RUBBER TUBE, AND METHOD OF PRODUCING THE SAME

Abstract

A rubber tube has an inner surface at least partly roughed so that the ratio (Rz/D) of the maximum height Rz of the inner surface to the inner diameter D of the tube is not less than 0.038. The ratio (Rp/D) of the maximum peak height Rp of the inner surface to the inner diameter D of the tube may be not less than 0.019. The ratio (Rv/D) of the maximum valley depth Rv of the inner surface to the inner diameter D of the tube may be not less than 0.019. The ratio (Ra/D) of the arithmetic average roughness Ra of the inner surface to the inner diameter D of the tube may be not less than 0.0036. The ratio (Rq/D) of the root mean square height Rq of the inner surface to the inner diameter D of the tube maybe not less than 0.0046. Thus, the rubber tube has a reduced adhesiveness.

Claims

1. A rubber tube having an inner surface roughened so that a ratio (R/D) of an inner surface roughness R of the tube to an inner diameter D of the tube is not less than a predetermined level.

2. The rubber tube according to claim 1, wherein the roughened inner surface includes an inner surface portion of a collapsible part of the tube.

3. The rubber tube according to claim 1, wherein the inner surface roughness R is a maximum height Rz, and a ratio Rz/D is not less than 0.038.

4. The rubber tube according to claim 1, wherein the inner surface roughness R is a maximum peak height Rp, and a ratio Rp/D is not less than 0.019.

5. The rubber tube according to claim 1, wherein the inner surface roughness R is a maximum valley depth Rv, and a ratio Rv/D is not less than 0.019

6. The rubber tube according to claim 1, wherein the inner surface roughness R is an arithmetic average roughness Ra, and a ratio Ra/D is not less than 0.0036.

7. The rubber tube according to claim 1, wherein the inner surface roughness R is a root mean square height Rq, and a ratio Rq/D is not less than 0.0046.

8. The rubber tube according to claim 1, wherein a material for the tube is a fluororubber

9. The rubber tube according to claim 8, wherein the fluororubber is FKM.

10. The rubber tube according to claim 1, which is a tube for a tube pump or a tube for a pinch valve.

11. A method of producing a rubber tube, the method comprising the steps of: preparing an outer mold defining an outer shape of the tube and an inner core rod defining an inner surface geometry of the tube; placing the inner core rod along a center line of the outer mold; and molding the rubber tube by the outer mold and the inner core rod; wherein the inner core rod has a surface portion roughened to a predetermined roughness.

12. The rubber tube producing method according to claim 11, wherein the roughened surface portion of the inner core rod is to be in contact with a part of an inner surface of the tube excluding 5-mm wide end portions of the tube.

13. The rubber tube producing method according to claim 11, wherein the surface portion of the inner core rod is roughened by a shot blast process.

14. The rubber tube producing method according to claim 13, wherein a blasting material for the shot blast process is glass beads.

Description

BRIEF DESCRIPTION OF THE DRAWING

[0017] FIGURE is a schematic perspective view illustrating a mold for molding a rubber tube according to one embodiment of the present invention.

EMBODIMENTS OF THE INVENTION

[0018] Embodiments of the present invention will hereinafter be described specifically.

<Mold>

[0019] FIGURE is a schematic perspective view illustrating a mold 10 for molding a rubber tube according to one embodiment of the present invention.

[0020] The mold 10 includes a lower mold 11, an upper mold 12 and an inner core rod 13 as its constituents. The mold 10 is a mold for molding a rubber tube having an inner diameter of 1 mm and an outer diameter of 2 mm. The surface (peripheral surface) of the inner core rod 13 is to be in contact with an inner surface of the molded rubber tube to define the inner surface geometry of the molded rubber tube.

[0021] The inner core rod 13 is a metal rod having a diameter of 1 mm. The surface of the inner core rod 13 is mirror-polished, and then a surface portion 13f of the inner core rod excluding end portions is properly roughened, for example, by a shot blast process.

[0022] A metal blasting material, a ceramic blasting material, a resin blasting material or a glass blasting material may be used for the shot blast process. The glass blasting material is particularly preferred because the surface of the inner core rod 13 is not contaminated.

[0023] The surface end portions 13e of the inner core rod 13 correspond to end portions of the molded rubber tube, and are not necessarily required to be shot-blasted. More specifically, the surface end portions (each having a width of about 5 mm) of the inner core rod 13 which are to be in contact with inner surface end portions of the molded rubber tube are not shot-blasted, but remain as mirror-polished surface portions 13e.

[0024] The rubber tube is molded from a fluororubber in the mold 10 including the inner core rod 13, whereby the rubber tube is produced with at least a middle portion of the inner surface thereof roughened.

[0025] Similarly, inner surfaces of the upper mold 12 and the lower mold 11 which are to be in contact with the outer surface of the tube may be roughened as required.

EXAMPLES

<Production Method>

[0026] Inner core rods 13 having different surface roughnesses for molds 10 were each prepared by shot-blasting a surface portion 13f of the inner core rod 13 of the mold 10 corresponding to an inner surface of a tube.

[0027] A fluororubber composition was prepared by kneading a vulcanizing agent, carbon, calcium hydroxide and a magnesium salt in predetermined proportions together with Du Pont's fluororubber Viton A700. Then, the fluororubber composition was press-molded at 177° C. in the molds 10, and further secondarily vulcanized at 232° C. at 24 hours. Thus, intended fluororubber tubes each having an inner diameter of 1 mm and an outer diameter of 2 mm were produced.

<Specifications for Examples and Comparative Examples>

[0028] The surface roughnesses (Rp, Rv, Rz, Ra, Rq) of the inner surface of a collapsible part of each of the tubes (each having an inner diameter of 1 mm and an outer diameter of 2 mm) produced by using the inner core rods 13 having different surface roughnesses in Comparative Examples and Examples, and the ratios of the respective surface roughnesses (Rp, Rv, Rz, Ra, Rq) to the inner diameter D are shown below.

Comparative Example 1

[0029] Rp=8.4 μm (Rp/D=0.0084), Rv=9.7 μm (Rv/D=0.0097), [0030] Rz=18.2 μm (Rz/D=0.018), Ra=2.0 μm (Ra/D=0.0020), [0031] Rq=2.6 μm (Rq/D=0.0026), and a restoration response time of 884 milliseconds

Comparative Example 2

[0032] Rp=11.6 μm (Rp/D=0.012), Rv=13.1 μm (Rv/D=0.013), [0033] Rz=24.7 μm (Rz/D=0.025), Ra=3.0 μm (Ra/D=0.0030), [0034] Rq=3.9 μm (Rq/D=0.0039), and a restoration response time of 886 milliseconds

Example 1

[0035] Rp=19.1 μm (Rp/D=0.019), Rv=18.7 μm (Rv/D=0.019), [0036] Rz=37.8 μm (Rz/D=0.038), Ra=3.6 μm (Ra/D=0.0036), [0037] Rq=4.6 μm (Rq/D=0.0046), and a restoration response time of 161 milliseconds

Example 2

[0038] Rp=19.7 μm (Rp/D=0.020), Rv=19.7 μm (Rv/D=0.020), [0039] Rz=39.4 μm (Rz/D=0.039), Ra=4.3 μm (Ra/D=0.0043), [0040] Rq=5.2 μm (Rq/D=0.0052), and a restoration response time of 154 milliseconds

Example 3

[0041] Rp=21.3 μm (Rp/D=0.021), Rv=23.6 μm (Rv/D=0.024), [0042] Rz=44.9 μm (Rz/D=0.045), Ra=4.0 μm (Ra/D=0.0040), [0043] Rq=5.2 μm (Rq/D=0.0052), and a restoration response time of 126 milliseconds

Example 4

[0044] Rp=22.8 μm (Rp/D=0.023), Rv=25.5 μm (Rv/D=0.025), [0045] Rz=48.3 μm (Rz/D=0.048), Ra=4.4 μm (Ra/D=0.0044), [0046] Rq=5.7 μm (Rq/D=0.0057), and a restoration response time of 107 milliseconds

Example 5

[0047] Rp=22.4 μm (Rp/D=0.022), Rv=28.3 μm (Rv/D=0.028), [0048] Rz=50.6 μm (Rz/D=0.051), Ra=5.0 μm (Ra/D=0.0050), [0049] Rq=6.1 μm (Rq/D=0.0061), and a restoration response time of 111 milliseconds

Example 6

[0050] Rp=26.0 μm (Rp/D=0.026), Rv=27.1 μm (Rv/D=0.027), [0051] Rz=53.1 μm (Rz/D=0.053), Ra=4.4 μm (Ra/D=0.0044), [0052] Rq=5.6 μm (Rq/D=0.0056), and a restoration response time of 109 milliseconds

Example 7

[0053] Rp=33.2 μm (Rp/D=0.033), Rv=32.8 μm (Rv/D=0.033), [0054] Rz=66.0 μm (Rz/D=0.066), Ra=5.7 μm (Ra/D=0.0057), [0055] Rq=7.2 μm (Rq/D=0.0072), and a restoration response time of 113 milliseconds

<Test Method>

[0056] The fluororubber tubes were each attached to a pinch valve driven at 24 V by a solenoid and, with the valve closed (with the tube collapsed), an air pressure of 100 kPa was applied to the tube from an inlet.

[0057] The restoration response time is defined as a time period elapsed from a time point (0 second) at which the solenoid is energized to electrically open the valve to a time point at which a pressure gage provided at an outlet of the valve detects a predetermined pressure level.

[0058] If a longer period of time is required for the restoration of the tube to an open state from a collapsed state due to the adhesiveness of the tube, the restoration response time is longer.

[0059] It is noted that the surface roughnesses of the inner surface of each of the tubes were determined by longitudinally cutting the tube into halves and observing the inner surface of the tube by means of a Keyence's laser microscope VK-X100.

<Test Results>

[0060] The results for Comparative Examples and Examples are collectively shown in Table 1.

TABLE-US-00001 TABLE 1 Comparative Comparative Example Example Example Example Example Example Example Example 1 Example 2 1 2 3 4 5 6 7 Rp (μm) 8.4 11.6 19.1 19.7 21.3 22.8 22.4 26 33.2 Rp/D 0.0084 0.012 0.019 0.02 0.021 0.023 0.022 0.026 0.033 Rv (μm) 9.7 13.1 18.7 19.7 23.6 25.5 28.3 27.1 32.8 Rv/D 0.0097 0.013 0.019 0.02 0.024 0.025 0.028 0.027 0.033 Rz (μm) 18.2 24.7 37.8 39.4 44.9 48.3 50.6 53.1 66 Rz/D 0.018 0.025 0.038 0.039 0.045 0.048 0.051 0.053 0.066 Ra (μm) 2 3 3.6 4.3 4 4.4 5 4.4 5.7 Ra/D 0.0020 0.0030 0.0036 0.0043 0.0040 0.0044 0.0050 0.0044 0.0057 Rq (μm) 2.6 3.9 4.6 5.2 5.2 5.7 6.1 5.6 7.2 Rq/D 0.0026 0.0039 0.0046 0.0052 0.0052 0.0057 0.0061 0.0056 0.0072 Restoration 884 886 161 154 126 107 111 109 113 response time (msec)

[0061] As apparent from the results shown in Table 1, the ratio (Rz/D) of the maximum height Rz of at least the part of the tube inner surface to the tube inner diameter D is preferably not less than 0.038, and the ratio (Rp/D) of the maximum peak height Rp of at least the part of the tube inner surface to the tube inner diameter D is preferably not less than 0.019. The ratio (Rv/D) of the maximum valley depth Rv of at least the part of the tube inner surface to the tube inner diameter D is preferably not less than 0.019, and the ratio (Ra/D) of the arithmetic average roughness Ra of at least the part of the tube inner surface to the tube inner diameter D is preferably not less than 0.0036. Further, the ratio (Rq/D) of the root mean square height Rq of at least the part of the tube inner surface to the tube inner diameter D is preferably not less than 0.0046.

[0062] This application corresponds to Japanese Patent Application No. 2016-050032 filed in the Japan Patent Office on Mar. 14, 2016, the disclosure of which is incorporated herein by reference in its entirety.