ORGANIC COMPOUND FOR ELECTROLUMINESCENCE DEVICE

Abstract

The present invention discloses an organic compound is represented by the following formula(1), the organic EL device employing the organic compound as fluorescent emitting guest shown deep blue color(CIEy=0.09˜0.12)and display good performance.

##STR00001##

wherein A, m and R.sub.1 to R.sub.3 are the same definition as described in the present invention.

Claims

1. A organic compound with a general formula(1) as follows: ##STR00034## wherein A represents the formula(2) to formula(5) ##STR00035## m represents an integer of 0 to 10, n represents an integer of 0 or 1, X is divalent bridge selected from the atom or group consisting from O, S and NR.sub.7, Y is divalent bridge selected from the atom or group consisting from O, S, C(R.sub.8)(R.sub.9), Si(R.sub.10)(R.sub.11) and NR.sub.12, Ar.sub.1 and Ar.sub.2 represent a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, R.sub.1 to R.sub.12 are independently selected from the group consisting of a hydrogen atom, a halide, a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, and a substituted or unsubstituted aralkyl group having 6 to 30 carbon atoms.

2. The organic compound according to claim 1, wherein the organic compound is selected from the group consist of: ##STR00036## ##STR00037## ##STR00038## ##STR00039## ##STR00040## ##STR00041##

3. A organic electroluminescence device comprising a pair of electrodes consisting of a cathode and an anode, and between the pairs of electrodes comprising at least a light emitting layer, one or more layers of organic thin film layer, wherein the light emitting layer comprising the organic compound according to claim 1.

4. The organic electroluminescence device according to claim 3, wherein the light emitting layer comprising the organic compound with a general formula(1) is a guest material.

5. The organic electroluminescence device according to claim 3, wherein the light emitting layer comprising the organic compound with a general formula(1) is a fluorescent emitter.

6. The organic electroluminescence device according to claim 3, wherein the light emitting layer emits fluorescent blue lights.

7. The organic electroluminescence device according to claim 3, wherein the device is an organic light emitting device.

8. The organic electroluminescent device according to claim 3, wherein the device is a lighting panel.

9. The organic electroluminescent device according to claim 3, wherein the device is a backlight panel.

Description

BRIEF DESCRIPTION OF THE DRAWING

[0011] FIG. 1 show one example of organic EL device in the present invention, and 6 is transparent electrode, 13 is metal electrode, 7 is hole injection layer which is deposited onto 6, 8 is hole transport layer which is deposited onto 7, 9 is fluorescent emitting layer which is deposited onto 8, 10 is hole blocking layer which is deposited onto 9, 11 is electron transport layer which is deposited onto 10, and 12 is electron injection layer which is deposited on to 11.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012] What probed into the invention is the organic compound and organic EL device using the organic compound. Detailed descriptions of the production, structure and elements will be provided in the following to make the invention thoroughly understood. Obviously, the application of the invention is not confined to specific details familiar to those who are skilled in the art. On the other hand, the common elements and procedures that are known to everyone are not described in details to avoid unnecessary limits of the invention. Some preferred embodiments of the present invention will now be described in greater detail in the follows. However, it should be recognized that the present invention can be practiced in a wide range of other embodiments besides those explicitly described, that is, this invention can also be applied extensively to other embodiments, and the scope of the present invention is expressly not limited except as specified in the accompanying claims

[0013] In a first embodiment of the present invention, the organic compound which can be used as fluorescent emitting guest for organic EL device are disclosed. The mentioned organic compound represented by the following formula(1):

##STR00004##

wherein A represents the formula(2) to formula(5)

##STR00005##

m represents an integer of 0 to 10, n represents an integer of 0 or 1, X is divalent bridge selected from the atom or group consisting from O, S and NR.sub.7, Y is divalent bridge selected from the atom or group consisting from O, S, C(R.sub.8)(R.sub.9), Si(R.sub.10)(R.sub.11) and NR.sub.12, Ar.sub.1 and Ar.sub.2 represent a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, R.sub.1 to R.sub.12 are independently selected from the group consisting of a hydrogen atom, a halide, a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, and a substituted or unsubstituted aralkyl group having 6 to 30 carbon atoms.

[0014] In this embodiment, some organic compounds are shown below:

##STR00006## ##STR00007## ##STR00008## ##STR00009## ##STR00010## ##STR00011##

[0015] Detailed preparation for the organic compound in the present invention could be clarified by exemplary embodiments, but the present invention is not limited to exemplary embodiments. EXAMPLE 1˜7 show the preparation for examples of the organic compound in the present invention. EXAMPLE 8 shows the fabrication of organic EL device and I-V-B, half-life time of organic EL device testing report.

EXAMPLE 1

Synthesis of Compound 1

Synthesis of 2-(biphenyl-2-yl)-7-bromo-9,9-dimethyl-9H-fluor-ene

[0016] ##STR00012##

[0017] A mixture of 35.2 g(100 mmol) of 2,7-dibromo-9,9-dimethyl-9H-fluorene, 21.8 g(110 mmol) of biphenyl-2-ylboronic acid, 2.31 g(2 mmol) of Pd(PPh.sub.3).sub.4, 75 ml of 2M Na.sub.2CO.sub.3, 150 ml of EtOH and 300 ml toluene was degassed and placed under nitrogen, and then heated at 100° C. for 12 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with ethyl acetate and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product(26.8 g, 63.0 mmol, 63%) as a white solid.

Synthesis of 12-bromo-10,10-dimethyl-10H-indeno[2,1-b] triphenylene

[0018] ##STR00013##

[0019] In a 3000 ml three-necked flask that had been degassed and filled with nitrogen, 26.8 g(60 mmol) of 2-(biphenyl-2-yl)-7-bromo-9,9-dimethyl-9H-fluorene was dissolved in anhydrous dichloromethane(1500 ml), 97.5 g(600 mmol) Iron(III)chloride was then added, and the mixture was stirred one hour. Methanol 500 ml were added to the mixture and the organic layer was separated and the solvent removed in vacuo. The residue was purified by column chromatography on silica(hexane-dichloromethane) afforded a white solid(10.7 g, 25.3 mmol, 40%). .sup.1H NMR(CDCl3, 400 MHz): chemical shift(ppm) 8.95(s, 1H), 8.79-8.74(m, 2H), 8.69-8.68(m, 3H), 7.84(d, J=8.0 Hz, 1H), 7.72˜7.65(m, 5H), 7.57(d, J=8.0 Hz, 1H), 1.66(s, 6H).

Synthesis of 2-(10,10-dimethyl-10H-indeno [2,1-b]triphenylen-12-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane

[0020] ##STR00014##

[0021] A mixture of 10.7 g(25.3 mmol) of 12-bromo-10,10-dimethyl-10H-indeno-[1,2-b]triphenylene, 7.7 g(30.3 mmol) of bis(pinacolato)diboron, 0.3 g(0.26 mmol) of Pd(PPh.sub.3).sub.4, 7.4 g(75.4 mmol) of potassium acetate, and 300 ml 1,4-dioxane was degassed and placed under nitrogen, and then heated at 90° C. for 16 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic phase separated and washed with ethyl acetate and water. After drying over magnesium sulfate, the solvent was removed in vacuo. The residue was purified by column chromatography on silica(hexane-dichloromethane) to give product(6.4 g, 13.7mmol, 54%) as a light-yellow solid; .sup.1H NMR(CDCl3, 400 MHz): chemical shift(ppm) 9.03(s, 1H), 8.81(d, J=7.84 Hz, 1H), 8.77(d, J=7.88 Hz, 1H), 8.70˜8.67(m, 3H), 8.02˜7.93 (m, 3H), 7.71˜7.67(m, 4H), 1.69(s, 6H), 1.42(s, 12H)

Synthesis of 12-(anthracen-9-yl)-10,10-dimethyl-10H-indeno [2,1-b]triphenylene

[0022] ##STR00015##

[0023] A mixture of 4.7 g(10 mmol) of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-12-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane, 2.8 g(11 mmol) of 9-bromoanthracene, 0.22 g(0.2 mmol) of tetrakis(triphenyl phosphine)palladium, 20 ml of 2M Na.sub.2CO.sub.3, 20 ml of EtOH and 50 ml toluene was degassed and placed under nitrogen, and then heated at 90° C. overnight. After finishing the reaction, the mixture was allowed to cool to room temperature. Then 150 ml of MeOH was added, while stirring and the precipitated product was filtered off with suction. To give 3.5 g(yield67%) of yellow product which was recrystallized from toluene.

Synthesis of 12-(10-bromoanthracen-9-yl)-10,10-dimethyl-10H-indeno [2,1-b]triphenylene

[0024] ##STR00016##

[0025] The resulting 12-(anthracen-9-yl)-10,10-dimethyl-10H-indeno [2,1-b]triphenylene(3.5 g) and DMF (35 ml) were added to a reaction vessel. N-bromosuccinimide(1.5 g) was added under ice-cooled conditions, and. the mixture was stirred for 9 hours. Water(350 ml) was added, the organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product(3.1 g, 5.2 mmol, 78%) as a yellow solid.

Synthesis of 3-(10-(10,10-dimethyl-10H-indeno [2,1-b] triphenylen-12-yl) anthracen-9-yl)-9-phenyl-9H-carbazole

[0026] ##STR00017##

[0027] A mixture of 3.1 g(5.2 mmol) of 12-(10-bromoanthracen-9-yl)-10, 10-dimethyl-10H-indeno [2,1-b]triphenylene, 2.2 g(6 mmol) of 9-phenyl -3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole, 0.22 g(0.2 mmol) of tetrakis(triphenylphosphine)palladium, 20 ml of 2M Na.sub.2CO.sub.3, 20 ml of EtOH and 50 ml toluene was degassed and placed under nitrogen, and then heated at 110° C. overnight. After finishing the reaction, the mixture was allowed to cool to room temperature. Then 150 ml of MeOH was added, while stirring and the precipitated product was filtered off with suction. To give 2.6 g(yield 67%) of yellow product which was recrystallized from toluene. MS(m/z,FAB.sup.+):761.4, .sup.1H NMR(CDCl.sub.3, 400 MHz): chemical shift(ppm) 9.11(s, 1H), 8.87(d, J=7.84 Hz, 1H), 8.80˜8.75(m, 2H), 8.71˜8.69(m, 2H), 8.28(d, J=7.84 Hz, 1H), 8.22˜8.11(m, 2H), 7.88˜7.82(m, 4H), 7.76˜7.63(m, 10H), 7.61˜7.44(m, 5H), 7.39˜7.28(m, 5H), 1.74(s, 6H).

EXAMPLE 2

Synthesis of Compound6

Synthesis of 10-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-12-yl)-N-phenyl-N-m-tolylanthracen-9-amine

[0028] ##STR00018##

[0029] A mixture of 6.0 g(10 mmol) 12-(10-bromoanthracen-9-yl)-10,10-dimethyl-10H-indeno[2,1-b]triphenylene, 3 g(15.1 mmol) of 3-methyl-N-phenylaniline, 0.05 g(0.2 mmol) of palladium(II)acetate, 0.15 g(0.4 mmol) of 2-(dicyclohexylphosphino)biphenyl, 2 g(20 mmol)of sodium tert-butoxide and 100 ml of O-xylene was refluxed under nitrogen overnight. After finishing the reaction, the solution was filtered at 100° C., to receive the filtrate, and the filtrate was added to 1L MeOH, while stirring and the precipitated product was filtered off with suction. To give 3.1 g(yield45%) of yellow product which was recrystallized from toluene. MS(m/z, FAB.sup.+):701.6

EXAMPLE 3

Synthesis of Compound12

Synthesis of N-(2-chlorophenyl)-9,9-dimethyl-9H-fluoren-2-amine

[0030] ##STR00019##

[0031] A mixture of 6.9 g(25.3 mmol) of 2-bromo-9,9-dimethyl-9H-fluorene, 3.2 g(25.3 mmol) of 2-chloroaniline, 0.11 g(0.5 mmol) of palladium(II) acetate, 0.55 g(1.0 mmol) of 1,1-bis(diphenyl-phosphino)ferrocene, 4.85 g (50.6 mmol) of sodium tert-butoxide and 100 ml toluene was degassed and placed under nitrogen, and then heated at 110° C. for overnight. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic phase separated and washed with ethyl acetate and water. After drying over magnesium sulfate, the solvent was removed in vacuo. The residue was purified by column chromatography on silica gel(hexane-dichloromethane) to give product(4.9 g, 18.0 mmol, 71%) as a light-yellow solid.

Synthesis of 3,3-dimethyl-1,3-dihydroindeno[2,1-b]carbazole

[0032] ##STR00020##

[0033] A mixture of 4.9 g(18.0 mmol) of N-(2-chlorophenyl)-9,9-dimethyl-9H-fluoren-2-amine, 0.4 g(1.6 mmol) of palladium(II) acetate, 75 ml of pivalic acid, 0.8 g of potassium carbonate (6 mmol) and 240 ml 1-methyl-2-pyrrolidone was degassed and placed under nitrogen, and then heated at 130° C. for 24 hours. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was recrystallized from hexane and dichloromethane to give product (2.1 g, 7.4 mmol, yield41%).

Synthesis of 3,3-dimethyl-1-phenyl-1,3-dihydroindeno[2,1-b] carbazole

[0034] ##STR00021##

[0035] A mixture of 4.9 g(18 mmol) 3,3-dimethyl-1,3-dihydroindeno [2,1-b]carbazole, 3.4 g(21.6 mmol) of bromobenzene, 0.1 g(0.4 mmol) of palladium(II)acetate, 0.3 g(0.8 mmol) of 2-(dicyclohexylphosphino)biphenyl, 4 g(40 mmol)of sodium tert-butoxide and 50 ml of o-xylene was refluxed under nitrogen overnight. After finishing the reaction, the solution was filtered at 100° C. to receive the filtrate, and the filtrate was added to 1L MeOH, while stirring and the precipitated product was filtered off with suction. To give(4.1 g, 11.5 mmol, 64%) of yellow product which was recrystallized from toluene.

Synthesis of 10-bromo-3,3-dimethyl-1-phenyl-1,3-dihydro indeno[2,1-b]carbazole

[0036] ##STR00022##

[0037] The resulting of 3,3-dimethyl-1-phenyl-1,3-dihydroindeno [2,1-b]carbazole(4.1 g) and DMF (40 ml) were added to a reaction vessel. N-bromosuccinimide(2 g) was added under ice-cooled conditions, and the mixture was stirred for 6 hours and then left for one night. 400 ml of water was added, the organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product(2.9 g, 6.7 mmol, 72%).

Synthesis of 3,3-dimethyl-l-phenyl-10-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-1,3-dihydroindeno[2,1-b]carbazole

[0038] ##STR00023##

[0039] A mixture of 2.9 g(6.7 mmol) of 10-bromo-3,3-dimethyl-1-phenyl-1,3-dihydroindeno[2,1-b]carbazole, 2.2 g(8.67 mmol) of bis(pinacolato) diboron, 0.36 g(0.32 mmol) of tetrakis(triphenylphosphine)palladium, 2 g (20.28 mmol) of potassium acetate, and 300 ml of 1,4-dioxane was degassed and placed under nitrogen, and then heated at 120° C. for 16 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with ethyl acetate and water, dried with anhydrous magnesium sulfate, the solvent was removed and the product was purified by column using a mixture of hexanes and ethyl acetate as eluent to get 2.4 g of light yellow product (yield76%).

Synthesis of 10-(10-(10,10-dimethyl-10H-indeno[2,1-b] triphenylen-12-yl)anthracen-9-yl)-3,3-dimethyl-l-phenyl-1,3-dihydroindeno[2,1-b] carbazole

[0040] ##STR00024##

[0041] A mixture of 3. g(5 mmol) of 12-(10-bromoanthracen-9-yl)-10, 10-dimethyl-10H-indeno[2,1-b]triphenylene, 2.4 g(5 mmol) of 3,3-dimethyl-1-phenyl-10-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-1,3-dihydroinden o[2,1-b]carbazole, 0.22 g(0.2 mmol) of tetrakis(triphenyl phosphine)palladium, 20 ml of 2M Na.sub.2CO.sub.3, 20 ml of EtOH and 50 ml toluene was degassed and placed under nitrogen, and then heated at 110° C. overnight. After finishing the reaction, the mixture was allowed to cool to room temperature. Than 150 ml of MeOH was added, while stirring and the precipitated product was filtered off with suction. To give 2.6 g (yield67%) of yellow product which was recrystallized from toluene. MS(m/z,FAB.sup.+):877.6, .sup.1H NMR (CDCl.sub.3, 400 MHz): chemical shift(ppm) 9.13(s, 1H), 8.85(d, J=7.84 Hz, 1H), 8.78˜8.74(m, 2H), 8.73˜8.68(m, 2H), 8.28˜8.24(m, 3H), 8.22˜8.11(m, 2H), 7.88˜7.82(m, 4H), 7.76˜7.63(m, 10H), 7.62˜7.43(m, 5H), 7.38˜7.28(m, 5H), 1.74(s, 6H), 1.57(s, 6H).

EXAMPLE 4

Synthesis of Compound17

Synthesis of 2-(10-(10,10-dimethyl-10H-indeno [2,1-b] triphenylen-12-yl)anthracen-9-yl)dibenzo[b,d]furan

[0042] ##STR00025##

[0043] Dibenzo[b,d]furan-2-ylboronic acid instead of 9-phenyl-3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole, except for using the same method as in synthesis Example1, the desired compound of Compound 17(1.4 g, yield=57%) was obtained.MS(m/z,FAB.sup.+):686.3.

EXAMPLE 5

Synthesis of Compound18

Synthesis of 4-(10-(10,10-dimethyl-10H-indeno[2,1-b] triphenylen-12-yl)anthracen-9-yl)dibenzo[b,d]thiophene

[0044] ##STR00026##

[0045] Dibenzo[b,d]thiophen-4-ylboronic acid instead of 9-phenyl-3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole, except for using the same method as in synthesis Example1, the desired compound of Compound18 yield=68%) was obtained. MS(m/z,FAB.sup.+):720.8.

EXAMPLE 6

Synthesis of Compound19

Synthesis of 4-(10-(10,10-dimethyl-10H-indeno[2,1-b] triphenylen-12-yl)anthracen-9-yl)dibenzo[b,d]thiophene

[0046] ##STR00027##

[0047] Dibenzo[b,d]thiophen-4-ylboronic acid instead of 9-phenyl-3-(4,4,5, 5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole, except for using the same method as in synthesis Example 1, the desired compound of Compound19 (1.8 g, yield=68%) was obtained. MS(m/z,FAB.sup.+):720.8.

EXAMPLE 7

Synthesis of Compound20

Synthesis of 4-(10-(10,10-dimethyl-10H-indeno[2,1-b]triphenyl en-12-yl)anthracen-9-yl)dibenzo [b,d]furan

[0048] ##STR00028##

[0049] Dibenzo[b,d]furan-4-ylboronic acid instead of 9-phenyl-3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole, except for using the same method as in synthesis Example1, the desired compound of Compound20 (2.6 g, yield=53%) was obtained. MS(m/z,FAB.sup.+):686.4.

General Method of Producing Organic El Device

[0050] ITO-coated glasses with 9-12 ohm/square in resistance and 120˜160 nm in thickness are provided(hereinafter ITO substrate) and cleaned in a number of cleaning steps in an ultrasonic bath(e.g. detergent, deionized water). Before vapor deposition of the organic layers, cleaned ITO substrates are further treated by UV and ozone. All pre-treatment processes for ITO substrate are under clean room(class 100).

[0051] These organic layers are applied onto the ITO substrate in order by vapor deposition in a high-vacuum unit(10.sup.−7 Torr), such as: resistively heated quartz boats. The thickness of the respective layer and the vapor deposition rate (0.1˜0.3 nm/sec) are precisely monitored or set with the aid of a quartz-crystal monitor. It is also possible, as described above, for individual layers to consist of more than one compound, i.e. in general a host material doped with a dopant material. This is achieved by co-vaporization from two or more sources.

[0052] Dipyrazino [2,3-f:2,3-]quinoxaline-2,3,6,7,10,11-hexacarbonitrile (HAT-CN) is used as hole injection layer in this organic EL device, N,N-Bis (naphthalene-1-yl)-N,N-bis(phenyl)-benzidine(NPB) is most widely used as the hole transporting layer; 10, 10-dimethyl-12-(10-(4-(naphthalene-1-yl)phenyl) anthracen-9-yl)-10H-indeno [2,1-b]triphenylene (H3) and 10, 10-dimethyl-13-(10-(3-(naphthalen-2-yl)phenyl)anthracen-9-yl)-10H-indeno [2,1-b]triphenyle ne(H4) are used as emitting host in organic EL device and N1,N1,N6,N6-tetram-tolylpyrene-1,6-diamine(D1) is used as blue guest for comparison; HB3(see the following chemical structure) are used as hole blocking material(HBM) and 1-(4-(10-(naphthalen-2-yl)anthracen-9-yl)phenyl)-2-phenyl-1H-benzo[d]imidazole(ET2) is used as electron transporting material to co-deposit with 8-hydroxyquinolato-lithium(LiQ) in organic EL device. The prior art of OLED materials for producing standard organic EL device control and comparable material in this invention shown its chemical structure as follows:

##STR00029## ##STR00030## ##STR00031##

[0053] A typical organic EL device consists of low work function metals, such as Al, Mg, Ca, Li and K, as the cathode by thermal evaporation, and the low work function metals can help electrons injecting the electron transporting layer from cathode. In addition, for reducing the electron injection barrier and improving the organic EL device performance, a thin-film electron injecting layer is introduced between the cathode and the electron transporting layer. Conventional materials of electron injecting layer are metal halide or metal oxide with low work function, such as: LiF, LiQ, MgO, or Li.sub.2O. On the other hand, after the organic EL device fabrication, EL spectra and CIE coordination are measured by using a PR650 spectra scan spectrometer. Furthermore, the current/voltage, luminescence/voltage and yield/voltage characteristics are taken with a Keithley 2400 programmable voltage-current source. The above-mentioned apparatuses are operated at room temperature(about 25° C.) and under atmospheric pressure.

EXAMPLE 8

[0054] Using a procedure analogous to the above mentioned general method, fluorescent emitting organic EL device having the following device structure was produced(See FIG. 1). Device: ITO/HAT-CN(20 nm)/NPB (110 nm)/Emitting host doped 5% Emitting guest(30 nm)/HB3/ET2 doped 50%LiQ(35 nm)/LiQ(1 nm)/Al(160 nm). The I-V-B(at 1000 nits) and half-life time of fluorescent emitting organic EL device testing report as Table 1. The half-life time is defined that the initial luminance of 1000 cd/m.sup.2 has dropped to half.

TABLE-US-00001 TABLE 1 Emitting Emitting Voltage Efficiency CIE Half-life time Host Guest (V) (cd/A) (y) (hour) H3 D1 5.0 5.6 0.18 450 H3 C1 4.5 4.8 0.11 380 H3 C6 4.8 4.6 0.10 350 H3 C12 4.8 4.5 0.09 480 H3 C17 5.0 4.4 0.12 220 H3 C18 4.5 4.0 0.11 180 H3 C19 4.5 3.8 0.11 250 H3 C20 4.5 4.2 0.12 280 H4 D1 5.5 5.2 0.19 420 H4 C1 4.8 4.2 0.11 300 H4 C6 4.5 4.6 0.09 250 H4 C12 5.0 4.0 0.10 400 H4 C17 4.8 4.5 0.11 200 H4 C18 4.6 4.2 0.12 110 H4 C19 4.8 3.6 0.12 200 H4 C20 4.5 4.0 0.12 240

[0055] In the above preferred embodiments for organic EL device test report(see Table 1), we show that the organic compound with a general formula(1) used as emitting guest material for organic EL in the present invention display good performance. More specifically, the organic EL device in the present invention use the organic compound with a general formula(1) as emitting guest material to collocate with emitting host material such as H3 and H4 shown lower power consumption, higher efficiency and longer half-life time.

[0056] To sum up, the present invention discloses an organic compound with a general formula(1) used as emitting guest material for organic EL device. The mentioned organic compound are represented by the following formula(1)

##STR00032##

wherein A represents the formula(2) to formula(5)

##STR00033##

m represents an integer of 0 to 10, n represents an integer of 0 or 1, X is divalent bridge selected from the atom or group consisting from O, S and NR.sub.7, Y is divalent bridge selected from the atom or group consisting from O, S, C(R.sub.8)(R.sub.9), Si(R.sub.10)(R.sub.11) and NR.sub.12, Ar.sub.1 and Ar.sub.2 represent a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, R.sub.1 to R.sub.12 are independently selected from the group consisting of a hydrogen atom, a halide, a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, and a substituted or unsubstituted aralkyl group having 6 to 30 carbon atoms.

[0057] Obvious many modifications and variations are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims the present invention can be practiced otherwise than as specifically described herein. Although specific embodiments have been illustrated and described herein, it is obvious to those skilled in the art that many modifications of the present invention may be made without departing from what is intended to be limited solely by the appended claims.