ADHESION-MODIFIED OLEFINIC THERMOPLASTIC ELASTOMERS, IN PARTICULAR TPE-V, TPE-O

Abstract

An olefinic thermoplastic elastomer composition comprising a rubber component and a polyolefin, characterised in that the composition further comprises an adhesion promoter system which in turn comprises one or more first adhesion promoters from the group of wetting adhesion promoters and one or more second adhesion promoters from the group of chemically reactive adhesion promoters.

Claims

1-11. (canceled)

12. Olefinic thermoplastic elastomer composition comprising a rubber component and a polyolefin, further comprising an adhesion promoter system which in turn comprises one or more first adhesion promoters from the group of wetting adhesion promoters and one or more second adhesion promoters from the group of chemically reactive adhesion promoters and one or more additives, selected from reinforcing and non-reinforcing fillers, processing oils, diluting or extending oils, plasticisers, waxes, stabilisers, oxidation inhibitors, cross-linking agents, processing aids, internal and external lubricants, pigments and colouring agents, wherein the thermoplastic polyolefin component is a thermoplastic crystalline or semi-crystalline polyolefin homopolymer and/or a thermoplastic crystalline or semi-crystalline polyolefin copolymer, the mono-olefin monomer of which comprises 2 to 7 carbon atoms, selected from: ethylene, propylene, 1-butene, isobutylene, 1-pentene, 1-hexene, 1-octene, 3-methyl-1-pentene, 4-methyl-1-pentene and 5 methyl-1-hexene, wherein the rubber component is selected from: the terpolymer rubbers of ethylene, propylene and a non-conjugated diene (EPDM) and/or a copolymer, specifically ethylene propylene rubber (EPR), ethylene/α-olefin copolymer rubber (FAM) or ethylene/α olefin/diene terpolymer rubber (EADM), wherein the group of wetting adhesion promoters is formed of ionomers, wherein the group of chemically reactive adhesion promoters is formed of maleic anhydride-grafted polymers, wherein the polymeric backbone thereof is formed by polypropylene, polyethylene, polypropylene-polyethylene copolymers, poly-α-olefins, ethylene-propylene-diene rubber (EPDM) and polyamides and is formed of graftable siloxanes, epoxides or epoxy or glycidyl compounds, wherein the adhesion promoter system content of the composition is between 1.5 and 10 wt. %.

13. Olefinic thermoplastic elastomer composition according to claim 12, characterised in that the mono-olefin monomer of the thermoplastic polyolefin component comprises 3 to 6 carbon atoms and is preferably propylene.

14. Olefinic thermoplastic elastomer composition according to claim 12, characterised in that the adhesion promoter system comprises two to eight, in particular two to six, particularly preferably two to four, adhesion promoters.

15. Method for producing an adhesion-modified TPE-V or TPE-O according to claim 1 in one step in which the adhesion promoter combination is added during the cross-linking step or in a plurality of steps in which the finished TPE-V compound is only subsequently adhesion-modified by means of mixing units such as single-screw extruders, twin screw extruders or Banbury mixers.

16. Use of an adhesion-modified TPE-V or TPE-O according to claim 1 for producing components in the automotive industry, shipbuilding, machine building, the electrical/electronics industry, the building and construction industry, medical technology, the pharmaceutical industry, the furniture industry, the packaging industry, the sports and leisure industry and in the field of office supplies, household goods and cosmetics, in order to produce metal polymer composites.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0018] The olefinic thermoplastic elastomer composition comprises a rubber component, a polyolefin and an adhesion promoter system, the adhesion promoter system comprising in turn one or more first adhesion promoters from the group of wetting adhesion promoters and one or more second adhesion promoters from the group of chemically reactive adhesion promoters. In this case, the rubber component is in particular cross-linkable in the case of TPE-V.

[0019] According to the invention, the thermoplastic polyolef in component is a thermoplastic crystalline or semi-crystalline polyolefin homopolymer and/or a thermoplastic crystalline or semi-crystalline polyolef in copolymer, the mono-olefin monomer of which comprises 2 to 7 carbon atoms; the monomer is in particular selected from: ethylene, propylene, 1-butene, isobutylene, 1-pentene, 1-hexene, 1-octene, 3-methyl-1-pentene, 4-methyl-1-pentene and 5-methyl-1-hexene. The mono-olefin monomer preferably comprises 3 to 6 carbon atoms, and is particularly preferably propylene.

[0020] The in particular cross-linkable rubber component is selected from: the terpolymer rubbers of ethylene, propylene and a non-conjugated diene (EPDM) and/or copolymers, for example ethylene propylene rubber (EPR), ethylene/α-olefin copolymer rubber (FAM) or ethylene/α-olefin/diene terpolymer rubber (EADM).

[0021] The adhesion promoter system necessarily comprises two types of adhesion promoters:

[0022] The group of adhesion promoters that provide for optimum wetting includes ionomers and ethylene vinyl-acetate rubber (EVM) having various vinyl acetate contents and comprising maleic anhydride-grafted polymers, polypropylene, polyethylene, polypropylene-polyethylene copolymers, poly-α-olefins, ethylene-propylene-diene rubbers (EPDM) and polyam ides forming the polymeric backbone thereof.

[0023] The group of adhesion promoters that provide for a chemical reaction between the TPE and the substrate is formed of adhesion promoters comprising one of the following functional groups: anhydride, epoxide, silane and esters thereof, carboxyl group, ester group and acid chloride. Coupling agents from the group of maleic anhydride-grafted polymers are particularly suitable, the polymeric backbone thereof being formed by polypropylene, polyethylene, polypropylene-polyethylene copolymers, poly-α-olefins, ethylene-propylene-diene rubber (EPDM), polyamides, graftable siloxanes, vinyl siloxanes and esters thereof, epoxides such as chain extenders, or epoxy or glycidyl compounds.

[0024] The adhesion promoter system comprises two to eight, in particular two to six, particularly preferably two to four, adhesion promoters, at least one of which belongs to one of the two required adhesion promoter groups and at least one other of which belongs to the other of the two required adhesion promoter groups, as already mentioned. Preferably, there are the same number of each of the two adhesion promoters groups; however, this is not absolutely necessary. According to the invention, the adhesion promoter system content of the composition is between 0.5 and 25 wt. %, preferably between 1.0 and 15 wt. %, particularly preferably between 1.5 and 10 wt. %. According to the invention, in this respect, the content of an adhesion promoter group is no lower than 0.5 wt. %.

[0025] Furthermore, the composition according to the invention may contain one or more additives, selected from reinforcing and non-reinforcing fillers, processing oils, diluting or extending oils, plasticisers, waxes, stabilisers, oxidation inhibitors, cross-linking agents, processing aids, internal and external lubricants, pigments and colouring agents. The cross-linking agents may be for example phenol resin-based cross-linking agents having, as the initiator, tin salts, for example tin halides or tin halide batches that may or may not contain water of crystallisation, and having metal oxides, for example calcium oxide, magnesium oxide and zinc oxide, as the retarder.

[0026] The cross-linking agents may also be organic peroxide-based cross-linking agents and one to three co-agents such as modified acrylates, methacrylates, isourates or cyanurates, polybutadienes, dimaleimides and the like, for example N,N′-m-phenylenedimaleimide, zinc diacrylate, triallyl isocyanurate (TIAC), triallyl cyanurate (TAC), trimethylolpropane triacrylate (TMPTA), trimethylolpropane trimethacrylate (TRIM), 1,2-polybutadiene such as liquid polybutadiene (Ricon 153) or solid syndiotactic polybutadiene, polysiloxane containing vinyl, propyl or ethoxy groups, and the like. Peroxides are in particular di-t-butyl peroxides, dicumyl peroxides, di(t-butylperoxyisopropyl)benzene, 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane, 2,5-dimethyl-2,5-di-(t-butylperoxy) hexyne and 3,3,5,7,7-pentamethyl-1,2,4-trioxepane. TPE-Os do not require any cross-linking agents. Other additives may be phenol resins having a percentage by weight of 0.01 wt. % to 15 wt. %, tin halides having a percentage by weight of 0.01 wt. % to 5 wt. % and metal oxides having a percentage by weight of 0 wt. % to 3 wt. %. Other additives, including fillers as described in “Rubber World Magazine Blue Book” and in “Zweifel et al., Plastics Additives Handbook, Hanser 2009”, are explicitly included here in the disclosure.

[0027] Fillers and extenders include conventional inorganic substances such as calcium carbonate, clays, silica, talcum, titanium dioxide and carbon black. In this case, the fillers can in particular have a plurality of additive effects. In general, the rubber processing oils that are suitable are paraffinic, naphthenic or aromatic oils derived from petroleum fractions. The type of the selected oil can be one which is usually used in combination with the specific rubber(s) of the present composition. These additives can comprise a significant amount of the formulated total composition.

[0028] In addition to glass, steel, metals, polar polymers such as polyamides, above all, suitable technical resins may also be considered as polar substrates. In particular, the invention is suitable for coating various polyamides, for example unfilled polyamide 6, unfilled polyamide 66, filled polyamide 6 and filled polyamide 66, boron glasses, quartz glasses, glasses, metals such as aluminium, iron or copper, and metal alloys such as stainless steel, steel, V2A-steel, brass or bronze.

[0029] The thermoplastic elastomer composition of the present invention can be applied to the substrate using various different methods and, owing to its composition, generates adhesion without any further special pretreatment of the surface. The surface of the substrate is optionally kept oil-free and/or is heated.

Examples

[0030] Where the sum of the percentages does not equal 100% in the following examples, one or more of the above-mentioned additives make up the remaining percentage.

[0031] Example 1: a thermoplastic elastomer composition according to the invention is composed of 20% PP, 40% EPDM, 10% fillers and 20% oil. It also contains 4% PP-g-MAH and 2% EPR-G-MAH. The cross-linking system is a phenolic cross-linking system. Example 1 has a Shore hardness of 40 D, a peel strength of 815 N on aluminium, 830 N on stainless steel and 780 N on steel. The failure mode is a cohesive failure mode on aluminium and a peel failure mode on the other two materials.

[0032] Example 2: a thermoplastic elastomer composition according to the invention is composed of 20% PP, 37% EPDM, 10% fillers and 20% oil. It also contains 6% PP-g-MAH and 3% ionomer. The cross-linking system is a phenolic cross-linking system. Example 2 has a Shore hardness of 40 D, a peel strength of 812 N on aluminium, 793 N on stainless steel and 822 N on steel. The relevant failure mode is a cohesive failure mode.

[0033] Example 3: a thermoplastic elastomer composition according to the invention is composed of 90.5% TPE-V. It also contains 7% PP-g-MAH and 2.5% ionomer. The cross-linking system is second extrusion. Example 3 has a Shore hardness of 50 A, a peel strength of 226 N on aluminium, 258 N on stainless steel and 253 N on steel. The relevant failure mode is a cohesive failure mode.

[0034] Example 4: a thermoplastic elastomer composition according to the invention is composed of 90% TPE-V. It also contains 6% PP-g-MAH and 4% EPR-g-MAH. The cross-linking system is second extrusion. Example 4 has a Shore hardness of 50 A, a peel strength of 258 N on aluminium, 231 N on stainless steel and 258 N on steel. The relevant failure mode is a cohesive failure mode.

[0035] Example 5: a thermoplastic elastomer composition according to the invention is composed of 7% polypropylene, 54% EPDM, 10% fillers and 17% oil. It also contains 4.5% PP-g-MAH and 4.5% EPR-g-MAH. The cross-linking system is a phenol resin. Example 5 has a Shore hardness of 55 A, an ultimate elongation of 260%, a σ max of 4.1 MPa, a density of 0.961 g/cm.sup.3, a peel strength of 67 N. The failure mode is a cohesive failure mode.

[0036] Example 6: a thermoplastic elastomer composition according to the invention is composed of 9% polypropylene, 56% EPDM, 10% fillers and 12% oil. It also contains 5% PP-g-MAH and 5% EPR-g-MAH. The cross-linking system is a peroxide. Example 6 has a Shore hardness of 55 A, an ultimate elongation of 400%, a σ max of 5.1 MPa, a density of 0.940 g/cm.sup.3, a peel strength of 84.6 N. The failure mode is a cohesive failure mode.

[0037] Example 7: a thermoplastic elastomer composition according to the invention is composed of 8% polypropylene, 49% EPDM, 9% fillers and 22% oil. It also contains 5% PP-g-MAH and 5% EPR-g-MAH. The cross-linking system is a peroxide. Example 6 has a Shore hardness of 55 A, an ultimate elongation of 480%, a σ max of 4.3 MPa, a density of 0.913 g/cm.sup.3, a peel strength of 81.5 N. The failure mode is a cohesive failure mode.

[0038] Example 8: the last example is composed of 40% polypropylene, 42% EPDM and 10% fillers. It also contains 5% PP-g-MAH and 2.5% ionomer. Example 12 has a Shore hardness of 40 D, a peel tensile strength of 354 N on aluminium, 608 N on stainless steel, 576 N on steel and 391 N on galvanised steel.

[0039] A comparative example uses Santoprene 191-55PA. The cross-linking system is a phenol resin. Comparative example 7 has a Shore hardness of 55 A, an ultimate elongation of 290%, a σ max of 2.9 MPa, a density of 0.950 g/cm.sup.3, a peel strength of just 34.0 N. The failure mode is a debonding failure mode.

[0040] The TPE-Vs according to the invention are produced in mixing units such as single-screw extruders, twin screw extruders, Banbury mixers or the like. They are produced either in one step in which the adhesion promoter combination is added into the mixing unit during the cross-linking step or alternatively in a plurality of steps, the finished TPE-V being subsequently adhesion-modified in the mixing units.

[0041] Using the preparation according to the invention, adhesion can be generated in one or more steps, without pretreating the polar surfaces. The finished adhesion-modified compound is sprayed directly onto a polar substrate by means of an injection-moulding machine, which substrate may be heated, in particular up to >50° C. Direct co-extrusion, two-component injection moulding (also referred to as overmoulding) and co-moulding applications are also possible, it also being possible to injection-mould sheets or complex geometries in a preliminary step without any adhesive bonds in the mould and to subsequently press said sheets or complex geometries against polar substrates such as metal or glass components. Using commonly used pressing methods, such as hydraulic pressing, it is possible to obtain durable solid metal-TPE-V composite parts and metal-TPE-V-metal sandwich structures in short pressing times, even using two different metals, such as steel and aluminium. Therefore, processing is not limited to melting processes.

[0042] The invention also makes it possible to form sandwich structures from two different metals such as steel and aluminium by means of a TPE-V intermediate layer, and this creates new and versatile possibilities in lightweight construction; it is in particular possible to produce new components in the automotive industry, in shipbuilding and in the electrical/electronics industry, which components are metal polymer composites. Other fields in which the invention can be used are the building and construction industry, office supplies, household goods, cosmetics, generally in machine building, medical technology, the pharmaceutical industry, the furniture industry, the packaging industry and also in the sports and leisure industry. In other words, the invention can be used in any field in which good adhesive properties are required and in which it is useful to use metal polymer composites.

[0043] According to the invention, the finished adhesion-modified compound can in this case be applied directly to a polar substrate by means of an injection-moulding machine (SGM), the surface temperature of which substrate should be >50° C. in the case of polymer substrates. In the case of metals, metal alloys and/or blends, the surface temperature should be >60° C.; this temperature can be reached using water or oil thermostats, induction heating, etc. Inorganic substrates such as sheet steel have to be oil-free.

[0044] The application can also be achieved by co-extrusion when the adhesion-modified TPE-V is applied to a heated polar substrate; for metals, the same restrictions apply as those in injection-moulding methods.

[0045] However, processing is not limited to melting processes; sheets and other geometries can also be injection-moulded in a preliminary step without adhesion in the moulds and adhesively pressed together with polar substrates, which in this case are intended to predominantly be metal components, by means of pressing processes in commonly used presses, e.g. hydraulic presses, within the shortest possible time period. In this case too, only the metal parts have to be oil-free. Solid metal-TPE-V composite parts are formed by the pressing process in this case, it also being possible to produce metal-TPE-V-metal sandwich structures, even using two different types of metal, e.g. steel-TPE-V-aluminium composites.

[0046] The hardness of the modified TPE-V can be in the range of from A 30 to D 60, without this causing the adhesion forces to be reduced as a result of changes to the formulation.