surface that can make the implant more susceptible to cracking or fracturing. See, e.g., Gahlert M, Burtscher D, Grunert I, Kniha H, Steinhauser E., Failure analysis of fractured dental zirconia implants, Clin. Oral Impl. Res. 23, 2012; 287-293. As a result of these and other difficulties, ceramic implant fabrication according to conventional methods is expensive, slow and capital intensive, typically requiring multiple six-axis grinding machines and other sophisticated production equipment.
[0204] Accordingly, an improved implant fabrication technique is provided, as described in more detail herein, that avoids or mitigates some or all of these problems and which increases manufacturing yields and reduces manufacturing time and expense. In accordance with one embodiment, as schematically illustrated in
[0205] Referring to
[0206] The dispersibility of powder particles within a binder is highly dependent on the forces between the particles. Accordingly, the use of small organic molecules such as fatty acids offers an attractive inter-particle potential, which dominates the rheological behavior of a suspension. Because particle agglomerates are frequently observed in starting ceramic powders, surfactants such as oleic acid and stearic acid (SA) are preferably added to the mixture to improve powder dispersion during mixing. The main function of such surfactants is to produce a modified powder surface so that steric stabilization between individual particles can be attained in the colloid to help evenly disperse the powder. For example, suitable surface modification of zirconia powder may be achieved by thoroughly ball-milling the YSZ powder with 3.0 vol % stearic acid (SA) before mixing with the binder. See, e.g., Wei Liu,z Zhipeng Xie,w,z Xianfeng Yang,z,y Yin Wu,z Cui Jia,z Tiezhu Bo,z and Linlin Wang, Surface Modification Mechanism of Stearic Acid to Zirconia Powders Induced by Ball Milling for Water-Based Injection Molding, J. Am. Ceram. Soc., 94 [5] 1327-1330 (2011), incorporated herein by reference in its entirety. Advantageously, the resulting SA coating limits the agglomeration of the YSZ powder and changes the nature of the powder surface from hydrophilic to hydrophobic, which decreases the shear viscosity of the feedstock and increases the water-debinding rate.
[0207] Preferably, an SA-coated superfine (0.5-10 μm dia.) or ultrafine (≤500 nm dia.) powder of 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 having an average particle size of between 0.05 and 0.25 μm, more preferably about 0.16 μm, and a BET surface area between about 5 and 30 m2/g, more preferably about 8.2 m2/g, is mixed with a water-soluble binder such as polyethylene glycol (PEG) or polyoxy-methylene (POM) to provide a feedstock injection molding operations. For example, suitable YSZ powders may be obtained from Farmeiya Advanced Materials Co., Ltd., Jiujiang, China, such as grade YSZ-F-DM-3.0. Alternatively, finer-grade YSZ powders may also be used with efficacy, including nano powders having an average particle size between 20 and 50 nm and a BET surface area between 15 and 40 m2/g, such as 3 mol % Y2O3 stabilized ZrO2 nano powder (product #40390N-9502) available from Inframat Advanced Materials LLC, Manchester, Conn. See, e.g., F. Mohd Foudzi, et al., Yttria stabilized zirconia formed by micro ceramic injection molding: Rheological properties and debinding effects on the sintered part, Ceramics International (2012), http://dx.doi.org/10.1016/j.ceramint. 2012.09.033, incorporated herein by reference in its entirety. Of course, those skilled in the art will appreciate that the fabrication techniques described herein are not limited to YSZ powders, but may be practiced using a wide variety and combination of ceramic and/or non-ceramic powders including, without limitation, zirconia, alumina, silica, porcelain, calcium phosphate β-tricalcium phosphate, hydroxylapatite, bioglass, silicon carbide, tungsten carbide, titanium, titanium oxide, vanadium, thorium, niobium, tantalum, calcium, and the like. However, SA-coated superfine or ultrafine powders comprising YSZ are preferred.
[0208] The SA-coated YSZ powder is preferably mixed with a water-soluble binder in sufficient ratio to achieve a solids loading of between 40% and 60% and more preferably about 48%. It has been found that YSZ solids loadings in this range provide sufficiently high green densities for sintering while maintaining good flowability in the injecting phase. The feedstock flow behavior is defined largely by the interactions between particles. During injection molding the particles slide past each other by translation and rotation. Accordingly, YSZ powders comprising spherical or nearly spherical particles are generally preferred as such particles can easily rotate and slip past each other in the feedstock stream. However, some degree of particle shape irregularity is also acceptable and can actually improve particle packing and shape stability during green-stage processing. Easy gliding is also supported by low binder viscosity, good wetting behavior and thorough coating of the powder surface. Preferably, all agglomerates are broken up during the mixing step in order to completely eliminate any enclosed pores and eliminate large irregular shaped compacts that might otherwise increase flow resistance and/or produce defects in the finished product.
[0209] The next step (
[0210] The next step (
[0211] Binder systems for water debinding mainly consist of a water-soluble binder which dissolves in water and a water-insoluble backbone binder which keeps the strength of the green body after the water-soluble binder has been removed. During initial water debinding a large fraction (e.g., 85% or more) of the organic binder material is dissolved in water and is extracted, leaving a green body having a generally interconnected porous structure. The remaining fraction of organic binder material is removed in one or more subsequent debinding steps, such as organic solvent debinding, catalytic debinding, thermal debinding, and/or the like. Higher solids loadings and smaller particle sizes generally lead to lower porosity, higher tortuosity of the pores, a lower interdiffusion coefficient and a slower debinding rate. Depending on the binder polymer used, these further debinding steps can be carried out by thermal and/or chemical decomposition. For example, POM-based binders are typically removed by catalytic debinding using concentrated nitric acid at 110° C. See, e.g., U.S. Pat. No. 8,674,018 to Maat et al, incorporated herein by reference in its entirety. Suitable examples of water-soluble binder systems include combinations of: i) acetanilide with polystyrene, ii) polyethylene glycol (PEG) with polymethyl-methacrylate (PMMA), iii) PEG with cellulose acetate butyrate, iv) PEG with polyvinyl butyral (PVB), and v) polyoxymethylene (POM).
[0212] Advantageously, the resulting interconnected porous structure evolved through water debinding, thermal debinding and/or catalytic debinding may also be used as a channel to introduce additional elements, compounds or materials through the porous outer surface of the partially debound green body 511 to a particular desired depth (e.g., less than 0.5 mm and preferably less than 0.1 mm). See, e.g., G. W. Liu, Z. P. Xie, W. Wang, Y. Wu and X. F. Yang, Fabrication of coloured zirconia ceramics by infiltrating water debound injection moulded green body, Advances in Applied Ceramics 2011 VOL 110 NO 1, p. 58, incorporated herein by reference in its entirety. These added elements, compounds or materials may be used, for example, to modify the color, translucency, surface texture, surface chemistry, surface hardness, crystallinity, porosity, electrical conductivity, or biological compatibility of the implant surface. For example, the water debound green body 511 may be fully or partially immersed in an aqueous solution containing ions of silver, gold, titanium, and/or other elements or compounds, as desired, so as to cause the ion solution to enter the porous surface of the green body 511 by capillary action and to diffuse interiorly to a desired depth. The depth of penetration can be controlled or adjusted by varying the concentration of the ion solution, temperature, agitation, exposure time, and/or other parameters affecting the duration of exposure or the rate of diffusion. As another example, the water debound green body 511 may be fully or partially immersed in a colloidal solution or fluidized bed comprising nanoparticles of titanium, zirconia, YSZ, α-tricalcium phosphate, hydroxyapatite, carbon, carbon nanotubes (CNT), and/or other particles sufficiently small in size such that at least some of the particles enter and remain lodged in the porous surface of the green body 511 and/or diffuse interiorly to a desired depth. As another example, the water debound green body 511 may be fully or partially exposed to an electric arc discharge, gas plasma, ionized gas, sublimation vapors, air-borne particulates, and/or other particles suspended in a fluid such that at least some of the surface-modifying elements, compounds or materials enter the porous surface of the green body 511 and/or diffuse interiorly to a desired depth.
[0213] In any one or more of the above described examples partial surface modification may be achieved by selectively exposing only a portion of the water debound green body 511 (e.g., the anchoring portion or the abutment portion) to the surface-modifying element, compound or material. For example, certain portions of the water debound green body 511 may be selectively dipped in an aqueous ion solution and/or certain portions of the green body 511 may be selectively masked with a masking element or a temporary coating prior to exposing the green body to the surface-modifying element, compound or material. In some embodiments, the surface-modifying element, compound or material itself forms a desired component of the finished post-sintered implant surface. For example, surface infused particles of titanium, zirconia, silica, boron, hydroxyapatite or YSZ may provide a desired surface chemistry, roughness and/or color that improves biological compatibility, osseointegration or aesthetic appeal of the finished implant product. In other embodiments, the surface-modifying element, compound or material is used only as an intermediate component to facilitate further modification of the post-sintered implant surface and/or the green body surface. For example, surface infused ions or particles of silver, gold, carbon or titanium may provide desired electrical conductivity at the surface of the green body 511 and/or the sintered implant in order to facilitate further surface modification through various electro-chemical reactions, electroplating, electric discharge machining (EDM), and/or similar surface modification techniques. In yet other embodiments, the surface-modifying element, compound or material may be extracted, dissolved, or otherwise removed from the post-sintered implant surface (e.g., via water, acid or other solvent, electrochemical reaction, or burning/oxidation) producing, for example, a porous outer YSZ ceramic surface having improved biological compatibility and/or osseointegration characteristics.
[0214] The final step (
[0215] In a typical sintering process, the debound green body 511 is heated in a kiln or furnace to an elevated temperature (e.g., 300-1500° C.) that is below the melting point of the material. The atoms making up the individual powder particles diffuse across the boundaries of the particles, eventually fusing the particles together forming one solid mass. Advantageously, because the sintering temperature is lower than the melting point of the material, the geometrical shape of the green body 511 can be precisely maintained while the individual powder particles gradually fuse together forming a densely sintered body 513. For example, in one embodiment a green body with finely detailed surface features is formed by injection molding a feedstock comprising ultrafine polycrystalline yttria-stabilized tetragonal zirconia powder (94.4% ZrO2, 5.0-5.3% Y2O3, 0.2-0.3% AI2O3) having an average particle size of between 0.05 and 0.25 μm thoroughly mixed in a water-soluble POM-based binder. After final debinding the debound green body is sintered by heating it from room temperature to 270° C. at a rate of about 3 K/min and holding for 1 hour, then heating it to 1500° C. at a rate of about 3 K/min and holding for 1 hour, then cooling it to 600° C. at a rate of about −5 K/min, followed by furnace cooling for one hour. Following initial sintering, hot isostatic pressing (HIP) is used to close any residual porosity and to gain additional density and strength. Preferably, the sintered body is placed in a pressurized vessel containing Argon gas maintained at a pressure of 150-250 MPa. The sintered body is heated from room temperature to 1350° C. at a rate of about 5 K/min and held for 2 hours, then cooled to 1200° C. at a rate of about 3 K/min and held for 1 hour, and then cooled to room temperature.
[0216] During conventional sintering the heat necessary to produce atomic diffusion is usually provided via one or more external heating elements and transferred to the green body 511 in a furnace or kiln via convection and/or infrared radiation. While the green body 511 is heating up, the external heat transfer mechanism (which heats the green body from the outside in) can lead to undesirable thermal gradients, which can result in cracks, shape distortions and/or other defects. To prevent the formation of undesirable thermal gradients during sintering, slow heating rates and/or isothermal holding periods are typically employed. For example, conventional sintering of 3 mol % YSZ is typically limited to a heating rate of only about 7° C. per minute. However, slower heating rates lead to growth of larger crystalline grains which generally results in decreased material properties such as strength, hardness, and toughness. Thus, rapid sintering and densification is generally preferred.
[0217] Microwave sintering (MWS) is another sintering method which uses microwaves to heat up a zirconia green body 511. It is well known that the conductivity of zirconia increases with temperature and that zirconia is actually a good electrical conductor at temperatures above 800-850° C. This allows a YSZ green body 511 to be heated from the inside out using microwaves or other electromagnetic fields. Combined with conventional heating mechanisms such as convection and radiation, microwave assisted sintering advantageously allows the green body 511 to be heated at a more rapid rate of 20° C. per minute or more without producing cracks, shape distortions or other defects.
[0218] In a further alternative embodiment, as illustrated in
[0219] For example, 3 mol % Y2O3 stabilized ZrO2 nano powder may be used as a starting material such as available from Inframat Advanced Materials LLC, Manchester, Conn. (product #4039ON-9502). Of course, those skilled in the art will appreciate that a wide variety of other ceramic and/or non-ceramic powders may also be used with efficacy. It is known in classic sintering theory that densification and grain growth are two competing processes, and both of them are driven by forces that are inversely proportional to grain size. Thus, the smaller the initial powder size, the larger the densification and grain growth rates during sintering. For SPS, a finer powder will usually attain higher densities and will undergo larger grain growth than a coarser powder under identical sintering conditions. In addition, finer powders will start to densify at lower temperatures and densify at greater rates than coarser powders. Thus, the effectiveness of realizing rapid densification by applying a fast heating rate using SPS is highly dependent on the particle size of the starting powder material. Accordingly, finer powders are particularly preferred for SPS, such as nano powders having an average particle size between 20 and 50 nm and a BET surface area between 15 and 40 m2/g.
[0220] In accordance with one embodiment, a powder compact or green body is initially formed using a powder compacting press, which packs and compresses ultrafine or nano powder material into a graphite die, such as the two part die 600 illustrated in
[0221] Once the powder compact is formed and/or compressed to a desired density, the graphite die 600 is mounted between two opposing punches (e.g., see
[0222] If desired, the SPS process may be further adjusted and/or modified so as to produce an even more densely sintered (e.g., greater than 98.5% and up to 99.9% of theoretical density) implant 611 having desired translucence properties. The most significant factor affecting the translucence of a ceramic is porosity which typically occurs at the grain boundaries. The surface of a pore is a boundary between phases with sharply different optical characteristics, which therefore intensely reflects and refracts light. The presence of a large number of pores makes ceramics opaque. Accordingly, one way to produce a translucent ceramic implant is to more densely sinter the ceramic material in order to reduce or eliminate pores at the grain boundaries.
[0223] In one embodiment a densely sintered ceramic implant is formed by sintering a powder compact of 3YSZ powder at 1100° C. for 10 minutes at a pressure of 400 MPa, producing a highly translucent zirconia implant having a transmission coefficient tc (including both direct and diffuse transmission) of greater than about 25% measured at a wavelength of 525 nm. In another embodiment a densely sintered ceramic implant is formed by sintering a powder compact of 3YSZ powder at 1075° C. for 12 minutes at a pressure of 500 MPa, producing a highly translucent zirconia implant having a transmission coefficient tc of greater than about 33% measured at a wavelength of 525 nm. In another embodiment a densely sintered ceramic implant is formed by sintering a powder compact of 3YSZ powder at 1050° C. for 16 minutes at a pressure of 600 MPa, producing a highly translucent zirconia implant having a transmission coefficient tc of greater than about 40% measured at a wavelength of 525 nm. In another embodiment a densely sintered ceramic implant is formed by sintering a powder compact of 3YSZ powder at 1025° C. for 22 minutes at a pressure of 750 MPa, producing a highly translucent zirconia implant having a transmission coefficient tc of greater than about 60% measured at a wavelength of 525 nm. In another embodiment a densely sintered ceramic implant is formed by sintering a powder compact of 3YSZ powder at 1100° C. for 18 minutes at a pressure of 700 MPa, producing a highly translucent zirconia implant having a transmission coefficient tc of greater than about 75% at a wavelength of 525 nm.
[0224] If desired, tinting and/or coloring of the implant 611 can be provided by introducing trace impurities and/or by annealing the sintered implant in an oxidizing atmosphere (e.g., annealing in air for 1-2 hours at 800° C.). See, e.g., H. Zhang, B. Kim, K. Morita, H. Yoshida, K. Hiraga and Y. Sakka, Fabrication of Transparent Yttria by High-Pressure Spark Plasma Sintering, J. Am. Ceram. Soc., 94 [10] 3206-3210 (2011) and H. Zhang, B. Kim, K. Morita, H. Yoshida, J. Lim and K. Hiraga, Optical Properties and Microstructure of Nanocrystalline Cubic Zirconia Prepared by High-Pressure Spark Plasma Sintering, J. Am. Ceram. Soc. 94 [9] 2981-2986 (2011), both of which are incorporated herein by reference in their entirety.
[0225] Composite Materials
[0226] In accordance with another aspect of the invention, an osseointegrative implant may be fabricated from a composite material. Composite materials may generally be defined as those materials that consist of two or more fundamentally different components that are able to act synergistically to produce material properties superior to those provided by either component alone. For example, it is known that alumina ceramics can be combined with hydroxyapatite in order to achieve a composite ceramic material having higher bioactivity. See, e.g., S. Zeng, Z. Yang, P. Ling, G. Xu and W. Cao, Materials Research Society Symposium Proceedings 292 (Biomolecular Materials), 271-275 (1993). Various alumina-zirconia composites have also been investigated for enhancing biocompatibility with bone tissue. See, e.g., B. A. Konduk A. H. Ucisik, Journal of the Australasian Ceramic Society, 37(1), 63-81 (2001).
[0227] In accordance with one embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture of polycrystalline yttria-stabilized tetragonal zirconia and alumina comprising by weight approximately 94.4% ZrO2, 5.0-5.3% Y2O3, and 0.2-0.3% AI2O3. In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising by weight approximately 75% to 85% of 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 15% to 25% titanium dioxide (TiO2). In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 85% to 95% of 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 5% to 15% titanium dioxide (TiO2). In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 75% to 95% of 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 5% to 25% of 6 mol % yttria-stabilized zirconia (Y2O3)6 (ZrO2)94. In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 75% of 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97, approximately 15% hydroxyapatite, and approximately 10% titanium dioxide (TiO2).
[0228] In each case described above and in other cases where two or more different materials are used to form a composite green body, the composition and/or the ratio of composite components may also be varied throughout the green body so as to provide various desired material properties at different locations of the finished implant (e.g., interior vs. exterior, inner threads vs. outer threads, subgingival vs. transgingival vs. supragingival, etc.) in order to enhance the overall performance characteristics of the implant. Such composite variations may be achieved in accordance with any number of well-known molding and/or forming techniques such as powder compacting, powder coating, casting, slip molding, injection molding, co-injection molding, spraying, dipping, rolling, masking, co-extrusion, multi-layer extrusion, sol-gel processing, 3D printing, and/or similar techniques.
[0229] In accordance with another aspect of the invention, a densely sintered osseointegrative implant is fabricated from a nanocomposite material prepared by the incorporation of a substantial portion by volume of carbon nanotubes in a finely powdered starting material. Carbon nanotubes (CNTs) are allotropes of carbon with a cylindrical nanostructure. CNTs are the strongest and stiffest materials yet discovered in terms of tensile strength and elastic modulus respectively. This strength results from the covalent sp2 bonds formed between the individual carbon atoms. The surface areas of CNTs can also be very high because, in the absence of agglomeration, every atom of a single walled nanotube lies on its surface. Another significant feature of CNTs is their very high aspect (length to diameter) ratio which is relevant to load transfer, heat transfer and electrical conductivity within a composite matrix.
[0230] CNTs provide a basic building block for producing many advanced engineering composite materials having unprecedented mechanical and thermal properties, including ultra-high elastic modulus (˜1 TPa), high tensile strength (˜150 GPa), high thermal conductivity (˜3000-6000 W/mK), and a low coefficient of thermal expansion (2.7×10-6/K to 4.4×10-6/K). The outstanding mechanical properties of CNTs provide particularly attractive advantages in the context of a ceramic implant. Added as a reinforcement material to a ceramic-based material (e.g., zirconia, alumina and/or hydroxyapatite), CNTs can substantially increase the torsional and bending strength of the implant while reducing its susceptibility to stress-induced crack propagation. This phenomena is illustrated in
[0231]
[0232] Table 1 below shows that a densely sintered composite body of 3YZT having 0.5 to 5 wt % of CNTs has a shear modulus that is 5% to 40% higher than that of monolithic 3YTZ.
TABLE-US-00001 TABLE 1 Material Composition Shear Modulus (GPa) 3YSZ 78 ± 6.5 3YSZ + 0.5 wt. % CNT 82 ± 5.4 3YSZ + 1.5 wt. % CNT 92 ± 4.3 3YSZ + 3.0 wt. % CNT 99 ± 3.8 3YSZ + 5.0 wt. % CNT 107 ± 3.8
[0233] See, e.g., M. Mazaheri, et al., Multi-walled carbon nanotube/nanostructured zirconia composites: Outstanding mechanical properties in a wide range of temperature, Compos. Sci. Technol. (2011), incorporated herein by reference in its entirety. See also, B. Milsom et al., The effect of carbon nanotubes on the sintering behaviour of zirconia, Journal of the European Ceramic Society 32 (2012) 4149-4156 and F. Inam et al., The sintering and grain growth behaviour of ceramic-carbon nanotube nanocomposites, Composites Science and Technology 70 (2010) 947-952.
[0234] There are two main kinds of carbon nanotubes relevant to the present invention: single-walled carbon nanotubes (SWCNTs) comprising individual cylinders 1-2 nm in diameter and made up of a single rolled graphene sheet, and multi-walled carbon nanotubes (MWCNTs) comprising a multi-layered structure made up of several concentric graphene cylinders, with weak Van der Waals forces binding the inner and outer tubes together. SWCNTs are significantly smaller in diameter compared to MWCNTs and the mechanical properties may differ significantly. MWCNTs consist of nested graphene cylinders coaxially arranged around a central hollow core with interlayer separations of about 0.34 nm, similar to the interplane spacing of graphite. MWCNTs are often curled, kinked and some of them are highly twisted with each other forming big CNT bundles having strong inter-tube van der Waals attraction.
[0235] If desired, some or all of the CNTs may be decorated with nanoparticles such as Au, Pd, Pt, Ag, Ti, or TiO2. See, e.g., F. Xin et al., Decoration of carbon nanotubes with silver nanoparticles for advanced CNT/polymer nanocomposites, Composites: Part A 42 (2011) 961-967, incorporate herein by reference in its entirety. Advantageously, decorated CNT's may be used to increase the electrical conductivity of the ceramic composite material, alter the color of the CNT (e.g., change it from black to silver or gold), improve biocompatibility, improve antibacterial characteristics, and/or improve dispersion and interfacial bonding between the CNTs and the ceramic base material. See, e.g., S. Ou et al., Research of antibacterial activity on silver containing yttria-stabilized-zirconia bioceramic, Ceramics International 39 (2013) 3591-3596, and E. Fortunati, Carbon nanotubes and silver nanoparticles for multifunctional conductive biopolymer composites, CARBON 49 (2011) 2370-2379. A wide variety of suitable SWCNT and MWCNT materials, both decorated and undecorated, are commercially available from sources such as Nanointegris Technologies Inc. in Menlo Park, Calif. and Sigma-Aldrich Corporation in St. Louis, Mo.
[0236] In accordance with one embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 95.0 to 97.5 wt % of powdered ceramic material such as 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 2.5 to 5.0 wt % of CNTs. In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising by approximately 97.5 to 99.5 wt % of powdered ceramic material such as 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 0.5 to 2.5 wt % of SWCNTs. In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 97.5 to 98.5 wt % of powdered ceramic material such as 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 1.5 to 2.5 wt % of MWCNTs. In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 97.5 to 98.5 wt % of powdered ceramic material such as 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 1.5 to 2.5 wt % of MWCNTs decorated with an electrically conductive metal such as silver, gold or titanium. In accordance with another embodiment, an osseointegrative implant is fabricated in whole or in part by densely sintering a green body formed from a composite powder mixture comprising approximately 97.5 to 98.5 wt % of 3 mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 1.5 to 2.5 wt % of silver-decorated CNTs.
[0237] Preferably, the CNT material is processed and mixed with the ceramic base powder material in such a way as to ensure a substantially homogeneous dispersion of CNTs within the composite mixture prior to sintering. For example, this may involve pre-treatment and/or chemical surface modification of the CNTs to improve dispersion within either a colloidal suspension or dry powder mixture. Advantageously, the unique flexible nature of CNTs allows them bend and pass through spaces between nanopowders and/or wrap around them. Any CNT agglomerates are preferably dispersed and/or removed prior to green body formation and the remaining individual nanotubes are thoroughly mixed and distributed uniformly throughout the composite mixture. Good dispersion and interfacial bonding between the CNTs and the ceramic base material is important in order to achieve desired mechanical and electrical properties in the post-sintered ceramic composite material.
[0238] Surface Modifications
[0239] Optionally, the outer surface of the implant or any portion thereof may be coated, anodized, treated, sandblasted, etched and/or otherwise modified so as to provide a desired surface roughness, surface chemistry, biocompatibility and/or bioactivity. In one embodiment, particles of titanium and/or titanium oxide are infused with the outer surface of at least the bone-engaging portions of a ceramic implant by electrical discharge machining, as described in more detail below, creating a strongly bonded titanium oxide layer up to 20 μm thick and having unique roughness and porosity characteristics favorable for promoting rapid and/or more thorough bone osseointegration (see, e.g. the SEM micrograph inset shown in
[0240] Electrical discharge machining (EDM) is an ablative material removal process that uses high-voltage electrical discharges passing through a dielectric fluid to erode and remove material from an electrically-conductive surface of a workpiece. During the EDM process the workpiece surface undergoes rapid melting and vaporization at the contact point of each electric discharge followed by rapid cooling and carrying away of ejected debris by the dielectric fluid. EDM is typically used to cut and/or form complex shapes in a hardened metal component such as a die or a mold that is otherwise difficult to machine using conventional cutting tools. EDM can also been used for surface modification, surface hardening and/or depositing various desired coatings on the outer surface of an electrically-conductive component. This latter process, also called electric discharge coating (EDC), can be used to deposit strongly-bonded coatings of material up to 20 μm thick.
[0241] In one embodiment, EDC is used to create a strongly-bonded titanium oxide layer on the outer surface of at least the bone-engaging portions of a ceramic implant. Preferably, the relevant portions of the implant are formed and/or treated so as to have a specific electrical resistance of 300 Ω-cm or less. For example, the electrical resistivity of ZrO2 can be reduced from in excess of 10E12 Ω-cm to about 100 Ω-cm by incorporating 0.1 wt % of SWCNT in the powder mixture that is used to form the green body or powder compact, as disclosed herein. Those skilled in the art will appreciate that well-dispersed carbon nanotubes form an interconnected percolation network through the insulating ZrO2 matrix such that the post-sintered CNT-ZrO2 composite ceramic exhibits an overall desired electrical conductivity that is sufficiently high to support the EDC process. Alternatively, as discussed in more detail herein in connection with
[0242] As illustrated in
[0243] The anode portion 651 is preferably shaped and configured to grip and hold the implant 611 and provide sufficient electrical connection to allow substantially arc-free current flow between the anode portion 651 and at least one electrically-conductive portion of the implant 611. If desired, an optional O-ring seal 655 may be provided between the anode portion 651 and the implant 611 in order to mask or shield selected portions of the implant. The anode portion 651 and the cathode portion 653 are also preferably insulated from one another by an electrical insulating barrier (not shown) in order to prevent current flow and/or arcing between the anode portion 651 and the cathode portion 653. One or more vents 657, 659 may be provided in the anode portion 651 and/or the cathode portion 653, as illustrated in
[0244] During the EDC process an electrical current is caused to flow from the titanium electrode (cathode) to the workpiece (anode) causing high-voltage arcing through the dielectric fluid, as illustrated in
[0245] To increase and/or control the erosion rate of the titanium cathode, it is preferably formed from a green powder compact and/or a partially- or fully-sintered compact of powdered titanium. Titanium powders having an average particle size of between about 45 μm and 180 μm are preferred, although finer or courser powders may also be used with efficacy (e.g., ranging between about 0.5 μm and 0.25 mm). Electrodes formed from finer powders typically lead to faster erosion of the cathode and result in more intricate and higher-surface-area roughness and porosity characteristics of the titanium oxide coating layer. Smaller size particles also create greater suspension effect in the dielectric fluid (e.g., DI water) as the cathode erodes, allowing for more uniform and/or higher concentrations of titanium oxide particles in the dielectric fluid.
[0246] Optionally, as illustrated in
[0247] In an alternative embodiment, a modified PMEDC process is used to create a fused titanium oxide layer on the outer surface of an otherwise non-electrically-conductive ceramic implant. According to this alternative embodiment a first layer of electrically conductive substance is applied to the surface of the implant to form a temporary or auxiliary electrode capable of initiating the PMEDC process. See, e.g., G. Kucukturka et al., A new method for machining of electrically nonconductive workpieces using electric discharge machining technique, Machining Science and Technology: An International Journal, Vol. 14, Issue 2, pgs. 189-207 (2010), and US20100038344 to Forster et al, each incorporated herein by reference in their entirety. For example, the bone-engaging portions of a non-conductive ceramic implant may be coated with a thin conductive layer (CL) of biocompatible material such as, for example, a 3-5 μm thick layer of titanium nitride (TiN) or titanium carbonitride (TiCN). Titanium nitride is non-toxic, meets FDA guidelines and has been used in a wide variety of medical devices such as scalpel blades, orthopedic bone saw blades and hip prostheses. It has a specific electrical resistivity of between 30 and 70 μΩ.Math.cm, providing suitable surface conductivity for sustaining the EDC process. TiN or TiCN can be readily applied to the non-conductive surface of a ceramic implant by physical vapor deposition (e.g., sputter coating, cathodic arc deposition or electron beam heating) and/or chemical vapor deposition. In both methods, pure titanium is sublimated and reacted with nitrogen in a high-energy, vacuum environment and the resulting vapors are caused to condense on the cooler exposed surfaces of the ceramic implant. During subsequent EDC and/or PMEDC processing (such as described above) the initial spark discharge formations occur between the titanium electrode and the CL. The CL may be partially or fully ablated and/or eroded in the process. However, as the EDC and/or PMEDC process continues, a spattered surface layer of titanium oxide develops on the surface of the implant providing sufficient surface conductivity to sustain the EDC coating process.
[0248] According to the various surface modification techniques disclosed and described herein, particles of titanium and/or titanium oxide are able to be infused with the outer surface of the bone-engaging portions of a ceramic or ceramic composite implant, creating a fused titanium oxide layer up to 20 μm thick having unique roughness and porosity characteristics favorable for promoting rapid and/or more thorough bone osseointegration. As illustrated in more detail in
APPLICATIONS AND EXAMPLES
[0249] Embodiments of the present invention may be employed, produced and carried out in a wide variety of clinical and commercial applications, as will be readily apparent to those skilled in the art. The following specific examples are provided for purposes of illustration and for better understanding of the invention and should not be taken as limiting the invention in any way.
Example 1
[0250] A single-stage threaded implant is formed having one or more of the features and geometries as illustrated and described above in connection with
Example 2
[0251] A single-stage press-fit implant is formed having one or more of the features and geometries as illustrated and described above in connection with
Example 3
[0252] A two-stage threaded ceramic implant is formed having one or more of the features and geometries as illustrated and described above in connection with
Example 4
[0253] A dental implant is formed according any of the Examples 1-3 wherein a circumferentially extending pattern of 50 to 250 discrete raised and/or sunken surface features are formed on an outer bone-engaging surface of the implant and wherein each discrete surface feature has a maximum height or depth relative to the implant surface of less than about 0.1 mm.
Example 5
[0254] A dental implant is formed according any of the Examples 1-4 wherein a pattern of raised and/or sunken surface features form a geometric pattern on an outer bone-engaging surface of the implant so as to provide a directionally-dependent coefficient of sliding friction for the implant that is at least 30% less in the implant insertion direction than in the implant extraction direction.
Example 6
[0255] A dental implant is formed according to any of the Examples 1-5 wherein the implant is formed at least in part by hot forging and/or cold forging a partially-shaped blank of pure titanium or titanium alloy material.
Example 7
[0256] A dental implant is formed according to any of the Examples 1-6 wherein the implant is formed at least in part by sintering a green body formed by slip casting, powder compacting or injection molding a feedstock comprising a powdered titanium or titanium alloy material having an average particle size of between 10 and 36 μm.
Example 8
[0257] A dental implant is formed according to any of the Examples 1-7 wherein the implant is formed at least in part by sintering a green body formed by slip casting, powder compacting or injection molding a ceramic feedstock comprising 3 mol % yttria-stabilized powdered zirconia having an average particle size of about 0.16 μm.
Example 9
[0258] A dental implant is formed according to any of the Examples 1-8 wherein the entire implant is molded or powder compacted in green stage to substantially its final geometry (enlarged to account for shrinkage during subsequent sintering), including substantially all final surface texturing and other desired surface features. The green stage implant is then debinded (if a binder is used) and sintered in one or more sintering operations to produce a finished dental implant product that does not require any grinding or machining operations.
Example 10
[0259] A dental implant is formed according to any of the Examples 1-9 wherein the implant is formed at least in part by injection molding a ceramic feedstock comprising powdered polycrystalline yttria-stabilized tetragonal zirconia comprising by weight approximately 94.4% ZrO2, 5.0-5.3% Y2O3 and 0.2-0.3% Al2O3 and having an average particle size between 0.05 and 0.25 μm and a BET surface between about 8.0 and 40.0 m2/g. The powdered YSZ is first coated with stearic acid by ball-milling for 4 hours with 3 vol % stearic acid solution. The SA-coated powder is then thoroughly mixed with a POM binder using a twin screw kneader until a solids loading of about 48% is reached.
Example 11
[0260] A dental implant is formed according to any of the Examples 1-10 wherein the implant is formed by sintering a debound green body. Prior to sintering, the debound green body is fully or partially immersed in an aqueous solution containing ions and/or particles of silver, gold, titanium, zirconia, YSZ, α-tricalcium phosphate, hydroxyapatite, carbon, carbon nanotubes, and/or other particles sufficiently small in size such that at least some of the particles enter and remain lodged in the porous surface of the green body and/or diffuse interiorly to a desired depth.
Example 12
[0261] A dental implant is formed according to any of the Examples 1-11 wherein the implant is formed by sintering a debound green body. Prior to sintering, the debound green body is fully or partially immersed in a colloidal solution containing particles of carbon, carbon nanotubes, and/or other carbon-based particles such that at least some of the particles enter and remain lodged in the porous surface of the green body and/or diffuse interiorly to a desired depth. The green body is then fully sintered in a vacuum chamber or other oxygen free environment. After sintering the implant is heated in an oxygen environment until substantially all of the carbon-based particles are fully oxidized and/or burned off leaving a porous outer surface having improved biological compatibility and/or osseointegration characteristics.
Example 13
[0262] A dental implant is formed according to any of the Examples 1-12 wherein the implant is formed at least in part by spark plasma sintering a powder compact formed by compacting finely powdered 3-mol % yttria-stabilized zirconia having an average particle size between about 10 and 50 nm and a BET surface area between about 15 and 75 m2/g. The powder compact is pressed into a graphite die by uniaxial pressing at 64 MPa followed by cold isostatic pressing at 200 MPa producing a compacted green body having a density of around 43% of theoretical density. A pulsed DC current is introduced through a pair of graphite plungers and is caused to pass directly through the powder compact, heating it at a rate exceeding 500° C./min. Once a sintering temperature of 1050° C. is reached mechanical pressure of up to 400 MPa is applied until the powdered material is densely compressed and sintered to a final density between about 96.5% and 99.9% of theoretical density, resulting in a densely sintered zirconia implant having an average grain size of about 0.75 μm in diameter and detailed surface features according to the internal geometries of the graphite die.
Example 14
[0263] A dental implant is formed according to any of the Examples 1-13 wherein at least the supragingival portions of the implant have greater than 75% translucence to visible light. The implant is formed at least in part by spark plasma sintering a powder compact formed by compacting finely powdered 3-mol % yttria-stabilized zirconia having an average particle size between about 5 and 30 nm and a BET surface area between about 20 and 100 m2/g. The powder compact is pressed into a graphite die by uniaxial pressing at 64 MPa followed by cold isostatic pressing at 200 MPa producing a compacted green body having a density of around 43% of theoretical density. A pulsed DC current is introduced through a pair of graphite plungers and is caused to pass directly through the powder compact, heating it at a rate exceeding 500° C./min. Once a sintering temperature of 1100° C. is reached mechanical pressure of up to 800 MPa is applied for about 10 minutes until the powdered material is densely compressed and sintered to a final density greater between about 99.5% and 99.9% of theoretical density, resulting in a densely sintered zirconia implant having desired translucence properties.
Example 15
[0264] A dental implant is formed according to any of the Examples 1-14 wherein the implant is formed at least in part by densely sintering a green body formed from a composite powder mixture comprising approximately 98.0 wt % of powdered 3-mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 2.0 wt % of SWCNTs.
Example 16
[0265] A dental implant is formed according to any of the Examples 1-15 wherein the implant is formed at least in part by densely sintering a green body formed from a composite powder mixture comprising approximately 97.5 wt % of powdered 3-mol % yttria-stabilized zirconia (Y2O3)3 (ZrO2)97 and approximately 2.5 wt % of MWCNTs decorated with silver, gold and/or titanium.
Example 17
[0266] A dental implant is formed according to any of the Examples 1-16 wherein at least the bone-engaging surfaces of the implant are surface modified by electrical discharge machining, to create a strongly bonded 12 μm thick titanium oxide layer having desired surface roughness and porosity characteristics favorable for promoting implant osseointegration.
Example 18
[0267] A dental implant is formed according to any of the Examples 1-17 wherein at least the bone-engaging surfaces of the implant are surface modified by a PMEDC process to create a strongly bonded 16 μm thick titanium oxide layer having desired surface roughness and porosity characteristics. A titanium cathode is used and is formed from a green powder compact of pure titanium powder having an average particle size of about 120 μm. Dionized water is used as the dielectric fluid. Titanium oxide powder having an average particle size of 25 μm is added to the dionized water and is maintained in fluid suspension at a concentration of 50 g/l using a pump having a flow rate of about 15 L/min. The PMEDC process is continued until at least a 16 μm thick titanium oxide layer is attained.
Example 19
[0268] A dental implant is formed according to any of the Examples 1-18 wherein at least a portion of the implant is formed from a non-electrically-conductive ceramic and wherein at least the bone-engaging surfaces of the implant are surface modified by a PMEDC process to create a strongly bonded 18 μm thick titanium oxide layer having desired surface roughness and porosity characteristics. An initial coating of 3.5 μm thick titanium nitride (TiN) is applied to the bone-engaging surfaces of the ceramic implant by physical vapor deposition in order to form a temporary conductive layer for initiating the PMEDC process. During PMEDC a titanium cathode is used which is formed from a partially-sintered powder compact of pure titanium powder having an average particle size of about 100 μm. Dionized water is used as the dielectric fluid. Pure titanium powder having an average particle size of 100 μm is added to the dionized water and is maintained in fluid suspension at a concentration of 40 g/l using a pump having a flow rate of about 20 L/min. The PMEDC process is continued until an 18 μm thick titanium oxide layer is attained.
OTHER APPLICATIONS AND MODIFICATIONS
[0269] Although this invention has been disclosed in the context of certain preferred embodiments and examples, those skilled in the art will appreciate that the present invention extends beyond the specifically disclosed embodiments to other alternative embodiments and/or uses of the invention and obvious modifications and equivalents thereof. Thus, it is intended that the scope of the present invention should not be limited by the particular preferred embodiments disclosed herein, but should be determined only by a fair reading of the claims that follow.