Abstract

Provided is a process for preparing certain silane precursor compounds, e.g., triiodosilane from trichlorosilane utilizing lithium iodide in powder form and catalyzed by tertiary amines. The process provides triiodosilane in high yields and high purity. Triiodosilane is a precursor compound useful in the atomic layer deposition of silicon onto various microelectronic device structures.

Claims

1. A process for preparing compounds of the formula (R.sup.1).sub.ySi(I).sub.z, wherein each R.sup.1 is independently chosen from hydrogen, C.sub.1-C.sub.9 alkyl, vinyl, or a C.sub.2-C.sub.4 alkynyl group, y is 0, 1, 2, or 3, and z is 1, 2, 3, or 4, and wherein y+z is equal to 4, which comprises contacting a compound of the formula (R.sup.1).sub.ySi(Cl).sub.z with lithium iodide in the presence of a tertiary amine, tetraalkylammonium halide, or tetraalkylphosphonium halide wherein the lithium iodide is in the form of a powder having an average particle size of less than about 2 mm.

2. The process of claim 1, wherein the particle size of the lithium iodide powder is less than about 1 mm.

3. The process of claim 1, wherein the particle size of the lithium iodide powder is less than about 0.5 mm.

4. The process of claim 1, wherein the particle size of the lithium iodide powder is less than about 0.1 mm.

5. The process of claim 1, wherein the compound of the formula (R.sup.1).sub.ySi(I).sub.z is triiodosilane.

6. The process of claim 1, wherein the compound of the formula (R.sup.1).sub.ySi(I).sub.z is chosen from CH.sub.3Si(I).sub.3, CH.sub.3CH.sub.2Si(I).sub.3, CH.sub.3CH.sub.2CH.sub.2Si(I).sub.3, CH.sub.3CH.sub.2CH.sub.2CH.sub.2Si(I).sub.3, (CH.sub.3).sub.2CHSi(I).sub.3, CH.sub.3CH.sub.2(CH.sub.3)CHSi(I).sub.3, (CH.sub.3).sub.3CSi(I).sub.3, CH.sub.3CH.sub.2CH.sub.2CH.sub.2Si(I).sub.3, (CH.sub.3).sub.3CCH.sub.2Si(I).sub.3, CH.sub.2═CHSi(I).sub.3, CH≡CSi(I).sub.3, CH≡CCH.sub.2Si(I).sub.3, CH.sub.3C≡CSi(I).sub.3, CH≡CCH.sub.2CH.sub.2Si(I).sub.3, CH.sub.3CH≡CCH.sub.2Si(I).sub.3, CH.sub.2 CH.sub.2CH.sub.2C≡CSi(I).sub.3, (CH.sub.3).sub.2Si(I).sub.2, CH.sub.3CH.sub.2).sub.2Si(I).sub.2, (CH.sub.3CH.sub.2CH.sub.2).sub.2Si(I).sub.2, (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.2Si(I).sub.2, ((CH.sub.3).sub.2CH).sub.2Si(I).sub.2, (CH.sub.3CH.sub.2(CH.sub.3)CH).sub.2Si(I).sub.2, ((CH.sub.3).sub.3C).sub.2Si(I).sub.2, (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.2Si(I).sub.2, ((CH.sub.3).sub.3CCH.sub.2).sub.2Si(I).sub.2, (CH.sub.2═CH).sub.2Si(I).sub.2, (CH≡C).sub.2Si(I).sub.2, (CH≡CCH.sub.2).sub.2Si(I).sub.2, (CH.sub.3C≡C).sub.2Si(I).sub.2, (CH≡CCH.sub.2CH.sub.2).sub.2Si(I).sub.2, (CH.sub.3CH≡CCH.sub.2).sub.2Si(I).sub.2, (CH.sub.2CH.sub.2CH.sub.2C≡C).sub.2Si(I).sub.2, (CH.sub.3).sub.3SiI, (CH.sub.3CH.sub.2).sub.3SiI, (CH.sub.3CH.sub.2CH.sub.2).sub.3SiI, (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.3SiI, ((CH.sub.3).sub.2CH).sub.3SiI, (CH.sub.3CH.sub.2(CH.sub.3)CH).sub.3SiI, ((CH.sub.3).sub.3C).sub.3SiI, (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.3SiI, ((CH.sub.3).sub.3CCH.sub.2).sub.3SiI, (CH.sub.2═CH).sub.3SiI, (CH≡C).sub.3SiI, (CH≡CCH.sub.2).sub.3SiI, (CH.sub.3C≡C).sub.3Si, (CH≡CCH.sub.2CH.sub.2).sub.3SiI, (CH.sub.3CH≡CCH.sub.2).sub.3SiI, and (CH.sub.2CH.sub.2CH.sub.2C≡C).sub.3SiI.

7. The process of claim 1, wherein the tertiary amine is a mono-amine.

8. The process of claim 7, wherein the tertiary amine is triethylamine.

9. The process of claim 1, wherein the tertiary amine has the formula: ##STR00004## wherein each R is independently hydrogen or a C.sub.1-C.sub.9 alkyl group, m is an integer of from 1 to 4, and n is an integer of from 2 to 5.

10. The process of claim 9, wherein the tertiary amine has the formula ##STR00005## wherein each R is independently hydrogen or a C.sub.1-C.sub.9 alkyl group.

11. The process of claim 9, wherein the tertiary amine has the formula ##STR00006## wherein each R is independently hydrogen or a C.sub.1-C.sub.9 alkyl group.

12. The process of claim 9, wherein each R is independently chosen from methyl and ethyl.

13. The process of claim 1, wherein the tertiary amine is N,N,N′,N′-tetraethylene diamine.

14. The process of claim 1, wherein the tertiary amine is N,N,N′,N″,N″-pentamethyldiethylenetriamine.

15. The process of claim 1, wherein the tetraalkylammonium chloride is tetrabutylammonium chloride.

16. The process of claim 1, wherein the tetraalkylphosphonium chloride is tetrabutylphosphonium chloride.

Description

DETAILED DESCRIPTION OF THE INVENTION

(1) The present invention provides a process for preparing compounds of the formula (R.sup.1).sub.ySi(I).sub.z, wherein each R.sup.1 is independently chosen from hydrogen, C.sub.1-C.sub.9 alkyl, vinyl, or a C.sub.2-C.sub.4 alkynyl group, y is 0, 1, 2, or 3, and z is 1, 2, 3, or 4, and wherein y+z is equal to 4, which comprises contacting a compound of the formula (R.sup.1).sub.ySi(Cl).sub.z with lithium iodide in the presence of a tertiary amine, wherein the lithium iodide is in the form of a powder having an average particle size of less than about 2 mm.

(2) In one embodiment, the compound of the formula (R.sup.1).sub.ySi(I).sub.z is triiodosilane.

(3) In another embodiment, R.sup.1 is chosen from methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, t-butyl, n-pentyl, neopentyl, vinyl, and C.sub.2-C.sub.4 alkynyl.

(4) In another embodiment, the compound of the formula (R.sup.1).sub.ySi(I).sub.z is chosen from the following:

(5) CH.sub.3Si(I).sub.3;

(6) CH.sub.3CH.sub.2Si(I).sub.3;

(7) CH.sub.3CH.sub.2CH.sub.2Si(I).sub.3;

(8) CH.sub.3CH.sub.2CH.sub.2CH.sub.2Si(I).sub.3;

(9) (CH.sub.3).sub.2CHSi(I).sub.3;

(10) CH.sub.3CH.sub.2(CH.sub.3)CHSi(I).sub.3;

(11) (CH.sub.3).sub.3CSi(I).sub.3;

(12) CH.sub.3CH.sub.2CH.sub.2CH.sub.2Si(I).sub.3;

(13) (CH.sub.3).sub.3CCH.sub.2Si(I).sub.3;

(14) CH.sub.2═CHSi(I).sub.3;

(15) CH≡CSi(I).sub.3;

(16) CH≡CCH.sub.2Si(I).sub.3;

(17) CH.sub.3C≡CSi(I).sub.3;

(18) CH≡CCH.sub.2CH.sub.2Si(I).sub.3;

(19) CH.sub.3CH≡CCH.sub.2Si(I).sub.3;

(20) CH.sub.2 CH.sub.2CH.sub.2C≡CSi(I).sub.3;

(21) (CH.sub.3).sub.2Si(I).sub.2;

(22) (CH.sub.3CH.sub.2).sub.2Si(I).sub.2;

(23) (CH.sub.3CH.sub.2CH.sub.2).sub.2Si(1).sub.2;

(24) (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.2Si(I).sub.2;

(25) ((CH.sub.3).sub.2CH).sub.2Si(I).sub.2;

(26) (CH.sub.3CH.sub.2(CH.sub.3)CH).sub.2Si(I).sub.2;

(27) ((CH.sub.3).sub.3C).sub.2Si(I).sub.2;

(28) (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.2Si(I).sub.2;

(29) ((CH.sub.3).sub.3CCH.sub.2).sub.2Si(I).sub.2;

(30) (CH.sub.2═CH).sub.2Si(I).sub.2;

(31) (CH≡C).sub.2Si(I).sub.2;

(32) (CH≡CCH.sub.2).sub.2Si(I).sub.2;

(33) (CH.sub.3C≡C).sub.2Si(I).sub.2;

(34) (CH≡CCH.sub.2CH.sub.2).sub.2Si(I).sub.2;

(35) (CH.sub.3CH≡CCH.sub.2).sub.2Si(I).sub.2;

(36) (CH.sub.2CH.sub.2CH.sub.2CEC).sub.2Si(I).sub.2;

(37) (CH.sub.3).sub.3SiI;

(38) (CH.sub.3CH.sub.2).sub.3SiI;

(39) (CH.sub.3CH.sub.2CH.sub.2).sub.3SiI;

(40) (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.3SiI;

(41) ((CH.sub.3).sub.2CH).sub.3SiI;

(42) (CH.sub.3CH.sub.2(CH.sub.3)CH).sub.3SiI;

(43) ((CH.sub.3).sub.3C).sub.3SiI;

(44) (CH.sub.3CH.sub.2CH.sub.2CH.sub.2).sub.3SiI;

(45) ((CH.sub.3).sub.3CCH.sub.2).sub.3SiI;

(46) (CH.sub.2═CH).sub.3SiI;

(47) (CH≡C).sub.3SiI;

(48) (CH≡CCH.sub.2).sub.3SiI;

(49) (CH.sub.3C≡C).sub.3SiI;

(50) (CH≡CCH.sub.2CH.sub.2).sub.3SiI;

(51) (CH.sub.3CH≡CCH.sub.2).sub.3SiI; and

(52) (CH.sub.2CH.sub.2CH.sub.2C≡C).sub.3SiI.

(53) In this process, commercially available lithium iodide powder may be utilized as is or with further milling to provide a powder of lithium iodide which has, in certain embodiments, a particle size diameter of less than 1, less than 0.5, or less than 0.1 mm.

(54) The tertiary amines may be mono-amines or polyamines. The tertiary amines can be of any structure and possess other functional groups, provided that said groups do not interfere in the displacement reaction of the invention; in this regard, such tertiary amines should not possess imine moieties. In the case of mono-amines, examples include compounds of the formula (R*).sub.3N, wherein each R* is independently chosen from C.sub.1-C.sub.6 alkyl groups. Examples include trimethylamine, triethylamine, tri-(n-propyl)amine, tri-(isopropyl)amine, tri-(n-butyl)amine, and the like. Polyamine compounds are generally alkylamines having two or more amine functional groups, separated by an alkylene linkage. In certain embodiments, the polyamine will have the following structure:

(55) ##STR00002##
wherein each R is independently hydrogen or a C.sub.1-C.sub.9 alkyl group, m is an integer of from 1 to 4, and n is an integer of from 2 to 5.

(56) In other embodiments, the tertiary amines have the formula

(57) ##STR00003##
wherein each R is independently hydrogen or a C.sub.1-C.sub.9 alkyl group. In other embodiments, the R group is independently chosen from methyl and ethyl.

(58) In certain embodiments, the process utilizes an aprotic non-polar solvent. Exemplary solvents include dichloromethane, chloroform, dichloroethane, carbon tetrachloride, pentane, hexane, cyclohexane, heptane, benzene, toluene, and the like.

(59) In certain embodiments, the process is conducted at ambient pressure and at temperatures of about 20° to 40° C. or 20° to 25° C.

(60) Upon suitable completion of the reaction, the crude product may be filtered through compatible filter media which can be composed of materials including glass, thermally activated diatomaceous earth, polypropylene, polyethylene, polytetrafluoroethylene (PTFE), perfluoroalkoxy alkanes (PFA), passivated stainless steel and nickel alloys thereof. The solvent separation from the filtrate can be accomplished by bulb-to-bulb distillation at a pressure ranging from 0.01 to 760 Torr and a temperature ranging from 20° C. to 110° C. Additional purification steps may include a short path vacuum distillation to separate the desired halosilane product from the mixed chloroiodosilane side products, the residual catalyst, and any catalyst-halosilane complexes formed in the course of the reaction, with the product purity from a short path distillation ranging from 95%-99%. Additional purification steps include the use of a fractional distillation under atmospheric pressure or vacuum conditions to achieve purities in excess of 99%.

(61) For ease of reference, “microelectronic device” includes semiconductor substrates, flat panel displays, phase change memory devices, solar panels, logic, DRAM, and 3D NAND devices, and other products including solar substrates, photovoltaics, and microelectromechanical systems (MEMS), manufactured for use in microelectronic, integrated circuit, or computer chip applications. Solar substrates include, but are not limited to, silicon, amorphous silicon, polycrystalline silicon, monocrystalline silicon, CdTe, copper indium selenide, copper indium sulfide, and gallium arsenide on gallium. The solar substrates may be doped or undoped. It is to be understood that the term “microelectronic device” is not meant to be limiting in any way and includes any substrate that will eventually become a microelectronic device or microelectronic assembly.

(62) The invention has been described in detail with particular reference to certain embodiments thereof, but it will be understood that variations and modifications can be affected within the spirit and scope of the invention.

Examples

(63) 1) Comparative Synthesis of Triiodosilane with and without TEEDA Catalyst (Lithium Iodide Powder, 5 Mol % N,N,N′,N′-Tetraethylethylenediamine, Dichloromethane)

(64) The following manipulations were performed in an inert atmosphere glovebox. Two 20 mL oven dried glass vials were equipped with PTFE coated magnetic stir fleas and charged with 4.93 g (36.9 mmol, 5 eq) lithium iodide powder (Merck, 99.9% trace metals, 99.1% Iodide by AgNO.sub.3 titration), followed by 10 mL anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 1.00 g (7.38 mmol) trichlorosilane resulting in a slurry of off-white solid suspended in a pinkish purple solution. To one of the vials was added 0.127 g N,N,N′,N′-Tetraethylethylenediamine (TEEDA) (3.69 mmol, 0.10 eq), and the reaction mixture immediately lost the pinkish-purple tinge and slowly turned pale yellow. Both vials were securely capped and stirred at ambient temperature while being periodically assayed by .sup.1H NMR to monitor the progress of the reaction. The following table shows the percent conversion over time for the reaction with TEEDA and without TEEDA. Both the reaction with and without TEEDA showed 10-15% of a decomposition product suspected to be a halogenated siloxane and varying amounts of species suspected to be mixed chloroiodosilanes. After 3 days, the reaction with the TEEDA catalyst was no longer monitored due to the disappearance of all the starting trichlorosilane and all but 2% of the putative chloroiodosilanes.

(65) TABLE-US-00001 % Conversion % HSiI.sub.3 % Conversion % HSiI.sub.3 Time (With (With (Without (Without (days) TEEDA) TEEDA) TEEDA) TEEDA) 3 100% 81%  77% 13% 12 NA NA  85% 45% 35 NA NA 100% 81%

(66) 2) Synthesis of Triiodosilane (Lithium Iodide Powder, 5 Mol % N,N,N′,N′-Tetraethylethylenediamine (TEEDA), Dichloromethane)

(67) The following manipulations were performed in an inert atmosphere glovebox. An oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 44.4 g (332 mmol, 4.5 eq) lithium iodide powder (Merck 99.9% trace metals basis, 99.1% Iodide by AgNO.sub.3 titration), followed by 50 mL anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 10.00 g trichlorosilane (73.8 mmol, 1 eq) resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.635 g N,N,N′,N′-Tetraethylethylenediamine (TEEDA) (3.69 mmol, 0.05 eq), immediately lost the pinkish-purple tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred for 78 hours at ambient temperature. The reaction mixture was assayed by .sup.1H NMR which indicated that all of the trichlorosilane had been consumed with the triiodosilane accounting for about 90% of the formed products. The reaction mixture was then allowed to stir for an additional 66 h and was assayed again by .sup.1H NMR which showed that the product distribution had not changed. The reaction mixture was then vacuum filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 80 mL of anhydrous pentane. The combined filtrates were transferred to an oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 15 torr) resulting in a yellow-green oil as the crude product. The crude product was vacuum distilled at 15 Torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. A forecut from 60° C. to 90° C. was discarded and the main fraction boiling at 103° C. was collected. The mass of the clear oil in the main fraction (98.4% by .sup.1H NMR) was 18.69 g *(60.5% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=3.91 (s, J=327.5 Hz). .sup.29Si{.sup.1H} NMR (C.sub.6D.sub.6): δ=−170.31.

(68) 3) Synthesis of Triiodosilane (Lithium Iodide Beads, 5 Mol % N,N,N′,N′-Tetraethylethylenediamine (TEEDA), Dichloromethane)*

(69) The following manipulations were performed in an inert atmosphere glovebox. An oven dried 1 L, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 222 g (1.66 mol, 4.5 eq) lithium iodide −10 mesh beads (Alfa Aesar, 99% trace metals basis), followed by 113 mL (150 g) anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 50.00 g trichlorosilane (369 mmol, 1 eq) resulting in a slurry of white beads suspended in a slightly pinkish solution. The reaction mixture was then treated with 3.17 g N,N,N′,N′-Tetraethylethylenediamine (TEEDA) (18.4 mmol, 0.05 eq), immediately lost the pinkish tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred at ambient temperature. The reaction mixture was periodically assayed by .sup.1H NMR and the percent conversion (based on trichlorosilane starting material) and % triiodosilane formed were monitored as shown in the table below. The reaction mixture was filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 300 mL of anhydrous pentane. The combined filtrates were transferred to an oven dried 500 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 15 Torr) resulting in a yellow-green oil with a large amount of residual solids as the crude product. The crude product was vacuum distilled at 15 torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. A forecut from 60° C. to 95° C. was discarded and the main fraction boiling at 99-100° C. was collected. The mass of the clear oil in the main fraction (96.2% by .sup.1H NMR) was 60.78 g *(38.6% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=3.91 (s, J=327.5 Hz). .sup.29Si{.sup.1H} NMR (C.sub.6D.sub.6): δ=−170.31.

(70) TABLE-US-00002 Time (days) % Conversion % HSiI.sub.3 1 86%  3% 7 86% 25% 17 90    52    36 97    72   

(71) 4) Synthesis of Triiodosilane (Lithium Iodide Powder, 5 Mol % N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA), Dichloromethane)

(72) The following manipulations were performed in an inert atmosphere glovebox. An oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 44.4 g (332 mmol, 4.5 eq) lithium iodide powder (Merck, 99.9% trace metals basis, 99.1% Iodide by AgNO.sub.3 titration), followed by 50 mL anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 10.00 g trichlorosilane (73.8 mmol, 1 eq) resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.639 g N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA), (3.69 mmol, 0.05 eq), immediately lost the pinkish-purple tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred at ambient temperature for a total of 74 hours. The reaction mixture was periodically assayed by .sup.1H NMR and the percent conversion (based on trichlorosilane starting material) and % triiodosilane formed were monitored. The reaction mixture was then vacuum filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 100 mL of anhydrous pentane. The combined filtrates were transferred to an oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 15 torr) resulting in a yellow-green oil as the crude product. The crude product was vacuum distilled at 14 Torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. A forecut from 60° C. to 95° C. was collected, massed (1.29 g), and assayed by .sup.1H NMR which indicated the presence of triiodosilane, a mixed chlor-iodosilane species, and several smaller impurity resonances. The triiodosilane accounted for 40-45% of the material present with the balance being impurities. The main fraction boiling at 95-96° C. was collected using a bath temp of 140-150° C. The mass of the clear, colorless oil in the main fraction (98.6% by .sup.1H NMR) was 23.28 g (75.8% yield). .sup.1H NMR (C.sub.6D.sub.6): 8=3.91 (s, J=327.5 Hz). .sup.29Si{.sup.1H} NMR (C.sub.6D.sub.6): 8=−170.31.

(73) TABLE-US-00003 Time (hours) % Conversion % HSiI.sub.3 4 86 52 68 96 89 74 96 90

(74) 5) Synthesis of Triiodosilane (Lithium Iodide Powder, 5 Mol % N,N,N′,N′-Tetraethylethylenediamine (TEEDA), Hexanes)

(75) The following manipulations were performed in an inert atmosphere glovebox. An oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 44.4 g (332 mmol, 4.5 eq) lithium iodide powder (Merck, 99.9% trace metals basis, 99.1% Iodide by AgNO.sub.3 titration), followed by 50 mL anhydrous hexanes resulting in an off-white slurry. To this slurry was added 10.00 g trichlorosilane (73.8 mmol, 1 eq) resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.635 g N,N,N′,N′-Tetraethylethylenediamine (TEEDA) (3.69 mmol, 0.05 eq), immediately lost the pinkish-purple tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred for a total of ? hours at ambient temperature. The reaction mixture was periodically assayed by .sup.1H NMR and the percent conversion (based on trichlorosilane starting material) and % triiodosilane formed were monitored. The reaction mixture was then vacuum filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 100 mL of anhydrous hexanes. The combined filtrates were transferred to an oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 15 torr) resulting in a yellow-green oil as the crude product. The crude product was vacuum distilled at 14-15 Torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. A forecut from 60° C. to 88° C. was discarded and the main fraction boiling at 99-100° C. was collected. The mass of the clear oil in the main fraction (96.8% by .sup.1H NMR) was 18.32 g (57.4% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=3.91 (s, J=327.5 Hz). .sup.29Si{.sup.1H} NMR (C.sub.6D.sub.6): δ=−170.31.

(76) TABLE-US-00004 Reaction Time Percent Percent Triiodosilane (hours) Conversion Formed 29 82 46 52 92 63 125 98 79 192 99 84

(77) 6) Synthesis of Triiodosilane (Lithium Iodide Powder, 5 Mol % N,N,N′,N′-Tetramethylethylenediamine (TMEDA), Dichloromethane)

(78) The following manipulations were performed in an inert atmosphere glovebox. An oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 45.2 g (338 mmol, 4.5 eq) lithium iodide powder (Merck, 99.9% trace metals basis, 99.1% Iodide by AgNO.sub.3 titration), followed by 50 mL anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 10.2 g trichlorosilane (75.3 mmol, 1 eq) resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.436 g N,N,N′,N′-Tetramethylethylenediamine (TMEDA) (3.76 mmol, 0.05 eq), immediately lost the pinkish-purple tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred for a total of 332 hours at ambient temperature. The reaction mixture was periodically assayed by H NMR and the percent conversion (based on trichlorosilane starting material) and % triiodosilane formed were monitored. The reaction mixture was then vacuum filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 100 mL of anhydrous pentanes. The combined filtrates were transferred to an oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 40 Torr) resulting in a slightly pink oil as the crude product. The crude product was vacuum distilled at 14-15 torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. A forecut from 50° C. to 98° C. was discarded and the main fraction boiling at 98-102° C. was collected. The mass of the clear oil in the main fraction (99.2% by .sup.1H NMR) was 17.81 g (57.1% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=3.91 (s, J=327.5 Hz). 29Si{1H} NMR (C.sub.6D.sub.6): δ=−170.31.

(79) TABLE-US-00005 Reaction Time Percent Percent Triiodosilane (hours) Conversion Formed 22 65 27 48 88 60 113 99 89 332 100 86.3

(80) 7) Synthesis of Diiodomethylsilane (Lithium Iodide Powder, 5 Mol % N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA), Dichloromethane)

(81) The following manipulations were performed in an inert atmosphere glovebox. A 20 mL oven dried glass vial was equipped with a PTFE coated magnetic stir flea and charged with 10.4 g (78.0 mmol, 3 eq) lithium iodide powder (Merck, 99.9% trace metals, 99.1% Iodide by AgNO.sub.3 titration), followed by 15 mL anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 3.00 g (26.0 mmol, 1 eq) dichloromethylsilane resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.225 g N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA) (1.3 mmol, 0.05 eq), and the reaction mixture immediately lost the pinkish-purple tinge and slowly turned pale yellow before eventually bleaching to a near colorless mixture. The vial was securely capped and stirred at ambient temperature while being periodically assayed by .sup.1H NMR to monitor the progress of the reaction. The following table shows the percent conversion over time for the reaction. After 144 hours of stirring, the reaction mixture showed no further changes in product distribution. The reaction mixture was filtered through a 1 cm bed of activated celite, washed with 40 mL of anhydrous pentane, and the filtrates stripped of volatiles under a 40 torr vacuum. The peach colored oil that resulted was assayed by .sup.1H NMR which indicated 95% purity with chloroiodomethylsilane being the dominant impurity. The mass of the product was 4.51 g (55.2% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=1.01 (d, J=3.01 Hz), 4.65 (q, J=3.01 Hz. 29Si{1H} NMR (C.sub.6D.sub.6): δ=−66.51

(82) TABLE-US-00006 Reaction Time Percent Percent Diiodomethylsilane (hours) Conversion Formed 4 63 27 78 89 89 144 92 92

(83) 8) Synthesis of Triiodosilane (Lithium Iodide Powder, 5 Mol % N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA), Toluene)

(84) The following manipulations were performed in an inert atmosphere glovebox. An oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 44.4 g (332 mmol, 4.5 eq) lithium iodide powder (Merck, 99.9% trace metals basis, 99.1% Iodide by AgNO.sub.3 titration), followed by 50 mL anhydrous toluene resulting in an off-white slurry. To this slurry was added 10.00 g trichlorosilane (73.8 mmol, 1 eq) resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.639 g N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA), (3.69 mmol, 0.05 eq), immediately lost the pinkish-purple tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred at ambient temperature for a total of 288 hours. The reaction mixture was periodically assayed by .sup.1H NMR and the percent conversion (based on trichlorosilane starting material) and % triiodosilane formed were monitored. The reaction was judged to be complete after 96 hours stirring. The reaction mixture was then vacuum filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 100 mL of anhydrous pentane. The combined filtrates were transferred to an oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 15 torr) resulting in a yellow-green oil as the crude product. The crude product was vacuum distilled at 15 Torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. The main fraction boiling at 98-102° C. was collected using a bath temp of 140-150° C. The mass of the clear, colorless oil in the main fraction (98.1% by .sup.1H NMR) was 17.33 g (56.2% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=3.91 (s, J=327.5 Hz). 29Si{.sup.1H} NMR (C.sub.6D.sub.6): δ=−170.31.

(85) TABLE-US-00007 Time (hours) % Conversion % HSiI.sub.3 3 62.2 28.5 48 94.5 65.9 72 98.7 82.0 288 100 94.7
1) Synthesis of Triiodosilane (Lithium Iodide Powder, 5 Mol % Triethylamine (TEA), DCM)
The following manipulations were performed in an inert atmosphere glovebox. An oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm was equipped with a PTFE coated stir egg and charged with 44.4 g (332 mmol, 4.5 eq) lithium iodide powder (Merck, 99.9% trace metals basis, 99.1% Iodide by AgNO.sub.3 titration), followed by 50 mL anhydrous dichloromethane resulting in an off-white slurry. To this slurry was added 10.00 g trichlorosilane (73.8 mmol, 1 eq) resulting in a slurry of off-white solid suspended in a pinkish purple solution. The reaction mixture was then treated with 0.373 g triethylamine (TEA), (3.69 mmol, 0.05 eq), immediately lost the pinkish-purple tinge and slowly turned pale yellow. The flask was sealed with a glass stopper and stirred at ambient temperature for a total of 24 hours. The reaction mixture was periodically assayed by .sup.1H NMR and the percent conversion (based on trichlorosilane starting material) and % triiodosilane formed were monitored. The reaction mixture was then vacuum filtered through a 1 cm celite bed in fritted funnel and the residual salts were washed with 100 mL of anhydrous pentane. The combined filtrates were transferred to an oven dried 250 mL, 1-neck round bottom flask with a gas/vacuum inlet sidearm and a PTFE stir egg. The filtrates were stripped of volatiles under reduced pressure (down to 15 torr) resulting in a yellow-green oil as the crude product. The crude product was vacuum distilled at 14 Torr using a short path distillation head and a stainless steel bead bath on a hotplate to heat the boiling pot. The main fraction boiling at 98-101° C. was collected using a bath temp of 140-150° C. The mass of the clear, colorless oil in the main fraction (95% by .sup.1H NMR) was 19.02 g (59.6% yield). .sup.1H NMR (C.sub.6D.sub.6): δ=3.91 (s, J=327.5 Hz). 29Si{1H} NMR (C.sub.6D.sub.6): δ=−170.31.

(86) TABLE-US-00008 Time (hours) % Conversion % HSiI.sub.3 2 96 94 24 96 93

(87) TABLE-US-00009 Reaction % Yield Time (After (Until no distillation, Halosilane further adjusted Substrate/ LiI increase in for Ex Scale Catalyst Solvent Form HSiI.sub.3) purity) 2 HSiCl.sub.3/10 g TEEDA DCM Powder  78 h 60.5 3 HSiCl.sub.3/50 g TEEDA DCM Bead  35 d 38.6 4 HSiCl.sub.3/10 g PMDETA DCM Powder  74 h 75.8 5 HSiCl.sub.3/10 g TEEDA Hexanes Powder 192 h 57.4 6 HSiCl.sub.3/10 g TMEDA DCM Powder 113   57.1 7 MeSiCl.sub.2H/ PMDETA DCM Powder 144   55.2 3 g 8 HSiCl.sub.3/10 g PMDETA Toluene Powder 96 (Est) 56.2 9 HSiCl.sub.3/10 g TEA DCM Powder  2 59.6