Orthopaedic implant and method for manufacturing such an orthopaedic implant

Abstract

This orthopedic implant includes a polymer substrate with an outer surface intended to be secured to a bone tissue. The outer surface is covered with metal particles including titanium. The particles include large primary particles and small secondary particles. The primary particles and the secondary particles are evenly distributed over the outer surface.

Claims

1. An orthopaedic implant, including: at least one substrate comprising at least one polymer plastic material that provides a polymer-plastic outer surface configured to be secured to a bone tissue; and particles of at least one metallic material comprising titanium partially covering the outer surface such that the surface area of the outer surface portion that is not covered with the particles is between 15% and 30% of the total surface area of the outer surface, wherein: the particles comprise primary particles and secondary particles; the primary particles have a grain size ranging from 180 μm to 600 μm; the primary particles are distributed over the outer surface such that primary interstices between the primary particles have surface areas that are approximately equal in which each surface area is within ±20% of a median surface area for the primary interstices; the secondary particles have a grain size ranging from 70 μm to 145 μm; and the primary particles and the secondary particles are distributed in a relatively uniform manner over the outer surface such that the secondary particles are present within the primary interstices between the primary particles.

2. The orthopaedic implant according to claim 1, wherein the polymer plastic material is selected from the group consisting of a polyethylene (PE), an ultra-high molecular weight polyethylene (UHMW-PE), a highly cross-linked polyethylene (XLPE), an E-vitaminized polyethylene, a polyurethane and a polyether ether ketone (PEEK).

3. The orthopaedic implant according to claim 1, wherein the or each metallic material is selected from the group consisting of pure titanium and alloys of titanium, chromium, cobalt and stainless steel.

4. The orthopaedic implant according to claim 1, wherein the primary particles and the secondary particles are composed of the same metallic material.

5. The orthopaedic implant according to claim 1, wherein the number of primary particles is between 5% and 50% of the sum of the number of primary particles and the number of secondary particles.

6. The orthopaedic implant according to claim 1, wherein the outer surface has generally the shape of a spheroidal portion.

7. The orthopaedic implant according to claim 1, wherein the substrate is a one-piece single substrate formed entirely from the polymer plastic material.

8. The orthopaedic implant according to claim 1, wherein the primary particles have a grain size ranging from 200 μm to 500 μm, and the secondary particles have a grain size ranging from 90 μm to 125 μm.

9. The orthopaedic implant according to claim 1, wherein the surface area of the outer surface portion that is not covered with the particles is between 20% and 25% of the total surface area of the outer surface.

10. The orthopaedic implant according to claim 1, wherein the number of primary particles is between 10% and 30% of the sum of the number of primary particles and the number of secondary particles.

11. The orthopaedic implant according to claim 1, wherein the outer surface has the shape of a half-sphere.

12. The orthopaedic implant according to claim 1, wherein the orthopaedic implant is an acetabular cup for a hip prosthesis.

13. The orthopaedic implant according to claim 1, wherein the outer surface is stepless.

14. A method of manufacturing the orthopaedic implant according to claim 1, the method comprising the steps of: heating the outer surface to a softening temperature of the polymer plastic material; partially covering the outer surface with the primary particles such that the primary interstices between the primary particles have surface areas that are approximately equal in which each surface area is within ±20% of the median surface area for the primary interstices; pressing a heated die against the outer surface so as to secure the primary particles to the outer surface; partially covering the outer surface with the secondary particles in a relatively uniform manner over the outer surface such that the secondary particles are present within the primary interstices between the primary particles; and pressing the heated die against the outer surface so as to secure the secondary particles to the outer surface.

15. The method according to claim 14, wherein the step of partially covering the outer surface with the primary particles is performed before the step of partially covering the outer surface with the secondary particles.

16. The method according to claim 14, wherein the step of partially covering the outer surface with the primary particles and the step of partially covering the outer surface with the secondary particles are performed in an enclosed volume that is pressurized and heated at a temperature lower than the melting temperature of the polymer plastic material.

17. The method according to claim 14, wherein the primary particles have a grain size ranging from 200 μm to 500 μm, and the secondary particles have a grain size ranging from 90 μm to 125 μm.

18. The method according to claim 14, wherein the orthopaedic implant is an acetabular cup for a hip prosthesis.

Description

(1) The present invention will be well understood and its advantages will also appear in the light of the following description, given only by way of a non-limiting example and made with reference to the appended drawings, wherein:

(2) FIG. 1 is a perspective view of an orthopaedic implant in accordance with the invention;

(3) FIG. 2 is a perspective view, truncated along plane II of FIG. 1 and along an angle different from FIG. 1, of the orthopaedic implant of FIG. 1;

(4) FIG. 3 is a top view of the orthopaedic implant of FIG. 1;

(5) FIG. 4 is a microscopic photography of a portion of the orthopaedic implant of FIG. 1;

(6) FIG. 5 is a microscopic photography, to half the scale of FIG. 4, of a portion of the orthopaedic implant of FIG. 1; and

(7) FIG. 6 is a schematic view illustrating a step of a method in accordance with the invention, for manufacturing the orthopaedic implant of FIGS. 1 to 5.

(8) FIG. 1 illustrates an orthopaedic implant 1, which forms an acetabular cup for hip prosthesis. In other words, the orthopaedic implant 1 is an acetabular implant. The orthopaedic implant 1 includes a substrate 2 comprising at least one polymer plastic material. In the example of the figures, the orthopaedic implant 1 includes only the substrate 2, which is in one-piece.

(9) The polymer plastic material forming the substrate 2 is a high-density polyethylene (HDPE). In practice, this polymer plastic material may be selected in the group consisting of a high-density polyethylene (HDPE), a highly cross-linked polyethylene (XLPE), a polyurethane and a polyether ether ketone (PEEK).

(10) The substrate 2 has an outer surface 3 which is intended to be secured to a bone tissue belonging to the non represented iliac bone. As shown in FIG. 2, the outer surface 3 has generally the shape of a half-spheroid or even a half-sphere, intended to be embedded in the iliac bone. The outer surface 3 has a diameter D3 of about 50 mm. Alternatively, the diameter of the outer surface can be selected between 40 mm and 70 mm.

(11) The substrate 2 further has an inner surface 4 located opposite to the outer surface 3. The inner surface 4 forms an acetabular cup surface, for the articulation of a non represented femoral head.

(12) As shown in FIG. 3, the outer surface 3 is partially covered with particles 5 of a metallic material composed here of pure titanium. In practice, the or each metallic material may be a titanium alloy, hence a material comprising titanium and another material, metallic or not, for example chromium, cobalt and stainless steel such as the 316LVM steel. For example, such alloys are defined in the ISO 5832 standard.

(13) A portion of the outer surface 3 is not covered with the particles 5. The surface area of this outer surface 3 portion not covered with the particles 5 represents about 25% of the total surface area of the outer surface 3. In other words, the particles 5 cover about 75% of the total surface area of the outer surface 3. In the example of the figures, the total surface area of the outer surface 3 is about 3930 mm.sup.2, while the surface area of this non-covered outer surface 3 portion.

(14) As shown in FIGS. 4 and 5, the particles 5 mainly comprise primary particles 51 and secondary particles 52. In the example of the figures, the primary particles 51 and the secondary particles 52 are composed of the same metallic material, pure titanium.

(15) The number of primary particles 51 represents substantially between 5% and 50%, preferably between 10% and 30%, of the sum of the number of primary particles 51 and the number of secondary particles 52, that is to say about the total number of particles 5. As a corollary, the number of secondary particles 52 represents substantially between 95% and 50%, preferably between 70% and 30%, of the sum of the number of primary particles 51 and the number of secondary particles 52.

(16) In the example of the figures, the total mass of primary 51 and secondary 52 particles may be for example comprised between 4 g and 20 g.

(17) The primary particles 51 have a grain size ranging substantially from 200 μm to 500 μm. The secondary particles 52 have a grain size ranging substantially from 90 μm to 125 μm.

(18) In practice, the primary particles 51 have a grain size ranging substantially from 180 μm to 600 μm. In practice, the secondary particles 52 have a grain size ranging substantially from 70 μm to 145 μm.

(19) The primary particles 51 and the secondary particles 52 are distributed in a relatively uniform manner over the outer surface 3. Thus, the primary interstices between primary particles 51 have approximately equal surface areas. These primary interstices house the secondary particles 52.

(20) As illustrated in FIG. 6, a method in accordance with the invention, for manufacturing the orthopaedic implant 1, comprises the steps of: placing the substrate 2 in a mold 101, which allows in particular performing the manufacturing method under a controlled atmosphere; heating the outer surface 3 to a softening temperature of the high-density polyethylene (HDPE); partially covering the outer surface 3 with primary particles 51, so that the primary particles 51 are distributed in a relatively uniform manner over the outer surface 3; pressing a heated die 102 against the outer surface 3, so as to secure the primary particles 51 to the outer surface.

(21) Furthermore, as shown in FIG. 6, such a manufacturing method comprises the steps of: partially covering the outer surface 3 with secondary particles 52, so that the secondary particles 52 are distributed in a relatively uniform manner over the outer surface 3; and pressing the heated die 102 against the outer surface 3, so as to secure the secondary particles 52 to the outer surface 3.

(22) In the method in accordance with the invention, the step of covering the outer surface 3 with the primary particles 51 is performed before the step of covering the outer surface 3 with the secondary particles 52.

(23) Alternatively, the primary particles and the secondary particles may be mixed beforehand to form a homogeneous powder. Thus, the step of covering the outer surface with the primary particles may be performed simultaneously in the step of covering the outer surface with the secondary particles.

(24) The step of covering the outer surface with the primary particles and the step of covering the outer surface with the secondary particles are performed by putting in contact in the enclosed volume of the mold 101 which is pressurized and heated at a temperature lower than the melting temperature of the polymer plastic material. To this end, dies 102 and 103 may exert pressures P102 and P103 on the mold 101. A spacer 104 distributes the pressures P102 and P103.

(25) In service, the orthopaedic implant 1 forms an acetabular cup for hip prosthesis or acetabular implant. The orthopaedic implant 1 is secured to a bone tissue belonging to the non represented iliac bone. The articulation of the femoral head is made on the inner surface 4.