Projected capacitive touch panel with silver-inclusive transparent conducting layer(s), and/or method of making the same

Abstract

Certain example embodiments relate to capacitive touch panels. First and second glass substrates are substantially parallel and spaced apart from one another. At least one multi-layer transparent conductive coating (TCC) is patterned into electrodes and located between the first and second substrates. The TCC(s) include(s) at least one conductive layer including silver, a dielectric layer including zinc oxide under and directly contacting the conductive layer including silver, and a dielectric layer(s) including tin oxide or silicon nitride over the conductive layer including silver. Processing circuitry electrically connects to the electrodes and measures an aspect of the electrodes' capacitance. A laminate material is located between the first and second glass substrates. The TCC(s), when blanket deposited, may have a visible transmission of at least 88%, a sheet resistances of no more than 10 ohms per square, and a haze of no more than 0.5%. Mutual and self-capacitance designs are disclosed.

Claims

1. A capacitive touch panel, comprising: first and second substrates that are substantially parallel and spaced apart from one another; at least one multi-layer transparent conductive coating patterned into a plurality of electrodes and located between the first and second substrates, the at least one multi-layer transparent conductive coating including at least one conductive layer comprising silver, a dielectric layer comprising zinc oxide under and directly contacting the conductive layer comprising silver, and a dielectric layer(s) comprising tin oxide or silicon nitride over the conductive layer comprising silver; processing circuitry electrically connected to the plurality of electrodes and configured to measure an aspect of the electrodes' capacitance; and a laminate material located between the first and second substrates.

2. The capacitive touch panel of claim 1, wherein the at least one transparent conductive coating comprises: a first dielectric layer comprising silicon nitride; the dielectric layer comprising zinc oxide; the conductive layer comprising silver; an upper contact layer over and contacting the conductive layer comprising silver; and a second dielectric layer comprising silicon nitride.

3. The capacitive touch panel of claim 2, wherein the at least one transparent conductive coating further comprises a dielectric layer comprising titanium oxide located between at least the first dielectric layer comprising silicon nitride and the dielectric layer comprising zinc oxide.

4. The capacitive touch panel of claim 2, wherein the at least one transparent conductive coating further comprises, between at least the first dielectric layer comprising silicon nitride and the dielectric layer comprising zinc oxide, a layer comprising titanium oxide, another layer comprising zinc oxide, and a layer comprising tin oxide.

5. The capacitive touch panel of claim 2, wherein the at least one transparent conductive coating further comprises, between at least the first dielectric layer comprising silicon nitride and the dielectric layer comprising zinc oxide, a layer comprising titanium oxide, another dielectric layer comprising zinc oxide, and another layer comprising titanium oxide.

6. The capacitive touch panel of claim 2, wherein the at least one transparent conductive coating further comprises an overcoat comprising zirconium oxide.

7. The capacitive touch panel of claim 1, further comprising first and second transparent conductive coatings respectively supported by the first and second substrates on major surfaces of the first and second substrates that face one another, the first and second transparent conductive coatings being patterned into first and second sets of electrodes respectively, and the laminate material laminating the first and second substrates together with the first and second transparent conductive coatings located between the first and second substrates.

8. The capacitive touch panel of claim 7, configured for use as a self-capacitance touch panel.

9. The capacitive touch panel of claim 7, configured for use as a mutual capacitance touch panel, wherein the first set of electrodes comprises transmit electrodes and the second set of electrodes comprises receive electrodes.

10. The capacitive touch panel of claim 1, further comprising first and second transparent conductive coatings respectively supported by opposing major surfaces of the laminate material, the first and second transparent conductive coatings being patterned into first and second sets of electrodes respectively, the capacitive touch panel being configured for use as a self-capacitance touch panel.

11. The capacitive touch panel of claim 10, further comprising an optically clear adhesive bonding together the first and second substrates with the first and second transparent conductive coatings located between the first and second substrates.

12. The capacitive touch panel of claim 1, further comprising: a conductive layer, different from the at least one transparent conductive coating, supported by a major surface of the laminate material; wherein the at least one transparent conductive coating is supported by a major surface of the first substrate that faces the second substrate, the capacitive touch panel being configured for use as a mutual capacitance touch panel.

13. The capacitive touch panel of claim 12, wherein the conductive layer that is different from the at least one transparent conductive coating is supported by the major surface of the laminate material that faces the second substrate.

14. The capacitive touch panel of claim 12, further comprising an optically clear adhesive bonding together the first and second substrates with the laminate material therebetween.

15. The capacitive touch panel of claim 12, wherein the conductive layer that is different from the at least one transparent conductive coating comprises ITO.

16. The capacitive touch panel of claim 1, wherein there is one transparent conductive coating, which is supported by the first substrate on a major surface thereof that faces the second substrate, the one transparent conductive coating being patterned into first and second sets of electrodes that are in substantially the same plane, the capacitive touch panel being configured for use as a mutual capacitance touch panel in which the first set of electrodes function as transmit electrodes and the second set of electrodes function as receive electrodes.

17. The capacitive touch panel of claim 1, wherein there is one transparent conductive coating, which is supported by the laminate material on a major surface thereof, the one transparent conductive coating being patterned into first and second sets of electrodes that are in substantially the same plane, the capacitive touch panel being configured for use as a mutual capacitance touch panel in which the first set of electrodes function as transmit electrodes and the second set of electrodes function as receive electrodes.

18. The capacitive touch panel of claim 17, further comprising an optically clear adhesive bonding together the first and second substrates with the laminate material therebetween.

19. The capacitive touch panel of claim 1, wherein the at least one multi-layer transparent conductive coating, when blanket deposited, has a visible transmission of at least 88% and a sheet resistance of no more than 10 ohms per square.

20. The capacitive touch panel of claim 1, wherein the at least one multi-layer transparent conductive coating, when blanket deposited, has a haze of no more than 0.5%.

21. The capacitive touch panel of claim 1, wherein the at least one multi-layer transparent conductive coating is room-temperature deposited and is not heat treated.

22. A display assembly, comprising: a flat panel display device; and a capacitive touch panel connected to the flat panel display device, the capacitive touch panel comprising: first and second substrates that are substantially parallel and spaced apart from one another; at least one multi-layer transparent conductive coating patterned into a plurality of electrodes and located between the first and second substrates, the at least one multi-layer transparent conductive coating including at least one conductive layer comprising silver, a dielectric layer comprising zinc oxide under and directly contacting the conductive layer comprising silver, and a dielectric layer(s) comprising tin oxide or silicon nitride over the conductive layer comprising silver; processing circuitry electrically connected to the plurality of electrodes and configured to measure an aspect of the electrodes' capacitance; and a laminate material located between the first and second substrates.

23. The display assembly of claim 22, wherein the flat panel display device is an LCD device.

24. The display assembly of claim 22, wherein the capacitive touch panel has a diagonal of at least 50 inches.

25. The display assembly of claim 22, wherein the at least one multi-layer transparent conductive coating, when blanket deposited, has a visible transmission of at least 88%, a sheet resistances of no more than 10 ohms per square, and a haze of no more than 0.5%.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) These and other features and advantages may be better and more completely understood by reference to the following detailed description of exemplary illustrative embodiments in conjunction with the drawings, of which:

(2) FIGS. 1(a) to 1(h) illustrate examples of related art projected capacitive touch panels;

(3) FIG. 2(a) illustrates a top or bottom plan layout of a projected capacitive touch panel according to an example embodiment;

(4) FIG. 2(b) illustrates a schematic representation of circuitry for the projected capacitive touch panel of FIG. 2(a) and/or 3;

(5) FIG. 3 illustrates a top or bottom plan layout of a projected capacitive touch panel according to another example embodiment;

(6) FIG. 4 illustrates a cross-sectional view of a silver-inclusive transparent conductive coating for a touch panel of FIGS. 2-3, according to certain example embodiments;

(7) FIG. 5 illustrates a cross-sectional view of another example silver-inclusive transparent conductive coating for a touch panel of FIGS. 2-3;

(8) FIG. 6 illustrates a cross-sectional view of yet another example silver-inclusive transparent conductive coating for a touch panel of FIGS. 2-3;

(9) FIG. 7 is a cross-sectional view of a display assembly according to an example embodiment of this invention, including a touch panel according to any of FIGS. 2-6 coupled to a liquid crystal panel, for use in electronic devices such as portable phones, portable pads, computers, and/or so forth, in accordance with certain example embodiments;

(10) FIG. 8 is a cross-sectional view of a touch panel display subassembly using a self-capacitance design approach, in accordance with certain example embodiments;

(11) FIG. 9 is a cross-sectional view of a touch panel display subassembly using another self-capacitance design approach, in accordance with certain example embodiments;

(12) FIG. 10 is a cross-sectional view of a touch panel display subassembly using a mutual capacitance design approach, in accordance with certain example embodiments;

(13) FIG. 11 is a cross-sectional view of a touch panel display subassembly using another mutual capacitance design approach, in accordance with certain example embodiments; and

(14) FIG. 12 is a cross-sectional view of a touch panel display subassembly using yet another mutual capacitance design approach, in accordance with certain example embodiments.

DETAILED DESCRIPTION

(15) A detailed description of certain example embodiments is provided with reference to the accompanying drawings. Like reference numerals indicate like parts throughout the drawings.

(16) FIG. 2(a) illustrates a top/bottom plan layout of a projected capacitive touch panel according to an example embodiment of this invention. Referring to FIG. 2(a), touch panel 20 is provided. Touch panel 20 includes a matrix of electrodes including n columns and m rows, provided on a substrate 40. The matrix of row/column electrodes is typically provided on the side of the substrate (e.g., glass substrate 40) that is opposite the side touched by person(s) using the touch panel. In other words, when the touch panel is touched by a finger, stylus, or the like, the substrate 40 is typically located between the finger and the matrix of row/column electrodes. A change in capacitance between adjacent row and column electrodes in the matrix as a result of the proximity of a finger or the like is sensed by the electronic circuitry, and the connected circuitry can thus detect where the panel is being touched by a finger or the like.

(17) For example, referring to FIG. 2(a), row 0 includes row electrodes x.sub.0,0, x.sub.1,0, x.sub.2,0, etc., through x.sub.n,0 and columns 0, 1 and 2 respectively include column electrodes y.sub.0, y.sub.1, y.sub.2, etc., through y.sub.n. Optionally, the x electrodes in a column direction may also be grouped for column sensing. The number of row and column electrodes is determined by the size and resolution of the touch panel. In this example, the top-right row electrode is x.sub.n,m.

(18) Each row electrode x.sub.0,0-x.sub.n,m of touch panel 20 is electrically connected to interconnect area 21 and corresponding processing circuitry/software by a conductive trace 22. Each column electrode y.sub.0-y.sub.n is also electrically connected to interconnect area 21 and corresponding processing circuitry/software. The conductive traces 22 are preferably formed of the same transparent conductive material as the row and column electrodes (e.g., same material as at least row electrodes x.sub.0,0, x.sub.1,0, x.sub.2,0, etc.). Thus, in certain example embodiments, the matrix of row and column electrodes and corresponding traces 22 can be formed on the substrate (e.g., glass substrate) 40 by forming a single coating (single or multi-layer coating) on the substrate and by performing only one (or maximum two) photolithography processes. In certain example embodiments, the silver-inclusive coating (e.g., see example coatings of FIGS. 4-6) is formed (e.g., sputter-deposited) on the substrate 40 and is then subjected to photolithography and/or laser patterning to pattern the silver-inclusive coating into traces 22, row electrodes x.sub.0,0, x.sub.1,0, x.sub.2,0, x.sub.0,1, x.sub.,0,2, x.sub.0,3, etc., through x.sub.n,m, and column electrodes y.sub.0-y.sub.n.

(19) Because the row electrodes x.sub.0,0-x.sub.n,m, column electrodes y.sub.0-y.sub.n, and traces 22 do not overlap as viewed from above/below, the row electrodes x.sub.0,0-x.sub.n,m, column electrodes y.sub.0-y.sub.n, and traces 22 may be formed on the same plane parallel (or substantially parallel) to substrate 40 on which the electrodes and traces are formed. Significant portions of traces 22 may also be parallel (or substantially parallel) to the column electrodes in the plane parallel (or substantially parallel) to the substrate 40.

(20) Accordingly, touch panel 20 may be made via a smaller number of photolithography or laser patterning steps while achieving traces that achieve sufficient transparency and conductivity, thereby reducing production costs and resulting in a more efficient touch panel for use in a display assembly or the like.

(21) FIG. 2(b) illustrates a schematic representation of circuitry for the touch panel 20 illustrated in FIG. 2(a), according to certain example embodiments. In touch panel 20, there is a capacitance between each row electrode and the adjacent column electrode (for example, between row electrode x.sub.0,0 and column electrode y.sub.0). This capacitance can be measured by applying a voltage to a column electrode (for example, column electrode y.sub.0) and measuring the voltage of an adjacent row electrode (for example, row electrode x.sub.0,0). When a user brings a finger or conductive stylus close to touch panel 20, changes in the local electrostatic field reduce the mutual capacitance. The capacitance change at individual points on the surface can be measured by measuring each pair of row electrodes and column electrodes in sequence.

(22) The traces 22 of each row electrode in the same row (for example, the traces 22 of row electrodes x.sub.0,0, x.sub.1,0, x.sub.2,0, etc., through x.sub.n,0 of row 0) may be electrically connected together (as shown in FIG. 2(b)). The interconnection of the first row segments to each other, second row segments to each other, etc., may be made on a flexible circuit(s) attached at the periphery of the touch panel in the interconnection area, so that no cross-overs are needed on the glass. In that instance, a voltage is applied to a column electrode and the voltage of each row is measured in sequence before the process is repeated with a voltage applied to another column. Alternatively, each trace 22 may be connected to signal processor 25 and the voltage of each trace 22 may be measured individually.

(23) The same capacitance may be measured by applying a voltage to a row electrode and measuring the voltage on an adjacent column electrode rather than applying a voltage to a column electrode and measuring the voltage of an adjacent row electrode.

(24) Signal processing (for example, applying and measuring voltages, measuring the capacitance between adjacent electrodes, measuring changes in capacitance over time, outputting signals in response to user inputs, etc.) may be performed by signal processor 25. Signal processor 25 may be one or more hardware processors, may include volatile or non-volatile memory, and may include computer-readable instructions for executing the signal processing. Signal processor 25 is electrically connected to the column electrodes y.sub.0-y.sub.n and electrically connected to the row electrodes x.sub.0,0-x.sub.n,m through the traces 22. Signal processor 25 may or may not be located on the same plane as row electrodes x.sub.0,0-x.sub.n,m, column electrodes y.sub.0-y.sub.n, and traces 22 (for example, in interconnect area 21 of FIG. 2(a)).

(25) FIG. 3 illustrates a layout of a projected capacitive touch panel according to other example embodiments. Referring to FIG. 3, touch panel 30 is similar to touch panel 20 of FIG. 2(a), except that touch panel 30 is divided into upper section 31 and lower section 32, each of which includes a matrix of electrodes including n columns and m rows. For example, row 0 of upper section 31 includes row electrodes x.sub.0,0, x.sub.1,0, x.sub.2,0, etc., through x.sub.n,0. Upper section 31 also includes column electrodes y.sub.0, y.sub.1, y.sub.2, etc., through y.sub.n. Likewise, lower section 32 would also include row electrodes, and column electrodes y.sub.0-y.sub.n that may be electrically separate from the column electrodes y.sub.0-y.sub.n of the upper section 31.

(26) Thus, lower section 32 also includes a matrix of row electrodes including n columns and m rows, and n column electrodes. Lower section 32 may have more or less rows than upper section 31 in different example embodiments.

(27) The number of row and column electrodes of touch panel 30 is determined by the size and resolution of the touch panel.

(28) Each column electrode of upper section 31 is electrically connected to interconnect area 21, and each row electrode of upper section 31 is electrically connected to interconnect area 21 by a trace 22. As with the FIG. 2 embodiment, traces may or may not be used for connecting the column electrodes of upper section 31 to the interconnect area. Each column electrode of lower section 32 is electrically connected to interconnect area 21′ and each row electrode of lower section 32 is electrically connected to interconnect area 21′ by a trace 22. Again, traces may or may not be used for connecting the column electrodes of the lower section 32 to the interconnect area 21′.

(29) Still referring to FIG. 3, touch panel 30 is similar to touch panel 20 in that there is a capacitance between each row electrode and the adjacent column electrode which may be measured by applying a voltage to a column electrode and measuring the voltage of an adjacent row electrode (or, alternatively, by applying a voltage to a row electrode and measuring the voltage of an adjacent column electrode). When a user brings a finger or conductive stylus close to touch panel 30, changes in the local electrostatic field reduce the mutual capacitance. The capacitance change at individual points on the surface can be measured by measuring the mutual capacitance of each pair of row electrodes and column electrodes in sequence.

(30) Because the row electrodes and column electrodes illustrated in FIG. 3 do not overlap, the row electrodes and column electrodes may be formed on the same plane, in the manner explained above in connection with FIG. 2. Accordingly, electrode structure for the touch panel 30 may be thin in nature and may be patterned with one process (for example, one photolithography process or one laser patterning process), which can reduce the production cost of the projected capacitive touch panel.

(31) As one of ordinary skill in the art will recognize, touch panels 20 and 30 described are not limited to the orientation described above and shown in FIGS. 2-3. In other words, the terms “row,” “column,” “x-axis,” and y-axis” as used in this application are not meant to imply a specific direction. Touch panel 20 of FIG. 2(a), for example, may be modified or rotated such that interconnect area 21 is located in any part of touch panel 20.

(32) As illustrated in FIGS. 2(a) and 3, narrow transparent conductive traces 22 are routed to electrically connect electrodes to interconnect area 21 (and interconnect area 21′). Because of the large resistance of the narrow ITO traces, narrow ITO traces may only been used in small touch panels, such as for smart phones. To use one of the layouts illustrated in FIGS. 2(a) and 3 on larger touch panels (for example, measuring more than 10 inches diagonally), a transparent conductive coating with low sheet resistance may be used. The silver inclusive coatings shown in FIGS. 4-6, for use in forming the row/column electrodes and traces 22, are advantageous in this respect because they have a much lower sheet resistance than typical conventional ITO traces.

(33) Examples of silver-inclusive transparent conductive coatings (TCCs) with low sheet resistance, for forming row electrodes, column electrodes, and traces 22 are illustrated in FIGS. 4-6, according to certain example embodiments. In each of FIGS. 4-6, the low sheet resistance and high transparency of the TCC allow the TCC to form the long narrow traces 22 of the touch panels illustrated in FIGS. 2(a) and 3, as well as the row and column electrodes.

(34) Referring to FIG. 4, coating (or layer system) 41 is provided, either directly or indirectly, on substrate 40. Substrate 40 may be, for example, glass. Coating 41 may include, for example, bottom dielectric silicon nitride based and/or inclusive layer 42 which may be Si.sub.3N.sub.4 (which may or may not be doped with other material(s) such as aluminum in certain example instances) or of the Si-rich type for haze reduction, or of any other suitable stoichiometry silicon nitride in different embodiments of this invention; a dielectric high index layer 43 of or including a material such as titanium oxide or niobium oxide, which may include titanium oxide (e.g., TiO.sub.2 or other suitable stoichiometry); and first and second dielectric layers of or including zinc oxide 44a and 44b that may be split by a dielectric “glue” layer 45 of or including tin oxide; a silver-based conductive layer 46; an upper contact layer including nickel and/or chromium 47 which may be oxided and/or nitrided; a second layer of or including tin oxide 48; and an outer-most protective layer 49 of or including silicon nitride. The dielectric high index layer 43 may be fully oxidized or sub-stoichiometric in different example embodiments. The seed layer comprising zinc oxide 44b and the upper contact layer of or including nickel and/or chromium 47 directly contact the silver-based conductive layer 46.

(35) While various thicknesses and materials may be used in layers in different embodiments of this invention, example thicknesses and materials for the respective sputter-deposited layers of coating 41 on the glass substrate 40 in the FIG. 4 embodiment are as follows, from the glass substrate outwardly:

(36) TABLE-US-00001 TABLE 1 More Preferred Preferred Example Example Thickness Thickness Thickness 1 Thickness 2 Ref Material (Å) (Å) (Å) (Å) 42 Si.sub.xN.sub.y  1-500 100-300 160 160 43 TiO.sub.x 75-125  85-115 100 100 44a ZnO 35-75  40-70 60 50 45 SnO 35-200  50-135 100 70 44b ZnO 30-200  40-130 60 100 46 Ag 60-110  70-100 85 85 47 NiCrOx 20-40  23-37 30 30 48 SnO 150-275  170-255 220 200 49 Si.sub.xN.sub.y  1-1000 100-500 220 250

(37) In certain example embodiments, the layers 44a and 44b may have matching or substantially matching thicknesses. For instance, the thicknesses of these layers may differ by no more than 15% in certain example instances, no more than 10% in other example instances, and no more than 3-5% in yet other example instances. This is the case with Example 1 above, but is not the case with Example 2 above.

(38) Referring to FIG. 5, another example transparent conductive coating (or layer system) 51 is provided, either directly or indirectly, on substrate 40. Substrate 40 may be, for example, glass. As with the FIG. 4 embodiment, FIG. 5 includes, for example, bottom dielectric silicon nitride based and/or inclusive layer 42 and a dielectric high index layer 43a, which may be of or include titanium oxide or niobium oxide (e.g., TiO.sub.2 or other suitable stoichiometry). However, as shown in FIG. 5, the first and second dielectric layers comprising zinc oxide 44a and 44b (which may be doped with Al or the like) are split by a layer of or including titanium oxide (e.g., TiO.sub.2 or other suitable stoichiometry) 43b. Another way of thinking about this is that the lower dielectric high index layer comprising titanium oxide 43 is split into two sub-layers (43a and 43b) by a first layer of or including zinc oxide 44a. An upper contact layer including nickel and/or chromium 47, which may be oxided and/or nitrided, a layer of or including tin oxide 48, a dielectric layer of or including zinc oxide 44c, and another dielectric silicon nitride based layer 49 may be provided above a conductive silver-based layer 46. A third zinc oxide inclusive layer 44c may be interposed between the layer comprising tin oxide 48 and the silicon nitride based layer 49. An optional zirconium oxide inclusive top coat 50 is shown as an outer-most layer (and thus above the silicon nitride based layer 49) in FIG. 5. This zirconium oxide inclusive top coat 50 may provide further durability improvements.

(39) While various thicknesses and materials may be used in layers in different embodiments of this invention, example thicknesses and materials for the respective sputter-deposited layers on the substrate 40 in the FIG. 5 embodiment are as follows, from the substrate 40 outwardly:

(40) TABLE-US-00002 TABLE 2 More Preferred Preferred Example Example Thickness Thickness Thickness 1 Thickness 2 Ref. Material (Å) (Å) (Å) (Å) 42 Si.sub.xN.sub.y  1-500  10-300 156 156 43c TiO.sub.x 15-50  30-40 33 35 44a ZnO 70-200  95-125 114 110 43b TiO.sub.x 15-50  30-40 33 35 44b ZnO 70-200  95-125 114 110 46 Ag 70-120  80-100 90 90 47 NiCrOx  1-100 10-50 30 30 48 SnO 110-150  115-145 130 130 44c ZnO 70-200  95-125 109 109 49 Si.sub.xN.sub.y 115-185  125-155 140 140 50 ZrO.sub.x  1-200 10-80 40 40

(41) FIG. 6 illustrates another example transparent conductive coating that may be used to form the row and column electrodes, and traces 22, in FIGS. 2-3. The coating of FIG. 6 includes, from the glass substrate 40 outwardly, dielectric layer of or including silicon nitride, lower contact layer 75 of or including NiCr, NiCrOx, NiCrNx or the like, conductive layer 46 of or including silver, upper contact layer 47 of or including NiCr, NiCrOx, NiCrNx or the like, dielectric layer 49 of or including silicon nitride, and optional overcoat 50 of a material such as zirconium oxide.

(42) A projected capacitive touch panel may be formed by using a silver-inclusive TCC (for example, coating 41 of FIG. 4, coating 51 of FIG. 5, or coating 61 of FIG. 6) patterned on a substrate 40 (for example, glass) in a layout to form the row electrodes x.sub.0,0-x.sub.n,m, column electrodes y.sub.0-y.sub.n, and traces 22 of touch panels 20 or 30 illustrated in FIGS. 2-3. Because the silver-inclusive TCC may be patterned with one photolithography process and/or laser patterning process, the overall cost of the projected capacitive panel is reduced.

(43) Silver-inclusive TCCs 41, 51, 61 are inexpensive, have a low sheet resistance (preferably less than 15 ohms/square, more preferably less than about 10 or 5 ohms/square, with an example being approximately 4 ohms per square) and maintain high transmittance (preferably, greater than 70%, more preferably greater than about 80 percent). The TCC (41, 51 or 61) may be deposited on a major surface of the substrate 40 away from the user so as to reduce corrosive exposure to the atmosphere or contact with a finger or stylus. For example, the example display assembly shown in FIG. 7 includes a touch panel (20 or 30) mounted on a liquid crystal display panel. The row electrodes, column electrodes, and traces are form at 41, 51, 61 in FIG. 7 on the surface of the glass substrate 40 opposite the finger, and the touch panel (20, 30) may be adhered to the LCD panel via an index-matching adhesive layer 85. The LCD panel includes first and second substrates (e.g., glass substrates) 100, 200 with a liquid crystal layer 300 provided therebetween. In order to form a touchscreen, the touch panel 20, 30 may be mounted on the LCD panel with a small air gap (not shown), or bonded to the display with an index-matching adhesive 85.

(44) The pixel pitch for projected capacitive touch panels may, for example, be in the range of from about 6 to 7 mm. Touch location can be determined more accurately, to about 1 mm, by signal processing and interpolation. If the line width/spacing for the traces 22 is approximately 10 μm to 20 μm, it can be calculated that a projected capacitive touch panel of at least 20 inches (measured diagonally) is possible for a TCC sheet resistance of about 4 ohms/square. Further optimization of the routing, signal processing and/or noise suppression allows for production of even larger touch panels (for example, greater than 40 or 50 inches diagonally).

(45) As will be appreciated from the above, certain example embodiments may include one or more low-E Ag-based coatings in a large area transparent touch electrode (LATTE) that can accommodate multi-touch points. The low-E Ag-based coatings may be used in place of, or together with, ITO in certain example embodiments. Furthermore, mutual capacitance and self-capacitance designs are contemplated herein.

(46) As described above, a self-capacitance design approach generally is concerned with the capacitance of a single electrode to ground. Human body capacitance (or capacitance from a stylus or the like) increases the capacitance of the electrode to ground. In a self-capacitance sensor system, each electrode in an array may be measured individually, e.g., as rows and columns are scanned or the like. Self-capacitance design sensors may be used in connection with certain example embodiments. For example, FIG. 8 is a cross-sectional view of a touch panel display subassembly 80 using a self-capacitance design approach, in accordance with certain example embodiments. The FIG. 8 example subassembly 80 includes first and second glass substrates 82a and 82b respectively supporting first and second low-E Ag-based coatings 84a and 84b. The first and second low-E Ag-based coatings 84a and 84b are separate self-capacitance touch electrodes, with one measuring a first direction (e.g., the x-direction) and the other measuring a second direction (e.g., the y-direction). A laminate material 86 may be used to bond the first and second substrates 82a and 82b together, with the first and second low-E Ag-based coatings 84a and 84b being protected by virtue of being sandwiched between the first and second substrates 82a and 82b. The laminate material 86 may be a generally optically clear material such as, for example, PET, PVB, EVA, PU, and/or the like.

(47) FIG. 9 is a cross-sectional view of a touch panel display subassembly 90 using another self-capacitance design approach, in accordance with certain example embodiments. The FIG. 9 example subassembly 90 functions similarly to the FIG. 8 example subassembly 80. However, in this case, the laminate material 86′ in the FIG. 9 example is shown supporting both of the first and second low-E Ag-based coatings 84a and 84b. The laminate material 86′ may be pre-coated with the first and second low-E Ag-based coatings 84a and 84b. It may be received in a roll form, and rolled out in certain manufacturing methods, in order to orient the first and second low-E Ag-based coatings 84a and 84b towards the first and second substrates 82a and 82b. An optically clear adhesive (OCA) may be used to bond the subassembly 90 together. In this regard, first and second OCA materials 92a and 92b are shown as being interposed between the laminate material 86′ and the first and second glass substrates 82a and 82b, respectively.

(48) In a mutual capacitance sensor, capacitance is measured between two electrodes. One electrode functions as the drive or transmit electrode, and the other electrode functions as the sense or receive electrode. Human body capacitance (or stylus capacitance, etc.) “steals” the charge, which decreases the capacitance between the electrodes. In a mutual capacitance sensor system, each electrode intersection in an array of electrode pairings may be measured individually. Mutual capacitance design sensors also may be used in connection with certain example embodiments. For example, FIG. 10 is a cross-sectional view of a touch panel display subassembly 101 using a mutual capacitance design approach, in accordance with certain example embodiments. In the FIG. 10 example subassembly 101, the first low-E coating 84a′ is used for transmission and the second low-E coating 84b′ is used for receiving. It will be appreciated that the transmit and receive functionality may be reversed in certain example embodiments. Similar to the FIG. 8 example, the FIG. 10 example subassembly 101 has the first and second low-E coatings 84a′ and 84b′ supported by the first and second glass substrates 82a and 82b, respectively, with the subassembly 101 being bonded together via laminate material 86. The first and second low-E coatings 84a′ and 84b′ may be organized as rows and columns in two layers, in a “bar and stripe” configuration, etc.

(49) FIG. 11 is a cross-sectional view of a touch panel display subassembly 111 using another mutual capacitance design approach, in accordance with certain example embodiments. In the FIG. 11 example subassembly 111, the transmit and receive electrodes are of different types and are supported by different types of substrates. More particularly, in FIG. 11, the first glass substrate 82a supports a transmit or receive low-E coating 113, and the laminate material 115 supports the other type (receive or transmit) of electrode 117, which is shown as being of or including ITO. The laminate material 115 may be PET, PVB, EVA, PU, and/or the like. Similar to as noted above, it may be a rolled material supporting the ITO 117, and it may be unrolled prior to subassembly 111 being laminated together. First and second OCA materials 92a and 92b are shown as being interposed between the laminate material 115 and the first and second glass substrates 82a and 82b, respectively. Although the electrode 117 is shown as being of or include ITO, it will be appreciated that another material (such as, for example, a metal mesh, carbon nanotubes, carbon nanobuds, and/or the like) may be used instead of the ITO. It also will be appreciated that instead of the shown configuration, (1) the low-E coating 113 may be supported by the laminate material 115 and the other electrode 117 may be supported by the first glass substrate 82a as if they were reversed in the FIG. 11 example, (2) the low-E coating 113 may be supported by the second glass substrate 82b and other electrode 117 may be supported by the laminate material 115 on a side opposite the second glass substrate 82b, (3) other electrode 117 may be supported by the second glass substrate 82b and the low-E coating 113 may be supported by the laminate material 115 on a side opposite the second glass substrate 82b, etc.

(50) In addition to the possible configurations described above in connection with FIG. 10, a one layer arrangement may be used in certain example embodiments. This may include, for example, a configuration with an interlocking diamond pattern with bridges (e.g., similar to FIG. 1(a) or the like), in a caterpillar design (e.g., similar to FIG. 3 or the like), etc. This may be used in connection with a design arrangement similar to that shown in FIG. 7, or in FIG. 12. That is, both the FIG. 7 and the FIG. 12 examples may include a low-E coating that is patterned with a single layer mutual touch pattern, with the low-E coating being used for both transmit and receive functionality in a mutual capacitance design. In the FIG. 7 example, the substrate supporting the low-E coating is the glass substrate. In the FIG. 12 example, the low-E coating 123 may be supported by the laminate material 86. The FIG. 12 example subassembly 121 also includes first and second OCA materials 92a and 92b being interposed between the laminate material 86 and the first and second glass substrates 82a and 82b, respectively.

(51) It will be appreciated that the low-E coatings discussed in connection with FIGS. 8-12 may be the same as, or similar to, the low-E coatings described above (e.g., in connection with FIGS. 4-6).

(52) It will be appreciated that techniques used herein may be used in connection with glass, non-glass (e.g., plastic), or both glass and non-glass substrates. For instance, in certain example embodiments, in the case where one or both of the conductive coatings are on a plastic film or other non-glass substrate, there need not be a second glass substrate but instead the non-glass substrate may be directly bonded to the display.

(53) It will be appreciated that the low-E Ag-based coatings used in large area transparent touch electrodes as described herein are advantageous over ITO-based electrodes and other technologies for a number of different reasons. For example, low-E Ag-based coatings as described herein tend to have a lower haze as compared to ITO-based coatings. The former typically will have haze less than 0.5%, more preferably less than 0.4% and sometimes as low as 0.25%. ITO, on the other hand, typically has a haze even when in a heat treated state of around 1%, and sometimes in the 0.75%-1% range. The reduction in haze is advantageous when it comes to providing higher resolution displays (e.g., as there currently is a move towards providing “4K resolution” products), and for facilitating readability in outdoor and sunny or high-light conditions. Reflection also tends to be lower for the low-E Ag-based coatings described herein, as compared to ITO-based coatings. The low-E Ag-based coatings described herein may have a reflection lower than 10%, more preferably lower than 7%, and typically around 5%. By contrast, ITO-based coatings typically have a reflection of about 10%.

(54) In a somewhat related regard, low-E Ag-based coatings as described herein offer a better resistivity/transmission tradeoff as compared to ITO-based coatings. ITO-based coatings typically offer a resistance of about 100 ohms per square with 89-90% transmission after heat treatment, whereas low-E Ag-based coatings as described herein can achieve a resistance of less than 25 ohms per square, preferably less than 15 ohms per square, more preferably less than 10 ohms per square, still more preferably less than 10 ohms per square, and sometimes less than 7 ohms per square, with 88% transmission. The low-E Ag-based coatings as described herein preferably have a transmission of at least 80%, more preferably at least 85%, and still more preferably at least 87-88%. The move to low-E Ag-based coatings as described herein is advantageous in this respect as it provides for lower power consumption, faster touch response times (lower latency), and enables capacitive touch technology to be employed on larger displays. ITO-based sensors with these metrics typically can be used with a 40 inch maximum panel, whereas the example techniques described herein can be used in connection with 40 inch, 50 inch, 110 inch, or even greater sized panels (e.g., as measured by a diagonal of the panel). It will be appreciated that the transmission, sheet resistance, haze, reflection measurements apply when the low-E Ag-based coating is blanked coated onto a 3 mm thick clear soda-lime-silica glass, absent an antireflective coating.

(55) In order to achieve the resistivity/transmission tradeoff noted above, ITO typically is thermally activated, post deposition, to increase the material's optical transmission and decrease its sheet resistance. The heat treatment process enables ITO-based coatings to improve their performance. Unfortunately, however, this introduces an extra processing step and limits the types of substrates to which they can be easily applied. By contrast, a low-E Ag-based coating may be formed using a room temperature coating process that does not necessarily require thermal activation. This opens the door to using different types of substrates (e.g., plastic substrates, PET, PVB, etc.), while providing significantly better optical and resistance properties as compared to non-heat treated ITO. In certain example embodiments, none of the touch panel substrates will be heat treated. In certain example embodiments, none of the touch panel substrates on which the low-E Ag-based coating is formed will be heat treated. On the other hand, in certain example embodiments, the low-E Ag-based coating of certain example embodiments may be heat treatable, which would allow large stock sheets to be coated, cut to size, and then heat treated (e.g., thermally tempered) with the coatings thereon, which can reduce manufacturing costs significantly.

(56) ITO in general also is brittle, and the heat treatment can increase its brittleness. By contrast, low-E Ag-based coatings as described herein are more flexible and thus can be more easily incorporated into flexible, curved, and other types of displays.

(57) ITO on PET is shipped in a non-heat treated condition on cylindrical rolls and may be heat treated when it is received by a customer to compensate for the rigidity of heat treated ITO. But because low-E, Ag-based coatings of the type described herein do not necessarily need to be thermally activated to achieve a good resistivity/transmission tradeoff, a customer can use a low-E Ag-based coating on PET/PVB directly off a roll without heat treating in some instances.

(58) It will be appreciated that the technology disclosed herein may be used in connection with a wide variety of applications including, for example, electronic displays, vending machines, mirrors, storefronts, office walls, etc.

(59) It will be appreciated that certain self-capacitance designs may be thought of as being “dual self-capacitance designs,” e.g., in the sense that there may be two self-capacitance sensors (e.g., one on surface 2 and one on surface 3), with the surface 2 sensor measuring X position and the surface 3 sensor measuring Y position, or the like. It also will be appreciated that although certain example sensor configurations have been described in detail, other sensor configurations may be used in connection with the technology disclosed herein. See, for example, Geoff Walker's “Fundamentals of Projected-Capacitive Touch Technology” presentation, version 1.2, for SID Display Week 2014, dated Jun. 1, 2014, the entire contents of which are hereby incorporated herein by reference.

(60) In certain example embodiments, glass substrate 40 with coating 41, 51, 61 thereon may be heat treated (e.g., thermally tempered), e.g., after coating, or chemically strengthened before coating. In general, the substrates described herein may be heat treated (e.g., heat strengthened and/or thermally tempered), and/or chemically tempered, in certain example embodiments. The terms “heat treatment” and “heat treating” as used herein mean heating the article to a temperature sufficient to achieve thermal tempering and/or heat strengthening of the glass inclusive article. This definition includes, for example, heating a coated article in an oven or furnace at a temperature of at least about 550 degrees C., more preferably at least about 580 degrees C., more preferably at least about 600 degrees C., more preferably at least about 620 degrees C., and most preferably at least about 650 degrees C. for a sufficient period to allow tempering and/or heat strengthening. This may be for at least about two minutes, or up to about 10 minutes, in certain example embodiments.

(61) Although an element, layer, layer system, coating, or the like, may be said to be “on” or “supported by” a substrate, layer, layer system, coating, or the like, other layers and/or materials may be provided therebetween.

(62) In certain example embodiments, a capacitive touch panel is provided. First and second substrates (e.g., glass substrates) are substantially parallel and spaced apart from one another. At least one multi-layer transparent conductive coating is patterned into a plurality of electrodes and located between the first and second substrates, with the at least one multi-layer transparent conductive coating including at least one conductive layer comprising silver, a dielectric layer comprising zinc oxide under and directly contacting the conductive layer comprising silver, and a dielectric layer(s) comprising tin oxide or silicon nitride over the conductive layer comprising silver. Processing circuitry is electrically connected to the plurality of electrodes and configured to measure an aspect of the electrodes' capacitance. A laminate material is located between the first and second substrates.

(63) In addition to the features of the previous paragraph, in certain example embodiments, the at least one transparent conductive coating may comprise: a first dielectric layer comprising silicon nitride; the dielectric layer comprising zinc oxide; the conductive layer comprising silver; an upper contact layer over and contacting the conductive layer comprising silver; and a second dielectric layer comprising silicon nitride.

(64) In addition to the features of the previous paragraph, in certain example embodiments, the at least one transparent conductive coating may further comprise a dielectric layer comprising titanium oxide located between at least the first dielectric layer comprising silicon nitride and the dielectric layer comprising zinc oxide.

(65) In addition to the features of either of the two previous paragraphs, in certain example embodiments, the at least one transparent conductive coating may further comprise, between at least the first dielectric layer comprising silicon nitride and the dielectric layer comprising zinc oxide, a layer comprising titanium oxide, another layer comprising zinc oxide, and a layer comprising tin oxide; and/or the at least one transparent conductive coating may further comprise, between at least the first dielectric layer comprising silicon nitride and the dielectric layer comprising zinc oxide, a layer comprising titanium oxide, another dielectric layer comprising zinc oxide, and another layer comprising titanium oxide.

(66) In addition to the features of any of the four previous paragraphs, in certain example embodiments, the at least one transparent conductive coating may further comprise an overcoat comprising zirconium oxide.

(67) In addition to the features of any of the five previous paragraphs, in certain example embodiments, first and second transparent conductive coatings may be respectively supported by the first and second substrates on major surfaces of the first and second substrates that face one another, with the first and second transparent conductive coatings being patterned into first and second sets of electrodes respectively, and with the laminate material laminating the first and second substrates together with the first and second transparent conductive coatings located between the first and second substrates. In such cases, in certain example embodiments, the capacitive touch panel may be configured for use as a self-capacitance touch panel and/or for use as a mutual capacitance touch panel, e.g., where the first set of electrodes comprises transmit electrodes and the second set of electrodes comprises receive electrodes. In a related regard, in addition to the features of any of the five previous paragraphs, in certain example embodiments, first and second transparent conductive coatings may be respectively supported by opposing major surfaces of the laminate material, with the first and second transparent conductive coatings being patterned into first and second sets of electrodes respectively, and with the capacitive touch panel being configured for use as a self-capacitance touch panel. In such cases, in certain example embodiments, an optically clear adhesive may bond together the first and second substrates with the first and second transparent conductive coatings located between the first and second substrates. In a related regard, in addition to the features of any of the five previous paragraphs, in certain example embodiments, a conductive layer, different from the at least one transparent conductive coating, may be supported by a major surface of the laminate material, and the at least one transparent conductive coating may be supported by a major surface of the first substrate that faces the second substrate, with the capacitive touch panel being configured for use as a mutual capacitance touch panel. In such cases, in certain example embodiments, the conductive layer that is different from the at least one transparent conductive coating may be supported by the major surface of the laminate material that faces the second substrate; and/or an optically clear adhesive may bond together the first and second substrates with the laminate material therebetween; and/or the conductive layer that is different from the at least one transparent conductive coating may comprise ITO. In a related regard, in addition to the features of any of the five previous paragraphs, in certain example embodiments, there may be one transparent conductive coating, which is supported by the first substrate on a major surface thereof that faces the second substrate, with the one transparent conductive coating being patterned into first and second sets of electrodes that are in substantially the same plane, and with the capacitive touch panel being configured for use as a mutual capacitance touch panel in which the first set of electrodes function as transmit electrodes and the second set of electrodes function as receive electrodes. In a related regard, in addition to the features of any of the five previous paragraphs, in certain example embodiments, there may be one transparent conductive coating, which is supported by the laminate material on a major surface thereof, with the one transparent conductive coating being patterned into first and second sets of electrodes that are in substantially the same plane, and with the capacitive touch panel being configured for use as a mutual capacitance touch panel in which the first set of electrodes function as transmit electrodes and the second set of electrodes function as receive electrodes. In such cases, in certain example embodiments, an optically clear adhesive may bond together the first and second substrates with the laminate material therebetween.

(68) In addition to the features of any of the six previous paragraphs, in certain example embodiments, the at least one multi-layer transparent conductive coating, when blanket deposited, may have a visible transmission of at least 88% and/or a sheet resistance of no more than 10 ohms per square.

(69) In addition to the features of any of the seven previous paragraphs, in certain example embodiments, the at least one multi-layer transparent conductive coating, when blanket deposited, may have a haze of no more than 0.5%.

(70) In addition to the features of any of the eight previous paragraphs, in certain example embodiments, the at least one multi-layer transparent conductive coating may be room-temperature deposited and/or may be not heat treated.

(71) In certain example embodiments, a display assembly including a flat panel display device is provided. A capacitive touch panel is connected to the flat panel display device. The capacitive touch panel comprises: first and second substrates (e.g., glass substrates) that are substantially parallel and spaced apart from one another; at least one multi-layer transparent conductive coating patterned into a plurality of electrodes and located between the first and second substrates, the at least one multi-layer transparent conductive coating including at least one conductive layer comprising silver, a dielectric layer comprising zinc oxide under and directly contacting the conductive layer comprising silver, and a dielectric layer(s) comprising tin oxide or silicon nitride over the conductive layer comprising silver; processing circuitry electrically connected to the plurality of electrodes and configured to measure an aspect of the electrodes' capacitance; and a laminate material located between the first and second substrates.

(72) In addition to the features of the previous paragraph, in certain example embodiments, the flat panel display device may be an LCD device.

(73) In addition to the features of either of the two previous paragraphs, in certain example embodiments, the capacitive touch panel may have a diagonal of at least 50 inches.

(74) In addition to the features of any of the three previous paragraphs, in certain example embodiments, the at least one multi-layer transparent conductive coating, when blanket deposited, may have a visible transmission of at least 88%, a sheet resistances of no more than 10 ohms per square, and/or a haze of no more than 0.5%.

(75) The forgoing exemplary embodiments are intended to provide an understanding of the disclosure to one of ordinary skill in the art. The forgoing description is not intended to limit the inventive concept described in this application, the scope of which is defined in the following claims.