PERVIOUS CONCRETE HAVING A SUPER-ABSORBENT POLYMER

Abstract

A pervious concrete composition comprising a superabsorbent polymer, thereby enabling a water/cement ratio of 0.35-0.50. The superabsorbent polymer can be a cross-linked sodium polyacrylate-acrylamide/acrylic acid copolymer. The invention further comprises methods of installing the pervious concrete compositions.

Claims

1. A pervious concrete composition comprising a cross-linked sodium polyacrylate, present in the range 0.025-0.125 wt. % of cement, and having a water:cement ratio of 0.35-0.50 by weight.

2. (canceled)

3. (canceled)

4. A pervious concrete composition comprising cross-linked sodium polyacrylate in the range 3.5-4.5 oz per cubic yard of material.

5. A composition, comprising: cement; optional cementitious materials selected from: fly ash, slag, and silica fume; coarse aggregate; water; and cross-linked sodium polyacrylate in the proportion 0.03-0.125% by weight of cement, wherein the water:cement ratio is in the range 0.35-0.50 by weight.

6. The composition of claim 5, wherein the water:cement ratio is in the range 0.41-0.42 by weight.

7. (canceled)

8. (canceled)

9. (canceled)

10. (canceled)

11. (canceled)

12. (canceled)

13. The pervious concrete composition of claim 1, having a water:cement ratio of 0.46-0.50 by weight.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0038] FIG. 1 is a graph showing the proportions of various phases of concrete, according to w/c ratio (data from University of Missouri Kansas City); w/c ratio ranges for regular pervious concrete (0.25-0.35), and the pervious concrete of the invention (0.35-0.50) are shown by vertical bars.

[0039] FIG. 2 shows compressive strength after 28 days of curing vs. water content (expressed as a ratio by weight of water to cement in the initial mix). The optimum ratio is shown as 0.43.

DETAILED DESCRIPTION

[0040] The instant technology is directed to a pervious concrete composition, and methods of making and using the same.

[0041] The technology includes a way of significantly increasing the w/c ratio of pervious concrete, and therefore its strength, durability and workability, to a range that is otherwise not achievable with current methods or admixtures.

[0042] The technology includes the use of a superabsorbent polymer (SAP) introduced into a pervious concrete mixture so that the mixture will absorb a volume of water into the SAP particles, thereby allowing for a significant increase in w/c ratio without decreasing the viscosity of the cement paste in a manner which would otherwise result in paste drain down or runoff. Water is released from the SAP over time, during curing.

[0043] Superabsorbent polymers are polymeric materials that can absorb and retain very large amounts of liquid per unit mass. Typically an SAP can absorb at least 50 times its own weight of water, and some SAP's can absorb up to 300 times their weight of water. Water molecules are trapped in a SAP via hydrogen bonding with polar groups on the polymer molecules. One common example, which can be used in the pervious concrete compositions herein, is formed from the polymerization of acrylic acid blended with sodium hydroxide in the presence of an initiator to give a poly-acrylic acid sodium salt. This salt is also referred to as sodium polyacrylate, “sodium polyacrylate, cross-linked”, and “acrylic acid polymer, sodium salt”. Other examples of SAP's that can be used in the pervious concrete compositions herein include, but are not limited to: potassium co-polymer of acrylic-acrylamide crosslinked, cross-linked acrylate copolymer partially neutralized to the sodium salt, 2-propenoic acid polymer, crosslinked with sodium 2-propenoate, and acrylic acid co-acrylamide. SAP's can be produced using gel, suspension, or solution polymerization methods, as would be within the capability of one skilled in the art.

[0044] The SAP is added to the PC mixture in a powdered form, as particles, or in solution. Suitable SAP's are obtainable from the following vendors: Pervious Enhancer Pro, San Carlos, Calif., and True Nutrition, Vista, Calif. 92081 (see, e.g., truenutrition.com/p-7254-hydromax-powder-100-grams.aspx). The SAP particle size is preferably 50-800 μm (micrometers).

[0045] Based on the proportion of SAP, an additional volume of water can be added to the cement mix in a manner that does not decrease, or lower, the viscosity of the mix. The addition of SAP allows the cement to retain its body and still cling to the aggregate particles, even with significantly higher w/c ratios than in a typical PC. The increased quantity of water absorbed by the SAP particles allows for mixes not just in the ideal w/c hydration range, but even above that point so that it is possible to compensate for potential moisture loss in transit during hot and or low humidity conditions if desired.

[0046] The SAP particles, when swollen with water, also act as a lubricant, yet do not thin the cement and water paste, and therefore provide the significant enhancement in workability of the paste and therefore the pervious concrete mix without the disadvantages associated with VMA, as described above.

[0047] A typical formulation is based on 2 oz. to 12 oz. of SAP per cubic yard of pervious concrete mix. Starting from a water/cement mixture, having a 0.35-0.50 w/c ratio, SAP is added in the range 0.03-0.125 wt. % of the total mix. The SAP absorbs some of the water and traps it in the mixture during transit. The trapped water is then liberated from the SAP as the mixture cures. (The terms set and cure are used interchangeably herein.) Preferred formulations have 3-8 oz. of SAP per cubic yard of pervious concrete mix, and still other formulations have 8-20 oz. of SAP per cubic yard of pervious concrete mix. It is to be understood that other suitable ranges can be inferred by matching lower and upper bounds of the aforementioned ranges. One preferred dosage used is 3.5-4 oz. per cubic yard (0.05 wt. %). The dosages employed correspond to 0.025-0.125 wt. % of SAP (0.1-0.14% wt. of water) in the pervious concrete mix. Acceptable ranges of SAP concentration, including datapoints within, are: 0.03-0.04 wt. %; 0.04-0.045 wt. %; 0.05-0.06 wt. %; 0.055-0.065 wt. %; 0.06-0.07 wt. %; 0.07-0.1 wt. %; 0.1-0.125 wt. %.

Mix Modifications

[0048] Pervious concrete is typically designed to have between 15-25% (by volume) voids, the most common target being in the range 17-23%. Once the void space in the aggregate is known, a person skilled in the art of pervious concrete mix formulation can determine the proper volume of cement paste needed to achieve particular design goals. The desired water:cement ratio, in the range of 0.35-0.50 (by weight), is then used to determine the proper quantity of both water and cement. When incorporating an SAP into the mix, the w/c ratio will typically be higher by 0.05-0.15 than a conventional pervious concrete mix that does not have a SAP. So, the preferred range of w/c in the mix will be 0.35-0.50. Other acceptable ranges include: 0.35-0.40; 0.40-0.45; and 0.45-0.50 by weight. Acceptable w/c ratios in the finished product include: 0.35, 0.36, 0.37, 0.38, 0.39, 0.40, 0.41, 0.42, 0.43, 0.44, 0.45, 0.46, 0.47, 0.48, 0.49, and 0.50.

Batching Procedure

[0049] In order to make a pervious concrete mix using SAP additives, the following aspects of technique should be considered.

[0050] In general, while the SAP can be added to the mix at any time during or after batching, to promote maximum dispersement of the SAP, workers should avoid placing the SAP into the mixing drum before the other components of the concrete mix because doing so may cause the SAP to be trapped in the front of the drum and not fully mix.

[0051] In a “dry plant”, the other mix components are introduced directly into and mixed in the truck drum. The SAP product may be introduced directly into the truck drum during or after batching but is preferably introduced after batching.

[0052] In a central batch or “wet plant”, mix components are introduced into a batching drum where they are pre-mixed before being poured into the drum of the truck. The SAP may be introduced into the truck hopper while (but not before) the batch drum is in the process of emptying the pre-mixed pervious concrete into the truck. If this is not possible, the procedure for a “dry plant” should be followed.

[0053] When loading less than a full load of pervious concrete, the truck operator should “back up” the pervious concrete mix, moving it towards the back of the drum so that the SAP can be manually placed, or tossed, directly onto the mix.

[0054] The SAP may be packaged in a disintegrating bag which can be tossed into the truck unopened, or the SAP can be poured from a bag or container.

[0055] When using a volumetric truck, the SAP maybe introduced into the water supply tank in advance of mixing.

[0056] The truck drum should be rotated at full speed, 12-15 rpm, for 3-6 minutes after addition of the SAP in order to fully disperse the SAP particles throughout the pervious concrete.

[0057] An additional 5 minutes of slow mixing, at 2-5 rpm, which typically takes place during transit to the jobsite, may be needed for full absorption of the SAP into the PC mix. A minimum of 75 revolutions of the drum, in total at full and slow speeds, should be performed.

[0058] In the case of a PC mix that includes SAP, a plastic covering may be laid over the pervious concrete after installation, as needed, to promote curing.

[0059] No special procedures are required or recommended for discharge of the PC mix from the truck and during installation.

Impacts and Benefits of the Invention

[0060] Concrete trucks often accumulate so much PC, which sticks to the inside of the truck and in the fins (due to either the low w/c or use of VMA's), that it has been recommended that a concrete supplier should not use the same truck for more than two consecutive loads of pervious concrete. By being able to use a higher water/cement ratio, afforded by the SAP, this problem is eliminated: the material does not stick and easily comes out of the truck, thereby keeping the trucks cleaner, and requiring less time and effort to maintain them. In addition, the concrete company or supplier is able to put their truck back in service much faster after hauling a PC that has an SAP additive. Many concrete companies have been reluctant to produce PC due to the additional time it takes to unload the material. The sooner the truck returns to the yard the sooner it can be sent out to deliver the next load, which means that operating profit is significantly impacted by truck turnaround times.

[0061] The use of SAP in a PC mixture also allows the supplier to compensate for the moisture loss that occurs during transport and installation in warm, dry, or windy weather.

[0062] By enabling the mix to have additional water, the flow characteristics of the pervious concrete mix are greatly increased, facilitating an increased discharge rate as well as a more complete discharge. The SAP-added composition slides down the concrete truck delivery chute more easily and more quickly, with little or no assistance of manual labor required; it spreads easily with less effort, and even exhibits the ability to self-consolidate to a degree that is superior to previous compositions in the art, further decreasing the levels of manpower and effort required for installation relative to a PC mix that does not have an SAP additive.

[0063] Because of the high water cement ratio, a SAP enhanced mix is much easier to work with than a regular PC mix. It therefore requires less time to install and thereby allows the curing plastic to be applied much sooner. This ensures that adequate levels of moisture remain within the slab for proper curing.

[0064] The other common challenge with conventional pervious concrete is the loss of water through evaporation while the mix is in transit to the job site and/or while at the job site during discharge and installation. The water captured in the SAP particles added to a pervious concrete mix as described herein is much less susceptible to evaporation, thereby reducing the overall moisture loss. This has two positive impacts. First, the use of the SAP allows for a mix that is actually above the previously contemplated ideal w/c for a pervious concrete, and thereby compensates for any evaporative moisture loss that does occur. Second, it is typical to have to stop the pour of a conventional pervious concrete mix several times and add additional water to the mix in order to make up for the evaporative moisture loss and in order to maintain the proper moisture level of the paste throughout the application process. When this is necessary, it adds a significant amount of additional time to the installation process (during which time even more evaporative water loss can occur). Time is of the essence during application of the mix; the mix has to be discharged, installed and covered in a short period of time. Continually stopping to add water delays the process unduly. Because of the nature of SAP's and the way they bind water molecules, there is significantly less evaporation loss from a pervious concrete mix that has SAP in it, and the need to add water on the job site is reduced or eliminated.

[0065] Overall, then, benefits to the producer include faster discharge and turnaround.

[0066] The cleaner drum is a benefit to the producers also. This too has been an issue for producers because drums that have been used to transport pervious concrete mixes (that are drier, and have lower w/c ratios, than regular concrete) require more time, effort and costs to clean the inside of the drums after delivery.

[0067] Another benefit of the use of SAPs is a reduced quantity of cement that needs to be used relative to conventional pervious concrete mixes. The increase in w/c ratio, while keeping overall paste volume the same, allows for less cement to be used overall vs. conventional pervious concrete mixes, while increasing strength due to the additional water available for more complete hydration. This allows for both a reduction in cost as well as reduction in the carbon footprint of the finished product.

[0068] The use of SAP's eliminates the need for both water reducers and viscosity modifiers, thereby resulting in cost savings from simpler processing, and use of fewer ingredients in the mix.

[0069] Another benefit to the producer is an extended delivery range. Once the hydration process starts and the cement starts to set (stiffen), typically 60 minutes after initial batching, a pervious concrete mix is no longer workable so any delay in the onset of hydration is highly desirable. Overall, it has been noted that higher ambient temperatures accelerate hydration and lower temperatures delay hydration. The additional water in the mix due to the SAP keeps the mix cooler and delays the onset of hydration in two ways. First, by reducing friction inside the rotating drum (thus resulting in less heat during transport). Second, the high specific heat capacity of water (relative to that of the other components of the mix) requires considerably more external energy (via higher air temperature) to raise the temperature of the overall mix.

[0070] The use of SAP's also makes it possible to save on labor costs due to faster discharge and installation times. Pervious concrete mixtures having added SAP's require less effort to place and finish.

[0071] Thus the use of SAP's provides benefits to the installer, due principally to the faster discharge, and faster install that are possible with the pervious concrete compositions of the present invention.

[0072] The use of SAP's also gives rise to increased quality in the finished product, arising from greater aggregate consolidation, which is a primary factor in pavement strength. The more aggregate to aggregate contact the stronger the pavement (and this is possible with the higher w/c ratios made possible by the use of SAP's).

[0073] The use of SAP's in a pervious concrete mix also makes it possible to install the curing cover sooner than with a conventional mix. This reduces the time the mix is exposed to air, wind, sun, and thereby locks in more moisture for more effective hydration.

[0074] Additional benefits to the pavement owner include improved appearance of the slab, increased durability, and an elimination of raveling. The higher level of consolidation and workability with SAP mixes allows for a tighter more consistently smoother appearance, which is more attractive to the customer. Increased durability, i.e., how well the slab holds up over time with continued use, also arises from a pervious concrete that has been formed with SAP's in the mix. Durability is a function of strength, and a pervious concrete mix that has a higher w/c ratio will be stronger.

[0075] Pervious concrete is also notorious for raveling, which is the dislodging of stones at the surface. The resulting appearance is quite unattractive and unacceptable to most owners. Another benefit of the mix that uses SAP's is that it eliminates or substantially reduces raveling, because the aggregate is held together more strongly than is the case with a conventional pervious concrete mix.

Examples

Example 1: Composition #1: Pervious Concrete Incorporating Sodium Poly-Acrylate

[0076] The composition of the SAP is 100% poly-acrylic acid sodium salt, also referred to as sodium polyacrylate. CAS Registry No. 09003-04-7.

[0077] The ideal dosage range is approx. 0.05% of the weight of cementitious materials, or 3.5-4.5 oz. per cubic yard.

Example 2 Composition #2

[0078] The general proportions of basic pervious concrete, when cured, according to the present invention are based on the following formula:

Aggregate: approx. 60%, by volume (typically) Cement paste
(combination of cement and/optional SCM's and water): approx. 20%, by volume
Air: approx. 20%, by volume
Aggregates can be either river/pea gravel or crushed rock

TABLE-US-00002 Ranges (volume) typical range general range (% by volume) Aggregates 57-63 55-65 Cement Paste 17-23 15-25 Air 17-23 13-30
Performance enhancing additives: [0079] SAP (by weight) 2.5 oz to 12 oz per cubic yard of concrete. [0080] Hydration stabilizer (by weight) 2-20 oz per 100 lbs of dry cement as determined by both environmental conditions and transport time from bath plant to job site. [0081] Fibers may be used in the range of 1.0 to 7.5 lbs per cubic yard. Fibers are used for reinforcement of pervious concrete, since rebar can't be used in pervious concrete.

[0082] SCM's are optional cementitious materials such as fly ash, slag, silica fume. These are industrial waste products commonly used in concrete to provide additional benefits such as increased curing and paste density. Their presence does not interfere with the performance of the SAP.

[0083] In general, the cement compositions may contain a coarse aggregate and in some cases additionally a small quantity of fine aggregate, typically not to exceed 10% of the total aggregate weight. The coarse aggregate is typically present in the range 50-85% of the total weight of the finished product. The fine aggregate, may be used at 1-10% of the weight of the coarse aggregate.

[0084] All references cited herein are incorporated by reference in their entireties.

[0085] The foregoing description is intended to illustrate various aspects of the instant technology. It is not intended that the examples presented herein limit the scope of the appended claims. The invention now being fully described, it will be apparent to one of ordinary skill in the art that many changes and modifications can be made thereto without departing from the spirit or scope of the appended claims.