METHOD FOR MANUFACTURING FDSOI

Abstract

The present application provides a method for manufacturing FDSOI devices. The method includes steps of: providing a semiconductor structure which comprises a silicon substrate, a buried oxide layer on the silicon substrate, a silicon-on-insulator layer on the buried oxide layer; and a hard mask layer on the silicon-on-insulator layer; performing spin coating of a photoresist on the hard mask layer to form a bulk silicon region; performing plasma anisotropic etching on the bulk silicon region to open a part of the buried oxide layer, and then performing isotropic etching, so that the silicon-on-insulator layer shrinks in the horizontal direction; performing plasma anisotropic etching to etch through the buried oxide layer to form a bulk silicon region trench; performing silicon epitaxial growth in the bulk silicon region trench. The silicon-on-insulator layer is still shrinks after the bulk silicon region trench is formed, as the result, there is no bump on the surface of the silicon-on-insulator layer, thus the process window becomes controllable.

Claims

1. A method for manufacturing FDSOI, at least comprising following steps: step 1. providing a semiconductor structure, wherein the semiconductor structure comprises: a silicon substrate; a buried oxide layer on the silicon substrate; a silicon-on-insulator layer on the buried oxide layer; and a hard mask layer on the silicon-on-insulator layer; step 2. performing spin coating with a photoresist layer on the hard mask layer, and performing lithographic exposure and development to form a bulk silicon region; step 3. performing plasma anisotropic etching on the bulk silicon region to open a part of the buried oxide layer, and then performing isotropic etching, wherein the silicon-on-insulator layer shrinks along a direction parallel to a top surface of the silicon substrate; step 4. performing anisotropic plasma etching through the buried oxide layer to form a bulk silicon region trench; step 5. removing residue from the photoresist layer after the plasma etching; and step 6. performing silicon epitaxial growth in the bulk silicon region trench.

2. The method for manufacturing FDSOI according to claim 1, wherein the hard mask layer in step 1 is a silicon nitride layer or a composite layer including a silicon oxide layer and a silicon nitride layer, wherein the silicon nitride layer is disposed on the silicon oxide layer.

3. The method for manufacturing FDSOI according to claim 2, wherein a thickness of the hard mask layer in step 1 is in a range of 100 Å-500 Å.

4. The method for manufacturing FDSOI according to claim 1, wherein a thickness of the silicon-on-insulator layer in step 1 is in a range of 100 Å-200 Å.

5. The method for manufacturing FDSOI according to claim 1, wherein the buried oxide layer in step 1 is a silicon dioxide layer, having a thickness in a range of 100 Å-300 Å.

6. The method for manufacturing FDSOI according to claim 1, wherein the photoresist layer in step 2 comprises an anti-reflection layer.

7. The method for manufacturing FDSOI according to claim 1, wherein the silicon-on-insulator layer in step 3 shrinks from 50 Å to 100 Å in a direction parallel to the top surface of the silicon substrate.

8. The method for manufacturing FDSOI according to claim 1, wherein a bottom surface of the bulk silicon region trench is lower than a bottom surface of the buried oxide layer by a range of 20 Å-100 Å in step 4.

9. The method for manufacturing FDSOI according to claim 1, wherein the method for removing the residue of the photoresist layer after the plasma etching in step 5 comprises a wet removal method or a combination of wet removal and dry removal.

10. The method for manufacturing FDSOI according to claim 1, wherein a surface of the epitaxial silicon layer is flush with an upper surface of the silicon-on-insulator layer after the silicon epitaxial growth is performed in step 6.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0023] FIG. 1 is a schematic diagram of the semiconductor structure after etching to open a part of a buried oxide layer, according to the present application.

[0024] FIG. 2 is a schematic diagram of the shrank structure of silicon-on-insulator layer after isotropic etching according to the present application.

[0025] FIG. 3 is a schematic diagram of the structure after forming a bulk silicon region trench by means of etching according to the present application.

[0026] FIG. 4 is a schematic diagram of the structure after the silicon epitaxial layer is formed in the bulk silicon region according to the present application.

[0027] FIG. 5 is a schematic diagram showing the epi-silicon surface being flush with the upper surface of the silicon-on-insulator layer after the silicon epitaxial growth according to the present application.

[0028] FIG. 6 is a flowchart of the method for manufacturing FDSOI according to the present application.

DETAILED DESCRIPTION OF THE DISCLOSURE

[0029] The implementation of the present application is described below with specific examples, and those skilled in the art can easily understand other advantages and effects of the present application from the content disclosed in the description. The present application can also be implemented or applied in other different specific embodiments, and various details in the description can also be modified or changed on the basis of different viewpoints and applications without departing from the spirit of the present application.

[0030] Please refer to FIG. 1 to FIG. 6. It should be noted that the drawings provided in the embodiments only schematically illustrate the basic concept of the present application. The drawings only show the components related to the present application but are not drawn according to the number, shape, and size of the components in actual implementation. The type, quantity, and proportion of each component can be changed at random during actual implementation, and the component layout type may be more complicated.

[0031] The present application provides a method for manufacturing a FDSOI device. FIG. 6 is a flowchart of the method for manufacturing FDSOI according to the present application. The method at least includes the following steps:

[0032] Step 1. Providing a semiconductor structure, wherein the semiconductor structure includes: a silicon substrate; a buried oxide layer on the silicon substrate; a silicon-on-insulator layer on the buried oxide layer; and a hard mask layer on the silicon-on-insulator layer.

[0033] Specifically, the hard mask layer in step 1 of this embodiment of the present application is a silicon nitride layer or a composite layer composed of a silicon oxide layer and a silicon nitride layer, and the silicon nitride layer is located on the silicon oxide layer in the composite layer. In this embodiment, the hard mask layer is a silicon nitride layer; in other embodiments, the hard mask layer may be a composite layer including a silicon nitride layer, and the silicon nitride layer is located on the silicon oxide layer in the composite layer.

[0034] Specifically, the thickness of the hard mask layer in step 1 of this embodiment of the present application is in the range of 100-500 Å. That is, the thickness of the silicon nitride layer in this embodiment is 100-500 Å. In other embodiments, the thickness of the composite layer is 100-500 Å.

[0035] Specifically, the thickness of the silicon-on-insulator layer in step 1 of this embodiment of the present application is 100-200 Å.

[0036] Specifically, the buried oxide layer in step 1 of this embodiment of the present application is a silicon dioxide layer, and the thickness thereof is in a range of 100-300 Å.

[0037] Step 2. Spin coating with a photoresist is performed on the hard mask layer, and exposure and development are performed to form a bulk silicon region. Specifically, the photoresist in step 2 of this embodiment of the present application includes an anti-reflection layer.

[0038] Step 3. Plasma anisotropic etching is performed on the bulk silicon region to open a part of the buried oxide layer, and then isotropic etching is performed, so that the silicon-on-insulator layer shrinks in the horizontal direction. Referring to FIG. 1, FIG. 1 is a schematic diagram of the semiconductor structure after etching to open a part of a buried oxide layer, according to the present application. The semiconductor structure includes: the silicon substrate 01; the buried oxide layer 02 on the silicon substrate 01; the silicon-on-insulator layer 03 on the buried oxide layer 02; and the hard mask layer 04 on the silicon-on-insulator layer 03. In step 3, the plasma anisotropic etching is performed on the bulk silicon region to open the buried oxide layer 02 and remain a part of the buried oxide layer, to form a groove. Then, the isotropic etching is performed to form a structure as shown in FIG. 2. FIG. 2 is a structural schematic diagram of the silicon-on-insulator layer shrinking after the isotropic etching according to the present application. The silicon-on-insulator layer 03 shrinks in the horizontal direction after the isotropic etching.

[0039] Specifically, the silicon-on-insulator layer in step 3 of this embodiment of the present application shrinks by 50-100 Å in the horizontal direction.

[0040] Step 4. Plasma anisotropic etching is performed to etch through the buried oxide layer to form a bulk silicon region trench. Referring to FIG. 3, FIG. 3 is a schematic diagram of the structure after forming the bulk silicon region trench by means of etching according to the present application. In step 4, the plasma anisotropic etching is performed to form the bulk silicon region trench A.

[0041] Specifically, the surface of the bulk silicon region trench is lower than the bottom surface of the buried oxide layer by 20-100 Å in step 4 of this embodiment of the present application.

[0042] Step 5. The photoresist and an etching residue are removed. Specifically, the method for removing the photoresist and the etching residue in step 5 of this embodiment of the present application includes a wet removal method or a combination of wet removal and dry removal. In this embodiment, the method for removing the photoresist and the etching residue is a wet removal method; in other embodiments, the photoresist and the etching residue may be removed by using a combined method of wet removal and dry removal.

[0043] Step 6. Silicon epitaxial growth is performed in the bulk silicon region trench. Referring to FIG. 4, FIG. 4 is a structural schematic diagram of performing the silicon epitaxial growth in the bulk silicon region trench to form the silicon epitaxial layer according to the present application. The formed silicon epitaxial layer and the substrate 01 form an integral body in FIG. 4. The silicon top surface is lower than the silicon-on-insulator layer after the silicon epitaxial growth in FIG. 4.

[0044] Specifically, the epi-silicon surface is flush with the upper surface of the silicon-on-insulator layer after the silicon epitaxial growth is performed in step 6 of this embodiment of the present application.

[0045] To sum up, the present application can realize a silicon epitaxial layer with no bump and controlled hard mask missing in an FDSOI process, thereby reducing process defects, expanding the FDSOI process window, and improving the device performance and product yield. Therefore, the present application effectively overcomes various defects in the prior art and thus has a high industrial value.

[0046] The above embodiments only exemplarily illustrate the principle and effects of the present application, bus are not intended to limit the present application. Any perform familiar with this technology can modify or change the above embodiments without departing from the spirit and scope of the present application. Therefore, any equivalent modification or change made by those with ordinary knowledge in the technical field without departing from the spirit and technical concept disclosed by the present application shall still be covered by the claims of the present application.