ECONOMICAL TIMEPIECE DISPLAY COMPONENT

Abstract

Economical method for manufacturing a timepiece display or hand-fitting component, wherein: there is chosen a first material which is easy to shape or to machine; a workpiece is made in the first material; a second material is chosen to make each aesthetical and/or visible surface of component, which is an amorphous metal alloy or has a nanocrystalline structure or includes nickel or nickel-phosphorus, or which is a pure metal or an alloy of gold and/or silver and/or copper and/or rhodium and/or titanium and/or aluminium; the workpiece is coated, at least on the surfaces intended to remain visible on the component, with a thick layer, of an initial thickness greater than 20 micrometres, of the second material; at least one aesthetical and/or visible surface, is diamond tool machined, removing all or part of the thick layer.

Claims

1. An economical method of manufacturing a timepiece display or hand-fitting component including at least one aesthetical and/or visible surface, wherein the following steps are performed in succession: there is chosen a first material that is easy to shape by deformation, and/or machining and/or injection and/or casting and/or galvanic growth, in order to make a workpiece; a workpiece is made in said first material: a second material is chosen to make each said aesthetical and/or visible surface, which is an amorphous metal alloy or has a nanocrystalline structure or includes nickel or nickel-phosphorus, or which is a pure metal or an alloy of gold and/or silver and/or copper and/or rhodium and/or titanium and/or aluminium; said workpiece is coated, at least on the surfaces intended to remain visible on the component in its operating position, with a thick layer, of an initial thickness greater than or equal to 20 micrometres, of said second material; at least one said aesthetical and/or visible surface which is intended to remain visible, is diamond tool machined, removing at least part of said thick layer of said second material.

2. The method according to claim 1, wherein said thick layer of said second material is made with a thickness greater than or equal to 50 micrometres.

3. The method according to claim 1, wherein said display or hand-fitting component is made with at least one said aesthetical and/or visible surface bordered by a protruding edge, wherein, said protruding edge, which delimits said aesthetical and/or visible surface, is made during the diamond machining.

4. The method according to claim 1, wherein, during said diamond machining operation, all said aesthetical and/or visible surfaces intended to remain visible are diamond machined, removing part of said thick layer of said second material, and, if comprised in said display or hand-fitting component, all the protruding edges which delimit said aesthetical and/or visible surfaces are diamond machined.

5. The method according to claim 1, wherein, during said diamond machining operation, at least one said aesthetical and/or visible surface intended to remain visible is diamond machined, removing part of said thick layer of said second material, with a surface condition comprised between 2 nm Ra and 100 nm Ra.

6. The method according to claim 1, wherein, during said diamond machining operation, there is kept a residual thickness greater than or equal to 5 micrometres of said thick layer of said second material, on each said aesthetical and/or visible surface.

7. The method according to claim 1, wherein, during said machining operation, at least 50% of the initial thickness of said thick layer of said second material is removed.

8. The method according to claim 1, wherein a galvanic or PVD or CVD or ALD or chemical colouring operation is performed to a small thickness of less than 5 micrometres, on at least one of said aesthetical and/or visible surfaces intended to remain visible, after said diamond machining operation.

9. The method according to claim 1, wherein said first material is chosen from among alloys of copper and/or aluminium and/or zinc.

10. The method according to claim 9, wherein brass is chosen for said first material.

11. The method according to claim 9, wherein an aluminium alloy is chosen for said first material.

12. The method according to claim 9, wherein a zinc alloy is chosen for said first material.

13. The method according to claim 1, wherein a POM or PS or PC or a polymer is chosen for said first material.

14. The method according to claim 13, wherein a charged material is chosen for said first material to make the first material electrically conductive.

15. The method according to claim 1, wherein said second material is chosen to be different from said first material.

16. The method according to claim 1, wherein nickel-phosphorus is chosen for said second material.

17. The method according to claim 1, wherein said workpiece is coated with said thick layer of said second material by bulk chemical deposition.

18. The method according to claim 1, wherein said workpiece is coated with said thick layer of said second material by electrodeposition.

19. The method according to claim 1, wherein said workpiece is made by deformation or stamping or punching.

20. The method according to claim 1, wherein said workpiece is made hollow and/or including at least one mounting foot.

21. The method according to claim 1, wherein said display or hand-fitting component is made in the form of a hand or an applique or a numeral or a symbol or a monogram or an indicator or an index or an aperture surround.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] Other features and advantages of the invention will appear upon reading the following detailed description, with reference to the annexed drawings, in which:

[0011] FIGS. 1 to 10 show schematic and cross-sectional views of different steps for implementation of the method according to the invention, in different alternatives:

[0012] FIG. 1 represents the manufacture of a workpiece in a first material.

[0013] FIG. 2 represents a blank formed by the same workpiece, coated with a thick layer of a second material.

[0014] FIG. 3 represents the diamond machining of an upper aesthetical and/or visible surface of this blank.

[0015] FIG. 4 represents the component finished by diamond machining all the aesthetical and/or visible surfaces of the blank.

[0016] FIG. 5 shows a perspective view of one such finished and ready-to-use component.

[0017] FIGS. 6 to 13 show schematic, perspective views of non-limiting examples of implementation of the invention:

[0018] FIG. 6 represents a hollow hand, with transverse and longitudinal cross-sections in FIGS. 6A and 6B.

[0019] FIG. 7 represents an applique provided with two feet.

[0020] FIG. 8 represents a numeral provided with two feet.

[0021] FIG. 9 represents a symbol provided with two feet.

[0022] FIG. 10 represents a monogram provided with one foot.

[0023] FIG. 11 represents an indicator.

[0024] FIG. 12 represents an index provided with two feet.

[0025] FIG. 13 represents an aperture surround provided with four feet.

[0026] FIG. 14 is a block diagram featuring a watch comprising a component made by the method according to the invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0027] The invention proposes to reduce both the cost and the weight of external or hand-fitting components, while ensuring a flawless appearance for such visible components and reducing manufacturing scrap as far as possible.

[0028] The invention proposes to form a component whose surface portion is made in a material compatible with finishing machining in order to obtain a regular surface finish with very low roughness.

[0029] This surface portion is formed in a thickness sufficient to ensure the homogeneity of the material, and thus to guarantee the final finish quality after machining.

[0030] The preferred finishing machining is diamond tool machining.

[0031] The invention thus concerns an economical method for manufacturing a timepiece display or hand-fitting component 1, formed by a hand 11, an applique 12, or similar, comprising at least one aesthetical and/or visible surface 2 intended to be visible to the user of a watch or similar.

[0032] According to the invention, the following steps are performed in succession: [0033] there is chosen a first material that is easy to shape by deformation and/or machining and/or injection and/or casting and/or galvanic growth, in order to make a workpiece 3; [0034] a workpiece 3 is made in this first material; [0035] a second material is chosen to make each aesthetical and/or visible surface 2, which is an amorphous metal alloy or has a nanocrystalline structure or includes nickel or nickel-phosphorus, or which is a pure metal or an alloy of gold and/or silver and/or copper and/or rhodium and/or titanium and/or aluminium; [0036] workpiece 3 is coated, at least on the surfaces intended to remain visible on the component in its operating position, with a thick layer 4, of an initial thickness E greater than or equal to 20 micrometres, of the second material; [0037] at least one aesthetical and/or visible surface 2 intended to remain visible is diamond machined, removing at least one part of an overthickness 5 comprised in thick layer 4 of the second material, with respect to the geometric position of the aesthetical and/or visible surface 2 concerned.

[0038] More particularly, overthickness 5 is entirely removed over the aesthetical and/or visible surface 2 concerned, during this first diamond machining operation, which may also be the only operation, depending on the appearance desired for the finished component 1.

[0039] In a particular implementation of the invention, thick layer 4 of the second material is made with an initial thickness E greater than or equal to 50 micrometres.

[0040] In a particular implementation of the invention, component 1 is made with at least one such aesthetical and/or visible surface 2 bordered by a protruding edge 9, and, during diamond machining, protruding edge 9 is made and delimits aesthetical and/or visible surface 2.

[0041] In a particular implementation of the invention, during the diamond machining operation, all the aesthetical and/or visible surfaces 2 intended to remain visible are diamond machined, removing at least part of overthickness 5 comprised in thick layer 4 of the second material, and, when comprised in component 1, all the protruding edges 9 which delimit these aesthetical and/or visible surfaces 2 are diamond machined.

[0042] In a particular implementation of the invention, during the diamond machining operation, at least one aesthetical and/or visible surface 2 intended to remain visible is diamond machined, removing part of thick layer 4 of the second material, with a surface condition comprised between 2 nm Ra and 100 nm Ra.

[0043] In a particular implementation of the invention, during the diamond machining operation, there is kept a residual thickness ER greater than or equal to 5 micrometres of thick layer 4 of the second material, on each aesthetical and/or visible surface 2.

[0044] In a particular implementation of the invention, during the diamond machining operation, at least 50% of initial thickness E of thick layer 4 of the second material is removed.

[0045] In a particular implementation of the invention, a galvanic or PVD or CVD or ALD colouring operation is performed to a small thickness of less than 5 micrometres, on at least aesthetical and/or visible surfaces 2 intended to remain visible, after the diamond machining operation.

[0046] In a particular implementation of the invention, the first material is chosen from among alloys of copper and/or aluminium and/or zinc.

[0047] In a particular implementation of the invention, brass is chosen for the first material.

[0048] In a particular implementation of the invention, an aluminium alloy is chosen for the first material.

[0049] In a particular implementation of the invention, a zinc alloy is chosen for the first material.

[0050] In a particular implementation of the invention, a POM or PS or PC or polymer is chosen for the first material.

[0051] In a particular implementation of the invention, a charged material is chosen for the first material to make it electrically conductive.

[0052] In a particular implementation of the invention, the second material is chosen to be different from the first material.

[0053] In a particular implementation of the invention, nickel-phosphorus is chosen for the second material.

[0054] In a particular implementation of the invention, workpiece 3 is coated with thick layer 4 of the second material by bulk chemical deposition.

[0055] In a particular implementation of the invention, workpiece 3 is coated with thick layer 4 of the second material by electrodeposition.

[0056] In a particular implementation of the invention, workpiece 3 is made by deformation or stamping or punching.

[0057] In a particular implementation of the invention, workpiece 3 is made hollow and/or including at least one mounting foot 10,

[0058] The creation of a hollow component 1, with a cavity 70 is advantageous in terms of weight and economy of materials, in particular when component 1 is a hand 11, shown here with a pipe 110, thereby minimising the unbalance.

[0059] In various particular implementations of the invention, display or hand-fitting component 1 is made in the form of a hand 11 or an applique 12 or a numeral 13 or a symbol 14 or a monogram 15 or an indicator 16 or an index 17 or an aperture surround 18.

[0060] The invention also concerns a watch 100 including at least one display or hand-fitting component 1 made by this method.

[0061] The diamond tool machined finish of such a component is distinguished by the perfect quality of its surface condition (mirror) and by the intersection of the sides which define sharp edges, which cannot be ensured by any other manufacturing method.