COMPOSITIONS AND PROCESSES FOR OPTIMIZING OXYGEN REDUCTION AND OXYGEN EVOLUTION REACTIONS

Abstract

Compositions and processes for optimizing oxygen reduction and oxygen evolution reactions are provided. Oxygen reduction and oxygen evolution catalysts include oxide compositions having a general formula a formula A.sub.2-xMO.sub.y, where x is electrochemically tuned to find optimal A content that delivers the best catalytic performance in a chemical system. The process provides the ability to find the optimal catalytic performance by tuning A and hence, the binding strength of O.

Claims

1. An oxygen reduction reaction (ORR) and/or oxygen evolution reaction (OER) catalyst comprising a formula A.sub.2-xMO.sub.y; wherein A is Li, wherein y is 2 to 3, wherein M comprises a precious metal, wherein the ORR and/or OER catalyst has an oxygen vacancy formation energy or oxygen binding energy of about −1 to about 1 eV/atom obtained by electrochemically tuning x in a range of 0 to 2.

2. The ORR and/or OER catalyst of claim 1 wherein M comprises at least one of Rh, Jr, Ru, Pd, Au, Ag, Os and mixtures thereof.

3. The ORR and/or OER catalyst of claim 1 wherein M is at least one of Rh, Pd, and mixtures thereof.

4. The ORR and/or OER catalyst of claim 1 wherein M is at least one Ru, Jr, and mixtures thereof.

5. The ORR and/or OER catalyst of claim 1 wherein M is selected from the group consisting of Pt/Fe, Rh/Ni, and Pd/Mn.

6. The ORR and/or OER catalyst of claim 1 wherein the ORR and/or OER catalyst is a layered crystal structure capable of insertion and desorption of lithium ions.

7. The ORR and/or OER catalyst of claim 1 wherein the ORR and/or OER catalyst is provided in a nanoparticle structure.

8. The ORR and/or OER catalyst of claim 1 wherein the ORR and/or OER catalyst is provided in a nanosheet structure.

9. An oxygen reduction reaction (ORR) and/or oxygen evolution reaction (OER) catalyst comprising a formula A.sub.2-xMO.sub.y; wherein A is Li, wherein y is 3, wherein M comprises is a precious metal selected from at least one of Rh, Jr, Ru, Pd, Au, Ag, Os and mixtures thereof, wherein the ORR and/or OER catalyst has an oxygen vacancy formation energy or oxygen binding energy of about −1 to about 1 eV/atom obtained by electrochemically tuning x in a range of 0 to 2, and the ORR and/or OER catalyst is provided in an at least one of a nanoparticle structure and a nanosheet structure.

10. The ORR and/or OER catalyst of claim 9 wherein M is at least one of Rh, Pd, and mixtures thereof.

11. The ORR and/or OER catalyst of claim 9 wherein M is at least one Ru, Jr, and mixtures thereof.

12. The ORR and/or OER catalyst of claim 9 wherein M is selected from the group consisting of Pt/Fe, Rh/Ni, and Pd/Mn.

13. The ORR and/or OER catalyst of claim 9 wherein the ORR and/or OER catalyst is a layered crystal structure capable of insertion and desorption of lithium ions.

14. A process for optimizing oxygen reduction or oxygen evolution catalytic activity, the process comprising: providing an oxygen reduction (ORR) and/or oxygen evolution reaction (OER) catalyst of a formula A.sub.2-xMO.sub.y; wherein A is Li, wherein x is 0 to 2, wherein y is 2 to 3, wherein M comprises a precious metal selected from at least one of Rh, Jr, Ru, Pd, Au, Ag, Os and mixtures thereof; and electrochemically tuning an initial value of x to improve catalytic activity of oxygen reduction or oxygen evolution reactions.

15. The process of claim 14 wherein M is at least one of Rh, Pd, and mixtures thereof.

16. The process of claim 14 wherein M is at least one of Ru, Jr, and mixtures thereof.

17. The process of claim 14 wherein M is selected from the group consisting of Rh/Ni and Pd/Mn.

18. The process of claim 14 wherein the electrochemically tuning of an initial value of x includes applying a bias to the ORR and/or OER catalyst.

19. The process of claim 14 wherein the process includes electrochemically tuning an amount of A by applying a current to the ORR and/or OER catalyst to provide an oxygen binding strength for absorption or desorption of oxygen.

20. The process of claim 14 wherein the ORR and/or OER catalyst is a layered crystal structure capable of insertion and desorption of lithium ions.

Description

BRIEF DESCRIPTION OF FIGURES

[0010] So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

[0011] FIG. 1 describes oxygen vacancy formation energies of Li.sub.2-xMO.sub.3 materials as a function of delithiation (x ranging between 0 and 2).

[0012] FIG. 2 shows a Pourbaix diagram used for determining the stability of the compositionally tuned layered material near oxygen evolution reaction potentials.

DETAILED DESCRIPTION

[0013] The following description is not to be taken in a limiting sense, but is made merely for the purpose of describing the general principles of exemplary embodiments. The scope of the invention should be determined with reference to the claims.

[0014] Cost effective catalysts material are provided that possess improved activity and stability, and which may include less expensive materials. The oxide compositions include compositions having a general formula A.sub.2-xMO.sub.y. In this aspect, x is a “handle” to find optimal A content that would deliver the best catalytic performance in a chemical system.

[0015] A process is provided for optimizing oxygen reduction or oxygen evolution catalytic activity. The process provides the ability to find the optimal catalytic performance or highest OER or ORR reaction rate or the lowest overpotential at a given current density for the given catalytic material, by tuning A and hence, the binding strength of O. The ability to electrochemically control the content of A, provides a “dynamic” catalyst, where one can apply and alternate between two biases to shift back and forth between two A contents in A.sub.2-xMO.sub.y, in an electrochemical setup, to dynamically tune the catalyst “on-the-fly” for optimal adsorption and desorption stages for catalytic reaction.

[0016] Oxide Compositions

[0017] Li-ion or similar rechargeable battery electrodes can be utilized and mobile ion content can be tuned to control the electronic structure of the material that governs O binding and ultimately the ORR or OER catalytic activity. Optimal catalytic activity is achieved at delithiation levels near, but before the evolution of O.sub.2 (i.e. discharge states of electrodes normally avoided in Li-ion battery operations). If these layered materials are delithiated too deeply below a certain Li content, then the oxygen in the material destabilizes and tends to form O—O dimers and evolve as O.sub.2 gas or react with other materials in the environment. This Li content threshold is a function of the structure of the oxide, chemical identity of the redox active or inactive metals, and other factors.

[0018] Oxide compositions include compounds having a general formula A.sub.2-xMO.sub.y. In this aspect, these layered materials include a mobile ion A, where A is an alkali metal such as lithium (Li) or sodium (Na). Li and Na are useful for electrochemically tuning a binding strength of oxygen.

[0019] Further to the general formula, M is a metal ion that may have multiple nominal oxidation states. In this aspect, M may include metals such as cobalt (Co), manganese (Mn), iron (Fe), nickel (Ni), titanium (Ti), vanadium (V), germanium (Ge), zirconium (Zr), molybdenum (Mo), hafnium (Hf), osmium (Os), ruthenium (Ru), rhodium (Rh), lead (Pb), tin (Sn), iridium (Jr), platinum (Pt), gold (Au), silver (Ag), and mixtures thereof. In another aspect, M includes metal ions such Pt, Rh, Jr, Ru, Pd, Au, Ag, Os and mixtures thereof.

[0020] In one aspect, M is a single element, and in another aspect, M is a mixture of elements. A mixture of M may include metals such as Pt, Rh, Jr, Ru, Pd, Au, Ag, Os and one or more elements that include Fe, Mn, Cu, and Ni. M may include any ratio of these elements. Some examples of element combinations include Pt/Fe, Rh/Ni and Pd/Mn and similar combinations.

[0021] The oxide composition has an oxygen vacancy formation energy or oxygen binding energy of about −1 to about 1 eV/atom. The oxygen binding strength, and therefore the ORR or OER catalytic performance of the oxide composition, can be controlled by altering the electronic structure of Li-ions in Li-metal oxide or similar Na-ion, Na-metal oxide.

[0022] For example, in a Li-rich Li.sub.2MnO.sub.3 electrode, Mn has a nominal oxidation state of 4+. As Li is being removed, the nominal oxidation state of Mn starts increasing. However, in actuality, electronic states of Mn (d-electrons) and O (p-electrons) are overlapping and with Li removal, electrons normally associated with O are being removed as well, inducing a valence state of −2+m for O. As this continues, and the electronic structure of O anion become more and more unfavorable for binding (i.e. nominal valence approaching −1, after a certain point, O-dimer formation in the material can be favored, and O.sub.2 gas may subsequently evolve. The Li.sub.2-xMnO.sub.3 material system can be scanned within 0<x<2 to find an optimal catalytically active composition, presence of which is expected from the demonstrated controllability of oxygen vacancy formation energy by tuning of x in FIG. 1.

[0023] FIG. 1 describes oxygen vacancy formation energies of Li.sub.2-xMnO.sub.3 materials as a function of delithiation (x). The figure demonstrates the ability to control 0 binding of strength of different metal oxide compositions via Li content. In this aspect, the oxide composition is a layered crystal structure capable of insertion and desorption of lithium or sodium ions. Outside the range of oxygen vacancy formation or binding energy where optimal material composition delivering the best catalytic activity (measured in terms of the current density) is, the current density would effectively be an order of magnitude lower. In this aspect, a current density for an optimal material composition delivering a significant catalytic activity is about 1 mA/cm.sup.2 or greater.

[0024] The oxide compositions may be provided as part of an electrode. In one aspect, surface areas of oxide compositions are enhanced by providing the oxide compositions in a nanoparticle structure or in a nanosheet structure.

[0025] Optimizing Oxygen Reduction or Oxygen Evolution Catalytic Activity

[0026] A process for optimizing oxygen reduction or oxygen evolution catalytic activity includes providing a metal oxide having a general formula A.sub.2-xMO.sub.y and electrochemically tuning an initial value of x to improve catalytic activity of oxygen reduction or oxygen evolution reactions. The initial value of x before tuning may be the as-synthesized composition of A.sub.2-xMO.sub.y.

[0027] The metal oxide of the general formula is a layered material that includes a mobile ion where A is an alkali metal such as lithium (Li) or sodium (Na). Li and Na are useful for electrochemically tuning a binding strength of oxygen. Further to the general formula, M is a metal ion that may have multiple nominal oxidation states. In this aspect, M may include metals such as cobalt (Co), manganese (Mn), iron (Fe), nickel (Ni), titanium (Ti), vanadium (V), germanium (Ge), zirconium (Zr), molybdenum (Mo), hafnium (Hf), osmium (Os), ruthenium (Ru), rhodium (Rh), lead (Pb), tin (Sn), iridium (Ir), platinum (Pt), gold (Au), silver (Ag), and mixtures thereof. In another aspect, M includes metal ions such Pt, Rh, Ir, Ru, Pd, Au, Ag, Os and mixtures thereof. In one aspect, M is a single element, and in another aspect, M is a mixture of elements. A mixture of M may include metals such as Pt, Rh, Ir, Ru, Pd, Au, Ag, Os and one or more elements that include Fe, Mn, Cu, and Ni.

[0028] The oxide composition is a layered crystal structure capable of insertion and desorption of lithium or sodium ions. In this aspect, the process includes electrochemically tuning an initial value of x by applying a bias or current to the metal oxide composition to provide an oxygen binding strength for adsorption or desorption of oxygen. The value of x is adjusted to provide the oxide composition with an oxygen vacancy formation energy or oxygen binding energy of about −1 to about 1 eV/atom. The tuning may depend upon the desired catalytic activity.

[0029] Maintaining Electrochemical Stability of an Oxide Composition

[0030] A process for maintaining electrochemical stability of an oxide composition in an oxygen reduction or oxygen evolution reaction includes providing a metal oxide having a general formula A.sub.2-xMO.sub.y and an electrolyte composition and preparing the metal oxide composition to have a region of stability in the Pourbaix diagram encompassing the OER or ORR working electrochemical potential and pH values. The electrolyte composition includes a salt of M and/or a salt of A.

[0031] The metal oxide of the general formula is a layered material that includes a mobile ion where A is an alkali metal such as lithium (Li) or sodium (Na). Li and Na are useful for electrochemically tuning a binding strength of oxygen. Further to the general formula, M is a metal ion that may have multiple nominal oxidation states. In this aspect, M may include metals such as cobalt (Co), manganese (Mn), iron (Fe), nickel (Ni), titanium (Ti), vanadium (V), germanium (Ge), zirconium (Zr), molybdenum (Mo), hafnium (Hf), osmium (Os), ruthenium (Ru), rhodium (Rh), lead (Pb), tin (Sn), iridium (Ir), platinum (Pt), gold (Au), silver (Ag), and mixtures thereof. In another aspect, M includes metal ions such Pt, Rh, Ir, Ru, Pd, Au, Ag, Os and mixtures thereof. In one aspect, M is a single element, and in another aspect, M is a mixture of elements. A mixture of M may include metals such as Pt, Rh, Ir, Ru, Pd, Au, Ag, Os and one or more elements that include Fe, Mn, Cu, and Ni. In this aspect, the oxide composition is a layered crystal structure capable of insertion and desorption of lithium or sodium ions.

[0032] As shown in FIG. 2, a Pourbaix diagram can be used to determine the stability of the compositionally tuned layered material near the oxygen evolution reaction potentials. Electrode potential can be adjusted in conjunction with O-binding strength for ensuring stability in the OER or ORR reaction regions. The potential of the electrode changes with Li content and shifts upward as more Li is removed. A and M concentrations in the electrolytes can be utilized to adjust the location of electrode potentials.

[0033] Conditions or parameters of aqueous solution systems within a system are monitored and maintained relative to the metal oxide stability area (or co-precipitation or metal oxide stability area when other metals are processed) with regard to electrochemical (oxidizing) potential (Eh) range and pH range at the prescribed system molarity, temperature and pressure in order to provide an Eh-pH combination to achieve stable solution equilibrium, as defined by the metal oxide stability area as delineated in, for example a Pourbaix Diagram. The process includes selecting an appropriate pH range for use with the particular metal salt and solvent employed by reference to a Pourbaix diagram. The lines in the Pourbaix Diagram show the equilibrium conditions, that is, where the activities are equal, for the species (or reaction products) on each side of that line. On either side of the line, one form of the species will instead be said to be predominant. The pH, and/or the suitable pH agent, is selected such that the formation of the metal oxide species is predominant over the formation of the metal hydroxide species.

[0034] FIG. 2 illustrates that by adjusting A and/or M salt concentration in electrolyte, one can shift or modify the shape of the stability region (as illustrated by arrows shown) for A.sub.2-xMO.sub.3 (catalyst), and hence make it relatively more stable under OER or ORR conditions.

[0035] In another aspect, electrochemical stability is enhanced by adding a salt of M and or a salt of A in the electrolyte. Layered crystal materials may be exfoliated and dispersed in an electrolyte to expose more surface area for catalytic activity.

[0036] Pourbaix diagram encompassing the metal oxide of interest can be obtained in advance from the literature or from theoretical calculations, and/or stability can be step by step controlled by incremental additions of salts of M or Li into the electrolyte. Electrolyte would normally have a large affinity for the dissolved ions of M and Li if it does not contain these ions upfront, hence can destabilize the metal oxide and result in its dissolution/degradation. The gradual addition of the corresponding M and/or Li salts into electrolyte can be used as a mechanism to lower the mentioned affinity of electrolyte for these ions, and support stabilization of the catalyst.

[0037] For example, if the metal oxide is not stable under the pH and electrochemical potential pertaining to its catalytic reaction (ORR or OER), addition of a salt of M to the electrolyte may stabilize it by increasing the chemical potential of M in the electrolyte (or decreasing the electrolytes affinity for M). Similarly, if the metal oxide is not stable under the pH and electrochemical potential pertaining to its catalytic reaction (ORR or OER), addition of a salt of Li to the electrolyte may stabilize it.

Example: Manufacture of Batteries Using Metal Oxide Catalyst Compositions

[0038] Batteries, such as for example lithium air batteries, may utilize the metal oxide compositions as catalysts. An example of manufacturing the lithium air battery is as follows. First, metal oxide catalyst, a conducting agent, and a binder are mixed, and then are added to an appropriate solvent to prepare a positive electrode slurry. The positive electrode slurry is coated and dried on a surface of a current collector, optionally followed by press-molding in order to improve the electrode density, thereby preparing a positive electrode.

[0039] Next, a negative electrode is mounted in one side of a case, and the positive electrode with a separator is mounted in another side opposite to the negative electrode, wherein the separator is disposed on the side of the positive electrode facing toward the negative electrode. An electrolyte is injected between the positive electrode and the negative electrode, a porous current electrode is disposed on the positive electrode, and a pressing member that allows air to reach the positive electrode is pushed to fix a cell, thereby completing the manufacture of the lithium air battery. A lithium ion conductive solid electrolyte membrane may be further disposed on one surface of the negative electrode.

[0040] The case may be divided into upper and lower parts, which contact the negative and positive electrodes, respectively. An insulating resin may be disposed between the upper and lower parts to electrically insulate the positive and negative electrodes from each other.

[0041] The lithium air battery may be either a lithium primary battery or a lithium secondary battery. The lithium air battery may have any of various shapes, and in some embodiments, may have a shape like a coin, a button, a sheet, a stack, a cylinder, a plane, or a horn. The lithium air battery may be used as a large-scale battery for electric vehicles.

[0042] During discharge of the battery, oxygen flows into the composite cathode from the outside and undergoes an oxygen reduction reaction (ORR) with lithium ions derived from the anode to produce a lithium oxide. On the other hand, during charge of the battery, oxidation of the lithium oxide occurs in an oxygen evolution reaction (OER), and lithium ions migrate to the anode and are electrodeposited as lithium metal.

[0043] While the invention herein disclosed has been described by means of specific embodiments, examples and applications thereof, numerous modifications and variations could be made thereto by those skilled in the art without departing from the scope of the invention set forth in the claims.