METHODS FOR THE PRODUCTION OF CALCIUM, MAGNESIUM, AND ZINC SALTS OF SUGAR ACIDS

Abstract

A method has now been found for the preparation of calcium, magnesium, and zinc salts of sugar acids, this being the object of the present invention, which is characterized in that the method may include providing a sugar and oxidizing the sugar to a sugar acid in the presence of a noble metal catalyst, oxygen, and a heterogeneous hydroxide source. Preferably the oxidation is carried out with a gold catalyst, and a heterogeneous source of magnesium, calcium, or zinc hydroxide. The oxidation can be performed in a batch or continuous manner.

Claims

1. A method of producing a salt of a sugar acid, comprising: oxidizing a sugar to produce a sugar acid in the presence of a noble metal catalyst, oxygen, and a heterogeneous hydroxide source in a reaction vessel.

2. The method of claim 1 wherein the noble metal catalyst is a gold catalyst.

3. The method of claim 1, wherein the oxidation is carried out as a batch reaction, and in which all the heterogeneous hydroxide source is added at a beginning of the batch reaction.

4. The method of claim 1, wherein the oxidation is carried out as a batch reaction, and in which the heterogeneous hydroxide source is added during the batch reaction.

5. The method of claim 1, wherein the oxidation is carried out as a continuous reaction, and in which the heterogeneous hydroxide source is added during the continuous reaction.

6. The method of claim 1, wherein the oxidation is carried out as a continuous reaction, and in which the heterogeneous hydroxide source is present in a molar ratio greater than 1:2 with the sugar.

7. The method of claim 1, wherein the heterogeneous hydroxide source is magnesium hydroxide, calcium hydroxide, or zinc hydroxide carbonate.

8. The method of claim 1, wherein the heterogeneous hydroxide source is magnesium hydroxide, magnesium oxide, or magnesium carbonate.

9. The method of claim 1, wherein the heterogeneous hydroxide source is calcium oxide, calcium hydroxide, or calcium carbonate.

10. The method of claim 1, wherein the heterogeneous hydroxide source is zinc hydroxide carbonate, zinc hydroxide, or zinc oxide.

11. The method of claim 1, wherein the sugar acid is an aldonic acid or a disaccharide that comprises an aldonic acid.

12. The method of claim 1, wherein the sugar acid is gluconic acid, galactonic acid, xylonic acid, arabinonic acid, L-threonic acid, lactobionic acid, or maltiobionic acid.

13. The method of claim 1, wherein the reaction vessel may be pressurized with oxygen to a pressure of about 60 psi to about 200 psi.

14. The method of claim 1, wherein a temperature of the reaction solution may be about 30° C. to about 70° C.

15. The method of claim 1, wherein the salt of the sugar acid is zinc gluconate, calcium gluconate, magnesium gluconate, magnesium xylonate, magnesium L-threonate, or magnesium lactobionate.

16. The method of claim 1, wherein the sugar is glucose, galactose, xylose, arabinose, L-threose, lactose, or maltose.

Description

DETAILED DESCRIPTION

[0007] Various embodiments are described below. The relationship and functioning of the various elements of the embodiments may better be understood by reference to the following detailed description. Embodiments, however, are not limited to those illustrated below. In certain instances details may have been omitted that are not necessary for an understanding of embodiments disclosed herein.

Definitions

[0008] As used herein, the term sugar refers to an aldose or a disaccharide that include an aldose with a free aldehyde. Examples of sugars include glucose, galactose, xylose, arabinose, L-threose, lactose, and maltose.

[0009] As used herein, the term sugar acid refers to an aldonic acid or a disaccharide that includes and aldonic acid, and salts thereof. Examples of sugar acids include gluconic acid, galactonic acid, xylonic acid, arabinonic acid, lactobionic acid, and maltiobionic acid.

[0010] As used herein, heterogeneous hydroxide source refers to a heterogenous source of magnesium hydroxide, calcium hydroxide, or zinc hydroxide.

[0011] As used herein, heterogeneous source of magnesium hydroxide refers to magnesium hydroxide, magnesium oxide, or magnesium carbonate.

[0012] As used herein, heterogeneous source of calcium hydroxide refers to calcium oxide, calcium hydroxide, or calcium carbonate.

[0013] As used herein, heterogeneous source of zinc hydroxide refers to zinc hydroxide carbonate (a compound with a formula of [ZnCO.sub.3].sub.2.[Zn(OH).sub.2].sub.3), zinc hydroxide, or zinc oxide.

[0014] The term “oxidation” as used herein refers to the conversion of an aldehyde group (—CHO) of a sugar to a carboxyl group (—COOH) by a chemical reaction or physical process.

[0015] The term oxygen as used herein refers to molecular oxygen (O.sub.2). Oxygen may be provided as a gas alone or as constituent of mixture of gases such as exist in atmospheric air.

Providing a Sugar

[0016] The sugar is a raw material for the production of a sugar acid salt. Sugars are readily available compounds and can be produced from many raw materials. For example, glucose is commonly available from the hydrolysis of starch; lactose can be produced from milk; glucose and galactose can be produced from lactose or biomass hydrolysis; and xylose can be produced from biomass hydrolysis. Hydrolyses of raw materials that produce sugars can be performed commercially either enzymatically or chemically. Other synthetic routes to sugar production are also common.

[0017] In some embodiments, the sugar may be glucose, galactose, xylose, arabinose, lactose, or maltose. In some embodiments, the sugar may be glucose. In some embodiments, the sugar may be galactose. In some embodiments, the sugar may be xylose. In some embodiments, the sugar may be arabinose. In some embodiments, the sugar may be lactose. In some embodiments, the sugar may be maltose.

[0018] Preferably the sugar is provided in a solution with a concentration greater than 0.1 M, and more preferably with a concentration greater than 0.5 M. In some aspects, the concentration of the sugar may be from about 0.1 M to about 7 M. In some aspects, the concentration of the sugar may be from about 0.5 M to about 5 M, about 0.5 M to about 4 M, about 0.5 M to about 3 M, about 0.5 M to about 2 M, or about 0.1 M to about 1 M. In some aspects, the solution may be an aqueous solution.

Sugar Oxidation

[0019] The method of producing a salt of a sugar acid may include oxidizing a sugar to a sugar acid in the presence of a noble metal catalyst, oxygen, and a heterogeneous source of hydroxide. In some aspects, the heterogeneous source of hydroxide may be a heterogeneous source of magnesium hydroxide, calcium hydroxide, or zinc hydroxide. Preferably the noble metal catalyst is a gold catalyst. The sugar acid product is formed as the metal salt associated with the hydroxide used in the reaction.

[0020] In some embodiments, sugar acid oxidation may be performed in a batch reaction where all the heterogenous hydroxide source required for the reaction is added at the beginning of the reaction.

[0021] In other embodiments, sugar oxidation may be performed in a batch reaction where a slurry of the heterogenous hydroxide source and water are metered into the reaction over time.

[0022] In another embodiment, sugar oxidation may be performed in a continuous reaction where a slurry of the heterogenous hydroxide source and either water or sugar solution are added during the reaction. In another embodiment, sugar oxidation may be performed in a continuous reaction where an excess of heterogenous hydroxide source is maintained in the reaction chamber resulting in a heterogenous hydroxide cation to sugar ratio greater than 1:2. In some aspects, the heterogenous hydroxide cation to sugar ratio may be from about 1:2 to about 1000:1. In some aspects, the heterogenous hydroxide to sugar ratio may be about 1:2, about 5:1, about 50:1, or about 500:1.

[0023] In some aspects, the reaction vessel may be pressurized with oxygen to a pressure of about 60 psi to about 200 psi. In some aspects, the reaction vessel may be may be pressurized with oxygen to a pressure of about 70 psi, about 80 psi, about 90 psi, about 100 psi, about 110 psi, about 120 psi, about 130 psi, about 140 psi, or about 150 psi.

[0024] In some aspects, the temperature of the reaction solution may be about 30° C. to about 70° C. In some aspects, the temperature of the reaction solution may be about 40° C., about 50° C., or about 60° C.

[0025] In some aspects, the resulting concentration of the salt of the sugar acid in the reaction solution may be from about 0.1 M to about 1 M. In some aspects, the resulting concentration of the salt of the sugar acid in the reaction solution may be from about 0.2 M, about 0.3 M, about 0.4 M, or about 0.5 M.

[0026] In some aspects, the oxidation may be carried out as a batch reaction. In the batch reaction, all of the heterogeneous hydroxide source may be added at a beginning of the batch reaction. In some aspects, the heterogeneous hydroxide source may be added during the batch reaction.

[0027] In some aspects, the oxidation may be carried out as a continuous reaction. For a continuous reaction, the heterogeneous hydroxide source may be added during the continuous reaction. In some aspects, the reactor may be charged with an excess amount of the heterogeneous hydroxide source and the sugar may be fed into the reactor continuously.

EXAMPLES

Example 1

[0028] A 0.60 M solution of glucose was provided. A 1 liter pressure vessel was provided to which the glucose solution was added and dosed with 4 g per liter of a 4.5 wt % of gold in the catalyst, and 17.5 g per liter magnesium hydroxide. The reaction vessel was pressurized with oxygen at 100 psi, and the temperature was raised to 50° C. The reaction was stirred for 2.9 hrs, after which it was cooled to room temperature and analyzed. The resulting solution had a 0.30 M concentration of magnesium gluconate, which constituted a 100% yield.

Example 2

[0029] A 0.68 M solution of glucose was provided. A 1.5 liter pressure vessel was proved capable of running in continuous mode. The reactor was charged with 900 ml of glucose solution along with 8 g per liter of a 4.5% gold catalyst and 19.8 g per liter of magnesium hydroxide. The reaction vessel was pressurized with 100 psi oxygen, and the temperature was raised to 70° C. After 1.5 hrs, the reaction began to operate in continuous mode by the addition of a glucose solution (0.70 M):magnesium hydroxide slurry (19.7 g per liter) at a rate of 5 ml per minute. Product solution was removed from the reaction vessel at a rate of approximately 5 ml per minute. The reaction proceeded for another 5.5 hrs. The resulting product solution had a concentration of 0.30 M magnesium gluconate, which constituted an 88% yield.

Example 3

[0030] A 0.5 M solution glucose was provided. In five separate experiments, a 1 liter pressure vessel was provided to which 0.5 liters of glucose solution was added and dosed with 4 g per liter of a 4.5% gold catalyst, and a heterogeneous hydroxide source as listed in Table 1. The reaction vessel was pressurized with oxygen at 100 psi. The reaction temperature and times of each experiment are given in Table 1, along with the respective glucose conversion and selectivity of each experiment.

TABLE-US-00001 TABLE 1 Reaction Glucose Glucose Heterogeneous Hydroxide Heterogeneous Temperature Tiem Conversion Selectivity Product Source Hydroxide (g) (C.) (hr) (%) (%) Zinc Gluconate Zinc Oxide 18.1 60 3.6 35 94 Zinc Gluconate Zinc Hydroxide Carbonate 124.9 60 5.3 26 85 Calcium Gluconate Calcium Carbonate 22.5 90 5.6 89 90 Calcium Gluconate Calcium Hydroxide 9.3 50 3.5 97 95 Magnesium Gluconate Magnesium Hydroxide 6.9 70 4.0 96 100 Magnesium Xylonate Magnesium Hydroxide 6.9 50 3.7 90 82 Magnesiom Lactobionate Magnesium Hydroxide 6.9 50 6.0 89 87 Magnesium L-Threonate Magnesium Hydroxide 6.9 70 3.00 100 99

[0031] All of the compositions and methods disclosed and claimed herein can be made and executed without undue experimentation in light of the present disclosure. While this invention may be embodied in many different forms, there are described in detail herein specific preferred embodiments of the invention. The present disclosure is an exemplification of the principles of the invention and is not intended to limit the invention to the particular embodiments illustrated. In addition, unless expressly stated to the contrary, use of the term “a” is intended to include “at least one” or “one or more.” For example, “a sugar” is intended to include “at least one sugar” or “one or more sugars.”

[0032] Any ranges given either in absolute terms or in approximate terms are intended to encompass both, and any definitions used herein are intended to be clarifying and not limiting. Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all subranges (including all fractional and whole values) subsumed therein.

Statements

[0033] 1. A method of producing a salt of a sugar acid, comprising:

[0034] oxidizing a sugar to produce a sugar acid in the presence of a noble metal catalyst, oxygen, and a heterogeneous hydroxide source in a reaction vessel.

[0035] 2. The method of 1 wherein the noble metal catalyst is a gold catalyst.

[0036] 3. The method of any one of 1-2, wherein the oxidation is carried out as a batch reaction, and in which all the heterogeneous hydroxide source is added at a beginning of the batch reaction.

[0037] 4. The method of any one of 1-2, wherein the oxidation is carried out as a batch reaction, and in which the heterogeneous hydroxide source is added during the batch reaction.

[0038] 5. The method of any one of 1-2, wherein the oxidation is carried out as a continuous reaction, and in which the heterogeneous hydroxide source is added during the continuous reaction.

[0039] 6. The method of any one of 1-2, wherein the oxidation is carried out as a continuous reaction, and in which the heterogeneous hydroxide source is present in a molar ratio greater than 1:2 with the sugar.

[0040] 7. The method of any one of 1-6, wherein the heterogeneous hydroxide source is magnesium hydroxide, calcium hydroxide, or zinc hydroxide carbonate.

[0041] 8. The method of any one of 1-7, wherein the heterogeneous hydroxide source is magnesium hydroxide, magnesium oxide, or magnesium carbonate.

[0042] 9. The method of any one of 1-7, wherein the heterogeneous hydroxide source is calcium oxide, calcium hydroxide, or calcium carbonate.

[0043] 10. The method of any one of 1-7, wherein the heterogeneous hydroxide source is zinc hydroxide carbonate, zinc hydroxide, or zinc oxide.

[0044] 11. The method of any one of 1-10, wherein the sugar acid is an aldonic acid or a disaccharide that comprises an aldonic acid.

[0045] 12. The method of any one of 1-11, wherein the sugar acid is gluconic acid, galactonic acid, xylonic acid, arabinonic acid, L-threonic acid, lactobionic acid, or maltiobionic acid.

[0046] 13. The method of any one of 1-12, wherein the reaction vessel may be pressurized with oxygen to a pressure of about 60 psi to about 200 psi.

[0047] 14. The method of any one of 1-13, wherein a temperature of the reaction solution may be about 30° C. to about 70° C.

[0048] 15. The method of any one of 1-14, wherein the salt of the sugar acid is zinc gluconate, calcium gluconate, magnesium gluconate, magnesium xylonate, magnesium L-threonate, or magnesium lactobionate.

[0049] 16. The method of any one of 1-15, wherein the sugar is glucose, galactose, xylose, arabinose, L-threose, lactose, or maltose.

[0050] Furthermore, the invention encompasses any and all possible combinations of some or all of the various embodiments described herein. It should also be understood that various changes and modifications to the presently preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modifications can be made without departing from the spirit and scope of the invention and without diminishing its intended advantages. It is therefore intended that such changes and modifications be covered by the appended claims.