POLYMERISABLE LC MEDIUM AND POLYMER FILM WITH NEGATIVE OPTICAL DISPERSION

Abstract

The invention relates to a polymerisable LC medium with negative optical dispersion, a polymer film with negative optical dispersion obtainable from such a medium, and the use of the polymerisable LC medium and polymer film in optical, electro optical, electronic, semiconducting or luminescent components or devices.

Claims

1. Polymerisable LC medium comprising one or more compounds of formula A, ##STR00036## wherein P is independently of one another, a polymerisable group, Sp is a spacer group or a single bond, L.sup.a is, in case of multiple occurrence identically or differently F, Cl, CN, SCN, SF.sub.5 or straight-chain or branched, optionally mono- or polyfluorinated alkyl, alkoxy, alkenyl, alkynyl, alkylcarbonyl, alkoxycarbonyl, or alkylcarbonyloxy or alkoxycarbonyloxy having 1 to 12 C atoms, or optionally halogenated alkyl, alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 5 C atoms, r is 0, 1, 2, 3 or 4, and one or more compounds of formula I, ##STR00037## wherein U.sup.1,2 are independently of each other selected from ##STR00038## including their mirror images, wherein the rings U.sup.1 and U.sup.2 are each bonded to the group —(B).sub.q— via the axial bond, and one or two non-adjacent CH.sub.2 groups in these rings are optionally replaced by O and/or S, and the rings U.sup.1 and U.sup.2 are optionally substituted by one or more groups L, Q.sup.1,2 are independently of each other CH or SiH, Q.sup.3 is C or Si, B is in each occurrence independently of one another —C≡C—, —CY.sup.1═CY.sup.2— or an optionally substituted aromatic or heteroaromatic group, Y.sup.1,2 are independently of each other H, F, Cl, CN or R.sup.0, q is an integer from 1 to 10, A.sup.1-4 are independently of each other selected from non-aromatic, aromatic or heteroaromatic carbocylic or heterocyclic groups, which are optionally substituted by one or more groups R.sup.5, and wherein each of -(A.sup.1-Z.sup.1).sub.m—U.sup.1—(Z.sup.2-A.sup.2).sub.n- and -(A.sup.3-Z.sup.3).sub.o—U.sup.2—(Z.sup.4-A.sup.4).sub.p- does not contain more aromatic groups than non-aromatic groups, Z.sup.1-4 are independently of each other —O—, —S—, —CO—, —COO—, —OCO—, —O—COO—, —CO—NR.sup.0—, —NR.sup.0—CO—, —NR.sup.0—CO—NR.sup.0—, —OCH.sub.2—, —CH.sub.2O—, —SCH.sub.2—, —CH.sub.2S—, —CF.sub.2O—, —OCF.sub.2—, —CF.sub.2S—, —SCF.sub.2—, —CH.sub.2CH.sub.2—, —(CH.sub.2).sub.3—, —(CH.sub.2).sub.4—, —CF.sub.2CH.sub.2—, —CH.sub.2CF.sub.2—, —CF.sub.2CF.sub.2—, —CH═CH—, —CY.sup.1═CY.sup.2—, —CH═N—, —N═CH—, —N═N—, —CH═CR.sup.0—, —C≡C—, —CH═CH—COO—, —OCO—CH═CH—, CR.sup.0R.sup.00 or a single bond, R.sup.0 and R.sup.00 are independently of each other H or alkyl with 1 to 12 C-atoms, m and n are independently of each other 0, 1, 2, 3 or 4, o and p are independently of each other 0, 1, 2, 3 or 4, R.sup.1-5 are independently of each other identical or different groups selected from H, halogen, —CN, —NC, —NCO, —NCS, —OCN, —SCN, —C(═O)NR.sup.0R.sup.00, —C(═O)X.sup.0, —C(═O)R.sup.0, —NH.sub.2, —NR.sup.0R.sup.00, —SH, —SR.sup.0, —SO.sub.3H, —SO.sub.2R.sup.0, —OH, —NO.sub.2, —CF.sub.3, —SF.sub.5, P-Sp-, optionally substituted silyl, or carbyl or hydrocarbyl with 1 to 40 C atoms that is optionally substituted and optionally comprises one or more hetero atoms, or denote P or P-Sp-, or are substituted by P or P-Sp-, wherein the compounds comprise at least one group R.sup.1-5 denoting or being substituted by P or P-Sp-, P is a polymerizable group, Sp is a spacer group or a single bond.

2. Polymerisable LC medium according to claim 1, characterized in that the compounds of formula A are selected from the following sub formulae, ##STR00039## wherein the parameter P has one of the meanings as given above under claim 1 and x, y, z, are independently of each other 0 or identical or different integers from 1 to 12.

3. Polymerisable LC medium according to claim 1, characterized in that the bridging group, or —(B).sub.q— in formula I, is selected from —C≡C—, —C≡C—C≡C—, —C≡C—C≡C—C≡C—, —C≡C—C≡C—C≡C—C≡C—, ##STR00040## wherein r is 0, 1, 2, 3 or 4, and L is selected from P-Sp-, F, Cl, Br, I, —CN, —NO.sub.2, —NCO, —NCS, —OCN, —SCN, —C(═O)NR.sup.0R.sup.00, —C(═O)X, —C(═O)OR.sup.0, —C(═O)R.sup.0, —NR.sup.0R.sup.00, —OH, —SF.sub.5, optionally substituted silyl, aryl with 1 to 12, and straight chain or branched alkyl, alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 12, wherein one or more H atoms are optionally replaced by F or Cl, wherein R.sup.0 and R.sup.00 are as defined in claim 1 and X is halogen.

4. Polymerisable LC medium according to claim 1, characterized in that the non-aromatic rings of the mesogenic groups where the bridging group is attached, or U.sup.1 and U.sup.2 in formula I, are selected from ##STR00041## wherein R.sup.5 has one of the meanings as given above in claim 1.

5. A polymerisable LC medium according to claim 1, wherein the aromatic and non-aromatic groups, or A.sup.1-4 in formula I, are selected from trans-1,4-cyclohexylene and 1,4-phenylene that is optionally substituted with one or more groups L wherein L is selected from P-Sp-, F, Cl, Br, I, —CN, —NO.sub.2, —NCO, —NCS, —OCN, —SCN, —C(═O)NR.sup.0R.sup.00, —C(═O)X, —C(═O)OR.sup.0, —C(═O)R.sup.0, —NR.sup.0R.sup.00, —OH, —SF.sub.5, optionally substituted silyl, aryl with 1 to 12, and straight chain or branched alkyl, alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 12, wherein one or more H atoms are optionally replaced by F or Cl, wherein R.sup.0 and R.sup.00 are as defined in claim 1 and X is halogen.

6. Polymerisable LC medium according to claim 1, characterized in that the linkage groups connecting the aromatic and non-aromatic cyclic groups in the mesogenic groups, or Z.sup.1-4 in formula I, are selected from —O—, —S—, —CO—, —COO—, —OCO—, —O—COO—, —CO—NR.sup.0—, —NR.sup.0—CO—, —NR.sup.0—CO—NR.sup.0—, —OCH.sub.2—, —CH.sub.2O—, —SCH.sub.2—, —CH.sub.2S—, —CF.sub.2O—, —OCF.sub.2—, —CF.sub.2S—, —SCF.sub.2—, —CH.sub.2CH.sub.2—, —(CH.sub.2).sub.3—, —(CH.sub.2).sub.4—, —CF.sub.2CH.sub.2—, —CH.sub.2CF.sub.2—, —CF.sub.2CF.sub.2—, —CH═CH—, —CY.sup.1═CY.sup.2—, —CH═N—, —N═CH—, —N═N—, —CH═CR.sup.0—, —C≡C—, —CH═CH—COO—, —OCO—CH═CH—, CR.sup.0R.sup.00 or a single bond, wherein R.sup.0, R.sup.00, Y.sup.1 and Y.sup.2 have the meanings given in claim 1

7. Polymerisable LC medium according to claim 1, characterized in that the polymerisable compounds of formula I are selected from the following subformulae: ##STR00042## ##STR00043## ##STR00044## wherein R.sup.1-5, A.sup.1-4, Z.sup.1-4, B, m, n, o, p and q have the meanings given in claim 1.

8. Polymerisable LC medium according to claim 1, characterized in that the polymerisable compounds of formula I are selected from the following subformulae: ##STR00045## ##STR00046## ##STR00047## ##STR00048## ##STR00049## wherein Z has one of the meanings of Z.sup.1 given in claim 1, R has one of the meanings of R.sup.1 given in claim 1 that is different from P-Sp-, and P, Sp, L and r are as defined in claim 1, and the benzene rings in the meosgenic groups are optionally substituted by one or more groups L as defined in claim 1.

9. A polymerisable LC medium according to claim 8, wherein the polymerisable compounds of formula I are selected from sub formulae I 25 or I 26, Z denotes —COO—, and r is in each occurrence 0.

10. A polymerisable LC medium according to claim 1, further comprising one or more further compounds that are optionally polymerisable and/or mesogenic or liquid crystalline.

11. Polymer film obtainable by polymerising a the polymerisable LC medium as defined in claim 1 in its LC phase in an oriented state in form of a thin film.

12. (canceled)

13. An optical, electronic or electro optical device, or a component thereof, comprising a polymer film according to claim 11.

14. An optical component according to claim 13, wherein said optical component is an optically uniaxial film selected from an A-plate, C-plate, negative C-plate or O-plate, a twisted optical retarder, a twisted quarter wave foil (QWF), an optically biaxial film, an achromatic retarder, an achromatic QWF or half wave foil (HWF), a film having a cholesteric, smectic, nematic or blue phase, a film having homeotropic, splayed, tilted, planar or blue-phase alignment, which is uniformly oriented or exhibits a pattern of different orientations.

15. An optical component according to claim 13, wherein said optical component is an optical compensation film for viewing angle enhancement of LCD's, a component in a brightness enhancement films, or an achromatic element in reflective or transflective LCD's.

16. A device or component according to claim 13, wherein said device or component is selected from electrooptical displays, LCDs, optical films, polarizers, compensators, beam splitters, reflective films, alignment layers, color filters, holographic elements, hot stamping foils, colored images, decorative or security markings, LC pigments, adhesives, non-linear optic (NLO) devices, optical information storage devices, electronic devices, organic semiconductors, organic field effect transistors (OFET), integrated circuits (IC), thin film transistors (TFT), Radio Frequency Identification (RFID) tags, organic light emitting diodes (OLED), organic light emitting transistors (OLET), electroluminescent displays, organic photovoltaic (OPV) devices, organic solar cells (O-SC), organic laser diodes (O-laser), organic integrated circuits (O-IC), lighting devices, sensor devices, electrode materials, photoconductors, photodetectors, electrophotographic recording devices, capacitors, charge injection layers, Schottky diodes, planarising layers, antistatic films, conducting substrates, conducting patterns, photoconductors, electrophotographic applications, electrophotographic recording, organic memory devices, biosensors, biochips, optoelectronic devices requiring similar phase shift at multiple wavelengths, combined CD/DVD/HD-DVD/Blu-Rays, reading, writing re-writing data storage systems, or cameras.

17. Device or component according to claim 13, wherein said device or component is selected from electro optical displays, LCDs, optical films, polarizers, compensators, beam splitters, reflective films, alignment layers, filters filters, holographic elements, hot stamping foils, colored images, decorative or security markings, LC pigments, adhesives, non-linear optic (NLO) devices, optical information storage devices, electronic devices, organic semiconductors, organic field effect transistors (OFET), integrated circuits (IC), thin film transistors (TFT), Radio Frequency Identification (RFID) tags, organic light emitting diodes (OLED), organic light emitting transistors (OLET), electroluminescent displays, organic photovoltaic (OPV) devices, organic solar cells (O-SC), organic laser diodes (O-laser), organic integrated circuits (O-IC), lighting devices, sensor devices, electrode materials, photoconductors, photodetectors, electrophotographic recording devices, capacitors, charge injection layers, Schottky diodes, planarising layers, antistatic films, conducting substrates, conducting patterns, photoconductors, electrophotographic applications, electrophotographic recording, organic memory devices, biosensors, biochips.

18. An optical, electronic or electro optical device, or a component thereof, comprising a polymerisable LC material according to claim 1.

19. An optical component according to claim 18, wherein said component is an optically uniaxial film selected from an A-plate, C-plate, negative C-plate or O-plate, a twisted optical retarder, a twisted quarter wave foil (QWF), an optically biaxial film, an achromatic retarder, an achromatic QWF or half wave foil (HWF), a film having a cholesteric, smectic, nematic or blue phase, a film having homeotropic, splayed, tilted, planar or blue-phase alignment, which is uniformly oriented or exhibits a pattern of different orientations.

20. An optical component according to claim 18, wherein said optical component is an optical compensation film for viewing angle enhancement of LCD's, a component in a brightness enhancement films, or an achromatic element in reflective or transflective LCD's.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0069] Preferably, the polymerisable LC medium comprises one, two or more compounds of formula A, more preferably one compound of formula A.

[0070] Preferably, the amount of compounds of formula A in the polymerisable LC medium as a whole is in the range from 1 to 40 wt. %, preferably from 5 to 35 wt. %.

[0071] Preferably, the polymerisable LC medium comprises one, two or more compounds of formula I, more preferably one compound of formula I.

[0072] Preferably, the amount of compounds of formula I in the polymerisable LC medium as a whole is below 50 wt. %, in particular in the range from 25 to 45 wt. %, and especially in the range from 30 to 40 wt. %.

[0073] In a preferred embodiment, the compounds of formula A are selected from the following sub formulae,

##STR00008##

wherein the parameter P has one of the meanings as given above under formula A and x, y, z, are independently of each other 0 or identical or different integers from 1 to 12.

[0074] Furthermore, preference is given to a polymerisable LC medium wherein the compounds of formula A are selected from the following sub formulae,

##STR00009##

[0075] In a further preferred embodiment, the compounds of formula A are selected from the group of compounds of formula A2 or A6, in particular a compound of formula A2.

[0076] In another preferred embodiment, the subgroups forming the bridging group B in formula I are preferably selected from groups having a bonding angle of 120° or more, preferably in the range of 180°. Very preferred are —C≡C— groups or divalent aromatic groups connected to their adjacent groups in para-position, like e.g. 1,4-phenylene, naphthalene-2,6-diyl, indane-2,6-diyl or thieno[3,2-b]thiophene-2,5-diyl.

[0077] Further possible subgroups include —CH═CH—, —CY.sup.1═CY.sup.2—, —CH═N—, —N═CH—, —N═N— and —CH═CR.sup.0— wherein Y.sup.1, Y.sup.2, R.sup.0 have the meanings given above.

[0078] Preferably the bridging group, or —(B).sub.q— in formula I, comprises one or more groups selected from the group consisting of —C≡C—, optionally substituted 1,4-phenylene and optionally substituted 9H-fluorene-2,7-diyl. The subgroups, or B in formula I, are preferably selected from the group consisting of —C≡C—, optionally substituted 1,4-phenylene and optionally substituted 9H-fluorene-2,7-diyl, wherein in the fluorene group the H-atom in 9-position is optionally replaced by a carbyl or hydrocarbyl group.

[0079] Very preferably the bridging group, or —(B).sub.q— in formula I, are selected from —C≡C—, —C≡C—C≡C—, —C≡C—C≡C—C≡C—, —C≡C—C≡C—C≡C—C≡C—,

##STR00010##

wherein r is 0, 1, 2, 3 or 4 and L has the meaning as described below.

[0080] In the guest compounds of the present invention, the non-aromatic rings of the mesogenic groups where the bridging group is attached, like U.sup.1 and U.sup.2 in formula I, are preferably selected from

##STR00011##

wherein R.sup.5 is as defined in formula I.

[0081] Preferably, the aromatic groups A.sup.1-4 in formula I, may be mononuclear, i.e. having only one aromatic ring (like for example phenyl or phenylene), or polynuclear, i.e. having two or more fused rings (like for example napthyl or naphthylene). Especially preferred are mono-, bi- or tricyclic aromatic or heteroaromatic groups with up to 25 C atoms that may also comprise fused rings and are optionally substituted.

[0082] Preferred aromatic groups include, without limitation, benzene, biphenylene, triphenylene, [1,1′:3′,1″ ]terphenyl-2′-ylene, naphthalene, anthracene, binaphthylene, phenanthrene, pyrene, dihydropyrene, chrysene, perylene, tetracene, pentacene, benzpyrene, fluorene, indene, indenofluorene, spirobifluorene, etc.

[0083] Preferred heteroaromatic groups include, without limitation, 5-membered rings like pyrrole, pyrazole, imidazole, 1,2,3-triazole, 1,2,4-triazole, tetrazole, furan, thiophene, selenophene, oxazole, isoxazole, 1,2-thiazole, 1,3-thiazole, 1,2,3-oxadiazole, 1,2,4-oxadiazole, 1,2,5-oxadiazole, 1,3,4-oxadiazole, 1,2,3-thiadiazole, 1,2,4-thiadiazole, 1,2,5-thiadiazole, 1,3,4-thiadiazole, 6-membered rings like pyridine, pyridazine, pyrimidine, pyrazine, 1,3,5-triazine, 1,2,4-triazine, 1,2,3-triazine, 1,2,4,5-tetrazine, 1,2,3,4-tetrazine, 1,2,3,5-tetrazine, and fused systems like carbazole, indole, isoindole, indolizine, indazole, benzimidazole, benzotriazole, purine, naphthimidazole, phenanthrimidazole, pyridimidazole, pyrazinimidazole, quinoxalinimidazole, benzoxazole, naphthoxazole, anthroxazole, phenanthroxazole, isoxazole, benzothiazole, benzofuran, isobenzofuran, dibenzofuran, quinoline, isoquinoline, pteridine, benzo-5,6-quinoline, benzo-6,7-quinoline, benzo-7,8-quinoline, benzoisoquinoline, acridine, phenothiazine, phenoxazine, benzopyridazine, benzopyrimidine, quinoxaline, phenazine, naphthyridine, azacarbazole, benzocarboline, phenanthridine, phenanthroline, thieno[2,3b]thiophene, thieno[3,2b]thiophene, dithienothiophene, dithienopyridine, isobenzothiophene, dibenzothiophene, benzothiadiazothiophene, or combinations thereof.

[0084] In the compounds of formula I, the non-aromatic carbocyclic and heterocyclic rings A.sup.1-4, include those which are saturated (also referred to as “fully saturated”), i.e. they do only contain C-atoms or hetero atoms connected by single bonds, and those which are unsaturated (also referred to as “partially saturated”), i.e. they also comprise C-atoms or hetero atoms connected by double bonds. The non-aromatic rings may also comprise one or more hetero atoms, preferably selected from Si, O, N and S.

[0085] The non-aromatic carbocyclic and heterocyclic groups may be mononuclear, i.e. having only one ring (like for example cyclohexane), or polynuclear, i.e. having two or more fused rings (like for example decahydronaphthalene or bicyclooctane). Especially preferred are fully saturated groups. Further preferred are mono-, bi- or tricyclic non-aromatic groups with up to 25 C atoms that optionally comprise fused rings and are optionally substituted. Very preferred are 5-, 6-, 7- or 8-membered carbocyclic rings wherein one or more non-adjacent C-atoms are optionally replaced by Si and/or one or more non-adjacent CH groups are optionally replaced by N and/or one or more non-adjacent CH.sub.2 groups are optionally replaced by —O— and/or —S—, all of which are optionally substituted.

[0086] Preferred non-aromatic groups include, without limitation, 5-membered rings like cyclopentane, tetrahydrofuran, tetrahydrothiofuran, pyrrolidine, 6-membered rings like cyclohexane, silinane, cyclohexene, tetrahydropyran, tetrahydrothiopyran, 1,3-dioxane, 1,3-dithiane, piperidine, 7-membered rings like cycloheptane, and fused systems like bicyclo[2.2.2]octane, tetrahydronaphthalene, decahydronaphthalene, indane, or combinations thereof.

[0087] Preferably the non-aromatic and aromatic rings, or A.sup.1-4 in formula I, are selected from trans-1,4-cyclohexylene and 1,4-phenylene that is optionally substituted with one or more groups L.

[0088] Very preferred are compounds of formula I wherein m and p are 1 and n and o are 1 or 2. Further preferred are compounds of formula I wherein m and p are 1 or 2 and n and o are 0. Further preferred are compounds wherein m, n, o and p are 2.

[0089] In the compounds of formula I, the linkage groups connecting the aromatic and non-aromatic cyclic groups in the mesogenic groups, or Z.sup.1-4, are preferably selected from —O—, —S—, —CO—, —COO—, —OCO—, —O—COO—, —CO—NR.sup.0—, —NR.sup.0—CO—, —NR.sup.0—CO—NR.sup.0—, —OCH.sub.2—, —CH.sub.2O—, —SCH.sub.2—, —CH.sub.2S—, —CF.sub.2O—, —OCF.sub.2—, —CF.sub.2S—, —SCF.sub.2—, —CH.sub.2CH.sub.2—, —(CH.sub.2).sub.3—, —(CH.sub.2).sub.4—, —CF.sub.2CH.sub.2—, —CH.sub.2CF.sub.2—, —CF.sub.2CF.sub.2—, —CH═CH—, —CY.sup.1═CY.sup.2—, —CH═N—, —N═CH—, —N═N—, —CH═CR.sup.0—, —C≡C—, —CH═CH—COO—, —OCO—CH═CH—, CR.sup.0R.sup.00 or a single bond, very preferably from —COO—, —OCO— and a single bond.

[0090] Preferably, in the compounds of formula I, the substituents on the rings, such as L, are preferably selected from P-Sp-, F, Cl, Br, I, —CN, —NO.sub.2, —NCO, —NCS, —OCN, —SCN, —C(═O)NR.sup.0R.sup.00, —C(═O)X, —C(═O)OR.sup.0, —C(═O)R.sup.0, —NR.sup.0R.sup.00, —OH, —SF.sub.5, optionally substituted silyl, aryl or heteroaryl with 1 to 12, preferably 1 to 6 C atoms, and straight chain or branched alkyl, alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 12, preferably 1 to 6 C atoms, wherein one or more H atoms are optionally replaced by F or Cl, wherein R.sup.0 and R.sup.00 are as defined in formula I and X is halogen.

[0091] Preferred substituents are selected from F, Cl, CN, NO.sub.2 or straight chain or branched alkyl, alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonlyoxy or alkoxycarbonyloxy with 1 to 12 C atoms, wherein the alkyl groups are optionally perfluorinated, or P-Sp-.

[0092] Very preferred substituents are selected from F, Cl, CN, NO.sub.2, CH.sub.3, C.sub.2H.sub.5, C(CH.sub.3).sub.3, CH(CH.sub.3).sub.2, CH.sub.2CH(CH.sub.3)C.sub.2H.sub.5, OCH.sub.3, OC.sub.2H.sub.5, COCH.sub.3, COC.sub.2H.sub.5, COOCH.sub.3, COOC.sub.2H.sub.5, CF.sub.3, OCF.sub.3, OCHF.sub.2, OC.sub.2F.sub.5 or P-Sp-, in particular F, Cl, CN, CH.sub.3, C.sub.2H.sub.5, C(CH.sub.3).sub.3, CH(CH.sub.3).sub.2, OCH.sub.3, COCH.sub.3 or OCF.sub.3, most preferably F, Cl, CH.sub.3, C(CH.sub.3).sub.3, OCH.sub.3 or COCH.sub.3, or P-Sp-.

##STR00012##

is preferably

##STR00013##

with L having each independently one of the meanings given above.

[0093] Preferably, the carbyl and hydrocarbyl groups, such as R.sup.1-5 in formula I, are preferably selected from straight-chain, branched or cyclic alkyl with 1 to 40, preferably 1 to 25 C-atoms, which is unsubstituted, mono- or polysubstituted by F, Cl, Br, I or CN, and wherein one or more non-adjacent CH.sub.2 groups are optionally replaced, in each case independently from one another, by —O—, —S—, —NH—, —NR.sup.0—, —SiR.sup.0R—, —CO—, —COO—, —OCO—, —O—CO—O—, —S—CO—, —CO—S—, —SO.sub.2—, —CO—NR.sup.0—, —NR.sup.0—CO—, —NR.sup.0—CO—NR.sup.00—, —CY.sup.1═CY.sup.2— or —C≡C— in such a manner that O and/or S atoms are not linked directly to one another, wherein Y.sup.1 and Y.sup.2 are independently of each other H, F, Cl or CN, and R.sup.0 and R.sup.00 are independently of each other H or an optionally substituted aliphatic or aromatic hydrocarbon with 1 to 20 C atoms.

[0094] Very preferably the carbyl and hydrocarbyl groups are selected from C.sub.1-C.sub.20-alkyl, C.sub.1-C.sub.20-oxaalkyl, C.sub.1-C.sub.20-alkoxy, C.sub.2-C.sub.20-alkenyl, C.sub.2-C.sub.20-alkynyl, C.sub.1-C.sub.20-thioalkyl, C.sub.1-C.sub.20-silyl, C.sub.1-C.sub.20-ester, C.sub.1-C.sub.20-amino, C.sub.1-C.sub.20-fluoroalkyl.

[0095] An alkyl or alkoxy radical, i.e. where the terminal CH.sub.2 group is replaced by —O—, can be straight-chain or branched. It is preferably straight-chain, has 2, 3, 4, 5, 6, 7 or 8 carbon atoms and accordingly is preferably ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, ethoxy, propoxy, butoxy, pentoxy, hexoxy, heptoxy, or octoxy, furthermore methyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, nonoxy, decoxy, undecoxy, dodecoxy, tridecoxy or tetradecoxy, for example.

[0096] Oxaalkyl, i.e. where one CH.sub.2 group is replaced by —O—, is preferably straight-chain 2-oxapropyl (=methoxymethyl), 2- (=ethoxymethyl) or 3-oxabutyl (=2-methoxyethyl), 2-, 3-, or 4-oxapentyl, 2-, 3-, 4-, or 5-oxahexyl, 2-, 3-, 4-, 5-, or 6-oxaheptyl, 2-, 3-, 4-, 5-, 6- or 7-oxaoctyl, 2-, 3-, 4-, 5-, 6-, 7- or 8-oxanonyl or 2-, 3-, 4-, 5-, 6-,7-, 8- or 9-oxadecyl, for example.

[0097] An alkyl group wherein one or more CH.sub.2 groups are replaced by —CH═CH— can be straight-chain or branched. It is preferably straight-chain, has 2 to 10 C atoms and accordingly is preferably vinyl, prop-1-, or prop-2-enyl, but-1-, 2- or but-3-enyl, pent-1-, 2-, 3- or pent-4-enyl, hex-1-, 2-, 3-, 4- or hex-5-enyl, hept-1-, 2-, 3-, 4-, 5- or hept-6-enyl, oct-1-, 2-, 3-, 4-, 5-, 6- or oct-7-enyl, non-1-, 2-, 3-, 4-, 5-, 6-, 7- or non-8-enyl, dec-1-, 2-, 3-, 4-, 5-, 6-, 7-, 8- or dec-9-enyl.

[0098] Especially preferred alkenyl groups are C.sub.2-C.sub.7-1E-alkenyl, C.sub.4-C.sub.7-3E-alkenyl, C.sub.5-C.sub.7-4-alkenyl, C.sub.6-C.sub.7-5-alkenyl and C.sub.7-6-alkenyl, in particular C.sub.2-C.sub.7-1E-alkenyl, C.sub.4-C.sub.7-3E-alkenyl and C.sub.5-C.sub.7-4-alkenyl. Examples for particularly preferred alkenyl groups are vinyl, 1E-propenyl, 1E-butenyl, 1E-pentenyl, 1E-hexenyl, 1E-heptenyl, 3-butenyl, 3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl, 4E-hexenyl, 4Z-heptenyl, 5-hexenyl, 6-heptenyl and the like. Groups having up to 5 C atoms are generally preferred.

[0099] In an alkyl group wherein one CH.sub.2 group is replaced by —O— and one by —CO—, these radicals are preferably neighboured. Accordingly these radicals together form a carbonyloxy group —CO—O— or an oxycarbonyl group —O—CO—. Preferably this group is straight-chain and has 2 to 6 C atoms. It is accordingly preferably acetyloxy, propionyloxy, butyryloxy, pentanoyloxy, hexanoyloxy, acetyloxymethyl, propionyloxymethyl, butyryloxymethyl, pentanoyloxymethyl, 2-acetyloxyethyl, 2-propionyloxy-ethyl, 2-butyryloxyethyl, 3-acetyloxypropyl, 3-propionyloxypropyl, 4-acetyloxybutyl, methoxycarbonyl, ethoxycarbonyl, propoxycarbonyl, butoxycarbonyl, pentoxycarbonyl, methoxycarbonylmethyl, ethoxy-carbonylmethyl, propoxycarbonylmethyl, butoxycarbonylmethyl, 2-(methoxycarbonyl)ethyl, 2-(ethoxycarbonyl)ethyl, 2-(propoxy-carbonyl)ethyl, 3-(methoxycarbonyl)propyl, 3-(ethoxycarbonyl)propyl, 4-(methoxycarbonyl)-butyl.

[0100] An alkyl group wherein two or more CH.sub.2 groups are replaced by —O— and/or —COO— can be straight-chain or branched. It is preferably straight-chain and has 3 to 12 C atoms. Accordingly it is preferably bis-carboxy-methyl, 2,2-bis-carboxy-ethyl, 3,3-bis-carboxy-propyl, 4,4-bis-carboxy-butyl, 5,5-bis-carboxy-pentyl, 6,6-bis-carboxy-hexyl, 7,7-bis-carboxy-heptyl, 8,8-bis-carboxy-octyl, 9,9-bis-carboxy-nonyl, 10,10-bis-carboxy-decyl, bis-(methoxycarbonyl)-methyl, 2,2-bis-(methoxycarbonyl)-ethyl, 3,3-bis-(methoxycarbonyl)-propyl, 4,4-bis-(methoxycarbonyl)-butyl, 5,5-bis-(methoxycarbonyl)-pentyl, 6,6-bis-(methoxycarbonyl)-hexyl, 7,7-bis-(methoxycarbonyl)-heptyl, 8,8-bis-(methoxycarbonyl)-octyl, bis-(ethoxycarbonyl)-methyl, 2,2-bis-(ethoxycarbonyl)-ethyl, 3,3-bis-(ethoxycarbonyl)-propyl, 4,4-bis-(ethoxycarbonyl)-butyl, 5,5-bis-(ethoxycarbonyl)-hexyl.

[0101] An alkyl or alkenyl group that is monosubstituted by CN or CF.sub.3 is preferably straight-chain. The substitution by CN or CF.sub.3 can be in any desired position.

[0102] An alkyl or alkenyl group that is at least monosubstituted by halogen is preferably straight-chain. Halogen is preferably F or Cl, in case of multiple substitutions preferably F. The resulting groups include also perfluorinated groups. In case of monosubstitution the F or Cl substituent can be in any desired position, but is preferably in w-position. Examples for especially preferred straight-chain groups with a terminal F substituent are fluoromethyl, 2-fluorethyl, 3-fluorpropyl, 4-fluorbutyl, 5-fluorpentyl, 6-fluorhexyl and 7-fluorheptyl. Other positions of F are, however, not excluded.

[0103] R.sup.0 and R.sup.00 are preferably selected from H, straight-chain or branched alkyl with 1 to 12 C atoms. —CY.sup.1═CY.sup.2— is preferably —CH═CH—, —CF═CF— or —CH═C(CN)—.

[0104] Halogen is F, Cl, Br or I, preferably F or Cl.

[0105] R.sup.1-5 can be an achiral or a chiral group. Particularly preferred chiral groups are 2-butyl (=1-methylpropyl), 2-methylbutyl, 2-methylpentyl, 3-methylpentyl, 2-ethylhexyl, 2-propylpentyl, in particular 2-methylbutyl, 2-methylbutoxy, 2-methylpentoxy, 3-methylpentoxy, 2-ethylhexoxy, 1-methylhexoxy, 2-octyloxy, 2-oxa-3-methylbutyl, 3-oxa-4-methylpentyl, 4-methylhexyl, 2-hexyl, 2-octyl, 2-nonyl, 2-decyl, 2-dodecyl, 6-methoxyoctoxy, 6-methyloctoxy, 6-methyloctanoyloxy, 5-methylheptyloxycarbonyl, 2-methylbutyryloxy, 3-methylvaleroyloxy, 4-methylhexanoyloxy, 2-chlorpropionyloxy, 2-chloro-3-methylbutyryloxy, 2-chloro-4-methylvaleryloxy, 2-chloro-3-methylvaleryloxy, 2-methyl-3-oxapentyl, 2-methyl-3-oxahexyl, 1-methoxypropyl-2-oxy, 1-ethoxypropyl-2-oxy, 1-propoxypropyl-2-oxy, 1-butoxypropyl-2-oxy, 2-fluorooctyloxy, 2-fluorodecyloxy, 1,1,1-trifluoro-2-octyloxy, 1,1,1-trifluoro-2-octyl, 2-fluoromethyloctyloxy for example. Very preferred are 2-hexyl, 2-octyl, 2-octyloxy, 1,1,1-trifluoro-2-hexyl, 1,1,1-trifluoro-2-octyl and 1,1,1-trifluoro-2-octyloxy.

[0106] Preferred achiral branched groups are isopropyl, isobutyl (=methylpropyl), isopentyl (=3-methylbutyl), isopropoxy, 2-methyl-propoxy and 3-methylbutoxy.

[0107] In another preferred embodiment the compounds of formula I comprise one or more terminal groups, like R.sup.1-4, or substituents, like R.sup.5, that are substituted by two or more polymerisable groups P or P-Sp-(multifunctional polymerisable groups). Suitable multifunctional polymerisable groups of this type are disclosed for example in U.S. Pat. No. 7,060,200 B1 or US 2006/0172090 A1. Very preferred are compounds comprising one or more multifunctional polymerisable groups selected from the following formulae:

—X-alkyl-CHP.sup.1—CH.sub.2—CH.sub.22  P1

—X′-alkyl-C(CH.sub.2P.sup.1)(CH.sub.2P.sup.2)—CH.sub.2P.sup.3  P2

—X′-alkyl-CHP.sup.1CHP.sup.2—CH.sub.2P.sup.3  P3

—X′-alkyl-C(CH.sub.2P.sup.1)(CH.sup.2P.sup.2)—C.sub.aH.sub.2a+1  P4

—X′-alkyl-CHP.sup.1—CH.sub.2P.sup.2  P5

—X′-alkyl-CHP.sup.1P.sup.2  P5

—X′-alkyl-CP.sup.1P.sup.2—C.sub.aH.sub.2a+1  P6

—X′-alkyl-C(CH.sub.2P.sup.1)(CH.sub.2P.sup.2)—CH.sub.2OCH.sub.2—C(CH.sub.2P.sup.3)(CH.sub.2P.sup.4)CH.sub.2P.sup.5  P7

—X′-alkyl-CH((CH.sub.2).sub.aP.sup.1)((CH.sub.2).sub.bP.sup.2)  P8

—X′-alkyl-CHP.sup.1CHP.sup.2—C.sub.aH.sub.2a+1  P9

wherein [0108] alkyl is straight-chain or branched alkylene having 1 to 12 C-atoms which is unsubstituted, mono- or polysubstituted by F, Cl, Br, I or CN, and wherein one or more non-adjacent CH.sub.2 groups are optionally replaced, in each case independently from one another, by —O—, —S—, —NH—, —NR.sup.0—, —SiR.sup.0R.sup.00—, —CO—, —COO—, —OCO—, —O—CO—O—, —S—CO—, —CO—S—, —SO.sub.2—, —CO—NR.sup.0—, —NR.sup.0—CO—, —NR.sup.0—CO—NR.sup.00—, —CY.sup.1═CY.sup.2— or —C≡C— in such a manner that O and/or S atoms are not linked directly to one another, with R.sup.0 and R.sup.00 having the meanings given above, or denotes a single bond, [0109] a and b are independently of each other 0, 1, 2, 3, 4, 5 or 6, [0110] X′ is as defined above, and [0111] P.sup.1-5 independently of each other have one of the meanings given for P above.

[0112] Very preferred compounds of formula I are those of the following sub formulae:

##STR00014## ##STR00015## ##STR00016## ##STR00017##

wherein R.sup.1-5, A.sup.1-4, Z.sup.1-4, B, m, n, o, p and q have one the meanings given above.

[0113] Especially preferred are compounds of the following sub formulae:

##STR00018## ##STR00019## ##STR00020## ##STR00021## ##STR00022##

wherein Z has one of the meanings of Z.sup.1 given above, R has one of the meanings of R.sup.1 as given above that is different from P-Sp-, and P, Sp, L and r are as defined above, and the benzene rings in the mesogenic groups are optionally substituted by one or more groups L as defined above.

[0114] Preference is furthermore given to a polymerisable liquid crystalline medium wherein the compounds of formula I are selected from the group of compounds of formula I 25 or I 26, in particular wherein Z denotes —COO—, r is in each occurrence 0, and P, Sp are as defined above.

[0115] P-Sp- in these preferred compounds is preferably P-Sp′-X′, with X′ preferably being —O—, —COO— or —OCOO—.

[0116] The compounds of formula I and suitable methods for their synthesis are disclosed in WO 2008/119427 A1.

[0117] Additionally, further polymerisable compounds can be added to the polymerisable LC material in accordance with the present invention. These compounds are preferably mesogenic or liquid crystalline. More preferably the LC material comprises one or more additional compounds selected from reactive mesogens (RMs), most preferably selected from mono- and direactive RMs.

[0118] The additional RMs can be prepared by methods which are known per se and which are described in standard works of organic chemistry like for example Houben-Weyl, Methoden der organischen Chemie, Thieme-Verlag, Stuttgart. Suitable RMs are disclosed for example in WO 93/22397, EP 0 261 712, DE 195 04 224, WO 95/22586, WO 97/00600, U.S. Pat. No. 5,518,652, U.S. Pat. No. 5,750,051, U.S. Pat. No. 5,770,107 and U.S. Pat. No. 6,514,578. Examples of particularly suitable and preferred RMs are shown in the following list.

##STR00023## ##STR00024## ##STR00025## ##STR00026##

wherein [0119] P.sup.0 is, in case of multiple occurrence independently of one another, a polymerisable group having one of the meanings given for P above, and is preferably an acryl, methacryl, oxetane, 3-ethyloxetane, epoxy, vinyloxy or styrene group, [0120] Sp.sup.0 is a spacer group having one of the meanings given for Sp′ above, [0121] X.sup.0 has one of the meanings given for X′ above, [0122] Sp.sup.0-X.sup.0 is preferably selected from —(CH.sub.2).sub.p1—, —(CH.sub.2).sub.p1—O—, —(CH.sub.2).sub.p1—CO—O— and —(CH.sub.2).sub.p1—O—CO—O—, wherein p1 is an integer from 1 to 12 and wherein these groups are linked to an adjacent ring via the O-atom if present, [0123] A.sup.0 and B.sup.0 are, in case of multiple occurrence independently of one another, 1,4-phenylene that is optionally substituted with 1, 2, 3 or 4 groups L, or trans-1, 4-cyclohexylene, [0124] Z.sup.0 is, in case of multiple occurrence independently of one another, —COO—, —OCO—, —CH.sub.2CH.sub.2—, —C≡C—, —CH═CH—, —CH═CH—COO—, —OCO—CH═CH— or a single bond, [0125] R.sup.0 is alkyl, alkoxy, thioalkyl, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 20, preferably 1 to 15 C atoms which is optionally fluorinated, or denotes Y.sup.0 or P-Sp.sup.0-X.sup.0—, [0126] Y.sup.0 is F, Cl, CN, NO.sub.2, OCH.sub.3, OCN, SCN, SF.sub.5, optionally fluorinated alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 4 C atoms, or mono- oligo- or polyfluorinated alkyl or alkoxy with 1 to 4 C atoms, [0127] X.sup.00 is —O—, —S—, —CO—, —COO—, —OCO—, —O—COO—, —CO—NR.sup.01—, —NR.sup.01—CO—, —NR.sup.01—CO—NR.sup.01—, —OCH.sub.2—, —CH.sub.2O—, —SCH.sub.2—, —CH.sub.2S—, —CF.sub.2O—, —OCF.sub.2—, —CF.sub.2S—, —SCF.sub.2—, —CF.sub.2CH.sub.2—, —CH.sub.2CF.sub.2—, —CF.sub.2CF.sub.2—, —CH═N—, —N═CH—, —N═N—, —CH═CR.sup.01—, —CF═CF—, —C≡C—, —CH═CH—COO—, —OCO—CH═CH— or a single bond, [0128] R.sup.01 is H or alkyl with 1 to 12 C-atoms, [0129] R* is a chiral alkyl or alkoxy group with 4 or more, preferably 4 to 12 C atoms, like 2-methylbutyl, 2-methyloctyl, 2-methylbutoxy or 2-methyloctoxy, [0130] Ch is a chiral group selected from cholesteryl, estradiol, or terpenoid radicals like menthyl or citronellyl, [0131] L is, in case of multiple occurrence identically or differently F, Cl, CN, SCN, SF.sub.5 or straight-chain or branched, optionally mono- or polyfluorinated alkyl, alkoxy, alkenyl, alkynyl, alkylcarbonyl, alkoxycarbonyl, or alkylcarbonyloxy or alkoxycarbonyloxy having 1 to 12 C atoms, (wherein the groups different from alkyl and alkoxy contain at least 2 C atoms and branched groups contain at least 3 C atoms) or optionally halogenated alkyl, alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy with 1 to 5 C atoms, [0132] r is 0, 1, 2, 3 or 4, [0133] u is 0 or 1, [0134] v and v are independently of each other 0, 1 or 2,
and wherein the benzene and napthalene rings can additionally be substituted with one or more identical or different groups L.

[0135] Especially preferably the polymerisable LC host component contains only achiral compounds and no chiral compounds.

[0136] Further preferably the polymerisable LC host component comprises one or more compounds selected from the group consisting of formulae MR3, MR4, MR7, MR8, MR9, MR10, MR18, MR27, MR28, DR1, DR5, DR6, DR7, DR8, and DR9.

[0137] Further preferably the polymerisable LC host component comprises one or more compounds selected from the following formulae:

##STR00027## ##STR00028##

wherein P.sup.0 and R.sup.0 are as defined above, R.sup.0 is preferably alkyl, alkoxy or alkylcarbonyloxy with 1 to 6 C-atoms, L is H or CH.sub.3, [0138] x and y are independently of each other 0 or identical or different integers from 1 to 12, [0139] z is on each occurrence independently of one another 0 or 1, with [0140] z being 0 if the adjacent x or y is 0.

[0141] Further preferably the polymerisable LC host component comprises one or more compounds selected from the following formulae:

##STR00029## ##STR00030## ##STR00031## ##STR00032## ##STR00033## ##STR00034##

wherein L is H or CH.sub.3.

[0142] The aforementioned RMs and their synthesis are known from prior art. For example, compounds DR1a1 and DR1a2 are described in D. J. Broer; G. Challa; G. N. Mol, Macromol. Chem, 1991, 192, 59, compounds MR10a1 and MR10a2 are described in U.S. Pat. No. 6,183,822, and compounds MR7a1 and MR7a2 are described in U.S. Pat. No. 5,720,900.

[0143] Preferably the polymerisable compounds of the polymerisable material are selected from mono- or direactive RMs, preferably having low birefringence.

[0144] Especially preferred is a polymerisable material having an absolute value of the birefringence from 0.01 to 0.2, very preferably from 0.04 to 0.16.

[0145] The general preparation of polymer LC films according to this invention is known to the ordinary expert and described in the literature, for example in D. J. Broer; G. Challa; G. N. Mol, Macromol. Chem, 1991, 192, 59. Typically a polymerisable LC material is coated or otherwise applied onto a substrate where it aligns into uniform orientation, and polymerised in situ in its LC phase at a selected temperature for example by exposure to heat or actinic radiation, preferably by photo-polymerisation, very preferably by UV-photopolymerisation, to fix the alignment of the LC molecules. If necessary, uniform alignment can be promoted by additional means like shearing or annealing the LC material, surface treatment of the substrate, or adding surfactants to the LC material.

[0146] As substrate for example glass or quartz sheets or plastic films can be used. It is also possible to put a second substrate on top of the coated material prior to and/or during and/or after polymerisation. The substrates can be removed after polymerisation or not. When using two substrates in case of curing by actinic radiation, at least one substrate has to be transmissive for the actinic radiation used for the polymerisation. Isotropic or birefringent substrates can be used. In case the substrate is not removed from the polymerised film after polymerisation, preferably isotropic substrates are used.

[0147] Suitable and preferred plastic substrates are for example films of polyester such as polyethyleneterephthalate (PET) or polyethylene-naphthalate (PEN), polyvinylalcohol (PVA), polycarbonate (PC) or triacetylcellulose (TAC), very preferably PET or TAC films. As birefringent substrates for example uniaxially stretched plastics film can be used. PET films are commercially available for example from DuPont Teijin Films under the trade name Melinex®.

[0148] The polymerisable material can be applied onto the substrate by conventional coating techniques like spin-coating or blade coating. It can also be applied to the substrate by conventional printing techniques which are known to the expert, like for example screen printing, offset printing, reel-to-reel printing, letter press printing, gravure printing, rotogravure printing, flexographic printing, intaglio printing, pad printing, heat-seal printing, ink-jet printing or printing by means of a stamp or printing plate.

[0149] It is also possible to dissolve the polymerisable material in a suitable solvent. This solution is then coated or printed onto the substrate, for example by spin-coating or printing or other known techniques, and the solvent is evaporated off before polymerisation. In many cases it is suitable to heat the mixture in order to facilitate the evaporation of the solvent. As solvents for example standard organic solvents can be used. The solvents can be selected for example from ketones such as acetone, methyl ethyl ketone, methyl propyl ketone or cyclohexanone; acetates such as methyl, ethyl or butyl acetate or methyl acetoacetate; alcohols such as methanol, ethanol or isopropyl alcohol; aromatic solvents such as toluene or xylene; halogenated hydrocarbons such as di- or trichloromethane; glycols or their esters such as PGMEA (propyl glycol monomethyl ether acetate), γ-butyrolactone, and the like. It is also possible to use binary, ternary or higher mixtures of the above solvents.

[0150] Uniform alignment of the polymerisable LC material, for example planar alignment (for preparing A plates) or homeotropic, i.e. perpendicular alignment (for preparing C plates) can be achieved for example by rubbing treatment of the substrate, by shearing the material during or after coating, by annealing the material before polymerisation, by application of an alignment layer, by applying a magnetic or electric field to the coated material, or by the addition of surface-active compounds to the material. Reviews of alignment techniques are given for example by I. Sage in “Thermotropic Liquid Crystals”, edited by G. W. Gray, John Wiley & Sons, 1987, pages 75-77; and by T. Uchida and H. Seki in “Liquid Crystals —Applications and Uses Vol. 3”, edited by B. Bahadur, World Scientific Publishing, Singapore 1992, pages 1-63. A review of alignment materials and techniques is given by J. Cognard, Mol. Cryst. Liq. Cryst. 78, Supplement 1 (1981), pages 1-77.

[0151] Especially preferred is a polymerisable material comprising one or more surfactants that promote a specific surface alignment of the LC molecules. Suitable surfactants are described for example in J. Cognard, Mol. Cryst. Liq. Cryst. 78, Supplement 1, 1-77 (1981). Preferred aligning agents for planar alignment are for example non-ionic surfactants, preferably fluoro-carbon surfactants such as the commercially available Fluorad FC-171® (from 3M Co.), Tego Twin 4100 ® (from Evonik), or Zonyl FSN® (from DuPont), multiblock surfactants as described in GB 2 383 040 or polymerisable surfactants as described in EP 1 256 617. Preferably the total concentration of surfactants in the polymerisable LC material is from 0.05 to 3%, very preferably from 0.1 to 1%.

[0152] It is also possible to apply an alignment layer onto the substrate and provide the polymerisable material onto this alignment layer. Suitable alignment layers are known in the art, like for example rubbed polyimide or alignment layers prepared by photoalignment as described in U.S. Pat. No. 5,602,661, U.S. Pat. No. 5,389,698 or U.S. Pat. No. 6,717,644.

[0153] Rubbed polyimide (PI) can for example be used to induce planar alignment, whereas an untreated glass substrate can for example be used to induce homeotropic alignment.

[0154] It is also possible to induce or improve alignment by annealing the polymerisable LC material at elevated temperature, preferably at its polymerisation temperature, prior to polymerisation.

[0155] Polymerisation is achieved for example by exposing the polymerisable material to heat or actinic radiation. Actinic radiation means irradiation with light, like UV light, IR light or visible light, irradiation with X-rays or gamma rays or irradiation with high energy particles, such as ions or electrons. Preferably polymerisation is carried out by UV irradiation. As a source for actinic radiation for example a single UV lamp or a set of UV lamps can be used. When using a high lamp power the curing time can be reduced. Another possible source for actinic radiation is a laser, like for example a UV, IR or visible laser.

[0156] Polymerisation is preferably carried out in the presence of an initiator absorbing at the wavelength of the actinic radiation. For this purpose the polymerisable LC material preferably comprises one or more initiators, preferably in a concentration from 0.01 to 10%, very preferably from 0.05 to 5%. For example, when polymerising by means of UV light, a photoinitiator can be used that decomposes under UV irradiation to produce free radicals or ions that start the polymerisation reaction. For polymerising acrylate or methacrylate groups preferably a radical photoinitiator is used. For polymerising vinyl, epoxide or oxetane groups preferably a cationic photoinitiator is used. It is also possible to use a thermal polymerisation initiator that decomposes when heated to produce free radicals or ions that start the polymerisation. Typical radical photoinitiators are for example the commercially available Irgacure® or Darocure® (Ciba AG, Basel, Switzerland). A typical cationic photoinitiator is for example UVI 6974 (Union Carbide).

[0157] The polymerisable material may also comprise one or more stabilizers or inhibitors to prevent undesired spontaneous polymerisation, like for example the commercially available Irganox® (Ciba AG, Basel, Switzerland), preferably in a concentration of from 0.005 to 1%, very preferably from 0.01 to 0.2%.

[0158] The curing time depends, inter alia, on the reactivity of the polymerisable material, the thickness of the coated layer, the type of polymerisation initiator and the power of the UV lamp. The curing time is preferably <5 minutes, very preferably <3 minutes, most preferably <1 minute. For mass production short curing times of <30 seconds are preferred.

[0159] A suitable UV radiation power is preferably in the range from 5 to 200 mWcm.sup.−2, more preferably in the range from 10 to 175 mWcm.sup.−2 and most preferably in the range from 15 to 150 mWcm.sup.−2.

[0160] In connection with the applied UV radiation and as a function of time, a suitable UV dose is preferably in the range from 25 to 7200 mJcm.sup.−2 more preferably in the range from 500 to 7200 mJcm.sup.−2 and most preferably in the range from 3000 to 7200 mJcm.sup.−2.

[0161] Preferably polymerisation is carried out in an inert gas atmosphere like nitrogen or argon.

[0162] The polymerisable material may also comprise one or more dyes having an absorption maximum adjusted to the wavelength of the radiation used for polymerisation, in particular UV dyes like e.g. 4,4″-azoxy anisole or Tinuvin® dyes (from Ciba AG, Basel, Switzerland).

[0163] In another preferred embodiment the polymerisable material comprises one or more monoreactive polymerisable non-mesogenic compounds, preferably in an amount of 0 to 50%, very preferably 0 to 20%. Typical examples are alkylacrylates or alkylmethacrylates.

[0164] In another preferred embodiment the polymerisable material comprises one or more di- or multireactive polymerisable non-mesogenic compounds, preferably in an amount of 0 to 50%, very preferably 0 to 20%, alternatively or in addition to the di- or multireactive polymerisable mesogenic compounds. Typical examples of direactive non-mesogenic compounds are alkyldiacrylates or alkyldimethacrylates with alkyl groups of 1 to 20 C atoms. Typical examples of multireactive non-mesogenic compounds are trimethylpropanetrimethacrylate or pentaerythritoltetraacrylate.

[0165] It is also possible to add one or more chain transfer agents to the polymerisable material in order to modify the physical properties of the polymer film. Especially preferred are thiol compounds, for example monofunctional thiols like dodecane thiol or multifunctional thiols like trimethylpropane tri(3-mercaptopropionate). Very preferred are mesogenic or LC thiols as disclosed for example in WO 96/12209, WO 96/25470 or U.S. Pat. No. 6,420,001. By using chain transfer agents the length of the free polymer chains and/or the length of the polymer chains between two crosslinks in the polymer film can be controlled. When the amount of the chain transfer agent is increased, the polymer chain length in the polymer film decreases.

[0166] The polymerisable material may also comprise a polymeric binder or one or more monomers capable of forming a polymeric binder, and/or one or more dispersion auxiliaries. Suitable binders and dispersion auxiliaries are disclosed for example in WO 96/02597. Preferably, however, the polymerisable material does not contain a binder or dispersion auxiliary.

[0167] The polymerisable material can additionally comprise one or more additives like for example catalysts, sensitizers, stabilizers, inhibitors, chain-transfer agents, co-reacting monomers, surface-active compounds, lubricating agents, wetting agents, dispersing agents, hydrophobing agents, adhesive agents, flow improvers, defoaming agents, deaerators, diluents, reactive diluents, auxiliaries, colourants, dyes, pigments or nanoparticles.

[0168] The polymer films and materials of the present invention can be used as retardation or compensation film for example in LCDs to improve the contrast and brightness at large viewing angles and reduce the chromaticity. It can be used outside the switchable LC cell of the LCD or between the substrates, usually glass substrates, forming the switchable LC cell and containing the switchable LC medium (incell application). The optical retardation (δ(λ)) of a polymer film as a function of the wavelength of the incident beam (λ) is given by the following equation (6):

δ(λ)=(2πΔn.Math.d)/λ  (6)

wherein (Δn) is the birefringence of the film, (d) is the thickness of the film and λ is the wavelength of the incident beam.

[0169] According to Snellius law, the birefringence as a function of the direction of the incident beam is defined as

Δn=sin Θ/sin Ψ  (7)

wherein sin Θ is the incidence angle or the tilt angle of the optical axis in the film and sin is the corresponding reflection angle.

[0170] Based on these laws, the birefringence and accordingly optical retardation depends on the thickness of a film and the tilt angle of optical axis in the film (cf. Berek's compensator). Therefore, the skilled expert is aware that different optical retardations or different birefringence can be induced by adjusting the orientation of the liquid-crystalline molecules in the polymer film.

[0171] The polymer film of the present invention can also be used as alignment film for other liquid-crystalline or RM materials as described, for example, in WO 2006/039980 A1. For example, they can be used in an LCD to induce or improve alignment of the switchable liquid-crystalline medium, or to align a subsequent layer of polymerisable liquid-crystalline material coated thereon. In this way, stacks of polymerized liquid-crystalline films can be prepared.

[0172] The thickness of a polymer film according to the present invention is preferably from 0.3 to 5 microns, very preferably from 0.5 to 3 microns, most preferably from 0.7 to 2.5 microns. For use as alignment layer, a thin film with a thickness of 0.05 to 1, preferably 0.1 to 0.4 microns is preferred.

[0173] The polymer film and materials of the present invention can be used in conventional LC displays, for example displays with vertical alignment like the DAP (deformation of aligned phases), ECB (electrically controlled birefringence), CSH (colour super homeotropic), VA (vertically aligned), VAN or VAC (vertically aligned nematic or cholesteric), MVA (multi-domain vertically aligned), PVA (patterned vertically aligned) or PSVA (polymer stabilised vertically aligned) mode; displays with bend or hybrid alignment like the OCB (optically compensated bend cell or optically compensated birefringence), R-OCB (reflective OCB), HAN (hybrid aligned nematic) or pi-cell (π-cell) mode; displays with twisted alignment like the TN (twisted nematic), HTN (highly twisted nematic), STN (super twisted nematic), AMD-TN (active matrix driven TN) mode; displays of the IPS (in plane switching) mode, or displays with switching in an optically isotropic phase.

[0174] The layers, films and materials of the present invention can be used for various types of optical films, preferably selected from optically uniaxial films (A-plate, C-plate, negative C-plate, O-plate), twisted optical retarders, like for example twisted quarter wave foils (QWF), achromatic retarders, achromatic QWFs or half wave foils (HWF), and optically biaxial films. The LC phase structure in the layers and materials can be selected from cholesteric, smectic, nematic and blue phases. The alignment of the LC material in the layer can be selected from homeotropic, splayed, tilted, planar and blue-phase alignment. The layers can be uniformly oriented or exhibit a pattern of different orientations.

[0175] The films can be used as optical compensator for viewing angle enhancement of LCD's or as a component in a brightness enhancement element, furthermore as an achromatic retarder, for example in reflective or transflective LCD's. Further preferred applications and devices include [0176] retarding components in optoelectronic devices requiring similar phase shift at multiple wavelengths, such as combined CD/DVD/HD-DVD/Blue-Ray, including reading, writing re-writing data storage systems [0177] achromatic retarders for optical devices such as cameras [0178] achromatic retarders for displays including OLED and LCD's.

[0179] The present invention is described above and below with particular reference to the preferred embodiments. It should be understood that various changes and modifications might be made therein without departing from the spirit and scope of the invention.

[0180] Above and below, unless stated otherwise, all percentages are percent by weight. All temperatures are given in degrees Celsius. “m.p.” denotes the melting point, “cl.p.” denotes the clearing point, “T.sub.g” denotes the glass transition temperature. Furthermore, C=crystalline state, N=nematic phase, S=smectic phase and I=isotropic phase. The data between or behind these symbols represent the transition temperatures. Δn denotes the optical anisotropy (Δn=n.sub.e−n.sub.o, where n.sub.o denotes the refractive index parallel to the longitudinal molecular axes and n.sub.e denotes the refractive index perpendicular thereto), measured at 550 nm and 20° C. The optical and electro optical data are measured at 20° C., unless expressly stated otherwise.

[0181] Method of measuring the refractive indices of novel single compounds: The refractive indices of a liquid crystal mixture commercially available from Merck KGaA under the product code ZLI4792 are measured using an Abbe refractometer at 20° C. and using a light of wavelength 550 nm. This mixture is then doped with 10% w/w of the compound under test and the refractive indices are remeasured. Extrapolation to 100% gives the refractive index of the compound under test.

[0182] Unless stated otherwise, the percentages of a component of a polymerisable LC material as given above and below are % in weight and refer to the total amount of solids in the polymerisable mixture, i.e. not including solvents.

[0183] Many of the compounds or mixtures thereof mentioned above and below are commercially available. All of these compounds are either known or can be prepared by methods which are known per se, as described in the literature (for example in the standard works such as Houben-Weyl, Methoden der Organischen Chemie [Methods of Organic Chemistry], Georg-Thieme-Verlag, Stuttgart), to be precise under reaction conditions which are known and suitable for said reactions. Use may also be made here of variants which are known per se, but are not mentioned here. Unless the context clearly indicates otherwise, as used herein plural forms of the terms herein are to be construed as including the singular form and vice versa.

[0184] Throughout the description and claims of this specification, the words “comprise” and “contain” and variations of the words, for example “comprising” and “comprises”, mean “including but not limited to”, and are not intended to (and do not) exclude other components. On the other hand, the word “comprise” also encompasses the term “consisting of” but is not limited to it.

[0185] Throughout the description and claims of this specification, the words “obtainable” and “obtained” and variations of the words, mean “including but not limited to”, and are not intended to (and do not) exclude other components. On the other hand, the word “obtainable” also encompasses the term “obtained” but is not limited to it.

[0186] It will be appreciated that variations to the foregoing embodiments of the invention can be made while still falling within the scope of the invention. Alternative features serving the same, equivalent, or similar purpose may replace each feature disclosed in this specification, unless stated otherwise. Thus, unless stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features.

[0187] All of the features disclosed in this specification may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive. In particular, the preferred features of the invention are applicable to all aspects of the invention and may be used in any combination. Likewise, features described in non-essential combinations may be used separately (not in combination).

[0188] It will be appreciated that many of the features described above, particularly of the preferred embodiments, are inventive in their own right and not just as part of an embodiment of the present invention. Independent protection may be sought for these features in addition to or alternative to any invention presently claimed.

[0189] The invention will now be described in more detail by reference to the following working examples, which are illustrative only and do not limit the scope of the invention.

EXAMPLES

[0190] For the preparation of the following mixtures, the following compounds and abbreviations are used:

##STR00035##

LC242 is a polymerisable chiral material commercially available from BASF AG (Ludwigshafen, Germany).

[0191] General Method for the Polymer Film Preparation:

[0192] First, a 33.3% w/w solution of the corresponding LC medium in Toluene/Cyclohexane solution (7:3) is prepared.

[0193] The solution is spin coated at 3000 rpm for 30 s onto a rubbed polyimide coated glass slide where it aligns homeotropically.

[0194] The sample is annealed at the given temperature for 60 s on a temperature controlled hot plate.

[0195] The sample is cooled for 60 s to 20° C. under a nitrogen atmosphere and then UV cured (365 nm filter, 80 mW/cm.sup.2) for 60 s at 20° C.

[0196] Retardation is measured at angles of incidence from −40° to 60° at 20° intervals at a temperature of 20° C. and at a wavelengths ranging from 400 to 700 nm.

Comparative Example 1

[0197] The following mixture having a clearing point of 81° C. and a birefringence of 0.06 at 550 nm is formulated (in wt. %):

TABLE-US-00001 Irgacure ® 369 1.00 Irganox ® 1076 0.12 LC242 24.98 RM 2 40.00 RM 3 17.91 RM 4 14.99 Zonyl FSO ® 100 1.00

[0198] The mixture can be annealed at temperatures ranging from 69 to 61° C.

[0199] The retardation profile (retardation dispersion and retardation versus viewing angle at different wavelengths) as shown in FIGS. 1a and 1b is measured using an ellipsometer, and the thickness of 2.29 μm is measured using a surface profiler.

[0200] The retardation dispersion values at different angles of incidence are shown in Table 1 below.

TABLE-US-00002 TABLE 1 Angle (°) 60 40 20 0 −20 −40 R.sub.550 119.1 131.5 141.8 146.2 143.7 135.2 R.sub.450/R.sub.550 0.909 0.906 0.905 0.905 0.905 0.905

[0201] In order to test the durability of the polymer film, the film is exposed to a temperature of 80° C. for a time up to 169 h. Table 1.1 summarizes the result of the durability test

TABLE-US-00003 TABLE 1.1 Time at 80° C. [h] 0 0.5 1 2 4 7 24 169 R(450)/R(550) 0.905 0.935 0.939 0.943 0.947 0.950 0.953 0.961

Example 1

[0202] The following mixture having a clearing point of 81° C. and a birefringence of 0.06 at 550 nm is formulated (in wt. %):

TABLE-US-00004 Irgacure ® 369 1.00 Irganox ® 1076 0.12 LC242 16.66 RM 1 37.63 RM 2 30.00 RM 4 13.59 Zonyl FSO ® 100 1.00

[0203] The mixture can be annealed at temperatures ranging from 80 to 51° C.

[0204] The retardation profile (retardation dispersion and retardation versus viewing angle at different wavelengths) as shown in FIGS. 2a and 2b is measured using an ellipsometer, and the thickness of 2.29 μm is measured using a surface profiler.

[0205] The retardation dispersion values at different angles of incidence are shown in Table 2 below.

TABLE-US-00005 TABLE 2 Angle (°) 60 40 20 0 −20 −40 R550 131.2 145.7 157.9 163.4 160.6 150.7 R450/R550 0.925 0.920 0.919 0.918 0.918 0.919

[0206] In order to test the durability of the polymer film, the film is exposed to a temperature of 80° C. for a time up to 169 h. Table 2.1 summarizes the result of the durability test

TABLE-US-00006 TABLE 2.1 Time at 80° C. [h] 0 0.5 1 2 4 7 24 169 R(450)/R(550) 0.900 0.909 0.910 0.912 0.912 0.913 0.915 0.919

Comparative Example 2

[0207] The following mixture having a clearing point of 83° C. and a birefringence of 0.06 at 550 nm is formulated (in wt. %):

TABLE-US-00007 Irgacure ® 369 1.00 Irganox ® 1076 0.12 LC242 26.30 RM 2 40.00 RM 3 18.87 RM 4 13.11 TegoTwin ® 4100 0.60

[0208] The mixture can be annealed at temperatures ranging from 71 to 65° C.

[0209] The retardation profile (retardation dispersion and retardation versus viewing angle at different wavelengths) as shown in FIGS. 3a and 3b is measured using an ellipsometer and the thickness of 2.29 μm is measured using a surface profiler.

[0210] The retardation dispersion values at different angles of incidence are shown in Table 3 below.

TABLE-US-00008 TABLE 3 Angle (°) 60 40 20 0 −20 −40 R550 129.4 142.5 153.8 159.1 156.7 147.9 R450/R550 0.925 0.920 0.918 0.917 0.918 0.920

[0211] In order to test the durability of the polymer film, the film is exposed to a temperature of 80° C. for a time up to 260 h. Table 3.1 summarizes the result of the durability test

TABLE-US-00009 TABLE 3.1 Time at 80° C. [h] 0 0.5 1 2 5 22 97 260 R(450)/R(550) 0.918 0.949 0.953 0.956 0.961 0.968 0.976 0.986

Example 2

[0212] The following mixture having a clearing point of 76° C. and a birefringence of 0.06 at 550 nm is formulated (in wt. %):

TABLE-US-00010 Irgacure ® 369 1.00 Irganox ® 1076 0.12 LC242 26.88 RM 1 37.63 RM 2 30.00 RM 4 3.77 TegoTwin ® 4100 0.60

[0213] The mixture can be annealed at temperatures ranging from 70 to 52° C.

[0214] The retardation profile (retardation dispersion and retardation versus viewing angle at different wavelengths) as shown in FIGS. 4a and 4b is measured using an ellipsometer and the thickness of 2.29 μm is measured using a surface profiler.

[0215] The retardation dispersion values at different angles of incidence are shown in Table 4 below.

TABLE-US-00011 TABLE 4 Angle (°) 60 40 20 0 −20 −40 R550 109.0 120.2 129.8 134.2 132.2 124.8 R450/R550 0.921 0.917 0.914 0.914 0.914 0.916

[0216] In order to test the durability of the polymer film, the film is exposed to a temperature of 80° C. for a time up to 260 h. Table 4.1 summarizes the result of the durability test

TABLE-US-00012 TABLE 4.1 Time at 80° C. [h] 0 0.5 1 2 5 22 97 260 R(450)/R(550) 0.914 0.922 0.924 0.924 0.926 0.928 0.931 0.934

[0217] Dispersion Control

[0218] The following mixtures comprising each 1.00 wt. % Irgacure® 369, 0.08 wt. % Irganox® 1076 and 1.00 wt. % Zonyl FSO® 100, are formulated (in wt. %):

TABLE-US-00013 No. RM 1 RM 2 RM 3 RM 4 LC 242 R.sub.450/R.sub.550 I 0.00 40.00 17.92 15.00 25.00 0.90 II 3.25 40.00 14.67 15.00 25.00 0.88 III 6.51 40.00 11.41 15.00 25.00 0.87 IV 9.77 40.00 8.15 15.00 25.00 0.85 V 13.04 40.00 4.88 15.00 25.00 0.83 VI 17.92 40.00 0.00 15.00 25.00 0.79

[0219] As can be seen from the values for R.sub.450/R.sub.550, RM 1 is required to achieve a strong negative dispersion effect and by using RM 1, dispersions as low as 0.79 can be achieved.