CHEMICALLY AMPLIFIED POSITIVE RESIST COMPOSITION AND RESIST PATTERN FORMING PROCESS

Abstract

A chemically amplified positive resist composition is provided comprising a base polymer which contains a polymer comprising an acid generating unit, a phenolic hydroxy group-containing unit, a unit containing a phenolic hydroxy group protected with an acid labile group, and a unit containing a carboxy group protected with an acid labile group. A resist pattern with a high resolution, reduced LER, improved rectangularity, and minimized influence of develop loading can be formed.

Claims

1. A chemically amplified positive resist composition comprising a base polymer protected with an acid labile group and adapted to turn alkali soluble under the action of acid, wherein said base polymer contains a polymer comprising an acid generating unit, a phenolic hydroxy group-containing unit, a unit containing a phenolic hydroxy group protected with an acid labile group, and a unit containing a carboxy group protected with an acid labile group, or a polymer comprising an acid generating unit, a phenolic hydroxy group-containing unit, and a unit containing a phenolic hydroxy group protected with an acid labile group and a polymer comprising an acid generating unit, a phenolic hydroxy group-containing unit, and a unit containing a carboxy group protected with an acid labile group, the acid generating unit is a repeat unit having any one of the following formulae (A1) to (A8), the phenolic hydroxy group-containing unit is a repeat unit having the following formula (B1), the unit containing a phenolic hydroxy group protected with an acid labile group is a repeat unit having the following formula (B2), and the unit containing a carboxy group protected with an acid labile group is a repeat unit having the following formula (B3), the aromatic ring-containing repeat units account for at least 60 mol % of the overall repeat units of the polymer in said base polymer, ##STR00111## ##STR00112## wherein R.sup.A is each independently hydrogen or methyl, X.sup.1 is a single bond, a C.sub.1-C.sub.6 aliphatic hydrocarbylene group, phenylene group, naphthylene group or C.sub.7-C.sub.18 group obtained by combining the foregoing, *—O—X.sup.11—, *—C(═O)—O—X.sup.11—, or *—C(═O)—NH—X.sup.11—, X.sup.11 is a C.sub.1-C.sub.6 aliphatic hydrocarbylene group, phenylene group, naphthylene group or C.sub.7-C.sub.18 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond or hydroxy moiety, X.sup.2 is a single bond or **—X.sup.21—C(═O)—O—, X.sup.21 is a C.sub.1-C.sub.20 hydrocarbylene group which may contain a heteroatom, X.sup.3 is a single bond, methylene, ethylene, phenylene, fluorinated phenylene, trifluoromethyl-substituted phenylene, *—O—X.sup.31—, *—C(═O)—O—X.sup.31—, or *—C(═O)—NH—X.sup.31—, X.sup.31 is a C.sub.1-C.sub.6 aliphatic hydrocarbylene group, phenylene group, fluorinated phenylene group, trifluoromethyl-substituted phenylene group, or C.sub.7-C.sub.20 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond or hydroxy moiety, *designates a point of attachment to the carbon atom in the backbone, **designates a point of attachment to the oxygen atom in the formula, X.sup.4 is a single bond or C.sub.1-C.sub.30 hydrocarbylene group which may contain a heteroatom, k.sup.1 and k.sup.2 are each independently 0 or 1, k.sup.1 and k.sup.2 are 0 when X.sup.4 is a single bond, R.sup.1 to R.sup.18 are each independently halogen or a C.sub.1-C.sub.20 hydrocarbyl group which may contain a heteroatom R.sup.1 and R.sup.2 may bond together to form a ring with the sulfur atom to which they are attached, R.sup.3 and R.sup.4, R.sup.6 and R.sup.7, or R.sup.9 and R.sup.10 may bond together to form a ring with the sulfur atom to which they are attached, R.sup.HF is hydrogen or trifluoromethyl, and Xa.sup.− is a non-nucleophilic counter ion, ##STR00113## wherein R.sup.B is hydrogen, fluorine, methyl or trifluoromethyl, R.sup.21 is halogen, an optionally halogenated C.sub.2-C.sub.8 saturated hydrocarbylcarbonyloxy group, optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyl group, or optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyloxy group, Y.sup.1 is a single bond, *—C(═O)—O— or *—C(═O)—NH—, *designates a point of attachment to the carbon atom in the backbone, A.sup.1 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group in which any constituent —CH.sub.2— may be replaced by —O—, a is an integer satisfying 0≤a≤5+2c-b, b is an integer of 1 to 3, and c is an integer of 0 to 2. ##STR00114## wherein R.sup.B is as defined above, R.sup.22 is halogen, an optionally halogenated C.sub.2-C.sub.8 saturated hydrocarbylcarbonyloxy group, optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyl group, or optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyloxy group, Y.sup.2 is a single bond, *—C(=O)—O— or *—C(═O)—NH—, *designates a point of attachment to the carbon atom in the backbone, A.sup.2 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group in which any constituent —CH.sub.2— may be replaced by —O—, R.sup.23 is an acid labile group when e is 1, and R.sup.23 is hydrogen or an acid labile group, at least one being an acid labile group, when e is 2 or 3, d is an integer satisfying 0≤d≤5+2f-e, e is an integer of 1 to 3, and f is an integer of 0 to 2, ##STR00115## wherein R.sup.B is as defined above, Y.sup.3 is a single bond, phenylene group, naphthylene group or a C.sub.1-C.sub.12 linking group having an ester bond, ether bond or lactone ring, and R.sup.24 is an acid labile group.

2. The positive resist composition of claim 1 wherein the acid generating unit is a repeat unit having the following formula (A4), the phenolic hydroxy group-containing unit is a repeat unit having the following formula (B1-1), the unit containing a phenolic hydroxy group protected with an acid labile group is a repeat unit having the following formula (B2-1), and the unit containing a carboxy group protected with an acid labile group is a repeat unit having the following formula (B3-1): ##STR00116## wherein R.sup.A, R.sup.B, X.sup.4, R.sup.9, R.sup.10, R.sup.11, b, and k.sup.1 are as defined above, Y.sup.3A is a single bond, phenylene group or naphthylene group, R.sup.25 and R.sup.26 are each independently an acid labile group having a C.sub.6-C.sub.20 aromatic hydrocarbon moiety and/or C.sub.5-C.sub.20 alicyclic hydrocarbon moiety.

3. The positive resist composition of claim 2 wherein said base polymer contains a polymer comprising repeat units having formula (A4), repeat units having formula (B1-1), repeat units having formula (B2-1), and repeat units having formula (B3-1).

4. The positive resist composition of claim 1 wherein the polymer in said base polymer further comprises a repeat unit having any one of the following formulae (C1) to (C3): ##STR00117## wherein R.sup.B is as defined above, g and h are each independently an integer of 0 to 4, i is an integer of 0 to 5, j is an integer of 0 to 2, R.sup.31 and R.sup.32 are each independently a hydroxy group, halogen, an optionally halogenated C.sub.2-C.sub.8 saturated hydrocarbylcarbonyloxy group, optionally halogenated C.sub.1-C.sub.8 saturated hydrocarbyl group, or optionally halogenated C.sub.1-C.sub.8 saturated hydrocarbyloxy group, R.sup.33 is an acetyl group, C.sub.1-C.sub.20 saturated hydrocarbyl group, C.sub.1-C.sub.20 saturated hydrocarbyloxy group, C.sub.2-C.sub.20 saturated hydrocarbylcarbonyloxy group, C.sub.2-C.sub.20 saturated hydrocarbyloxyhydrocarbyl group, C.sub.2-C.sub.20 saturated hydrocarbylthiohydrocarbyl group, halogen, nitro group, or cyano group, R.sup.33 may also be hydroxy when j is 1 or 2, Y.sup.4 is a single bond, *—C(═O)—O— or *—C(═O)—NH—, *designates a point of attachment to the carbon atom in the backbone, A.sup.3 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group in which some constituent —CH.sub.2— may be replaced by —O—.

5. The positive resist composition of claim 1 wherein said base polymer further contains a polymer comprising repeat units having formula (B1) and repeat units of at least one type selected from repeat units having formula (B2) and repeat units having formula (B3), but not repeat units having formula (A1) to (A8).

6. The positive resist composition of claim 1, further comprising a fluorinated polymer comprising repeat units of at least one type selected from repeat units having the following formula (D3), repeat units having the following formula (D4), repeat units having the following formula (D5), and repeat units having the following formula (D6) and optionally repeat units of at least one type selected from repeat units having the following formula (D1) and repeat units having the following formula (D2): ##STR00118## wherein R.sup.C is each independently hydrogen or methyl, R.sup.D is each independently hydrogen, fluorine, methyl or trifluoromethyl, R.sup.101 is hydrogen or a C.sub.1-C.sub.5 straight or branched hydrocarbyl group in which a heteroatom-containing moiety may intervene in a carbon-carbon bond, R.sup.102 is a C.sub.1-C.sub.5 straight or branched hydrocarbyl group in which a heteroatom-containing moiety may intervene in a carbon-carbon bond, R.sup.103 is a C.sub.1-C.sub.20 saturated hydrocarbyl group in which at least one hydrogen atom is substituted by fluorine and in which some constituent —CH.sub.2— may be replaced by an ester bond or ether bond, R.sup.104 , R.sup.105, R.sup.107 and R.sup.108 are each independently hydrogen or a C.sub.1-C.sub.10 saturated hydrocarbyl group, R.sup.106, R.sup.109, R.sup.110 and R.sup.111 are each independently hydrogen, a C.sub.1-C.sub.15 hydrocarbyl group, C.sub.1-C.sub.15 fluorinated hydrocarbyl group, or acid labile group, when R.sup.106, R.sup.109, R.sup.110 and R.sup.111 each are a hydrocarbyl or fluorinated hydrocarbyl group, an ether bond or carbonyl moiety may intervene in a carbon-carbon bond, x is an integer of 1 to 3, y is an integer satisfying 0≤y≤5+2z-x, z is 0 or 1, m is an integer of 1 to 3, Z.sup.1 is a single bond, *—C(═O)—O— or *—C(═O)—O— or *designates a point of attachment to the carbon atom in the backbone, Z.sup.2 is a single bond, —O—, *—C(═O)—O—Z.sup.21—Z.sup.22— or *—C(═O)—NH—Z.sup.21—Z.sup.22—, Z.sup.21 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group, Z.sup.22 is a single bond, ester bond, ether bond or sulfonamide bond, *designates a point of attachment to the carbon atom in the backbone, and Z.sup.3 is a C.sub.1-C.sub.20 (m+1)-valent hydrocarbon group or C.sub.1-C.sub.20 (m+1)-valent fluorinated hydrocarbon group.

7. The positive resist composition of claim 1, further comprising an organic solvent.

8. The positive resist composition of claim 1, further comprising a photoacid generator.

9. The positive resist composition of claim 8 wherein the photoacid generator contains an anion having an acid strength pKa of equal to or more than −2.0.

10. The positive resist composition of claim 1 wherein a resist film formed of the composition has a dissolution rate of at least 50 nm/sec in an over-exposed region.

11. A resist pattern forming process comprising the steps of: applying the chemically amplified positive resist composition of claim 1 onto a substrate to form a resist film thereon, exposing the resist film patternwise to high-energy radiation, and developing the exposed resist film in an alkaline developer.

12. The process of claim 11 wherein the high-energy radiation is EUV or EB.

13. The process of claim 11 wherein the substrate has the outermost surface of a material containing at least one element selected from chromium, silicon, tantalum, molybdenum, cobalt, nickel, tungsten, and tin.

14. The process of claim 11 wherein the substrate is a photomask blank.

15. A photomask blank which is coated with the chemically amplified positive resist composition of claim 1.

Description

DESCRIPTION OF EMBODIMENTS

[0082] As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. “Optional” or “optionally” means that the subsequently described event or circumstances may or may not occur, and that description includes instances where the event or circumstance occurs and instances where it does not. The notation (Cn-Cm) means a group containing from n to m carbon atoms per group. The terms “group” and “moiety” are interchangeable. In chemical formulae, Me stands for methyl, Ac stands for acetyl, and the broken line designates a valence bond.

[0083] The abbreviations and acronyms have the following meaning.

[0084] EB: electron beam

[0085] EUV: extreme ultraviolet

[0086] Mw: weight average molecular weight

[0087] Mu: number average molecular weight

[0088] Mw/Mn: molecular weight distribution or dispersity

[0089] GPC: gel permeation chromatography

[0090] PEB: post-exposure bake

[0091] PAG: photoacid generator

[0092] LER: line edge roughness

[0093] CDU: critical dimension uniformity

[0094] It is understood that for some structures represented by chemical formulae, there can exist enantiomers and diastereomers because of the presence of asymmetric carbon atoms. In such a case, a single formula collectively represents all such isomers. The isomers may be used alone or in admixture.

[0095] The high-energy radiation encompasses UV, deep UV, EB, EUV, X-ray, γ-ray and synchrotron radiation.

Positive Resist Composition

[0096] One embodiment of the invention is a chemically amplified positive resist composition comprising a base polymer which is protected with an acid labile group and adapted to turn alkali soluble under the action of acid.

[0097] The base polymer contains a polymer comprising an acid generating unit, a phenolic hydroxy group-containing emit, a unit containing a phenolic hydroxy group protected with an acid labile group, and a unit containing a carboxy group protected with an acid labile group; or a polymer comprising an acid generating unit, a phenolic hydroxy group-containing unit, and a unit containing a phenolic hydroxy group protected with an acid labile group and a polymer comprising an acid generating unit, a phenolic hydroxy group-containing unit, and a unit containing a carboxy group protected with an acid labile group.

[0098] The acid generating unit is a repeat unit having any one of the following formulae (A1) to (A8). Notably, these repeat units are also referred to as repeat units A1 to A8, respectively, hereinafter.

##STR00009## ##STR00010##

[0099] In formulae (A1) to (A8), R.sup.A is each independently hydrogen or methyl. X.sup.1 is a single bond, a C.sub.1-C.sub.6 aliphatic hydrocarbylene group, phenylene group, naphthylene group or C.sub.7-C.sub.18 group obtained by combining the foregoing, *—O—X.sup.11—, *—C(═O)—O—X.sup.11—, or *—C(═O)—NH—X.sup.11—. X.sup.11 is a C.sub.1-C.sub.6 aliphatic hydrocarbylene group, phenylene group, naphthylene group or C.sub.7-C.sub.18 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond or hydroxy moiety. X.sup.2 is a single bond or **—X.sup.21—C(═O)—O—. X.sup.21 is a C.sub.1-C.sub.20 hydrocarbylene group which may contain a heteroatom. X.sup.3 is a single bond, methylene, ethylene, phenylene, fluorinated phenylene, trifluoromethyl-substituted phenylene, *—O—X.sup.31—, *—C(═O)—O—X.sup.31—, or *—C(═O)—NH—X.sup.31—. X.sup.31 is a C.sub.1-C.sub.6 aliphatic hydrocarbylene group, phenylene group, fluorinated phenylene group, trifluoromethyl-substituted phenylene group, or C.sub.7-C.sub.20 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond or hydroxy moiety. The asterisk (*) designates a point of attachment to the carbon atom in the backbone, and the double asterisk (**) designates a point of attachment to the oxygen atom in the formula. X.sup.4 is a single bond or C.sub.1-C.sub.30 hydrocarbylene group which may contain a heteroatom. The subscripts k.sup.1 and k.sup.2 are each independently 0 or 1, k.sup.1 and k.sup.2 are 0 when X.sup.4 is a single bond.

[0100] The repeat unit having formula (A4) or (A8) is a unit which generates an acid upon exposure to high-energy radiation, the acid having a sulfonyl group and being difluoromethylated at β-position thereof. The acid has an acid strength adequate for the deprotection of a polymer comprising units having a phenolic hydroxy group protected with an acetal, tertiary alkyl or tert-butoxycarbonyl group. When a polymer comprising the repeat unit is used as a base polymer in a resist composition, it is possible to properly control the movement and diffusion of the generated acid.

[0101] A photoacid generator capable of generating an arene sulfonic acid upon exposure to high-energy radiation is also commonly used for the deprotection of a polymer comprising units having a phenolic hydroxy group protected with an acetal, tertiary alkyl or tert-butoxycarbonyl group. However, when an arene sulfonic acid-generating unit is introduced as the repeat unit in a base polymer with the intention of attaining the same effect as in the present invention, the resulting base polymer is not always dissolvable in a solvent because of low solvent solubility. In contrast, the polymer comprising repeat units having formula (A4) or (A8) is fully lipophilic and easy to prepare and handle, and a resist composition is readily prepared therefrom.

[0102] In formulae (A2) and (A6), X.sup.2 is a single bond or **—X.sup.21—C(═O)—O— wherein X.sup.21 is a C.sub.1-C.sub.20 hydrocarbylene group which may contain a heteroatom. Examples of the hydrocarbylene group X.sup.21 are given below, but not limited thereto.

##STR00011##

[0103] In formulae (A2) and (A6), R.sup.HF is hydrogen or trifluoromethyl. Examples of the repeat units A2 and A6 wherein R.sup.HF is hydrogen are as exemplified in U.S. Pat. No. 8,105,748 (JP-A 2010-116550). Examples of the repeat units A2 and A6 wherein R.sup.HF is trifluoromethyl are as exemplified in U.S. Pat. No. 8,057,985 (JP-A 2010-077404). Examples of the repeat units A3 and A7 are as exemplified in U.S. Pat. No. 8,835,097 (JP-A 2012-246265) and U.S. Pat. No. 8,900,793 (JP-A 2012-246426).

[0104] In formulae (A1) and (A5), Xa.sup.− is a non-nucleophilic counter ion. Examples of the non-nucleophilic counter ion Xa.sup.− are as exemplified in U.S. Pat. No. 8,349,533 (JP-A 2010-113209) and U.S. Pat. No. 7,511,169 (JP-A 2007-145797).

[0105] In formulae (A4) and (A8), X.sup.4 is a single bond or C.sub.1-C.sub.30 hydrocarbylene group which may contain a heteroatom. The hydrocarbylene group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include alkanediyl groups such as methanediyl, ethane-1,2-diyl, propane-1,3-diyl, butane-1,4-diyl, pentane-1,5-diyl, hexane-1,6-diyl, heptane-1,7-diyl, octane-1,8-diyl, nonane-1,9-diyl, decane-1,10-diyl, undecane-1,11-diyl, dodecane-1,12-diyl, tridecane-1,13-diyl, tetradecane-1,14-diyl, pentadecane-1,15-diyl, hexadecane-1,16-diyl, and heptadecane-1,17-diyl; cyclic saturated hydrocarbylene groups such as cyclopentanediyl, cyclohexanediyl, norbornanediyl, and adamantanediyl; arylene groups such as phenylene, methylphenylene, ethylphenylene, n-propylphenylene, isopropylphenylene, n-butylphenylene, isobutylphenylene, sec-butylphenylene, tert-butylphenylene, naphthylene, methylnaphthylene, ethylnaphthylene, n-propylnaphthylene, isopropylnaphthylene, n-butylnaphthylene, isobutylnaphthylene, sec-butylnaphthylene, and tert-butylnaphthylene; and combinations thereof.

[0106] In the hydrocarbylene group, some or all of the hydrogen atoms may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen and some constituent —CH.sub.2— may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy moiety, cyano moiety, fluorine, chlorine, bromine, iodine, carbonyl moiety, ether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride, or haloalkyl moiety.

[0107] Preferred examples of the anion in the monomer from which repeat units A4 and A8 are derived are shown below, but not limited thereto.

##STR00012## ##STR00013##

[0108] In formulae (A1) to (A8), R.sup.1 to R.sup.18 are each independently halogen or a C.sub.1-C.sub.20 hydrocarbyl group which may contain a heteroatom.

[0109] Suitable halogen atoms include fluorine, chlorine, bromine and iodine. The C.sub.1-C.sub.20 hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C.sub.1-C.sub.20 alkyl groups such as methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-pentyl, n-pentyl, n-hexyl, n-octyl, 2-ethylhexyl, n-nonyl and n-decyl: C.sub.3-C.sub.20 cyclic saturated hydrocarbyl groups such as cyclopentyl, cyclohexyl, cyclopentylmethyl, cyclopentylethyl, cyclopentylbutyl, cyclohexylmethyl, cyclohexylethyl, cyclohexylbutyl, norbornyl, tricyclo[5.2.1.0.sup.2.6]decanyl, adamantyl, and adamantylmethyl; and C.sub.6-C.sub.20 aryl groups such as phenyl, naphthyl and anthracenyl. In the hydrocarbyl groups, some or all of the hydrogen atoms may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, and a moiety containing a heteroatom such as oxygen, sulfur or nitrogen may intervene in a carbon-carbon bond, so that the group may contain a hydroxy, fluorine, chlorine, bromine, iodine, cyano, carbonyl, ether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride or haloalkyl.

[0110] Also, R.sup.1 and R.sup.2 may bond together to form a ring with the sulfur atom to which they are attached, R.sup.3 and R.sup.4, R.sup.6 and R.sup.7, or R.sup.9 and R.sup.10 may bond together to form a ring with the sulfur atom to which they are attached. Examples of the ring are shown below.

##STR00014##

[0111] Exemplary structures of the sulfonium cation in formulae (A2) to (A4) are shown below, but not limited thereto.

##STR00015## ##STR00016## ##STR00017## ##STR00018## ##STR00019## ##STR00020## ##STR00021## ##STR00022## ##STR00023## ##STR00024## ##STR00025## ##STR00026## ##STR00027## ##STR00028## ##STR00029## ##STR00030## ##STR00031## ##STR00032##

[0112] Exemplary structures of the iodonium cation in formulae (A5) to (A8) are shown below, but not limited thereto.

##STR00033## ##STR00034## ##STR00035## ##STR00036##

[0113] Of the repeat units A1 to A8, repeat unit A4 is preferred for the processing of photomask blanks because its acid strength is most appropriate in designing the acid-labile eliminating group on a polymer.

[0114] The repeat units A1 to A8 are capable of generating an acid upon exposure to high-energy radiation. The acid-generating units bound to a polymer enable to appropriately control acid diffusion and hence, to form a pattern with reduced LER. Since the acid-generating unit is bound to a polymer, the phenomenon that acid volatilizes from the exposed region and re-deposits on the unexposed region during bake in vacuum is suppressed. This is effective for reducing LER and for mitigating any geometric degradation due to unwanted film thickness reduction in the unexposed region.

[0115] The repeat units A1 to A8 are preferably incorporated in a range of 0.1 to 30 mol %, more preferably 0.5 to 20 mol % based on the overall repeat units of the polymer in the base polymer. The repeat units A1 to A8 used herein may be of one type or a mixture of two or more types.

[0116] The phenolic hydroxy group-containing unit is a repeat unit having the following formula (B1), which is also referred to as repeat unit B1, hereinafter.

##STR00037##

[0117] In formula (B1), R.sup.B is hydrogen, fluorine, methyl or trifluoromethyl.

[0118] In formula (B1), R.sup.21 is halogen, an optionally halogenated C.sub.2-C.sub.8 saturated hydrocarbylcarbonyloxy group, optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyl group, or optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyloxy group. The saturated hydrocarbyl group and saturated hydrocarbyl moiety in the saturated hydrocarbylcarbonyloxy group and saturated hydrocarbyloxy group may be straight, branched or cyclic, and examples thereof include alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl, pentyl, and hexyl, cycloalkyl groups such as cyclopropyl, cyclobutyl, cyclopentyl and cyclohexyl, and combinations thereof. A carbon count within the upper limit ensures good solubility in alkaline developer. Groups R.sup.21 may be identical or different when “a” is 2 or more.

[0119] In formula (B1), Y.sup.1 is a single bond, *—C(═O)—O— or *—C(═O)—NH—. The asterisk (*) designates a point of attachment to the carbon atom in the backbone.

[0120] In formula (B1), A.sup.1 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group in which any constituent —CH.sub.2— may be replaced by —O—. The saturated hydrocarbylene group may be straight, branched or cyclic and examples thereof include C.sub.1-C.sub.10 alkanediyl groups such as methylene, ethane-1,2-diyl, propane-1,3-diyl, butane-1,4-diyl, pentane-1,5-diyl, hexane-1,6-diyl, and structural isomers thereof: C.sub.3-C.sub.10 cyclic saturated hydrocarbylene groups such as cyclopropanediyl, cyclobutanediyl, cyclopentanediyl, and cyclohexanediyl; and combinations thereof.

[0121] In formula (B1), “a” is an integer satisfying 0≤a≤5+2c-b, b is an integer of 1 to 3, and c is an integer of 0 to 2.

[0122] Preferred examples of the repeat unit B1 wherein both Y.sup.1 and A.sup.1 are a single bond include units derived from 3-hydroxystyrene, 4-hydroxystyrene, 5-hydroxy-2-vinylnaphthalene, and 6-hydroxy-2-vinylnaphthalene. Of these, repeat units having the formula (B1-1) are more preferred.

##STR00038##

Herein R.sup.B and b are as defined above.

[0123] Preferred examples of the repeat unit B1 wherein Y.sup.1 is other than a single bond are shown below, but not limited thereto. Herein R.sup.B is as defined above.

##STR00039## ##STR00040## ##STR00041##

[0124] The repeat units B1 are preferably incorporated in a range of 10 to 95 mol %, more preferably 30 to 85 mol % based on the overall repeat units of the polymer in the base polymer. It is noted that when the polymer contains additional repeat units of at least one type selected from repeat units having formulae (B3) and (B4) contributing to high etching resistance, the additional repeat units having a phenolic hydroxy group as a substituent group, the sum of repeat units B1 and additional repeat units preferably falls in the above range. The repeat units B1 used herein may be of one type or a mixture of two or more types.

[0125] The unit containing a phenolic hydroxy group protected with an acid labile group is a repeat unit having the following formula (B2), also referred to as repeat unit B2, hereinafter.

##STR00042##

[0126] In formula (B2), R.sup.B is as defined above. R.sup.22 is halogen, an optionally halogenated C.sub.2-C.sub.8 saturated hydrocarbylcarbonyloxy group, optionally halogenated C.sub.1-C.sub.6 saturated hydrocarbyl group, or optionally halogenated C.sub.1-.sub.6 saturated hydrocarbyloxy group. The saturated hydrocarbyl group and saturated hydrocarbyl moiety in the saturated hydrocarbylcarbonyloxy group and saturated hydrocarbyloxy group may be straight, branched or cyclic, and examples thereof are as exemplified above for R.sup.21 in formula (B1). A carbon count within the upper limit ensures good solubility in alkaline developer. Groups R.sup.22 may be identical or different when d is 2 or more.

[0127] In formula (B2), Y.sup.2 is a single bond, *—C(═O)—O— or *—C(═O)—NH—. The asterisk (*) designates a point of attachment to the carbon atom in the backbone.

[0128] In formula (B2), A.sup.2 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group in which any constituent —CH.sub.2— may be replaced by —O—. The saturated hydrocarbylene group may be straight, branched or cyclic, and examples thereof are as exemplified above for A.sup.1 in formula (B1).

[0129] In formula (B2), R.sup.23 is an acid labile group when e=1. R.sup.23 is hydrogen or an acid labile group, at least one being an acid labile group, when e=2 or 3.

[0130] In formula (B2), d is an integer satisfying 0≤d≤5+2f-e, e is an integer of 1 to 3, and f is an integer of 0 to 2.

[0131] The unit containing a carboxy group protected with an acid labile group is a repeat unit having the following formula (B3), also referred to as repeat unit B3, hereinafter.

##STR00043##

[0132] In formula (B3), R.sup.B is as defined above. Y.sup.3 is a single bond, phenylene group, naphthylene group or a C.sub.1-C.sub.12 linking group having an ester bond, ether bond or lactone ring. R.sup.24 is an acid labile group. The acid labile group represented by R.sup.23 and R.sup.24 is not particularly limited as long as it is eliminated under the action of acid, leaving an acidic group. It may be any of acid labile groups which are commonly used in many well-known chemically amplified resist compositions.

[0133] The repeat unit B2 is a unit having a phenolic hydroxy group whose hydrogen is substituted by an acid labile group, preferably a unit derived from hydroxystyrene or hydroxyphenyl (meth)acrylate in which the hydrogen atom of the hydroxy group is substituted by an acid labile group. Examples of the monomer from which repeat unit B2 is derived are shown below, but not limited thereto. Herein R.sup.B and R.sup.23 are as defined above.

##STR00044##

[0134] The repeat unit B3 is a unit having a carboxy group whose hydrogen is substituted by an acid labile group, preferably a unit derived from a hydroxy-containing (meth)acrylate in which the hydrogen atom of the hydroxy group is substituted by an acid labile group. Examples of the monomer from which repeat unit B3 is derived are shown below, but not limited thereto. Herein R.sup.B and R.sup.24 are as defined above.

##STR00045## ##STR00046## ##STR00047## ##STR00048##

[0135] Examples of the acid labile groups R.sup.23 and R.sup.24 include those described in U.S. Pat. No. 9,164,392 (JP-A 2014-219657, paragraphs [0030]-[0082]).

[0136] Of the acid labile groups, groups having the following formulae (AL-1) to (AL-19) are preferred.

##STR00049## ##STR00050## ##STR00051##

[0137] In formulae (AL-1) to (AL-19), R.sup.L1 is each independently a saturated hydrocarbyl group or C.sub.6-C.sub.20 aryl group. R.sup.L2 and R.sup.L4 are each independently hydrogen or a C.sub.1-C.sub.20 saturated hydrocarbyl group. R.sup.L3 is a C.sub.6-C.sub.20 aryl group. The saturated hydrocarbyl group may be straight, branched or cyclic. Typical of the aryl group is phenyl. R.sup.F is fluorine or trifluoromethyl. The subscript n is an integer of 1 to 5.

[0138] It is preferred to select a tertiary hydrocarbyl group as the acid labile group because a pattern with reduced LER is obtained even when a resist film is formed to a thickness of 10 to 100 nm and exposed to a small size pattern of light so as to provide a line width of 45 nm or less. The tertiary hydrocarbyl group is preferably of 4 to 18 carbon atoms because a monomer for polymerization is collectable through distillation. The group attached to the tertiary carbon atom in the tertiary hydrocarbyl group is typically a C.sub.1-.sub.20 saturated hydrocarbyl group which may contain an oxygen-containing functional group such as an ether bond or carbonyl group while the groups attached to the tertiary carbon atom may bond together to form a ring.

[0139] Examples of the group attached to the tertiary carbon atom include methyl, ethyl, propyl, adamantyl, norbornyl, tetrahydrofuran-2-yl, 7-oxanorbornan-2-yl, cyclopentyl, 2-tetrahydrofuryl, tricyclo[5.2.1.0.sup.2,6]decyl, tetracyclo[4.4.0.1.sup.2.5.1.sup.7,10]dodecyl, and 3-oxo-1-cyclohexyl.

[0140] Examples of the tertiary hydrocarbyl group include tert-butyl, tert-pentyl, 1-ethyl-1-methylpropyl, 1,1-diethylpropyl, 1,1,2-trimethylpropyl, 1-adamantyl-1-methylethyl, 1-methyl-1-(2-norbornyl)ethyl, 1-methyl-1-(tetrahydrofuran-2-yl)ethyl, 1-methyl-1-(7-oxanorbornan-2-yl)ethyl, 1 -methylcyclopentyl, 1-ethylcyclopentyl, 1-propylcyclopentyl, 1-isopropylcyclopentyl, 1-cyclopentylcyclopentyl, 1-cyclohexylcyclopentyl, 1-(2-tetrahydrofuryl)cyclopentyl, 1-(7-oxanorbornan-2-yl)cyclopentyl, 1-methylcyclohexyl, 1-ethylcyclohexyl, 1-isopropylcyclohexyl, 1-cyclopentylcyclohexyl, 1-cyclohexylcyclohexyl, 2-methyl-2-norbornyl, 2-ethyl-2-norbornyl, 8-methyl-8-tricyclo[5.2.1.0.sup.26]decyl, 8-ethyl-8-tricyclo[5.2.1.0.sup.2,6]decyl, 3-methyl-3-tetracyclo[4.4.0.1.sup.2,5.1.sup.7.10]dodecyl, 3-ethyl-3-tetracyclo[4.4.0.1.sup.2,5.1.sup.7,10]dodecyl, 3-isopropyl-3-tetracyclo[4.4.0.1.sup.2,5.1.sup.7,10]dodecyl, 2-methyl-2-adamantyl, 2-ethyl-2-adamantyl, 2-isopropyl-2-adamantyl, 1-methyl-3-oxo-1-cyclohexyl, 1-methyl-1-(tetrahydrofuran-2-yl)ethyl, 5-hydroxy-2-methyl-2-adamantyl, 5-hydroxy-2-ethyl-2-adamantyl, and 2-(4-fluorophenyl)-2-propyl.

[0141] Also, an acetal group having the formula (AL-20) is often used as the acid labile group. It is a good choice of acid labile group that ensures to form a pattern having a relatively rectangular interface between pattern features and the substrate.

##STR00052##

[0142] In formula (AL-20), R.sup.LS is hydrogen or a C.sub.1-C.sub.10 saturated hydrocarbyl group. R.sup.L6 is a C.sub.1-C.sub.30 saturated hydrocarbyl group.

[0143] R.sup.L5 is selected in accordance with how to design the sensitivity of the labile group to acid. For example, hydrogen is selected for the design that the group having a relatively high stability is decomposed with a strong acid. A straight alkyl group is selected for the design that utilizes a relatively high reactivity to provide a high sensitivity relative to pH changes. Depending on a combination with an acid generator and a basic compound blended in a resist composition, a hydrocarbyl group in which the carbon attached to the acetal carbon is a secondary carbon atom is preferably selected as R.sup.L5 for the design that is substituted at an end with a relatively higher alkyl group as R.sup.L6 and experiences a large solubility change upon decomposition. Examples of the group RL.sup.5 attached to the acetal carbon via a secondary carbon atom include isopropyl, sec-butyl, cyclopentyl and cyclohexyl.

[0144] Of the acetal groups, those groups wherein R.sup.L6 is a C.sub.7-C.sub.30 polycyclic alkyl group are preferred in order to gain a higher resolution. When R.sup.L6 is a polycyclic alkyl group, it is preferred that the secondary carbon in the polycyclic structure form a bond with the acetal oxygen. A polymer relying on an attachment on the secondary carbon atom in the cyclic structure is stable as compared with an attachment on the tertiary carbon atom, ensuring that the resist composition is improved in shelf stability and not degraded in resolution. The polymer has a high glass transition temperature (Tg) as compared with the case wherein R.sup.L6 is attached on the primary carbon atom via a straight alkyl group of at least one carbon atom, so that the resist pattern after development may not undergo geometrical failure during bake.

[0145] Preferred examples of the group having formula (AL-20) are shown below, but not limited thereto. Herein R.sup.L5 is as defined above.

##STR00053##

[0146] Of the repeat units B2, units having the formula (B2-1) are preferred. Of the repeat units B3, units having the formula (B3-1) are preferred.

##STR00054##

[0147] Herein R.sup.B is as defined above. Y.sup.3A is a single bond, phenylene group or naphthylene group. R.sup.25 and R.sup.26 are each independently an acid labile group having a C.sub.6-C.sub.20 aromatic hydrocarbon moiety and/or C.sub.5-C.sub.20 alicyclic hydrocarbon moiety.

[0148] The repeat units B2 are preferably incorporated in a range of 2 to 40 mol % based on the overall repeat units of the polymer in the base polymer. The repeat units B3 are preferably incorporated in a range of 2 to 40 mol % based on the overall repeat units of the polymer in the base polymer. The sum of repeat units B2 and B3 is preferably incorporated in a range of 5 to 60 mol % based on the overall repeat units of the polymer in the base polymer.

[0149] Where the base polymer is of the design that it is a mixture of repeat units of two types in which a phenolic hydroxy group and a carboxy group are protected with acid labile groups, the influence of develop loading is suppressed because the dissolution rate of exposed region is improved due to the carboxylate framework while maintaining pattern robustness due to the phenol framework, and the dissolution contrast between exposed and unexposed regions is optimized while maintaining a satisfactory resolution in the exposed region. As a consequence, a pattern with a minimal size difference is obtained independent of pattern density. In the fabrication of photomasks wherein the development conditions employed therein are stronger than in the processing of wafer substrates, it is required to form a pattern with a minimal size difference while maintaining a satisfactory resolution and suppressing the influence of develop loading. Then the chemically amplified positive resist composition of the invention is best suited for the processing of photomask substrates.

[0150] In a preferred embodiment, the polymer in the base polymer further comprises repeat units of at least one type selected from repeat units having the formula (C1), repeat units having the formula (C2), and repeat units having the formula (C3), which are also referred to as repeat units C1, C2 and C3, respectively.

##STR00055##

[0151] In formulae (C1) and (C2), g and h are each independently an integer of 0 to 4.

[0152] In formulae (C1) and (C2), R.sup.31 and R.sup.32 are each independently a hydroxy group, halogen, an optionally halogenated C.sub.2-C.sub.8 saturated hydrocarbylcarbonyloxy group, optionally halogenated C.sub.1-C.sub.8 saturated hydrocarbyl group, or optionally halogenated C.sub.1-C.sub.8 saturated hydrocarbyloxy group. The saturated hydrocarbyl group, saturated hydrocarbyloxy group and saturated hydrocarbylcarbonyloxy group may be straight, branched or cyclic. Groups R.sup.31 may be identical or different when g is 2 or more. Groups R.sup.32 may be identical or different when h is 2 or more.

[0153] In formula (C3), R.sup.B is as defined above, i is an integer of 0 to 5, and j is an integer of 0 to 2.

[0154] In formula (C3), R.sup.33 is an acetyl group, C.sub.1-C.sub.20 saturated hydrocarbyl group, C.sub.1-C.sub.20 saturated hydrocarbyloxy group, C.sub.2-C.sub.20 saturated hydrocarbylcarbonyloxy group, C.sub.2-C.sub.20 saturated hydrocarbyloxyhydrocarbyl group, C.sub.2-C.sub.20 saturated hydrocarbylthiohydrocarbyl group, halogen, nitro group, or cyano group. R.sup.33 may also be hydroxy when j is 1 or 2. The saturated hydrocarbyl group, saturated hydrocarbyloxy group, saturated hydrocarbylcarbonyloxy group, saturated hydrocarbyloxyhydrocarbyl group and saturated hydrocarbylthiohydrocarbyl group may be straight, branched or cyclic. Groups R.sup.33 may be identical or different when i is 2 or more.

[0155] In formula (C3), Y.sup.4 is a single bond, *—C(═O)—O— or *—C(═O)—NH—. The asterisk (*) designates a point of attachment to the carbon atom in the backbone. In formula (C3), A.sup.3 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group in which some constituent —CH.sub.2— may be replaced by —O—. The saturated hydrocarbylene group may be straight, branched or cyclic and examples thereof are as exemplified for A.sup.1 in formula (B1).

[0156] When repeat units of at least one type selected from repeat units C1 to C3 are incorporated, better performance is obtained because not only the aromatic ring possesses etch resistance, but the cyclic structure incorporated into the main chain also exerts the effect of improving resistance to etching and EB irradiation during pattern inspection step.

[0157] The repeat units C1 to C3 are preferably incorporated in a range of at least 5 mol % based on the overall repeat units of the polymer in the base polymer for obtaining the effect of improving etch resistance. Also, the repeat units C1 to C3 are preferably incorporated in a range of up to 35 mol %, more preferably up to 30 mol % based on the overall repeat units of the polymer in the base polymer. When the repeat units C1 to C3 are incorporated, their content of up to 35 mol % is preferred because the risk of forming development defects is eliminated. Each of the repeat units C1 to C3 may be of one type or a combination of plural types.

[0158] The total content of repeat units B1, repeat units B2, repeat units B3, and repeat units of at least one type selected from repeat units C1 to C3 is preferably at least 60 mol %, more preferably at least 70 mol % based on the overall repeat units of the polymer in the base polymer.

[0159] The polymer may further comprise (meth)acrylate units protected with an acid labile group and/or (meth)acrylate units having an adhesive group such as a lactone structure or a hydroxy group other than phenolic hydroxy, as commonly used in the art. These repeat units are effective for fine adjustment of properties of a resist film, but not essential.

[0160] Examples of the (meth)acrylate unit having an adhesive group include repeat units having the following formula (C4), repeat units having the following formula (C5), and repeat units having the following formula (C6), which are also referred to as repeat units C4, C5, and C6, respectively. While these units do not exhibit acidity, they may be used as auxiliary units for providing adhesion to substrates or adjusting solubility.

##STR00056##

[0161] In formulae (C4) to (C6), R.sup.B is as defined above. R.sup.34 is —O— or methylene. R.sup.35 is hydrogen or hydroxy. R.sup.36 is a C.sub.1-C.sub.4 saturated hydrocarbyl group, and k is an integer of 0to 3.

[0162] When the repeat units C4 to C6 are included, their content is preferably 0 to 30 mol %, more preferably 0 to 20 mol % based on the overall repeat units of the polymer. Each of the repeat units C4 to C6 may be of one type or a combination of plural types.

[0163] In another embodiment, the base polymer is a mixture of a polymer containing repeat units A1 to A8 and a polymer not containing repeat units A1 to A8, specifically a polymer containing repeat units of at least one type selected from repeat units having formula (B1), repeat units having formula (B2), and repeat units having formula (B3), but not repeat units A1 to A8. The mixture preferably consists of 100 parts by weight of the polymer containing repeat units A1 to A8 and 2 to 5,000 parts by weight, more preferably 10 to 1,000 parts by weight of the polymer not containing repeat units A1 to A8.

[0164] The polymer may be synthesized by combining suitable monomers optionally protected with a protective group, copolymerizing them in the standard way, and effecting deprotection reaction if necessary. The copolymerization reaction is preferably radical or anionic polymerization though not limited thereto. For the polymerization reaction, reference may be made to JP-A 2004-115630, for example.

[0165] The polymer should preferably have a Mw of 1,000 to 50,000, and more preferably 2,000 to 20,000. A Mw of at least 1,000 eliminates the risk that pattern features are rounded at their top, inviting degradations of resolution and LER. A Mw of up to 50,000 eliminates the risk that LER is degraded when a pattern with a line width of up to 100 nm is formed. As used herein, Mw is measured by GPC versus polystyrene standards using tetrahydrofuran (THF) or dimethylformamide (DMF) solvent.

[0166] The polymer preferably has a narrow molecular weight distribution or dispersity (Mw/Mn) of 1.0 to 2.0, more preferably 1.0 to 1.9, even more preferably 1.0 to 1.8. A polymer with such a narrow dispersity eliminates the risk that foreign particles are left on the pattern after development and the pattern profile is aggravated.

[0167] The base polymer is designed such that the dissolution rate in alkaline developer is preferably up to 8 nm/min, more preferably up to 6 nm/min even more preferably up to 5 nm/min. In the advanced generation of lithography wherein the coating film on the substrate is in a thin film range of up to 100 nm, the influence of pattern film thickness loss during alkaline development becomes strong. When the polymer has an alkaline dissolution rate of greater than 8 nm/min, pattern collapse occurs, i.e., a small size pattern cannot be formed. The problem becomes outstanding in the fabrication of photomasks requiring to be defectless and having a tendency of strong development process. It is noted that the dissolution rate of a base polymer in alkaline developer is computed by spin coating a 16.7 wt % solution of a polymer in propylene glycol monomethyl ether (PGME) solvent onto a 8-inch silicon wafer, baking at 100° C. for 90 seconds to form a film of 1,000 nm thick, developing the film in a 2.38 wt % aqueous solution of tetramethylammonium hydroxide (TMAH) at 23° C. for 100 seconds, and measuring a loss of film thickness.

Fluorinated Polymer

[0168] The positive resist composition may further comprise a fluorinated polymer which contains repeat units of at least one type selected from repeat units having the formula (D3), repeat units having the formula (D4), repeat units having the formula (D5), and repeat units having the formula (D6), and which may contain repeat units of at least one type selected from repeat units having the formula (D1) and repeat units having the formula (D2), for the purposes of enhancing contrast, preventing chemical flare of acid upon exposure to high-energy radiation, preventing mixing of acid from an anti-charging film in the step of coating an anti-charging film-forming material on a resist film, and suppressing unexpected unnecessary pattern degradation. It is noted that repeat units having formulae (D1), (D2), (D3), (D4), (D5), and (D6) are also referred to as repeat units D1, D2, D3, D4, D5, and D6, respectively, hereinafter. Since the fluorinated polymer also has a surface active function, it can prevent insoluble residues from re-depositing onto the substrate during the development step and is thus effective for preventing development defects.

##STR00057##

[0169] In formulae (D1) to (D6), R.sup.C is each independently hydrogen or methyl. R.sup.D is each independently hydrogen, fluorine, methyl or trifluoromethyl. R.sup.101 is hydrogen or a C.sub.1-C.sub.5 straight or branched hydrocarbyl group in which a heteroatom-containing moiety may intervene in a carbon-carbon bond. R.sup.102 is a C.sub.1-C.sub.5 straight or branched hydrocarbyl group in which a heteroatom-containing moiety may intervene in a carbon-carbon bond. R.sup.103 is a C.sub.1-C.sub.20 saturated hydrocarbyl group in which at least one hydrogen is substituted by fluorine and some constituent —CH.sub.2— may be replaced by an ester bond or ether bond. R.sup.104, R.sup.105, R.sup.107 and R.sup.108 are each independently hydrogen or a C.sub.1-C.sub.10 saturated hydrocarbyl group. R.sup.106, R.sup.109, R.sup.110 and R.sup.111 are each independently hydrogen, a C.sub.1-C.sub.15 hydrocarbyl group or fluorinated hydrocarbyl group, or an acid labile group, with the proviso that an ether bond or carbonyl moiety may intervene in a carbon-carbon bond in the hydrocarbyl groups or fluorinated hydrocarbyl groups represented by R.sup.106, R.sup.109, R.sup.110 and R.sup.111. The subscript x is an integer of 1 to 3, y is an integer satisfying: 0≤y≤5+2z-x, z is 0 or 1, and m is an integer of 1 to 3. Z′ is a single bond, *—C(═O)—O— or *—C(═O)—NH— wherein the asterisk (*) designates a point of attachment to the carbon atom in the backbone. Z.sup.2 is a single bond, —O—, *—C(═O)—O—Z.sup.21—Z.sup.22— or *—C(═O)—NH—Z.sup.21—Z.sup.22—, wherein Z.sup.21 is a single bond or a C.sub.1-C.sub.10 saturated hydrocarbylene group, Z.sup.22 is a single bond, ester bond, ether bond or sulfonamide bond, and the asterisk (*) designates a point of attachment to the carbon atom in the backbone. Z.sup.3 is a C.sub.1-C.sub.20 (m+1)-valent hydrocarbon group or C.sub.1-C.sub.20 (m+1)-valent fluorinated hydrocarbon group.

[0170] Examples of the C.sub.1-C.sub.5 hydrocarbyl groups R.sup.101 and R.sup.102 include alkyl, alkenyl and alkynyl groups, with the alkyl groups being preferred. Suitable alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, and n-pentyl. In these groups, a moiety containing a heteroatom such as oxygen, sulfur or nitrogen may intervene in a carbon-carbon bond.

[0171] In formula (D1), —OR.sup.101 is preferably a hydrophilic group. In this case, R.sup.101 is preferably hydrogen or a C.sub.1-C.sub.5 alkyl group in which oxygen intervenes in a carbon-carbon bond.

[0172] Examples of the repeat unit D1 are given below, but not limited thereto. Herein R.sup.C is as defined above.

##STR00058## ##STR00059## ##STR00060## ##STR00061##

[0173] Z.sup.1 is preferably *—C(═O)—O— or *—C(═O)—NH—. Also preferably R.sup.C is methyl. The inclusion of carbonyl in Z.sup.1 enhances the ability to trap the acid originating from the anti-charging film. A polymer wherein R.sup.C is methyl is a robust polymer having a high Tg which is effective for suppressing acid diffusion. As a result, the resist film is improved in stability with time, and neither resolution nor pattern profile is degraded.

[0174] The C.sub.1-C.sub.10 saturated hydrocarbylene group Z.sup.21 may be straight, branched or cyclic and examples thereof include methanediyl, ethane-1,1-diyl, ethane-1,2-diyl, propane-1,1-diyl, propane-1,2-diyl, propane-1,3-diyl, propane-2,2-diyl, butane-1,1-diyl, butane-1,2-diyl, butane-1,3-diyl, butane-2,3-diyl, butane-1,4-diyl, and 1,1-dimethylethane-1,2-diyl.

[0175] The C.sub.1-C.sub.20 saturated hydrocarbyl group having at least one hydrogen substituted by fluorine, represented by R.sup.103, may be straight, branched or cyclic and examples thereof include the alkyl and cyclic saturated hydrocarbyl groups exemplified above for the hydrocarbyl groups R.sup.1 to R.sup.18 in formulae (A1) to (A8), with at least one hydrogen being substituted by fluorine.

[0176] Examples of the repeat unit D2 are given below, but not limited thereto. Herein R.sup.C is as defined above.

##STR00062## ##STR00063##

[0177] Examples of the C.sub.1-C.sub.10 saturated hydrocarbyl group represented by R.sup.104, R.sup.105, R.sup.107 and R.sup.108 include alkyl groups such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, and n-decyl, and cyclic saturated hydrocarbyl groups such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, adamantyl, and norbornyl. Inter alia, C.sub.1-C.sub.6 saturated hydrocarbyl groups are preferred.

[0178] Examples of the C.sub.1-C.sub.15 hydrocarbyl group represented by R.sup.106, R.sup.109, R.sup.110 and R.sup.111 include alkyl, alkenyl and alkynyl groups, with the alkyl groups being preferred. Suitable alkyl groups include n-undecyl, n-dodecyl, tridecyl, tetradecyl and pentadecyl as well as those exemplified above. The fluorinated hydrocarbyl groups correspond to the foregoing hydrocarbyl groups in which some or all carbon-bonded hydrogen atoms are substituted by fluorine atoms.

[0179] Examples of the C.sub.1-C.sub.20 (m+1)-valent hydrocarbon group or fluorinated hydrocarbon group Z.sup.3 include the foregoing hydrocarbyl groups and fluorinated hydrocarbyl groups, with m number of hydrogen atoms being eliminated.

[0180] Examples of the repeat units D3 to D6 are given below, but not limited thereto. Herein R.sup.D is as defined above.

##STR00064## ##STR00065## ##STR00066## ##STR00067##

[0181] The repeat unit D1 and/or D2 is preferably incorporated in an amount of 5 to 85 mol %, more preferably 15 to 80 mol % based on the overall repeat units of the fluorinated polymer. The repeat units D3 to D6 are preferably incorporated in an amount of 15 to 95 mol %, more preferably 20 to 85 mol % based on the overall repeat units of the fluorinated polymer. Each of repeat units D1 to D6 may be used alone or in admixture.

[0182] The fluorinated polymer may comprise additional repeat units as well as the repeat units D1 to D6. Suitable additional repeat units include those described in U.S. Pat. No. 9,091,918 (JP-A 2014-177407, paragraphs [0046]-[0078]). When the fluorinated polymer comprises additional repeat units, their content is preferably up to 50 mol % based on the overall repeat units.

[0183] The fluorinated polymer may be synthesized by combining suitable monomers optionally protected with a protective group, copolymerizing them in the standard way, and effecting deprotection reaction if necessary. The copolymerization reaction is preferably radical or anionic polymerization though not limited thereto. For the polymerization reaction, reference may be made to JP-A 2004-115630.

[0184] The fluorinated polymer should preferably have a Mw of 2,000 to 50,000, and more preferably 3,000 to 20,000. A fluorinated polymer with a Mw of less than 2,000 helps acid diffusion, degrading resolution and detracting from age stability. A polymer with too high Mw has a reduced solubility in solvent, with a risk of leaving coating defects. The fluorinated polymer preferably has a dispersity (Mw/Mn) of 1.0 to 2.2, more preferably 1.0 to 1.7.

[0185] In the positive resist composition, the fluorinated polymer is preferably used in an amount of 0.01 to 30 parts, more preferably 0.1 to 20 parts, even more preferably 0.5 to 10 parts by weight per 80 parts by weight of the base polymer.

[0186] Organic Solvent

[0187] The chemically amplified positive resist composition may further comprise an organic solvent. The organic solvent used herein is not particularly limited as long as the components are soluble therein. Examples of the organic solvent are described in JP-A 2008-111103, paragraphs [0144] to [0145] (U.S. Pat. No. 7,537,880). Specifically, exemplary solvents include ketones such as cyclohexanone and methyl-2-n-pentyl ketone; alcohols such as 3-methoxybutanol, 3-methyl-3-methoxybutanol, 1-methoxy-2-propanol, 1-ethoxy-2-propanol, and diacetone alcohol; ethers such as propylene glycol monomethyl ether (PGME), ethylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monoethyl ether, propylene glycol dimethyl ether, and diethylene glycol dimethyl ether; esters such as propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monoethyl ether acetate, ethyl lactate (EL), ethyl pyruvate, butyl acetate, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, t-butyl acetate, t-butyl propionate, and propylene glycol mono-t-butyl ether acetate; and lactones such as γ-butyrolactone (GBL), and mixtures thereof. Where an acid labile group of acetal foam is used, a high boiling alcohol solvent such as diethylene glycol, propylene glycol, glycerol, 1,4-butanediol or 1,3-butanediol may be added to accelerate deprotection reaction of acetal.

[0188] Of the above organic solvents, it is recommended to use 1-ethoxy-2-propanol, PGMEA, PGME, cyclohexanone, EL, GBL, and mixtures thereof.

[0189] In the positive resist composition, the organic solvent is preferably used in an amount of 200 to 10,000 parts, more preferably 400 to 5,000 parts by weight per 80 parts by weight of the base polymer. The organic solvent may be used alone or in admixture.

[0190] Photoacid Generator

[0191] The positive resist composition may further comprise a photoacid generator (PAG), also referred to as acid generator of addition type. The PAG used herein may be any compound capable of generating an acid upon exposure to high-energy radiation. Suitable PAGs include sulfonium salts, iodonium salts, sulfonyldiazomethane, N-sulfonyloxyimide, and oxime-O-sulfonate acid generators.

[0192] Suitable PAGs include nonafluorobutane sulfonate, partially fluorinated sulfonates described in JP-A 2012-189977, paragraphs [0247]-[0251], partially fluorinated sulfonates described in JP-A 2013-101271, paragraphs [0261]-[0265], and those described in JP-A 2008-111103, paragraphs [0122]-[0142] and JP-A 2010-215608, paragraphs [0080]-[0081]. Among others, arylsulfonate and alkanesulfonate type PAGs are preferred because they generate acids having an appropriate strength to deprotect the acid labile group in the repeat units having formula (B2) or (B3).

[0193] The preferred PAGs are compounds having a sulfonium anion of the stricture shown below. Notably the cation that pairs with the anion is as exemplified for the sulfonium cation in formulae (A2) to (A4).

##STR00068## ##STR00069## ##STR00070## ##STR00071## ##STR00072## ##STR00073## ##STR00074## ##STR00075## ##STR00076## ##STR00077## ##STR00078##

[0194] Preferably, the photoacid generator generates an acid having a pKa value of equal to or more than −2.0. The upper limit of pKa is preferably 2.0. Notably, the pKa value is computed using pKa DB in software ACD/Chemsketch ver: 9.04 of Advanced Chemistry Development Inc.

[0195] An appropriate amount of the photoacid generator of addition type used is 1 to 30 parts, more preferably 2 to 20 parts by weight per 80 parts by weight of the base polymer. The photoacid generator may be used alone or in admixture.

[0196] Quencher

[0197] The positive resist composition preferably contains a quencher. The quencher is typically selected from conventional basic compounds. Conventional basic compounds include primary, secondary, and tertiary aliphatic amines, mixed amines, aromatic amines, heterocyclic amines, nitrogen-containing compounds with carboxy group, nitrogen-containing compounds with sulfonyl group, nitrogen-containing compounds with hydroxy group, nitrogen-containing compounds with hydroxyphenyl group, alcoholic nitrogen-containing compounds, amide derivatives, imide derivatives, and carbamate derivatives. Also included are primary, secondary, and tertiary amine compounds, specifically amine compounds having a hydroxy group, ether bond, ester bond, lactone ring, cyano group, or sulfonic ester bond as described in JP-A 2008-111103, paragraphs [0146]-[0164], and compounds having a carbamate group as described in JP 3790649. Inter alia, tris[2-(methoxymethoxy)ethyl]amine, tris[2-(methoxymethoxy)ethyl]amine-N-oxide, dibutylaminobenzoic acid, morpholine derivatives, and imidazole derivatives are preferred. Addition of a basic compound is effective for further suppressing the diffusion rate of acid in the resist film or correcting the pattern profile.

[0198] Onium salts such as sulfonium salts, iodonium salts and ammonium salts of carboxylic acids which are not fluorinated at α-position as described in U.S. Pat. No. 8,795,942 (JP-A 2008-158339) may also be used as the quencher. While an α-fluorinated sulfonic acid, imide acid, and methide acid are necessary to deprotect the acid labile group, an α-non-fluorinated carboxylic acid is released by salt exchange with an α-non-fluorinated onium salt. An α-non-fluorinated carboxylic acid functions as a quencher because it does not induce substantial deprotection reaction.

[0199] Examples of the onium salt of α-non-fluorinated carboxylic acid include compounds having the formula (F1).

R.sup.201—CO.sub.2.sup.−Mq.sup.+  (F1)

[0200] In formula (F1), R.sup.201 is hydrogen or a C.sub.1-C.sub.40 hydrocarbyl group which may contain a heteroatom, exclusive of the hydrocarbyl group in which the hydrogen bonded to the carbon atom at α-position of the carboxy group is substituted by fluorine or fluoroalkyl.

[0201] The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C.sub.1-C.sub.40 alkyl groups such as methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, n-pentyl, test-pentyl, n-hexyl, n-octyl, 2-ethylhexyl, n-nonyl, n-decyl; C.sub.3-C.sub.40 cyclic saturated hydrocarbyl groups such as cyclopentyl, cyclohexyl, cyclopentylmethyl, cyclopentylethyl, cyclopentylbutyl, cyclohexylmethyl, cyclohexylethyl, cyclohexylbutyl, norbornyl, tricyclo[5.2.1.0.sup.2,6]decanyl, adamantyl, and adamantylmethyl; C.sub.2-C.sub.40 alkenyl groups such as vinyl, allyl, propenyl, butenyl and hexenyl: C.sub.3-C.sub.40 cyclic unsaturated aliphatic hydrocarbyl groups such as cyclohexenyl; C.sub.6-C.sub.40 aryl groups such as phenyl, naphthyl, alkylphenyl groups (e.g., 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, 4-ethylphenyl, 4-tert-butylphenyl, 4-n-butylphenyl), dialkylphenyl groups (e.g., 2,4-dimethylphenyl and 2,4,6-triisopropylphenyl), alkylnaphthyl groups (e.g., methylnaphthyl and ethylnaphthyl), dialkylnaphthyl groups (e.g., dimethylnaphthyl and diethylnaphthyl): and C.sub.7-C.sub.40 aralkyl groups such as benzyl, 1-phenylethyl and 2-phenylethyl.

[0202] In these groups, some hydrogen may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, and some carbon may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy moiety, cyano moiety, carbonyl moiety, ether bond, thioether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride, or haloalkyl moiety. Suitable heteroatom-containing hydrocarbyl groups include heteroaryl groups such as thienyl: alkoxyphenyl groups such as 4-hydroxyphenyl, 4-methoxyphenyl, 3-methoxyphenyl, 2-methoxyphenyl, 4-ethoxyphenyl, 4-tert-butoxyphenyl, 3-tert-butoxyphenyl; alkoxynaphthyl groups such as methoxynaphthyl, ethoxynaphthyl, n-propoxynaphthyl and n-butoxynaphthyl; dialkoxynaphthyl groups such as dimethoxynaphthyl and diethoxynaphthyl; and aryloxoalkyl groups, typically 2-aryl-2-oxoethyl groups such as 2-phenyl-2-oxoethyl, 2-(1-naphthyl)-2-oxoethyl and 2-(2-naphthyl)-2-oxoethyl.

[0203] In formula (F1), Mq.sup.+ is an onium cation. The onium cation is preferably selected from sulfonium, iodonium and ammonium cations, more preferably sulfonium and iodonium cations. Exemplary sulfonium cations are as exemplified above for the sulfonium cation in formulae (A2) to (A4). Exemplary iodonium cations are as exemplified above for the iodonium cation in formulae (A5) to (A8).

[0204] Examples of the anion of the salt having formula (F1) are shown below, but not limited thereto.

##STR00079## ##STR00080## ##STR00081## ##STR00082## ##STR00083##

[0205] A sulfonium salt of iodized benzene ring-containing carboxylic acid having the formula (F2) is also useful as the quencher.

##STR00084##

[0206] In formula (F2), R.sup.301 is hydroxy, fluorine, chlorine, bromine, amino, nitro, cyano, or a C.sub.1-C.sub.6 saturated hydrocarbyl, C.sub.1-C.sub.6 saturated hydrocarbyloxy, C.sub.2-C.sub.6 saturated hydrocarbylcarbonyloxy or C.sub.1-C.sub.4 saturated hydrocarbylsulfonyloxy group, in which some or all hydrogen may be substituted by halogen, or —N(R.sup.301A)—C(═O)—R.sup.301B, or —N(R.sup.301A)—C(═O)—O—R.sup.301B. R.sup.301A is hydrogen or a C.sub.1-C.sub.6 saturated hydrocarbyl group. R.sup.301B is a C.sub.1-C.sub.6 saturated hydrocarbyl or C.sub.2-C.sub.8 unsaturated aliphatic hydrocarbyl group.

[0207] In formula (F2), x is an integer of 1 to 5, y is an integer of 0 to 3, and z is an integer of 1 to 3. L.sup.1 is a single bond, or a C.sub.1-C.sub.20 (z+1)-valent linking group which may contain at least one moiety selected from ether bond, carbonyl moiety, ester bond, amide bond, sultone ring, lactam ring, carbonate moiety, halogen, hydroxy moiety, and carboxy moiety. The saturated hydrocarbyl, saturated hydrocarbyloxy, saturated hydrocarbylcarbonyloxy, and saturated hydrocarbylsulfonyloxy groups may be straight, branched or cyclic. Groups R.sup.301 may be the same or different when y and/or z is 2 or 3.

[0208] In formula (F2), R.sup.302, R.sup.303 and R.sup.304 are each independently halogen, or a C.sub.1-.sub.20 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C.sub.1-C.sub.20 alkyl, C.sub.2-C.sub.20 alkenyl, C.sub.6-C.sub.20 aryl, and C.sub.7-C.sub.20 aralkyl groups. In these groups, some or all hydrogen may be substituted by hydroxy, carboxy, halogen, oxo, cyano, nitro, sultone, sulfone, or sulfonium salt-containing moiety, or some carbon may be replaced by an ether bond, ester bond, carbonyl moiety, amide bond, carbonate moiety or sulfonic ester bond. Also R.sup.302 and R.sup.303 may bond together to form a ring with the sulfur atom to which they are attached.

[0209] Examples of the compound having formula (F2) include those described in U.S. Pat. No. 10,295,904 (JP-A 2017-219836). These compounds exert a sensitizing effect due to remarkable absorption and an acid diffusion controlling effect.

[0210] A nitrogen-containing carboxylic acid salt compound having the formula (F3) is also useful as the quencher.

##STR00085##

[0211] In formula (F3), R.sup.401 to R.sup.404 are each independently hydrogen, -L.sup.2-CO.sub.2.sup.−, or a C.sub.1-C.sub.20 hydrocarbyl group which may contain a heteroatom. R.sup.401 and R.sup.402, R.sup.402 and R.sup.403, or R.sup.403 and R.sup.404 may bond together to form a ring with the carbon atom to which they are attached. L.sup.2 is a single bond or a C.sub.1-C.sub.20 hydrocarbylene group which may contain a heteroatom. R.sup.405 is hydrogen or a C.sub.1-C.sub.20 hydrocarbyl group which may contain a heteroatom.

[0212] In formula (F3), the ring R is a C.sub.2-C.sub.6 ring containing the carbon and nitrogen atoms in the formula, in which some or all of the carbon-bonded hydrogen atoms may be substituted by a C.sub.1-C.sub.20 hydrocarbyl group or -L.sup.2-CO.sub.2.sup.− and in which some carbon may be replaced by sulfur, oxygen or nitrogen. The ring may be alicyclic or aromatic and is preferably a 5- or 6-membered ring. Suitable rings include pyridine, pyrrole, pyrrolidine, piperidine, pyrazole, imidazoline, pyridazine, pyrimidine, pyrazine, imidazoline, oxazole, triazole, morpholine, thiazine, and triazole rings.

[0213] The carboxylic onium salt having formula (F3) has at least one -L.sup.2-CO.sub.2.sup.−. That is, at least one of R.sup.401 to R.sup.404 is -L.sup.2-CO.sub.2.sup.−, and/or at least one of hydrogen atoms bonded to carbon atoms in the ring R is substituted by -L.sup.2-CO.sub.2.sup.−.

[0214] In formula (F3), Q.sup.+ is a sulfonium, iodonium or ammonium cation, with the sulfonium cation being preferred. Examples of the sulfonium cation are as exemplified above for the cation in formulae (A2) to (A4).

[0215] Examples of the anion in the compound having formula (F3) are shown below, but not limited thereto.

##STR00086## ##STR00087## ##STR00088## ##STR00089## ##STR00090## ##STR00091##

[0216] Weak acid betaine compounds are also useful as the quencher. Non-limiting examples thereof are shown below.

##STR00092## ##STR00093## ##STR00094##

[0217] Also useful are quenchers of polymer type as described in U.S. Pat. No. 7,598,016 (JP-A 2008-239918). The polymeric quencher segregates at the resist surface after coating and thus enhances the rectangularity of resist pattern. When a protective film is applied as is often the case in the immersion lithography, the polymeric quencher is also effective for preventing a film thickness loss of resist pattern or rounding of pattern top.

[0218] When used, the quencher is preferably added in an amount of 0 to 50 parts, more preferably 0.1 to 40 parts by weight per 80 parts by weight of the base polymer. The quencher may be used alone or in admixture.

[0219] Surfactant

[0220] The positive resist composition may contain any conventional surfactants for facilitating to coat the composition to the substrate. A number of surfactants are known in the art as described in JP-A 2004-115630, and any suitable one may be chosen therefrom. The amount of surfactant added is preferably 0 to 5 parts by weight per 80 parts by weight of the base polymer. It is noted that the surfactant need not be added when the positive resist composition contains a fluorinated polymer as mentioned above, which also plays the role of a surfactant.

[0221] From the standpoint of improving the develop loading effect, the chemically amplified positive resist composition is preferably designed such that a resist film formed therefrom in an over-exposed region may have a dissolution rate in alkaline developer of at least 50 nm/sec, more preferably at least 70 nm/sec. As long as the dissolution rate is at least 50 nm/sec, the resist film is uniformly dissolved in alkaline developer independent of a pattern layout difference in the case of a grouped/isolated pattern, and the variation of line width can be minimized. It is noted that the dissolution rate of an over-exposed region is computed by spin coating the positive resist composition onto a 8-inch silicon wafer, baking at 110° C. for 60 seconds to form a resist film of 90 nm thick, exposing the resist film to KrF excimer laser radiation in a sufficient energy dose to complete deprotection reaction on the polymer, baking at 110° C. for 60 seconds, developing the film in a 2.38 wt % TMAH aqueous solution at 23° C., and measuring a loss of film thickness by means of a resist development analyzer.

[0222] Also preferably, the resist film formed from the positive resist composition in an unexposed region has a dissolution rate in alkaline developer of up to 10 nm/min, more preferably up to 8 nm/min, even more preferably up to 6 nm/min. Where the resist film is in the thin film range of up to 100 nm, the influence of pattern film thickness loss in alkaline developer becomes greater. If the dissolution rate in unexposed region is more than 10 nm/min, pattern collapse will occur, failing to form a small size pattern. The problem becomes outstanding in the fabrication of photomasks requiring to be defectless and having a tendency of strong development process. It is noted that the dissolution rate of an unexposed region is computed by spin coating the positive resist composition onto a 6-inch silicon wafer, baking at 110° C. for 240 seconds to form a resist film of 80 nm thick, developing the film in a 2.38 wt % TMAH aqueous solution at 23° C. for 80 seconds, and measuring a loss of film thickness.

Pattern Forming Process

[0223] A further embodiment of the invention is a process for forming a resist pattern comprising the steps of applying the chemically amplified positive resist composition onto a substrate to form a resist film thereon, exposing patternwise the resist film to high-energy radiation, and developing the exposed resist film in an alkaline developer.

[0224] The resist composition is first applied onto a substrate on which an integrated circuit is to be formed (e.g., Si, SiO, SiO.sub.2, SiN, SiON, TiN, WSi, BPSG, SOG, or organic antireflective coating) or a substrate on which a mask circuit is to be formed (e.g., Cr, CrO, CrON, MoSi.sub.2, Si, SiO, SiO.sub.2, SiON, SiONC, CoTa, NiTa, TaBN, or SnO.sub.2) by a suitable coating technique such as spin coating. The coating is prebaked on a hot plate at a temperature of preferably 60 to 150° C. for 1 to 20 minutes, more preferably at 80 to 140° C. for 1 to 10 minutes. The resulting resist film is generally 0.03 to 2 μm thick.

[0225] The resist film is then exposed to a desired pattern of high-energy radiation such as UV, deep-UV, excimer laser radiation (KrF, ArF, etc.), EUV, x-ray, γ-ray, synchrotron radiation or EB. Exposure using EUV or EB is preferred.

[0226] When UV, deep-UV, excimer laser, EUV, x-ray, γ-ray or synchrotron radiation is used as the high-energy radiation, the resist film is exposed thereto through a mask having a desired pattern in a dose of preferably 1 to 500 mJ/cm.sup.2, more preferably 10 to 400 mJ/cm.sup.2. When EB is used as the high-energy radiation, the resist film is exposed thereto directly in a dose of preferably 1 to 500 μC/cm.sup.2, more preferably 10 to 400 μC/cm.sup.2.

[0227] The exposure may be performed by conventional lithography whereas the immersion lithography of holding a liquid between the resist film and the mask may be employed if desired. In the case of immersion lithography, a protective film which is insoluble in water may be formed on the resist film.

[0228] After the exposure, the resist film may be baked (PEB) on a hotplate preferably at 60 to 150° C. for 1 to 20 minutes, more preferably at 80 to 140° C. for 1 to 10 minutes.

[0229] After the exposure or PEB, the resist film is developed in a developer in the form of an aqueous alkaline solution for preferably 0.1 to 3 minutes, more preferably 0.5 to 2 minutes by conventional techniques such as dip, puddle and spray techniques. A typical developer is a 0.1 to 5 wt %, preferably 2 to 3 wt % aqueous solution of tetramethylammonium hydroxide (TMAH) or another alkali. In this way, the desired pattern is formed on the substrate.

[0230] The positive resist composition of the invention is useful in forming a resist pattern having a satisfactory resolution and reduced LER. The positive resist composition is also useful in forming a resist pattern on a substrate having a surface layer of a material which is less adhesive to a resist film with a likelihood of later pattern stripping or pattern collapse. Examples of such substrate include substrates having sputter deposited on their outermost surface a layer of metallic chromium or a chromium compound containing one or more light elements such as oxygen, nitrogen and carbon, and substrates having an outermost layer of SiO, SiO.sub.x, or a tantalum, molybdenum, cobalt, nickel, tungsten or tin compound. The substrate to which the positive resist composition is applied is most typically a photomask blank which may be of transmission or reflection type.

[0231] The resist pattern forming process is successful in forming patterns having a high resolution, minimized influence of develop loading, and a reduced size difference independent of a pattern density (grouped or isolated) even on a substrate (typically photomask blank) whose outermost surface is made of a material tending to affect resist pattern profile such as a chromium, silicon or tantalum-containing material.

EXAMPLES

[0232] Examples of the invention are given below by way of illustration and not by way of limitation. The abbreviation “pbw” is parts by weight. For copolymers, the compositional ratio is a molar ratio and Mw is determined by GPC versus polystyrene standards.

[1] Synthesis of Sulfonium Salt

Synthesis Example 1

[0233] Synthesis of sulfonium salt PM-1

##STR00095##

[0234] Sodium 3,3,3-trifluoro-2-hydroxy-2-trifluoromethylpropane-1-sulfonate was synthesized according to the method of U.S. Pat. No. 8,283,104 (JP-A 2010-215608). To 132 g of an aqueous solution containing sodium 3,3,3-tifluoro-2-hydroxy-2-trifluoromethylpropane-1-sulfonate (corresponding to 0.1 mol of sodium 3,3,3-trifluoro-2-hydroxy-2-tifluoromethylpropane-1-sulfonate), 200 g of methylene chloride and 20.4 g of benzyltrimethylammonium chloride were added, followed by 30 minutes of stirring. After stirring, the aqueous solution was subjected to separatory operation, extraction and water washing. The organic layer was concentrated. Methyl isobutyl ketone was added to the concentrate, followed by concentration again. Diisopropyl ether was added to the concentrate for recrystallization. The solid precipitate was collected and dried in vacuum, yielding a benzyltrimethylammonium salt.

[0235] To the benzyltrimethylammonium salt, 15.0 g of triethylamine and 200 g of methylene chloride were added. Under ice cooling, 11.5 g of methacryloyl chloride was added to the mixture. The solution was stiffed at room temperature overnight, after which 100 g of water was added to quench the reaction. The reaction solution as quenched was subjected to separatory operation and extraction. An aqueous solution of triphenylsulfonium chloride was added to the extracted organic layer, followed by 30 minutes of stirring, separatory operation, and water washing. The organic layer was concentrated. Methyl isobutyl ketone was added to the concentrate, followed by concentration again. Diisopropyl ether was added to the concentrate for recrystallization. The solid precipitate was collected and dried in vacuum, obtaining the target compound, triphenylsulfonium 2-(methacryloyloxy)-3,3,3-trifluoro-2-trifluoromethylpropane-1-sulfonate (PM-1) as white solid (yield 85%).

[2] Synthesis of Polymer

Synthesis Example 2-1

[0236] Synthesis of Polymer P-1

[0237] In nitrogen atmosphere, a 200-mL dropping cylinder was charged with 25.5 g of a 50.0 wt % PGMEA solution of 4-hydroxystyrene, 9.3 g of ethylcyclopentyl methacrylate, 12.7 g of 1-(1-methylcyclopentyloxy)-4-vinylbenzene, 17.5 g of PM-1, 4.1 g of dimethyl-2,2′-azobis(2-methylpropionate) (tradename V-601 by Fujifilm Wako Pure Chemical), and 24 g of γ-butyrolactone and 30 g of PGMEA as solvent to form a monomer solution.

[0238] In nitrogen atmosphere, a 300-mL flask was charged with 40 g of γ-butyrolactone and heated at 80° C. The monomer solution was added dropwise to the flask over 4 hours. After the completion of dropwise addition, the polymerization solution was continuously stirred for 18 hours while maintaining its temperature at 80° C. The polymerization solution was cooled to room temperature and added dropwise to 400 g of diisopropyl ether. The solution was statically held whereupon a solid precipitated. Diisopropyl ether was decanted off and the solid precipitate was dissolved in 100 g of acetone. The acetone solution was added dropwise to 400 g of diisopropyl ether whereupon a solid precipitated. The solid precipitate was collected by filtration and dissolved in 100 g of acetone again. The acetone solution was added dropwise to 400 g of water whereupon a solid precipitated. The solid was collected by filtration and dried at 40° C. for 40 hours, obtaining 35 g of a polymer as white solid. The polymer designated Polymer P-1 was analyzed by .sup.1H-NMR, .sup.13C-NMR and GPC, with the results shown below.

##STR00096##

Synthesis Examples 2-2 to 2-58 and Comparative Synthesis Examples 1-1 to 1-2

[0239] Synthesis of Polymers P-2 to P-58 and Comparative Polymers cP-1 to cP-2

[0240] Polymers P-2 to P-58 and Comparative Polymers cP-1 to cP-2 were synthesized by the same procedure as Synthesis Example 2-1 except that the type and amount (mol %) of monomers were changed. hi Table 1, the incorporation ratio is a molar ratio.

TABLE-US-00001 TABLE 1 Incorporation Incorporation Incorporation Incorporation Incorporation ratio ratio ratio ratio ratio Unit 1 (mol %) Unit 2 (mol %) Unit 3 (mol %) Unit 4 (mol %) Unit 5 (mol %) Mw Mw/Mn P-1 PM-1 10.0 A-1 40.0 C-1 25.0 C-5 25.0 — — 18,000 1.78 P-2 PM-1 10.0 A-1 40.0 B-1 10.0 C-1 20.0 C-5 20.0 17,400 1.79 P-3 PM-1 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-5 20.0 17,600 1.77 P-4 PM-2 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-5 20.0 17,900 1.78 P-5 PM-2 10.0 A-1 40.0 B-3 10.0 C-1 20.0 C-5 20.0 17,500 1.76 P-6 PM-2 10.0 A-1 40.0 B-4 10.0 C-1 20.0 C-5 20.0 17,400 1.78 P-7 PM-2 10.0 A-1 40.0 B-2 10.0 C-2 20.0 C-6 20.0 17,700 1.77 P-8 PM-2 10.0 A-1 40.0 B-2 10.0 C-3 20.0 C-5 20.0 17,700 1.75 P-9 PM-2 10.0 A-1 40.0 B-2 10.0 C-4 20.0 C-5 20.0 17,800 1.76 P-10 PM-2 10.0 A-1 40.0 B-2 10.0 C-9 20.0 C-5 20.0 17,500 1.77 P-11 PM-2 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-6 20.0 17,600 1.78 P-12 PM-2 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-7 20.0 17,400 1.75 P-13 PM-2 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-8 20.0 17,600 1.78 P-14 PM-2 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-12 20.0 17,500 1.76 P-15 PM-2 10.0 A-1 40.0 B-2 10.0 C-13 20.0 C-5 20.0 17,400 1.75 P-16 PM-2 10.0 A-1 40.0 B-2 10.0 C-14 20.0 C-5 20.0 17,500 1.77 P-17 PM-2 10.0 A-1 40.0 B-2 10.0 C-15 20.0 C-5 20.0 17,500 1.78 P-18 PM-2 10.0 A-1 40.0 B-2 10.0 C-16 20.0 C-5 20.0 17,400 1.77 P-19 PM-2 10.0 A-1 40.0 B-2 10.0 C-17 20.0 C-5 20.0 17,600 1.78 P-20 PM-2 10.0 A-1 40.0 B-2 10.0 C-18 20.0 C-5 20.0 17,700 1.76 P-21 PM-2 10.0 A-1 40.0 B-2 10.0 C-10 20.0 C13 20.0 17,800 1.75 P-22 PM-2 10.0 A-1 40.0 B-2 10.0 C-11 20.0 C13 20.0 17,600 1.76 P-23 PM-3 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-5 20.0 18,600 1.76 P-24 PM-4 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-5 20.0 17,600 1.75 P-25 PM-5 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-5 20.0 18,700 1.76 P-26 PM-6 10.0 A-1 40.0 B-2 10.0 C-1 20.0 C-5 20.0 18,800 1.76 P-27 PM-2 5.0 A-1 35.0 C-1 30.0 C-5 30.0 — — 18,400 1.79 P-28 PM-2 25.0 A-1 35.0 C-1 20.0 C-5 20.0 — — 17,900 1.77 P-29 PM-2 10.0 A-2 50.0 C-1 20.0 C-5 20.0 — — 18,000 1.78 P-30 PM-2 10.0 A-3 40.0 C-1 25.0 C-5 25.0 — — 18,200 1.79

TABLE-US-00002 TABLE 2 Incorporation Incorporation Incorporation Incorporation Incorporation ratio ratio ratio ratio ratio Unit 1 (mol %) Unit 2 (mol %) Unit 3 (mol %) Unit 4 (mol %) Unit 5 (mol %) Mw Mw/Mn P-31 PM-2 10.0 A-2 50.0 B-3 10.0 C-1 15.0 C-5 15.0 18,300 1.77 P-32 PM-2 10.0 A-2 50.0 C-2 20.0 C-6 20.0 — — 18,100 1.78 P-33 PM-2 10.0 A-2 50.0 C-3 20.0 C-7 20.0 — — 18,200 1.79 P-34 PM-2 10.0 A-2 50.0 C-4 20.0 C-8 20.0 — — 18,400 1.78 P-35 PM-2 10.0 A-2 50.0 C-1 20.0 C-6 20.0 — — 18,100 1.77 P-36 PM-2 10.0 A-2 50.0 C-1 20.0 C-7 20.0 — — 18,200 1.78 P-37 PM-2 10.0 A-2 50.0 C-1 20.0 C-8 20.0 — — 18.500 1.78 P-38 PM-2 10.0 A-2 50.0 C-2 20.0 C-5 20.0 — — 18,100 1.78 P-39 PM-2 10.0 A-2 50.0 C-2 20.0 C-7 20.0 — — 18,200 1.79 P-40 PM-2 10.0 A-2 50.0 C-2 20.0 C-8 20.0 — — 18,300 1.78 P-41 PM-2 10.0 A-2 50.0 C-3 20.0 C-5 20.0 — — 18,300 1.78 P-42 PM-2 10.0 A-2 50.0 C-3 20.0 C-6 20.0 — — 18,300 1.79 P-43 PM-2 10.0 A-2 50.0 C-3 20.0 C-8 20.0 — — 18,400 1.78 P-44 PM-2 10.0 A-2 50.0 C-4 20.0 C-5 20.0 — — 18,400 1.79 P-45 PM-2 10.0 A-2 50.0 C-4 20.0 C-6 20.0 — — 18,400 1.79 P-46 PM-2 10.0 A-2 50.0 C-4 20.0 C-7 20.0 — — 18,500 1.78 P-47 PM-2 10.0 A-2 50.0 C-1 40.0 — — — — 18,200 1.77 P-48 PM-2 10.0 A-2 50.0 C-5 40.0 — — — — 17,800 1.78 P-49 PM-2 10.0 A-2 50.0 B-2 10.0 C-5 15.0 C-1 15.0 17,700 1.77 P-50 PM-2 5.0 A-2 50.0 B-2 10.0 C-5 15.0 C-1 20.0 17,800 1.76 P-51 PM-2 10.0 A-2 50.0 C-13 20.0 C-1 20.0 — — 17,700 1.77 P-52 PM-2 10.0 A-2 40.0 B-2 10.0 C-13 20.0 C-1 20.0 17,600 1.76 P-53 PM-2 10.0 A-2 50.0 C-19 20.0 C-1 20.0 — — 17,800 1.77 P-54 PM-2 10.0 A-2 45.0 B-2 10.0 C-19 15.0 C-1 20.0 17,600 1.76 P-55 PM-2 10.0 A-2 45.0 B-2 10.0 C-20 15.0 C-1 20.0 17,600 1.76 P-56 PM-2 10.0 A-2 50.0 C-1 35.0 C-5 5.0 — — 18,200 1.77 P-57 PM-2 5.0 A-2 70.0 C-2 10.0 C-I9 15.0 — — 18,000 1.74 P-58 PM-2 10.0 A-1 55.0 B-2 10.0 C-2 10.0 C-19 15.0 18,100 1.73

TABLE-US-00003 TABLE 3 Incorpontion Incorporation Incorporation Incorporation Incorporation ratio ratio ratio ratio ratio Unit 1 (mol %) Unit 2 (mol %) Unit 3 (mol %) Unit 4 (mol %) Unit 5 (mol %) Mw Mw/Mn cP-1 PM-2 10.0 A-1 57.0 B-2 10.0 C-1 23.0 — — 17,600 1.79 cP-2 PM-2 10.0 A-1 50.0 B-2 10.0 C-5 30.0 — — 17.200 1.78

[0241] The structure of repeat units incorporated in the polymers is shown below.

##STR00097## ##STR00098## ##STR00099## ##STR00100## ##STR00101## ##STR00102## ##STR00103##

[0242] The dissolution rate of a polymer in alkaline developer was computed by spin coating a 16.7 wt % solution of the polymer in propylene glycol monomethyl ether (PGME) solvent onto a 8-inch silicon wafer, baking at 100° C. for 90 seconds to form a film of 1,000 nm thick, developing the film in a 2.38 wt % aqueous solution of tetramethylammonium hydroxide (TMAH) at 23° C. for 100 seconds, and measuring a loss of film thickness. Polymers P-1 to P-58 and Comparative Polymers cP-1 to cP-2 showed a dissolution rate of up to 5 nm/min.

Synthesis Examples 3-1 to 3-11

[0243] Synthesis of Polymers AP-1 to AP-11

[0244] Polymers AP-1 to AP-11 were synthesized by the same procedure as Synthesis Example 2-1 except that the monomers were changed.

##STR00104## ##STR00105## ##STR00106## ##STR00107##

[0245] Polymers AP-1 to AP-11 showed a dissolution rate of up to 5 nm/min.

[3] Preparation of Chemically Amplified Positive Resist Compositions

Examples 1-1 to 1-90 and Comparative Examples 1-1 to 1-3

[0246] Positive resist compositions were prepared by dissolving selected components in an organic solvent in accordance with the formulation shown in Tables 4 to 8, and filtering the solution through a UPE filter with a pore size of 0.02 The organic solvent was a mixture of 340 pbw of PGMEA, 1,700 pbw of EL, and 1,360 pbw of PGME, to which 0.075 pbw of surfactant FC-4430 (3M) was added.

TABLE-US-00004 TABLE 4 Photoacid Resist Resin 1 Resin 2 generator Quencher Additive composition (pbw) (pbw) (pbw) (pbw) (pbw) Example 1-1 R-1 P-1 — — Q-1 — (80) (7.0) 1-2 R-2 P-1 — PAG-A (3) Q-1 — (80) PAG-B (2) (8.0) 1-3 R-3 P-1 — PAG-C (7) Q-1 — (80) (7.5) 1-4 R-4 P-1 AP-5 PAG-A (3) Q-1 — (40) (40) PAG-B (2) (6.0) 1-5 R-5 P-1 AP-5 PAG-C (16) Q-1 — (40) (40) (10.0) 1-6 R-6 P-1 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (6.0) (5) 1-7 R-7 P-1 AP-5 PAG-A (3) Q-1 D-2 (40) (40) PAG-B (2) (6.0) (5) 1-8 R-8 P-1 AP-5 PAG-A (3) Q-1 D-3 (40) (40) PAG-B (2) (6.0) (5) 1-9 R-9 P-1 AP-5 PAG-A (3) Q-2 — (40) (40) PAG-B (2) (9.0) 1-10 R-10 P-1 AP-5 PAG-A (3) Q-3 — (40) (40) PAG-B (2) (8.0) 1-11 R-11 P-2 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-12 R-12 P-3 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-13 R-13 P-4 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-14 R-14 P-5 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-15 R-15 P-6 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-16 R-16 P-7 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-17 R-17 P-8 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-18 R-18 P-9 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-19 R-19 P-10 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-20 R-20 P-11 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-21 R-21 P-12 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-22 R-22 P-13 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-23 R-23 P-14 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-74 R-24 P-15 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-25 R-25 P-16 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5)

TABLE-US-00005 TABLE 5 Photoacid Resist Resin 1 Resin 2 generator Quencher Additive composition (pbw) (pbw) (pbw) (pbw) (pbw) Example 1-26 R-26 P-17 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-27 R-27 P-18 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-28 R-28 P-19 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-29 R-29 P-20 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-30 R-30 P-21 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-31 R-31 P-22 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-37 R-32 P-23 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-33 R-33 P-24 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-34 R-34 P-25 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-35 R-35 P-26 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-36 R-36 P-27 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (4.5) (5) 1-37 R-37 P-28 AP-5 — Q-1 D-1 (40) (40) (8.0) (5) 1-38 R-38 P-29 — — Q-1 D-1 (80) (7.0) (5) 1-39 R-39 P-29 — PAG-A (3) Q-1 D-1 (80) PAG-B (2) (8.0) (5) 1-40 R-40 P-29 — PAG-C (5) Q-1 D-1 (80) (7.5) (5) 1-41 R-41 P-29 AP-1 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-42 R-42 P-29 AP-2 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-43 R-43 P-29 AP-2 PAG-C (8) Q-1 D-1 (40) (40) PAG-B (3) (9.0) (1.5) 1-44 R-44 P-29 AP-2 PAG-C (8) Q-1 D-1 (40) (40) PAG-B (3) (18.0) (1.5) 1-45 R-45 P-29 AP-3 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-46 R-46 P-29 AP-4 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-47 R-47 P-29 AP-5 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-48 R-48 P-29 AP-6 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-49 R-49 P-29 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-50 R-50 P-29 AP-7 PAG-A (3) Q-1 D-1 (20) (60) PAG-B (2) (5.5) (5)

TABLE-US-00006 TABLE 6 Photoacid Resist Resin 1 Resin 2 generator Quencher Additive composition (pbw) (pbw) (pbw) (pbw) (pbw) Example 1-51 R-51 P-29 AP-7 PAG-C (7) Q-1 D-1 (40) (40) (5.5) (5) 1-52 R-52 P-29 AP-7 PAG-A (3) Q-2 D-1 (40) (40) PAG-B (2) (9.0) (5) 1-53 R-53 P-29 AP-7 PAG-A (3) Q-3 D-1 (40) (40) PAG-B (2) (12.0) (5) 1-54 R-54 P-29 AP-8 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-55 R-55 P-30 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-56 R-56 P-31 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-57 R-57 P-32 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-58 R-58 P-33 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-59 R-59 P-34 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-60 R-60 P-35 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-61 R-61 P-36 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-62 R-62 P-37 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-63 R-63 P-38 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-64 R-64 P-39 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-65 R-65 P-40 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-66 R-66 P-41 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-67 R-67 P-42 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-68 R-68 P-43 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-69 R-69 P-44 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-70 R-70 P-45 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-71 R-71 P-46 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (5) 1-72 R-72 P-47 P-48 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (8.0) (5) 1-73 R-73 P-47 (20) AP-7 PAG-A (3) Q-1 D-1 P-48 (20) (40) PAG-B (2) (5.5) (5) 1-74 R-74 P-29 AP-2 PAG-A (3) Q-1 D-4 (40) (40) PAG-B (2) (20.0) (1.5) 1-75 R-75 P-29 AP-2 PAG-C (8) Q-1 D-4 (40) (40) PAG-B (3) (15) (1.5) 1-76 R-76 P-49 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-77 R-77 P-50 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (4.5) (3)

TABLE-US-00007 TABLE 7 Photoacid Resist Resin 1 Resin 2 generator Quencher Additive composition (pbw) (pbw) (pbw) (pbw) (pbw) Example 1-78 R-78 P-51 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-79 R-79 P-52 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-80 R-80 P-53 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-81 R-81 P-54 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-82 R-82 P-55 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.5) (3) 1-83 R-83 P-56 AP-7 PAG-A (3) Q-1 D-1 (40) (40) PAG-B (2) (5.0) (5) 1-84 R-84 P-29 AP-2 PAG-A (3) Q-1 D-5 (40) (40) PAG-B (2) (12.0) (1.5) 1-85 R-85 P-57 AP-9 PAG-C (3) Q-1 D-1 (40) (40) PAG-B (2) (12.0) (3) 1-86 R-86 P-57 AP-10 PAG-C (3) Q-1 D-1 (40) (40) PAG-B (2) (12.0) (3) 1-87 R-87 P-57 AP-11 PAG-C (3) Q-1 D-1 (40) (40) PAG-B (2) (12.0) (3) 1-88 R-88 P-58 AP-9 PAG-C (3) Q-1 D-1 (40) (40) PAG-B (2) (16.0) (3) 1-89 R-89 P-58 AP-10 PAG-C (3) Q-1 D-1 (40) (40) PAG-B (2) (16.0) (3) 1-90 R-90 P-58 AP-11 PAG-C (3) Q-1 D-1 (40) (40) PAG-B (2) (16.0) (3)

TABLE-US-00008 TABLE 8 Photoacid Resist Resin 1 Resin 2 generator Quencher Additive composition (pbw) (pbw) (pbw) (pbw) (pbw) Comparative 1-1 CR-1 cP-1 AP-7 PAG-A (3) Q-1 D-1 Example (40) (40) PAG-B (2) (5.5) (5) 1-2 CR-2 cP-2 — — Q-1 D-1 (80) (7.5) (5) 1-3 CR-3 P-48 — PAG-A (3) Q-1 D-1 (80) PAG-B (2) (8.0) (5)

[0247] In Tables 4 to 8, quenchers Q-1 to Q-3, photoacid generators PAG-A to PAG-C, and polymers D-1 to D-5 have the structures shown below.

##STR00108## ##STR00109## ##STR00110##

[4] EB Lithography Test

Examples 2-1 to 2-90 and Comparative Examples 2-1 to 2-3

[0248] Using a coater/developer system ACT-M (Tokyo Electron Ltd.), each of the positive resist compositions (R-1 to R-90, CR-1 to CR-3) was spin coated onto a photomask blank of 152 mm squares having the outermost surface of chromium and prebaked on a hotplate at 110° C. for 600 seconds to form a resist film of 80 nm thick. The thickness of the resist film was measured by an optical film thickness measurement system Nanospec (Nanometrics Inc.). Measurement was made at 81 points in the plane of the blank substrate excluding a peripheral band extending 10 min inward from the blank periphery, and an average film thickness and a film thickness range were computed therefrom.

[0249] The resist film was exposed to EB using an EB writer system EBM-5000Plus (NuFlare Technology Inc., accelerating voltage 50 kV), then baked (PEB) at 110° C. for 600 seconds, and developed in a 2.38 wt % TMAH aqueous solution, thereby yielding a positive pattern. The resist pattern was evaluated as follows. The patterned mask blank was observed under a top-down scanning electron microscope (TD-SEM). The optimum dose (Eop) was defined as the exposure dose (μC/cm.sup.2) which provided a 1:1 resolution at the top and bottom of a 200-nm 1:1 line-and-space (LS) pattern. The LS resolution (or maximum resolution) was defined as the minimum line width of a L/S pattern that could be resolved at the optimum dose. The edge roughness (LER) of a 200-nm LS pattern was measured under SEM.

[0250] The develop loading was evaluated by forming a 200-nm LS pattern at the dose (μC/cm.sup.2) capable of resolving a 1:1 LS pattern of 200 nm design at a ratio 1:1 and a 200-nm LS pattern including dummy patterns having a density of 15%, 25%, 33%, 45%, 50%, 55%, 66%, 75%, 85%, and 95% arranged around the center pattern, measuring the size of spaces under SEM, and comparing the size difference among grouped and isolated patterns. Also, the pattern was visually observed to judge whether or not the profile was rectangular.

[0251] The dissolution rate of an over-exposed region is computed by spin coating the resist solution onto a 8-inch silicon wafer, baking at 110° C. for 60 seconds to form a resist film of 90 nm thick, exposing the resist film to KrF excimer laser radiation in a dose (mJ/cm.sup.2) capable of resolving a 200-nm 1:1 LS pattern at a ratio 1:1, baking at 110° C. for 60 seconds, developing the film in a 2.38 wt % TMAH aqueous solution at 23° C., and measuring a loss of film thickness by means of a resist development rate analyzer (RDA-800 by Litho Tech Japan Corp.). The results are shown in Tables 9 to 12.

TABLE-US-00009 TABLE 9 Develop Dissolution rate Optimum Maximum loading in over-exposed Resist dose resolution LER variation Pattern region composition (μC/cm.sup.2) (nm) (nm) (Δnm) profile (nm/s) Example 2-1 R-1 160 30 4.2 1.5 rectangular 350 2-2 R-2 158 30 4.3 1.4 rectangular 360 2-3 R-3 158 30 4.2 1.4 rectangular 360 2-4 R-4 162 30 4.4 1.6 rectangular 240 2-5 R-5 157 30 4.3 1.4 rectangular 240 2-6 R-6 159 30 4.2 1.3 rectangular 245 2-7 R-7 158 30 4.2 1.4 rectangular 245 2-8 R-8 158 30 4.2 1.4 rectangular 245 2-9 R-9 159 30 4.4 1.5 rectangular 240 2-10 R-10 160 30 4.3 1.5 rectangular 240 2-11 R-11 159 30 4.4 1.5 rectangular 180 2-12 R-12 161 30 4.4 1.6 rectangular 180 2-13 R-13 160 30 4.5 1.5 rectangular 180 2-14 R-14 159 30 4.5 1.5 rectangular 180 2-15 R-15 160 30 4.4 1.4 rectangular 180 2-16 R-16 162 30 4.5 1.5 rectangular 180 2-17 R-17 161 30 4.5 1.6 rectangular 180 2-18 R-18 160 30 4.4 1.5 rectangular 180 2-19 R-19 159 30 4.4 1.5 rectangular 180 2-20 R-20 157 30 4.5 1.5 rectangular 180 2-21 R-21 158 30 4.6 1.6 rectangular 180 2-22 R-22 159 30 4.4 1.5 rectangular 180 2-23 R-23 160 30 4.5 1.4 rectangular 180 2-24 R-24 158 30 4.5 1.5 rectangular 180 2-25 R-25 159 30 4.4 1.6 rectangular 180 2-26 R-26 160 30 4.4 1.4 rectangular 180 2-27 R-27 161 30 4.5 1.5 rectangular 180 2-28 R-28 160 30 4.5 1.5 rectangular 180 2-29 R-29 161 30 4.4 1.6 rectangular 180 2-30 R-30 158 30 4.6 1.4 rectangular 180

TABLE-US-00010 TABLE 10 Develop Dissolution rate Optimum Maximum loading in over-exposed Resist dose resolution LER variation Pattern region composition (μC/cm.sup.2) (nm) (nm) (Δnm) profile (nm/s) Example 2-31 R-31 159 30 4.4 1.5 rectangular 180 2-32 R-32 159 30 4.5 1.5 rectangular 180 2-33 R-33 153 40 4.8 1.6 rectangular 190 2-34 R-34 155 40 4.8 1.6 rectangular 190 2-35 R-35 169 35 4.7 1.7 rectangular 140 2-36 R-36 158 30 4.5 1.5 rectangular 210 2-37 R-37 156 30 4.4 1.5 rectangular 220 2-38 R-38 159 30 4.5 1.5 rectangular 330 2-39 R-39 157 30 4.4 1.4 rectangular 335 2-40 R-40 158 30 4.4 1.4 rectangular 335 2-41 R-41 160 30 4.3 1.3 rectangular 200 2-42 R-42 161 30 4.4 1.4 rectangular 200 2-43 R-43 210 30 3.8 1.2 rectangular 200 2-44 R-44 330 28 3.5 1.1 rectangular 200 2-45 R-45 160 30 4.4 1.4 rectangular 200 2-46 R-46 161 30 4.3 1.3 rectangular 200 2-47 R-47 160 30 4.2 1.3 rectangular 200 2-48 R-48 161 30 4.3 1.3 rectangular 200 2-49 R-49 160 30 4.1 1.2 rectangular 200 2-50 R-50 160 30 4.3 1.4 rectangular 200 2-51 R-51 160 30 4.3 1.3 rectangular 200 2-52 R-52 162 30 4.4 1.5 rectangular 200 2-53 R-53 162 30 4.4 1.4 rectangular 200 2-54 R-54 160 30 4.4 1.4 rectangular 200 2-55 R-55 157 35 4.6 1.4 rectangular 210 2-56 R-56 163 30 4.5 1.6 rectangular 140 2-57 R-57 160 30 4.5 1.5 rectangular 200 2-58 R-58 161 30 4.5 1.5 rectangular 200 2-59 R-59 159 30 4.4 1.4 rectangular 200 2-60 R-60 158 30 4.4 1.4 rectangular 200

TABLE-US-00011 TABLE 11 Develop Dissolution rate Optimum Maximum loading in over-exposed Resist dose resolution LER variation Pattern region composition (μC/cm.sup.2) (nm) (nm) (Δnm) profile (nm/s) Example 2-61 R-61 159 30 4.5 1.5 rectangular 200 2-62 R-62 158 30 4.5 1.5 rectangular 200 2-63 R-63 159 30 4.4 1.5 rectangular 200 2-64 R-64 160 30 4.5 1.4 rectangular 200 2-65 R-65 161 30 4.5 1.4 rectangular 200 2-66 R-66 158 30 4.4 1.4 rectangular 200 2-67 R-67 159 30 4.4 1.4 rectangular 200 2-68 R-68 158 30 4.3 1.5 rectangular 200 2-69 R-69 159 30 4.5 1.5 rectangular 200 2-70 R-70 161 30 4.4 1.4 rectangular 200 2-71 R-71 162 30 4.6 1.6 rectangular 200 2-72 R-72 156 30 4.4 1.4 rectangular 380 2-73 R-73 160 30 4.5 1.5 rectangular 220 2-74 R-74 400 28 3.2 1.0 rectangular 240 2-75 R-75 320 28 3.3 1.1 rectangular 210 2-76 R-76 161 30 4.6 1.5 rectangular 180 2-77 R-77 160 30 4.5 1.5 rectangular 170 2-78 R-78 160 30 4.5 1.6 rectangular 200 2-79 R-79 159 30 4.6 1.6 rectangular 180 2-80 R-80 157 30 4.6 1.5 rectangular 200 2-81 R-81 158 30 4.5 1.5 rectangular 180 2-82 R-82 160 30 4.6 1.4 rectangular 180 2-83 R-83 161 30 4.2 1.3 rectangular 70 2-84 R-84 325 30 3.4 1.1 rectangular 210 2-85 R-85 310 30 3.3 1.5 rectangular 150 2-86 R-86 315 30 3.2 1.4 rectangular 160 2-87 R-87 320 30 3.2 1.4 rectangular 160 2-88 R-88 300 30 3.3 1.2 rectangular 200 2-89 R-89 305 30 3.3 1.2 rectangular 200 2-90 R-90 305 30 3.3 1.2 rectangular 200

TABLE-US-00012 TABLE 12 Develop Dissolution rate Optimum Maximum loading in over-exposed Resist dose resolution LER variation region composition (μC/cm.sup.2) (nm) (nm) (Δnm) Pattern profile (nm/s) Comparative 2-1 CR-1 162 35 4.6 3.8 rectangular 30 Example 2-2 CR-2 158 50 5.2 1.7 inversely tapered 350 2-3 CR-3 160 50 5.5 1.7 inversely tapered 380

[0252] All the chemically amplified positive resist compositions (R-1 to R-90) within the scope of the invention show satisfactory resolution, reduced LER, rectangular pattern profile, and controlled values of develop loading. Of the comparative resist compositions (CR-1 to CR-3), composition CR-1 has so low an over-exposed region dissolution rate that the control of develop loading is insufficient. In compositions CR-2 and CR-3, because the design of base polymers is insufficient, not all resolution, LER and pattern rectangularity are met although the develop loading is fully controlled.

[0253] This accounts for the design of base polymers. That is, an acid diffusion controlling effect is obtained by designing a PAG-bound polymer framework. By combining a phenolic acid-labile group with an acrylic acid-labile group, optimization of a pattern profile due to phenolic units and optimization of an exposed region dissolution rate due to acrylic units are attained. As a result, all resolution, LER, pattern rectangularity, and develop loading control are achieved. The resist pattern forming process using the positive resist composition is effective in photolithography for the fabrication of semiconductor devices and the processing of photomask blanks of transmission and reflection types.

[0254] Japanese Patent Application No. 2021-043151 is incorporated herein by reference.

[0255] Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims.