PACKAGING METHOD AND ASSOCIATED PACKAGING STRUCTURE

Abstract

The present disclosure provides a packaging method, including: providing a first semiconductor substrate; forming a bonding region on the first semiconductor substrate, wherein the bonding region of the first semiconductor substrate includes a first bonding metal layer and a second bonding metal layer; providing a second semiconductor substrate having a bonding region, wherein the bonding region of the second semiconductor substrate includes a third bonding layer; and bonding the first semiconductor substrate to the second semiconductor substrate by bringing the bonding region of the first semiconductor substrate in contact with the bonding region of the second semiconductor substrate; wherein the first and third bonding metal layers include copper (Cu), and the second bonding metal layer includes Tin (Sn). An associated packaging structure is also disclosed.

Claims

1. A packaging method, comprising: providing a first semiconductor substrate; forming a bonding region on the first semiconductor substrate, wherein the bonding region of the first semiconductor substrate includes a first bonding metal layer and a second bonding metal layer; providing a second semiconductor substrate having a bonding region, wherein the bonding region of the second semiconductor substrate includes a third bonding layer; and bonding the first semiconductor substrate to the second semiconductor substrate by bringing the bonding region of the first semiconductor substrate in contact with the bonding region of the second semiconductor substrate; wherein the first and third bonding metal layers include copper (Cu), and the second bonding metal layer includes Tin (Sn).

1. The method of claim 1, further comprising: providing a bonding temperature in a range from about 240 degrees Celsius to about 300 degrees Celsius.

3. The method of claim 2, further comprising: applying a pressing force being about 1 MPa to about 2 MPa per unit area or below in order to press the first and second semiconductor substrates against each other.

4. The method of claim 1, further comprising reacting the Sn included in the second bonding metal layer with the Cu included in the first and third bonding metal layers to form Cu.sub.3Sn until the Sn is substantially fully consumed.

5. The method of claim 1, wherein the first semiconductor substrate includes a Micro-Electro-Mechanical Systems (MEMS) device.

6. The method of claim 1, further comprising: removing a portion of the first semiconductor substrates.

7. A packaging method, comprising: providing a first semiconductor substrate; forming a bonding region on the first semiconductor substrate, wherein the bonding region of the first semiconductor substrate includes a first bonding metal layer; providing a second semiconductor substrate having a bonding region, wherein the bonding region of the second semiconductor substrate includes a second bonding layer; bonding the bonding region of the first semiconductor substrate with the bonding region of the second semiconductor substrate by utilizing an ancillary bonding metal; and applying a pressing force being about 1 MPa to about 2 MPa per unit area or below in order to press the first and second semiconductor substrates against each other.

8. The method of claim 7, wherein the first and second bonding metal layers include copper (Cu).

9. The method of claim 7, wherein the ancillary bonding metal includes Tin (Sn).

10. The method of claim 7, further comprising: providing a bonding temperature in a range from about 240 degrees Celsius to about 300 degrees Celsius.

11. The method of claim 7, further comprising: reacting the Sn included in the ancillary bonding metal layer with the Cu included in the first and second bonding metal layers to form Cu.sub.3Sn until the Sn is substantially fully consumed.

12. The method of claim 7, wherein the bonding of the bonding region of the first semiconductor substrate with the bonding region of the second semiconductor substrate by utilizing the ancillary bonding metal comprises: applying the ancillary bonding metal on the first bonding metal layer before the bonding.

13. The method of claim 7, wherein the bonding of the bonding region of the first semiconductor substrate with the bonding region of the second semiconductor substrate by utilizing the ancillary bonding metal comprises: applying the ancillary bonding metal on the second bonding metal layer before the bonding.

14. The method of claim 7, wherein the formation of the bonding region on the first semiconductor substrate comprises: depositing the first bonding metal layer on the first semiconductor substrate; and etching a portion of the first bonding metal layers to form the bonding region.

15. The method of claim 7, further comprising: etching the first semiconductor substrate to form a bonding mesa.

16. The method of claim 7, wherein the second semiconductor substrate includes an opening on a surface thereof, and a metal layer in the second semiconductor substrate is exposed through the opening to form the bonding region of the second semiconductor substrate.

17. The method of claim 7, wherein the first semiconductor substrate includes a Micro-Electro-Mechanical Systems (MEMS) device.

18. The method of claim 7, further comprising removing a portion of the first semiconductor substrates.

19. A packaging structure, comprising: a first semiconductor substrate having a first bonding region thereon; and a second semiconductor substrate having a second bonding region thereon; wherein the first bonding region is bonded with the second bonding region, and a bonding interface between the first and second bonding regions includes Cu.sub.3Sn.

20. The packaging structure of claim 19, wherein the first and second bonding regions include copper (Cu).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0005] Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

[0006] FIGS. 1-11 are a series of cross-sectional views illustrating processing steps to fabricate a CMOS-MEMS device structure.

DETAILED DESCRIPTION

[0007] The following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

[0008] Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

[0009] Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in the respective testing measurements. Also, as used herein, the term “about” generally means within 10%, 5%, 1%, or 0.5% of a given value or range. Alternatively, the term “about” means within an acceptable standard error of the mean when considered by one of ordinary skill in the art. Other than in the operating/working examples, or unless otherwise expressly specified, all of the numerical ranges, amounts, values and percentages such as those for quantities of materials, durations of times, temperatures, operating conditions, ratios of amounts, and the likes thereof disclosed herein should be understood as modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the present disclosure and attached claims are approximations that can vary as desired. At the very least, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. Ranges can be expressed herein as from one endpoint to another endpoint or between two endpoints. All ranges disclosed herein are inclusive of the endpoints, unless specified otherwise.

[0010] The present invention relates generally to bonding, particular to eutectic bonding. The following description is presented to enable one of ordinary skill in the art to make and use the invention and is provided in the context of a patent application and its requirements. Various modifications to the preferred embodiment and the generic principles and features described herein will be readily apparent to those skilled in the art. Thus, the present invention is not intended to be limited to the embodiment shown but is to be accorded the widest scope consistent with the principles and features described herein.

[0011] In the described embodiments, Micro-Electro-Mechanical Systems (MEMS) refers to a class of structures or devices fabricated using semiconductor-like processes and exhibiting mechanical characteristics such as the ability to move or deform. MEMS often, but not always, interact with electrical signals. MEMS devices include, but are not limited to, gyroscopes, accelerometers, magnetometers, pressure sensors, and radio-frequency components, In some embodiments, a MEMs device structure may include a plurality of the aforesaid MEMs devices, Silicon wafers containing a MEMS device or a MEMS device structure are referred to as MEMS wafers.

[0012] In the described embodiments, MEMS device may refer to a semiconductor device implemented as a micro-electro-mechanical system. A MEMS device structure may refer to any feature associated with an assembly of a plurality of MEMS devices. An engineered silicon-on-insulator (ESOI) wafer may refer to a SOI wafer with cavities beneath the silicon device layer or substrate. Cap or handle wafer typically refers to a thicker substrate used as a carrier for the thinner silicon sensing substrate in a silicon-on-insulator wafer. Cap or handle substrate and cap or handle wafer can be interchanged. In the described embodiments, a cavity may refer to an opening or recession in a substrate wafer and enclosure may refer to a fully enclosed space.

[0013] To describe the features of the invention in more detail, apparatus and fabrication methods to achieve a MEMS device with features including improved bonding temperature and pressing force applied during bonding are disclosed.

[0014] FIGS. 1-11 are a series of cross-sectional views illustrating processing steps to fabricate a MEMS device assembly, or a MEMS device, according to an embodiment of the present disclosure. In FIG. 1, a sensing substrate 104 and a cap substrate 101 are bonded together with a thin dielectric film 103 therebetween to form an ESOI substrate 102. Please note that in the exemplary embodiment of the present disclosure, the sensing substrate 104 and the cap substrate 101 are bonded together by fusion bonding at relatively high processing temperatures, which enables more complete removal of chemical species from the dielectric materials in the substrates prior to sealing cavities of the MEMS structures. Both substrates are annealed during bonding, which reduces outgassing of chemical species during the cavity formation process. The MEMS structures bonded by fusion bonding are mechanically stronger compared to metal bonding due to a higher bonding ratio. In addition, fusion bonding enables the formation of through substrate vias (TSVs) in the MEMS structures without degrading yield. However, the concept of the present disclosure is not limited thereto. One of ordinary skill in the art would recognize many variations, modifications, and alternatives. The concept of the present disclosure may be also applied to other types of MEMS device assembly in some embodiments.

[0015] The thin dielectric film 103 includes materials such as silicon oxide or other insulating layer. Along with a surface of the cap substrate 101, a plurality of cavities 112 of desired sizes are defined and patterned on through isotropic etching, for example, but this is not a limitation of the present disclosure. One of ordinary skill in the art would recognize many variations, modifications, and alternatives, The plurality of cavities 112 are utilized to accommodate an adjacent movable proof mass of a MEMS device to be fabricated. The size of each cavity 112 may be determined according to the movable proof mass and/or desired performance of the MEMS device. In some embodiments, each cavity 112 may be of different depth or dimension than the other cavities.

[0016] The sensing substrate 104 is then thinned using a grinding and/or other thinning process to achieve the desired thickness as illustrated in FIG. 2. Existing thinning techniques like Chemical Mechanical Planarization (CMP) and/or Reactive Ion Etching (RIE) can be used to achieve the desired thickness. Suitable grinding and polishing equipments may be used for the thinning process. One of ordinary skill in the art would recognize many variations, modifications, and alternatives. In some other embodiments, an etch stop layer is integrated into sensing substrate 104 in order to facilitate precision control of the thinning process. One of ordinary skill in the art would recognize many variations, modifications, and alternatives.

[0017] Referring to FIG. 3, a metal layer 302 is then deposited on the sensing substrate 104, In this embodiment, the metal layer 302 includes a copper (Cu) layer. In particular, the metal layer 302 includes a thin titanium (Ti) layer beneath the Cu layer. In some embodiments, the metal layer 302 is deposited using electroplating, physical vapor deposition (PVD), or a Chemical Vapor Deposition (CVD) process. One of ordinary skill in the art would recognize many variations, modifications, and alternatives. Referring to FIG. 4, another metal layer 304 different from the metal layer 302 is then deposited on the metal layer 302. In this embodiment, the metal layer 304 includes a tin (Sn) layer, In some embodiments, the metal layer 304 is deposited using electroplating, physical vapor deposition (PVD), or a Chemical Vapor Deposition (CVD) process. One of ordinary skill in the art would recognize many variations, modifications, and alternatives.

[0018] The next step shown in FIG. 5 is to pattern and etch the metal layers 302 and 304 according to a structure of the MEMS device to be produced. As a consequence of the pattern and etch operation, a plurality of bonding regions 402′ and 404′ are formed for bonding in following steps, such as eutectic bonding being employed in the exemplary embodiment. In particular, each bonding region 402′ includes metal layers 402 and 406; and each bonding region 404′ includes metal layers 404 and 408, wherein the metal layers 406 and 408 are regarded as ancillary bonding metal layers during the bonding operation to form eutectic bond.

[0019] For purposes of clarity, a photolithography process in which a photoresist layer is deposited on the metal layer 304 and patterned to form an etch mask is not shown in this process flow. The dimensions of the etch mask may be tightly controlled during photolithography and the etch mask may be formed from any suitable material that is resistant to the etching process used to etch the metal layers. In some embodiments, an etch mask of Silicon Nitride (Si.sub.3N.sub.4) is utilized. In some other embodiments, a photoresist layer can serve as the etch mask. One of ordinary skill in the art would recognize many variations, modifications, and alternatives. Although a one dimensional cross section is illustrated in FIG. 5, it will be evident to one of skill in the art that a two-dimensional pattern of the desired geometry is formed in the metal layers 302 and 304. In some embodiments, the bonding regions 402′ and 404′ may further comprise nickel (Ni), germanium (Ge), aluminum (Al). In other embodiments, other materials such as gold (Au), indium (In), or other solders having good adhesion underlying layers and improved wetting capability may be used for the bonding regions.

[0020] A first shallow cavity etch is performed selectively to the sensing substrate 104. During the first shallow cavity etch, shallow cavities are formed to reach a certain depth measured from a surface of the sensing substrate 104 of FIG. 5. After the first shallow cavity etch, a plurality of first step bonding mesas 502 and 504 are left and protruding from an etched surface of the sensing substrate 104 as can be seen in FIG. 6. To be more specific, the plurality of first step bonding mesas 502 and 504 are located beneath the bonding regions 402′ and 404′. The plurality of first step bonding mesas 502 and 504 carry the conductive bonding regions 402′ and 404′ to form a stack structure. In the exemplary embodiment, the width of the plurality of first step bonding mesas 502 and 504 may be substantially equal or wider than the bonding regions 402′ and 404′. The side walls of the plurality of first step bonding mesas 502 and 504 may be vertical or tapered. One of ordinary skill in the art would recognize many variations, modifications, and alternatives.

[0021] The sensing substrate 104 is then patterned and etched to form the sensing substrate as illustrated in FIG. 7. The sensing substrate includes a proof-mass, balanced or unbalanced, suspended by at least one spring or elastic device and free to move in at least one of the x-, y-, and z-directions, with at least one electrode embedded in the at least one spring or elastic device. The at least one spring or elastic device is attached to a support structure, which is attached to the sensing substrate 104. The proof-mass, support structure, and at least one electrode are fabricated in the same semiconductor layers as the drive/sense circuitry. In some embodiments, the at least one spring or elastic device and the support structure form a network of supports. The proof-mass, suspended by the network of supports, is free to move in any direction. The MEMS capacitively senses or produces movement of the proof-mass in any direction. In some embodiments, the direction can include a direction along at least one of the x-, y-, and z-directions.

[0022] In some embodiments, the patterning and etching techniques used to form the sensing substrate may vary depending on the type of the MEMS device. For example, the patterning and etching for a MEMS accelerometer is different from the patterning and etching used for a MEMS gyroscope. Existing etching techniques like anisotropic etching, RIE, or the like may be used. In some embodiments, the thickness of the sensing substrate 104 can vary as a function of position along the length of the sensing substrate, where the length is defined along a direction orthogonal to the thickness of the substrate. For example, the sensing substrate 104 may have a first thickness at one end, a second thickness in the center, and a third thickness at the other end.

[0023] Next, as illustrated in FIG. 8A, the ESOI substrate 102 and a complementary metal-oxide semiconductor (CMOS) wafer 106 are pre cleaned and then aligned prior to eutectic bonding. In the present disclosure, a CMOS wafer can be termed as a CMOS substrate. The CMOS wafer 106 may include a substrate 812. The substrate 812 may comprise a semiconductor material such as silicon, although other semiconductor materials may be used. A plurality of CMOS devices 814 (such as transistors) is formed at a surface of substrate 812. Furthermore, an interconnect structure 816 is formed to electrically couple to the CMOS devices 814. The interconnect structure 816 may include dielectric layers, which further include low-k dielectric layers, non-low-k dielectric layers such as passivation layers, and the like. Metal lines and vias, which may be formed of copper, aluminum, and combinations thereof, are formed in the dielectric layers.

[0024] A top dielectric layer 810 of the interconnect structure 816 is patterned, and a plurality of openings, including openings 802 and 804 corresponding to the bonding regions 402′ and 404′, are formed in the top dielectric layer 810. As a result, bonding regions 806 and 808 are exposed. The dielectric layer 810 has a different melting characteristic compared to a bonding metal of a plurality of bonding regions 806 and 808 of the CMOS substrate 106. In the exemplary embodiment, the bonding regions 806 and 808 include a Cu layer. In particular, the bonding regions 806 and 808 further include a thin Ti layer beneath the Cu layer. However, this is not a limitation of the present invention.

[0025] In some other embodiments, another metal layer different from the bonding metal of the bonding regions 806 and 808 is further formed on the bonding regions 806 and 808 for eutectic bonding. The metal layer form on the bonding regions 806 and 808 includes the metal the same with that of the metal layers 406 and 408. One embodiment is illustrated in FIG. 8B, wherein metal layers 406′ and 408′ are electroplated onto the bonding regions 806 and 808 respectively. In still some other embodiments, the same or similar to FIG. 8B, another metal layer different from the bonding metal of the bonding regions 806 and 808 is further formed on the bonding regions 806 and 808 for eutectic bonding, but the metal layers 406 and 408 of FIG. 8B is omitted. One embodiment is illustrated in FIG. 8C, wherein Sn layers 406′ and 408′ are electroplated onto the bonding regions 806 and 808 respectively, and the bonding regions of the sensing substrate 104 includes only the metal layers 402 and 404.

[0026] Thereafter, the bonding regions 402′ and 404′ (or the metal layer 402 and 404 for FIG. 8C) of the ESOI substrate 102 is brought in contact with the bonding regions 806 and 808 (or the metal layers 406′ and 408′ for FIGS. 8B and 8C) through the openings 802 and 804 of the CMOS wafer 106. During the bonding, both the ESOI substrate 102 and the CMOS wafer 106 are heated, and a pressing force is applied to press the ESOI substrate 102 and the CMOS wafer 106 against each other when the temperature is elevated. In other words, the bonding interface between the ESOI substrate 102 and the CMOS wafer 106 is subjected to heat and a pressing force in order to reflow the metal comprised in the bonding regions 402′ and 404′ (or the metal layer 402 and 404 for FIG. 8C) and the corresponding bonding regions 806 and 808 (and the metal layers 406′ and 408′ for FIGS. 8B and 8C) of the CMOS wafer 106. The pressing force is applied on the ESOI substrate 102 against the CMOS wafer 106, and/or on the CMOS wafer 106 against the ESOI substrate 102 so as to create hermetic seals.

[0027] Reflow of the metal results in a fused bond structure that provides an ohmic contact between the ESOI substrate 102 and the CMOS wafer 106. In the exemplary embodiment, the bond between the ESOI substrate 102 and the CMOS wafer 106 includes a Cu—Sn eutectic bond. This eliminates the need for providing a separate electrical path for the signals between the sensing substrate and the CMOS wafer 106. Eutectic reactions are a triple point in the phase diagram where solid alloys mixtures transform directly to a liquid phase. The eutectic melting temperature for the Cu—Sn bond is about 231 degrees Celsius, in order to ensure an adequate or sufficient eutectic reaction for the Cu—Sn bond, a bonding temperature provided during the eutectic bonding process may be higher than the eutectic temperature. In this embodiment, a bonding temperature provided during the eutectic bonding process may be in a range from about 240 degrees Celsius to about 300 degrees Celsius with a pressing force being about 1 MPA to about 2 MPa per unit area or below. However, this is not a limitation of the present disclosure.

[0028] Compared with existing eutectic bonds, the disclosed Cu—Sn eutectic bond has a lower bonding temperature and a lower bonding pressing force by using a Cu—Sn eutectic bond. In particular, some existing eutectic bonds including the Au—In bond, the Au—Sn bond, the Au—Ge bond, the Au—Si bond, and the Al—Ge bond, wherein the the Au—Sn bond, the Au—Ge bond, the Au—Si bond, and the Al—Ge bond all requires a high bonding temperature. The Au—Sn bond has a eutectic melting temperature of about 280 degrees Celsius, and requires a bonding temperature in a range of about 280 degrees Celsius to about 310 degrees Celsius. The Au—Ge bond has a eutectic melting temperature of about 361 degrees Celsius, and requires a bonding temperature in a range of about 380 degrees Celsius to about 400 degrees Celsius. The Au—Si bond has a eutectic melting temperature of about 363 degrees Celsius, and requires a bonding temperature in a range of about 390 degrees Celsius to about 415 degrees Celsius. The Al—Ge bond has a eutectic melting temperature of about 419 degrees Celsius, and requires a bonding temperature in a range of about 430 degrees Celsius to about 450 degrees Celsius.

[0029] Although the Au—In bond has a eutectic melting temperature of about 156 degrees Celsius, and requires a bonding temperature in a range of about 180 degrees Celsius to about 210 degrees Celsius which is not higher than the disclosed Cu—Sn bond. However, the Au—In bond is regarded as incompatible with the standard CMOS process. Moreover, the Au—In bond, the Au—Sn bond, the Au—Ge bond, the Au—Si bond, and the Al—Ge bond all have a pressing force being above about 10 MPa per unit area, which may become inapplicable when technology shrinkages.

[0030] Upon cooling, a microstructure is formed as shown in FIG. 9, which is both strong and hermetic. Eutectic metal compositions have several benefits as sealing materials, including the ability to accurately deposit and define the metals in desired patterns, the tolerance to surface deviations, roughness and particulates, plus metals' inherent hermeticity and conductivity. Hermeticity, the degree of air tightness for a vessel or package, is useful for MEMS packages because the mechanical and electrical functionality of the device within the package typically relies on critical environmental control. Change in the atmosphere inside the package can bring about a shift in performance or even a total failure of the device.

[0031] For the embodiment configured as FIG. 8A, an alloy 1006 in FIG. 9 is formed by the metal layer 406 and at least a portion of the metal layers 402 and 806; and similarly, an alloy 1008 is formed by the metal layer 408 and at least a portion of the metal layers 404 and 808. For the embodiment configured as FIG. 8B, an alloy 1006 in FIG. 9 is formed by the metal layers 406, 406′ and at least a portion of the metal layers 402 and 806; and similarly, an alloy 1008 is formed by the metal layers 408, 408′ and at least a portion of the metal layers 404 and 808. For the embodiment configured as FIG. 8C, an alloy 1006 in FIG. 9 is formed by the metal layer 406′ and at least a portion of the metal layers 402 and 806; and similarly, an alloy 1008 is formed by the metal layer 408′ and at least a portion of the metal layers 404 and 808. In particular, the metal layers 406, 408, 406′ and 408′ are substantially fully reacted with the above or beneath metal layers 402, 404, 802 and 804.

[0032] In the exemplary embodiment, the alloys 1006 and 1008 include Cu.sub.3Sn. Some unreacted Cu remained after the bonding is acceptable. But any unreacted Sn remained after the bonding is not desired because Sn is less stable than Cu and Cu.sub.3Sn. In order to fully consume Sn in the metal layers 406, 408, 406′ and 408′, a thickness of the metal layers 406, 408, 406′ and 408′ may be predetermined in accordance with a thickness of the metal layers 402, 404, 802 and 804 above or beneath the metal layers 406, 408, 406′ and 408′.

[0033] In a subsequent step, a pad opening step is performed. Portions 902 and 904 of the cap substrate 101 are removed as shown in FIG. 10, for example, in an etching step or a grind-open step. The resulting structure is shown in FIG. 11. Bond pads 1002 and 1004 in CMOS substrate 106 are hence no longer covered by the ESOI substrate 102. Bond pads 1002 and 1004 are exposed from CMOS substrate 106 in order to receive external bonding or wiring. In some embodiments, the etching is anisotropic, and hence edges of the cap substrate 101 of FIG. 11 are substantially straight. Alternatively, the portions 902 and 904 can be removed by a grind-open step, wherein a grinding wheel or blade is used to erase the portions 902 and 904. In some embodiments, the sensing substrate 104 may be thinned using a grinding and/or other thinning process to achieve a desired thickness before the formation of the MEMS-device-comprising package is finished.

[0034] The present disclosure provides a method for producing an improved bond of wafer level package (WLP) that has been widely used in three-dimensional (3D) IC, chip scale package (CSP) and MEMS device assembly. However, the disclosed bond and associated method are not limited to the WLP or the 3D IC, CSP and MEMS device. The disclosed bonding process can be integrated into the standard CMOS process, thus yielding a simplified, low cost solution. Compared with existing eutectic bonds, the disclosed Cu—Sn eutectic bond has a lower bonding temperature and a lower bonding pressing force by using a Cu—Sn eutectic bond.

[0035] Some embodiments of the present disclosure provide a packaging method. The packaging method includes: providing a first semiconductor substrate; forming a bonding region on the first semiconductor substrate, wherein the bonding region of the first semiconductor substrate includes a first bonding metal layer and a second bonding metal layer; providing a second semiconductor substrate having a bonding region, wherein the bonding region of the second semiconductor substrate includes a third bonding layer; and bonding the first semiconductor substrate to the second semiconductor substrate by bringing the bonding region of the first semiconductor substrate in contact with the bonding region of the second semiconductor substrate; wherein the first and third bonding metal layers include copper (Cu), and the second bonding metal layer includes Tin (Sn).

[0036] Some embodiments of the present disclosure provide a packaging method. The packaging method includes: providing a first semiconductor substrate; forming a bonding region on the first semiconductor substrate, wherein the bonding region of the first semiconductor substrate includes a first bonding metal layer; providing a second semiconductor substrate having a bonding region, wherein the bonding region of the second semiconductor substrate includes a second bonding layer; bonding the bonding region of the first semiconductor substrate with the bonding region of the second semiconductor substrate by utilizing an ancillary bonding metal; and applying a pressing force being about 1 MPA to about 2 MPa per unit area or below in order to press the first and second semiconductor substrates against each other.

[0037] Some embodiments of the present disclosure provide packaging structure. The packaging structure includes a first semiconductor substrate having a first bonding region thereon; and a second semiconductor substrate having a second bonding region thereon; wherein the first bonding region is bonded with the second bonding region, and a bonding interface between the first and second bonding regions includes Cu.sub.3Sn.

[0038] The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure.