PROCESS FOR THE RECOVERY OF COBALT AND TUNGSTIC ACID AND/OR ITS DERIVATIVES FROM AQUEOUS SOLUTIONS

Abstract

This invention relates to a process for the recovery of cobalt ions and tungstic acid and/or its derivatives from aqueous solutions, such as in particular the spent catalytic waters deriving from processes for the oxidative cleavage of vegetable oils. In particular this invention relates to a process for the recovery of cobalt ions and tungstic acid and/or its derivatives which provides for the use of cation-exchange resins.

Claims

1. A process for recovering Cobalt ions and tungstic acid and/or its derivatives from an aqueous solution, which comprises the following steps: a) removing Cobalt ions by contacting said aqueous solution with a cationic exchange resin; b) separating said aqueous solution from the cationic exchange resin; c) concentrating said aqueous solution obtained from step b), obtaining a concentrated aqueous solution containing tungstic acid and/or its derivatives; d) eluting the Cobalt ions from the cationic exchange resin of step b) with an acid aqueous solution.

2. The process according to claim 1, in which said aqueous solution comes from the exhausted catalytic waters deriving from oxidative cleavage processes of vegetable oils.

3. The process according to claim 1, comprising before step a) a preliminary purification step for separating an organic phase from said aqueous solution.

4. The process according to claim 3, in which said separation of the organic phase is performed by decantation.

5. The process according to claim 4, in which said decantation is performed in presence of an organic solvent.

6. The process according to claim 5, in which said organic solvent is selected from the group consisting of n-hexane, n-heptane, n-octane, n-nonanoic acid and mixtures thereof.

7. The process according to claim 6, in which said organic solvent is n-octane, nonanoic acid or mixtures thereof.

8. The process according to claim 1, in which said cationic exchange resin is crosslinked.

9. The process according to claim 1, in which said cationic exchange resin is of the strong acid type.

10. The process according to claim 9, in which the functional group of said cationic exchange resin of the strong acid type is constituted by sulphonic groups.

11. The process according to claim 1, in which said acid aqueous solution of the d) step is constituted by an aqueous solution of an acid selected from the group consisting of hydrochloric acid, sulphonic acid, phosphoric acid, hydrobromic acid, acetic acid.

12. The process according to claim 1, in which said step a) is performed with a ionic exchange column.

13. The process according to claim 12, in which said aqueous solution is fed to step a) with a flow rate comprised between 1 and 50 BV*/h (LHSV).

14. The process according to claim 2, comprising before step a) a preliminary purification step for separating an organic phase from said aqueous solution.

15. The process according to claim 2, in which said cationic exchange resin is crosslinked.

16. The process according to claim 3, in which said cationic exchange resin is crosslinked.

17. The process according to claim 4, in which said cationic exchange resin is crosslinked.

18. The process according to claim 5, in which said cationic exchange resin is crosslinked.

19. The process according to claim 6, in which said cationic exchange resin is crosslinked.

20. The process according to claim 2, in which said cationic exchange resin is of the strong acid type.

Description

EXAMPLE 1

[0038] 28 kg of process flow originating from stage b) of a process for the oxidative cleavage of sunflower oil having a high oleic acid content carried out in accordance with Example 1 in application WO 2008/138892 were reheated to 80° C. in the presence of 2.8 kg of n-octane and allowed to settle until an organic phase had separated out, thus obtaining 8.4 litres of spent catalytic waters containing approximately 2400 ppm of cobalt ions and tungstic acid and/or its derivatives in a concentration corresponding to approximately 8000 ppm of tungsten.

[0039] Subsequently the spent catalytic waters obtained after separation of the organic phase were fed by gravity at 25° C. and BV/H=2 to an ion-exchange column (height 1 m and diameter 40 mm) packed with 216.2 grams (dry weight, corresponding to 800 ml of wet resin) of Amberlyst™ 15WET resin (concentration of active sites on the dry resin=4.7 eq/kg; concentration of active sites on the wet resin=1.8 meq/ml; surface area 53 m.sup.2/g, pore diameter=300 Å).

[0040] During the treatment it was possible to establish that cobalt was effectively being adsorbed by the resin by observing progressive colouration of the resin bed. Table 1 shows details of the amount of adsorption (expressed as cm of colouration of the resin bed) as a function of the volume of the catalytic waters fed and the residual cobalt concentration in the aqueous solution obtained at the exit from the column, once separated from the cation-exchange resin.

TABLE-US-00001 TABLE 1 Residual cobalt concentration in waters separated Cobalt adsorption Catalytic from the resin (cm colouration waters fed (ppm) of the resin bed) (ml) 0.15 25 1766 0.08 41 3561 0.06 60 5242 0.03 79 7256 0.16 86 7806 0.11 92 8216 0.06 93 8423

[0041] The aqueous solution separated from the cation-exchange resin was subsequently concentrated by evaporating off approximately 90% of the water, thus obtaining an aqueous solution containing tungstic acid and/or its derivatives in a concentration corresponding to approximately 80000 ppm of tungsten. The said solution was used as a catalytic solution in a reaction for the hydroxylation of vegetable oils, and revealed no differences of any kind with respect to a fresh solution having the same concentration.

[0042] 6.3 kilograms of an aqueous solution of sulfuric acid (sulfuric acid concentration 6.5% by weight) were fed countercurrently to the ion-exchange column containing the cation-exchange resin on which the cobalt was adsorbed, separating out an aqueous solution containing approximately 3150 ppm of cobalt ions, indicating almost total recovery of the cobalt initially present in the spent catalytic waters.

EXAMPLE 2

[0043] Example 1 was repeated, feeding 8.6 litres of the same spent catalytic waters containing 2400 ppm of cobalt ions and tungstic acid and/or its derivatives in a concentration corresponding to approximately 8000 ppm of tungsten to the ion-exchange column containing the cation-exchange resin from which the cobalt had been eluted at the end of Example 1.

[0044] During the treatment it was possible to verify that cobalt was effectively being newly adsorbed from the resin through observing progressive colouration of the resin bed. In a similar way to Example 1, Table 2 shows details of the amount of adsorption (expressed as cm of colouration of the resin bed) as a function of the volume of the catalytic waters fed and the residual cobalt concentration in the aqueous solution obtained at the exit from the column, once separated from the cation-exchange resin.

TABLE-US-00002 TABLE 2 Residual cobalt concentration in waters separated Cobalt adsorption Catalytic from the resin (cm colouration waters fed (ppm) of the resin bed) (ml) 0.32 13.5 863 0.55 32 2702 0.61 54 4854 0.72 76.5 6750 0.69 92 8667

[0045] The aqueous solution separated out from the cation-exchange resin was then subsequently concentrated by evaporating approximately 90% of the water, thus obtaining an aqueous solution containing tungstic acid and/or its derivatives in a concentration corresponding to approximately 80000 ppm of tungsten. The said solution was used as a catalytic solution in a reaction for the hydroxylation of vegetable oils without differences of any kind in comparison with a fresh solution at the same concentration.

[0046] 2.1 kilograms of an aqueous solution of sulfuric acid (sulfuric acid concentration 6.5% by weight) were fed countercurrently to the ion-exchange column containing the cation-exchange resin on which the cobalt was adsorbed, separating out an aqueous solution containing 9830 ppm of cobalt ions, indicating almost total recovery of the cobalt initially present in the spent catalytic waters and maintaining the effectiveness of the cationic resin.