MEDICAL DEVICE WITH PLASMA MODIFIED OXIDE LAYER AND METHOD OF FORMING SUCH A DEVICE

Abstract

A method of modifying a surface of a medical device for implantation or disposition inside a patient is described. The medical device comprises a structure having at least one surface. The method includes the steps of: placing the medical device into a plasma chamber substantially free from contaminants and substantially sealing the plasma chamber from the atmosphere; removing at least an outermost layer of any oxide layer from the at least one surface of the structure by a plasma oxide-removal process, whilst maintaining the plasma chamber under seal from the atmosphere; and subsequently forming a new oxide layer at the least one surface of the structure by introducing at least one gas into the plasma chamber, whilst maintaining the plasma chamber under seal from the atmosphere. A medical device including a bulk material and an oxide layer disposed over at least one surface of the medical device. The oxide layer is substantially pure and free from contaminants.

Claims

1-15. (canceled)

16. A medical device having a structure for implantation or disposition inside a patient, the structure including: a bulk material; and an oxide layer disposed over at least one surface of the medical device; wherein the oxide layer is substantially pure and free from contaminants.

17. A medical device according to claim 16 wherein the new oxide layer is carbon/calcium free.

18. A medical device according to claim 17 wherein the oxide layer is between about 3 and 18 nm in thickness.

19. A medical device according to claim 16, wherein the bulk material is a nickel titanium alloy.

20. A medical device according to claim 16 wherein the medical device is or includes a stent.

21. A medical device according to claim 20, also including a coating on the oxide layer.

22. A medical device according to claim 21, wherein the coating is or includes a therapeutic substance.

23. A medical device according to claim 22, wherein the therapeutic substance is an anti-proliferative substance.

24. A medical device according to claim 23, wherein the anti-proliferative substance is paclitaxel.

25. A vascular stent, comprising: a metal alloy stent structure, the stent structure having at least one surface provided by the metal alloy; and a carbon/calcium free oxide layer at the at least one surface of the metal alloy stent structure.

26. A vascular stent according to claim 25, wherein the oxide layer has no level of carbon or calcium detectable by X-ray photoelectron spectroscopy.

27. A vascular stent according to claim 26, wherein the oxide layer has a thickness between about 2 nm and 50 nm.

28. A vascular stent according to claim 27, wherein the thickness is between 3 and 18 nm.

29. The vascular stent of claim 27, wherein the oxide layer is passivated.

30. The vascular stent of claim 25, wherein the metal alloy stent structure is a nitinol stent structure, and wherein the oxide layer has an acidic polar surface energy of at least about 3.7 Dynes/cm and no measurable basic polar energy.

31. The vascular stent of claim 25, wherein the metal alloy stent structure is a nitinol stent structure, and the nitinol stent structure is free of a nickel rich sublayer under the oxide layer.

32. A medical device according to claim 25, also including a coating on the oxide layer.

33. A medical device according to claim 32, wherein the coating is or includes a therapeutic substance.

34. A medical device according to claim 33, wherein the therapeutic substance is an anti-proliferative substance.

35. A medical device according to claim 34, wherein the anti-proliferative substance is paclitaxel.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0063] Embodiments of the present invention are described below, by way of example only, with reference to the accompanying drawings, in which:

[0064] FIG. 1 is a side elevational view of an exemplary vascular stent;

[0065] FIG. 2 is a schematic representation of the stent of FIG. 1 in the process of being deployed in a patient's vessel to treat a stenosis;

[0066] FIG. 3A is a schematic diagram of a plasma chamber apparatus used in the preferred method of forming a medical device according to the teachings herein;

[0067] FIG. 3B is a schematic diagram of an electropolishing and neutralising apparatus used in a method of forming a medical device according to the teachings herein;

[0068] FIG. 4 is a flow chart of a preferred method;

[0069] FIG. 5 is a schematic diagram of a transverse cross-sectional view of a stent strut of the stent of FIGS. 1 and 2 to show the oxidised contact surface and bioactive material coating;

[0070] FIGS. 6A and 6B show XPS depth profiling of a number of nitinol stents;

[0071] FIG. 7A is a schematic view of the oxide layer on pure titanium

[0072] FIG. 7B is a schematic view of a structurally ordered TiO.sub.2 surface with two types of hydroxides, acidic and basic hydroxides;

[0073] FIG. 8 is a schematic diagram for the model of an oxide-covered metal showing the various layers and their composition;

[0074] FIG. 9 is a schematic diagram of an apparatus including a water bath for dunking the stents into liquid water after the plasma process;

[0075] FIGS. 10 to 15 show XPS quantification of OH and water on NiTi oxide surface;

[0076] FIG. 16 is a table showing treatment conditions for four stents, A, B, C and D in a plasma chamber whilst removing the oxide layer from the surface of the stents and regrowing a new oxide layer at that;

[0077] FIGS. 17-20 show XPS data for the surfaces of stents A, B, C and D cited in the table of FIG. 16; and

[0078] FIG. 21 shows comparable XPS data for a plasma cleaned surface.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0079] It is to be understood that the drawings are schematic only and not to scale. Often only the principal components relevant to the teachings herein are shown in the drawings, for the sake of clarity.

[0080] The embodiments described below focus on a stent, in particular, a coated stent. It is to be understood, however, that these are examples only and that the teachings herein can be applied to a large range of medical devices, both for temporary placement in a patient and also for long term placement. Other examples include stent grafts, vascular filters and plugs, valvuloplasty devices, prostheses and so on.

[0081] Referring first to FIG. 1, there is shown an exemplary vascular stent 10 to which the teachings herein can be applied. The stent 10 is generally a tubular structure 12, in this example formed of a plurality of stent rings 14 which extend in series coaxially along the length of the tubular structure 12 and are coupled to one another by means of tie bars 16, as is well known in the art. In this example, the stent rings 14 are formed of a plurality of strut sections 18 arranged a zigzag shape. At the end of the stent 10 there may be provided radiopaque markers 20, again of a type well known in the art.

[0082] The stent 10 may be self-expanding or balloon expandable and made of any suitable material, of which many are known in the art. Examples of suitable materials are given below.

[0083] Referring also to FIG. 2, the stent 10 can be seen in the process of being deployed into a vessel 24, by means of an introducer assembly of which the distal end components 22 are visible in FIG. 2. These typically include a carrier element having a dilator tip 26 at the distal end thereof. The dilator tip 26 has a lumen therein for the passage of a guide wire 28. The components of the introducer assembly are not relevant to the teachings herein.

[0084] In the example in FIG. 2, the stent 10 is being deployed in order to treat a stenosis 300 of the vessel 24 and also to keep the vessel 24 open for the passage of blood therethrough.

[0085] FIG. 6 shows XPS depth profiling of a number of off-the-shelf nitinol stents at 0 Å and 6 Å. An oxide layer on a bulk metal has a depth, and a surface onto which a coating may be applied. The oxide layer includes an outermost layer adjacent the surface of the layer. The outermost layer may have a different composition and therefore different properties from the rest of the oxide layer. The oxide layer of a nitinol stent includes titanium dioxide, the thermodynamically unstable titanium monoxide and nickel oxides. The outermost layer of the oxide is generally mainly titanium dioxide. At the exposed surface titanium hydroxide, contamination and water can be seen via various techniques. If the pressure/humidity/temperature favour it, a water layer may form over the hydroxide layer. FIG. 7A is a schematic view of the oxide layer on pure titanium. The distinction between the bulk metal and the oxide layer can be clearly seen, as well as the difference between the oxide layer and the surface of the oxide. FIG. 7B is a schematic view of a structurally ordered TiO.sub.2 surface with two types of hydroxides, acidic and basic hydroxides, extending out from the surface. The presence of hydroxyl groups at the surface may enable better bonding of a bioactive material coating to the surface. The hydroxyl groups may bond to the bioactive material by hydrogen bonding. As such the hydroxyl groups may act as lewis acids or lewis bases.

[0086] In FIG. 6, the XPS results at 0 Å show the composition of the outermost surface layer and the results at 6 Å show the composition of the bulk oxide on nitinol stents. The results show, that the bulk oxide includes between 6.0-10.7% carbon contamination in the stents profiled in FIG. 6A, and between 20.9-21.3% carbon contamination in the stents profiled in FIG. 6B.

[0087] The oxide forms spontaneously after electropolishing. Unfortunately, the oxide is always contaminated by either environmental contaminants or by contaminants from the electropolishing bath. Carbon contamination from the atmosphere or residuals from the electropolishing bath can account for a significant proportion of the oxide. Calcium deposits may also be present in the oxide which are also from residuals in the electropolishing bath. Carbon and silicon oil contamination reduces the adherence of paclitaxel and other drugs to the surface of the stent, whilst calcium deposits act as channels for corrosion to propagate into the stent. For a nitinol stent the surface of the oxide layer, the surface onto which a drug will be coated, may include titanium hydroxide and titanic acids which are formed when the surface is exposed to air and/or moisture. Hydroxide groups and water may also be present at the surface. Contaminants may be adsorbed at the surface.

[0088] The inventors have discovered that careful control of the formation of an oxide on the surfaces of the bulk structure of the medical device can result in substantially pure oxide layer at the surface which has a number of advantages. Firstly, by having a purer oxide layer the device may have improved corrosion resistance. Secondly, by having an even, substantially contaminant free surface the surface of the device may bind more effectively to a coating placed on the surface, such as a pharmaceutical drug coating.

[0089] Often, the deployment of a stent alone in the vessel does not provide a permanent solution as closure of the vessel can reoccur, such as by restenosis. This can be caused by a number of factors, including damage to the tissue of the vessel 24 during the vessel opening or angioplasty procedure, reoccurrence of the original causes of the stenosis, body reaction to the presence of a foreign body in the vessel, and so on.

[0090] In the example described briefly above in connection with FIG. 2, it has been found that the administration of suitable bioactive agents into the vessel wall from the stent can substantially retard or prevent subsequent closure of the vessel due to restenosis. Bioactive agents released from the stent can also treat many other medical conditions, including the original disease of the tissue. A variety of bioactive agents suitable for such purposes are known in the art including, for instance, anti-thrombogenic agents, thrombin inhibitors, tissue plasminogen activators, thrombolytic agents, fibrinolytic agents, vasospasm inhibitors, antiplatelet agents, anti-proliferative agents and so on. A particularly effective bioactive agent known in the art is paclitaxel, others including dexamethasone, heparin and numerous other agents and compounds. A list of suitable bioactive agents is given at the end of this specification, though it is to be understood that the list is not exhaustive.

[0091] The bioactive material is coated onto the medical device, for example the stent 10 of FIG. 1, so as to be released from the medical device into the tissues of the vessel 24, and should be dispensed at a rate suitable for treating the required medical condition. In the case of a stent or other implantable medical device, it may be desirable for the bioactive material to be released over a prolonged period of time, for example weeks or months. In the case of a medical device that is temporarily deployed in a patient's vessel, the bioactive agent should typically be released from the device in a very short period of time, for instance within seconds or minutes, although sometimes could be up to an hour or more.

[0092] It is important that the bioactive agent is held onto the medical device during deployment of the device in the patient without excessive loss of bioactive material into the patient's bloodstream, for instance. For this purpose, the prior art has suggested restraining the bioactive material, for instance in a containment or time release layer or matrix. Examples include: porous polymer layers into which bioactive material can be embedded, enclosed chambers holding the bioactive material, outer coatings disposed over the bioactive material and which dissolve or open during the deployment process, encapsulation of the bioactive material in capsules or pellets, and so on. Such containment measures can lead to a number of disadvantages, including undesirable delayed administration of the bioactive material into body tissues, presence of a foreign substance in the body, possible onset of stenosis caused by the carrier device, and so on.

[0093] The optimal solution is to apply the bioactive agent in the absence of any containment or time release substance and from a layer which is predominantly or entirely made of bioactive agents. In this manner, after administration of the bioactive agent or agents, the medical device remains free of agent delivery substances (polymer layers, for example) and no unnecessary carrier substances are released into the patient's body. The problem, however, has existed with getting a bioactive agent to be held sufficiently well and reliably on the medical device.

[0094] The inventors have discovered that certain treatments of the medical device, and in particular the surface or surfaces of the device intended to be coated with one or more bioactive agents, can substantially increase the adhesion of the bioactive agent to the medical device before and during deployment of the device in the patient. Furthermore, the inventors have discovered that controlled formation of a pure, substantially contaminant free oxide layer on the surface can substantially increase the adhesive characteristics of the surface, to such an extent that it is not necessary to use other mechanisms to retain a bioactive agent on the device. The inventors have also found that the oxide layer may be tailored so as to bind to particular drugs especially well. For example, a more acidic polar oxide layer will bind well to a basic polar drug and vice versa.

[0095] As shown in FIGS. 6A and 6B a naturally formed oxide layer, that is at least partially formed by atmospheric contact, can result in the formation of an impure or non-uniform oxide, leading to non-uniform characteristics to the oxide and poor retention of bioactive material. This is typically resolved by using a containment layer or agent. It has not previously been considered that a uniform oxide layer could be formed on the structure of a medical device and in a manner that containment materials or layers could be avoided.

[0096] Where the base material is nitinol, the oxide layer formed using the method of the present invention will be predominantly titanium dioxide. When coated with PTX the oxide has a polar acidic nature, binding well to the polar basic PTX coatings. By forming a more pure titanium oxide layer, reducing the proportion of contaminant in the layer, the oxide layer is more polar acidic in nature and therefore binds better to polar basic coatings such as PTX.

[0097] The oxide layer may be modified further by addition of doping agents to be the conjugate of the polar characteristic of the bioactive material, or to be amphoteric. Thus, for a bioactive material which is a base (or predominantly a base) the oxide is formed to be more polar acidic. On the other hand, for a bioactive material which is acidic (or predominantly acidic) the oxide is formed to be more polar basic. The treatment provides a totality or preponderance of acid or base species of the at least one surface of the device intended to be coated or modified for other reasons. These form a characteristic to the device surface and provide a bonding site for the base or acid conjugate of the bioactive material. The acid or base species do not form a polymer matrix, for instance. Bonding of the bioactive agent is by means of covalent forces, in which the base/acid or acid/base combinations form a Lewis adduct. Bioactive material molecules which overlie those directly attached to their covalent species will bind to other bioactive material molecules by same species covalent bonds.

[0098] In practice, the treatment leads to an increase in the polar acid or polar base energy component of the surface or surfaces, which leads to a significant increase in the quality of adhesion of bioactive agent to the contact surface of the medical device also to a substantial improvement in uniformity of the contact surface(s) of the medical device.

[0099] A significant improvement in bioactive material retention is experienced by oxide layer modification alone. Better retention may be achieved in some cases by first cleaning the contact surface or surfaces of the medical device to remove impurities, generally acquired during and after the manufacturing process. This can substantially increase the amount of carbon functional groups on the contact surface(s) of the medical device, leading to an even more uniform coating of bioactive material across the contact surface of the medical device.

[0100] The specific embodiments described below are directed to a stent formed of nickel titanium alloy (for instance Nitinol) which is coated with paclitaxel, a preferred bioactive agent. The skilled person will appreciate that this is an example only and that the teachings herein are applicable to the other stent materials, including metals and metal alloys. The teachings herein are similarly not limited to stents only and can be applied to other medical devices of the types mentioned elsewhere in this specification.

[0101] Referring now to FIG. 3A, this shows a schematic diagram of a plasma chamber 200 apparatus for treating a stent 10 so as to grow in controlled manner the oxide on the stent surfaces in order to change the bonding characteristics of the surface. The treated oxide exhibits a very high percentage of titanium dioxide. The treatment suppresses the amount of nickel in the oxide layer, which the inventors have discovered adversely affects the retention of basic bioactive agents. In the inventors' experience nickel metal is basic while titanium oxide is acidic, as evidenced by the polar energy tests described below. Moreover, the treatment in the preferred embodiment eliminates contaminants such as carbon and/or calcium and other impurities in the oxide layer, resulting in a significantly more uniform oxide coating.

[0102] The new oxide layer is advantageously grown to be at least 3 nm thick. Where the oxide layer is substantially pure and uniform such a thickness may be sufficient to reduce the effect caused by variations in the underlying structure. The inventors have found that the preferred oxide layers produce a reliable performance which is practically unaffected by variations in the underlying structure. This is a significant benefit, both clinically and in meeting or exceeding regulatory specifications.

[0103] Any acidic species in the oxide layer increases the acidic polar component of the surface energy of the contact surface, providing good adhesion characteristics to the surface, for holding a bioactive agent (being the conjugate base) onto the contact surface. The same applies to the opposite arrangement of a polar basic oxide and the conjugate of a polar acidic bioactive material. The resulting structure is substantially better than what can be achieved with a non-modified contact surface of a medical device. Furthermore, this oxidation process increases the reliability of the overlying coat, in that a more consistent dosage of bioactive agent is applied on the contact surface during batch coating.

[0104] Even though it has been found that controlled formation of the oxide layer per se provides a notable increase in adhesion of a bioactive agent onto the medical device, cleansing of the contact surface or surfaces prior to oxidation can in some cases result in even better bioactive material retention on the medical device.

[0105] A preferred method described below in connection with FIGS. 3A, 3B and 4 treats a nickel titanium alloy stent. The alloy may be Nitinol, but in some embodiments the alloy is modified by the addition of one or more acidic or basic components.

[0106] FIGS. 3A, 3B and the accompanying description make reference to a stent 10. It is to be understood, though, that stents are often batch processed and that a plurality of stents will be treated simultaneously in each of the treatment stages. As batch processing of this nature is known, it is not described herein any further but it is to be understood that this is intended to form an integral part of this disclosure.

[0107] Prior to the treatment of the stent in the plasma chamber 200 apparatus shown in FIG. 3A, the stent may be cleaned in a one or multiple stage process, if it is found to be required. FIG. 3B is a schematic diagram of an electropolishing and neutralising apparatus which may be used prior to plasma removal of the oxide layer. A first cleaning stage (step 100 in FIG. 4) uses a variety of cleaning solutions, such as for example an alcohol solution including ethanol to remove larger and volatile impurities from the contact surface.

[0108] Second and third stages (steps 104 and 106 of FIG. 4) are electropolishing and neutralisation of the surface. The basic components of the apparatus and the method are shown in FIGS. 3A, 3B and 4. The skilled person will appreciate that the apparatus and method will include other components and steps standard in the art and which are not therefore described herein.

[0109] In the electropolishing stage 30 (and step 104 in FIG. 4) the stent 10, typically provided on a support such as a mandrel 40, is disposed into an etching solution, typically acidic, in the bath 30. This stage also includes the components 32 necessary for carrying out electropolishing and in this regard any suitable electropolishing device may be used, as is the case with the electropolishing fluid used in the bath 30. The electropolishing stage 30 (and step 104) is, preferably, operated to remove at least about 2%, at least about 10%, or at least about 20% up to at least about 30% by weight of the material of the stent 10, in order to etch away the exposed surfaces of the stent 10 to remove heat affected zones, in the course of which there are also removed surface containments and any natively formed oxide layer. The bulk material of the stent 10 is, in some embodiments, standard Nitinol.

[0110] In order to avoid further contamination of the stent 10, in particular at the end of the electropolishing process, above the electropolishing solution in the bath 30, that is in the top portion 34 of the chamber 30, there is preferably provided an inert gaseous blanket which does not contain oxygen or water. Suitable inert blankets could be argon or nitrogen gas or any other noble gas.

[0111] The stage 30 may be provided with a solution changing/cleansing unit 36 for cleaning/changing the electropolishing solution so that the stent can be exposed to clean solution. The unit 36 may include one or more sensors for sensing the state of the electropolishing solution.

[0112] The neutralisation stage 50 may have similar components to the electropolishing stage 30, and includes a solution of neutralisation fluid, typically a base compound, for washing and removing acidic components from the exposed surfaces of the stent. The neutralisation stage 50 will also typically include driving unit 52 of a type commonly known in the art. The stent 10 may be retained on the holder 40 during this process. The neutralisation bath 50 is also preferably provided with an isolation blanket 34 similar to that of the electropolishing stage 30 and this again may be of a noble gas such as argon, or nitrogen, for instance. The blanket 34 is preferably oxygen and water free.

[0113] As soon as the stent leaves the electropolishing acid bath a native oxide layer forms almost instantaneously on any exposed surfaces. Such an instantaneously produced oxide layer will typically have a thickness of around 3 nanometres. The composition of the native layer will be dependent upon a number of factors such as the nature of the bulk material, cleanliness of the electropolishing bath and of the stent itself going into the bath, purity of the gaseous blanket, how the stent is handled after electropolishing and the neutralising chemicals used, and the composition of the surrounding atmosphere at the time of oxidation. This may lead to an uneven oxide layer across the surfaces of the stent and can also result in the oxide layer having inconsistent characteristics such as by being contaminated with elements which will affect the performance of the oxide layer. For example, a native oxide is likely to contain significant quantities of carbon, and potentially calcium and silicon.

[0114] As described, following electropolishing the stent is oxidised naturally in the air. This is generally the state in which stents can be purchased from a manufacturer. The stent is then disposed in a plasma chamber 200, subjected to a plasma oxide-removal process (see step 108, FIG. 4) and then a new oxide layer is formed on the exposed surface (see step 110, FIG. 4).

[0115] The plasma chamber 200 includes a sample holder 210 for supporting a stent 10, an electrode 220 and high frequency generator 230 for stimulating matter to a plasma state. The apparatus includes a vacuum pump 260 for removing air from the chamber, so as to eliminate contaminants from the chamber and create a vacuum inside the chamber. The apparatus includes a hydrogen gas supply 245 and an argon gas supply 255, and valves 240 and 250 for controlling the flow of the gases into the plasma chamber 200. It will be appreciated that other gases may be used in their place, or in addition. In place of argon, for example, another noble gas may be used. The apparatus also includes an oxygen source 275 and an oxygen valve 270 for allowing a controlled flow of oxygen into the plasma chamber so as to form a new oxide on the stent surface. The plasma chamber 200 may be heated so as to control the rate of oxidation.

[0116] A variety of plasma cleaning systems may be used, for example a Diener Femto type B system, or a Diener Pico system having a 13.56 MHz generator and a quartz glass chamber. The electropolished stent is placed into the plasma chamber, and a vacuum is applied to the chamber to evacuate the system of contaminants and air. Hydrogen and/or argon gas is introduced into the plasma chamber 200 at flow rates of approximately 30 sccm and at an estimated pressure of 0.4 mbar. The high frequency generator is activated to stimulate the gases in the plasma chamber into a plasma state. The plasma chamber is set to 13.56 MHz & 100 Watts for 5 minutes. During this time the hydrogen and/or argon plasma removes the oxide layer and the argon plasma may even remove the nickel rich sublayer from the surface of the stent. The vacuum pump remains on throughout the oxide-removal process to remove matter from the plasma chamber. After the oxide layer has been removed the high energy source (plasma) is switched off and the gases are turned off by closing the valves. The chamber is evacuated using the vacuum pump.

[0117] Preferably, the hydrogen and argon gases are mixed together in a mixer valve before they enter the plasma chamber. This mixing results in a more uniform process.

[0118] The stent then remains in the plasma chamber, without exposing the stent to the atmosphere, and a new oxide layer is formed on the surface of the stent by introducing oxygen gas into the plasma chamber via the oxygen valve at a flow rate of approximately 30 sccm. During this step the plasma remains switched off. Preferably the oxygen is pure oxygen gas. The plasma chamber is preferably supplied with very small quantities of oxygen, into the chamber 200. This ensures controlled oxidation of the exposed surfaces of the bulk material of the stent 10. During formation of the new oxide layer the vacuum pump remains switched on so as to continue drawing matter from the chamber. The plasma source is switched off whilst the new oxide layer is formed. After formation of the new oxide layer the vacuum pump is switched off and the chamber is vented with oxygen gas before the stent can be removed for coating.

[0119] In some embodiments argon, or another noble gas, is also introduced into the plasma chamber at the same time as the oxygen gas. The noble gas is used to control the rate of oxidisation at the surface so as to ensure an even thickness oxide layer. Preferably, the oxygen and argon gases are mixed together in a mixer valve before they enter the plasma chamber. This mixing ensures production of a more uniform oxide layer.

[0120] Heat can be applied to the plasma chamber to optimise the oxide if required. Diffusion is temperature dependent. Titanium has to diffuse from the bulk metal and bond with oxygen. Nickel will also diffuse out from the bulk, but titanium will diffuse at a faster rate, covering over the nickel and resulting in titanium oxides at the surface. The predominantly titanium dioxide layer can have elemental nickel, and nickel oxide in it, but titanium dioxide should always dominate the outermost layer of the oxide. The higher the temperature the more diffusion occurs and the thicker the oxide will be.

[0121] A pure, substantially contaminant free and even thickness new oxide layer is formed on the surface of the stent. At this point the stents will have improved corrosion resistance due to the cleanliness of the oxide.

[0122] Following the formation of the oxide layer on the stent 10, the device may then be coated with a layer of bioactive material, for example paclitaxel or any of the other bioactive materials disclosed herein. This may be singularly or in combination with one or more other bioactive materials. The result is a significantly improved bioactive material coated medical device. If the stents are to be further coated it is preferred that they be transferred as fast as possible to the coating equipment, for example within one hour or at least in the same day, so as to avoid contamination of the new oxide layer. Parts may be stored in ultra-clean glass vials to prolong this period and avoid contamination.

[0123] The stent may be coated (step 112 in FIG. 4) by any of a variety of systems including, for example, dipping, spraying and rolling. The bioactive material may be provided in pure form but more typically in solution or suspension in a volatile solvent such as ethanol or the like. The bioactive material may be coated onto the exposed surfaces of the stent 10 in one or more passes, in dependence upon the amount of bioactive material to be applied to the stent 10. Dipping will be typically be a single pass, although it is not excluded that the stent may be dipped in a multiple of times. Spraying and rolling may more commonly involve multiple passes.

[0124] The bioactive material coating is dried at the end of the coating stage and may also be dried between passes in a multiple-pass coating process. Drying may be by natural drying or forced drying.

[0125] The oxidised stent may optionally be cleaned prior to coating (step 112 in FIG. 4), although this will be dependent upon the nature of the handling of the stent 10 following its oxidation. For example, if the stent has been stored for some time after formation of the new oxide layer, it may be preferable to clean it before use. Such cleaning may be with an alcohol such as ethanol or with a weak plasma to remove any carbon deposits or other non-volatile deposits without removing any of the oxide layer.

[0126] Instead of, or in addition to, doping the oxide, it is contemplated that polar acidic or polar basic components could be added to the bulk material of the stent, in this example to the nickel titanium alloy of the stent. In accordance with the example given above, this may be by the addition of magnesium, aluminium, cerium, zinc, molybdenum, tungsten, niobium, tantalum, vanadium, zirconium, in concentrations typically less than 1000 parts per million as a dopant or in greater concentrations as an alloying element into the bulk material. These components are not designed to effect the structural characteristics of the bulk material, in this case to act as a shape memory alloy, but to effect the characteristics of the subsequently formed oxide layer, by the drawing out of these components from the bulk material to the surface and then into the oxide layer in order at stage 60, in order to provide the oxide layer with a polar acidic or polar base characteristic.

[0127] Referring briefly to FIG. 5, this shows a transverse cross-sectional view of a stent, such as the stent 10 shown in FIGS. 1, 2 and 3A and 3B. The tubular structure 12 of the stent, in particular strut 120, thereof has had its oxide layer 122 formed in the manner taught herein, so as to be amphoteric or to be polar acidic or polar basic. Bioactive agent 124 is deposited onto the oxide layer 122 (for example by spraying, rolling or dipping). It is not necessary to embed the bioactive agent in any containment matrix or layer, as is done in the prior art. It is preferred that the bioactive agent layer 124 is distinct from the base support (formed of the structure 120 and oxide 122). Thus, the exposed surface of the bioactive material layer 124 is solely the bioactive material (and possibly any functional groups included with it, such as excipients and so on).

[0128] At the interstice 130 between the bulk material 110 of the structure of stent 10 and the formed oxide layer 122 there may be remnants of contaminant materials, for example silicon. However, the electropolishing process will remove the majority of any such contaminants, including silicon, and at worst there may be some slight residue with crevasses on the surface of the bulk material. However, these will be minor and not affect the functional characteristics of the bulk material or of the subsequently formed oxide layer. Similarly, at the interstice 132 between the oxide layer 122 and the layer of bioactive material 124 there may be some minor residue of contaminants. Again, by controlled handling this can be minimised.

[0129] The oxide layer 122 of the stent 10, having a high polar acid or polar base characteristic, readily attracts its conjugate bioactive agent. This provides a uniform and consistent coating of bioactive agent across the contact surface or surfaces of the stent and therefore a consistent dosage of bioactive agent. Furthermore, it is possible in some cases to load a greater amount of bioactive agent to the contact surface of the stent.

[0130] The higher surface energy of the stent permits a greater variety of coating methods, given the greater adhesive characteristics of the oxide surface(s).

[0131] Although the method and system described above and in conjunction with treatment of a stent, the same method and system can be used to treat other medical devices.

[0132] In some cases it may be preferred that the bioactive agent is released quickly into the patient's tissues and for this purpose an excipient, such as urea and/or urea derivatives, gallates and gallate derivatives (such as epi gallo catechin gallate), saccharides and/or saccharide derivatives, chitin and/or chitin derivatives, ascorbic acid, citric acid, sterates and/or sterate derivatives, polyvinyl pyrolidone, dicalcium phosphate dihydrate, eudragit polymers and/or eudragit polymers derivatives, cellulose and/or cellulose derivatives, PEG, poylsorbate 80, sodium lauryl sulphate, chitosan, magnesium dioxide, silicon dioxide, carbonate derivatives, plasdone, butylated hydroxyanisole, succinic acid, sodium dioctyl sulfosuccinate, precirol ATO 5, may be added to the bioactive agent. The excipient will speed up the release of the bioactive agent once the medical device is deployed within the patient, for instance by the excipient dissolving within the patient's blood plasma and providing for quick release of the bioactive agent. When an excipient is used, this may be as a sublayer between the layer of bioactive material and the medical device or as a layer above the layer of bioactive material. The excipient acts to speed the release of the bioactive agent (drug for example), compared to a drug per se or a drug held in a containment or time release layer. In the case of a sublayer of excipient, the functionalisation of the surface to be coated will be matched to the nature of the excipient and the excipient matched to the bioactive agent or agents.

[0133] The bioactive material can be any of a large variety and many bioactive materials for coating medical devices are known in the art. The layer of bioactive material applied to the functionalised surfaces of the device may be of a single bioactive material or a combination of different bioactive agents, in dependence upon the desired treatment. There may also be provided other active agents in the bioactive material layer, such as excipients or other release facilitators.

[0134] The bioactive material of the coating may include at least one of: paclitaxel and/or paclitaxel derivatives, rapamycin and/or rapamycin derivatives, docetaxel and/or docetaxel derivatives, cabazitaxel and/or cabazitaxel derivatives, taxane and/or taxane derivatives, estrogen or estrogen derivatives; heparin or another thrombin inhibitor, hirudin, hirulog, argatroban, D-phenylalanyl-L-poly-L-arginyl chloromethyl ketone or another antithrombogenic agent, or mixtures thereof; urokinase, streptokinase, a tissue plasminogen activator, or another thrombolytic agent, or mixtures thereof; a fibrinolytic agent; a vasospasm inhibitor; a calcium channel blocker, a nitrate, nitric oxide, a nitric oxide promoter or another vasodilator; an antimicrobial agent or antibiotic; aspirin, ticlopdine or another antiplatelet agent; colchicine or another antimitotic, or another microtubule inhibitor; cytochalasin or another actin inhibitor; a remodelling inhibitor; deoxyribonucleic acid, an antisense nucleotide or another agent for molecular genetic intervention; GP IIb/IIIa, GP Ib-IX or another inhibitor or surface glycoprotein receptor; methotrexate or another antimetabolite or antiproliferative agent; an anti-cancer chemotherapeutic agent; dexamethasone, dexamethasone sodium phosphate, dexamethasone acetate or another dexamethasone derivative, or another anti-inflammatory steroid; dopamine, bromocriptine mesylate, pergolide mesylate or another dopamine agonist; 60Co (having a half life of 5.3 years), 192Ir (73.8 days), 32P (14.3 days), 111In (68 hours), 10 90Y (64 hours), 99mTc (6 hours) or another radio therapeutic agent; iodine containing compounds, barium-containing compounds, gold, tantalum, platinum, tungsten or another heavy metal functioning as a radiopaque agent; a peptide, a protein, an enzyme, an extracellular matrix component, a cellular component or another biologic agent; captopril, enalapril or another angiotensin converting 15 enzyme (ACE) inhibitor; ascorbic acid, alphatocopherol, superoxide dismutase, deferoxyamine, a 21-aminosteroid (lasaroid) or another free radical scavenger, iron chelator or antioxidant; angiopeptin; a 14C-, 3H-, 131I1-, 32P- or 36S-radiolabelled form or other radio labelled form of any of the foregoing; or a mixture of any of these.

[0135] The preferred embodiments described above relate to a nickel titanium alloy stent. Other examples are stainless steel, cobalt chromium and cobalt platinum stents. In these cases, the oxide is preferably formed primarily of Cr.sub.2O.sub.3. These examples of stent may also be subjected to doping of the oxide and/or of the bulk material in the manner described above.

[0136] The teachings herein provide a medical device which is more resistant to corrosion.

[0137] The teachings herein also make it possible to attach bioactive agents to the surfaces of medical devices without having to rely on binding agents or polymer of other matrix materials as in the prior art. Binding agents are considered to be substances which enhance the adhesion of a bioactive material layer at the support surface and generally act to retard the release of the bioactive agent or agents. A polymer or other matrix performs a similar role. Binding agents and matrices act as containment mechanisms.

[0138] It may be desirable to form hydroxyl groups at the surface of an implantable device to improve bonding with a bioactive material coating. Many implantable alloys (SS304, SS316, CoCr, Nobel metal alloys, NiTi and other titanium based alloys) can be hydroxylated, as can many implantable polymers. The hydroxides of the transition metals and post-transition metals usually have the metal in the +2 (M=Mn, Fe, Co, Ni, Cu, Zn) or +3 (M=Fe, Ru, Rh, Ir) oxidation state. None are soluble in water, and many are poorly defined. One complicating feature of the hydroxides is their tendency to undergo further condensation to the oxides, a process called olation. Hydroxides of metals in the +1 oxidation state are also poorly defined or unstable. For example, silver hydroxide Ag(OH) decomposes spontaneously to the oxide (Ag.sub.2O). Copper(I) and gold(I) hydroxides are also unstable, although stable adducts of CuOH and AuOH are known. The polymeric compounds M(OH)2 and M(OH)3 are in general prepared by increasing the pH of an aqueous solutions of the corresponding metal cations until the hydroxide precipitates out of solution. On the converse, the hydroxides dissolve in acidic solution. Zinc hydroxide Zn(OH)2 is amphoteric, forming the zincate ion Zn(OH)42- in strongly alkaline solution.

[0139] Some metals, e.g. V, Cr, Nb, Ta, Mo, W, tend to exist in high oxidation states.

[0140] Rather than forming hydroxides in aqueous solution, they convert to oxo clusters by the process of olation, forming polyoxometalates.

[0141] Acid-base properties are of considerable importance in the interaction between polar organic molecules and oxide surfaces and play an important role in phenomena such as corrosion inhibition and the adhesive behaviour. The presence of a hydroxylated surface also plays a significant role in the interaction of oxide surfaces with ambient water vapor. Water vapor adsorbs onto the outermost hydroxylated layer by forming a hydrogen bonded network on the hydroxylated surface. Thus, the nature of surface hydroxyls on metal oxide films is important in a number of surface phenomena involving metals. Not only are the acid-base properties of an oxide film of great interest, but so too is the surface concentration of the hydroxyl groups. There have been numerous studies on determination of the concentration of surface hydroxyls. However there have been few studies on the quantitative determination of the concentration of surface hydroxyl groups on low-area oxide covered metals, i.e. sheets or foils.

[0142] The surface oxide film on any given metal can be represented by the system shown in FIG. 8. The oxide film of thickness d consists of an outermost layer of chemisorbed water, a hydroxylated region of depth t.sub.hydrox and the innermost portion of the oxide film of depth t.sub.MO. The entire oxide film is covered by an overlayer of adsorbed organic contamination of thickness t.sub.c. This layer is referred to as carbon contamination. It has been assumed that the thickness of the hydroxylated region is due to a single layer of OH groups, i.e. up to 2.7 Å in thickness. This assumption does not hold for all metals. With aluminum for example, exposure to humid air produces a thickened hydroxide layer.

[0143] It is important to note that the outermost layer of organic carbon contamination includes oxygen-containing functional groups, i.e. C—O and O—C═O species which can complicate XPS analysis of the thickness of the OH and water layers. McCafferty and Wightman report the following corrected or compensated values for titanium in table 1 clearly identifying that the hydroxyl region was consistently 9.5 Å in thickness no matter the pre-treatment. Corrections required can be appreciable if the level of surface contamination is high. The correction decreases with a reduction in carbon contamination after either argon plasma treatment or sputtering of the carbon overlayer.

TABLE-US-00001 TABLE 1 The XPS binding energies for titanium metal/metal oxide systems with thickness calculations for the oxide and hydroxyl region. Depth of Thickness hydroxyl Surface of oxide region treatment film (Å) t.sub.hydrox (Å) I.sub.OH/I.sub.O As received 48 9.5 0.562 42 9.5 0.528 Ultrasonic 40 9.5 0.367 cleaned Argon 32 9.5 0.559 plasma

[0144] Hydroxyl (OH) groups may be formed at the surface of a metal oxide by the following process: [0145] 1. Plasma cleaning with H.sub.2O vapour is designed to remove volatile and non-volatile contamination on the surface of stents including carbon [0146] 2. Stable OH formation occurs on stent surfaces in the plasma processes in the following possible ways: [0147] a. Directly after the plasma is turned off as H.sub.2O is still being supplied into the chamber and the surface will have enough energy and dangling bonds to dissociate the water molecule creating OH [0148] b. In a similar manner to ‘a’ but the 0 and H molecules may be present in the plasma chamber left over from the plasma process [0149] c. By dunking the stents into liquid water after the plasma process without exposing them to atmosphere beforehand [0150] d. After the cleaned parts have been removed from the plasma chamber into the atmosphere assuming a non H and O gas is used during the plasma treatment and subsequent venting of the chamber

[0151] FIG. 9 shows a plasma chamber setup including a water bath in which stents can be ‘dunked’ into water post plasma cleaning or oxide removal without exposing them to the atmosphere beforehand. Water can be supplied via the H.sub.2O valve. Water vapour will be created when the water vapour valve opens and the pressures begin to equalise to the main chambers pressure (0.4 mbar) and 100 sccm flow rate. The pressures will never actually equalise, due to the constant vacuum being applied to the main chamber and H.sub.2O valve restriction between the main chamber and the side chamber. In effect the vacuum created in the main chamber will constantly draw water vapour from the side chamber. The water vapour is used as the plasma gas during plasma cleaning.

[0152] When the vacuum is turned off in the main chamber, the H.sub.2O valve can now be used to equalise the pressures. After which point the door between the chambers can be opened and the stents dunked into the bottle with water inside. The stents can be stored in this bottle until the next process keeping them free of contamination. Hydroxyl groups (OH groups) will form on the stents following these hydrolysis equations of titanium in an aqueous solution:

Ti—OH+H.sub.2O—[Ti—O].sup.−+H.sub.3O.sup.+

Ti—OH+H.sub.2O.sup.−[Ti—OH.sub.2]+OH.sup.−

[0153] FIGS. 10 to 15 show XPS quantification of OH and water on NiTi oxide surface after the surface has been washed with ethanol, and after it has been plasma cleaned. In the figures E=ethanol wash and P=plasma. The results obtained highlight the efficiency of plasma in removing or reducing carbon contamination depending on its state. They show that the oxide remains relatively unaffected and that Ti-OH is formed after plasma treatment without the carbon contamination over layer.

[0154] FIG. 16 is a table showing treatment conditions for four stents, A, B, C and D in a plasma chamber whilst removing the oxide layer from the surface of the stents and regrowing a new oxide layer at that surface. The machine used was the Diener Pico machine. This has a 13.56 MHz generator and a quartz glass chamber. The Pico system is a low-pressure system which has been found to be particularly useful for treating the intricate surface of a stent. As the plasma is in effect floating all around the stent, it can easily reach all surfaces of the stent to remove the oxide layer from the surface.

[0155] The inventors found that in a single batch of stents received from one manufacturer, the chemical composition of the surfaces of the individual stents within the batch could vary hugely. In particular the nickel content of the surface of the stent varied a lot. Due to the differences between the surfaces of the stents each stent was cut in half, one half was treated, and the other half left untreated. In this way the true result of the oxide removal and regrowth process on a given surface can be seen. FIGS. 17-20 show XPS data for the surfaces of stents A, B, C and D. The two columns in each graph compare the surface of one half of the stent as received (original), with the surface of the other half of the stent once treated in the plasma chamber under the conditions shown in the table of FIG. 16.

[0156] The XPS data shows that the original oxide layer has been removed from the stent and a new purer oxide layer has been grown on the surface. For a nitinol stent the surface is usually thought to be TiO.sub.2, but it is not as simple as that. NiO.sub.2 is also present and as the oxide layer thickens it can trap other contaminants in the oxide layer, such as elemental nickel, calcium, and other contaminants. As seen in the XPS data, there is less nickel present at the surface on the stent after the stent has been treated. This means that the contaminated oxide layer must have been removed, and replaced with a new purer oxide layer of TiO.sub.2. In addition to the decrease in nickel, the inventors have also observed a greater decrease in carbon contamination than was achieved simply by plasma cleaning alone. The surfaces treated according to the invention show the lowest amount of carbon at the surface that they have seen to date. This supports the idea that the original contaminated oxide layer has been removed and replaced with a new purer oxide layer.

[0157] FIG. 21 shows XPS data for plasma cleaned stent surface, compared with the surface of the same stent as received (original). When the inventors simply plasma cleaned a surface, without regrowing a new oxide layer at the surface (as shown in FIGS. 10-15), they observed a smaller decrease in carbon contamination at the surface, and an increase in nickel and titanium at the surface of the stent in the XPS data. It is thought that this is because the metal underneath the oxide is exposed during cleaning.

[0158] All optional and preferred features and modifications of the described embodiments and dependent claims are usable in all aspects of the invention taught herein. Furthermore, the individual features of the dependent claims, as well as all optional and preferred features and modifications of the described embodiments are combinable and interchangeable with one another.

[0159] The disclosure in the abstract accompanying this application is incorporated herein by reference.