SEMICONDUCTOR PHOTODIODE FUNCTIONING IN A WIDE BAND RANGE AND OBTAINING METHOD THEREOF

Abstract

A semiconductor photodiode which functions in a wide band range up to medium wave infrared and far wavelengths in addition to visible region and near infrared includes: a light absorber region in micro structure which can provide light absorbance upon being roughened by laser; a first electrical lower contact coated with metal materials such as aluminium (Al), silver (Ag); a silicon which consists of crystalline silicon (c-Si); a second electrical lower contact which is coated with metal materials such as aluminium (Al), silver (Ag); a chalcogen doped hyper-filled silicone region which is obtained as a result of doping by pulse laser to the silicone region implanted by chalcogen elements; and upper electrical contact parts which are coated generally in the thickness range of 10 nm-1000 nm by using two-layered alloys with aluminium (Al)—(Al)-silver (Ag), two-layered alloys with titanium (Ti)-gold (Au), three-layered alloys with Ti-Platinum(Pt)—Au—Ag or three-layered alloys with Ti-lead(Pb)—Ag.

Claims

1. A semiconductor photodiode, comprising: a light absorber region in a micro structure configured to provide a light absorbance upon being roughened by a laser; a first electrical lower contact coated with first metal materials comprising aluminium (Al) and silver (Ag); a silicon consisting of crystalline silicon (c-Si); a second electrical lower contact coated with second metal materials comprising Al and Ag; a chalcogen doped hyper-filled silicone region obtained as a result of doping by a pulse laser to a silicone region implanted by chalcogen elements; and upper electrical contact parts coated generally in a thickness range of 10 nm-1000 nm by using two-layered alloys with Al—Al—Ag, two-layered alloys with titanium (Ti)-gold (Au), three-layered alloys with Ti-Platinum(Pt)—Au—Ag or three-layered alloys with Ti-lead(Pb)—Ag.

2. The semiconductor photodiode according to claim 1, wherein the first electrical lower contact is made of a first metal creating ohmic contact.

3. The semiconductor photodiode according to claim 1, wherein the second electrical lower contact is made of a second metal creating ohmic contact.

4. The semiconductor photodiode according to claim 1, wherein the upper electrical contact parts are made of a third metal creating ohmic contact.

5. The semiconductor photodiode according to claim 1, wherein the semiconductor photodiode functions in a wide band range up to medium and long infrared wavelengths in addition to a visible region and a near infrared region.

6. The semiconductor photodiode according to claim 1, wherein the semiconductor photodiode enables to keep incoming low-energy photons and to show a high reaction.

7. The semiconductor photodiode according to claim 1, wherein the semiconductor photodiode has a chance to function in a wider wavelength in army, law-enforcement forces, defense industry in a night view, health, industrial fields comprising an electric field and a heat insulation, information technology and a photovoltaic energy sector.

8. A semiconductor photodiode obtaining method, comprising: preparing silicone samples; implanting chalcogen elements to a single surface of surfaces of a silicone to obtain an implanted silicone surface; doping the implanted silicone surface upon melting the implanted silicone surface by a pulse laser to complete laser assisted doping; melting a non-implanted region of the silicone by the pulse laser in an impact mode; creating a mesa structure for a measurement of an electrical signal and an electro-optical signal from the implanted silicone surface; coating the surfaces of the silicone with a metal to receive the electrical signal and an optoelectric signal from the implanted silicone surface; and performing thermal annealing to create an ohmic contact between the metal and the silicone and improve structural stresses and defects occurred.

9. The semiconductor photodiode obtaining method according to claim 8, wherein the step of preparing the silicone samples is implemented by using semiconductor p-type/n-type Si, Si or Si crystals having a resistivity value of 1-10 Ω.Math.cm.

10. The semiconductor photodiode obtaining method according to claim 8, wherein the step of implanting the chalcogen elements to the single surface of the silicone is implemented by implanting S, Se and Te elements, wherein the S, Se and Te elements are the chalcogen elements and are passively implanted to the surfaces of the silicone.

11. The semiconductor photodiode obtaining method according to claim 8, wherein the step of implanting the chalcogen elements to the single surface of the silicone is implemented by doping the implanted silicone surface by using a laser assisted doping technique with the chalcogen elements.

12. The semiconductor photodiode obtaining method according to claim 8, wherein the step of doping the implanted silicone (4) surface upon melting the implanted silicone surface by the pulse laser to complete the laser assisted doping is implemented by making a number of laser pulses on the implanted silicone surface implanted with the chalcogen elements.

13. The semiconductor photodiode obtaining method according to claim 8, wherein in the step of doping the implanted silicone surface upon melting the implanted silicone surface by the pulse laser to complete the laser assisted doping, a transaction is a carried out at predetermined values of parameters comprising a laser power, a number of laser radiation pulse, a pulse frequency, a pulse duration, a scanning speed and a wavelength while melting a layer, wherein the chalcogen elements are located in a chalcogen doped silicone material by the pulse laser.

14. The semiconductor photodiode obtaining method according to claim 8, wherein the step of doping the implanted silicone surface upon melting the implanted silicone surface by the pulse laser to complete the laser assisted doping enables to avoid disappearance or ablation of a layer, wherein the chalcogen elements are located, by working at optimum values or preventing the silicone atoms and the chalcogen elements from associating adequately in consequence of not melting a layer adequately.

15. The semiconductor photodiode obtaining method according to claim 8, wherein the step of doping the implanted silicone surface upon melting the implanted silicone surface by the pulse laser to complete the laser assisted doping implements over doping of an implanted surface side of the silicone by working at optimum values, wherein the implanted surface side is the chalcogen elements located at a nanometer depth.

16. The semiconductor photodiode obtaining method according to claim 8, wherein the step of doping the implanted silicone surface upon melting the implanted silicone surface by the pulse laser to complete the laser assisted doping prevents a reduction of a concentration of implanted chalcogen elements through evaporation and implements over doping by performing a number of laser pulses.

17. The semiconductor photodiode obtaining method according to claim 8, wherein the step of doping the implanted silicone surface upon melting the implanted silicone surface by the pulse laser to complete the laser assisted doping enables the silicone to exhibit reactiveness at longer wavelengths by creating a wider intermediate energy band.

18. The semiconductor photodiode obtaining method according to claim 8, wherein the step of melting the non-implanted region of the silicone by the pulse laser in the impact mode includes: carrying out transactions of surface roughening or texturizing a non-implanted surface of the silicone located on a table by melting/ablating through the pulse laser under a vacuum in a vacuum chamber, a gas atmosphere comprising an air, an inert gas or non-inert gases or in a distilled water environment; obtaining a micro/nano structures enabling absorption of light, wherein the micro/nano structures are an absorber layer; and creating an absorption of light in a wide band wavelength by reducing a surface reflection of the silicone.

19. The semiconductor photodiode obtaining method according to claim 8, wherein the step of melting the non-implanted region of the silicone by the pulse laser in the impact mode and the non-impact mode processes doped and non-doped surfaces independently of each other in order to change/develop optical, electro-optical and energy band structure features of the silicone by carrying out transactions on a non-implanted surface in order not to reduce an implant concentration.

20. The semiconductor photodiode obtaining method according to claim 8, wherein the step of creating the mesa structure for the measurement of the electrical signal and the electro-optical signal from the implanted silicone surface creates the mesa structure for photodetectors by using a classical/standard mesa etching technique or a photolithography mesa abrasion technique or a photolithography mesa abrasion technique.

21. The semiconductor photodiode obtaining method according to claim 8, wherein the step of creating the mesa structure for the measurement of the electrical signal and the electro-optical signal from the implanted silicone surface creates the mesa structure by abrasing requested points at requested depths by laser, on a chalcogen doped silicone surface with optimum parameters.

22. The semiconductor photodiode obtaining method according to claim 8, wherein in the step of creating the mesa structure for the measurement of the electrical signal and the electro-optical signal from the implanted silicone surface, a silicone oxide occurring on the implanted silicone surface during an abrasion is removed from the implanted silicone surface by applying hydrogenfluoride, and a mesa is obtained.

23. The semiconductor photodiode obtaining method according to claim 8, wherein the step of coating the surfaces with the metal to receive the electrical signal and the optoelectric signal from the implanted silicone surface obtains a first electrical lower contact, a second electrical lower contact and upper electrical contact parts by classical/standard metal coating or metalization techniques.

24. The semiconductor photodiode obtaining method according to claim 8, wherein in the step of coating the surfaces with the metal to receive the electrical signal and the optoelectric signal from the implanted silicone surface, a first electrical lower contact, a second electrical lower contact and upper electrical contact are obtained when a non-implanted side of the silicone is seated on a glass surface coated with a metal film and points of abrasion silicone surfaces are coated with a metal upon being evaporating by pulses made by the pulse laser in a vacuum environment.

25. The semiconductor photodiode obtaining method according to claim 8, wherein the step of performing the thermal annealing to create the ohmic contact between the metal and the silicone and improve the structural stresses and defects occurred is carried out between temperature values of 350 K-900 K and a time interval of 5 min-60 min.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] “A Semiconductor Photodiode Functioning in a Wide Band Range and Obtaining Method Thereof” realized to fulfil the objectives of the present invention is shown in the figures attached, in which:

[0015] FIG. 1 is a side view of the inventive semiconductor photodiode.

[0016] FIG. 2 is a flowchart related to the inventive semiconductor photodiode obtaining method.

[0017] The components illustrated in the figures are individually numbered, where the numbers refer to the following: [0018] 8. Semiconductor photodiode [0019] 9. Light absorber region [0020] 10. First electrical lower contact [0021] 11. Silicone [0022] 12. Second electrical lower contact [0023] 13. Chalcogen doped hyper-filled silicone region [0024] 14. Upper electrical contact

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0025] The inventive semiconductor photodiode (1) functioning in a wide band range comprises: [0026] a light absorber region (2) in micro structure which can provide light absorbance upon being roughened by laser; [0027] a first electrical lower contact (3) which is coated with metal materials such as aluminium (Al), silver (Ag); [0028] a silicon (4) which consists of crystalline silicon (c-Si); [0029] a second electrical lower contact (5) which is coated with metal materials such as aluminium (Al), silver (Ag); [0030] a chalcogen doped hyper-filled silicone region (6) which is obtained as a result of doping by pulse laser to the silicone (4) region implanted by chalcogen elements; and [0031] upper electrical contact (7) parts which are coated generally in the thickness range of 10 nm-1000 nm by using two-layered alloys with aluminium (Al)—(Al)-silver (Ag), two-layered alloys with titanium (Ti)-gold (Au), three-layered alloys with Ti-Platinum(Pt)—Au—Ag or three-layered alloys with Ti-lead(Pb)—Ag.

[0032] In a preferred embodiment of the invention, the first electrical lower contact (3) is made of a metal creating ohmic contact.

[0033] In a preferred embodiment of the invention, the second electrical lower contact (5) is made of a metal creating ohmic contact.

[0034] In a preferred embodiment of the invention, the upper electrical contact (7) is made of a metal creating ohmic contact.

[0035] In a preferred embodiment of the invention, the semiconductor photodiode (1) functioning in a wide band range can function in a wide band range up to medium and long infrared wavelengths in addition to visible region and near infrared.

[0036] In a preferred embodiment of the invention, the semiconductor photodiode (1) functioning in a wide band (of electromagnetic spectrum) range enables to keep incoming low-energy photons and to show high reaction.

[0037] In a preferred embodiment of the invention, by means of the semiconductor photodiode (1) functioning in a wide band range; preferred semiconductor photodiodes have the chance to function in a wider wavelength in army, law-enforcement forces, defense industry (night view), various health, industrial fields (electric field, heat insulation, etc.), information technology and energy sector (photovoltaic).

[0038] The inventive semiconductor photodiode (1) obtaining method (100) comprises steps of: [0039] preparing the silicone (4) samples (101); [0040] implanting the chalcogen elements to a single surface of the silicone (4) (102); [0041] doping the implanted silicone (4) surface upon melting it by pulse laser (laser assisted doping) (103); [0042] melting the non-implanted (other surface) region of the silicone (4) by pulse laser (impact/non-impact) (104); [0043] creating mesa (rasterization) structure (microfabrication) for measurement of electrical and electro-optical signal from the silicone (4) surface (105); [0044] coating the surfaces with metal in order to receive electrical and optoelectric signal from the silicone (4) surface (106); and [0045] performing thermal annealing in order to create ohmic contact between the metal and the silicone (4) and improve the structural stresses and defects occurred (107).

[0046] In a preferred embodiment of the invention, semiconductor “p-type/n-type Si(100), Si(111) or Si(110)” crystals having resistivity value of 1-10 Ω.Math.cm are used while preparing the silicone (4) samples (101).

[0047] In a preferred embodiment of the invention, S, Se and Te elements—that are chalcogen elements—are passively implanted to any surface of the silicone for the transaction of implanting the chalcogen elements to a single surface of the silicone (4) (102) (the implant parameters are shown in the Table 1). Here, the silicone (4) surface is doped by using laser assisted doping technique with the chalcogen elements.

TABLE-US-00001 TABLE 1 Implant parameters Elements Doping Energy Doping Doses Sample (Silicon) Sulfur (S)  90-250 keV 10.sup.16-17 ion/cm.sup.2 p-type/n-type Selenium (Se) 150-500 keV 10.sup.14-16 ion/cm.sup.2 Si (100), Si (111), Tellurium (Te) 150-500 keV 10.sup.14-16 ion/cm.sup.2 Si (110), Mono-crystalline material production: Czochralski method (CZ) and Float Zone method (FZ) FZ

[0048] In a preferred embodiment of the invention, a small number of laser pulses are performed on the silicone (4) surface—that is implanted with the chalcogen elements—in the transaction of doping the implanted silicone (4) surface upon melting it by pulse laser (laser assisted doping) (103) (the related laser pulse parameters are shown in the Table 2). It is required to carry out transaction at suitable values of parameters such as laser power, number of laser radiation pulse, pulse frequency, pulse duration, scanning speed and wavelength while melting the layer wherein the chalcogen elements are located in the chalcogen doped silicone (4) material by laser. Not working at optimum values included in the Table 2 causes the layer, wherein the chalcogen elements are located, to disappear by being be melted excessively (ablation) or causes the silicone (4) atoms and the chalcogen elements not to be able to associate adequately in consequence of not being able to melt the said layer adequately. Thereby, over doping the implanted surface side of the silicone (4) (the chalcogen elements that are located at nanometer depth) is realized. The reason of performing a small number of laser pulses is to prevent reduction of the concentration of the implanted chalcogen elements through evaporation and to realize over doping. Thus, the silicone (4) enhances reactiveness at longer wavelengths by creating a wider intermediate energy band. In addition, it exhibits advantage for making microfabrication (rasterization).

TABLE-US-00002 TABLE 2 Laser pulse parameters for the implanted silicone surface Laser mode, Laser Number of Repetition Laser Scanning Laser Pulse/ Frequency Energy Speed Scanning Sample Brust (impact) 0.5-1.7 5-10 1-5 p-type/n-type mode, J/cm.sup.2 mm/s Si (100), Si (111), continuous Si (110), mode Mono-crystalline ≤50 kHz material production: Czochralski method (CZ) and Float Zone method (FZ)

[0049] In a preferred embodiment of the invention, the silicone (4) crystals are placed to a table at first for the transaction of melting the non-implanted (other surface) region of the silicone (4) by pulse laser (impact/non-impact) (104). This table whereon the silicone (4) crystals are located are taken to a vacuum chamber and the environment is vacuumed. Or the transaction can also be carried out under gas (for example: air, inert gas or non-inert gases, etc.) atmospheres or in distilled water environment. After the environment suitable for the transaction is created; the surface is roughened (texturized) by melting/ablating the non-implanted (not comprising the chalcogen elements) surface of the silicone (4) through pulse laser, micro/nano structures (absorber layer) enabling absorption of light are obtained, and light absorbance is provided/enhanced in wide band wavelength by reducing the surface reflection of the silicone (4). In order not to reduce the implant concentration, transaction is carried out in this surface (the related laser pulse parameters are shown in the Table 3). Thereby, transaction can be carried out on doped and non-doped surfaces independently of each other in order to change/develop optical, electro-optical and energy band structure features of the silicone (4).

TABLE-US-00003 TABLE 3 Laser pulse parameters for the non-implanted silicone surface Laser mode, Laser Number of Repetition Laser Scanning Laser Pulse/ Frequency Energy Speed Scanning Sample Brust (impact)/ 0.5-3 5-10 ≤3000 p-type/n-type continuous J/cm.sup.2 mm/s Si (100), Si (111), (non-impact) Si (110), mode, Mono-crystalline ≤50 kHz material production: Czochralski method (CZ) and Float Zone method (FZ)

[0050] In a preferred embodiment of the invention, the transaction of creating mesa (rasterization) structure (microfabrication) for measurement of electrical and electro-optical signal from the silicone (4) surface (105) creates mesa structure for photodetectors by using classical/standard mesa etching technique or photolithography mesa abrasion (rasterization) technique or photolithography mesa abrasion technique (FIG. 1). Use of laser abrasion method is another technique for creating mesa structure. Mesa structure is created by abrasing the requested points at requested depths by laser, on the chalcogen doped silicone (4) surface with optimum parameters. Silicone oxide occurs on the surface during abrasion however mesa is obtained by removing the oxidized layer from the surface by applying HF (hydrogenfluoride).

[0051] In a preferred embodiment of the invention, classical/standard metal coating (metalization) techniques are used in the transaction of coating the surfaces with metal in order to receive electrical and optoelectric signal from the silicone (4) surface (106). Thus, the first electrical lower contact (3), the second electrical lower contact (5) and the upper electrical contact (7) are obtained. The semiconductor photodiode structure indicating the metal layers obtained after the metal coating transactions are carried out are also shown in the FIG. 1.

[0052] In another embodiment of the invention, in the transaction of coating the surfaces with metal in order to receive electrical and optoelectric signal from the silicone (4) surface (106), the non-implanted side of the silicone (4) is seated on the glass surface that is coated with metal thin film and certain points of the abrasion silicone (4) surfaces are coated with metal upon being evaporating by the pulses made by the pulse laser in vacuum environment. Thereby, the first electrical lower contact (3), the second electrical lower contact (5) and the upper electrical contact (7) are obtained. (The semiconductor photodiode structure indicating the metal layers obtained after the metal coating transactions are carried out are also shown in the FIG. 1.).

[0053] In a preferred embodiment of the invention, the transaction of performing thermal annealing in order to create ohmic contact between the metal and the silicone (4) and improve the structural stresses and defects occurred (107) is carried out between temperature values of 350K-900K and time interval of 5 min-60 min.

[0054] Within these basic concepts; it is possible to develop various embodiments of the inventive semiconductor photodiode functioning in a wide band range (1) and obtaining method thereof (100); the invention cannot be limited to examples disclosed herein and it is essentially according to claims.