A CRYSTALLINE, TWO DIMENSIONAL POLYMERS AND A PROCESS FOR THE PREPARATION THEREOF

Abstract

The present invention relates to a crystalline, two dimensional polymer of Formula I and a process for the preparation thereof.

##STR00001##

Claims

1. A crystalline, two dimensional polymer of Formula (I), ##STR00025## wherein R.sub.1 to R6 are same or different and independently selected from hydrogen, alkyl, substituted or unsubstituted alkyl, substituted or unsubstituted aryl, hetroalkyl or heteroaryl; wherein n is the number of repeating units of the polymer and n is in the range of 3 to 6 but not 4; and wherein Ar is an aromatic ring.

2. The polymer of formula (I) as claimed in claim 1, wherein said R.sub.1 to R6 are same or different and independently selected from hydrogen, ##STR00026## and wherein Ar is selected from ##STR00027##

3. The polymer of formula (I) as claimed in claim 1, wherein said polymer is selected from BIP-1, BIP-2 or BIP-3; having formula as: ##STR00028## ##STR00029##

4. A process for preparation of the crystalline, two dimensional polymers of Formula (I) comprising: a) adding halogen to pyrene in a solvent at a temperature ranging from 25° C. to 30° C. to obtain a reaction mixture followed by stirring the reaction mixture at a temperature in the range of 100 to 150° C. for a time period in the range of 2 to 5 hours to obtain 1,3,6,8-tetrahalopyrene; b) charging a mixture of boronic acid, 1,3,6,8-tetrahalopyrene of step (a), palladium catalyst and a base in a solvent at a temperature in the range of 100 to 150° C. for a time period in the range of 60 to 80 hours to obtain 1,3,6,8-tetrakis(4-(methoxycarbonyl)phenyl)pyrene; c) heating a mixture of 1,3,6,8-tetrakis(4-(methoxycarbonyl)phenyl)pyrene of step (b) and a base in a solvent at a temperature in the range of 60 to 80° C. for a time period in the range of 8 to 10 hours followed by drying the solvent to obtain a residue; d) adding water into the residue of step (c) followed by stirring at a temperature in the range of 25° C. to 30° C. for a time period in the range of 1 to 3 hours and adjusting pH in the range of 1 to 2 to obtain 1,3,6,8-tetrakis (p-benzoic acid) pyrene; and e) charging a mixture of 1,3,6,8-tetrakis(p-benzoic acid) pyrene of step (d), 1,2,4,5-benzenetetramine tetrahydrochloride and a catalyst in a solvent at a temperature in the range of 120° C. to 160° C. for a time period in the range of 45 to 48 hours to obtain a solution and continuing stirring at a temperature in the range of 180° C. to 200° C. for a time period in the range of 45 to 48 hours followed by adjusting pH of the solution to 8-9 to obtain the polymer; wherein the polymer is a Benzimidazole-linked two dimensional polymer.

5. The process as claimed in claim 4, wherein said halogen of step (a) is selected from bromine, chlorine or iodine and said solvent of step (a) is selected from nitrobenzene, toluene or dimethyl formamide.

6. The process as claimed in claim 4, wherein said boronic acid of step (b) is selected from 4-(methoxycarbonyl)phenyl)boronic acid or 4-Methoxycarbonylphenylboronic acid pinacol ester.

7. The process as claimed in claim 4, wherein said palladium catalyst of step (b) is selected from tetrakis(triphenylphosphine) palladium or Palladium(II) acetate; said solvent of step (b) is selected from dioxane, tetrahydrofuran or toluene; and said base of step (b) is selected from potassium tribasic phosphate, potassium carbonate, potassium acetate or sodium carbonate.

8. The process as claimed in claim 4, wherein said base of step (c) is selected from sodium hydroxide, potassium hydroxide or lithium hydroxide and the solvent of step (c) is selected from tetrahydrofuran, dioxane, water or mixture thereof.

9. The process as claimed in claim 4, wherein said solvent of step (e) is selected from polyphosphoric acid; dioxane, tetrahydrofuran, toluene or a mixture thereof and the catalyst of step (e) is polyphosphoric acid.

10. A device comprising the two dimensional polymer of Formula (I), wherein said polymer of formula (I) is selected from BIP-1, BIP-2 or BIP-3.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] FIG. 1: A) Before polymerization of BIP-1; B) After polymerization of BIP-1; C) Isolated yield; D) BIP-1 pellet

[0017] FIG. 2: Comparison of UV-Visible absorption spectra of 1, model derivatives 3, 4, and BIP-1 oligomers

[0018] FIG. 3: TEM images of BIP-1 showing layered nature of 2D-sheets

[0019] FIG. 4: SEM images of 2D-polymer showing the sheet morphology of the BIP-1, drop casted from MeOH suspension

[0020] FIG. 5: Comparison of PXRD patterns of BIP-1 experimental (dotted) and simulated pattern for an AA stacking mode (solid)

[0021] FIG. 6: a) BET N.sub.2 sorption isotherm curves and b) pore-size distribution profile of BIP-1 measured at 77 K

[0022] FIG. 7: PXRD pattern for BILP (H. M. El-Kaderi et al. J. Mater. Chem., 2012, 22, 25409-25417) sample reproduced, indicating amorphous materials.

[0023] FIG. 8: Proton conductivity measurements carried out for BIP-1 (in compacted pellet of the powdered sample), using quasi-four-probe AC impedance measurements a) under different relative humidity at 95° C.; b) different temperature at 95% relative humidity humidified conditions in a home-made setup.

[0024] FIG. 9: a) Photograph of BIP-2 isolated solid, b-d) Photograph of BIP-2 polymerization image, e) high-angle annular dark-field (HAADF) image, TEM elemental mapping images of BIP-2 elemental mapping for f) C-K g) N-K h) TEM image of BIP-2 layered sheets i) Selected area diffraction measurements of BIP-2; j) SEM image of BIP-2 layered sheets; k) MALDI-TOF MS of model derivative of BIP-2 polymer.

[0025] FIG. 10: a) BET N.sub.2 sorption isotherm curves of BIP-2 measured at 77 K; b) Pore-size distribution profile of BIP-2

[0026] FIG. 11: TEM images of BIP-2

[0027] FIG. 12: SEM images of BIP-2

[0028] FIG. 13: TEM image of BIP-3

[0029] FIG. 14: The fuel cell life test of the BIP-1 membrane is performed at open-circuit voltage condition

DETAILED DESCRIPTION OF THE INVENTION

[0030] The invention will now be described in detail in connection with certain preferred and optional embodiments, so that various aspects thereof may be more fully understood and appreciated.

[0031] The present invention provides a crystalline, two dimensional polymer of Formula I and a process for the preparation thereof.

[0032] In an embodiment, the present invention provides a crystalline, two dimensional polymer of Formula I;

##STR00003##

wherein R.sub.1 to R.sub.6 are same or different and independently selected from hydrogen, alkyl, substituted or unsubstituted alkyl, substituted or unsubstituted aryl, heteroalkyl or heteroaryl;
wherein n is the number of repeating units of the polymer and n is in the range of 3 to 6 but not 4; and
wherein Ar is an aromatic ring.

[0033] In preferred embodiment, the present invention provides a crystalline, two dimensional polymer of Formula (I),

##STR00004##

wherein R.sub.1 to R.sub.6 are same or different and independently selected from hydrogen,

##STR00005##

wherein Ar is selected from

##STR00006##

n is the number of repeating units of the polymer.

[0034] The crystalline, two dimensional polymer of Formula (I) is selected from BIP-1, BIP-2 or BIP-3; having formula as:

##STR00007## ##STR00008##

[0035] In another embodiment, the present invention provides a crystalline, two dimensional polymer of Formula I, wherein n is the number of benzimidazole units in the polymer, and n is 3-6, but not 4, wherein the proton conductivity of the polymers is in the range of 10.sup.−2 to 10.sup.−4.

[0036] In still another embodiment, the present invention provides the crystalline, two dimensional polymers of formula (I) wherein n represents number of benzimidazole units, where n is 3-6 but not 4.

[0037] The crystalline, two dimensional polymers of Formula (I) is selected from BIP-1, BIP-2 or BIP-3.

[0038] Imidazole covalently linked in the crystalline 2D-polymer backbone nullifies the stability and durability issues of the doping approach. The 2D-polymer structure exhibits ultrahigh proton conductivity in the pristine form without any additional dopants such as imidazole, phosphoric acid. The crystalline, two dimensional polymers of Formula (I) are used in fuel cell, quasi-four-probe AC impedance measurements to find out the proton conductivity value.

[0039] In yet another embodiment, the present invention provides a process for the preparation of the crystalline, two dimensional polymers of Formula (I) comprising the steps of: [0040] a) adding halogen to pyrene in a solvent at a temperature ranging from 25° C. to 30° C. to obtain a reaction mixture followed by stirring the reaction mixture at a temperature in the range of 100 to 150° C. for a time period in the range of 2 to 5 hours to obtain 1,3,6,8-tetrahalopyrene; [0041] b) charging a mixture of boronic acid, 1,3,6,8-tetrahalopyrene of step (a), palladium catalyst, and a base in a solvent at a temperature in the range of 100 to 150° C. for a time period in the range of 60 to 80 hours to obtain 1,3,6,8-tetrakis(4-(methoxycarbonyl)phenyl)pyrene; [0042] c) heating a mixture of 1,3,6,8-tetrakis(4-(methoxycarbonyl)phenyl)pyrene of step (b) and a base in a solvent at a temperature in the range of 60 to 80° C. for a time period in the range of 8 to 10 hours followed by drying the solvent to obtain a residue; [0043] d) adding water into the residue of step (c) followed by stirring at a temperature in the range of 25° C. to 30° C. for a time period in the range of 1 to 3 hours and adjusting pH in the range of 1 to 2 to obtain 1,3,6,8-tetrakis (p-benzoic acid) pyrene; and [0044] e) charging a mixture of 1,3,6,8-tetrakis(p-benzoic acid) pyrene of step (d), 1,2,4,5-benzenetetramine tetrahydrochloride and a catalyst in a solvent at a temperature in the range of 120° C. to 160° C. for a time period in the range of 45 to 48 hours to obtain a solution and continuing stirring at a temperature in the range of 180° C. to 200° C. for a time period in the range of 45 to 48 hours followed by adjusting pH of the solution to 8-9 to obtain the polymer;
wherein the polymer is a Benzimidazole-linked two dimensional polymer.

[0045] The halogen of step (a) is selected from bromine, chlorine or iodine.

[0046] The solvent of step (a) is selected from nitrobenzene, toluene or dimethyl formamide.

[0047] The boronic acid of step (b) is selected from 4-(methoxycarbonyl)phenyl)boronic acid or 4-Methoxycarbonylphenyl)boronic acid pinacol ester.

[0048] The palladium catalyst of step (b) is selected from tetrakis(triphenylphosphine) palladium or Palladium (II) acetate (Pd(OAc).sub.2).

[0049] The solvent of step (b) is selected from dioxane, tetrahydrofuran or toluene.

[0050] The base of step (b) is selected from potassium tribasic phosphate, potassium carbonate, potassium acetate or sodium carbonate.

[0051] The base of step (c) is selected from sodium hydroxide (NaOH), potassium hydroxide or lithium hydroxide.

[0052] The solvent of step (c) is selected from tetrahydrofuran, dioxane, water or a mixture thereof, preferably the solvent is THF/water (ratio 1:1) mixture or dioxane:water (1:1).

[0053] The solvent of step (e) is selected from polyphosphoric acid; dioxane, tetrahydrofuran, toluene or a mixture thereof.

[0054] The catalyst of step (e) is polyphosphoric acid.

[0055] In a preferred embodiment, the present invention provides a process for the preparation of BIP-1 as shown in Scheme 1.

##STR00009## ##STR00010## ##STR00011##

[0056] The present invention also provides a process for preparation of 1,4-bis (1H-benzo[d]imidazol-2-yl) benzene (3) comprising charging terephthalic acid, o-phenylenediamine, polyphosphoric acid (PPA) as solvent in presence of catalyst at 150° C. for 24 hours, further continuing stirring at the 190° C. for 24 hours under oxygen followed by adjusting the pH of the solution to 8-9 to obtain product of 1,4-bis (1H-benzo[d]imidazol-2-yl) benzene (3).

##STR00012##

[0057] The present invention also provides a process for preparation of model derivative 1,3,6,8-tetrakis (4-(1H-benzo[d]imidazol-2-yl) phenyl) pyrene (pyrene imidazole model derivative) (4) comprising charging 1,3,6,8-tetrakis(p-benzoic acid) pyrene, o-phenylenediamine, polyphosphoric acid (PPA) as solvent in presence of catalyst at 150° C. for 24 hours further continuing stirring at the 190° C. for 24 hours under oxygen followed by adjusting the pH of the solution to 8-9 to obtain product of 1,3,6,8-tetrakis (4-(1H-benzo[d]imidazol-2-yl) phenyl) pyrene (4).

##STR00013##

[0058] FT-IR spectrum of BIP-1 reveals that the broad peak corresponds to N—H stretching in the range from 3412 cm.sup.−1 (free N—H) to 3200 cm-1 (hydrogen bonded N—H), while the intense new band that appeared at 1634 cm.sup.−1 (C═N) can be assigned to vibrations from the benzimidazole ring skeleton. The intensity of the C═O band at 1691 cm.sup.−1 in (3) is substantially disappeared in BIP-1, suggesting the consumption of monomer during 2D-polymerization.

.sup.13C cross-polarisation magic angle spinning (.sup.13C CP-MAS NMR) spectrum of BIP-1 contains signals between 170 ppm-125 ppm arise from benzimidazole and other remaining aromatic units.

[0059] FIG. 1 depicts a) Photo of the reaction tube before polymerization with both monomers and PPA; b) Image of the reaction tube after polymerization after 48 hours; c) Photograph of polymer after isolation and d) picture of BIP-1 Pellet used for proton conductivity measurements.

[0060] FIG. 2 depicts a comparison of the UV-Vis absorption spectrum of BIP-1 oligomers with model derivatives that are absorbing in the 280-480 nm range, indicated the presence of benzimidazole moiety in the molecule. A broad peak exhibited by BIP-1 in solid state UV-Vis absorption similar to that of the model derivative 4, has also endorsed the polymerization.

[0061] FIG. 3 depicts that multilayer stacks of 2D-polymer structure as observed by transmission electron microscope (TEM) images of BIP-1 and points to both the extended 2D-polymerization and the preferable strong π-stacking between the layers. TEM images of BILP-1 (Imidazole linked Pyrene 2DP by acid route) samples were prepared by dispersing polymer in methanol 50 μl drop casted on the Cu grid.

[0062] FIG. 4 depicts that Scanning electron microscope (SEM) image of BIP-1 showed solid state feature of the 2D-polymer comprising of layered-sheets.

[0063] FIG. 5 depicts comparison of PXRD patterns of BIP-1 experimental (dotted) and simulated pattern for an AA stacking mode (solid). Powder X-ray diffraction (PXRD) patterns of BIP-1 exhibited an intense peak at 3.7°, corresponding to the reflection from the (100) plane. The peak in the region 2θ=25° patterns of BIP-1 is due to the reflection from the (001) plane. The π-π stacking distance between 2D-polymer layers are calculated to be 3.3 and 3.6 Å from the d spacing between 001 plane. The AA stacking mode is confirmed by the peak position and intensity of the PXRD pattern.

[0064] FIG. 6 depicts a) BET N.sub.2 sorption isotherm curves and b) pore-size distribution profile of BIP-1 measured at 77 K. Confirms the 2D-polymerization happened as shown in the scheme 2, resulting in well-defined porous polymer.

[0065] FIG. 7 depicts PXRD-pattern for BILP (H. M. El-Kaderi group) sample reproduced, indicating amorphous materials. BILP-10 published by H. M. EI-Kaderi et al.; the polymer has no long range ordering, evident from PXRD which lacks sharp peak in the PXRD. It is clear from the PXRD analysis of BIP-1 that new synthetic route helps to undergo thermodynamically controlled reversible condensation reaction of the monomers, which results in a crystalline framework.

[0066] FIG. 8 depicts proton conductivity measurements carried out for BIP-1 (in compacted pellet of the powdered sample), using quasi-four-probe AC impedance measurements a) under different relative humidity at 95° C.; b) different temperature at 95% relative humidity humidified conditions in a home-made setup is placed between two stainless steel electrodes and the set up is placed inside a temperature controlled incubator which is also connected to a electrochemical work station. This experiment clearly shows that 95% relative humidity at 95° C., the material imparts least resistance and results the best proton conductivity of 3.2 X10.sup.−2 S cm.sup.−1.

[0067] The benzimidazole linked pyrene 2D polymer (BILP-1) synthesized using aldehyde and amine, reported by El-Kaderi and co-workers also tested for proton conductivity and found that the values are pretty low in the order of 10.sup.−5 S cm.sup.−1 only.

[0068] The polymer BIP-2 structure is predesigned to obtain a 2D polymer with increased imidazole linkages in periodic units with triangular pore structure. Hexakis(4-carboxyphenyl)benzene synthesized and characterized according to the report by Furukawa and coworkers (Inorg. Chem. 2015, 54, 10065-10072) as shown in the Scheme 4.

##STR00014##

Synthetic scheme for the preparation of imidazole linked model derivative of BIP-2, 2,2′-(3′,4′,5′,6′-tetrakis(4-(1H-benzo[d]imidazol-2-yl)phenyl)-[1,1′:2′,1″-terphenyl]-4,4 ″-diyl)bis(1H-benzo[d]imidazole) (6) is as shown in scheme 5.

##STR00015##

.sup.13C CP-MAS NMR spectrum of BIP-2 observes a signal around 150 ppm that corresponds to NC(Ph)N in the benzimidazole units as well as other signals in the aromatic range, that arise from monomeric aromatic regions in the polymer repeating units.

[0069] FIG. 9a denotes the photograph for the progress of polymerization and is monitored with time and after sufficient precipitation is observed, the reaction mixture is filtered and collected. The 2D-polymer is then kept overnight in saturated aqueous NaHCO.sub.3 solution, again washed with water by soxhlet extraction until the filtrate is neutral to pH and followed in methanol for 12 hours in order to remove water from polymer matrix and is dried under vacuum. FIGS. 9(b) and 9(c) denotes that the multilayer stacks of 2D-polymer structure as revealed by TEM images of 2D-polymer suspension in methanol that points to both the extended 2D-polymerization and the preferable strong π-stacking between the layers. The extended polymerization is further confirmed by the scanning electron microscope (SEM) image.

[0070] FT-IR spectra of monomers 5, 2 and model derivative 6 and BIP-2 in KBr pellet observed broad bands from 3100 to 3235 cm.sup.−1 corresponds to free N—H and hydrogen bonded N—H, new bands with stretching frequency at 1635 and 1360cm.sup.−1 corresponds to C═N and C—N, respectively. The absence of strong peak located at 1700 cm.sup.−1 indicated the full consumption of both monomers containing carboxylic acid and amine functional moieties during the formation of benzimidazole unit.

[0071] FIG. 10 denotes a) BET N.sub.2 sorption isotherm curves of BIP-2 measured at 77 K; b) Pore-size distribution profile of BIP-2. Confirms the 2D-polymerization happened as shown in the scheme 7 resulting in well-defined porous polymer.

[0072] FIG. 11 depicts TEM images of BIP-2. TEM images of BIP-2 showing layered sheets, selected area diffraction (SAD) of BIP-2 showing crystalline ordering samples were prepared by dispersing polymer in methanol 20 μl drop casted on the Cu grid.

[0073] FIG. 12 depicts SEM images of BIP-2. SEM image of BIP-2 samples are prepared by dispersing polymer in methanol by sonication for about 5 min drop casted on silicon substrate, dried.

[0074] FIG. 13 depicts TEM images of BIP-3 showing layered sheets, samples are prepared by dispersing polymer in methanol 20 μl drop casted on the Cu grid.

[0075] Summary of quasi-four-probe AC impedance measurements under different temperature 95% relative humidified (RH) conditions BIP-1 (1.44 mm thick pellet)

TABLE-US-00001 TABLE 1 Temperature Variation at 95% RH Proton Resistance Conductivity SI. No Condition (Ohm) (S/cm) 1 60° C., 95% RH 9.5 1.1 × 10.sup.−2 2 70° C., 95% RH 4.3 2.5 × 10.sup.−2 3 80° C., 95% RH 3.9 2.8 × 10.sup.−2 4 95° C., 95% RH 3.3 3.2 × 10.sup.−2

[0076] Summary of quasi-four-probe AC impedance measurements under different humidified conditions at 95° C. BIP-1 (1.44 mm thick pellet)

TABLE-US-00002 TABLE 2 RH Variation at 95° C. Proton Resistance Conductivity SI. No Condition (Ohm) (S/cm) 1 95° C., 60% RH 540 2.0 × 10.sup.−4 2 95° C., 70% RH 275 3.9 × 10.sup.−4 3 95° C., 80% RH 86 1.2 × 10.sup.−3 4 95° C., 95% RH 3.3 3.2 × 10.sup.−2

[0077] FIG. 14 depicts the fuel cell life test of the BIP-1 membrane at open-circuit voltage condition. Insets show the photographs of BIP-PMMA membrane (4 cm.sup.2) (left) and MEA by sandwiching BIP-PMMA membrane between two electrodes, maintaining an active area of 4 cm.sup.2 (right). The open-circuit voltage remains stable for more than 1 h after an initial dip.

EXAMPLES

[0078] Following examples are given by way of illustration therefore should not be construed to limit the scope of the invention.

Example 1: Synthesis of 1,3,6,8-tetrabromopyrene

[0079] ##STR00016##

[0080] To pyrene 1.01 g (5.0 mmol) in nitrobenzene (15 mL) was added bromine 3.52 g (22.0 mmol) dropwise at room temperature, and the mixture was stirred at 120° C. for 4 h. The reaction mixture was filtered, and the residue was washed with methanol (50 mL) and acetone (50 mL). After drying under reduced pressure, 1,3,6,8-tetrabromopyrene was obtained as a pale yellow solid in 2.54 g, Yield: 98%. (due to poor solubility, 1,3,6,8-tetrabromopyrene is not characterized in this step and directly used for the next step)

Example 2: Synthesis of 1,3,6,8-tetrakis (4-(methoxycarbonyl)phenyl)pyrene

[0081] ##STR00017##

[0082] A mixture of 4-(methoxycarbonyl)phenyl)boronic acid 1.040 g (5.80 mmol), 1,3,6,8-tetrabromopyrene 0.500 g (0.97 mmol), tetrakis(triphenylphosphine) palladium (0) 0.030 g (0.026 mmol), and potassium tribasic phosphate 1.1 g (5.30 mmol) in dry dioxane (20 mL) was charged in a 30 mL sealed tube filled with argon and capped. This mixture was stirred under argon for 72 h at 130° C. in an oil bath. The reaction mixture was evaporated to dryness and the solid residue was washed with water to remove inorganic salts. The insoluble material was extracted with chloroform (three times by 50 mL), and the solvent volume was reduced under vacuum. The residue was boiled in tetrahydrofuran for two hour and filtered;

[0083] the resulting filtrate contained mainly impurities. Pure 1,3,6,8-tetrakis(4-(methoxycarbonyl)phenyl)pyrene obtained as an yellow solid, 0.58 g, Yield: 82%..sup.2

.sup.1H NMR (400 MHz, CDCl.sub.3): δ ppm 4 (s, 12H), 7.76 (d, 8H), 8.02 (s, 2H), 8.16 (s, 4H), 8.24 (d, 8H). MALDI-TOF MS: m/z calculated for C.sub.48H.sub.34O.sub.8 [M].sup.+: 738.2254, found: 738.1611.

[0084] FT-IR (KBr): 2954, 1724, 1606, 1428, 1275, 1107, 710 cm.sup.−1.

Example 3: 1,3,6,8-tetrakis (p-benzoic acid) pyrene (1)

[0085] ##STR00018##

[0086] To a 250 mL round bottom flask containing 0.58 g (0.78 mmol) of solid 1,3,6,8-tetrakis(4-(methoxycarbonyl)phenyl)pyrene, a solution containing 1.5 g (37.5 mmol) NaOH in 100 mL of a THF/water (ratio 1:1) mixture was added and the resultant suspension was vigorously stirred under reflux overnight. The solvents were removed under vacuum and water was added to the residue which formed a clear yellow solution. The clear yellow solution was stirred at room temperature for 2 h and the pH value was adjusted to 1 using concentrated HCl. The resulting yellow solid was collected by filtration, and washed with water several times. The crude product was recrystallized from DMF, filtered, washed with chloroform and dried under vacuum. This gave the pure product, as yellow solid 0.49 g, Yield: 91%.

.sup.1H NMR (400 MHz, DMSO-d.sub.6): δ ppm 7.82 (d, 8H), 8.05 (s, 2H), 8.12 (d, 8H), 8.17 (s, 4H), 13.11 (s, 4H). MALDI-TOF MS: m/z calculated for C.sub.44H.sub.26O.sub.8 [M].sup.+: 682.1628, found: 682.1432.FT-IR (KBr): 3414-3070, 2893, 1691, 1610, 1423, 1285, 859 cm.sup.−1.

Example 4: Benzimidazole-linked 2D-polymer (BIP-1)

[0087] Teflon capped pressure tube (10 ml) filled with argon was charged with 20 mg (30 μmol) 1,3,6,8-tetrakis(p-benzoic acid) pyrene, 17 mg (60 μmol) of 1,2,4,5-benzenetetramine tetrahydrochloride (2) and in the presence of 3 mL of PPA as solvent and catalyst. The reaction was stirred at 150° C. for 48 h and then stirred at 190° C. for 48 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated NaHCO.sub.3, 2D-polymer was precipitated. After filtration, the polymer was obtained as dark coloured powder. The powder collected and then soxhlet extraction was performed with water, methanol, acetone for 12 hours and then dried at 100° C. under vacuum for 12 hours to give a dark coloured powder, 32 mg, Yield (Isolated): 80%.

##STR00019##

Example 5: Model Derivative 1: 1,4-bis (1H-benzo[d]imidazol-2-yl) benzene (3)

[0088] ##STR00020##

[0089] Teflon capped pressure tube (10 ml) filled with argon, was charged with 20 mg (120 μmol) of terephthalic acid, 26 mg (240 μmol) of o-phenylenediamine in the presence of 3 mL of polyphosphoric acid (PPA) as solvent, catalyst. The reaction was heated at 150° C. for 24 h and then stirred at 190° C. for 24 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated sodium hydrogen carbonate (NaHCO.sub.3), product was precipitated. Thus obtained crude product was then further purified by recrystallization with methanol to give pure 1, 4-bis(1H-benzo[d]imidazol-2-yl) benzene, as a pale off white solid, 34 mg, Yield: 91%..sup.3

.sup.1H NMR (500 MHz, DMSO-d.sub.6): δ ppm 7.26 (m, 4H), 7.69 (m, 4H), 8.35 (s, 4H), 13.13 (s, 2H). MALDI-TOF MS: m/z calculated for C.sub.20H.sub.14N.sub.4 [M].sup.+: 310.1218, found: 310.979. FT-IR (KBr): 3420, 3046, 2917, 1643, 1438, 1318, 1117, 734.

Example 6: Model Derivative 2: 1,3,6,8-tetrakis (4-(1H-benzo[d]imidazol-2-yl) phenyl) pyrene (pyrene imidazole Model Derivative) (4)

[0090] ##STR00021##

[0091] Teflon capped pressure tube (10 ml) filled with argon, was charged with 20 mg (30 μmol) of 1,3,6,8-tetrakis(p-benzoic acid) pyrene, 14.2 mg of o-phenylenediamine (131 μmol) in the presence of 3 mL of PPA as solvent, catalyst. The reaction was heated at 150° C. for 24 h and then stirred at 190° C. for 24 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated sodium hydrogen carbonate (NaHCO.sub.3), product was precipitated. Thus obtained crude product was then further purified by recrystallization with methanol to give pyrene imidazole model derivative, as a pale yellow solid, 24 mg, Yield: 84%.

.sup.1H NMR (500 MHz, DMSO-d.sub.6): δppm 7.27 (m, 8H), 7.6 (d, 4H), 7.73 (d, 4H), 7.98 (d, 8H), 8.22 (m, 4H), 8.37 (s, 4H), 8.45 (d, 8H), 13.11 (s, 4H). MALDI-TOF MS: m/z calculated for C.sub.68H.sub.42N.sub.8 [M].sup.+: 970.3532, found: 970.0503. FT-IR (KBr): 3390, 3261, 1648, 1209, 1146, 897, 701.

Example 7: The Synthesis of 2,2′-(3′,4′,5′,6′-tetrakis(4-(1H-benzo[d]imidazol-2-yl)phenyl)-[1,1′:2′,1″-terphenyl]-4,4″-diyl)bis(1H-benzol[d]imidazole) (6)

[0092] Teflon capped pressure tube (10 ml) filled with argon, was charged with 25 mg (31.3 μmol) of Hexakis(4-carboxyphenyl)benzene, 20.6 mg of o-phenylenediamine (190.9 μmol) in the presence of 3 mL of PPA as solvent, catalyst. The reaction was heated at 150° C. for 24 h and then stirred at 190° C. for 24 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated sodium hydrogen carbonate (NaHCO.sub.3), product was precipitated. Thus obtained crude product was then further purified by recrystallization with methanol to give 2,2′-(3′,4′,5′,6′-tetrakis(4-(1H-benzo[d]imidazol-2-yl)phenyl)-[1,1′:2′,1″-terphenyl]-4,4″-diyl)bis(1H-benzo[d]imidazole), as a pale yellow solid, 31 mg, Yield: 80%. MALDI-TOF MS: m/z calculated for C.sub.68H.sub.43N.sub.8 [M+1].sup.+: 1231.47, found: 1231.2944. C.sub.84H.sub.55N.sub.12Na.sup.+[M+1+Na].sup.+: 1254.45 found: 1254.2770. FT-IR (KBr): 3100-3400, 1635, 1395, 1123, 850, 742.

Example 8: Synthesis of BIP-2

[0093] Teflon capped pressure tube (10 ml) filled with argon was charged with 25 mg (31.3 μmol) hexakis(4-carboxyphenyl)benzene, 26.67 mg (93.9 μmol) of 1,2,4,5-benzenetetramine tetrahydrochloride and in the presence of 3 mL of PPA as solvent and catalyst. The reaction was stirred at 150° C. for 48 h and then stirred at 190° C. for 48 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated sodium NaHCO.sub.3, 2D-polymer was precipitated. After filtration, the polymer was obtained as dark colored powder. The powder was collected and then soxhlet extraction was performed with water, methanol, acetone for 12 hours and then dried at 100° C. under vacuum for 12 hours to give a dark colored powder, 36 mg. Yield (Isolated): 76%.

##STR00022##

Example 9: The Preparation of 1,3,5-tris(1H-benzo[d]imidazol-2-yl)benzene Model Derivative

[0094] A Teflon capped pressure tube (10 ml) filled with argon, was charged with 25 mg (118.9 μmol) of benzene-1,3,5-tricarboxylic acid, 38.6 mg of o-phenylenediamine (356.9 μmol) in the presence of 3 mL of PPA as solvent, catalyst. The reaction was heated at 150° C. for 24 h and then stirred at 190° C. for 24 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated NaHCO.sub.3, product was precipitated. Thus obtained crude product was then further purified by reprecipitation with methanol to give 1,3,5-tris(1H-benzo[d]imidazol-2-yl)benzene, as a pale yellow solid, 40 mg, Yield: 78%. MALDI-TOF MS: m/z calculated for C.sub.27H.sub.18N.sub.6[M+1].sup.+:427.16, found: 427.065.

##STR00023##

Example 10: Procedure for the Synthesis for benzimidazole 2D-polymer BIP-3

[0095] Teflon capped pressure tube (10 ml) filled with argon was charged with 40.5 mg (142.7 μmol) benzene-1,3,5-tricarboxylic acid, 20 mg (95.1 μmol) of 1,2,4,5-benzenetetramine tetrahydrochloride and in the presence of 3 mL of PPA as solvent and catalyst. The reaction was stirred at 150° C. for 48 h and then stirred at 190° C. for 48 h under oxygen. After the pH of the resulting mixture was adjusted to 8-9 with saturated sodium hydrogen carbonate (NaHCO.sub.3), 2D-polymer was precipitated.

##STR00024##

Example 11: Experimental Procedure for Proton Conductivity

[0096] Proton conducting ability was investigated using two-probe A.C impedance measurements under humidified conditions. In a home-made setup, pellet (13 mm diameter) was placed between two stainless steel electrodes and the set up was placed inside a temperature controlled humidity chamber (SH-241, ESPEC Co. Ltd., Japan), which was also connected to a BioLogic electrochemical work station (VMP-3). The sample was left to equilibrate at each temperature for at least 1 h or until a steady state was reached. The electrochemical impedance measurements were performed in the frequency range of 1 MHz-0.1 Hz using input voltage amplitude of 10 mV.

Example 12: Conductivity Measurement

[0097] Total of 190 mg of BIP sample was pressed into a die under 1000 psi for 2 min curing time to obtain uniform pellets (˜1.2 mm in thickness, 13 mm in diameter). In case of BIP pellet the proton conductivity is measured at different temperatures (from 60° C. to 95° C.) under 95% RH. In each case, the proton conductivity is calculated using the Pouillet's equation, σ=L/(R×A), wherein σ is the conductivity (Scm.sup.−1), L is the thickness of the measured sample (cm) and A is the electrode area (incm.sup.2). The resistance is calculated using the high frequency intercept of the Ny quist plot measured by the impedance spectroscopy.

Example 13: Preparation of BIP Membrane

[0098] BIP membrane was prepared by a film casting method using a BIP (35 wt %)—PMMA mixture in dimethylacetamide (DMAc). A slurry of BIP and Polymethyl methacrylate (PMMA) in DMAc was prepared by sonication and followed by stirring at 80° C. for 12 h. The membrane was casted by pouring the slurry onto a Petri dish; majority of the solvent was evaporated in a ventilated oven at a temperature of 80° C. after 3 hours. The membrane was then peeled off, washed with water to remove the residual DMAc, and dried in an oven at 110° C. for 12 h.

Example 14: The Fuel Cell Experiments

[0099] The Fuel cell experiments were performed in a Fuel Cell Technologies Inc., instrument. The operation temperature was 50° C. and at 100% RH. The gas feeding conditions were H.sub.2 (100 sccm) and O.sub.2 (100 sccm) respectively. The membrane electrode assembly (MEA) was made by sandwiching the electrodes with the membrane. For this, Pt/C (40 wt %) was brush coated on a gas diffusion layer with a Platinum loading of 1 mg cm.sup.−2. The anode and cathode electrodes were having an active area of 4 cm.sup.2 and the membrane is kept in between the electrodes. The assembly was hot pressed at 0.5 ton for 1 minute at 130° C. and obtained the MEA. In a fuel cell fixture, MEA was fixed between the graphite plates and the life test was performed at the open circuit voltage (OCV) conditions.

Advantages of the Invention

[0100] 1. Enhancement of conductivity and enables ultrahigh proton-conduction in pristine form without any additional dopants. [0101] 2. Crystalline material was obtained starting with an acid (in place of an aldehyde) and good yields were obtained indicating the cyclization was completed [0102] 3. Provides framework tunability [0103] 4. Chemically stable [0104] 5. Easy material fabrication [0105] 6. Feasibility of hybridization with other materials [0106] 7. Sustainable in harsh fuel cell operating conditions [0107] 8. Large surface area and lightweight