Gas Migration Mitigation for Oil and Gas Well Cements

Abstract

A method of using a nanosilica-containing cement in a well cementing operation in a well, the method comprising the steps of pumping a nanosilica-containing cement formulation into the well, wherein the nanosilica-containing cement formulation comprises maltodextrin-coated nanosilica and a cement formulation, where the maltodextrin-coated nanosilica comprises nanosilica particles encapsulated by maltodextrin coating, wherein the pH of the nanosilica-containing cement formulation is between 9 and 14, maintaining a temperature in the well due to a temperature of a formation surrounding the well, wherein the disintegration of the maltodextrin coating is initiated due to the temperature and pH of the nanosilica-containing cement, exposing the nanosilica particles due to the disintegration of the maltodextrin coating from the maltodextrin-coated nanosilica, and reacting the nanosilica particles with the cement formulation such that the transition time is reduced.

Claims

1. A method of using a nanosilica-containing cement in a well cementing operation in a well, the method comprising the steps of: pumping a nanosilica-containing cement formulation into the well, wherein the nanosilica-containing cement formulation comprises maltodextrin-coated nanosilica and a cement formulation, where the maltodextrin-coated nanosilica comprises nanosilica particles encapsulated by maltodextrin coating, wherein the pH of the nanosilica-containing cement formulation is between 9 and 14; maintaining a temperature in the well due to a temperature of a formation surrounding the well, wherein the disintegration of the maltodextrin coating is initiated due to the temperature and pH of the nanosilica-containing cement; exposing the nanosilica particles due to the disintegration of the maltodextrin coating from the maltodextrin-coated nanosilica; and reacting the nanosilica particles with the cement formulation to form a set cement, wherein the transition time of the nanosilica-containing cement formulation is reduced compared to the transition time of the cement formulation.

2. The method of claim 1, further comprising the steps of: mixing an amount of maltodextrin with a nanosilica particle solution to produce a maltodextrin-containing solution, where the nanosilica particle solution comprises the nanosilica particles suspended in water, where mixing continues until all of the maltodextrin is dissolved; mixing an amount of borate with the maltodextrin-containing solution to produce a pre-reaction mixture, wherein the borate is selected from the group consisting of sodium tetraborate, potassium tetraborate, boric acid, and combination of the same; sonicating the pre-reaction mixture in an ultrasonic bath to produce a sonicated mixture at a temperature between 90° F. (32.2° C.) and 100° F. (37.8° C.); mixing the sonicated mixture at ambient conditions for at least 12 hours to produce the reaction mixture; and separating the reaction mixture to produce the maltodextrin-coated nanosilica, wherein the maltodextrin is covalently bound to a surface of the nanosilica particles through a boronic ester functional group.

3. The method of claim 1, further comprising the step of mixing the maltodextrin-coated nanosilica and the cement formulation to produce the nanosilica-containing cement formulation.

4. The method of claim 1, wherein the nanosilica particles in the nanosilica-containing cement formulation are present in an amount between 0.01% by weight of cement and 10% by weight of cement.

5. A composition to provide on-demand release of a silica nanoparticle into a cement formulation, the composition comprising: a maltodextrin-coated nanosilica particle comprising: a nanosilica particle, and a maltodextrin coating, where the maltodextrin coating comprises a boronic ester bound maltodextrin surrounding the nanosilica particle; and the cement formulation comprising water and a cement.

6. The composition of claim 5, where the nanosilica is present in an amount between 0.01% by weight of cement and 10% by weight of cement.

7. A method of producing a nanosilica-containing cement formulation, the method comprising the steps of: mixing an amount of maltodextrin with a nanosilica particle solution to produce a maltodextrin-containing solution, where the nanosilica particle solution comprises nanosilica particles suspended in water, where mixing continues until all of the maltodextrin is dissolved; mixing an amount of borate with the maltodextrin-containing solution to produce a pre-reaction mixture, wherein the borate is selected from the group consisting of sodium tetraborate, potassium tetraborate, boric acid, and combination of the same; sonicating the pre-reaction mixture in an ultrasonic bath to produce a sonicated mixture at a temperature between 90° F. (32.2° C.) and 100° F. (37.8° C.); mixing the sonicated mixture at ambient conditions for at least 12 hours to produce the reaction mixture; separating the reaction mixture to produce a maltodextrin-coated nanosilica; and mixing the maltodextrin-coated nanosilica with cement formulations to produce the nanosilica-containing cement formulations, wherein the cement formulations comprise water and a cement.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] These and other features, aspects, and advantages of the scope will become better understood with regard to the following descriptions, claims, and accompanying drawings. It is to be noted, however, that the drawings illustrate only several embodiments and are therefore not to be considered limiting of the scope as it can admit to other equally effective embodiments.

[0016] FIG. 1 is a schematic showing cement placement and gas migration in oil and gas wells.

[0017] FIG. 2 is a schematic representation of the reaction between maltodextrin, sodium tetraborate, and a nanosilica particle to produce a maltodextrin-coated nanosilica.

[0018] FIG. 3 is a schematic representation of an maltodextrin-coated nanosilica after a change in temperature results in the disintegration of the maltodextrin-coated nanosilica into a maltodextrin coating fragment and the nanosilica particle.

[0019] FIG. 4 is a raw XRD diffraction pattern and match of Saudi G cement.

[0020] FIG. 5 is a graph of thermogravimetric analysis from Example 2.

[0021] FIG. 6A is a DLS analysis (intensity distribution) of uncoated nanosilica particles.

[0022] FIG. 6B is a DLS analysis of a maltodextrin-coated nanosilica.

[0023] FIG. 6C is a DLS analysis of a maltodextrin-coated nanosilica.

[0024] In the accompanying Figures, similar components or features, or both, may have a similar reference label.

DETAILED DESCRIPTION

[0025] While the scope of the apparatus and method will be described with several embodiments, it is understood that one of ordinary skill in the relevant art will appreciate that many examples, variations and alterations to the apparatus and methods described here are within the scope of the embodiments.

[0026] Accordingly, the embodiments described are set forth without any loss of generality, and without imposing limitations, on the embodiments. Those of skill in the art understand that the scope includes all possible combinations and uses of particular features described in the specification.

[0027] The maltodextrin-coated nanosilica compositions described here advantageously overcome the problems associated with prior generations of nanosilicas. The maltodextrin coating on the nanosilica particle is a stimuli-responsive coating that can degrade under certain temperature or pH conditions. Advantageously, the maltodextrin-coated nanosilica when added to a cement slurry can shorten the transition time of the cement slurry after placement within the well. Advantageously, the maltodextrin-coated nanosilica can be used in cement compositions, where the released nanosilica particles can improve the cement properties. Advantageously, the maltodextrin-coated nanosilica can be better dispersed in the cement formulations compared to silica nanoparticles without encapsulation. Advantageously, the maltodextrin-coated nanosilica provides a method to modulate the reactivity of nanosilica particles in cement formulations. Advantageously, the nanosilica-containing cement formulations can improve cement properties and processes, including acceleration of the cementing process, early gel strength development, reduction of cement porosity, greater control over cement formulation rheology and improvements on colloidal silica nanoparticle dispersions can be achieved.

[0028] In order to mitigate the issues of cement slurry gelation, the methods to encapsulate the nanosilica particles render the nanoparticles inert to the surrounding cement slurry. The compositions and methods described can delay release of the nanosilica particles to the cement slurry such that the gelation phenomena are not observed when the cement slurry is being placed in the well. The release of the nanosilica particles allows for the exposure of the nanosilica particles to the cement when already placed such that the rheological side effects of the nanosilica particles do not inhibit the pumpability of the cement slurry. The nanosilica particles can be released from the maltodextrin coating due to the temperature and pH after the cement slurry is placed in the well. After decomposition of the maltodextrin coating, the isolated nanosilica particle is activated to provide rapid acceleration of the tricalcium silicate (C.sub.3S) hydration to calcium silicate hydrate (C-S-H). Rapid acceleration corresponds to gel strength development between 100 and 500 lbf/100 sq ft.

[0029] As used throughout, “nanosilica loading” refers to the amount of nanosilica solids per unit volume of fluid.

[0030] As used throughout, “disintegrate” or “disintegration” means breaking into smaller parts or pieces, such as fragmentation. In the context of disintegration of molecules, the parent molecule breaks into smaller, lower molecular weight species.

[0031] As used throughout, “well-mixed” means a fluid composition that is thoroughly blended such that the fluid composition approaches a homogeneous mixture where all components are equally distributed throughout the fluid composition.

[0032] Compositions are directed to an maltodextrin-coated nanosilica. The maltodextrin-coated nanosilica includes a nanosilica particle and a maltodextrin coating. The maltodextrin coating surrounds the nanosilica particle preventing reaction between the nanosilica particle and the cement formulation. Each individual nanosilica particle can be encapsulated with a maltodextrin coating. Alternately, an aggregate of nanosilica particles can be encapsulated with a maltodextrin coating.

[0033] The nanosilica particles can be any type of nanoparticle silica. In at least one embodiment, the nanosilica particles can include colloidal silica nanoparticles.

[0034] The maltodextrin coating is a boronic ester bound maltodextrin polymer surrounding the nanosilica particles. Maltodextrin is a short chain of 3 to 17 repeating glucose units (oligosaccharides) principally linked through glycosidic bonds that can dissolve in water. The maltodextrin coating is hydrophilic. Advantageously, the hydrophilic nature of the maltodextrin coating enables the dispersion of the maltodextrin-coated nanosilica. The reaction between maltodextrin, sodium tetraborate and the nanosilica particles is shown in FIG. 2. The Si—OH functionalities on the surface of the nanosilica particles are condensed with borate to render the maltodextrin-coated nanosilica. The sacrificial nature of the maltodextrin coating means the maltodextrin coating can disintegrate, as illustrated in FIG. 3. The maltodextrin-coated nanosilica (A) disintegrates upon application of heat to produce a maltodextrin coating fragment (B) and nanosilica particle (C).

[0035] In at least one embodiment, the disintegration can be due to an increase in the temperature of the maltodextrin-coated nano silica. The target temperature to trigger disintegration of the maltodextrin coating is between 180° F. (82° C.) and 932° F. (500° C.) and alternately, between 180° F. (82° C.) and 228° F. (108.9° C.). At temperatures of 120° F. (48.9° C.) and below, the temperature is not adequate to cause the maltoxdextrin coating to disintegrate and the nanosilica particle is not released and cannot react with the cement. At temperatures of 250° F. (121.1° C.) and above, the presence of nanosilica particles on the cement is minimal compared to the impact due of other components in the cement.

[0036] In at least one embodiment, the maltodextrin coating disintegrates due to the pH of the cement formulation. At pH between 9 and 14 and alternately between 10 and 14, the glycosidic bonds of the maltodextrin can cleave causing disintegration.

[0037] The maltodextrin-coated nanosilica can be prepared according to the following methods and embodiments. An amount of maltodextrin can be mixed with a nanosilica particle solution. The nanosilica particle solution contains nanosilica particles suspended in water. The nanosilica particle solution can be prepared by adding nanosilica particles dropwise to water or can be obtained commercially. The nanosilica particles can be suspended in water with a concentration of nanosilica particles in an amount between 0.05% by weight of water (bwow) and 40% bwow. The concentration of nanosilica particles in the nanosilica-containing water can depend on the volume of maltodextrin-coated nanosilica to be produced. The nanoparticle solution can be stirred to ensure a well-mixed nanosilica particle solution.

[0038] The maltodextrin can be mixed with the nanosilica particle solution at ambient conditions. Mixing can be achieved by any means that results in dissolving the maltodextrin to produce a maltodextrin-containing water that is well-mixed. In at least one embodiment, mixing can be achieved by stirring the maltodextrin into the nanosilica particle solution. The amount of maltodextrin that can be used is between 0.1 and 45 wt % in a nanosilica particle solution containing between 0.05% bwow and 40% bwow. The amount of maltodextrin and the rate of addition can be selected based on obtaining a maltodextrin-containing water where all of the maltodextrin is dissolved. The maltodextrin can be added in a solid form, such as a powder.

[0039] After the maltodextrin completely dissolves the borate can be added to the maltodextrin-containing water to produce a pre-reaction mixture. Examples of borates suitable for use include sodium tetraborate, potassium tetraborate, boric acid, and combination of the same. The volume of borate and the rate of addition can be selected based on the volume of maltodextrin-coated nanosilica to be produced. The pre-reaction mixture can be stirred for a period of time after addition of the borate. The maltodextrin is added before the borate to facilitate hydrogen boding between the maltodextrin and the nanosilica particles before the introduction of the borate crosslinker. If the borate was added before the maltodextrin than the borate would crosslink the nanosilica particles and the maltodextrin coating would not be formed. By introducing the maltodextrin before the borate, a thin layer of maltodextrin hydrogen bonded on the surface of the nanosilica particles, this thin layer is then crosslinked by the sodium tetraborate.

[0040] The pre-reaction mixture is then sonicated in an ultrasonic bath at a temperature of between 90° F. (32.2° C.) and 100° F. (37.8° C.) for at least one hour to produce the reaction mixture. Increasing the temperature increases the solubility of borate allowing the borate ester formation between the maltodextrin layer and nanosilica particles. Sonicating the pre-reaction mixture helps to disperse the nanosilica particles and reduces the probability of interparticle crosslinking. Additionally, the dilute conditions of the reaction can help to avoid interparticle crosslinking. Interparticle crosslinking needs to be avoided because it reduces the surface area of the nanosilica particles. Reduced surface area of the nanosilica particles translates into less effective additive in reducing the transition time of the cement.

[0041] Mixing of the reaction mixture continues after the ultrasonic bath at ambient temperature for a mixing time. The temperature can be reduced after the borate dissolves. The reaction continues during the mixing step and the mixing time is selected to ensure complete consumption of the borate and to maximize formation of the ester bonds between maltodextrin and nanosilica particles. In at least one embodiment, the mixing time is at least 12 hours.

[0042] The reaction mixture can then be separated to produce the maltodextrin-coated nanosilica. Any separation unit capable of separating a particle from a liquid can be used. Separation units can include filters, evaporation units, centrifuge units, and combinations of the same.

[0043] Maltodextrin-coated nanosilica can be used in well cementing operations and in construction industry cementing operations as gas migration additives. Well cementing operations includes any cementing operating occurring in a well in a subsurface formation. Wells can include oil wells, gas wells, and combinations of the same. The temperature of the nanosilica-containing cement formulation can be maintained due to the temperature of the formation surrounding the well.

[0044] In at least one embodiment, the maltodextrin-coated nanosilica can be mixed in cement formulations to produce nanosilica-containing cement formulations. The nanosilica-containing cement formulations include maltodextrin-coated nanosilica and cement formulations. The cement formulations can include water and a cement. The cement can be any Portland cement containing calcium silicates, aluminosilicates, or combinations of the same. The nanosilica-containing cement formulations can include nanosilica particles in an amount between 0.1% by weight of cement (bwoc) and 10% bwoc. Advantageously, the maltodextrin coating of the maltodextrin-coated nanosilica can reduce agglomerations of silica nanoparticles due in part to the hydrophilic nature of the maltodextrin coating. Advantageously, the maltodextrin coating of the maltodextrin-coated nanosilica can maintain the pumpability of the nanosilica-containing cement formulations at increased nanosilica loading.

[0045] The maltodextrin coating can act as a protective barrier isolating the nanosilica particles from calcium silicates in the cement and their reaction products with water. Isolating the nanosilica particles can delay reaction between the nanosilica particles and calcium silicates until desired, such that the cement properties can be optimized when the cement formulation is the desired location.

[0046] The temperature and pH of the maltodextrin-coated nanosilica can initiate the disintegration of the maltodextrin coating leaving the nanosilica particle dispersed in the cement formulation. The nanosilica particle dispersed in the cement formulation can improve the properties of the cement and set cement, including improving the mechanical properties, accelerating the cement set time, and serving as a gas migration additive. The dispersed nanosilica particle can accelerate the hydration reaction of the calcium silicate to produce calcium-silicate-hydrate, or set cement. The cement formulation with the nanosilica particles dispersed sets at an accelerated rate relative to cements without nanosilica particles. The nanosilica-containing cement formulation can have a reduced transition time compared to cements in the absence of nanosilica particles. The transition time is measured as the amount of time needed for a cement to have a static gel strength (SGS) between 100 lbf/100 sq ft (48 Pa) to 500 lbf/100 sq ft (240 Pa). The maltodextrin coating does not participate in the hydration reactions of the calcium silicate. In at least one embodiment, the nanosilica particle can undergo a pozzolanic reaction to yield a calcium silicate hydrate. In at least one embodiment, the nanosilica particle can act as a nucleation site during cement hydration. Cement properties that can be improved include reduced gas migration, improved initial gel strength of the cement, improved mechanical strength of the set cement, and accelerated cement setting.

[0047] The reactions between nanosilica particles and calcium in the cement can begin to occur within 1 minute of the disintegration of the maltodextrin coating, alternately within 5 minutes of the disintegration of the maltodextrin coating, and alternately within 1 hour of the disintegration of the maltodextrin coating. The reactions can continue until the reactants are depleted or the hardened cement reduces the ability for the reactants to interact.

[0048] The maltodextrin-coated nanosilica and the nanosilica-containing cement formulations are in the absence of dextran.

EXAMPLES

[0049] The following experiments were performed to tests various aspects of the gas migration additive and impact on cement slurry formulations.

Example 1. Nanosilica Synthesis and Characterization

[0050] Nanosilica particles (ST-XS, CASRN: 7732-18-5, 7631.86-9, 20 wt %) were obtained from Nissan Chemical America Corporation (Houston, Tex.). Maltodextrin (CAS: 9050-36-6) was acquired from Spectrum Chemical Manufacturing Corporation (New Brunswick, N.J.). Sodium tetraborate (CAS:1330-43-4) from Sigma Aldrich (St. Louis, Mo.) was purchased and used as received.

[0051] Samples of maltodextrin-coated nanosilica were prepared according to the following methodology. The amount of ST-XS was added drop by drop into water under stirring at 300 revolutions per minute (rpm) at ambient temperature. Stirring was allowed to continue for 15 minutes after complete addition. The amount of maltodextrin was then slowly added to the mixture as it was continuously stirred. Stirring was continued for 15 minutes until the maltodextrin completely dissolved in water to produce the maltodextrin-containing water. Then the amount of sodium tetraborate was slowly added to the mixture under stirring and stirring was continued for 15 minutes after all of the sodium tetraborate was added. The pre-reaction mixture was sonicated in an ultrasonic bath (Branson Ultrasonics Corporation (Brookfield, Conn.) 5800 Ultrasonic Cleaner, 2.5 gallon, 40 kHz) for 1 hour at a temperature between 90° F. and 100° F., followed by stirring for 12 hours at 300 rpm at ambient temperature. The reaction mixture was then filtered with an EZFlow® Syringe Filter from Foxx Life Sciences (Salem, N.H.) with a diameter of 25 mm and a pore size of 0.45 μm to recover the maltodextrin-coated nanosilica. The amounts of each component are shown in Table 3. The volume of water in each sample was 100 mL. The ST-XS 20 wt % solution contained approximately 7.8 grams of silica nanoparticles.

TABLE-US-00001 TABLE 3 Pre-reaction mixture composition Materials Sample 1 Sample 2 Water (g) 100 100 ST-XS (g) 39 39 Maltodextrin (g) 0.325 0.325 Sodium tetraborate (g) 0.050 0.025

[0052] Thermogravimetric analyses (TGA) of the maltodextrin-coated nanosilica were performed on a TA Instruments (New Castle, Del.) Thermogravimetric Analyzer (SDT Q600). Prior to running the TGA, water was removed from the samples through a drying step (under air) followed by drying in a vacuum oven at 100° F. for a week to ensure maximum removal of water. Thermogravimetric analysis was then performed with uncoated nanosilica (ST-XS) and the samples, Sample 1 and Sample 2. All samples tested were heated, at a constant rate of 20° C. per min using air as the furnace gas, from room temperature to 1000° C. to ensure complete removal of residual water in uncoated nanoparticles and removal of residual water and organic content in the maltodextrin-coated nanosilica samples. By using the uncoated nanosilica particle as a baseline, the Baseline Sample, for the presence of residual water, a percentage mass loss due to organic content removal was then determined for the maltodextrin-coated nanosilica, shown in Table 4. The theoretical weight loss was calculated as the weight of maltodextrin and sodium tetraborate divided by the weight of the nanosilica particles, maltodextrin, and sodium tetraborate as a percentage. The experimental weight loss was calculated as the difference between the weight loss of the maltodextrin-coated nanosilica and the weight loss of the uncoated nanosilica. The weight loss of the uncoated nanosilica is assumed to be from water and other organic material present with the nanosilica particles. Thus, subtracting the difference in the uncoated nanosilica from the maltodextrin-coated nanosilica determines the weight loss purely due to the maltodextrin-borate coating. The mass percentage of the maltodextrin coating was also estimated by determining the percentage ratio of experimental mass loss to theoretical mass loss.

TABLE-US-00002 TABLE 4 Analysis of mass loss for Sample 1 and Sample 2 of nanosilica particle Theoretical Experimental Percentage of weight loss (%) weight loss (%) maltodextrin coating (%) Sample 1 4.6 3.94 86 Sample 2 4.3 2.67 62

[0053] Dynamic light scattering (DLS) and zeta potential measurements were performed using a Litesizer™ 500 particle analyzer running Kalliope software from Anton Paar (Houston, Tex.) with a 40 mW semiconductor laser, λ=658 nm. The temperature was stabilized to ±0.1° C. of the set temperature 25° C. All samples were prepared in Milli-Q water at a concentration of about 77 mg/ mL nanosilica particles and filtered through a 0.45 μm pore size filter to remove dust prior to measurement. Hydrodynamic radii were calculated by the non-negative least squares (NNLS) algorithm and the zeta potential was determined by the Smoluchowski approximation using the manufacturer's software. Forced single exponential fitting scheme (cumulant method) was used to determine the overall mean size by intensity distribution. The results of the DLS measurements are shown in Table 5.

TABLE-US-00003 TABLE 5 Results of DLS and zetal potential measurements. Hydrodynamic Polydispersity Zeta potential diameter (nm) Index (mV) Baseline Sample 13.17 0.282 −25.5 ± 1.2 Sample 1 28.44 0.225 −26.9 ± 0.6 Sample 2 17.92 0.216 −18.4 ± 0.7

[0054] An increase in the hydrodynamic diameter in the maltodextrin-coated nanosilica samples was seen when compared to the uncoated nanosilica particles. The increase in hydrodynamic diameter indicated the presence of polymer tethered to the surface of nanosilica particles. A higher hydrodynamic diameter was seen in Sample 1 over Sample 2 due to the presence of larger tethered maltodextrin content in the former sample. In addition, the higher concentration of sodium tetraborate used in Sample 1 may help to increase chain branching which can contribute to the higher hydrodynamic diameter. Zeta potential values provide an indirect measurement of the net charge on the nanoparticle surface. The zeta potential value for Sample 1 shifted to a slightly more negative value when compared to the Baseline Sample due to the presence of sodium tetraborate on the surface of the particle. The value of the zeta potential for Sample 1 at −26.9 mV is in the standard range for stable colloidal suspensions of nanosilica particles. Sample 2 shifted to a slightly less negative value when compared to the Baseline Sample. The DLS intensity distribution plots are shown in FIGS. 4A-4C. FIG. 4A shows the DLS analysis (intensity distribution) for the Baseline Sample. FIG. 4B shows the DLS analysis (intensity distribution) for Sample 1. FIG. 4C shows the DLS analysis (intensity distribution) for Sample 2.

Example 2. Cement Slurry Formulation and Characterization

[0055] Cement slurry formulations were developed and tested at different temperatures for high pressure/high temperature (HPHT) thickening time and multiple analysis cement system II (MACSII) transition time using HPHT ultrasonic cement analyzers (UCAs) and HPHT consistometer testing. In the formulations, the cement was a Saudi class G cement and the gas migration additive (nanosilica additive) was a Sample from Example 1, as indicated. In order to compare the efficacy of the gas migration additives, the components were tuned to achieve a set HPHT pump time. The UCAs used were Chandler 4265 HT. All tests were carried out according to API Recommended Practice 10B. The pressure in all tests with the UCA was set to 20.7 MPa. The temperature ramps were set to ramp to the target temperatures in 0.5 hour. There were four different target temperatures set in the UCA experiments 120° F., 180° F., 250° F., and 228° F. The HPHT consistometers were Chandler Model 8340.

[0056] A. Slurry Formulation Designs for 120° F.

[0057] The slurry formulations for the 120° F. tests were developed according to the compositions shown in Table 6. A retarder system of zinc oxide and AMPS/acrylic acid copolymer was used. The slurry formulations were adjusted to display thickening times to 100 Bearden units of consistency (Bc) of approximately 6 hours. For each test, a 30 minute ramp time to 120° F. was used to determine the transition time.

TABLE-US-00004 TABLE 6 Slurry formulation designs for 120° F. Baseline Uncoated Sample 1 Formulation Formulation Formulation Amount (g) % BWOC Amount (g) % BWOC Amount (g) % BWOC Saudi class G cement 785 100 785 100 785 100 Water 347 N/A 347 N/A 347 N/A Hydroxyethylcellulose 1.00 0.13 1.00 0.13 1.00 0.13 AMPS Acrylic Acid 1.85 0.236 1.85 0.236 1.94 0.247 copolymer Zinc Oxide 0.59 0.075 0.59 0.075 0.61 0.078 Nanosilica Additive 0 0 3.93 0.05 gps 3.93 0.05 gps

[0058] For the tests at 120° F., the slurry formulations were adjusted to display thickening times to 100 Bearden units of consistency (Bc) of approximately 6 hours. For each test, a 30 minute ramp time to 120° F. was used. Three hours of conditioning at 120° F. was used to determine the transition time. Thickening times and transition times for each sample are shown in Table 7.

TABLE-US-00005 TABLE 7 Thickening times and transition times Baseline Uncoated Sample 1 Formulation Formulation Formulation Thickening time to  6 hours and  5 hours and  5 hour and 70 Bc 15 minutes 54 minutes 49 minutes Thickening time to  6 hours and  6 hours and  6 hours and 100 Bc 23 minutes  2 minutes  2 minutes Transition times 42 minutes 60 minutes 64 minutes

[0059] The results in Table 7 suggest no advantage to the use of maltodextrin-coated nanosilica in a cement formulation in terms of thickening time or transition time. Furthermore, the maltodextrin-coated nanosilica in Sample 1 Formulation does not improve the transition time relative to the use of uncoated nanosilica in the Uncoated Formulation. At a temperature of 120° F., the results suggest that the maltodextrin remains intact, in other words the maltodextrin coating does not thermally degrade, and there may have been some free maltodextrin which acted as a mild cement retarder, hence the longer transition time with the coated nanosilica.

[0060] B. Slurry Formulation Designs for 180° F.

[0061] The slurry formulations for the 180° F. tests were developed according to the compositions shown in Table 8. The slurry formulations were adjusted to display thickening times to 100 Bearden units of consistency (Bc) of approximately 6 hours. For each test, a 30 minute ramp time to 180° F. was used. Three hours of conditioning at 180° F. was used to determine the transition time. A retarder system of zinc oxide and AMPS/acrylic acid copolymer was used. The slurry formulations were mixed at room temperature (about 21° C.) in a Fann 686CS cement stand mixer using deionized water for the mixing times outlined in API RP 10B.

TABLE-US-00006 TABLE 8 Slurry designs for 180° F. Baseline Uncoated Sample 1 Sample 2 Formulation Formulation Formulation Formulation Amount (g) % BWOC Amount (g) % BWOC Amount (g) % BWOC Amount (g) % BWOC Saudi class G cement 785 100 785 100 785 100 785 100 Water 347 N/A 347 N/A 347 N/A 347 N/A Hydroxyethylcellulose 1.00 0.13 1.00 0.13 1.00 0.13 1.00 0.13 AMPS Acrylic Acid 1.85 0.236 1.94 0.247 1.94 0.247 1.18 0.150 copolymer Zinc Oxide 0.59 0.075 0.61 0.078 0.61 0.078 0.38 0.049 Nanosilica Additive 0 0 3.93 0.05 gps 3.93 0.05 gps 3.94 0.05 gps

[0062] For the tests at 180° F., the slurry formulations were adjusted to display thickening times to 100 Bc of approximately 4 hours. For each test, a 30 minute ramp time to 180° F. was used. Two hours of conditioning at 180° F. was used to determine the transition time. Thickening times and transition times for each sample are shown in Table 9.

TABLE-US-00007 TABLE 9 Thickening times and transition times Baseline Uncoated Sample 1 Sample 2 Formulation Formulation Formulation Formulation Thickening time  4 hours  3 hours and  4 hours and  4 hours and to 70 Bc 57 minutes  7 minutes  2 minutes Thickening time  4 hours  4 hours and  4 hours and  4 hours and to 100 Bc  1 minute 11 minutes 10 minutes Transition times 39 minutes 41 minutes 29 minutes 10 minutes

[0063] The results in Table 9 show different activity of the nanosilica particles at 180° F. than from the results in Table 7. The results show that cement slurries, the slurry formulations containing the gas migration additives, have substantially shorter transition times compared to the slurry formulations with no nanosilica or uncoated nanosilicas. Thus, the results suggest that at temperatures of 180° F. the maltodextrin coating degrades and leads to the release of the nanosilica particle (C) from the maltodextrin coating (B) as shown in the schematic of FIG. 5, where (A) represents the maltodextrin-coated nanosilica.

[0064] A comparison of the static gel strength development between the Baseline Formulation, the Sample 1 Formulation and the Sample 2 Formulation is shown in FIG. 6. FIG. 6 shows a comparison of the gel strength development at 180° F. of the slurry formulations from 0 to 500 lbf/100 sq ft.

[0065] C. Slurry Formulation Designs for 250° F.

[0066] The slurry formulations for the 250° F. tests were developed according to the compositions shown in Table 10. The slurry formulations were adjusted to display thickening times to 100 Bearden units of consistency (Bc) of approximately 6 hours. For each test, a 30 minute ramp time to 250° F. was used. Three hours of conditioning at 250° F. was used to determine the transition time. A retarder system of zinc oxide and AMPS/acrylic acid copolymer was used.

TABLE-US-00008 TABLE 10 Slurry designs for 250° F. Baseline Uncoated Sample 1 Sample 2 Formulation Formulation Formulation Formulation Amount (g) % BWOC Amount (g) % BWOC Amount (g) % BWOC Amount (g) % BWOC Saudi class G cement 785 100 785 100 785 100 785 100 Water 347 N/A 347 N/A 347 N/A 347 N/A Hydroxyethylcellulose 1.00 0.13 1.00 0.13 1.00 0.13 1.00 0.13 AMPS Acrylic Acid 6.50 0.835 6.83 0.879 7.51 0.968 7.51 0.968 copolymer Zinc Oxide 5.50 0.707 5.70 0.734 6.27 0.808 6.27 0.808 Nanosilica Additive 0 0 3.93 0.05 gps 3.93 0.05 gps 3.93 0.05 gps

[0067] For the tests at 250° F., the slurry formulations were adjusted to display thickening times to 100 Bc of approximately 4 hours. For each test, a 30 minute ramp time to 250° F. was used. Thickening times and transition times for each sample are shown in Table 11.

TABLE-US-00009 TABLE 11 Thickening times and transition times Baseline Uncoated Sample 1 Sample 2 Formulation Formulation Formulation Formulation Thickening time  3 hours and  4 hours and  3 hours and  3 hours and to 70 Bc 57 minutes 11 minutes 47 minutes 56 minutes Thickening time  4 hours and  4 hours and  3 hours and  4 hours and to 100 Bc  3 minute 15 minutes 51 minutes  1 minute Transition times 10 minutes —*  9 minutes 10 minutes *Transition time not available

[0068] The results in Table 11 show rapid transition times for each sample. This could be a result of the chemistry of the retarder system. Alternately, the difference in transition time could be due to instrument error.

[0069] The Sample 2 Formulation shows a substantially higher compressive strength at 12 and 24 hours as compared with the other slurry formulations. The Sample 2 Formulation showed compressive strengths of 1470 and 3737 psi for 12 and 24 hours. This was the highest early strength of the four slurries. The Sample 2 slurry also showed the highest 96 hour compressive strength at 4820 psi as compared with 4174 psi for the Baseline Formulation, 4204 psi for the Uncoated Formulation, and 3791 psi for the Sample 1 Formulation. The results show that the nanosilica-containing cement formulations, the slurry formulations containing the gas migration additives, have substantially shorter transition times compared to the slurry formulations with no nanosilica or uncoated nanosilicas. Thus, the results suggest that at temperatures of 180° F. the maltodextrin coating degrades and leads to the release of the nanosilica particle (C) from the maltodextrin coating (B) as shown in the schematic of FIG. 5, where (A) represents the maltodextrin-coated nanosilica.

[0070] D. Slurry Formulation Designs for 228° F.

[0071] The slurry formulations for the 228° F. tests were developed according to the compositions shown in Table 12. The slurry formulations were adjusted to display thickening times to 100 Bc of approximately 4 hours. For each test, a 30 minute ramp time to 228° F. was used. Two hours of conditioning at 228° F. was used to determine the transition time. The retarder system was HR-12 and HR-25.

TABLE-US-00010 TABLE 12 Slurry designs for 228° F. Baseline Sample 2 Formulation Formulation Amount (g) % BWOC Amount (g) % BWOC Saudi class G 635.54 100 635.3 100 cement Water 193.37 N/A 191.81 N/A Silica flour 222.44 35 222.35 35 Microbond-HT 31.78 5 31.76 5 CFR-3 1.91 0.3 1.91 0.3 Halad-344 0.64 0.1 0.64 0.1 HR-12 6.48 1.02 5.83 0.092 HR-25 0.54 0.085 0.49 0.077 Latex 89.66   1.5 gps 89.62  1.5 gps Stabilizer-434 17.93  0.3 gps 17.92  0.3 gps Dair-3000 0.62 0.012 gps 0.62 0.012 gps Nanosilica 0 0 3.18  0.05 gps Additive

[0072] For the tests at 228° F., the slurry formulations were adjusted to display thickening times to 100 Bc of approximately 5 hours. For each test, a 30 minute ramp time to 250° F. was used. Thickening times and transition times for each sample are shown in Table 11.

TABLE-US-00011 TABLE 13 Thickening times and transition times Baseline Sample 2 Formulation Formulation Thickening time to 70 Bc  4 hours and  4 hours and 41 minutes 13 minutes Thickening time to 100 Bc  4 hours and  4 hours and 53 minutes 21 minutes Transition times  5 hours and  4 hours and 46 minutes 58 minutes

[0073] The results in Table 13 suggest degradation of the maltodextrin coating similar to the results seen in Table 9.

[0074] Comparing the results observed in Tables 9 and 11 to the results recorded in Table 13, shows the impact that different retarder systems can have on the transition time. The introduction of the maltodextrin-coated nanosilica in the Sample 2 Formulation in Table 12 reduces the transition time compared to the formulation without nanosilica particles. However, the impact is minimal compared to the results of the formulations shown in Tables 9 and 11. This suggests that the retarder system can impact the effectiveness of the gas migration additive.

[0075] The maltodextrin-coated nanosilica reduces the transition times observed from 180° F. to 228° F. in cement slurries. The impact is minimal at temperatures of 250° F., where all slurry formulations showed transition times of 10 minutes or less.

[0076] Although the embodiments have been described in detail, it should be understood that various changes, substitutions, and alterations can be made hereupon without departing from the principle and scope. Accordingly, the scope of the embodiments should be determined by the following claims and their appropriate legal equivalents.

[0077] There various elements described can be used in combination with all other elements described here unless otherwise indicated.

[0078] The singular forms “a”, “an” and “the” include plural referents, unless the context clearly dictates otherwise.

[0079] Optional or optionally means that the subsequently described event or circumstances may or may not occur. The description includes instances where the event or circumstance occurs and instances where it does not occur.

[0080] Ranges may be expressed here as from about one particular value to about another particular value and are inclusive unless otherwise indicated. When such a range is expressed, it is to be understood that another embodiment is from the one particular value to the other particular value, along with all combinations within said range.

[0081] As used here and in the appended claims, the words “comprise,” “has,” and “include” and all grammatical variations thereof are each intended to have an open, non-limiting meaning that does not exclude additional elements or steps.