SPACER FOR INSULATED GLASS UNITS

Abstract

A spacer is provided that is shapable into a spacer frame, and during manufacture of an insulating glass unit, can be mounted on the glass panes. The spacer is formed having an inner surface, an outer surface and two lateral surfaces extending at either side of the spacer from the inner surface to the outer surface, and comprises a profiled body. The profiled body comprises two mutually spaced lateral faces running parallel to its longitudinal direction and a base body that extends between the lateral faces and has an outer and an inner face. The profiled body comprises at least in one part of its volume a quantity of particulate desiccant that is embedded in a plastics material. The spacer is coilable about an axis, perpendicularly to the lateral surfaces, and takes a flexurally rigid form in a plane perpendicular to the lateral surfaces.

Claims

1. A spacer for insulating glass units, wherein the spacer is formed having an inner surface, an outer surface and two lateral surfaces extending at either side of the spacer from the inner surface to the outer surface, and wherein the spacer comprises a profiled body, wherein the profiled body comprises two mutually spaced lateral faces running parallel to its longitudinal direction and a base body that extends between the lateral faces and has an outer and an inner face, wherein the profiled body is made from a plastics material and comprises at least in one part of its volume a quantity of particulate desiccant that is embedded in the plastics material, wherein the spacer is coilable about an axis, perpendicularly to the lateral surfaces, and wherein the spacer takes a flexurally rigid form in a plane perpendicular to the lateral surfaces.

2. The spacer according to claim 1, wherein the spacer has a coilability such that there is a deflection of the spacer of approximately 1 mm or more, by comparison with an unloaded condition, wherein the deflection is determined at the outer surface of the spacer as the outer surface thereof lies on two supporting bodies at a loading span L.sub.S of 100 mm, as measured in a longitudinal direction of the spacer, and with a force F of 50 N acting in a centre of the loading span L.sub.S, wherein the force F is introduced into the spacer perpendicularly to a support plane defined by the two supporting bodies.

3. The spacer according to claim 1, wherein the spacer has a flexural strength at which a deflection of the spacer is approximately 10 mm or less by comparison with an unloaded condition, wherein the deflection is determined at a lateral surface as the lateral surface lies on two supporting bodies at a loading span of 100 mm, as measured in a longitudinal direction of the spacer, and with a force of 100 N acting in a centre of the loading span, wherein the force of 100 N is introduced into the spacer perpendicularly to the lateral surface.

4. The spacer according to claim 1, wherein reinforcing elements are embedded in the plastics material of the profiled body.

5. The spacer according to claim 1, wherein on either side of the base body the profiled body has lateral walls that extend from the base body and beyond its inner face by approximately 0.5 mm or more, and form the lateral faces of the profiled body.

6. The spacer according to claim 1, wherein the spacer has a height H of approximately 5 mm or less.

7. The spacer according to claim 1, wherein the spacer has a width B of approximately 14 mm to approximately 40 mm.

8. The spacer according to claim 7, wherein the spacer is intended for triple glazing and has a width of approximately 30 mm or more and an aspect ratio A, as seen in a cross section perpendicular to a longitudinal direction, defined as a quotient of the width B of the spacer and the height H of the spacer (A=B/H), wherein the aspect ratio A has a value of approximately 6 or more.

9. (canceled)

10. The spacer according to claim 1, wherein the particulate desiccant is selected from silicates, sulfates, oxides in the form of zeolite, calcium sulfate, silica gel, layered silicate, tectosilicate, phosphorus oxide, aluminium oxide, alkali metal oxide and/or alkaline earth metal oxide or mixtures thereof, wherein the desiccant comprises a 3A zeolite with an average pore size of approximately 3 angstroms.

11. The spacer according to claim 1, wherein the particulate desiccant is embedded in the plastics material in a proportion of approximately 35 weight % to approximately 45 weight % in relation to a total weight of the profiled body.

12. The spacer according to claim 1, wherein the particulate desiccant is embedded in the plastics material in the form of granules and/or a powder.

13. (canceled)

14. The spacer according to claim 1, wherein the plastics material of the profiled body is selected such that after storage in a standard atmosphere (50%±10% relative air humidity at a temperature of 23° C.±2° C.) for a storage period of 48 hours the spacer has a moisture content of approximately 50% or less of a maximum moisture absorption capacity.

15-16. (canceled)

17. The spacer according to claim 1, wherein the spacer has on the inner surface a continuous groove parallel to the lateral surfaces and at a spacing from each of the lateral surfaces, for receiving a glass pane edge of a further glass pane.

18. The spacer according to claim 17, wherein the spacer has on the inner surface two mutually spaced projections that run parallel to the longitudinal direction of the spacer and between which the groove is formed.

19-21. (canceled)

22. The spacer according to claim 1, wherein the plastics material of the profiled body has, at least in certain regions, a pore structure, wherein the average pore size is approximately 5 μm to approximately 150 μm, and wherein a pore volume is approximately 40% by volume or less of a volume of the profiled body.

23. The spacer according to claim 1, wherein the profiled body has, on an outer and/or inner face of the base body and/or on the lateral walls, recesses that run substantially transversely to a longitudinal direction of the profiled body at regular intervals.

24. The spacer according to claim 1, wherein the spacer has on the outer surface a barrier layer that has a barrier effect in respect of gases and/or air moisture, wherein the barrier layer is selected from a metal foil, a multiple-layer foil with a polymer-based backing film and at least one layer of metal, metal oxide or ceramic, a coating of platelet-like nanoparticles, a flexible glass layer, a diffusion-inhibiting polymer film or a polymer film laminate.

25. The spacer according claim 1, wherein the spacer has on the outer surface a barrier layer that has a barrier effect in respect of gases and/or air moisture, wherein the barrier layer takes the form of a coating on the profiled body and comprises a layer of metal, metal oxide or ceramic, platelet-like nanoparticles.

26. (canceled)

27. An insulating glass unit having two outer glass panes that are held at a predetermined spacing by a spacer frame, wherein the spacer frame comprising a spacer according to claim 1.

28. The insulating glass unit according to claim 27, wherein the two outer glass panes are bonded to the spacer by means of a primary sealant in the region of the lateral surfaces, wherein the primary sealant is selected from synthetic rubber, polyisobutylene, butyl rubber, polyurethane, silicone polymer, silane-modified polymer, polysulfide and polyacrylate.

29-30. (canceled)

31. The insulating glass unit according to claim 27, wherein the spacer has a groove on the inner surface side, in which the edge of a third glass pane is inserted.

Description

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

[0081] These and further advantageous embodiments of the spacers according to the invention and of insulating glass units formed using them are explained in more detail below with reference to the drawing, in which, individually:

[0082] FIGS. 1A to 1D show a first embodiment of the spacer according to the invention, some in different installation situations in an insulating glass unit, and variants of this spacer;

[0083] FIGS. 2A and 2B show a further embodiment of a spacer according to the invention and a variant thereof;

[0084] FIGS. 3A to 3D show a further embodiment of the spacer according to the invention, some in different installation situations in an insulating glass unit, and a variant of the spacer;

[0085] FIGS. 4A and 4B show two variants of an insulating glass unit with spacers according to the invention;

[0086] FIGS. 5A to 5D show a schematic test set-up for determining the deflection of spacers according to the invention perpendicular to their outer surface;

[0087] FIGS. 6A to 6D show a schematic test set-up for determining the deflection of spacers according to the invention perpendicular to a lateral surface;

[0088] FIGS. 7a to 7i show schematic profile geometries of the spacer profiles a) to i) in Table 1;

[0089] FIGS. 8A to 8C show measurement curves obtained with different types of spacers using a test set-up according to FIG. 5 and FIG. 6;

[0090] FIGS. 9A to 9E show further embodiments of the spacer according to the invention and variants thereof, some in different installation situations in an insulating glass unit;

[0091] FIG. 10 shows a further embodiment of a spacer according to the invention;

[0092] FIG. 11 shows a further embodiment of a spacer according to the invention, with a plurality of variations of a functional element;

[0093] FIGS. 12A to 12C show further embodiments of the spacer according to the invention with different functional elements, in the condition installed in an insulating glass unit; and

[0094] FIGS. 13A to 13F show different versions of the making of a connection between two spacer end regions of the spacer in FIG. 1A.

DETAILED DESCRIPTION OF THE DRAWINGS

[0095] FIGS. 1A-1D show a plurality of variants of a first embodiment of a spacer according to the invention, in a cross section perpendicular to the longitudinal direction of the spacers.

[0096] When determining the height H and the width B of a spacer profile according to the invention, the corresponding values of a rectangle that includes the cross section of the spacer are taken as a basis, as indicated in FIG. 1A.

[0097] FIG. 1A shows a spacer 10 according to the invention that comprises a coilable profiled body 12 having a base body 18 and two mutually spaced lateral walls 14, 16 that run parallel to its longitudinal direction and, with the base body 18, form a U-shaped profile geometry. The lateral walls also form the lateral faces of the profiled body and, in part, the lateral surfaces of the spacer.

[0098] Arranged on the upper side of the base body 18 of the spacer 10 is a barrier layer or vapour barrier layer 20 that preferably extends from the one lateral face of the lateral wall 14, over the upper side (outer surface) 17 of the base body 18 to the second lateral face of the lateral wall 16. In the mounted condition, the outer surface is arranged adjacent to the outer edge of the insulating glass unit.

[0099] Suitable vapour barrier layers 20 are for example stainless steel foils having a thickness of approximately 10 μm to approximately 20 μm, and multiple-layer foils of which the individual layers are coated with metal and/or ceramic.

[0100] Here, the inner surface of the spacer 10 is formed by the inner surface 19 of the base body 18, which extends from the lateral wall 14 over the base body 18 to the lateral wall 16.

[0101] The plastics material from which the profiled body 12, together with its base body 18 and the lateral walls 14 and 16, is made is selected for example from polypropylene, polyethylene, styrene acrylonitrile copolymer (SAN), acrylic butadiene styrene copolymer (ABS), acrylic styrene acrylonitrile copolymer (ASA), polyvinyl chloride (PVC), polyamide 6 (PA6), polyamide 66 (PA66), polyethylene terephthalate (PET) or blends of these polymers. This preferred selection also applies to the spacers according to the invention described below.

[0102] For example, the plastics material contains glass fibres in a proportion of approximately 10 weight % and a desiccant in a proportion of approximately 40 weight %, in each case in relation to the total weight of the profiled body of the spacer.

[0103] Typically, the spacers according to the invention are manufactured by an extrusion method.

[0104] FIG. 1B shows the spacer 10 from FIG. 1A in a situation in which it is installed in an insulating glass unit 25, wherein a first glass pane 22 is arranged abutting against the lateral surface of the spacer 10, which is formed by the lateral wall 14 of the profiled body and the vapour barrier layer 20, and a second glass pane 24 is arranged abutting against the second lateral surface thereof, which is formed by the lateral wall 16 and the vapour barrier layer 20. Here, the ends 21a, 21b of the vapour barrier layer 20 are angled off in form and embedded in the plastics material of the base body 18, as known for example from DE 10 2010 006 127 A1.

[0105] The two glass panes 22, 24 are connected to the spacer 10 in a substance-to-substance bond at the lateral surfaces, in each case by way of a primary sealant such as a butyl compound 26, 27. The lateral butyl application (primary sealant) 26, 27 conventionally remains ductile, so pumping movements of the pane under load from wind and climatic load can be taken up. For this reason, it is not adequate for holding together the bond between the panes of the insulating glass unit in the long term. A further sealant, the secondary sealant, which cures and holds the insulating glass unit together is needed.

[0106] The two glass panes 22, 24 are held parallel and at a predetermined spacing from one another by the spacer 10. The upper side of the base body 18 here forms the outer side, that is to say the outer surface of the spacer 10 and the outer edge region of the insulating glass unit 25. In addition, a secondary sealant 28, 29 is applied in the region of the outer edge region, adjacent to the respective glass panes and the outer surface of the spacer 10.

[0107] The primary butyl sealant 26, 27 is applied substantially over the entire lateral faces of the lateral walls 14, 16 and the lateral surfaces of the spacer 10. The secondary sealant 28, 29 takes the form of a wedge-shaped configuration at the outer edge region of the insulating glass unit 25, as seen in cross section.

[0108] Another situation in which the spacer 10 from FIG. 1A is installed in an insulating glass unit 25 is illustrated in FIG. 1C. In this variant, a secondary sealant 30 is applied over the entire face of the vapour barrier layer 20 (outer surface) of the spacer 10, with the result that the secondary sealant 30 extends parallel to this layer, from the one glass pane 22 to the other glass pane 24. In this case, the glass panes 22, 24 are bonded to the lateral surfaces of the spacer and the lateral faces of the lateral walls 14, 16 by a primary sealant 32, 34.

[0109] FIG. 1D shows a further variant of the coilable spacer 10 according to the invention in cross section, wherein the spacer is provided with the reference numeral 40 and comprises a profiled body 42 having a base body 48 and, arranged to either side thereof, lateral walls 44, 46 that, together with the base body 48 of the spacer 40, form a U-shaped profile cross section. Applied to the upper outer side of the spacer 40 is a barrier or vapour barrier layer 50 that extends from the first lateral face of the lateral wall 44, over the entire outer face of the base body 48 to the second lateral face of the lateral wall 46, and in large part covers both this and the first lateral face. On its downwardly oriented (in the installed condition of the spacer, oriented towards the inner space of the insulating glass unit) inner face 52 (inner surface of the spacer 40), the base body 48 has a structure comprising longitudinal ribs 54 that are distributed parallel to one another and spaced at regular intervals over the entire width of the inner face 52.

[0110] The parallel ribs 54 on the inner surface 52 of the spacer 40 make the surface on the inner side of the spacer larger and thus promote faster absorption of water vapour. Further, this structure may also have a positive effect on the appearance of the spacer.

[0111] FIG. 2A shows a further embodiment of a spacer 80 according to the invention that comprises a profiled body 82 (which in this case at the same time represents the base body) that has a planar outer face 88 and parallel lateral faces 84 and 86 that are oriented perpendicularly to the outer face 88. Arranged on the outer face 88 is a vapour barrier layer 90 that extends from the first lateral face 84, over the outer face 88 to the second lateral face 86, and covers the majority of the lateral faces. The vapour barrier layer 90 forms the outer surface of the spacer 80 in the region of the outer face 88 and the majority of its lateral surfaces.

[0112] The inner face 92 of the profiled body 82, on the opposite side to the planar outer face 88, is concave in form and extends substantially from the first lateral face 84 to the second lateral face 86. The inner face 92 forms the inner surface of the spacer 80.

[0113] A modified embodiment of a spacer 100 according to the invention is shown in FIG. 2B. The spacer 100 has a profiled body 101 having a base body 102 that has a planar outer face 108 and, arranged perpendicularly thereto, a first and a second lateral face 104, 106. The spacer 100 has on its outer surface a vapour barrier layer 110 that extends over the outer face 108 and also in large part over the lateral faces 104, 106.

[0114] Further, the spacer 100 has an inner surface 112 that is concave in form and additionally has ribs 114 running parallel to the longitudinal direction of the spacer 100 and regularly spaced from one another.

[0115] A further embodiment of the spacer according to the invention is shown in FIG. 3A, wherein the spacer 120 once again has a profiled body 121 having a base body 122 and, laterally delimiting this, lateral walls 124, 126. The lateral walls 124, 126 are oriented parallel to one another and substantially perpendicularly to a planar outer surface 128.

[0116] Provided on the outer surface 128 is a vapour barrier layer 130 that extends from the first lateral face of the lateral wall 124, over the outer face of the base body 122 to the second lateral face of the lateral wall 126, and likewise in large part covers the lateral faces.

[0117] The spacer 120 further has an inner surface 132 that takes a substantially planar form and has, centrally between the lateral walls 124, 126, a groove 134 that runs in the longitudinal direction of the spacer and is delimited by two parallel strip-like projections 136, 137. The spacing between the free ends of the projections 136, 137 is preferably selected to be somewhat smaller than the width of the groove in the region of its root. The groove 134 serves to receive a central, third glass pane (not illustrated) that divides the inner space within an insulating glass unit into two sub-volumes. In the embodiment of the spacer 120 shown, the sub-volumes of the inner space of the insulating glass unit are substantially the same size. In contrast hereto, as a result of an off-centre arrangement of the groove 134 and the two projections 136, 137 delimiting the groove 134, the sub-volumes may be of different sizes, in order for example to create an asymmetrical construction if this is made necessary by further requirements such as anti-drop protection, statics, etc.

[0118] FIG. 3B shows a variant of the spacer 120 in the form of a spacer 140. The spacer 140 has a profiled body 141 having a base body 142 and, laterally delimiting this, lateral walls 144, 146. The lateral walls 144, 146 are oriented parallel to one another and substantially perpendicularly to an outer surface 148 of the spacer 140.

[0119] Provided on the outer surface 148 is a vapour barrier layer 150 that extends from the first lateral face of the lateral wall 144, over the outer face of the base body 142 to the second lateral face of the lateral wall 146, and likewise in large part covers the lateral faces.

[0120] The substantially planar base body 142 further has an inner face 152 that has, centrally between the lateral walls 144, 146, a groove 154 that runs in the longitudinal direction of the spacer 140 and is delimited by two parallel strip-like projections 156, 157. The spacing between the free ends of the projections 156, 157 is preferably selected to be somewhat smaller than the width of the groove 154 in the region of its root. The groove 154 serves to receive a central, third glass pane (not illustrated) that divides the inner space within an insulating glass unit into two sub-volumes. In the embodiment of the spacer 140 shown, the sub-volumes of the inner space of the insulating glass unit are substantially the same size. As described in the context of FIG. 3A, this may be deviated from where necessary.

[0121] In this embodiment, the regions of the inner face 152 between the lateral walls 144 and 146 and the groove 154 and the associated projections 156, 157 are not planar but are provided with ribs 158 that are arranged parallel and at regular intervals.

[0122] FIG. 3C shows the spacer 140 from FIG. 3B in a situation in which it is installed in an insulating glass unit 170, wherein a first glass pane 172 is arranged abutting against the lateral surface formed by the lateral wall 144 and the vapour barrier layer 150 of the spacer 140, and a second glass pane 174 is arranged abutting against the second lateral surface thereof (corresponding to the lateral face of the lateral wall 146 and the vapour barrier layer 150). The two glass panes 172, 174 are each bonded to the spacer 140 by way of a primary butyl sealant 176, 177. The two glass panes 172, 174 are held in a parallel arrangement at a predetermined spacing from one another by the spacer 140. The upper side of the base body 152 (outer face) in this case forms the outer edge region of the insulating glass unit 170.

[0123] The primary butyl sealant 176, 177 is applied to the spacer 140 substantially over the entire height of the lateral faces of the lateral walls 144, 146. A secondary sealant 178, 179 takes the form of a wedge-shaped configuration at each of the outer edge regions of the insulating glass unit 170, as seen in cross section towards the outer glass panes.

[0124] A third glass pane 180 is held in the groove 154, between the projections 156, 157, and divides the inner space of the insulating glass unit between the outer glass panes 172, 174 into two sub-volumes. The glass pane 180 may be made from the same material as the glass panes 172, 174 and have the same thickness, but it frequently takes a thinner form, since the glass pane 180 is exposed to smaller loads than the glass panes 172, 174. For this reason, the glass pane 180 can also be made from a different material, such as plexiglass, or indeed by replaced by a plastics film. In each case, the intermediate space between the panes is divided into smaller sub-volumes, with the result that convection currents can be reduced or substantially entirely suppressed. This results in better thermal insulation values in the insulating glass units.

[0125] Another situation in which the spacer 140 from FIG. 3B is installed is illustrated in FIG. 3D. In this variant, a primary butyl sealant 182, 183 is applied to the lateral faces of the lateral walls 144 and 146 or to the regions of the vapour barrier layer 150 arranged there. A secondary sealant 184 is applied over the entire face of the outer surface of the spacer 140, with the result that it extends parallel to the outer surface from the one glass pane 172 to the other glass pane 174 and abuts sealingly against both glass panes and against the outer surface (vapour barrier layer 150).

[0126] Once again, a third glass pane 180 is inserted and held in the groove 154, between the projections 156, 157, and divides the inner space of the insulating glass unit 170 into two sub-volumes between the outer glass panes 172, 174.

[0127] The effect described above of further improving the thermal insulation values of insulating glass units that comprise a third, central glass pane is explained again in detail with reference to FIGS. 4A and 4B. These also make it clear that, as a result of the one-piece spacer for triple glazing, an offset such as can arise between the three glass panes in the case of two conventionally used spacers is avoided.

[0128] FIG. 4A shows an insulating glass unit 200 with two parallel glass panes 202, 204 that are held mutually parallel and at a spacing by means of spacer segments 10a and 10b that correspond to the spacer 10 in FIG. 1A.

[0129] The glass panes 202, 204 are bonded to the spacer segments 10a, 10b by a primary butyl sealant 210a, 211a, 210b, 211b. A secondary sealant 230a, 230b is applied to the entire outer surface of the spacer 10 (in this case the portions 10a, 10b) in a manner analogous to the embodiment described in connection with FIG. 1C, and also abuts sealingly against the glass panes 202, 204.

[0130] The insulating glass unit 200 has a single inner space 220 delimited only by the glass panes 202, 204 and the spacer 10, which is arranged peripherally at the edge region of the glass panes. The spacer segments running in the vertical direction, and the corresponding portions of primary butyl sealant and secondary sealant, are not illustrated in FIG. 4A, for the sake of clarity.

[0131] FIG. 4B shows an insulating glass unit 240 having two parallel glass panes 242, 244 that are held mutually parallel and at a spacing by means of spacer segments 120a and 120b that correspond to the spacer 120 in FIG. 3A.

[0132] The glass panes 242, 244 are bonded to the spacer segments 120a, 120b by a primary butyl sealant 246a, 246b, 247a, 247b. A secondary sealant 250a, 250b is used in a manner analogous to the embodiment described in connection with FIG. 3D.

[0133] A third, central glass pane 246 is inserted in the grooves 134a, 134b of the spacer segments 120a, 120b, and divides the inner space of the insulating glass unit 240 into two separated sub-volumes 252, 254.

[0134] The divided inner space of the insulating glass unit 240 has sub-volumes 252, 254 and is outwardly delimited only by the glass panes 242, 244, the spacer 120, which is arranged peripherally at the edge region of these glass panes, and the primary (butyl) sealant 246a, 246b, 247a, 247b and the secondary sealant 250a, 250b. The spacer segments running in the vertical direction, and the corresponding portions of butyl adhesive and secondary sealant, are not illustrated in FIG. 4A, for the sake of clarity.

[0135] FIG. 5A shows schematically a test arrangement 300 for determining the deflection of a spacer according to the invention (in this case, by way of example, the spacer 10) or indeed the flexural strength in conformance with DIN EN ISO 178 (2013). The specimen of the spacer 10 that is used for the test has a length L.sub.P of 150 mm and is positioned on two supporting bodies 302, 304, wherein the support points maintain a predetermined spacing L.sub.S of 100 mm from one another, also called the loading span below. The two supporting bodies 302, 304 define a support plane.

[0136] Positioned centrally in relation to the loading span L.sub.S is a partly cylindrical die 306 having a planar contour by means of which a force F can be introduced to the spacer, perpendicularly to the support plane.

[0137] For the coilability or rollability of the spacer according to the invention, the deflection relative to an unloaded condition is important, and this is measured at the outer surface of the spacer for measuring in each case (here for example the outer surface 17 of the spacer 10), with the force introduced by the die 306 being 50 N.

[0138] In FIG. 5B, the test arrangement 300 is shown with a spacer 460, in a sectional illustration along the line VB-VB, perpendicular to the longitudinal direction of the spacer 460 and parallel to the direction of the active force F.

[0139] In part-FIGS. 5C and 5D, the two spacers 10 and 460 are shown in an orientation in which the respective outer surface 17 or 470, which lies on the supporting bodies 302, 304 during the test for deflection, faces downwards.

[0140] Preferably, the spacer according to the invention has a coilability such that, with a force of 50 N acting in the centre of the loading span, there is a deflection of approximately 1 mm or more, preferably approximately 1.3 mm or more, more preferably approximately 1.7 mm or more by comparison with an unloaded condition. The deflection is measured at the outer surface 17 and 470 (in this case at the barrier layer 20 and 472 respectively) of the spacer, in the centre of the loading span, as the spacer lies on the two supporting bodies 302, 304 at a loading span of 100 mm, as measured in the longitudinal direction of the spacer. The force of 50 N is introduced into the spacer perpendicularly to a support plane defined by the supporting bodies (and also perpendicularly to the outer surface) (test method A; cf. FIGS. 5A and 5B).

[0141] For handling of the spacers according to the invention during manufacture of the insulating glass units, it is preferable if the spacers have a flexural strength, under a force introduced perpendicularly to a lateral face (in this case 14; 468) or lateral surface, at which deflection of the spacer (10; 460) in a position according to FIGS. 6A and 6B under a force of 100 N acting in the centre of the loading span L.sub.S is approximately 10 mm or less, preferably approximately 5 mm or less, more preferably approximately 3 mm or less, relative to an unloaded condition.

[0142] The deflection is determined at one of the lateral surfaces (in this case 14, 16; 466, 468) of the spacer, centrally in relation to the loading span, as the lateral surface lies on the two supporting bodies 302, 304 of the test arrangement 300 with a loading span L.sub.S of 100 mm, as measured in the longitudinal direction of the spacer. The typical specimen length L.sub.P is 150 mm. The force of 100 N is introduced into the spacer perpendicularly to the lateral surfaces (test method B). This test requires an orientation of the spacers in the manner illustrated for the spacers 10 and 460 in detail FIGS. 6C and 6D. For correct performance of the test, the spacer can be held in the orientation shown in detail FIGS. 6A and 6B by guide elements 310, 312 without this having a noticeable influence on the measurement results. The guide elements 310, 312 can be held in position, parallel and at a predetermined spacing from one another, such that the spacer 10, 460 can be received between them with little play.

[0143] As mentioned above, a loading span or support distance L.sub.S of 100 mm and a length of the specimen body L.sub.P of approximately 150 mm are used as the test parameters when measuring the flexural strength in conformance with DIN EN ISO 178. The other test parameters are as follows:

[0144] Initial load: 1 N (test method variants A and B)

[0145] Test speed: 10 mm/min (test method variants A and B)

[0146] Radii R1 (die 306) and R2 (supporting bodies 302, 304): 5 mm

[0147] Once the spacer to be tested has been put in position on the supporting bodies 302, 304, the die 306 is brought into contact with the spacer 10, 460 under the initial load, and this stabilises the spacer 10, 460 in position. Then the test die 306 is moved perpendicularly downwards at the predetermined test speed, wherein the force then acting on the specimen body (spacer) is recorded as a function of the travel performed by the test die 306 (cf. FIGS. 8A to 8C). This distance corresponds substantially to the deflection of the specimen body.

[0148] The spacer profiles are laid with the outer surface oriented downwards (test method A—for deflection perpendicular to the outer surface; FIG. 5A/5B) and with the outer surface oriented to the side (test method B—for deflection or flexural strength perpendicular to the lateral face; FIG. 6A/6B).

[0149] With the test method variant A, the outer surface is defined as the side that, when the spacer is in the condition installed in an insulating glass unit, is arranged adjacent to the outer periphery of the insulating glass unit. When the three-point bend test is performed, the die 306 of the test arrangement 300, also called the compression die, presses perpendicularly downwards from above against the specimen (in this case spacer 10 or 460) at L.sub.S/2.

[0150] With the test method variant B (deflection perpendicular to the lateral surface), if the spacer undergoes pronounced distortion and deviates to a great extent from the desired orientation during measurement, then a suitable guide must be used to keep the specimen body in the perpendicularly upright orientation. The guide may be a or if necessary two separate loosely abutting guide plates, as described above, which limit lateral deviation of the specimen bodies but allow perpendicular movement of the specimen body substantially unimpeded, in particular as it is pushed in by the compression die. This is illustrated in FIGS. 6A and 6B, and reference may be made here to the description thereof.

[0151] The specimen bodies must be free of visible damage (e.g. irreversible deformation, cracks, ruptures, etc.) and represent a conventional good product condition that also meets the quality requirements for mounting in insulating glass units. The values obtained in the test methods A and B are substantially independent of any moisture absorption by the desiccant that occurs before the test methods are performed.

[0152] The width B of the spacers according to the invention is preferably approximately 12 mm to approximately 44 mm, more preferably approximately 14 mm to approximately 40 mm.

[0153] There is no need to condition the specimen bodies before measurement. The specimen bodies are preferably tested in a standard atmosphere of 23° C.±2° C. at 50%±10% air humidity.

[0154] Measurement ends in the event of rupture or destruction of the specimen body, or when the maximum travel of the die 306 is reached.

[0155] The measurements are performed such that the deflection path is recorded and stored, and can be output as a force-displacement curve.

[0156] The test methods A and B are carried out on specimens according to the invention and specimens from the prior art.

[0157] More detailed characterisation of the specimens can be seen in Table 1 below. There is a schematic overview of the profile geometries in FIG. 7 (detail FIGS. 7a to 7i).

[0158] Specimen a) corresponds to an exemplary embodiment of the present invention with the following properties:

[0159] The spacer is formed as a solid profile of polypropylene with 20 weight % of glass fibres (GF 20) and 40 weight % of desiccant (3A zeolite powder; average particle size approximately 6 to 9 μm; available from Grace GmbH & Co KG under the name Sylosiv K300), in each case relative to the total weight of the spacer. The geometry also corresponds to the spacer 460 of FIG. 9C. As the barrier layer there was used a stainless steel foil 10 μm thick. The spacer is coilable/rollable onto a core having a diameter of 300 mm. The spacer is intended for triple glazing with two intermediate spaces between the panes, each of 12 mm, and a central pane 4 mm thick.

[0160] Specimen b) corresponds to an exemplary embodiment of the present invention with the following properties:

[0161] The spacer is formed as a solid profile of polypropylene with 10 weight % of glass fibres (GF 10) and 40 weight % of desiccant (3A zeolite powder; average particle size approximately 6 to 9 μm; available from Grace GmbH & Co KG under the name Sylosiv K300), in each case relative to the total weight of the spacer. The geometry also corresponds to the spacer 10 of FIG. 1A. As the barrier layer there was used a stainless steel foil 10 μm thick. The spacer is coilable/rollable onto a core having a diameter of 300 mm.

[0162] Specimen c) is a conventional spacer, available from Rolltech A/S under the name Chromatech® Ultra F2. The spacer is made from polypropylene and has on its outer surface a stainless steel strip approximately 0.1 mm thick as the barrier layer. The spacer takes the form of a hollow profile and is not rollable. Desiccant can be put into the hollow chamber within the hollow profile.

[0163] Specimen d) is a conventional spacer, available from Rolltech A/S under the name Multitech®. The spacer is made from a plastics hollow profile of styrene acrylonitrile polymer (SAN) with approximately 35 weight % of glass fibres (GF 35), relative to the total weight of the spacer, wherein there is applied to the outer surface of the spacer profile a metallised foil as the barrier layer. Desiccant can be put into the hollow chamber within the hollow profile. The spacer is not rollable.

[0164] Specimen e) is a conventional spacer for triple insulating glass units that is available from SWISSPACER Vetrotech Saint-Gobain (International) AG under the name SWISSPACER TRIPLE. The two intermediate spaces between the panes are each 16 mm in size. The thickness of the central pane is 2 mm. The spacer is likewise made from a plastics hollow profile with two hollow chambers made from SAN with approximately 35 weight % of glass fibres (GF 35), relative to the total weight of the spacer, and a metallised plastics foil as the barrier layer. Desiccant can be put into the hollow chambers within the hollow profile. The spacer is not rollable.

[0165] Specimen f) is a conventional spacer, available from Thermoseal Group under the name Thermobar®. The spacer is made from a plastics hollow profile of polypropylene with approximately 40 weight % of glass fibres (GF 40), relative to the total weight of the spacer, onto the outer surface of which a metallised foil is applied as the barrier layer. Desiccant can be put into the hollow chamber within the hollow profile. The spacer is not rollable.

[0166] Specimen g) is a conventional rollable spacer, available from Edgetech under the name Super Spacer® Premium. The spacer is formed as a solid profile and made from an expanded silicone material in which a desiccant (approximately 47 weight %) is embedded. Applied to the outer surface of the solid profile is a metallised foil as the barrier layer.

[0167] Specimen h) is a conventional rollable spacer based on polyurethane, available from Glasslam under the name WorldSpacer™. The spacer is formed as a solid profile and is made from an expanded polyurethane material in which a desiccant (approximately 45 weight %) is embedded. Applied to the outer surface of the solid profile is a stainless steel strip approximately 50 μm thick as the barrier layer.

[0168] Specimen i) is a conventional rollable spacer, available from the Soytas Group under the name Panaspacer. The spacer comprises a corrugated reinforcing element made from polycarbonate, which takes up the majority of the cross sectional surface. This reinforcing element is covered laterally and to the inside by a barrier layer. On the inside, above the barrier layer, is additionally a foam material in which desiccant is embedded. The manufacturer does not specify the proportion of desiccant.

[0169] Table 1 also shows the values of the Shore hardness D of the specimens according to the invention and the rollable specimens from the prior art, where these are available, for comparison.

TABLE-US-00001 TABLE 1 Intermediate space between Cross Width B × Weight Desiccant panes section height H per metre content Shore Polymer Specimen [mm] (schematic) [mm] × [mm] [g/m] [wt. %] hardness D material a) Inventive 2 × 12 + FIG. 7a   27 × 4.5 92.5 40 approx. 80 PP GF 20 profile central pane of 4 mm b) Inventive 16 FIG. 7b   16 × 4.5 50.5 40 approx. 77 PP GF 10 profile c) Chromatech 16 FIG. 7c 15.5 × 6.9 59.1 0 — PP Ultra F2 d) Multitech 16 FIG. 7d 15.5 × 6.5 45.5 0 — SAN GF 35 e) Swisspacer 2 × 16 + FIG. 7e   33 × 6.7 98.3 0 — SAN GF 35 Triple central pane of 2 mm f) Thermobar 16 FIG. 7f 15.5 × 6.5 44.9 0 — PP GF 40 g) Super Spacer 16 FIG. 7g 16.0 × 4.8 78 47 approx. 10 expanded Premium silicone h) Worldspacer 20 FIG. 7h 19.3 × 5.6 152.4 45 approx. 18 expanded PU i) Panaspacer 14 FIG. 7i 14.0 × 7.1 69.5 g ? approx. 17 polycarbonate

[0170] FIGS. 8A and 8B show the measurement results in the form of such force-displacement curves, for a selection of spacers a) and b) according to the present invention and c) to g) according to the prior art, measured in accordance with the test method variant A. The measurement curves for the specimens h) and i) are not shown, since their course corresponds substantially to the course of the curve of the specimen g), that is to say of a conventional rollable specimen.

[0171] FIG. 8C shows the measurement results in the form of force-displacement curves for the specimens a) and b) according to the invention and, according to the prior art, c) to e) and g) to i), wherein the conventional specimens g) to i) are rollable specimens. Here, measurement was in accordance with the test method variant B. The measurement curve for the specimen f) is not shown in FIG. 8C, since it coincides substantially with the curve of the specimen d).

[0172] FIG. 9A shows a further embodiment of a spacer 400 according to the invention, with a profiled body 402 that has a base body with a planar outer face 404 and parallel lateral faces 406 and 408 that are oriented perpendicularly to the outer face 404. Arranged on the outer face 404 is a vapour barrier layer 410 that extends from the first lateral face 406, over the outer surface 404 to the second lateral face 408, and forms the great majority of the lateral surfaces of the spacer. The inner face 412 of the base body (inner surface of the spacer), on the opposite side to the planar outer face 404, is concave in form and extends substantially from the first lateral face 406 to the second lateral face 408.

[0173] The ends of the lateral faces 406, 408 that are adjacent to the inner surface 412 have respectively outwardly protruding bead-like projections 414, 416 that, in the condition in which the spacer is installed in an insulating glass unit, abut directly against the glass panes and hold the lateral faces 406, 408, including the lateral surfaces formed by the vapour barrier layer 410, at a small spacing from the respective glass pane and thus create a defined space for receiving butyl adhesive compound. Further, in this way it is possible to prevent butyl adhesive compound from entering the inner space within the insulating glass unit and being visible there.

[0174] A further embodiment of a spacer 430 according to the invention is shown in FIG. 9B, wherein the spacer 430 once again has a profiled body 432 with a base body 434 and lateral faces 436, 438 that are laterally adjacent thereto. The lateral faces 436, 438 are oriented mutually parallel and substantially perpendicular to a planar outer surface 440.

[0175] Provided on the outer surface 440 is a vapour barrier layer 442 that extends from the first lateral face 436, over the outer surface 440 to the second lateral face 438 and, likewise, in large part covers the lateral faces 436, 438 and thus forms a large part of the lateral surfaces of the spacer 430.

[0176] Further, the base body 434 has an inner face 444 that has, centrally between the lateral faces 436, 438, a groove 446 that runs in the longitudinal direction of the spacer 430 and is delimited by two parallel projections 448, 449. The spacing between the free ends of the projections 448, 449 is preferably selected to be somewhat smaller than the width of the groove 446 in the region of its root. The groove 446 serves to receive a central, third glass pane (not illustrated) that divides the inner space of an insulating glass unit into two sub-volumes.

[0177] The inner face 444 (inner surface of the spacer 430) takes a concave form respectively in the regions between the lateral face 436 and the projection 448, and the lateral face 438 and the projection 449.

[0178] The ends of the lateral faces 436, 438 that are adjacent to the inner face 444 have respectively outwardly protruding bead-like projections 450, 452 that, in the condition in which the spacer is installed in an insulating glass unit, abut directly against the glass panes and hold the lateral faces 436, 438 at a small spacing from the respective glass pane and thus create a defined space for receiving butyl adhesive compound. Further, in this way it is possible to prevent butyl adhesive compound from entering the inner space within the insulating glass unit and being visible there.

[0179] Further, in the exemplary embodiment shown in FIG. 9B, there is applied to each of the lateral surfaces (in this case on the surface portions of the vapour barrier layer 442 that cover the lateral faces 436, 438) a volume 454, 456 of primary sealant (butyl adhesive compound) that is sufficient to ensure sealing and bonding between the glass pane to be supplied and the lateral surfaces of the spacer 430. Here, the primary sealant 454, 456 is illustrated in the uncompressed condition.

[0180] FIG. 9C shows a variant of the spacer 430 according to the invention from FIG. 9B.

[0181] The spacer 460 according to the invention in accordance with FIG. 9C has a profiled body 462 with a base body 464 and lateral faces 466, 468 that laterally delimit it. The lateral faces 466, 468 are oriented mutually parallel and substantially perpendicular to a planar outer surface 470.

[0182] Provided on the outer surface 470 of the spacer 460 is a vapour barrier layer 472 that extends from the first lateral face 466, over the outer surface 470 to the second lateral face 468 and, likewise, in large part covers the lateral faces 466, 468.

[0183] Further, the base body 464 has an inner face 474 that has, centrally between the lateral faces 466, 468, a groove 476 that runs in the longitudinal direction of the spacer 460 and is delimited by two parallel projections 478, 479. The spacing between the free ends of the projections 478, 479 is preferably selected to be somewhat smaller than the width of the groove 476 in the region of its root. The groove 476 serves to receive a central, third glass pane (not illustrated) that divides the inner space of an insulating glass unit into two sub-volumes.

[0184] The inner face 474 takes a concave form respectively in the regions between the lateral face 466 and the projection 478, and between the lateral face 468 and the projection 479, and is provided with ribs 480 that run mutually parallel and are spaced at regular intervals in the longitudinal direction of the spacer 460.

[0185] The ends of the lateral faces 466, 468 that are adjacent to the inner face 474 have respectively outwardly protruding bead-like projections 482, 484 that, in the condition in which the spacer 460 is installed in an insulating glass unit, abut directly against the glass panes and hold the lateral faces 466, 468 at a small spacing from the respective glass pane and thus create a defined space for receiving butyl adhesive compound. Further, in this way it is possible to prevent butyl adhesive compound from entering the inner space within the insulating glass unit and being visible there.

[0186] FIGS. 9D and 9E show the spacer 460 incorporated into a triple insulating glass unit 500 with two glass panes 502, 504, which are arranged on the outside, to either side of the spacer 460, against its lateral surfaces (lateral faces 466 and 468), and a central glass pane 506 that is inserted in the groove 476. The glass panes 502, 504 are bonded to the spacer 460 by a compressed primary butyl sealant 508, 509 that extends substantially over the entire lateral faces 466 and 468. Adjoining the compound of butyl sealant, a secondary sealant 510, 511 is applied in a wedge-shaped cross section at the outer edge of the respective glass pane 502 and 504 and portions of the outer surface 470 (FIG. 9D), or it extends as a continuous layer 512 at a substantially constant thickness over the entire outer surface 470 (FIG. 9E). The bead-like projections 482, 484 delimit the volumes of primary butyl adhesive in the direction of the inner space of the insulating glass unit 500.

[0187] As a result of the wedge-shaped application of the secondary sealant 510, 511 in FIG. 9D, by comparison with the conventionally used continuous application of the secondary sealant 512 in FIG. 9E, it is possible to save on a considerable quantity of secondary sealant. Moreover, thermal conduction in this region is reduced, so the Psi values for the edge bond are smaller.

[0188] The glass panes 502, 504 in FIG. 9E are, once again, bonded to the lateral faces of the spacer 460 by a primary sealant 508, 509.

[0189] FIG. 10 shows a further embodiment of a spacer 530 according to the invention, which has a profiled body 532 with a substantially planar base body 534 adjoined on either side by lateral walls 536, 538 having lateral faces 540, 542.

[0190] Slots 544 are introduced in the free ends of the lateral walls 536, 538 at regular intervals, perpendicularly to the longitudinal direction of the spacer 530. Likewise, at regular intervals in the outer face 546 of the base body 534 there are introduced slots 548, which extend perpendicularly to the longitudinal direction over the entire width of the base body 534.

[0191] As seen in the longitudinal direction of the spacer 530, the slots 544 and 548 are either arranged offset from one another, as illustrated, or else are in an identical position in the longitudinal direction (not shown). This formation of a spacer according to the invention allows the use of comparatively rigid plastics materials and where appropriate comparatively high contents of desiccant in the plastics material for formation of the profiled body, with the rollability of the spacer nonetheless being retained. Moreover, as a result of an appropriate configuration of these slots, the plastic deformations and restoring forces that may result from coiling can be reduced to such an extent that, simply by being bonded with primary sealant, the spacer remains in the desired position in relation to the glass panes until the secondary sealant, which is applied afterwards, has cured.

[0192] FIG. 11 shows a further embodiment of the present invention in the form of a spacer 560. The spacer 560 has a profiled body 562 with a base body 564 and two lateral walls 566, 568 that are integrally formed on the base body 564, to either side thereof, and provide the lateral faces 570, 572 of the profiled body 562.

[0193] The spacer 560 has on its outer surface 574 a barrier layer 576 that extends from the first lateral face 570, over the outer face of the base body to the lateral face 572, and also covers large parts of the lateral faces 570, 572, forming the lateral surfaces of the spacer 560.

[0194] Provided at the free ends of the lateral walls 566, 568 are functional elements that are integrally formed on the free ends as latching projections 578, 580 facing the respectively other lateral wall.

[0195] The latching projections 578, 580 are at a spacing from the inner face 582 of the base body 564 and are thus suitable for holding, with positive locking between them and the inner face 582, a separately manufactured component for the purpose of creating further functionalities for the spacer 560.

[0196] For the purpose of holding such components on the spacer 560 according to the invention with positive locking, it is possible to provide, as an alternative or in addition, grooves 584, 586 in the base body 566, in the region of the inner face 582.

[0197] FIG. 11 shows some variations of an exemplary component 590 that is suitable for creating further functionalities for the spacer 560, and which has a substantially strip-like base body 592 that can be held with positive locking by the latching projections 578, 580 such that it abuts against the inner face 582 in combination with the base body 564 of the spacer 560. In this arrangement, the component 590 extends from the one lateral wall 566 of the profiled body 562 to the other 568.

[0198] As an alternative or in addition, the base body 592 of the functional component 590 may be equipped with projections 596, 598 on its surface 594 that, in the mounted condition, faces the inner face 582, wherein the projections 596, 598 are preferably shaped to be complementary with the grooves 584, 586 in the base body 564 of the spacer 560, such that the projections 596, 598 are connectable to the grooves 584, 586 with positive locking.

[0199] On its opposite side to the surface 594 of the base body, the component 590 may have a centrally arranged receptacle 600 for a third glass pane (not illustrated). The spacer 560 can thus be used both for double glazing and triple glazing, and in the latter case needs only to be retrofitted with the functional component 590.

[0200] In a first variation, in the case of the functional component 590′ the receptacle 600′ can be arranged off-centre, with the result that it is possible, in a triple glazing produced therewith, to create an inner space between the panes that is divided into a smaller and a larger sub-volume.

[0201] In a second variant of the functional component 590″, it has, centrally, the receptacle 600″ for a third glass pane and moreover a structured surface with ribs 602″ that are spaced from one another regularly and mutually parallel and run in the longitudinal direction of the component 590″. This allows the spacer 560 to be modified in appearance on its surface that faces the inner space of the insulating glass unit and is thus visible in the installed condition.

[0202] In a third variant of the functional component 590′″, the receptacle 600′″ is positioned off-centre, and the surface is once again modified in appearance by ribs 602′″.

[0203] Because the functional components are manufactured separately, the choice of material for their manufacture is freely selectable. In particular, the material need not necessarily be selected depending on its coilability, since the functional components may indeed be connected to the spacer only immediately before manufacture of the spacer frame.

[0204] FIGS. 12A to 12C show further examples of spacers according to the invention that have functional elements by means of which further, customised functionalities may easily be created for the spacers where necessary.

[0205] FIG. 12A shows a spacer 622 according to the invention in the condition in which it is installed at the edge of an insulating glass unit 620. The spacer 622 has a first and a second glass pane 624, 626 at a predetermined spacing, and is firmly connected to these by a primary butyl sealant 628, 629 and a secondary sealant (for example polysulfide, polyurethane, silicone or hot melt butyl) 630, 631.

[0206] The spacer 622 has a profiled body 632 with a base body 634 and two lateral walls 636, 638 that are formed parallel to one another on either side of the base body 634 and of which the outer lateral faces form the lateral surfaces of the spacer 622, which are in contact with the glass panes 624, 626.

[0207] Integrally formed on its inner face 640 are functional elements in the form of latching projections 642, 644, and these protrude perpendicularly from the base body 634 of the profiled body 632 and extend parallel and mutually spaced in the longitudinal direction of the spacer. Formed between the latching projections 642, 644 is a groove-like receptacle 646 in which a functional component 648 can be inserted and held with positive locking by the latching projections 642, 644.

[0208] In the present exemplary embodiment, the functional component 648 is intended to have a plurality of functions. A first function consists in providing a groove 650 for receiving the edge of a third glass pane 652. Further functions are taken on by two planar elements 654, 656, which extend in opposite directions on either side of the groove 650, towards the first and the second glass pane. The planar elements 654, 656 on the one hand cover the inner face of the base body 634 and so provide the possibility of modifying the appearance of the spacer 622. Moreover, the planar elements 654, 656 of the functional component 648 create fillable cavities on their sides facing the profiled body 632, which in the present exemplary embodiment are charged with desiccant bodies 658, 660 that provide an additional moisture absorption capacity. The desiccant bodies 658, 660 may in this case fill the cavities entirely or—as shown here—partly, as required.

[0209] The spacer 622 may be equipped with a stainless steel strip 662 on its outer surface. The stainless steel strip 662 takes on the function of a barrier layer that extends rectilinearly, substantially from the first glass pane 624 to the second glass pane 626, and projects somewhat towards the lateral faces. As a result, a barrier layer on the lateral faces can be dispensed with, since the primary butyl sealant also adjoins the stainless steel strip from below and, together with the stainless steel strip, creates a continuous sealing plane. Because of the planar form taken by the stainless steel strip 662, a relatively large material thickness can be used for it, with the spacer nonetheless remaining readily coilable.

[0210] FIG. 12B shows an edge region of an insulating glass unit 670 having two glass panes 674, 676 that are held at a spacing by a spacer 672 according to the invention.

[0211] A secondary sealant 680 is applied to the outer surface 678 of the spacer 672, extending in the transverse direction of the insulating glass unit 670 over the entire width of the spacer 672, from the glass pane 674 to the glass pane 676. Provided between the lateral walls 686, 688 and the glass panes is a primary butyl sealant 710, 711.

[0212] The spacer has a profiled body 682 with a base body 684 on either side of which lateral walls 686, 688 are integrally formed. Integrally formed on the base body 684, on the inner face thereof remote from the outer surface 678, are two strip-like latching projections 690, 692 that form a receptacle 694 between them. A functional component 695 can be inserted with positive locking in the receptacle 694.

[0213] Here, similarly to the embodiment shown in FIG. 12A, the functional component 695 has a plurality of functions. First, the functional component 695 forms a receiving groove 696 in which a third glass pane 698 can be inserted by means of its edge region. Further, two planar elements 700, 702 that extend from the region of the groove 696 in both directions to the glass panes 674, 676 and the lateral walls 686, 688 form, together with the profiled body 682 of the spacer 672, closed hollow chambers on either side of the latching projections 690, 692, which can be charged with desiccant bodies 704, 706 in order to adjust the moisture absorption capacity of the spacer 672 to a predetermined value. Moreover, the planar elements 700, 702 serve to create the appearance taken by the spacer 672 on its visible side in the mounted condition.

[0214] It is possible for a web-like projection 708 to be provided in the receiving groove 696 so that the central glass pane 698 is not pushed right to the root of the groove during assembly. As a result of the corresponding configuration of the projection 708, it is possible for it to be compressed in the event of a high degree of thermal expansion of the central pane. This is particularly important in the case of panes made of plastics material, which have considerably greater thermal expansion than glass panes. In this case the projection 708 acts in the manner of a spring that can be compressed when necessary.

[0215] Finally, FIG. 12C shows an edge region of an insulating glass unit 720 having two glass panes 724, 276 that are held at a spacing by a spacer 722 according to the invention.

[0216] A secondary sealant 730 is applied to the outer surface 728 of the spacer 722, extending in the transverse direction of the insulating glass unit 720 over the entire width of the spacer 722, from the glass pane 724 to the glass pane 726. Provided between the lateral walls 736, 738 and the glass panes 724, 726 is a primary butyl sealant 748, 749.

[0217] The spacer 722 has a profiled body 732 with a base body 734 on either side of which lateral walls 736, 738 are integrally formed. Integrally formed on the base body 734, on the inner surface thereof remote from the outer surface 728, are two strip-like latching projections 740, 742 that form a receptacle 744 between them. A third glass pane 746 can be inserted in the receptacle 744 with positive locking.

[0218] Further, the profiled body 732 of the spacer 722 has two planar elements 750, 752 that extend from the region of the projections 740, 742 forming the groove 744 in both directions to the glass panes 724, 726 and the lateral walls 736, 738 and, together with the base body 734 of the spacer 722, form substantially closed hollow chambers on either side of the projections 740, 742, which can be charged with desiccant bodies 754, 756 in order to adjust the moisture absorption capacity of the spacer 722 to a predetermined value. Moreover, the planar elements 750, 752 serve to create the appearance taken by the spacer 722 on its visible side in the mounted condition.

[0219] FIGS. 13A to 13F, by means of a spacer 10 according to the invention as seen in FIG. 1A, show different ways of joining together end regions of a spacer according to the invention. This applies both to the end regions of coiled spacers and to the end regions of a portion of a spacer that has already been cut to length in order to form a frame of an insulating glass unit.

[0220] FIG. 13A illustrates the production of a butt joint 800 of spacer end regions 802, 804 by means of plastics welding, for example using an ultrasound welding or mirror welding technique. The upper part of the illustration is a sectional view perpendicular to the longitudinal direction of the spacer. The central part of the illustrations shows the spacer end regions 802, 804 in a plan view of the base body 18, and the illustrations to the side thereof respectively show a lateral view of the lateral walls 14 and 16. The welded butt joint 800 preferably extends from a lateral wall 14, over the base body 18 to the lateral wall 16.

[0221] FIG. 13B illustrates the production of a further variant of a butt joint 810 of modified spacer end regions 812, 814 by means of plastics welding, for example using an ultrasound welding or mirror welding technique, or indeed using an adhesive technique, for example with the aid of a metal adhesive tape (not illustrated). The two end regions 812, 814 are respectively provided with complementary projections and recesses 816, 818 (for example for a tongue-and-groove connection).

[0222] Once again, the central part of the illustrations shows the spacer end regions 812, 814 in a plan view of the base body 18, and the illustrations to the side thereof respectively show a lateral view of the lateral walls 14 and 16. The welded butt joint 810 preferably extends from a lateral wall 14, over the base body 18 to the lateral wall 16.

[0223] FIG. 13C illustrates the production of a further variant of a butt joint 820 of spacer end regions 822, 824 by means of a positively locking clip connection, which where appropriate may additionally be secured by plastics welding, for example using an ultrasound welding or mirror welding technique, or indeed using an adhesive technique, for example with the aid of a metal adhesive tape (not illustrated).

[0224] Once again, the central part of the illustrations shows the spacer end regions 822, 824 in a plan view of the base body 18, and the illustrations to the side thereof respectively show a lateral view of the lateral walls 14 and 16. The butt joint 820, where appropriate secured by welding, preferably extends from a lateral wall 14, over the base body 18 to the lateral wall 16.

[0225] FIG. 13D illustrates the production of a further variant of a butt joint 830 of spacer end regions 832, 834 by means of a positively locking clip connection, which where appropriate may be secured by plastics welding, for example using an ultrasound welding or mirror welding technique, or indeed using an adhesive technique, for example with the aid of a metal adhesive tape (not illustrated). For this purpose, the end regions 832, 834 are provided with complementary projections and recesses 836, 838 in the region of the lateral walls 14, 16, in a manner analogous to the variant of FIG. 13B.

[0226] Once again, the central part of the illustrations shows the spacer end regions 832, 834 in a plan view of the base body 18, and the illustrations to the side thereof respectively show a lateral view of the lateral walls 14 and 16. The butt joint 830, where appropriate additionally secured by welding, preferably extends from a lateral wall 14, over the base body 18 to the lateral wall 16.

[0227] FIG. 13E illustrates the production of a further variant of a butt joint 840 of spacer end regions 842, 844 by means of a positively locking connection (in this case a dovetail joint in the region of the base body 18), which where appropriate may additionally be secured by plastics welding, for example using an ultrasound welding or mirror welding technique, or indeed using an adhesive technique, for example with the aid of a metal adhesive tape (not illustrated).

[0228] Once again, the central part of the illustrations shows the spacer end regions 842, 844 in a plan view of the base body 18, and the illustrations to the side thereof respectively show a lateral view of the lateral walls 14 and 16. The butt joint 840, where appropriate additionally secured by welding, preferably extends from a lateral wall 14, over the base body 18 to the lateral wall 16.

[0229] FIG. 13F illustrates the production of a further variant of a butt joint 850 of spacer end regions 852, 854 by means of a positively locking hook-and-clip connection of the lateral walls 14, 16, which for this purpose are provided at the end regions 852, 854 with hook-shaped complementary projections and recesses 856, 858. Where appropriate, the butt joint 850 may additionally be secured by plastics welding, for example using an ultrasound welding or mirror welding technique, or indeed using an adhesive technique, for example with the aid of a metal adhesive tape (not illustrated).

[0230] Once again, the central part of the illustrations shows the spacer end regions 852, 854 in a plan view of the base body 18, and the illustrations to the side thereof respectively show a lateral view of the lateral walls 14 and 16. The butt joint 850, where appropriate secured by welding, preferably extends from a lateral wall 14, over the base body 18 to the lateral wall 16.

[0231] It is common to all embodiments in FIG. 13 that the spacer end regions can be held in position against one another when a spacer frame is closed, as a result of which manufacture of the insulating glass units is simplified.

[0232] Moreover, the connection techniques shown can also be used to use up offcut pieces of spacers when a spacer frame is manufactured.

[0233] The connection techniques shown with reference to the spacer 10 in FIG. 13 can also be used analogously on all spacers according to the invention, in particular also on spacers according to the invention that have a relatively complex geometry, such as that of the spacers 120 and 460 in FIGS. 3A and 9C respectively.