Strand-shaped elements and polymer composition for preparing same

Abstract

The invention relates to strand-shaped elements and polymer compositions used for preparing the strand-shaped elements. The strand-shaped elements comprise an inner structure and a halogen-free polymer composition surrounding the inner structure. The polymer composition includes a linear very low density polyethylene (VLDPE) composition and one or more polyolefin-elastomers. In addition, the polymer composition includes a flame retardant filler.

Claims

1. Strand-shaped element comprising: (i) an inner structure; and (ii) a polymer composition surrounding the inner structure, wherein the polymer composition is obtainable or obtained by compounding at least the following components: (a) 24-32 wt.-% of a mixture of linear very low density polyethylene (VLDPE) compositions, wherein said mixture comprises 20-26 wt.-% of a first composition having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, as measured according to ISO 1183, and 1-7 wt.-% of a second composition having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, as measured according to ISO 1183; (b) 10-17 wt.-% of a polyolefin-elastomer, which is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C., as determined in the polymer composition or in pure form and a melting point of below 40° C., and wherein the polyolefin-elastomer has a density in the range from 0.80 g/cm.sup.3 to 0.90 g/cm.sup.3, as measured according to ASTM D792, and wherein the polyolefin-elastomer has an elongation at break of at least 1000%, as measured by ASTM D638; (c) a flame retardant filler in an amount of 55-65 wt-%, which is aluminum hydroxide; (d) 0.1-3.0 wt.-% of an antioxidant; and (e) 0.5-2.5 wt.-% of a coupling agent composition; and wherein the polymer composition has an elongation at break in the range from 150% to 500%, as measured by IEC 60811-501, and wherein the strand-shaped element is obtainable or obtained by applying the polymer composition of (ii) by extrusion to the inner structure.

2. The strand-shaped element according to claim 1, wherein the linear very low density polyethylene (VLDPE) composition is contained in an amount of 26-30 wt.-% and has a density in the range from 0.86 g/cm.sup.3 to 0.93 g/cm.sup.3, as measured according to ISO 1183, and having a melting point of above 110° C.

3. The strand-shaped element according to claim 1, wherein the polyolefin-elastomer consists of one or more polyolefin-elastomers which are contained in an amount of 11-14 wt.-%.

4. The strand-shaped element according to claim 1, wherein the linear very low density polyethylene composition has a density in the range from 0.85 g/cm.sup.3 to 0.92 g/cm.sup.3, as measured according to ISO1183.

5. The strand-shaped element according to claim 1, having an outer diameter of 7.5-9.0 mm.

6. The strand-shaped element according to claim 1, having an MFI of at least 9 g/10 min, as measured according to EN ISO 1133.

7. The strand-shaped element according to claim 1, wherein the linear very low density polyethylene (VLDPE) composition having a melting point above 110° C.

8. The strand-shaped element according to claim 1, which passes the alternate bending test (EN 50396).

9. Polymer composition obtainable or obtained by compounding and extrusion of at least the components (a)-(e) as defined in claim 1.

10. The strand-shaped element according to claim 1, having an outer diameter of about 8.2 mm.

11. The strand-shaped element according to claim 1, having an outer diameter of about 8.2 mm, and which passes the alternate bending test according to EN 50396 with 30,000-50,000 cycles.

12. The strand-shaped element according to claim 7, wherein the linear very low density polyethylene (VLDPE) composition has a melting point which is below 120° C.

13. The strand-shaped element according to claim 1, wherein the polyolefin-elastomer is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C., as determined in the polymer composition or in pure form, and a melting point of below 40° C.

14. Strand-shaped element comprising: (i) an inner structure; and (ii) a polymer composition surrounding the inner structure, wherein the polymer composition is obtainable or obtained by compounding at least the following components: (a) 24-32 wt.-% of a mixture of two different types of linear very low density polyethylene (VLDPE) compositions, wherein said mixture comprises 20-26 wt.-% of a first composition having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, as measured according to ISO 1183, and 1-7 wt.-% of a second composition having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, as measured according to ISO 1183; (b) 10-17 wt.-% of a polyolefin-elastomer, which is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C., as determined in the polymer composition or in pure form and a melting point of below 40° C., and wherein the polyolefin-elastomer has a density in the range from 0.80 g/cm.sup.3 to 0.90 g/cm.sup.3, as measured according to ASTM D792, and wherein the polyolefin-elastomer has an elongation at break of at least 1000%, as measured by ASTM D638; (c) a flame retardant filler in an amount of 55-65 wt.-%, which is aluminum hydroxide; (d) 0.1-3.0 wt.-% of an antioxidant; and (e) 0.5-2.5 wt.-% of a coupling agent composition; and wherein the polymer composition has a strength at break in the range from 7.5 MPa to 15.0 MPa, as measured by IEC 60811-501, and wherein the strand-shaped element is obtainable or obtained by applying the polymer composition of (ii) by extrusion to the inner structure.

Description

DETAILED DESCRIPTION

(1) The invention relates to the following items:

(2) 1. Strand-shaped element comprising:

(3) (i) an inner structure; and

(4) (ii) a polymer composition surrounding the inner structure, wherein the polymer composition is obtainable or obtained by compounding at least the following components:

(5) (a) 24-32 wt.-% of a mixture of two different types of linear very low density polyethylene (VLDPE) compositions, each having a density in the range from 0.85 g/cm.sup.3 to 0.93 g/cm.sup.3, as measured according to ISO 1183;

(6) (b) 10-17 wt.-% of a polyolefin-elastomer, which is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C. as determined in the polymer composition or in pure form provided, for example, from the DSC measurement; and/or melting point of below 40° C. also provided, for example from the DSC measurement;

(7) (c) a flame retardant filler, which is a mineral hydroxide/hydrated metal-based filler;

(8) (d) 0.1-3.0 wt.-% of an antioxidant; and

(9) (e) 0.5-2.5 wt.-% of a coupling agent composition; and wherein

(10) the polymer composition has

(11) (aa) an elongation at break in the range from 150% to 500%, preferably 350% to 500%, or 350% to 450%, as measured by IEC 60811-501, preferably measured by using the strand-shaped element without the inner structure and/or

(12) (bb) a strength at break in the range from 7.5 MPa to 15.0 MPa, or 7.5 MPa to 10.0 MPa, or 7.5 MPa to 9.0 MPa, as measured by IEC 60811-501, preferably measured by using the strand-shaped element without the inner structure and

(13) wherein the strand-shaped element is obtainable or obtained by applying the polymer composition of (ii) by extrusion to the inner structure.

(14) The strength at break is measured in accordance with IEC 60811-501 and as required by DIN EN 50363-8, preferably before ageing. During ageing, the samples are placed into an oven for 7 days at 80° C., then put into a desiccator and then tested. The deviation in elongation and tensile strength is preferably not bigger than ±20%. Unless otherwise stated, all values referred to herein are measured without ageing.

(15) The strand-shaped element, wherein the two different types of linear very low density polyethylene (VLDPE) compositions of the mixture each have a density in the range from 0.85 g/cm.sup.3 to 0.92 g/cm.sup.3.

(16) 2. The strand-shaped element according to item 1, wherein the linear very low density polyethylene (VLDPE) composition is contained in an amount of 26-30 wt.-% and has a density in the range from 0.86 g/cm.sup.3 to 0.93 g/cm.sup.3, as measured according to ISO 1183, and having a melting point of above 110° C., e.g., related to the differential scanning calorimetry (DSC) measurement.

(17) 3. The strand-shaped element according to item 1 or 2, wherein the polyolefin-elastomer consists of one or more polyolefin-elastomers which are contained in an amount of 11-14 wt.-%.

(18) 4. The strand-shaped element according to item 3, wherein the polyolefin-elastomer(s) is/are (an) ultra-low density random ethylene-octene copolymer(s) having a glass transition temperature of below −50° C. as determined in the polymer composition or in pure form, wherein the melting point is, e.g., determined by DSC measurement, and/or having a melting point of below 40° C. as determined in the polymer composition or in pure form, wherein the melting point is, e.g., determined by DSC measurement, wherein, by way of example, Engage® 8842 of Dow has a very low melting point of 38° C.

(19) 5. The strand-shaped element according to any preceding item, wherein the flame retardant filler is present in an amount of 55-65 wt.-%, preferably 55-58%.

(20) 6. The strand-shaped element according to any preceding item, wherein the linear very low density polyethylene composition comprises a mixture of two different types of linear very low density polyethylene compositions, preferably a mixture of 20-26 wt.-% of a first composition, preferably having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, preferably of about 0.9 g/cm.sup.3, as measured according to ISO 1183, and 1-7 wt.-% of a second composition, preferably having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, preferably of about 0.9 g/cm.sup.3, as measured according to ISO 1183. Preferably, the VLDPE, which is present in a higher amount, has a higher melt flow rate compared with the other VLDPE. Preferably, the VLDPE being present in an amount of 1-7 wt.-% has a melt flow index of 2-5 as determined according to ASTM1238 (190° C./2.16 kg; g/10 min), while the VLDPE being present in an amount of 20-26 wt.-% has a melt flow index of 8-15 as determined according to ASTM1238 (190° C./2.16 kg; g/10′).

(21) 7. The strand-shaped element according to any preceding item, wherein the linear very low density polyethylene composition has a density in the range from 0.85 g/cm.sup.3 to 0.92 g/cm.sup.3, preferably in the range from 0.85 g/cm.sup.3 to 0.90 g/cm.sup.3, as measured according to ISO1183.

(22) 8. The strand-shaped element according to any preceding item, wherein the polyolefin-elastomer has a density in the range from 0.80 g/cm.sup.3 to 0.90 g/cm.sup.3, preferably of about 0.859 g/cm.sup.3, as measured according to ASTM D792.

(23) 9. The strand-shaped element according to any preceding item, wherein the polyolefin-elastomer (composition) has an elongation at break, preferably measured by using the strand-shaped element without the inner structure, of at least 1000%, further preferred at least 1100%, most preferably about 1200%, as measured by ASTMD638.

(24) 10. The strand-shaped element according to any preceding item, wherein the polyolefin-elastomer has a value of ShoreD hardness of less than 20, as measured by ASTM D2240 (compression molded sample, wherein a sample of the polyolefin-elastomer is molded into a plate). The ShoreD hardness of the strand-shaped element/polymer composition preferably is 32-38.

(25) 11. The strand-shaped element according to any preceding item, wherein the polymer composition can be applied by hot-melt extrusion at a temperature in the range from 100° C. to 175° C., preferably 100-170° C.

(26) 12. The strand-shaped element according to any preceding item, wherein the flame retardant filler is fine precipitated hydrated metal-based filler, e.g., aluminum hydroxide, preferably having about 99.4% purity. One example of such filler is Martinal® OL-104 LEO.

(27) 13. The strand-shaped element according to any preceding item, wherein the coupling agent composition is a mixture of vinyltriethoxysilane and 1,1-di(tert-butylperoxy)-3,3,5-trimethylcyclohexane.

(28) 14. The strand-shaped element according to any preceding item, wherein the antioxidant is a phenolic antioxidant, preferably tetrakis[methylene-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]methane.

(29) 15. The strand-shaped element according to any preceding item, wherein the inner structure comprises from 1 to 8 elements, each having diameters of up to 4.0 mm, such as diameters from 0.5 to 4.0 mm, and preferably having from 2 to 5 elements. The elements can each include a static/moving current media or communication media, which can be a metal wire, wherein the wire can be one piece of metal, preferably the wire is further stranded. The wire can be surrounded by a polymer layer to form the element.

(30) 16. The strand-shaped element according to any preceding item, wherein the polymer composition does not contain a plasticizer.

(31) 17. The strand-shaped element according to any preceding item, wherein the polymer composition does not contain a high density polyethylene homopolymer having a density of 0.94 g/cm.sup.3 or higher, preferably not containing a high density polyethylene homopolymer having a density of 0.92 g/cm.sup.3 or higher.

(32) 18. The strand-shaped element according to any preceding item, wherein the polymer composition does not contain a polysiloxane.

(33) 19. The strand-shaped element according to any preceding item, wherein the polymer composition surrounds the inner structure to provide a sheath for mechanical protection of the elements.

(34) 20. The strand-shaped element according to any preceding item, wherein, the glass transition temperature of the polyolefin-elastomer/ultra-low density random ethylene-octene copolymer is −58° C.

(35) 21. The strand-shaped element according to any preceding item, wherein the polymer composition is not UV crosslinked.

(36) 22. The strand-shaped element according to any preceding item, having an MFI of at least 9 g/10 min, as measured according to EN ISO 1133 under the conditions at 150° C. and the load of 21.6 kg.

(37) 23. The strand-shaped element according to any preceding item, wherein the density of the polyolefin-elastomer/ultra-low density random ethylene-octene copolymer is in the range from 0.80 g/cm.sup.3 to 0.90 g/cm.sup.3, as measured according to ISO 1183.

(38) 24. The strand-shaped element according to any preceding item, wherein the polymer composition has a value of ShoreD hardness of 32-38.

(39) 25. The strand-shaped element according to any preceding item, wherein the linear very low density polyethylene (VLDPE) composition having a melting point above 110° C., preferably has a melting point which is below 120° C. measured and/or determined by the method of DSC measurement.

(40) 26. The strand-shaped element according to any preceding item, wherein the linear very low density polyethylene (VLDPE) composition has a Vicat temperature (Vicat softening temperature) of above 50° C. temperature, for example, measured according to the ASTM D1525 method.

(41) 27. The strand-shaped element according to any preceding item, which passes the alternate bending test (EN 50396).

(42) 28. Polymer composition obtainable or obtained by compounding at least the components (a)-(e).

(43) In the context of the present invention, the “strand-shaped element” can be an elongated device for conjunction and/or connection of two devices for transferring electrical charges and/or information such as for power transmission or telecommunications. For example, the “strand-shaped element” can be a cable. In such a “strand-shaped element”, the inner structure can consist of one ore more elements (which are surrounded by the polymer composition). Each element can include an electric conductor as a static/moving current medium or communication medium. The electric conductor is optionally itself surrounded by a shielding or sheathing, in particular a polymer composition/coating, thereby forming the element. The electrical conductor can be a wire, preferably comprising or consisting of one or more, e.g., 52, metal strands (e.g., copper strands), wherein the wire is optionally itself surrounded by a shielding or sheathing, thereby forming the element. The cable can, e.g., be used as low voltage cable such as for use in vacuum cleaner applications.

(44) In the context of the present invention, the weight percentages indicated for the components of the polymer composition are indicated as weight percentages based on the total weight of the polymer composition.

(45) Linear very low density polyethylenes (VLDPEs) as used herein are homopolymers.

(46) In the context of the present invention, the “linear very low density polyethylene (VLDPE)”, “ultra-low density random ethylene-octene copolymer (polyolefin-elastomer)” and any other polymer component can be used in the form of commercially available products. Since these products may contain minor amounts of additives (e.g., antioxidants), in addition to, e.g., pure polyethylene or ethylene-octene copolymer, the aforementioned terms, e.g., “linear very low density polyethylene (VLDPE)”, and “ultra-low density random ethylene-octene copolymer (polyolefin-elastomer)”, encompass compositions comprising such minor amounts of additives, e.g., amounts of additives of below 1.0 wt.-% or below 0.5 wt.-%. It can reasonably be expected that such minor amounts of additives do not have a significant impact on the final properties of the polymer composition.

(47) In the context of the present invention, the parameters defined herein, in particular in the claims, can either be determined by testing the strand-shaped element, the polymer composition, or the single/pure components of the polymer composition. A person skilled in the art can determine the most feasible approach. For example, if the density of a VLDPE, which is present in the polymer composition of a strand-shaped element, is not known, the VLDPE may be extracted from the polymer composition and analyzed. If the glass transition temperature or melting point of a polyolefin-elastomer, which is present in the polymer composition of a strand-shaped element, is unknown, these parameters can be determined via DSC methods on the polymer composition.

(48) As disclosed above, the invention relates to a strand-shaped element comprising or consisting of an inner structure (i) and a polymer composition (ii). The strand-shaped element can be configured and can be used for connecting two devices for exchange of charges/information between the devices.

(49) Component (i) represents an inner structure, which can consist of one or more elements including a static/moving charge medium or communication medium. The inner structure/elements can have an elongated form with two ends in order to, e.g., each have a length of up to several kilometers. The elongated elements are aligned and are surrounded by component (ii). Furthermore, the static/moving current medium or communication medium of each of the elements can itself be surrounded by a coat, e.g., polymer coat/composition, which provides a shielding or sheathing. The one or more optionally surrounded static/moving current media or communication media together form component (i). Component (ii) mechanically protects component (i). During use of the strand-shaped element, components (i) and (ii) may be subjected to many bending movements and pull force. As explained above, the strand-shaped element disclosed herein may have sufficient flexibility to avoid breaking thereof even after a very long period of use (determined by the alternate bending test).

(50) Component (ii) is a halogen-free polymer composition/component surrounding the element(s), i.e., component (i). It is not excluded, but less preferred, that there are additional coatings which either surround component (ii) or which are between components (i) and (ii).

(51) The polymer composition is obtainable or obtained by compounding and extrusion, preferably HFFR compounding, of at least components (a)-(d) as defined above.

(52) The mixture of two different types of linear very low density polyethylene (VLDPE) compositions is present in a total amount of 24-32 wt.-%, further preferred 26-30 wt.-%. It may have a density in the range from 0.86 g/cm.sup.3 to 0.93 g/cm.sup.3, as measured according to ISO 1183, and may have a melting point of above 110° C. as determined by differential scanning calorimetry. Such commercially available polyethylenes are, e.g., Clearflex® MQF0 of Versalis and Clearflex® CLD0 of Polimeri Europa.

(53) One embodiment is 24.0-25.5% Clearflex® MQF0, 4.0-4.5% Clearflex® CLD0 and 13-14% Engage 8842 with, e.g., 56-57%, e.g., 56%, or 57% flame retardant filler, and optional components as defined in items 1 and 2 adding up to 100% herein.

(54) The mixture of the linear very low density polyethylene (VLDPE) compositions has a melting point above 110° C., e.g., related to the differential scanning calorimetry (DSC) measurement, preferably has a melting point which is below 120° C. as, e.g., also determined by differential scanning calorimetry (DSC).

(55) The mixture of linear very low density polyethylene (VLDPE) compositions can have a Vicat temperature (Vicat softening temperature) of above 50° C. for example, measured according to the ASTM D1525 method.

(56) The polyolefin-elastomer can comprise one or more different types of polyolefin-elastomers. The polyolefin-elastomer is preferably present in an amount of 8-16 wt.-%, further preferred 10-16 wt.-%, or 12-14 wt.-%. The one or more polyolefin elastomers are ultra-low density random ethylene-octane copolymers having a glass transition temperature of below −50° C. as determined by differential scanning calorimetry, and a melting point of below 60° C. or below 50° C., preferably below 40° C., as determined by differential scanning calorimetry. Such commercially available polyolefin-elastomers are Engage® 8842, Engage® 8180, Engage® 8130, and Engage® 8150 of Dow.

(57) The flame retardant filler is preferably present in an amount of 55-65 wt.-% and is a mineral hydroxide/hydrated mineral. Preferably, the polymer composition does not contain further polyethylene components and/or further polyolefin-elastomers.

(58) Compounding of the polymer composition can be performed by mixing the components in a molten state, e.g. in an Intermixer. A device which can suitably be used for extrusion in this context is an extruder, e.g., a twin screw extruder, single screw kneading extruder.

(59) The flame retardant filler or fillers used in the present invention are halogen free. According to the present invention, mineral hydroxides, i.e., mineral fillers which are hydrated oxides can be used. For example, aluminum or magnesium hydroxides, can be used. When exposed to high temperatures, the mineral fillers decompose through endothermic reaction and release large quantities of water, so as to stop the flame propagation. The flame retardant filler preferably is aluminum hydroxide, preferably fine precipitated aluminum hydroxide of about 99.4% purity. One example of such filler is Martinal® OL-104 LEO of Albemarle.

(60) Preferably, the flame retardant filler is used in an amount of 55-65 wt.-%, preferably 55-58%. In one embodiment, a combination of Clearflex MQF0, Clearflex CLD0 and Engage® 8842 is used.

(61) The polymer composition further comprises (d): 0.1-3.0 wt.-% of an antioxidant; and (e):

(62) 0.5-2.5 wt.-% of a coupling agent composition.

(63) The polymer composition has

(64) (aa) an elongation at break in the range from 150% to 500%, preferably from 300% to 500%, preferably 350% to 450%, or 350% to 400%, as measured by IEC 60811-501, preferably before ageing and preferably by using the strand-shaped element without the inner elements, in particular a strand-shaped element in the form of a hollow cable with conductors removed according to EN 50363-8, and/or,

(65) (bb) a strength at break in the range from 7.5 MPa to 15.0 MPa, as measured by IEC 60811-501.

(66) The mixture of two different types of linear very low density polyethylene composition can be a mixture of 20-26 wt.-% of a first composition having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, preferably of about 0.90 g/cm.sup.3, as measured according to ISO 1183, and 1-7 wt.-% of a second composition having a density in the range from 0.85 g/cm.sup.3 to 0.95 g/cm.sup.3, preferably of about 0.90 g/cm.sup.3, as measured according to ISO 1183.

(67) The mixture of linear very low density polyethylene compositions can have a density in the range from 0.85 g/cm.sup.3 to 0.92 g/cm.sup.3, preferably in the range from 0.85 g/cm.sup.3 to 0.90 g/cm.sup.3, as measured according to ISO 1183.

(68) The polyolefin-elastomer can have a density in the range from 0.80 g/cm.sup.3 to 0.90 g/cm.sup.3, preferably of about 0.86 g/cm.sup.3, as measured according to ASTM D792.

(69) The polyolefin-elastomer composition used for preparing the polymer composition (ii) can have an elongation at break of at least 1000%, further preferred at least 1100%, most preferably about 1200%, as measured by ASTMD638.

(70) The polyolefin-elastomer can have a value of ShoreD hardness of less than 20, as measured by ASTM D2240 (compression molded sample).

(71) The polymer composition can be applied by hot-melt extrusion at a temperature in the range from 100° C. up to 175° C., in a preferred embodiment of the invention in a range from 100° C. to 170° C.

(72) The coupling agent composition can be a mixture of vinyltriethoxysilane (Dynasilan® VTEO of Evonik) and 1,1-di(tert-butylperoxy)-3,3,5-trimethylcyclohexane (Trigonox 29-050 of AkzoNobel).

(73) The antioxidant can be a phenolic antioxidant, preferably tetrakis[methylene-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] methane (e.g., Irganox 1010 of BASF).

(74) The inner structure of the strand-shaped element can comprise from, e.g., 1 to 8 elements, each preferably having a diameter of up to 4.0 mm, such as diameters from 0.5 to 4.0 mm, and preferably having from 2 to 5 elements. Preferably, the strand-shaped element has an outer diameter of between 6.2 and 10 mm, preferably about 8.2 mm, such as 7.5 to 9 mm. Preferably, the elements are elongated and/or stranded. The static/moving current medium or communication medium of the elongated elements is preferably surrounded by a polymer composition. The static/moving current media or communication media can be wires, such as copper wires, and can optionally be surrounded by an insulation/polymer composition. The cross-section of each element with insulation, i.e. the cross-section of each of the static/moving current medium or communication medium with surrounding polymer, can for example be from 0.5 to 4.0 mm.sup.2, preferably 0.5 to 1.5 mm.sup.2. Preferably, 3-5 elements, preferably 3 elements, are used. The elements, comprising the static/moving current medium or communication medium which are surrounded by a polymer composition, are brought in contact with and the polymer composition (ii) is then applied to the elements in an extrusion process. In one embodiment, the polymer composition does not contain a plasticizer.

(75) The polymer composition preferably does not contain a high density polyethylene homopolymer having a density of 0.94 g/cm.sup.3 or higher, preferably not containing a high density polyethylene homopolymer having a density of 0.92 g/cm.sup.3 or higher.

(76) The polymer composition preferably does not contain a polysiloxane. The polymer composition preferably does not contain a maleic anhydride grafted polymer.

(77) The polymer composition surrounds the elements to provide insulation for mechanical protection of the elements as well as protection of people from contact with electrical current. The polymer composition surrounding elements is preferably provided in the form of a sheath. For example, the polymer composition coating the elements has a tubular shape.

(78) The glass transition temperature of the polyolefin-elastomer/ultra-low density random ethylene-octene copolymer preferably is −58° C. In one embodiment, the density of the polyolefin-elastomer/ultra-low density random ethylene-octene copolymer is in the range from 0.80 g/cm.sup.3 to 0.90 g/cm.sup.3, as measured according to ISO 1183.

(79) The polymer composition is preferably not UV crosslinked.

(80) In one embodiment, the strand-shaped element has an MFI of at least 9 g/10 min, as measured according to EN ISO 1133 under the conditions at 150° C. and the load of 21.6 kg.

(81) The invention also refers to a polymer composition obtainable or obtained by compounding at least the components (a) to (e) as described above. Further details of the polymer composition are also disclosed herein.

(82) In one embodiment, the polymer composition has a ShoreD hardness of less than 32-38, as measured by ASTM D2240 (compression molded sample). The aforementioned properties can, e.g., be determined by using the polymer composition in the form of a hollow cable with conductors removed according to EN 50363-8.

(83) The process for preparing a strand-shaped element as disclosed herein may comprise the steps of:

(84) Providing an inner structure, preferably comprising one or more elements including a static/moving current medium or communication medium;

(85) (ii) compounding the components of the polymeric composition and then extrusion of the polymeric composition as described herein onto the one or more elements; and

(86) (iii) obtaining said strand-shaped element.

(87) The step of compounding and extrusion is performed in two steps and in different devices:

(88) (iia) a compounding step, e.g. in a mixer, and afterwards (iib) the extrusion step in an extruder.

EXAMPLES

(89) The following examples describe the present invention in detail, but are not to be construed to be in any way limiting for the present invention.

(90) VLDPE1 (Clearflex MQF0 of eni/versalis): Is a linear very low density polyethylene (VLDPE) having a density in the range from 0.85 g/cm.sup.3 to 0.93 g/cm.sup.3, as measured according to ISO 1183, and having a melting point of above 110° C. It has a melt flow index of 8-15 as determined according to ASTM1238 (190° C./2.16 kg; g/10′).

(91) VLDPE2 (Clearflex CLD0 of Polimeri Europa, Eni): Is a linear very low density polyethylene (VLDPE) having a density in the range from 0.85 g/cm.sup.3 to 0.93 g/cm.sup.3, as measured according to ISO 1183, and having a melting point of above 110° C. It has a melt flow index of 2-5 as determined according to ASTM1238 (190° C./2.16 kg; g/10 min).

(92) POE1 (Engage 8842, random octene copolymer): Is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C. and having a melting point of below 40° C.

(93) PGE2 (Exact8203 of ExxonMobil, block octene copolymer): Is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C. and having a melting point of below 40° C. The polymer has an MFI of 3.0 g/10 min, a density of 0.888 g/ccm, a melting point of 72° C., a glass transition temperature of <−75° C. and a Vicat softening point of 51° C.

(94) POE3 (Engage HM7487 of the Dow Chemical Company, random octene copolymer): Is an ultra-low density random ethylene-octene copolymer having a glass transition temperature of below −50° C. and having a melting point of below 40° C. The polymer has an MFI of <0.5 g/10 min, a density of 0.862 g/ccm, a melting point of 37° C., a and a glass transition temperature of <−57° C.

(95) The test method and sample preparation for the measurement of the elongation is performed as with a sheathing material described in EN 50363-8, wherein the strand-shaped element without the inner structure is subjected to the measurement.

(96) The compositions in the examples were extruded into cables using a HFFR extruder, with HFFR extrusion head and HFFR screw, at a temperature in the range from 100° C. up to 175° C. The process conditions can be chosen by a person skilled in the art.

Example—1

(97) Composition 1:

(98) Composition 1 is characterized by a combination of a VLDPE (VLDPE1), in an amount of 25 wt.-% and a block octene copolymer (PGE2) in an amount of 10 wt.-%. At a high filler level of ATH (aluminum hydroxide) of 63%, the elongation was below 300%.

(99) TABLE-US-00001 Composition 1 25 % VLDPE1 10 % POE2 63 % ATH 1 % Antioxidant 1 % Coupling agent

(100) The measured elongation was <300%. Composition 1 passed the alternate bending test, EN 50396.

Example—2

(101) Composition 2:

(102) Composition 2 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 32 wt.-%. The two VLDPEs are used in combination with a block octene copolymer (PGE2). An additional low level of ATH (aluminum hydroxide) of 58% gives a high elongation.

(103) TABLE-US-00002 Composition 2 24 % VLDPE1 8 % VLDPE2 8 % POE2 58 % ATH 1 % Antioxidant 1 % Coupling agent

(104) The measured elongation was >300%. Reducing the ATH level from 63% to 58% reduces the flame retardancy.

Example—3

(105) Composition 3:

(106) Composition 3 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 32 wt.-%. The two VLDPEs are used in combination with a random octene copolymer (POE3). Even at a high filler level of ATH (aluminum hydroxide) of 58%, a very high elongation was obtained.

(107) TABLE-US-00003 Composition 3 24 % VLDPE1 8 % VLDPE2 8 % POE3 58 % ATH 1 % Antioxidant 1 % Coupling agent

(108) The measured elongation was >400%. A comparison between Compositions 2 and 3 seems to confirm the concept underlying the present invention. That is, the specific combination and amounts of components provides the desired elongation.

Example—4

(109) Composition 4 (Comparative Example):

(110) Composition 4 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 32 wt.-%. The two VLDPEs are used in combination with a propylene-based elastomer.

(111) TABLE-US-00004 Composition 4 24 % VLDPE1 8 % VLDPE2 8 % Propylene-based elastomer (copolymer) 58 % ATH 1 % Antioxidant 1 % Coupling agent

(112) The measured elongation was <300%. The measured tensile strength was <7.5 MPa. A comparison between Compositions 3 and 4 seems to suggest that the use of a propylene-based elastomer does not provide a very high elongation.

Example—5

(113) Composition 5 (Comparative Example):

(114) Composition 5 is characterized by a combination of EVA (ethylene vinyl acetate) in an amount of 16 wt.-%. The EVA is used in combination with a block octene copolymer (POE2).

(115) TABLE-US-00005 Composition 5 16 % EVA 15 % POE2 63 % ATH 1 % Antioxidant 5 % Coupling agent MAH-PE

(116) The measured elongation was <300%. The composition failed the hot pressure test (80° C.>50%). A comparison between the above compositions seems to suggest that the use of EVA does not provide a very high elongation and dimensional stability. Additionally, another coupling agent does not improve the properties.

Example—6

(117) Composition 6 (Comparative Example):

(118) Composition 6 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 28 wt.-%. The two VLDPEs are used in combination with an α-olefin copolymer.

(119) TABLE-US-00006 Composition 6 21 % VLDPE1 7 % VLDPE2 7 % α-olefin copolymer (Vestoplast 750) 63 % ATH 1 % Antioxidant 1 % Coupling agent

(120) The measured elongation was <300%. A comparison between the above compositions seems to suggest that the use of a random ethylene-octene copolymer is superior to the use of an α-olefin copolymer regarding elongation at break.

(121) Composition 7 (Comparative Example):

(122) Composition 7 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 20 wt.-%. The two VLDPEs are used in combination with an amorphous propylene-ethylene copolymer and POE2.

(123) TABLE-US-00007 Composition 7 16 % VLDPE1 4 % VLDPE2 10 % POE2 5 % Amorphous propylene- ethylene copolymer, Eastoflex 1060PL 63 % ATH 1 % Antioxidant 1 % Coupling agent

(124) The measured elongation was >300%. The composition failed the hot pressure test (hot pressure test 80° C.>50%). The experiment seems to show how changing the polymer compositions results in deterioration of the properties.

(125) Composition 8:

(126) Composition 8 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 18 wt.-%. The two VLDPEs are used in combination with a random octene copolymer (POE3) in an amount of 17%.

(127) TABLE-US-00008 Composition 8 14 % VLDPE1 4 % VLDPE2 17 % POE3 63 % ATH 1 % Antioxidant 1 % Coupling agent

(128) The measured elongation was >400%. The composition failed the hot pressure test (80° C.>50%). The example seems to suggest that the amount of POE was too high for mechanical stability at high temperatures but good for elongation at break at room temperature.

(129) Composition 9:

(130) Composition 9 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 23 wt.-%. The two VLDPEs are used in combination with a random octene copolymer in an amount of 13%.

(131) TABLE-US-00009 Composition 9 20 % VLDPE1 3 % VLDPE2 13 % POE1 62 % ATH 1 % Antioxidant 1 % Coupling agent

(132) The measured elongation was >400%. The flexibility test was achieved with a test strand-shaped element.

(133) Composition 10:

(134) Composition 10 is characterized by a combination of two VLDPEs, i.e., VLDPE1 and VLDPE2, in a total amount of 30 wt.-%. The two VLDPEs are used in combination with a random octene copolymer (PGE1) in an amount of 10%.

(135) TABLE-US-00010 Composition 10 20 % VLDPE1 10 % VLDPE2 10 % POE1 58 % ATH 1 % Antioxidant 1 % Coupling agent

(136) The measured elongation was >430%. With this formulation, the flexibility test can be achieved with a strand-shaped element with three inner elements, each having a cross-section of 1.5 mm.sup.2.

CITED LITERATURE

(137) EP1102282 A1

(138) DE3633056 A1

(139) WO 2010015876 A1

(140) WO 2013030795 A1

(141) WO 2002026879 A1

(142) WO 2007032573 A1

(143) WO 2008014597 A1 and

(144) WO 2010024602 A2