RESURFACING CUP FOR ACETABULUM HEMIARTHROPLASTY OF THE HIP JOINT

Abstract

The present invention disclosed resolves the main problems of bone-sparing hip resurfacing surgery by using only an acetabular component in which the femoral head articulates, being only shaved to a spherical shape and cleared of osteophytes that could impinge on the acetabulum and so restrict the range of motion. The inner surface of the resurfacing cup is aspherical in shape creating an annular contact with the femoral head. The inner, articulating surface of the cup (10) is ADLC or pyrolytic carbon coated to reduce friction and wear of the femoral head. The surgical approach is well developed with surgery time significantly reduced by avoiding the use of the femoral resurfacing component. The cup is preferably of the double¬shell type for cementless fixation, but it can also be made as a single shell for cementless or cemented fixation. Should a revision surgery due to wear of the femoral head become necessary, the cup can be retained and combined with a dual mobility femoral component.

Claims

1. An acetabular resurfacing cup 10 for hemiarthroplasty of the hip joint.

2. An acetabular resurfacing cup 10 of claim 1, wherein the shape of the inner surface facing the femoral head 201, is of aspherical shape.

3. An acetabular resurfacing cup 10 of claim 2, wherein there is an annular section 17 of the inner surface which is of spherical shape.

4. An acetabular resurfacing cup 10 of claim 3, wherein the angle 18 covered by the annular spherical section 17 is in the range of 10 to 20 degrees.

5. An acetabular resurfacing cup 10 of claim 3, wherein the angle 19 from the axis of symmetry 20 to the annular spherical section 17 is in the range of 30 to 45 degrees.

6. An acetabular resurfacing cup 10 of, claim 3 wherein the axis of symmetry 23 of the inner shape of the cup is offset from the main axis of symmetry 20 of the cup by an angle 24 in the range of 15 to 25 degrees.

7. An acetabular resurfacing cup 10 of claim 1, wherein the inner surface of the cup facing the femoral head is coated by a carbon-based material such as ADLC and/or pyrolytic carbon.

8. An acetabular resurfacing cup 10 of, claim 1 adapted for cementless fixation.

9. An acetabular resurfacing cup 10 of claim 8, adapted for cementless fixation which is a double shell construct 11/12.

10. An acetabular resurfacing cup 10 of claim 8, adapted for cementless fixation which is a single shell construct 25.

11. An acetabular resurfacing cup 10 of, claim 1 adapted for cemented fixation.

12. A hip prosthesis consisting of an acetabular resurfacing cup according to claim 1.

13. A femoral head shaver 27 for preparing a femoral head for articulation, particularly for articulation inside an acetabular resurfacing cup 10 of claim 1.

14. A combination of an acetabular resurfacing cup 10 of claim 1 and an artificial femoral component.

15. The combination according to claim 14, wherein said artificial femoral component is a femoral head adapted for dual mobility revision total hip replacement 30/31/33.

Description

LIST OF FIGURES

[0027] FIG. 1 shows a hip replacement total-prosthesis according to the state of the art.

[0028] FIG. 2 shows a hip replacement hemi-prosthesis according to the state of the art.

[0029] FIG. 3 shows a resurfacing hip replacement prosthesis according to the state of the art.

[0030] FIG. 4 shows a hemi replacement prosthesis of the hip joint according to the invention.

[0031] FIG. 5 shows a double shell acetabular hemi hip replacement prosthesis according to the invention.

[0032] FIG. 6 shows a single shell acetabular hemi replacement prosthesis according to the invention.

[0033] FIG. 7 shows a femoral head shaving instrument according to the invention.

[0034] FIG. 8 shows a revision surgery with a dual mobility femoral head component.

DETAILED DESCRIPTION

[0035] A state of the art total hip replacement prosthesis, FIG. 1, comprises an acetabulum cup 1 fixed to the pelvis 100, a femoral stem 2 fixed to the femur 200 with the femoral head 3 attached to the stem 2. A typical configuration today has a polymeric cup inlay, most commonly from a cross-linked UHMWPE, backed by a metal shell with a porous coating facing the bone. The stem for cementless fixation may be coated with a porous layer too, or alternatively rough-blasted with a thin coating of, for example, hydroxyapatite. The head can be metallic or ceramic. In an alternative to cementless fixation, both the cup and the stem can be cemented into respective bones using so-called bone cement, a two-component poly-methyl-methacrylate.

[0036] A state of the art hemi hip replacement prosthesis, FIG. 2, comprises only a femoral component. A femoral stem 4 is fixed to the femur 200. A large diameter femoral head 5 is fitted to the stem 4 either directly, or via a smaller head to form a bi-polar hem i-prosthesis.

[0037] A Birmingham-type resurfacing total hip prosthesis, FIG. 3, comprises a femoral component 6 with a large diameter head, usually cemented to cap the femoral head, reamed down to accommodate the prosthetic head and the centering pin 7 with some space allowed to be filled with bone cement 8. The acetabular component 9 is usually of cementless type, hammered into the reamed acetabulum 100.

[0038] A hip replacement hemi-prosthesis according to this invention, shown in FIG. 4, spares most of the femur 200 and relies on only an acetabulum resurfacing cup 10, fixed into the pelvis 100. The size of the cup 10 is selected to fit over the native femoral head 201, which is reamed into a spherical shape by removing as little cartilage and bone as possible to create a spherical shape, removing all gross deformities in form of osteophytes which tend to form at the neck of the femur. The cup is preferably of cementless type, but it could also be cemented into the reamed-out acetabulum.

[0039] A double shell acetabular cup according to the invention, shown in FIG. 5a, comprises an outer shell 11 and an inner shell 12. A double shell acetabular cup for a total hip replacement is disclosed in U.S. Pat. No. 7,776,097 by Tepic and Malchau. The cup may comprise perforations 13 in the outer shell to allow for a rapid invasion by bone. The outside, bone-facing surface of the shell 11, may be coated by porous material such as titanium and hydroxyapatite 14 thereby providing additional micro fixation. The press-fit stability of the cup in the reamed-out acetabulum may be enhanced by small extensions such as ribs 15 in the outer shell close to the opening of the cup. The inner shell 12 may be fitted, e.g. snap-press fitted into the outer shell 11 at the opening of the cup leaving a small gap 16 between the shells. The size of the gap is usually about 0.5 to about 1.5 mm.

[0040] This combination results in a highly compliant metal construct for integration into the pelvic bone without stress shielding observed when thick, stiff metal backing is used for conventional total hip cups. Preferably, the inner shell of the cup is from harder and/or stronger material than the outer shell. In certain embodiments, the tensile strength of the metal forming the outer shell is about 300 to about 600 MPa, preferably from about 350 MPa to about 550 MPa and/or the hardness on the Vickers scale (Hv) of the metal forming the outer shell is about 100 to about 250 Hv, preferably from about 120 to about 200 Hv. In certain embodiments, the tensile strength of the metal forming the inner shell is about 700 to about 1,000 MPa, preferably about 800 to about 950 MPa, more preferably about 900 MPa, and/or the hardness on the Vickers scale (Hv) of the metal forming the inner shell is about 280 to about 450 Hv, preferably about 300 to about 400 Hv, more preferably about 350 Hv.

[0041] Preferred metals for the shells are titanium and titanium alloys. For example, the outer shell could be produced from a commercially pure (c.p.) titanium grade 2, or preferably grade 4. Alternatively, a titanium-aluminum-niobium alloy can be used for its higher strength but also superb biocompatibility. The inner shell needs to be stronger and harder than is possible with c.p. grades of titanium, so an alloy like titanium-aluminum-niobium (Ti6Al7Nb) and/or possibly titanium-aluminum-vanadium (Ti6Al4V) are preferred choices. Titanium c.p. grades' tensile strength is in the range of 350 to 550 MPa; hardness in the range of 120 to 200 on the Vickers scale (Hv). Corresponding values for the Ti6Al7Nb and Ti6Al4V alloys are 900 MPa and 350 Hv.

[0042] The inner shell is of aspherical shape, providing the general advantages presented in the U.S. Pat. No. 8,323,346 by Tepic. The inner surface 17, over an annular band covering an angle 18 of 5 to 30 degrees, more preferably 10 to 20 degrees is spherical in shape. It is offset from axis 20 by an angle 19 of 25 to 50 degrees, more preferably 30 to 45 degrees. The section of the cup between the band 17 and the pole is shaped so as to create a gap 21 with respect to the spherical shape of the annulus 17. From section 17 out towards the opening of the cup, the shape of the inner shell is also deviating from a sphere creating a gap 22. The aspherical shape of the inner surface of the cup aids in lubrication and lowers the friction and wear of the articulation.

[0043] To further reduce friction and wear of the femoral head articulating in the replacement cup, the inner surface of the inner shell is coated by a suitable material, e.g. by ADLC or by pyrolytic carbon.

[0044] For the optimal function of the aspherical articulation the axis of symmetry of the inner surface shape 23, should be offset with respect to the axis of symmetry 20 of the whole cup as shown in FIG. 5b. The angle 24 of 5 to 30 degrees, more preferably of 15 to 25 degrees would bring the axis 23 into the middle of the range of the joint force in gait. When implanting into the pelvis the offset 24 should be placed in the superior direction of the pelvis.

[0045] An alternative make-up of the acetabular cup for hemi hip replacement is shown in FIG. 6. A single shell 25 with an inner shape as disclosed for the cup of FIG. 5 is either coated on the outside by a porous layer 26 for cementless bony ingrowth, or is adapted for cemented fixation into a reamed-out acetabulum in which case the outer surface is usually only textured or provided by other such means for improved interface to the bone cement. Cups of this type may be produced by either conventional machining or additive manufacturing. Preferred metals for cementless fixation are titanium alloys. For cemented type cup, cobalt-chromium alloys can also be used and the choice here can also be expanded to some stainless steels suitable for ADLC coating.

[0046] An instrument 27 to shave the femoral head into a spherical shape is shown on FIG. 7. It should be used with caution and preferably only by hand. The reamer 27 covers about a hemisphere, i.e. the inner surface of the reamer over about 180 degrees included angle is covered by cutting flutes 28. Openings 29 in the reamer allow for bone chips to be removed during and after reaming of the femoral head.

[0047] If a revision surgery would become necessary, the cup 10 of the present invention as described above can be retained and only a femoral component can be inserted, FIG. 8. The primary head 31 seated on the femoral neck 32 of the stem 30, is snap-fitted with a secondary head 33, made out of a polymer, such as UHMWPE or poly-ether-ether-ketone (PEEK). This secondary head can now be articulated inside the cup 10.

[0048] A partial hip without the cup disclosed in patent application US 2013/0060345A by Tepic, has been used in hundreds of dogs for over 8 years without any indication of the heads penetrating into the pelvis. In some cases, the dogs revert to full function of the hip in a matter of weeks albeit somewhat slower than with a total hip replacement. In other cases, recovery has been slower, taking several months to reach a steady state. It is unclear at this time what might slow down the recovery, but it safe to say that this is tied to the process of bone remodeling around the joint. As the reaming of the acetabulum is always done to the maximum depth without penetrating the medial wall of the acetabulum, the bone exposed to the articulation will vary a lot—from a dense subchondral bone to a soft cancellous bone and possibly some remnants of the cartilage covered areas.

[0049] In the procedure disclosed in this invention, the reaming of the femoral head will be less aggressive and in many cases, the bone just under the articulating surface is dense and sclerotic, possibly devoid of any pain receptors. This should cut the recovery time in addition to cutting the time of surgery and hence contribute to an increase of the all-important benefit-to-cost ratio.