OPACIFYING CLUSTERS FOR USE IN PAINT COMPOSITIONS

Abstract

An opacifying cluster which may be added to a coating composition to provide a coating composition with low gloss and a high level of opacity. The opacifying cluster can include a polymeric latex binder coalescing cluster components into a generally homogeneous particle. The cluster components may include discrete polymeric particles each defining a closed void volume therein, a plurality of inorganic pigment particles, and a plurality of extender pigment particles. The clusters may also include a porosity of the polymeric latex binder thereof defining a binder void volume. Also provided is a paint product including such a pigment cluster.

Claims

1. An opacifying cluster particle suitable for latex paint compositions to provide increased opacity, the opacifying cluster particle comprising: a polymeric latex binder coalescing cluster components into a generally homogeneous particle; the cluster components include discrete polymeric particles each defining a closed void volume therein, a plurality of optional inorganic pigment particles, and a plurality of extender pigment particles; and a porosity of the polymeric latex binder defining a binder void volume.

2. The opacifying cluster particle of claim 1, wherein the opacifying cluster particle has a total void volume including a total closed void volume of all the discrete polymeric particle closed void volumes and the binder void volume of the polymeric latex binder.

3. The opacifying cluster particle of claim 2, wherein the total void volume is from about 1 percent to about 35 percent by volume of the opacifying cluster particle.

4. The opacifying cluster particle of claim 1, wherein an average closed void volume of each discrete polymeric particle is about 0.4 microns to about 0.7 microns in size.

5. The opacifying cluster particle of claim 1, wherein an average particle size of the opacifying cluster particle is from about 5 microns to about 44 microns.

6. The opacifying cluster particle of claim 1, wherein the opacifying cluster particle has an outer surface defined at least by a portion of the polymeric latex binder and wherein the outer surface has a surface porosity.

7. The opacifying cluster particle of claim 6, wherein the surface porosity is formed by one or more interstices each from about 0.050 μm to about 0.150 μm in size.

8. The opacifying cluster particle of claim 1, wherein a glass transition temperature of the discrete polymeric particles is greater than a glass transition temperature of the polymeric latex binder.

9. The opacifying cluster particle of claim 1, comprising from about 1 percent to about 30 percent by volume of the polymeric latex binder, from about 10 percent to about 70 percent by volume of the discrete polymeric particles, from about 0 percent to about 6 percent by volume of the inorganic pigment particles; and the balance being the extender pigment particles.

9. The opacifying cluster particle of claim 1, comprising from about 1 percent to about 30 percent by volume of the polymeric latex binder, from about 10 percent to about 70 percent by volume of the discrete polymeric particles, from about 0 percent to about 6 percent by volume of the inorganic pigment particles; and the balance being the extender pigment particles.

10. The opacifying cluster particle of claim 9, wherein a pigment volume concentration in the opacifying cluster particle of the discrete polymeric particles, the inorganic pigment particles, and the extender pigment particles relative to the volume of total solids is greater than or equal to a critical pigment volume concentration.

11. The opacifying cluster particle of claim 1, wherein the extender pigment particles are about 0.1 to about 1 microns in size and selected from calcium carbonate, clay, silica, and mixtures thereof.

12. The opacifying cluster particle of claim 1, wherein the inorganic pigment particles are about 0.1 to about 1.0 microns in size and selected from titanium dioxide, zinc oxide, and mixtures thereof.

Description

BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWING

[0020] The disclosure may take physical form in certain parts and arrangement of parts, embodiments of which will be described in detail in this specification and illustrated in the accompanying drawings which form a part hereof and wherein:

[0021] FIG. 1 shows a top view of: region (a), which is an exemplary embodiment of a surface coated by a paint having only large-size extenders, and region (b), which is an exemplary embodiment of a surface coated by a paint including opacifying clusters in place of at least a portion of the large-size extenders included in the paint shown in region (a);

[0022] FIG. 2(a) shows a schematic, cross-sectional view of an exemplary embodiment of an opacifying cluster;

[0023] FIG. 2(b) shows a schematic, cross-sectional view of an alternative exemplary embodiment of an opacifying cluster;

[0024] FIG. 3 shows a schematic view of equipment that may be used to produce opacifying clusters;

[0025] FIG. 4 shows a schematic, cross-sectional view of an alternative exemplary embodiment of an opacifying cluster;

[0026] FIG. 5 shows a graphical representation of the size distribution of opacifying clusters compared to a large-size extender;

[0027] FIG. 6(a) shows a graphical representation of the opacity of the surfaces coated by paints having large-size extenders versus paints opacifying clusters;

[0028] FIG. 6(b) shows a graphical representation of the sheen of representative surfaces coated by paints having large-size extenders versus paints having opacifying clusters; and

[0029] FIG. 7 shows a graphical representation of the ability of dusters to provide opacity similar to prior opaque polymers and relative to the inability of large size extenders to improve opacity; and

[0030] FIG. 8 shows a graphical representation of the ability of opacifying clusters herein to reduce sheen similar to other large particle size extenders and as compared to prior opaque polymers inability to achieve such results.

[0031] The drawings herein are not necessarily drawn to scale and schematic views do not necessarily represent the actual product or components thereof, but intended to generally represent various components thereof.

DETAILED DESCRIPTION

[0032] Certain terminology is used herein for convenience only and is not to be taken as a limitation on the present disclosure. Relative language used herein is best understood with reference to the drawings, in which like numerals are used to identify like or similar items. Further, in the drawings, certain features may be shown in somewhat schematic form.

[0033] It is also to be noted that the phrase “at least one of”, if used herein, followed by a plurality of members herein means one of the members, or a combination of more than one of the members. For example, the phrase “at least one of a first widget and a second widget” means in the present application: the first widget, the second widget, or the first widget and the second widget. Likewise, “at least one of a first widget, a second widget and a third widget” means in the present application: the first widget, the second widget, the third widget, the first widget and the second widget, the first widget and the third widget, the second widget and the third widget, or the first widget and the second widget and the third widget.

Glossary of Terms

[0034] “Opacity” as used herein refers to the ability of a film to scatter light based on the thickness of the film. The opacity is often expressed as S/mil and may be in the form of Kubelka-Munk scattering coefficients as determined using a modification of ASTM D2805-70 as described by J. E. McNutt and H. L. Ramsey in American Paint and Coatings Journal, April 1988 p. 46 by the weight drawdown method, which is incorporated herein by reference.

[0035] “Opaque polymer” as used herein refers to a polymer or polymeric network that encloses or substantially encloses a defined volume. An opaque polymer may be a discrete polymeric particle where each polymer particle defines a closed void volume therein. In some embodiments, an opaque polymer comprises polystyrene. Opaque polymers are commercially available from commercial vendors. Exemplary commercially available opaque polymers are Ropaque Ultra EF and/or Ropaque OP-96 EF (both available from the Dow Chemical Company, Midland, Mich.). In certain embodiments the defined volume of an opaque polymer comprises air forming a void that scatters light. In certain other embodiments the defined volume of an opaque polymer comprises a liquid such as water. For embodiments including a liquid within the defined volume, the liquid is eventually replaced with air, creating a void that scatters light. Opaque polymers may be used as a partial replacement for TiO.sub.2 in paints or other coatings to enhance hiding and whiteness in paints and coatings.

[0036] “Binder void volume” as used herein refers to the volume percentage of a coalesced polymer structure (such as a coalesced binder) that comprises air when applied as a part of a coating to a surface and dried.

[0037] “Opaque polymer void volume” as used herein refers to the volume of the void that is enclosed by, or substantially enclosed by, an opaque polymer,

[0038] “Void volume” or total void volume as used herein refers to the volume percentage of a material that comprises air when applied as part of a coating to a surface and dried. Void volume or total void volume is generally the sum of opaque polymer void volume and hinder void volume.

[0039] “Pigment clusters” or opacifying cluster as used herein generally refers to different components, such as binder, opaque polymer, pigment, extenders, and/or other materials which may be used to enhance, or otherwise change the properties of, a paint composition wherein the components may be coalesced together into particles as are described herein. In some embodiments, pigment clusters and opacifying clusters are not held together with chemical bonding or covalent bonding. In other embodiments, components of pigment clusters and opacifying clusters (such as pigment) are not held to other components (such as binder) with hydrogen bonding or other types of bonding.

[0040] “Pigment volume concentration” or “PVC” as used herein refers to a number that represents the volume of pigment compared to the volume of all solids, In the field of paints and coatings, PVC is a useful measure because the binder acts as the material to unite all the pigment and other raw materials into the paint and the PVC value ensures there is enough binder to enable the paint to adhere properly to whatever it has been applied over in addition to containing all of the other components of the paint. If a paint has no pigment at all it will usually be very glossy and have a PVC of zero. An example is clear gloss paints. Flat paints have a very high pigment loading and have high PVCs (usually in the range from about 55% up to about 80%). Another non-limiting exemplary range of PVC in which pigment can be loaded is from about 60% to about 75%. Primers and undercoats vary from 30% to about 50% PVC as do semi-gloss, satin and low sheen paints, Gloss colored paints can vary from 3% to about 20% PVC depending on the color of the paint. Generally the darker the color of the gloss paint the lower the PVC. Additionally, it is thought that the lower the PVC of a paint is, the better its mechanical properties (such as tensile strength, and consequently, exterior durability) will be. PVC may be expressed as a percentage. For example, if a coating has a PVC of 30, then 30% of the total binder/pigment blend is pigment, and 70% is binder solids on a volume basis.

[0041] “Critical pigment volume concentration” or “CPVC” as used herein is the point at which there is just enough binder to wet (entirely surround) the pigment particles. As PVC reaches and then increases above CPVC, mechanical properties of the paint deteriorate. Above CPVC, with insufficient binder to satisfy pigment surface and fill interstitial spaces, air is introduced into the film resulting in a decrease in film integrity. However, above CPVC, increased air and pigment interface results in a substantial boost in pigment scattering efficiency. A film below the CPVC has excess resin and may exhibit a smooth surface that reflects light or appears to be glossy, As the PVC of a film approaches CPVC, the film will appear to be flatter, although the aforementioned loss of mechanical properties may become a limiting factor in how close to CPVC a paint producer wishes to provide the PVC.

[0042] “Y.sub.black” as used herein represents the reflectance value of a coating and measures the ability of a coating to cover against a black background. Measurement of Y.sub.black may be done as part of measurement of contrast ratio.

[0043] “Y.sub.white” as used herein represents the reflectance value of a coating and measures the ability of a coating to reflect light against a white background. Measurement of Y.sub.white, may be done as part of measurement of contrast ratio.

[0044] “Contrast Ratio” as used herein is calculated as Y.sub.black/Y.sub.white and is the ratio of the reflectance of a film on a black substrate to that of an identical film on a white substrate. ASTM D2805-11 provides for the measurement of contrast ratio.

[0045] “Binder” as used herein is a material that may be used to form a cluster from different components (ex., pigments, small sized extenders, and/or opaque polymers) by coalescing and mechanically connecting the components. Latex polymers are a non-limiting example of a binder that may be dispersed in water using a dispersant and film formation (or other network formation) occurs by joining (or coalescence) of these solid particles as water evaporates or is otherwise driven off. Exemplary binders which may be used in the present disclosure include, but are not limited to, polyvinyl acetates, vinyl acrylics, styrene butadiene, styrene acrylics, and ethylene vinyl acrylics. Other exemplary binders include, but are not limited to solvent-borne binders and water reducible binders.

[0046] “Small size extender” as used herein refers to particles of minerals, clay, ground and precipitated silica, or other fillers which may be used to reduce the quantity of the pigment required to achieve a desired hiding ability, sheen, etc., without significantly affecting the color of the paint established by the pigment, and having a particle size of from about 0.1 μm to about 1 μm. Small size extenders that may be purchased commercially include, but are not limited to Omyacarb UF (Omya North America). Extender pigment particles used within a cluster may be small size extender particles. Any suitable small size extender that one of skill in the art would use in a coatings application may be used in the coatings and paint products of the present disclosure without departing from the scope of the present disclosure.

[0047] “Large size extender” as used herein refers to particles of minerals, clay, or other fillers which may be used to reduce the quantity of the pigment required to achieve a desired hiding ability, sheen, etc., without significantly affecting the color of the paint established by the pigment, and having a particle size of greater than 5 μm. In some embodiments a large size extender is from about 5 μm to about 50 μm. In other embodiments, a large size extender is from about 10 μm to about 15 μm. Extender pigment particles not used or coalesced within an opacifying cluster, but otherwise added to a latex paint composition may be large size extender particles.

[0048] “Pore” or interstices as used herein is an opening at the surface of a structure such as a polymer, polymer cluster, or opacifying cluster. In one embodiment, a pore may form at the outer surface of an opacifying cluster and the components of the outer surface of an opacifying cluster may comprise components selected from the group consisting of: binders, opaque polymers, small-size extenders, pigments, and combinations thereof.

[0049] “Sheen” as used herein may also sometimes be referred to as “gloss”. It is thought that because most extenders have a refractive index of light that is close to the refractive index of the binders of most coatings, below CPVC an extender/latex film will be largely transparent to visible light. In a coating, a gloss finish indicates that the surface which has a coating applied to it (i.e., is “finished”) it is shiny or glass-like. The gloss of a surface is described as the reflection of light from the surface that is independent of color. ASTM D523 or D532-14 may be used to measure sheen. The prescribed angle at which light is reflected off the surface may vary, but for the purposes of this disclosure to measure 85 Sheen, is measured at 85° relative to the surface reflecting the light. ASTM D523 or D532-14 may also be used to describe 60 Gloss which is measured at 60° relative to the surface reflecting the light. One of skill in the art is able to determine relative levels of gloss (low versus high) in context of each coating.

[0050] “Paint” as used herein refers to any mixture comprising different types of raw materials, each with its own function, which must be balanced to achieve the desired properties in the final product or film coating. The two primary functions of paint are decoration and protection. A paint may contain a solvent (which can include a volatile component derived from a petroleum distillate for a solvent-based paint, or a low VOC, or no-VOC, or water for a water-based paint), a binder, a pigment, fillers (such as an extender or a plurality of extenders of different sizes) and an additive, which may impart different functionality to the paint or final coating. Embodiments may include an opacifying cluster as a component thereof, optionally in combination with at least one of the solvent, binder, pigment, filler and additive.

[0051] “Burnish” as used herein refers to the ability of a coating to retain its gloss value after being subjected to mechanical forces, such as abrasion, Burnish may be measured through ASTM D6736-08.

[0052] “Refractive Index” as used herein refers to a measurement that describes how light propagates through a material or medium. If needed, Refractive Index may be measured through one or more of ASTM D1218, D1747, or D542.

Opacifying Cluster Particle Constituents

[0053] The present disclosure is directed to compositions of, methods for using, and methods for making opacifying duster particles that are compatible to form a component of surface coatings such as latex paints which provide, among other features, a surface film of low gloss and high opacity. The unique opacifying clusters of the present disclosure increase opacity with increasing PVC similar to the commonly used prior opaque polymers, but contrary to the prior opaque polymers, the opacifying clusters herein can also be used to reduce gloss and sheen (similar to large size extender particles) to achieve a matte or egg-shell finish. Thus, the clusters herein may be used over a wide range of gloss and sheen values not previously obtainable with conventional opaque polymers.

[0054] Turning to more of the specifics, FIG. 1 shows an exemplary top view of an applied film 10 of paint against a white backing 11 in region (a), which is shown extending beyond the lowermost boundary of the film 10 in FIG. 1 for illustrative purposes, wherein the applied film contains large size extenders and there is the appearance of windows 12 (shown as light spots in FIG. 1 relative to the surrounding film material) in the applied film 10. The formation of such windows is undesirable to users because of the need for additional coatings of paint to completely hide a substrate. Region (b) in FIG. 1 includes an applied film 10 against a white backing 11 similar to that in region (a), wherein the applied film 10 in region (b) is formed with a paint including the opacifying clusters disclosed herein. In the surface coating which is prepared. including the opacifying clusters there is a greatly reduced appearance of windows 12 in the applied film 10, however, the complete absence of windows 12 is not required. In some embodiments the binder polymer is coalesced to form a network or backbone. In other embodiments the binder polymer is not covalently bonded to the other constituents. In certain embodiments the opaque polymer particles are discrete polymeric particles. In certain other embodiments the opaque polymer is processed with the outlet temperature being high enough (for example, above the glass transition temperature (T.sub.g) of the opaque polymer), as described in detail below with respect to the Manufacture of Opacifying clusters. In yet other embodiments still, the opaque polymer is coalesced to other opaque polymer or binder,

[0055] FIG. 2(a) shows the cross sectional view of an exemplary embodiment of an opacifying cluster 20. The cluster 20 comprises a volume of binder material 23 having an outer surface 21 wherein the outer surface further comprises a plurality of interstices or pores 22. The plurality of pores 22 collectively establish the porosity of the opacifying cluster 20. In one embodiment the outer surface 21 comprises a binder material or polymeric latex binder. In another embodiment the outer surface comprises any number of components which may be selected from the group consisting of: binders, opaque polymers, pigments, small-size extenders and combinations thereof. In some embodiments the interstices or pores 22 have a diameter or size of from about 0.050 μm to about 0.150 μm. In other embodiments the pores have a diameter or size of about 0.1 μm. Without wishing to be limited by theory, it is thought that because of the relatively small pore diameter or size and the relative tortuosity of the inner structure of an opacifying cluster 20, the latex from the paint solution does not enter into the voids (both the voids within the opacifying cluster 20 and the voids 28 in any binder) within the opacifying cluster 20 (i.e., the latex material does not displace the air inside the voids inside the opacifying cluster 20), thus preserving the optical qualities such as the light scattering ability of the opacifying cluster 20, rendering the opacifying cluster 20 an effective alternative to large-size extenders unlike clays, for example, which are penetrated b the latex material from a paint solution, thus causing the clay particles to lose their optical qualities.

[0056] The opacifying cluster 20 further comprises binder material or polymeric latex binder 23 which mechanically coalesces or binds the various components of the opacifying cluster 20 to form a mixture, including an opaque polymer 24, small-size extender 25 (or extender pigment particles), and/or pigment 26 (or inorganic pigment particles). The opaque polymer 24 may comprise polymer which encloses or substantially encloses an opaque polymer void volume 27. The opaque polymer 24 may include discrete polymeric particles each defining a closed void volume therein. In some embodiments the polymer of the opaque polymer is polystyrene. Suitable opaque polymers may be available from commercial vendors such as Ropaque Ultra EF or Ropaque OP-96 EF (both available from the Dow Chemical Company, Midland, Mich.). some embodiments the opaque polymer void volume 27 has a diameter or size from about 0.3 μm to about 0.8 μm. In other embodiments the opaque polymer void volume 27 has a diameter of from about 0.4 μm to about 0.7 μm. In other embodiments still the opaque polymer void volume 27 has a diameter of from about 0.5 μm to about 0.6 μm. In some embodiments the opaque polymer 24 has a polymer thickness of from about 0.075 μm to about 0.150 μm. In other embodiments the opaque polymer has a polymer thickness of from about 0.100 μm to about 0.120 μm. The opacifying duster 20 also comprises a binder void volume 28 which is the result of empty spaces which form within the opacifying cluster 20 during formation of the cluster—for example, during spray drying.

[0057] FIG. 2(b) shows an alternative embodiment of an opacifying cluster 20 of the present disclosure. In the embodiment shown in FIG. 2(b) the outer surface 21 may comprise binder material 23 and opaque polymer 24, pigment 26, and small-size extender 25. As described in additional detail herein, the amount of polymer 24, pigment 26 and small-size extender 25 may vary from opacifying cluster to opacifying cluster and depends on the input feeds during the manufacture of the opacifying clusters. Surprisingly, it is discovered that not all components are necessary to provide functional opacifying clusters. For example, FIG. 4 shows yet an additional embodiment of an opacifying cluster 20 of the present disclosure. In the embodiment of FIG. 4 the opacifying cluster comprises only opaque polymer 24 which has been processed at a temperature that is significantly above T.sub.g of the opaque polymer 24.

[0058] The binder material or polymeric latex binder 23 may have a relatively low glass transition temperature (T.sub.g) and in some embodiments the T.sub.g of the binder material 23 is from about 0° C. to about 60° C. In other embodiments the T.sub.g of the binder material 23 is from about 5° C. to about 60° C. In another embodiment still, the T.sub.g of the binder material 23 is from about 15° C. to about 50° C.

[0059] The opaque polymer 24 or the polymer of the discrete polymeric particles each defining a closed void volume therein may have a relatively high glass transition temperature (T.sub.g) and in some embodiments the T.sub.g of the opaque polymer is from about 100° C. to about 120° C. In other embodiments the T.sub.g of the opaque polymer is from about 100° C. to about 110° C.

[0060] In some embodiments, the difference in T.sub.g of the binder 23 to the T.sub.g opaque polymer 24 is greater than 80° C., In other embodiments, the difference in T.sub.g of the binder to the T.sub.g opaque polymer is greater than 40° C. In other embodiments, still the difference in T.sub.g of the binder to the. T.sub.g opaque polymer is greater than 10° C.

[0061] In some embodiments, the binder is a latex material. Exemplary binders which may be used in the present disclosure include, but are not limited to, polyvinyl acetates, vinyl acrylics, styrene butadiene, styrenes, styrene acrylics, ethylene vinyl acrylics. Other exemplary binders are solvent-borne binders and water reducible binders.

[0062] One suitable non-limiting example of a material to use as the pigment or inorganic pigment particle 26 is TiO.sub.2. In other embodiments the pigment 26 comprises zinc oxide. It is to be understood, however, that the scope of the present disclosure is not limited to titanium dioxide or zinc oxide as the pigment and that any suitable material may be used, In some embodiments the pigment 26 has a diameter of from about 0.1 μm to about 1.0 μm. In other embodiments the pigment 26 has a diameter of from about 0.3 μm to about 0.5 μm,

[0063] In an embodiment, the small-size extender 25 (or extender pigment particles within the cluster) of the present disclosure could be CaCO.sub.3. Other non-limiting examples of materials which may be used as small-size extenders are clay, silica (both ground and precipitated), a fine talc or any other small extender that may be used in the art, and combinations thereof. In some embodiments, the small-size extenders 25 are from about 0.1 μm to about 1.0 μm. In other embodiments, the small size extenders 25 are from about 0.3 μm to about 0.8 μm. In other embodiments, still the small size extenders 25 are from about 0.5 μm to about 0.7 μm. In sonic embodiments, the opacifying cluster 20 does not have any small-size extender 25.

[0064] The opacifying clusters 20 are formed through mechanical entanglement or coalescence of the binder and the constituents. In some approaches, there is no covalent or chemical bonding within the clusters. The formation of the opacifying clusters 20 via temperature elevation (using a method such as spray drying) provides for relatively uniform opacifying clusters 20. The opacifying clusters 20 also which have void volumes that comprise both opaque polymer void volume 27 and binder void volume 28 due to the water being driven out of the binder in the opacifying clusters 20. In certain non-limiting embodiments, the void volume is from about 1% to about 35% by volume of the opacifying cluster 20. In other non-limiting embodiments, the void volume is from about 15% to about 30% by volume of the opacifying cluster. In other non-limiting embodiments still, the void volume is from about 25% to about 30% by volume of the opacifying cluster.

[0065] In some exemplary opacifying clusters 20, the volume percentage of solids of pigment 26 in an opacifying cluster 20 is from 0 to about 6%. In other exemplary embodiments, the volume percentage of solids of pigment 26 in an opacifying cluster 20 is greater than or equal to CPVC. In still other embodiments, the volume percentage of solids of pigment 26 in an opacifying cluster is about 1 to about 6%, in other approaches, about 2 to about 4%, and in yet other approaches, about 2.5%.

[0066] In other exemplary embodiments, the volume percentage of solids of binder in an opacifying cluster 20 is from about 1% to about 30%. In another exemplary embodiment, the volume percentage of solids of binder in an opacifying cluster is from about 5% to about 30%.

[0067] Some embodiments of the present opacifying cluster 20 have a volume percentage of solids of opaque polymer 24 of from about 0% to about 90%. In other exemplary embodiments, the volume percentage of solids of opaque polymer 24 in an opacifying cluster 20 is from about 10% to about 70%. In other exemplary embodiments still, the volume percentage of solids of opaque polymer 24 in an opacifying cluster 20 is from about 30% to about 50%.

[0068] In some exemplary embodiments, the volume percentage of solids of small-size extender 25 is from about 0% to about 90%. In many embodiments the volume percentage of solids of small size extender 25 comprises the balance of the opacifying cluster.

[0069] In some exemplary approaches, the opacifying clusters may exhibit a density of about 7 to about 20 pounds/gallon. In other approaches, the opacifying clusters may exhibit a density of about 7 to about 15 pounds/gallon, and in yet other approaches, about 10 to about 12 pounds per gallon. It will be appreciated, that such exemplary densities apply to all the various approaches of opacifying clusters provided herein.

[0070] In some aspects, the opacifying clusters herein are structured or engineered composite particles including the various particle constituents or components described throughout this disclosure. The constituents or particle components are generally uniformly or homogeneously dispersed or spread consistently throughout the composite particle. In some approaches, the cluster particles are spray dried particles. In other words, and in some approaches, the composite particles of this disclosure are not a core/shell-type structure and are free-of or devoid of any coatings or surface layers thereof prior to being combined in a latex paint composition.

Manufacture of Opacifying Clusters

[0071] FIG. 3 provides a spray dryer 30 that may be used to manufacture the opacifying clusters of the present disclosure. According to the embodiment illustrated in FIG. 3, the spray dryer 30 includes an air supply blower 31 that feeds inlet air into a chamber 36 for atomizing a slurry comprising components to be included in the opacifying clusters 20, such as pigment 26, opaque polymer 24, and latex, for example. The air supply blower 31 can be a rotary, positive displacement fan, turbine, or any other suitable airflow device that can supply the volumetric flow rates into the chamber 36 to achieve the atomization described herein. An electric air heater 34 such as a radiant element, steam conduit, or other suitable heat source in thermal communication with the air supplied by the air supply blower 31 is operable to establish the desired temperature of the inlet air being introduced to the chamber 36 via a nozzle 38. The atomized slurry is drawn from the chamber 36 into a cyclone dryer 33 by a negative pressure established by an exhaust blower 32 which, like the air supply blower 31, can be a rotary, positive displacement fan, turbine, or any other suitable airflow device that can establish the exhaust volumetric flow rates described herein. Once through the chamber 36, the entrained opacifying dusters 20 in the form of a dry powder are removed from the airflow by a filter 33. The filter 33 can be any suitable separation device that can remove a substantial portion of the entrained powder from the airflow such as a cyclone separator, for example, that uses centrifugal force to expel the entrained produce radially outward, toward a perforated peripheral wall provided with a filter material, for example. The airflow can be occasionally interrupted to allow the particulate opacifying clusters 20 to be deposited into a collection container 37, which can be isolated from the system with a large ball valve 40 or other suitable flow control device.

[0072] A controller 39 is provided to control operation of the various components of the spray dryer 30 in accordance with the methods of manufacturing the opacifying clusters 20 described herein. An embodiment of the controller 39 generally includes a non-transitory, computer-readable medium 41 storing computer-executable instructions that, when executed by a computer processor 42, cause the controller 39 to communicate with the various operational components of the spray dryer 30 to manufacture the opacifying clusters 20 under the conditions described herein.

[0073] In use, the inlet air supply blower 31 and the exhaust blower 32 are started by the controller 39 to introduce a suitable amount of nozzle air to assist in atomization of the opacifying cluster slurry. Filters 33 on the spray dryer 30 are equipped with an air pulse mechanism 44 to occasionally release powder from filters 33. The electric air heater 34 is then set to deliver the desired temperature at the inlet 35.

[0074] When the temperature of the outlet of the chamber 36 reaches about 85° C. then water is pumped to the atomizer at a rate to maintain a constant outlet temperature. Once the spray dryer 30 has reached steady state with the desired outlet temperature with only water and atomization air, the water feed is switched to the slurry including the components to be included in the opacifying clusters 20. Once through the chamber 36, the resultant dry powder is separated in a cyclone and collected in a container 37 using the ball valve 40 or any other valve that may be well-suited for such an application.

[0075] FIG. 4 shows a cross-sectional view of an exemplary opacifying cluster 20 of the present disclosure, comprising only opaque polymer 24 which has been processed at a very high outlet temperature (above the T.sub.g of the opaque polymer 24) to coalesce the opaque polymers 24 together. In the opacifying cluster 20 shown, the opaque polymer 24 is distributed in a higher amount towards the outer surface 21 of the opacifying cluster 20 than within a central region of the opacifying cluster 20. Without wishing to be limited by theory, it is thought that during the manufacturing process, as water that acts as a carrier of the components into the spray dryer evaporates during the spray drying process, lighter and/or less dense components (such as opacifying clusters) are moved towards the outer surface. In other embodiments, binder material may also coalesce at the outer surface according to the same proposed principle.

Size Distribution of the Opacifying Cluster

[0076] An exemplary volume percentage of opacifying clusters 20 included in an illustrative embodiment of a paint composition is from about 50% to about 60%. In certain embodiments, the volume percentage of opacifying clusters in a paint composition is less than or equal to CPVC.

[0077] FIG. 5 shows the distribution of sizes of the opacifying clusters of the present disclosure as well as the distribution of particle sizes in exemplary large-size extenders (Duramite, available from Imerys Performance Materials, Roswell, Ga.) which are viable for commercial use. Surprisingly, it is found that the opacifying clusters made according to the present disclosure are substantially similar in size (i.e., have a relatively uniform size distribution) when compared to the exemplary large-size extenders. From FIG. 5 it is clear that the opacifying clusters of the present disclosure are substantially similar in size distribution to comparable commercially available large-size extenders. In one embodiment, the opacifying clusters have an average particle size of from about 5 μm to about 44 μm. 1 h another embodiment, the opacifying clusters have an average particle size of from about 7 μm to about 30 μm. In another embodiment still, the opacifying clusters have an average particle size of from about 10 μm to about 20 μm. In yet another embodiment, the opacifying clusters have an average particle size of from about 10 μm to about 15 μm. It is highly desirable to provide consistently-sized and relatively small (greater than 325 mesh in size) extenders for an even, non-grainy, composition when the opacifying clusters are used in a paint coating.

Properties of the Composition

[0078] When added to a paint composition as a replacement for at least a portion, which can optionally be less than all, or optionally all of the large size extenders, the opacifying clusters of the present disclosure provide improved optical properties compared to a control paint composition which utilizes large size extenders that is devoid of the opacifying clusters described herein. Table 1 shows the comparison of an exemplary paint composition that includes opacifying clusters and a control paint composition that does not contain any opacifying clusters.

[0079] From Table 1 we can see that the paint clusters provide an improvement in the contrast ratio (C/R) and opacity (S) of the composition. In Table 1: NVV is volume solids, PVC is pigment volume concentration, extender and TiO.sub.2 levels are expressed as pounds per 100 gallons or if easier divide by 100 to express as pound/gal. The TiO.sub.2 is actually a 75% slurry (i.e., the actual level of TiO.sub.2 may be calculated by multiplying the listed amount by 0.75). Y is the reflectance over white and black, respectively, and C/R is the contrast ratio.

[0080] Table 1: Performance Results of a Paint Composition Having Opacifying clusters

TABLE-US-00001 TABLE 1 Performance Results of a Paint Composition Having Opacifying clusters Large-Size Opacifyin TiO.sub.2 Measured 60 85 Sample Extender g cluster slurry NVV PVC Y.sub.white Y.sub.black C/R wt/gal S/mil gloss sheen Contro1 140 0 212 41.7 30.8 0.9079 0.8548 0.942 10.84 1.86 10.8 11.5 Sample A 0 75 212 41.7 30.8 0.9229 0.8879 0.962 10.32 2.47 10.6 12.2

[0081] The contrast ratio of Sample A is higher than the contrast ratio (C/R) of the Control that does not have the opacifying clusters. The opacity (S/mil) of Sample A is about 32% higher than the opacity of the Control.

[0082] FIG. 6(a) is a graphical representation of measurements of opacity of coatings applied from paint compositions containing exemplary opacifying clusters having 42.5 PVC opaque polymer, 42.5 PVC CaCO.sub.3, 5 PVC TiO.sub.2, and the balance of the opacifying cluster being latex versus an equal amount of ground calcium carbonate (used as a large-size extender). The paint used comprises about 38% binder, 10% water, 13% large size extender, 20% pigment slurry, and the balance being other additives. The x-axis is the extender PVC of the paint. The cluster composition of the graph is a paint with both clusters and large size extenders. From a paint formulation perspective, increasing PVC replaces latex with extender or opacifying clusters. Both the large-size extender and the opacifying clusters improves the opacity of the resultant coating.

[0083] FIG. 6(b) is a graphical representation of sheen measurements of the compositions described in FIG. 6(a). The composition that contains the large-size extender and the opacifying clusters (i.e., cluster composition) has a sheen that is relatively high whereas the composition that contains the opacifying clusters has a relatively low sheen.

[0084] An exemplary embodiment of a paint according to the present disclosure is a paint product comprising at least one solvent, at least one binder, at least one pigment and a PVC of opacifying clusters wherein the PVC of opacifying clusters in the paint is below CPV. However, embodiments of the opacifying clusters comprise a PVC of pigment in the opacifying clusters that approaches CPUC.

[0085] In yet other aspects, the opacifying clusters herein may be structured or spray dried granular optical particles for use in coatings, such as latex paint compositions. The clusters may include different optically active components coalesced within the particle and with selected refractive indexes so that the opacifying duster includes one or more discrete components with refractive indexes from 1 to 3.0. A difference of refractive index between the first component and the second component may be about 0.5 to about 2.0

[0086] For instance and in one approach, the opacifying clusters herein may include a first component or particle therein with a first refractive index. The first component or particle may have a refractive index of about 1.5 to about 3.0, in other approaches, about 1.5 to about 2.7, and in other approaches, about 2.0 to about 3.0. In some approaches, the first component may be an inorganic pigment particle such as titanium dioxide, latex binder, calcium carbonate and the like, and combinations thereof.

[0087] The opacifying duster may also include a second component or particle with a second refractive index different than the first refractive index. The second component or particle may have a refractive index of about 1.0 to 2.0, in other approaches, 1.0 to about 1.5, and in other approaches, 1.2 to about 2.0, and in yet other approaches, 1.0 to 1.2. In some approaches, the second component may be a discrete polymer particles defining an internal void of air or water. In other approaches, the second component may be an opaque polymer. The internal void of the second component may be 0.3 to about 0.8 microns in size.

[0088] In some approaches, the cluster may include yet another or third component or particle with a third refractive index that may be the same as to different than either the first or second refractive index. The third component may have a refractive index from about 1.4 to about 2.0. The third component may be a small size extender particle. The first, second, and third components or particles may be coalesced into a composite particle by a latex binder.

EXAMPLES

[0089] The practice and advantages of the opacifying clusters and latex paint compositions including such clusters may be demonstrated by the following examples, which are presented for purposes of illustration and not limitation. Unless otherwise indicated, all amounts, percentages, and ratios are by weight.

Example 1

[0090] An exemplary opacifying cluster is prepared by spray drying a 50% solids slurry of Omyacarb UF, OP-96, TiO.sub.2 and Latex, On a volume basis, the finished cluster comprises 42.5 Omyacarb UF 42.5% OP-96, 5% TiO.sub.2 and 10% latex binder. The average particle size of the Opacifying clusters measured using a Malvern Mastersizer (Malvern Instruments, Malvern, UK) is 12 microns.

Example 2

[0091] Another exemplary opacifying cluster is prepared by spray drying a 44% solids slurry of hydrite clay, OP-96, TiO.sub.2 and latex. On a volume percentage of solids basis, the finished cluster comprises 37,5% clay. 37.5% OP-96, 5% TiO.sub.2 and 20% latex binder. The average particle size of the Opacifying clusters is 12.7 microns.

Example 3

[0092] Another exemplary opacifying cluster is prepared by spray drying a 50% solids slurry of Omyacarb UF, OP-96 and latex. On a volume percentage of solids basis, the finished cluster comprises 30% Omyacarb UF, 60% OP-96 and 10% latex binder. The average particle size of the Opacifying clusters is 14.6 microns.

Example 4

[0093] Another exemplary opacifying cluster is prepared by spray drying a 31% solids slurry of OP-96 and latex. On a volume percentage of solids basis, the finished cluster comprises 90% OP-96 and 10% latex binder. The average particle size of the Opacifying clusters is 112 microns.

Example 5

[0094] Another exemplary opacifying cluster is prepared by spray drying a 60% solids slurry of Omyacarb UF, TiO.sub.2 and latex. On a volume percentage of solids basis, the finished cluster is composed of 85% Omyacarb UF, 5% TiO, and 10% latex binder. The average particle size of the Opacifying clusters is 12.7 microns.

Examples 6-17

[0095] The properties of opacifying clusters versus a commercially available large-size extender is CaCO.sub.3 (Duramite) is shown in the table. The composition of the exemplary opacifying clusters is provided in the table. CaCo.sub.3 as used in the opacifying clusters is Omyacarb UF. Opaque polymer commercially available from Dow is used in each sample. The balance of the composition of each sample is latex binder. The paint used comprises about 38% binder, 10% water, 13% large size extender (or equivalent opacifying cluster amounting to the 6.2 gallons provided in Table 2 below), 20% pigment slurry, and the balance being other additives.

TABLE-US-00002 TABLE 2 Properties of Various Extenders and/or Opacifying clusters Pounds of Sample Composition Needed To Thickness (Percentage Provide 6.2 of Applied CaCo3/Opaque Gallons of Coating Y-Value Y-Value Contrast Sample Polymer/TiO.sub.2) Extender (mils) (white) (black) Ratio S/Mil Gloss Sheen Duramite 100/0/0 140 2.5 0.9079 0.8548 0.942 1.86 10.8 11.5 Example 6 42.5/42.5/5 89 2.5 0.9239 0.8881 0.961 2.43 7 7.3 Example 7 37.5/37.5/5 79 2.5 0.9204 0.8844 0.961 2.41 7.3 8.6 Example 8 45/45/0 83 2.5 0.9147 0.8754 0.957 2.18 7.9 8.6 Example 9 30/60/0 73 2.5 0.9182 0.8797 0.958 2.27 7.4 6.2 Example 10 0/90/0 51 2.5 0.9256 0.8901 0.962 2.49 10.6 11.8 Example 11 43.75/43.75/2.5 85 2.5 0.9221 0.8854 0.960 2.33 9.8 11.3 Example 12 20.1/58.4/2.5 75 2.5 0.9229 0.8879 0.962 2.47 10.6 12.2 Example 13 0/85/5 57 2.5 0.9280 0.8942 0.964 2.59 11 14 Example 14 42.5/42.5/5 90 2.5 0.9209 0.8841 0.960 2.43 10 14 Example 15 30/60/0 51 2.5 0.9190 0.8775 0.955 2.25 8.6 9 Example 16 85/0/5 111 2.5 0.9184 0.8759 0.954 2.25 32 63 Example 17 80/0/5 118 2.5 0.9182 0.8148 0.953 2.19 13 17

Example 18

[0096] A comparison of opacifying clusters of the present disclosure to conventional opaque polymers (Ropaque) and conventional large size extenders (Duramite) in latex paint compositions was conducted. FIGS. 7 and 8 illustrate opacity in terms of contrast ratio and sheen relative to increasing PVC of the latex paint compositions. FIG. 7 illustrates the ability of conventional opaque polymer and opacifying clusters herein to maintain or increase opacity with increasing PVC while increasing the amount of large size extenders leads to a dramatic decrease in opacity. The drop in opacity with increasing volume of large size extenders may be due to the large windows that such extenders form in the paint. FIG. 8 illustrates the unique ability of the opacifying clusters herein to also function similar to large size extenders to decrease sheen. Conventional opaque polymers, as also shown in FIG. 8, are not able to decrease sheen like the opacifying clusters of the present disclosure and prior large size extenders. The composition of the opacifying clusters used for FIGS. 7 and 8 includes 2.5% TiO.sub.2, 58.3% opaque polymer, 29.2% calcium carbonate, and 10% binder.

Example 19

[0097] The opacifying clusters herein also achieve the increased opacity with desired burnish levels at the same time. Such burnish levels can also be achieved with decreasing or removing completely the levels of commonly used durability increasing particles, such as polyvinyl chloride particles (PVC particles, Geon 215, PolyOne Corporation, about 22 microns average size) to provide improved burnish.

[0098] For this example, spray dried opacifying clusters (SD clusters) were prepared with about 29 volume percent small size extender (calcium carbonate), 58.4 volume percent opaque polymer (Ropaque 96), about 2.5 volume percent titanium dioxide, and 10 volume percent latex were prepared according to the present disclosure. The SD clusters for this Example had an average particle size of about 22 microns, which is similar to the Geon particles. The clusters were added to a latex paint composition. The latex paint composition also included large size extenders (Minspar 4, the Quartz Corporation, about 7 microns average size), and opaque polymer (Ropaque 96). Tables 3 to 6 provide the composition of evaluated latex paints, opacity values, and burnish testing of the exemplary clusters as compared to control paints using the Geon polyvinyl chloride particles instead.

TABLE-US-00003 TABLE 3 Latex Paint Compositions SD Clusters (22 Opaque TiO2 TiO2 ID Sample Extender Geon microns) Polymer (slurry)* (dry) NVV A Control 90 50 0 85 300 0 41.1 B 18 90 0 51.5 85 300 0 41.1 C 19 90 0 71.4 85 225 0 41.1 D Control 30 55 0 0 0 45 33.3 E 20 30 0 56.6 0 0 45 33.3 F Control 60 19 0 89.7 280 0 38.8 G 21 60 0 19.6 89.7 280 0 38.8 H Control 35.5 20 0 0 0 50 32.7 I 22 35.5 0 20.6 0 0 50 32.6 *75% slurry (amount of TiO2 may he calculated by multiplying the listed amount by 0.75.)

TABLE-US-00004 TABLE 4 Opacity Opacity Factor y-value Y value 60 85 (Opacity/Dry ID Sample PVC (white) (black) C/R s/mil gloss sheen TiO.sub.2) A Control 38.8 0.919 0.874 0.952 2.11 5 3.6  1:106 B 18 49.3 (38.8) 0.925 0.893 0.965 2.56 4.6 3.8 1:87 C 19 49.3 (38.8) 0.915 0.88 0.961 2.51 4.1 2.6 1:66 D Control 9 0.868 0.648 0.746 0.49 6.7 2.9 1:91 E 20 23.1 (9.0)  0.871 0.701 0.805 0.72 5.6 2.9 1:62 F Control 37.2 0.923 0.888 0.962 2.56 10.5 13.9 1:82 G 21 4.17 (37.2) 0.928 0.899 0.969 2.64 9.1 11.6 1:79 H Control 10.6 0.866 0.682 0.788 0.63 14 13.4 1:79 I 22 15.9 (10.6) 0.869 0.7005 0.812 0.75 12.7 12.1 1:66

TABLE-US-00005 TABLE 5 Burnish at 60 gloss % Increase % increase (5 cycles) (25 cycles) 60 gloss 60 gloss 60 gloss from from Sample (initial) (5 cycles) (25 cycles) Initial Initial Control 5.3 5.7 5.9 8% 11% 18 5   5.4 5.7 8% 14% 19 4.2 4.4 4.6 5% 10% Control — — — — — 20 — — — — — Control 10.6  12.2  12.2  15%  15% 21 9.2 10.6  10.8  15%  17% Control — — — — — 22 — — — — —

TABLE-US-00006 TABLE 6 Burnish at 85 Sheen % Increase % increase 85 (5 cycles) (25 cycles) Sheen 85 Sheen 85 sheen from from Sample (initial) (5 cycles) (25 cycles) Initial Initial Control 3.7 4.4 5.1 19% 38% 18 3.8 4.8 5.1 26% 34% 19 2.7 3.5 4.1 30% 52% Control — — — — — 20 — — — — — Control 13.5  14.7  15.1   9% 12% 21 11.5  12.9  13.3  12% 16% Control — — — — — 22 — — — — —

[0099] As shown, sample 18 achieves a better opacity in terms of contrast ratio (C/R) than its control (line above it) with the same paint composition but without the clusters and using Geon instead. Sample 19, which reduces the level of TiO2 as compared to the control and sample 18, still achieves a better opacity than its control. Similar opacity results are shown relative to controls for samples 20, 21, and 22. All invective samples achieved the desired opacity while maintaining acceptable burnish levels without the poly vinyl chloride durability particles, Sample IDs A to E are matte finish and F to I are satin finish.

Example 20

[0100] Another example comparing opacifying clusters of the present disclosure to latex paint compositions including or free of polyvinyl chloride particles similar to Example 19 was performed. For this Example, the opacifying clusters were of the same composition of Example 19, but had an average particle size of about 17 microns. Tables 7 to 10 provide the results.

TABLE-US-00007 TABLE 7 Latex Paint Compositions SD Clusters Opaque TiO2 TiO2 Sample Extender Geon (17 microns) Polymer (slurry)* (dry) NVV Control 90 50 0 85 300 0 41.1 23 90 0 51.5 85 300 0 41.1 24 125 0 51.5 85 225 0 41.1 25 125 0 66.3 63.7 225 0 41.1 26 125 0 81.1 42.5 225 0 41.1 27 125 0 95.8 21.2 225 0 41.1 Control 60 19 0 89.7 280 0 38.8 28 50 0 19.6 89.7 280 0 38.8 *75% slurry (amount of TiO2 may be calculated by multiplying the listed amount by 0.75.)

TABLE-US-00008 TABLE 8 Opacity y-value Y value 60 85 Sample PVC (white) (black) C/R s/mil gloss sheen Control 38.8 0.919 0.877 0.954 — 5 4 23 49.3 (38.8) 0.927 0.893 0.964 — 5 5 24 49.2 (38.8) 0.92 0.877 0.953 — 4.9 4.9 25 49.2 (38.8) 0.92 0.879 0.955 — 4.3 3.8 26 49.2 (38.8) 0.92 0.877 0.953 — 3.7 3.1 27 49.2 (38.8) 0.922 0.878 0.953 — 3.4 2.6 Control 37.2 0.924 0.887 0.96 — 11 16 28 4.17 (37.2) 0.926 0.893 0.964 — 10 14

TABLE-US-00009 TABLE 9 Burnish at 60 Gloss % Increase % increase 60 gloss 60 gloss 60 gloss (5 cycles) (25 cycles) Sample (initial) (5 cycles) (25 cycles) from Initial from Initial Control 4.9 5.4 5.6 10% 14% 23 4.8 5.3 5.6 10% 17% Control 5.2 5.6 5.9 8% 13 5 24 4.6 4.9 5 7% 9% 25 4.1 4.2 4.3 2% 5% 26 3.4 3.6 3.7 6% 9% 27 3.2 3.2 3.3 0% 3% Control 9.7 11.3 11.7 16% 21% 28 8.9 10.2 10.4 15% 17%

TABLE-US-00010 TABLE 10 Burnish at 85 Sheen 85 % Increase % Increase Sheen 85 sheen 85 Sheen (5 cycles) (25 cycles) Sample (initial) (5 cycles) (25 cycles) from Initial from Initial Control 43.5 4.5 4.9 29% 40% 23 4.6 6.1 6.8 33% 48% Control 3.6 4.3 4.5 19% 25% 24 4.3 5.2 6 21% 40% 25 3.4 4.6 5.1 35% 50% 26 2.7 3.8 5.2 41% 93% 27 2.4 4.1 5.3 71% 121% Control 13 14.4 14.7 11% 13% 28 12 13.9 14.2 16% 18%

[0101] For both Examples 19 and 20, Y-value (white) is measured by ASTM E1331-15; Y-value (black) is measured by ASTM E1331-15, contrast ratio (C/R) is measured by ASTM D2805; 60 gloss is measured by ASTM D523-14; 85 Sheen is measured by ASTM D523-14 and Burnish is measured by ASTM D6736-08. In all examples and throughout this disclosure, unless otherwise specified, all measurements herein are made at about 23±1° C. and about 50% relative humidity.

[0102] All publications, patent applications, and issued patents mentioned herein are hereby incorporated in their entirety by reference. Citation of any reference is not an admission regarding any determination as to its availability as prior art to the claimed disclosure.

[0103] The dimensions and values disclosed herein are not to be understood as being strictly limited to the exact numerical values recited. Instead, unless otherwise specified, such as dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value. For example, a dimension disclosed as “40 mm” is intended to mean “about 40 mm”.

[0104] While particular embodiments of the present disclosure have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the disclosure. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this disclosure.

[0105] A latex paint composition comprising:

[0106] solvent, at least one first polymeric binder, optional pigment particles, and a plurality of discrete opacifying cluster particles;

[0107] each discrete pacifying cluster particle includes a second polymeric latex binder coalescing cluster components into a generally homogeneous particle wherein the second polymeric latex binder is the same as or different from the at least one first polymeric binder;

[0108] the cluster components include discrete polymeric particles each defining a closed void volume therein, a plurality of optional inorganic pigment particles, and a plurality of extender pigment particles; and

[0109] a porosity of the polymeric latex binder defining a binder void volume.

[0110] The latex paint composition according to claim 13, wherein a pigment volume concentration of the discrete opacifying cluster particles in the latex paint composition is below the critical pigment volume concentration.

[0111] The latex paint composition of claim 13, wherein each opacifying cluster particle comprises a total void volume including a total closed void volume of all the discrete polymeric particles closed void volumes and the binder void volume of the second polymeric latex binder.

[0112] The latex paint composition of claim 15, wherein the total void volume is from about 1% to about 35% by volume of the opacifying cluster.

[0113] The latex paint composition of claim 13, wherein an average closed void volume of each discrete polymeric particle is about 0.4 microns to about 0.7 microns in size.

[0114] The latex paint composition according to claim 13, wherein the optional pigment particles includes one of inorganic pigment particles, additional discrete polymeric particles each defining a closed void volume therein not coalesced within the opacifying cluster particles, extender pigment particles not coalesced within the opacifying cluster particles, and mixtures thereof.

[0115] The latex paint composition according to claim 18, wherein the latex paint composition, when dried, includes about 50 to about 85 volume percent of the first polymeric binder, about 0 to about 45 volume percent extender pigment particles not coalesced within the opacifying clusters particles, about 0 to about 20 volume percent discrete polymeric particles each defining a closed void volume therein not coalesced within the opacifying cluster particles, about 0 to about 20 volume percent inorganic pigment particles, and about 5 to about 50 volume percent opacifying cluster particles.

[0116] The latex paint composition according to claim 13, wherein the opacifying cluster particles have an outer surface defined at least by a portion of the second polymeric latex binder and wherein the outer surface has a surface porosity.

[0117] The latex paint composition according to claim 20, wherein the surface porosity is formed by interstices each averaging in size from about 0.050 microns to about 0.150 microns.

[0118] The latex paint composition according to claim 13, wherein a glass transition temperature of the discrete polymeric particles in the opacifying cluster particles is greater than a glass transition temperature of the second polymeric latex binder in the opacifying cluster particles.

[0119] The latex paint composition of claim 13, wherein each opacifying cluster particle has an average particle size from about 5 microns to about 44 microns.

[0120] The latex paint composition of claim 13, wherein each opacifying cluster particle includes from about 1% to about 30% by volume of the second polymeric latex binder, from about 10 to about 70 percent by volume of the discrete polymeric particles, from about 0 to about 6 percent by volume of the inorganic pigment particles; and the balance being the extender pigment particles.

[0121] The latex paint composition of claim 13, wherein the pigment volume concentration in the opacifying cluster is greater than or equal to a critical pigment volume concentration.

[0122] A latex paint composition exhibiting improved contrast ratio and opacity, the latex paint composition comprising.

[0123] solvent, a polymeric latex binder, pigment particles and a plurality of spray dried opacifying cluster particles;

[0124] Each spray dried opacifying cluster particle including discrete polymeric particles each defining a closed void volume therein coalesced into a generally homogeneous particle, optional polymeric binder, optional inorganic pigment particles, and optional pigment extender particles; and:

[0125] Wherein the latex paint composition, when dried as a paint film, exhibits about 10 to about 35 percentage increase in opacity as compared to a latex paint composition with the same level of the pigment particles but not including the spray dried opacifying cluster particles.

[0126] The latex paint composition of claim 26, further exhibiting about 0.01 to about 0.02 unit increase in contrast ratio as compared to a latex paint composition with the same level of the pigment particles but not including the spray dried opacifying cluster panicles.

[0127] The latex paint composition of claim 26, wherein the improvement in opacity is exhibited over latex paint compositions with a gloss value from about 0 to about 30 and a sheen value from about 0 to about 30.

[0128] The latex paint composition of claim 26, wherein a dried latex paint composition exhibits less than about 20 percent increase in gloss and less than about 50 increase in sheen upon 25 scrub cycles per the procedures of ASTM D6736-01.

[0129] The latex paint composition of claim 29, wherein the latex paint composition includes less than about 10 weight percent of poly vinyl chloride particles.

[0130] The latex paint composition of claim 26, further comprising an opacity factor of about 1:60 to about 1:90 in terms of a ratio of opacity to dry pigment loading.

[0131] The latex paint composition of claim 26, wherein the spray dried opacifying cluster particle has a total void volume including a total closed void volume of all the discrete polymeric particle closed void volumes and the binder void volume of the polymeric latex binder,

[0132] The latex paint composition of claim 26, wherein the total void volume is from about 1 percent to about 35 percent by volume of the spray dried opacifying cluster particle.

[0133] The latex paint composition of claim 26, wherein an average closed void volume of each discrete polymeric particle is about 0.4 microns to about 0.7 microns in size.

[0134] The latex paint composition of claim 26, wherein an average particle size of the spray dried opacifying cluster particle is from about 5 microns to about 44 microns.

[0135] The latex paint composition of claim 26, wherein the spray dried opacifying cluster particle has an outer surface defined at least by a portion of the polymeric latex hinder and wherein the outer surface has a surface porosity.

[0136] The latex paint composition of claim 26, wherein the surface porosity is formed by one or more interstices each from about 0.050 μm to about 0.150 μm in size.

[0137] The latex paint composition of claim 26, wherein a glass transition temperature of the discrete polymeric particles is greater than a glass transition temperature of the polymeric latex binder.

[0138] The latex paint composition of claim 26, wherein the opacifying cluster includes from about 1 percent to about 30 percent by volume of the polymeric latex binder, from about 10 percent to about 70 percent by volume of the discrete polymeric particles, from about 0 percent to about 6 percent by volume of the inorganic pigment particles; and the balance being the pigment extender particles.

[0139] The latex paint composition of claim 26, wherein the pigment volume concentration in the spray dried opacifying cluster is greater than or equal to the critical pigment volume concentration.

[0140] The latex paint composition of claim 26, wherein the optional extender pigment particles are about 0.1 to about 1 microns in size and selected from calcium carbonate, clay, silica, talc, and combinations thereof.

[0141] The latex paint composition of claim 26, further comprising an opacity factor of about 1:60 to about 1:90 in terms of a ratio of opacity to dry pigment loading.

[0142] A latex paint composition exhibiting improved contrast ratio and opacity over a range of gloss values, the latex paint composition comprising

[0143] Solvent, a polymeric latex binder, and pigment particles;

[0144] Wherein the latex paint composition, when dried as a paint film, exhibits about 10 to about 35 percentage increase in opacity as compared to a latex paint composition with the same level of the pigment particles but not including the spray dried opacifying cluster particles; and

[0145] Wherein the improvement in opacity is exhibited with latex paint compositions having a gloss value from about 0 to about 30 and a sheen value from about 0 to about 30.

[0146] The latex paint composition of claim 43, further comprising a plurality of spray dried opacifying cluster particles, wherein each spray dried opacifying cluster particle including discrete polymeric particles each defining a closed void volume therein coalesced into a generally homogeneous particle, optional polymeric binder, optional inorganic pigment particles, and optional pigment extender particles.

[0147] A particulate cluster for use in a coating composition, the particulate cluster comprises: (a) a first component having a first refractive index; (b) a second component having a second refractive index; wherein the first component and the second component are connected by a coalesced latex hinder material.

[0148] The particulate cluster of claim 45, wherein the first refractive index of the first component is from about 1 to about 1.5 and the second refractive index of the second component is from about 1.5 to about 3.

[0149] The particulate cluster of claim 45, wherein the difference in refractive index between the first component and the second component is about 0.5 to about 2.0.