HIGH-ENTROPY ALLOY FOAM AND MANUFACTURING METHOD FOR THE FOAM

Abstract

The present invention relates to a HEA foam prepared by selective dissolution of a second phase within a two-phase separating alloy comprising the HEA and a manufacturing method thereof. The manufacturing method of the HEA foam of the present invention has the effect of preparing a novel HEA foam, which was not available in the past, by leaving only a first phase after manufacturing a two-phase separating alloy comprising a first phase by HEA, wherein at least 3 metal elements act as a common solvent.

Furthermore, the HEA foam of the present invention has a structure, wherein pores are distributed inside the HEA, in which at least 3 metal elements act as a common solvent. By adding a functional characteristic of low heat conductivity, etc., to the existing high strength characteristic of HEA, the HEA foam of the present invention can exhibit a complex effect by the combination of the two particular effects, thereby being capable of exhibiting excellent physical characteristics.

Claims

1. A two-phase separating alloy, comprising: a first phase comprising a high-entropy alloy (HEA) material, in which at least 3 metal elements act as a common solvent; and a second phase comprising at least one metal element (M).

2. The two-phase separating alloy of claim 1, wherein: all metal elements comprised in the high-entropy alloy (HEA) material on the first phase have an equiatomic ratio within an error range of 10 at. %.

3. The two-phase separating alloy of claim 1, wherein: the first phase has a dendritic structure and the second phase is located in interdendritic regions.

4. The two-phase separating alloy of claim 1, wherein: the high-entropy alloy (HEA) material on the first phase comprises at least 3 metal elements among Cr, Mn, Fe, Co, and Ni; the high-entropy alloy (HEA) material has a face-centered cubic crystal structure; and the metal element material (M) on the second phase comprises at least one metal element among Cu, Ag, and Au.

5. The two-phase separating alloy of claim 4, wherein: the high-entropy alloy (HEA) material and the metal element material (M) are represented by a composition ratio of M.sub.100-x(HEA).sub.x (with the proviso, 5≦x≦90 at. %).

6. The two-phase separating alloy of claim 4, wherein: the high-entropy alloy (HEA) material further comprises at least one metal element among Ti, V, and Al; and at least one metal element among Ti, V, and Al, is comprised 15 at. % or less relative to the high-entropy alloy (HEA) material.

7. The two-phase separating alloy of claim 4, wherein: the high-entropy alloy (HEA) material further comprises at least one metal element among B, Si, Y, Zr, Nb, Mo, Ta, W, and Bi; and at least one element among B, Si, Y, Zr, Nb, Mo, Ta, W, and Bi is comprised 10 at. % or less relative to the high-entropy alloy (HEA) material.

8. The two-phase separating alloy of claim 1, wherein: the high-entropy alloy (HEA) material on the first phase comprises at least one metal element among Ti, V, and Cr, and at least one metal element among Zr, Nb, Mo, Hf, Ta, and W; the high-entropy alloy (HEA) material has a body-centered cubic crystal structure; and the metal element material (M) on the second phase comprises at least one metal element among Y, La, Ce, Nd, Gd, Tb, Dy, Ho, and Er.

9. The two-phase separating alloy of claim 8, wherein: the high-entropy alloy (HEA) material and the metal element material (M) are represented by a composition ratio of M.sub.100-x(HEA).sub.x (with the proviso, 1≦x≦25 at. %).

10. The two-phase separating alloy of claim 8, wherein: the high-entropy alloy (HEA) material further comprises at least one metal element among B, C, N, Al, and Si; and at least one element among B, C, N, Al, and Si is comprised 10 at. % or less relative to the high-entropy alloy (HEA) material.

11. A manufacturing method of a HEA foam, comprising: a step for preparing a raw material for preparing at least 3 metal elements that constitute a high-entropy alloy (HEA) material and at least one metal element material (M) having a positive (+) heat of mixing relationship with at least 3 metal elements that constitute the high-entropy alloy (HEA) material; a step for preparing an alloy for preparing a two-phase separating alloy, wherein a first phase comprising the high-entropy alloy (HEA) material and a second phase comprising at least one metal element (M) are separated from each other, by dissolving all the metal elements comprised in the step for preparing an alloy followed by cooling; and a step for selectively removing only the second phase and forming pores.

12. The manufacturing method of claim 11, wherein: in the step for preparing the alloy, the first phase has a dendritic structure and the second phase is located in interdendritic regions; and in the step for preparing pores, the second phase is removed from the two-phase separating alloy and thus pores, which are located in the interdendritic regions, are formed.

13. The manufacturing method of claim 11, wherein: in the step for preparing pores, the second phase is removed through an electrochemical dealloying process using nitric acid.

14. HEA foam comprising a high-entropy alloy (HEA) material, in which at least 3 metal elements act as a common solvent, and pores located therein.

15. The HEA foam of claim 14, wherein: the HEA foam has a dendritic structure.

16. The HEA foam of claim 14, wherein: the high-entropy alloy (HEA) material comprises at least 3 metal elements among Cr, Mn, Fe, Co, and Ni; and the high-entropy alloy (HEA) material has a face-centered cubic crystal structure.

17. The HEA foam of claim 16, wherein: the high-entropy alloy (HEA) material further comprises at least one metal element among Ti, V, and Al; and at least one metal element among Ti, V, and Al, is comprised 15 at. % or less relative to the high-entropy alloy (HEA) material.

18. The HEA foam of claim 16, wherein: the high-entropy alloy (HEA) material further comprises at least one metal element among B, Si, Y, Zr, Nb, Mo, Ta, W, and Bi; and at least one element among B, Si, Y, Zr, Nb, Mo, Ta, W, and Bi is comprised 10 at. % or less relative to the high-entropy alloy (HEA) material.

19. The HEA foam of claim 14, wherein: the high-entropy alloy (HEA) material comprises at least one metal element among Ti, V, and Al; and at least one metal element among Zr, Nb, Mo, Hf, Ta, and W; and the high-entropy alloy (HEA) material has a body-centered cubic crystal structure.

20. The HEA foam of claim 19, wherein: the high-entropy alloy (HEA) material further comprises at least one metal element among B, C, N, Al, and Si; and at least one element among B, C, N, Al, and Si is comprised 10 at. % or less relative to the high-entropy alloy (HEA) material.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0043] FIG. 1 is a flowchart schematically illustrating the process of the present invention.

[0044] FIG. 2 shows the heat of mixing relationship between elements constituting the element group I and the element group II, which constitute the two-phase separating FCC HEA.

[0045] FIG. 3 shows the results of scanning electron microscope and X-ray spectroscopic analysis with respect to Example 2 among the high-entropy two-phase separating alloys prepared by alloying the elements which constitute the element group I and the element group II.

[0046] FIG. 4 shows the XRD analysis results with respect to Examples 1 to 5.

[0047] FIG. 5 shows a table illustrating the heat of mixing relationship between the elements constituting the element group Ill, the element group IV, and the element group V, which constitute the two-phase separating BCC HEA.

[0048] FIG. 6 is a diagram comparing the amounts of heat of mixing and atoms between the element group Ill, the element group IV, and the element group V, confirming the large differences in the amount of atoms between each element group.

[0049] FIG. 7 shows (a) a concept diagram with respect to the process for forming a two-phase separating alloy having an interdendritic composite structure of the present invention and (b) images of the compositions of Comparative Example 14 and Example 20 observed under scanning electron microscope and the results of energy dispersive spectroscope (EDS) component analysis.

[0050] FIG. 8 shows the results of XRD analysis for Examples 17, 20, and 23.

[0051] FIG. 9 shows a schematic diagram illustrating that a high-entropy foam can be prepared from a prepared two-phase separating alloy in a nitric acid solution via dealloying.

[0052] FIG. 10 shows the actual analysis results of the surface of Example 20 observed under scanning electron microscope before and after performing a dealloying process.

[0053] FIG. 11 shows the XRD analysis results of Examples 2 and 20 before and after performing a dealloying process.

[0054] FIG. 12 shows the cross-sectional images of the high-entropy alloy foam prepared in Example 20 illustrating the difference in depth of formed foams from the surface according to the dealloying time.

[0055] FIG. 13 shows the measurement results of thermal diffusion coefficient (a, thermal diffusivity) with regard to the two-phase separating alloy prepared in Example 2 and the alloy prepared in Comparative Example 4 and the alloy foam prepared in Example 2.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0056] Examples according to the present invention are explained in detail with reference to the accompanying drawings.

[0057] FIG. 1 is a flowchart schematically illustrating the entire process for obtaining HEA foam of the present invention.

[0058] First, the two-phase separating alloy including the high-entropy alloy (HEA) according to Examples includes a first phase L1, which includes HEA where constituting elements of at least 3 components act as a common solvent and constitute a solid solution, and a second phase L2 which includes a separate metal material apart from the first phase, and the first phase and the second phase are separated from each other and co-present.

[0059] The HEA foam according to Examples are prepared by removing the second phase by selectively dealloying from the two-phase separating alloy including the HEA described above.

[0060] Here, the two-phase separating alloy can be divided into two types; HEA, which has an FCC crystal structure, and HEA, which has a BCC crystal structure. The process of designing the alloys is as follows.

[0061] Design of Two-Phase Separating FCC HEA

[0062] The step relates to designing a two-phase separating HEA with a face-centered cubic crystal structure, i.e., an FCC crystal structure. First, as the element group II constituting the FCC HEA which forms the first phase, at least 3 metal elements may be selected from Ni, Co, Cr, and Mn.

[0063] Next, the element group I, which is a major element for forming the second phase and mostly has a positive (+) heat of mixing relationship with the constituting elements may be at least one metal element selected from Cu, Ag, and Au.

[0064] FIG. 2 is a table summarizing the heat of mixing relationship between the elements reviewed in the present exemplary embodiment.

[0065] A heat of mixing relationship may be established between Fe, Ni, Co, Cr, and Mn, which are the elements constituting the first phase of HEA, where the difference in enthalpy of mixing (ΔH.sub.mix) is ±10 or less kJ/mole of atom, and Cu, Ag, and Au have a positive (+) heat of mixing relationship with elements, which constitute HEA, and thus can be easily separated.

[0066] Here, Fe, Ni, Co, Cr, and Mn, which are the constituting elements for the first phase have the heat of mixing relationship in the range of about +2 kJ/mol to about −7 kJ/mol (ΔH.sub.mix≦±10 kJ/mole of atom) with each other. Additionally, Fe, Ni, Co, Cr, and Mn have a similar atomic radius in the range of about ±10% as shown in Table 1 below. Accordingly, Fe, Ni, Co, Cr, and Mn can easily form a HEA solid solution.

TABLE-US-00001 TABLE 1 Element Cr Mn Fe Co Ni Atomic radius (pm) 166 139 156 152 149

[0067] For example, Cu has a relatively large positive (+) heat of mixing relationship with each of Fe, Ni, Co, Cr, and Mn. Accordingly, Cu may have a miscibility gap with HEA that induces the separation of a liquid (the separation of the first phase and the second phase) and a monotectic reaction (L.fwdarw.a HEA solid solution+L2) may occur. Additionally, since the tie-line of the monotectic reaction is formed over a broad composition range, the phase between HEA and Cu can be easily separated at the time of solidification.

[0068] Preparation of Two-Phase Separating FCC HEA

[0069] A two-phase separating alloy including HEA can be prepared by an arc melting method.

[0070] Since the arc melting method embody high temperature via arc plasma, a homogeneous solid solution in bulk shape can be rapidly formed, and minimize the impurities such as oxides and pores, and thus selected. In addition to the arc melting method, it may be prepared using a commercial casting process by utilizing an induction casting method which has an agitation effect by electromagnetic field during dissolution and resistance heating method capable of precise temperature control. Furthermore, a commercial casting method capable of dissolving high melting point metals may be used, and may be prepared by spark plasma sintering via powder metallurgy after preparing raw materials in powder, etc., or by sintering at high temperature/high pressure using hot isostatic pressing sintering. Here, the sintering method has a merit in that the method enables a more precise control of microstructures and preparation of parts with a desired shape.

[0071] The following Table 2 shows compositions of Comparative Examples and the phases represented by the compositions for the comparison with those in Examples according to the present invention.

TABLE-US-00002 TABLE 2 Specimen Composition Crystal Structure Example 1 Cu.sub.20(FeNiCo).sub.80 2 phase FCC (L1 + L2) Example 2 Cu.sub.20(FeNiCoCr).sub.80 2 phase FCC (L1 + L2) Example 3 Cu.sub.20(FeNiCoCrMn).sub.80 2 phase FCC (L1 + L2) Example 4 CuFeNiCoCrMnV.sub.0.5 2 phase FCC (L1 + L2) Example 5 CuFeNiCoCrMnTi.sub.0.5 2 phase FCC (L1 + L2) Example 6 CuFeNiCoCrMnAl.sub.0.5 2 phase FCC (L1 + L2) Example 7 Cu.sub.90(FeNiCoCr).sub.10 2 phase FCC (L1 + L2) Example 8 Cu.sub.80(FeNiCoCr).sub.20 2 phase FCC (L1 + L2) Example 9 Cu.sub.70(FeNiCoCr).sub.30 2 phase FCC (L1 + L2) Example 10 Cu.sub.60(FeNiCoCr).sub.40 2 phase FCC (L1 + L2) Example 11 Cu.sub.50(FeNiCoCr).sub.50 2 phase FCC (L1 + L2) Example 12 Cu.sub.40(FeNiCoCr).sub.60 2 phase FCC (L1 + L2) Example 13 Cu.sub.30(FeNiCoCr).sub.70 2 phase FCC (L1 + L2) Example 14 Cu.sub.10(FeNiCoCr).sub.90 2 phase FCC (L1 + L2) Comparative Ni Single FCC Example 1 Comparative NiCo Single FCC Example 2 Comparative FeNiCo Single FCC Example 3 Comparative FeNiCoCr Single FCC Example 4 Comparative FeNiCoCrMn Single FCC Example 5 Comparative Cu Single FCC Example 6 Comparative Cu.sub.20Ni.sub.80 Single FCC Example 7 Comparative CuFe FCC Fe + FCC Cu Example 8 Comparative CuNiCo Single FCC Example 9 Comparative Cu.sub.20(FeNi).sub.80 Single FCC Example 10

[0072] FIG. 3 shows images observed under scanning electron microscope with respect to Example 2 and the phase separating phenomenon can be confirmed by the difference in clear contrast between each phase. That is, the dark region in FIG. 3 represents the first phase part by HEA, and the bright part represents the second phase part by Cu, and these can be confirmed by X-ray spectroscopic analysis and energy dispersive X-ray spectroscopy (EDS).

[0073] Such a phenomenon can be more explicitly confirmed by an analysis using X-ray. FIG. 4 shows the results of XRD analysis with respect to Examples according to the present invention. Here, Cu which has a positive heat of mixing with the FCC HEA, which has a composition of Fe—Ni—Co, Fe—Ni—Co—Cr, and Fe—Ni—Co—Cr—Mn, was analyzed by 20% alloying relative to HEA. In fact, the alloys of Example 1 to 3 showed peaks which represent the results of phase separation into L1 and L2, however, in the cases of Comparative Examples 7 and 10, where phase-separation HEA cannot be constituted, phase separation was not observed.

[0074] The two-phase separating alloy including HEA according to the present invention may further include at least one an element among Ti, V, and Al in an amount of about 15 at. % or less relative to the entire alloy element (Examples 4 to 6). Examples 4 to 6 can also have structures with two-phase separation.

[0075] Examples 7 to 15 show the cases where the composition ratio between HEA and Cu in two-phase separating alloys of Fe—Ni—Co—Cr HEA and Cu was controlled. As the result of XRD analysis, in Examples 7 to 15 where the Cu ratio was shown to vary from about 10 at. % to about 90 at. %, the peaks by both L1 and L2 phases were observed thus confirming the formation of two-phase separating alloys. That is, even in cases where the Cu ratio was variously changed from about 5 at. % to about 90 at. % in the amphiphilic composition range of tie-line including a monotectic reaction, the phenomenon of separation of the first phase L1 and the second phase L2 can be maintained, wherein the microstructures may be altered depending on the Cu ratio.

[0076] Furthermore, the two-phase separating alloys according to Examples may exhibit unique physical characteristics because the physical property included in the second phase is combined to the excellent physical property of HEA as the L1 phase by HEA and the L2 phase by a metal are separated.

[0077] For example, the electric conductivity of Cu may be combined to HEA thereby exhibiting extremely excellent electric conductivity. The alloy with the FeCoCrNiCu composition corresponding to Example 2 exhibited a unique characteristics with excellent micro-strength and electric conductivity compared to the existing conventional alloys.

[0078] Meanwhile, the two-phase separating alloy including HEA may further include heterogeneous elements for the control of mechanical properties of HEA via precipitation. For example, a two-phase separating alloy including HEA may include at least one an element selected from B, Si, Y, Zr, Nb, Mo, Ta, W, and Bi in an amount of about 10 at. % or less relative to that of HEA, and thereby, the mechanical characteristic can be improved while maintaining the L1 phase of HEA and the L2 phase of a metal. For example, heterogeneous elements can strengthen alloys by making a trace amount of deposition.

[0079] Design of Two-Phase Separating BCC HEA

[0080] Similarly to the FCC HEA described above, the two-phase separating BCC HEA can also exhibit a phase-separation effect within the amphiphilic composition of the tie-line including a monotectic reaction by an appropriate design of alloys. The two-phase separating alloy including HEA includes a first phase of BCC HEA, where at least 3 constituting elements act as a common solvent via control of a miscibility gap formed within the alloy of BCC HEA thereby constituting a solid solution, and a second phase, which is a composition material immiscible with the first phase, wherein the first phase and the second phase are separated from each other.

[0081] First, the BCC HEA to form the first phase of the two-phase separating alloy including HEA may include at least 3 metal elements among Ti, V, Cr, Zr, Nb, Mo, Hf, Ta, and W.

[0082] Here, in order to prevent that the first phase of BCC HEA forms an extreme layered structure and becomes separated due to the difference in density with the immiscible metal (or alloy) constituting the second phase, Ti, V, and Cr, which are elements having an atomic amount lower than that of Y, may be classified into element group IV, whereas, Zr, Nb, Mo, Hf, Ta, and W, which are elements having an atomic amount higher than that of Y, may be classified into element group V.

[0083] The first phase of the two-phase separating alloy including HEA includes at least one kind of an element from the element group IV and must include at least one kind of an element from the element group V.

[0084] The second phase includes Y and at least one kind of lanthanide element such as La, Ce, Nd, Gd, Tb, Dy, Ho, and Er, which have a relatively large positive (+) heat of mixing relationship with the constituting elements of the first phase, and these elements are classified into the element group III.

[0085] FIG. 5 is a table in which the heat of mixing relationship of elements that constitute the present invention are summarized.

[0086] Referring to FIG. 5, it can be seen that the elements of Ti, V, Cr, Zr, Nb, Mo, Hf, Ta, and W, which constitute the BCC HEA of the first phase, have a similar heat of mixing relationship where the difference of enthalpy of mixing (ΔH.sub.mix) is within the range of about ±10 kJ/mole of atom. In contrast, it can be confirmed that Y and the elements of the lanthanides described above have a large amount of heat of mixing relationship with the elements of Ti, V, Cr, Zr, Nb, Mo, Hf, Ta, and W, which constitute the BCC HEA of the first phase, in an amount of about +10 kJ/mole of atom or higher, respectively.

[0087] FIG. 6 shows a diagram illustrating the element group III, the element group IV, and the element group V, in which the elements constituting the present invention are classified according to the atomic amount and heat of mixing relationship. As can be seen in this diagram, there is a big difference in atomic amount between the element group III and the element group V and thus an extreme phase-separation behavior due to a difference in density may occur. In order to prevent such a phenomenon and embody the microstructure of a uniform composite alloy, a design of an alloy was performed such that, among the metal elements that constitute the BCC HEA, those elements which have atomic amount smaller than that of Y, which is an alloy element constituting an immiscible region, was classified into the element group IV while those elements which have atomic amount greater than that of Y was classified into the element group V, and at least one element from each group should be included in the alloy.

[0088] As can be seen in the diagram, it was confirmed that there is a similar heat of mixing (ΔH.sub.mix≦±10 kJ/mole of atom) relationship in the range of about −6 to about +2 kJ/mol between the constituting elements, exclusive of Y, and as shown in Table 3 below, it was confirmed that each of the alloying elements has a similar difference of ±10% or less in atomic radius and is thus a suitable condition for constituting HEA.

TABLE-US-00003 TABLE 3 Element Ti V Cr Zr Nb Mo Hf Ta W Atomic 200 192 200 230 208 201 225 209 210 radius (pm)

[0089] In contrast, for example, Y has a big positive (+) heat of mixing relationship in the amount of about +15 kJ/mole of atom or higher with all the elements constituting the HEA with a body-centered cubic crystal structure. Accordingly, in the case of an alloy, which is prepared by a combination of BCC HEA (the first phase), which consists of the element group IV and the element group V, and the element group III (the second phase), the first phase and the second phase may be easily separated when a melt solution is solidified.

[0090] Preparation of Two-Phase Separating BCC HEA

[0091] The two-phase separating alloy including HEA may be prepared by arc melting method. Meanwhile, hereinafter, among the Y and lanthanide elements which constitute the element group III, the description has been mostly focused on Y, which shows a representative characteristic in the heat of mixing relationship with the element group V, atomic amount, etc., but the exemplary embodiments are not limited thereto.

[0092] Since arc melting method is explained in detail above and is thus omitted herein below.

[0093] The following Table 4 shows each of the compositions in Examples and Comparative Examples and the crystal structures on the phase and microstructures on the phase that appear when each composition is solidified.

TABLE-US-00004 TABLE 4 Microstructure Composition Crystal Structure Shape Example 15 Y—Ti—MoNb 2 phase (BCC + Interdendritic HCP) composite structurization Example 16 Y—Ti—MoNbHf 2 phase (BCC + Interdendritic HCP) composite structurization Example 17 Y—Ti—MoNbHfTa 2 phase (BCC + Interdendritic HCP) composite structurization Example 18 Y—TiV—Mo 2 phase (BCC + Interdendritic HCP) composite structurization Example 19 Y—TiV—MoNb 2 phase (BCC + Interdendritic HCP) composite structurization Example 20 Y—TiV—MoNbTa 2 phase (BCC + Interdendritic HCP) composite structurization Example 21 Y—TiVCr—Mo 2 phase (BCC + Interdendritic HCP) composite structurization Example 22 Y—TiVCr—MoNb 2 phase (BCC + Interdendritic HCP) composite structurization Example 23 Y—TiVCr—MoNbTa 2 phase (BCC + Interdendritic HCP) composite structurization Comparative VNbMoTaW Single phase A single solid Example 11 (BCC) solution of BCC Comparative NbMoHfTaW Single phase A single solid Example 12 (BCC) solution of BCC Comparative Y—MoNb 2 phase (BCC + Solidification Example 13 HCP) with a separate alloy with a layered structure Comparative Y—MoNbTa 2 phase (BCC + Solidification Example 14 HCP) with a separate alloy with a layered structure

[0094] FIG. 7 shows (a) a concept diagram with respect to the process for forming a two-phase separating alloy having an interdendritic composite structure of the present invention and (b) images of the compositions of Comparative Example 14 and Example 20 observed under scanning electron microscope and the results of energy dispersive spectroscope (EDS) component analysis.

[0095] As can be seen in FIG. 7(a), in the HEA which consists of only the elements of the element group V, the layered separation phenomenon that it is extremely separated due to the difference in atomic amount with the Y element of the element group III can be confirmed, and thus, a two-phase separating alloy having a composite interdendritic structure cannot be prepared. Accordingly, the two-phase separating alloy including HEA should surely include the element group IV, which has a relatively small atomic amount and is easy to form BCC HEA by easily forming a solid solution with the element group V, and by doing so, an interdendritic composite structure between the first phase, which includes BCC HEA, and the second phase, which includes a metal immiscible with the first phase, can be formed.

[0096] FIG. 7(b) shows the scanning electron microscope and energy dispersive spectroscope (EDS) component analysis results of the Y—MoNbTa composition of Comparative Example 14 and the Y—TiV—MoNbTa composition of Example 20. As can be seen above, in the case of the alloy with the composition of Comparative Example, the Y-rich phase and the BCC HEA phase with the MoNbTa composition had a layered structure and an extremely separated alloy was formed, whereas, in the case of the composition of Example 20 where Ti and V, elements of the element group IV, were added to Comparative Example 4, a preferable microstructure with an interdendritic composite structure was obtained.

[0097] Here, FIG. 8 shows the results of XRD analysis with regard to the phase-separation BCC HEA including one to three elements of the element group IV, respectively, and correspond to Examples 17, 20, and 23. It was confirmed that a two-phase separating behavior with a BCC-HCP crystal structure between the first phase of the BCC HEA composition and the second phase of Y-rich phase, by performing the alloying by selecting at least one kind of element Y selected from the element group III, 1 to 3 kinds of elements selected from the element group IV, and at least 2 kinds of elements selected from the element group V, through each of the analysis results.

[0098] From the above results of X-ray diffraction analysis, it was confirmed that in the present invention, regardless of the number of elements in each element group, an interdendritic composite structured two-phase separating alloy, consisting of the dendritic region of the BCC HEA composition, which consists of the element group IV and the element group V, and the dendritic region mainly consisting of the element group I.

[0099] Furthermore, in the two-phase separating alloy of the present invention, the first phase including the BCC HEA and the second phase including a metal (or alloy) which is immiscible with the first phase are composite structured and thus the physical property of the immiscible metal is combined with the excellent mechanical properties of the BCC HEA, thereby improving the unique physical characteristics.

[0100] Meanwhile, the two-phase separating alloy including HEA may further include at least one an element selected from B, C, N, Si, and Al in an amount of 10 at. % or less relative to that of HEA, for the control of mechanical properties via precipitation of BCC HEA. Accordingly, the alloy can improve mechanical properties via micro-precipitation while maintaining the first phase of BCC HEA matrix and the second phase of immiscible metal matrix.

[0101] Preparation of High-Entropy Alloy Foam

[0102] The HEA foam according to Examples have a composite structure where pores are from inside of HEA. An alloy foam or metal foam decreases its density by internal pores but due to its large surface area it is being used as electrode materials, heat storing materials, etc., and efforts to utilize its heat-blocking characteristic by pores forms inside, etc., have been continued. Additionally, an artificial composite material, which is difficult to form naturally, may be prepared by filling the pores with a different material.

[0103] HEA foam is prepared using a two-phase separating alloy including HEA, and the manufacturing method includes a step for preparing a metal element as a raw material for preparing a two-phase separating alloy; a step for preparing an alloy for preparing a two-phase separating alloy; and a step for removing the second phase from the two-phase separating alloy.

[0104] Here, the two-phase separating alloy including HEA includes both the two-phase separating alloy including FCC HEA described above and the two-phase separating alloy including BCC HEA.

[0105] The step for preparing a raw material is a step for preparing a raw material which is designed by the design of the two-phase separating alloy described above, and the step for preparing an alloy is the same as explained above in the preparation of a two-phase separating alloy and thus the detailed explanation is omitted herein below.

[0106] The step for removing the second phase is a step for removing only the second phase L2 from an alloy thereby leaving only the first phase L1 which includes HEA and alters the position where the second phase L2 was located with pores thereby forming HEA foam.

[0107] FIG. 9 is a schematic diagram illustrating the chemical dealloying process by the present invention. The dendritic region corresponding to the second phase can be removed by the difference in galvani potential by promoting galvani battery reaction by dipping the prepared two-phase separating alloy into a diluted nitric acid solution. Here, it is possible to completely remove the second phase and it is also possible to retain a part thereof for the control of porosity by controlling the processing time.

[0108] FIG. 10 shows images of specimens of Example 20 composition observed under scanning electron microscope before and after dealloying process. As can be seen in FIG. 10, in the case of the Y—TiV—MoNbTa composition alloy, it was confirmed that the interdendritic composite structure between the TiV—MoNbTa HEA dendrite and the Y-rich dendrite in a casting state (left), and BCC HEA foam of the MoNbTa composition having a unique pore structure can be prepared by selective dissolution of the Y-rich interdendritic regions after dealloying (right).

[0109] In other words, it was confirmed that the pores in which the interdendritic regions were removed inside of the entire structural body by selective galvanic corrosion, and as such, it was confirmed that the foam with a porous structure can be formed.

[0110] FIG. 11 shows the results of XRD analysis with respect to (a) FCC HEA two-phase separating alloy of Example 2 and (b) BCC HEA two-phase separating alloy of Example 20 before and after the removal of L2 phase.

[0111] As illustrated, it was confirmed that the peak of the second phase, which was confirmed in Example 2 and Example 20, disappeared after going through with the step for removing the second phase by the electrochemical dealloying process. That is, it was confirmed by X-ray analysis that chemical dealloying process is a process suitable for the preparation of HEA foam.

[0112] FIG. 12 shows cross-sectional images illustrating that the porosity of the HEA foam prepared in Example 20 can be controlled by the processing time of dealloying. From the images illustrated therein, it can be seen that the dealloying proceeded along with the depth direction according to time passage, and for example in (a) depicting the cross-section of the as-cast state, it was confirmed that the corrosion proceeded partially up to the depth of about 300 μm in the case of (b) where the entire dealloying process was proceeded only for 4 hours in a diluted nitric acid solution having a concentration of 0.3 mol/L.

[0113] FIG. 13 shows the measurement results of thermal diffusion coefficient with respect to the two-phase separating FCC HEA of Example 2 and the HEA foam prepared from the alloy of Comparative Example 4 and Example 2, and the values are proportional to thermal conductivity.

[0114] Here, the HEA foam prepared in Example 2 by removing L2 phase showed a decrease of about 75% in thermal conductivity compared to Example 4, and also showed a decrease of about 66% compared to the HEA with a structure of a single solid solution of Comparative Example 4, which is known to have a superbly low thermal conductivity even compared to the general alloy. This is due to the pores formed inside the HEA foam having very low thermal conductivity, and it is speculated that the alloy with a foam structure can be highly applicable to a thermal barrier material, etc., by using the characteristic.

[0115] Additionally, in the case of an alloy foam, a physical property different from that of the original material alloy may appear by the pore structures formed inside the foam, and representatively, it is known that elongation can increase due to the limitation in crack propagation. Although only the results of thermal conductivity characteristics were provided with respect to the HEA in Examples of the present invention, various changes in physical properties according to the formation of HEA foam may be utilized.

[0116] Additionally, the HEA foam prepared from the two-phase separation of Example 2 showed a porosity of about 18 vol. %, and as in two-phase separating alloys in other Examples, Cu composition can control the porosity by controlling the ratio on the second phase.

[0117] Meanwhile, when the ratio of the metal or alloy that constitutes the second phase is extremely high, the HEA foam may not show the connected dendrite or, even when connected, the conjugation may be too weak thus becoming difficult to finally maintain the perfect shape. Here, the HEA foam may be prepared by a method of sintering the pieces of the precipitated HEA foam.

[0118] While this invention has been described with reference to preferred embodiments, a skilled person in the art to which the present invention pertains will be able to understand that the embodiments are for illustrative explanation of the technical concepts of the present invention and various modifications can be made within the scope not departing from the technical concepts of the present invention. Accordingly, the scope of the present invention should not be interpreted by particular embodiments but based on the description in the scope of claims and all the technical concepts within the equivalent scope thereof should be interpreted to be included within the scope of the present invention.