METHOD FOR PREPARING MICROSTRUCTURE ON SURFACE OF GLASS BY TITANIUM OXIDE NANOPARTICLE-ASSISTED INFRARED NANOSECOND LASER

Abstract

A method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser, including the following steps: (1) dropwise applying a titanium oxide nanoparticle hydrogel onto the surface of a glass sample; (2) pressing another piece of glass on the surface of the hydrogel, so the hydrogel is evenly distributed between the two pieces of glass, and allowing the two pieces of glass to stand horizontally for a period of time to air-dry the hydrogel; (3) separating the two pieces of glass to obtain a glass with a uniform titanium oxide nanoparticle coating; (4) forming a microstructure using an infrared nanosecond laser with a wavelength of 1064 nm; and (5) performing after-treatment, including ultrasonically cleaning the sample with acetone, absolute ethanol and deionized water respectively for 10 min to remove titanium oxide nanoparticles attached to the surface, to obtain a glass sample with the microstructure.

Claims

1. A method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser, comprising: dropwise applying a titanium oxide nanoparticle hydrogel onto the surface of a glass sample; then pressing another piece of glass on the surface of the titanium oxide nanoparticle hydrogel, so that the titanium oxide nanoparticle hydrogel is evenly distributed between the two pieces of glass, and allowing the two pieces of glass to stand horizontally until the titanium oxide nanoparticle hydrogel is solidified; separating the two pieces of glass to obtain a glass with a uniform titanium oxide nanoparticle coating; forming a microstructure using laser; and performing after-treatment to obtain a glass sample with the microstructure.

2. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 1, wherein the glass is quartz glass.

3. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 1, wherein the laser is infrared nanosecond laser.

4. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 3, wherein the wavelength of the infrared nanosecond laser is 1064 nm, and laser processing parameters comprise an average laser power of 2 W-10 W, a pulse frequency of 20-200 kHz, and a scanning speed of 1000-2000 mm/min.

5. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 1, wherein the volume of the titanium oxide nanoparticle hydrogel per unit area is 0.1-0.2 μL/mm.sup.2.

6. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 1, wherein the concentration of the titanium oxide nanoparticle hydrogel is 35-40%.

7. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 1, wherein the horizontal standing time is 5-10 min.

8. The method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser according to claim 1, wherein specific steps of the after-treatment are: ultrasonically cleaning the glass sample with acetone, absolute ethanol and deionized water respectively to remove titanium oxide nanoparticles attached to the surface.

9. A glass sample having a microstructure prepared by the method according to claim 1.

10. Application of the glass sample having a microstructure according to claim 9 in the field of biomedicine or aerospace.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0025] The accompanying drawings constituting a part of this application are used for providing further understanding for this application. Exemplary embodiments of this application and descriptions thereof are used for explaining this application and do not constitute any inappropriate limitation to this application.

[0026] FIG. 1 is a schematic diagram of the method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser of Embodiment 1 of the present invention.

[0027] FIG. 2 is a glass microstructure processed by the preparation method of Embodiment 1 of the present invention.

[0028] FIG. 3 is a glass microfluidic channel processed by the preparation method of Embodiment 1 of the present invention.

[0029] FIG. 4 is a partial morphology of the glass microfluidic channel processed by the preparation method of Embodiment 1 of the present invention.

[0030] 1. 40 mm×20 mm quartz glass sample 1; 2. 35% titanium oxide nanoparticle hydrogel in mass fraction; 3. Pipette; 4. 40 mm×20 mm quartz glass sample 2; 5. Infrared nanosecond laser pulse; and 6. Focusing mirror used by laser.

DETAILED DESCRIPTION

[0031] It should be noted that, the following detailed descriptions are exemplary, and are intended to provide a further description to this application. Unless otherwise specified, all technical and scientific terms used herein have the same meaning as commonly understood by those of ordinary skill in the art to which this application belongs.

[0032] It should be noted that terms used herein are only for the purpose of describing specific implementations and are not intended to limit the exemplary implementations of this application. As used herein, the singular form is intended to include the plural form, unless the context clearly indicates otherwise. In addition, it should further be understood that terms “comprise” and/or “include” used in this specification indicate that there are features, steps, operations, devices, components, and/or combinations thereof.

[0033] As described in the related art section, in view of the problems that the current commonly used excimer lasers in glass processing have low processing efficiency and high cost, quartz glass has a very low absorption rate for the 1064 nm infrared nanosecond laser, and material removal cannot be realized, the present invention provides a method for preparing a microstructure on the surface of glass by titanium oxide nanoparticle-assisted infrared nanosecond laser, comprising the following steps:

[0034] step (1): dropwise applying a titanium oxide nanoparticle hydrogel onto the surface of a glass sample;

[0035] step (2): pressing another piece of glass on the surface of the hydrogel, so that the hydrogel is evenly distributed between the two pieces of glass, and then allowing the two pieces of glass to stand horizontally for a period of time until the titanium oxide nanoparticle hydrogel is air-dried;

[0036] step (3): separating the two pieces of glass to obtain a glass with a uniform titanium oxide nanoparticle coating;

[0037] step (4): forming a microstructure using an infrared nanosecond laser with a wavelength of 1064 nm; and

[0038] step (5): performing after-treatment, specifically, ultrasonically cleaning the sample obtained in step 3 with acetone, absolute ethanol and deionized water respectively for 10 min to remove titanium oxide nanoparticles attached to the surface, and obtain a glass sample with the microstructure.

[0039] Preferably, the volume of the 35% titanium oxide nanoparticle hydrogel used on a 40 mm×20 mm glass sheet in step (1) is 30 μL, and the volume of the titanium oxide nanoparticle hydrogel per unit area of the glass surface is 0.1-0.2 μL/mm.sup.2.

[0040] Preferably, the standing time in step (2) is 5 min.

[0041] The present invention will be further described in detail below in conjunction with specific embodiments. It should be pointed out that the specific embodiments are for explaining rather than limiting the present invention.

Embodiment 1

[0042] step (1): Referring to step 1 in FIG. 1, 30 μL of titanium oxide nanoparticle hydrogel (Alfa Aesar, Titanium (IV) oxide https://www.alfa.com/en/catalog/044517/) with the mass fraction of 35% was dropwise applied to a 40 mm×20 mm glass sample surface, where the volume of the titanium oxide nanoparticle hydrogel per unit area of the glass surface is 0.18 μL/mm.sup.2;

[0043] step (2): Referring to step 2 in FIG. 1, another piece of 40 mm×20 mm glass was pressed on the surface of the hydrogel, so that the hydrogel was evenly distributed between the two pieces of glass, and then the two pieces of glass were allowed to stand horizontally for 5 min to air-dry the titanium oxide nanoparticle hydrogel;

[0044] step (3): Referring to step 3 in FIG. 1, the two pieces of glass were separated to obtain a glass with a uniform titanium oxide nanoparticle coating;

[0045] step (4): Referring to step 4 in FIG. 1, a microstructure was processed using an infrared nanosecond laser with a wavelength of 1064 nm, where the parameters of laser ablation are that the average laser power is 5 W, the pulse frequency is 100 kHz, and the scanning speed is 2000 mm/min; and

[0046] step (5): After-treatment was performed, specifically, the sample obtained in step 3 was ultrasonically cleaned with acetone, absolute ethanol and deionized water respectively for 10 min to remove titanium oxide nanoparticles attached to the surface, and obtain a glass sample with the microstructure. FIG. 2 is a three-dimensional morphology of the final processed microgrooves, FIG. 3 is an overall picture of the final processed microfluidic channels, and FIG. 4 is a partial morphology of the microfluidic channels.

[0047] It can be seen from FIGS. 2 and 4 that there are no cracks on the surfaces of the microgrooves and microfluidic channels, and the processing effect is good.

[0048] It should be finally noted that, the foregoing descriptions are merely preferred embodiments of the present invention, but are not intended to limit the present invention. Although the present invention is described in detail with reference to the foregoing embodiments, a person skilled in the art should understand that they may still make modifications to the technical solutions described in the foregoing embodiments or make equivalent replacements to some technical features thereof. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention shall fall within the protection scope of the present invention. The specific implementations of the present invention are described above with reference to the accompanying drawings, but are not intended to limit the protection scope of the present invention. Those skilled in the art should understand that various modifications or deformations may be made without creative efforts based on the technical solutions of the present invention, and such modifications or deformations shall fall within the protection scope of the present invention.