Method for producing roll-bonded metal sheets

Abstract

A roll-bonded clad metal sheet and a method for producing a roll-bonded clad metal sheet is provided. The roll-bonded clad sheet includes a metallic base material layer and a metallic cladding material layer which are joined to one another by a metallurgical bond. The metallic cladding material layer includes a nickel-based material whose chemical composition includes, in % by mass, a proportion of more than 50% of Ni and a proportion of 3.1% of Nb. The metallurgical bond is obtained by a thermomechanical rolling process including a first rolling phase for prerolling, a second rolling phase for final forming and a cooling time between the first rolling phase and the second rolling phase, wherein a final rolling temperature of the second rolling phase is set to a value equal to or less than 880° C.

Claims

1. A process for producing a roll-bonded clad metal sheet, wherein the process comprises: bringing together a metallic base material layer and a metallic cladding material layer to produce an intermediate layer packet; heating the intermediate layer packet to yield a heated layer packet; thermomechanical rolling the heated layer packet, comprising: performing a first rolling phase for prerolling the heated layer packet to form a metallurgical bond between the metallic base material layer and the metallic cladding material layer; cooling the heated layer packet after the first rolling phase; and performing a second rolling phase for final forming of a layer packet, wherein: the metallic cladding material layer comprises a nickel-based material whose chemical composition comprises, in % by mass, 58%≤Ni≤73%, 20%≤Cr≤25%, 0%≤Fe≤5%, 0%≤C≤0.1%, 0%≤Mn≤0.5%, 0%≤Si≤0.5%, 0%≤Co≤1%, 0%≤Al≤0.4%, 0%≤Ti≤0.4%, 0%≤P≤0.015%, 0%≤S≤0.015%, 8%≤Mo≤10%, 1.5%≤Nb+Ta≤2.8%, and balance impurities, and a final rolling temperature of the second rolling phase is set to a value equal to or less than 880° C.

2. The process as claimed in claim 1, wherein a proportion of Nb is ≤2.5%.

3. The process as claimed in claim 1, wherein the chemical composition comprises, in % by mass, one or more of the following elements: 0%≤Ta≤1%, 0%≤B≤0.008%, Cu≤0.5%, W≤1%, V≤0.5%, N≤0.05%, Mg≤0.05%, Ca≤0.05%, Pb≤0.002%, Zn≤0.002%, or Sn≤0.002%.

4. The process as claimed in claim 1, wherein the metallic base material layer comprises a carbon steel.

5. The process as claimed in claim 4, wherein the carbon steel has, in % by mass, carbon content of C≤0.30% and a chemical composition comprising one or more of the ranges: 0%≤Si≤0.50%, 1.10%≤Mn≤1.65%, 0%≤P≤0.022%, 0%≤S≤0.010%, 0%≤Nb≤0.05%, 0%≤Ti≤0.06%, or 0%≤V≤0.10%.

6. The process as claimed in claim 1, wherein the first rolling phase is carried out at an initial rolling temperature of from 1000° C. to 1200° C.

7. The process as claimed in claim 1, wherein the final rolling temperature is lower than a recrystallization stop temperature of the metallic base material layer.

8. The process as claimed in claim 1, wherein the cooling comprises cooling the heated layer packet in air for a cooling time from 3 to 15 minutes.

9. The process as claimed in claim 1, wherein the nickel-based material is a nickel-chromium-molybenum-niobium alloy.

10. The process as claimed in claim 1, wherein the final rolling temperature is set to a value equal to or less than 850° C.

11. A process for producing a roll-bonded clad metal sheet, wherein the process comprises: bringing together a metallic base material layer and a metallic cladding material layer to produce an intermediate layer packet; heating the intermediate layer packet to yield a heated layer packet; thermomechanical rolling the heated layer packet, comprising: performing a first rolling phase for prerolling the heated layer packet to form a metallurgical bond between the metallic base material layer and the metallic cladding material layer; cooling the heated layer packet after the first rolling phase; and performing a second rolling phase for final forming of a layer packet, wherein: the metallic cladding material layer comprises a nickel-based material whose chemical composition comprises, in % by mass, a proportion of more than 50% of Ni and a proportion of 0.5%≤Nb≤3.1%, and a final rolling temperature of the second rolling phase is set to a value equal to or less than 880° C. and is lower than a recrystallization stop temperature of the metallic base material layer.

12. The process as claimed in claim 11, wherein the proportion of Nb is 2.5%.

13. The process as claimed in claim 11, wherein the nickel-based material is a nickel-based alloy.

14. The process as claimed in claim 11, wherein the first rolling phase is carried out at an initial rolling temperature of from 1000° C. to 1200° C.

15. The process as claimed in claim 11, wherein the cooling comprises cooling the heated layer packet in air for a cooling time from 3 to 15 minutes.

16. A process for producing a roll-bonded clad metal sheet, wherein the process comprises: bringing together a metallic base material layer and a metallic cladding material layer to produce an intermediate layer packet; heating the intermediate layer packet to yield a heated layer packet; thermomechanical rolling the heated layer packet, comprising: performing a first rolling phase for prerolling the heated layer packet to form a metallurgical bond between the metallic base material layer and the metallic cladding material layer; cooling the heated layer packet after the first rolling phase, wherein the cooling comprises cooling the heated layer packet in air for a cooling time from 3 to 15 minutes; and performing a second rolling phase for final forming of a layer packet, wherein: the metallic cladding material layer comprises a nickel-based material whose chemical composition comprises, in % by mass, a proportion of more than 50% of Ni and a proportion of 0.5%≤Nb≤3.1%, and a final rolling temperature of the second rolling phase is set to a value equal to or less than 880° C.

17. The process as claimed in claim 16, wherein the proportion of Nb is ≤2.5%.

18. The process as claimed in claim 16, wherein the final rolling temperature is set to a value equal to or less than 850° C.

19. A process for producing a roll-bonded clad metal sheet, wherein the process comprises: bringing together a metallic base material layer and a metallic cladding material layer to produce an intermediate layer packet; heating the intermediate layer packet to yield a heated layer packet; thermomechanical rolling the heated layer packet, comprising: performing a first rolling phase for prerolling the heated layer packet to form a metallurgical bond between the metallic base material layer and the metallic cladding material layer; cooling the heated layer packet after the first rolling phase; and performing a second rolling phase for final forming of a layer packet, wherein: the metallic cladding material layer comprises a nickel-based material whose chemical composition comprises, in % by mass, a proportion of more than 50% of Ni and a proportion of 0.5%≤Nb≤3.1%, and a final rolling temperature of the second rolling phase is set to a value equal to or less than 850° C.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) Working examples and embodiments of the invention are illustrated by way of example below with the aid of the schematic drawings, with a different degree of detail sometimes being used in the drawings. The drawings are not true to scale. The same reference numerals denote the same or similar parts.

(2) FIG. 1 shows various stages of a working example of a process according to the invention for producing roll-bonded clad metal sheets.

(3) FIG. 2 shows a temperature profile of a working example of a process according to the invention.

(4) FIG. 3 shows a temperature profile of an example for determining the yield stress of a base material layer and a cladding material layer.

(5) FIG. 4 depicts by way of example the yield stress curves of a base material layer and two cladding material layers having different Nb contents as a function of the temperature, with the number of passes during forming being reported as parameter.

(6) FIG. 5 shows by way of example the yield stress curve of a cladding material having an Nb content of 3.5% and the yield stress curve of an identically processed cladding material having an Nb content of 2.0%.

(7) FIG. 6 shows a graph in which the rate of loss of material in mm/a determined in the Streicher test ASTM G 28 A is plotted against the Nb content in % by mass for various cladding materials.

(8) FIG. 7 shows a graph in which the critical pit corrosion temperature CPT in ° C. determined in the corrosion test ASTM G 48 C is plotted against the Nb content in % by mass for various cladding materials.

(9) FIG. 8 shows a graph in which the critical pit corrosion temperature CPT in ° C. determined in the Green Death Test is plotted against the Nb content in % by mass for various cladding materials.

DETAILED DESCRIPTION

(10) FIG. 1 shows a series of process stages of a working example of a process according to the invention for producing roll-bonded clad metal sheets.

(11) In cladding by roll bonding, composite materials having a metallurgical bond between at least two layers composed of at least two different metallic materials are produced. Step S1 depicts a phase of the production process in which a cladding material layer 102 is laid on top of a base material layer 101.

(12) Both the base material layer 101 and the cladding material layer 102 are previously produced metallic layers which initially rest on top of one another without a metallic bond. Both material layers 101, 102 can have been produced separately beforehand as metal sheets or strips in a factory producing metal products.

(13) The layer thickness of the base material layer 101 is usually greater than the layer thickness of the cladding material layer 102. The task of the base material layer 101 is usually to withstand the static and dynamic loads while the cladding material layer 102 serves first and foremost to protect the base material layer 101 against corrosive attack by aggressive ambient media. However, the cladding material layer 102 can also be included partly or completely into the calculation of the wall strength of the finished roll-bonded clad metal sheet for withstanding the static and dynamic loads.

(14) The base material can, for example, be a carbon steel. The cladding material can be, for example, a nickel-based alloy, in particular a nickel-chromium-molybdenum-niobium alloy.

(15) The materials used for producing roll-bonded clad metal sheets and their physical properties are known and standardized in the industry. A customer requiring, for example, a roll-bonded clad metal sheet for offshore pipelines can, on the basis of the properties prescribed according to standards (chemical composition of the materials, layer thicknesses, corrosion resistance to various ambient media, toughness properties, strength and expansion properties, pit corrosion resistance, weldability, etc.), be assured that the particular requirements in respect of the abovementioned properties are satisfied. Particularly when roll-bonded clad metal sheets are used in the oil and gas sector, carbon steels which correspond to the applicable standard API 5L, in particular API 5L grade X65, DNV OS-F101, ISO 3183 or comparable standards, are usually employed as base material. As cladding material, use is made of, for example, a nickel-based alloy, for example Alloy 625 having the material number 2.4856, the chemical composition of which has been indicated above.

(16) Apart from the one-sided application of the cladding material layer 102 to the base material layer 101 which is illustrated by way of example in FIG. 1, it is also possible to provide two-sided application of cladding material layers 102 to the base material layer 101 located in between. It is likewise possible for a plurality of base material layers 101 between which one or more cladding material layers 102 are arranged to be provided. A practical example of such a multilayer arrangement is shown in FIG. 1; here, two base material layers 101_1, 101_2 and two cladding material layers 102_1 and 102_2 are used and are arranged on top of one another in the order 101_1, 102_1, 102_2, 101_2, with a separation medium optionally being able to be introduced between the cladding material layers in order to avoid bonding between the two cladding materials. For example, ceramic materials can be used as separation media.

(17) The placing of the material layers 101, 102 on top of one another is indicated by the arrows A in FIG. 1. The stack of layers produced by laying the material layers 101, 102 on top of one another is referred to as layer packet 110. The layer packet 110a, which is produced, for example, by placing the layers 101_1, 102_1 and 102_2, 101_2 on top of one another, is one of the possible variants according to which the layer 110 can be realized in practice.

(18) The layer packet 110 is heated in step S2. According to FIG. 2, which shows an illustrative temperature profile of a working example of a process according to the invention, the layer packet 110 is heated to a temperature T1.

(19) Heating can, for example, be effected in a furnace 120, see step S2 in FIG. 1. As furnace 120, it is possible to use, for example, a push furnace in which the layer packet 110 is pushed through the furnace 120 and discharged by means of a pushing and discharging device.

(20) The layer packet 110 can be present in the furnace 120 for a first period of time Δt.sub.1. During the time Δt.sub.1, uniform heating over the cross section of the material layers 101, 102 can be achieved. The temperature T1 can, for example, be in the range from 1000° C. to 1200° C. In particular, the temperature can be the same as or higher or lower than 1050° C., 1100° C. or 1150° C.

(21) Immediately after, for example, discharge of the layer packet 110 from the furnace 120 (step S2), the layer packet 110 is rolled in a first rolling phase WP1 (step S3). Rolling in the first rolling phase WP1 can consist of one or more rolling steps (passes). Rolling in the first rolling phase WP1 is also referred to as prerolling. Prerolling is usually carried out in one or more roll stands 130, with the number of passes compared to the number of roll stands (equal to or greater than one) being able to be increased by reversing rolling.

(22) During prerolling (WP1), the materials are homogenized and the thickness of the layer packet 110 is reduced. Furthermore, the metallurgical bond between the base material layer 101 and the cladding material layer 102 is produced. The mechanical properties of the future roll-bonded clad metal sheet are not yet set during prerolling. The layer packet 110 having a reduced thickness is denoted by the reference symbol 110′ in FIG. 1.

(23) The layer packet 110′ is subsequently cooled over a time Δt.sub.2, see FIG. 1, step S4. During cooling, the temperature, for example, goes below the recrystallization stop temperature Trs. Cooling can, for example, be carried out in air and the cooling time Δt.sub.2 can, for example, be from 1 to 3 minutes or else up to 15 minutes. The cooling time Δt.sub.2 is usually dependent on the thickness of the layer packet 110′ and on the desired temperature difference between the first rolling phase WP1 and the second rolling phase WP2 which follows the cooling time Δt.sub.2.

(24) As mentioned above, it is also possible, differently from what is shown merely by way of example in FIG. 2, to employ a temperature profile which does not decrease monotonically but has one or more intermediate heating phases during the cooling time Δt.sub.2. In this case, too, it is advantageous for the temperature of the layer packet 110′ to be below the recrystallization stop temperature Trs during the second rolling phase WP2 (or in some cases even at the beginning thereof), since otherwise the effect of the thermomechanical rolling process used here in respect of the desired improvement in the toughness properties of the finished product (roll-bonded clad metal sheet) becomes smaller.

(25) Thermomechanical rolling differs from conventional hot rolling in that the last passes of the concluding rolling phase are carried out below Trs, with the entire rolling process usually comprising at least two rolling phases WP1 and WP2 with at least one intermediate, targeted, i.e. controlled in terms of time and/or temperature, cooling phase and possible intermediate heating phases. The (at least) second or concluding rolling phase WP2 of thermomechanical rolling is also referred to as final rolling or finishing rolling.

(26) In FIG. 1, the second rolling phase WP2 is carried out in a roll stand 150 (see step S5) which can be identical to the roll stand 130 or differ from the roll stand 130. As in the case of prerolling, the finishing rolling (WP2) can be carried out in a reversing or nonreversing manner in one or more roll stands. Here too, the number of passes depends on the initial thickness of the layer packet 110′, the desired reduction in thickness, the desired final degree of deformation, the physical properties of the materials which are rolled, etc.

(27) The initial rolling temperature Twa in the rolling phase WP2 is selected in such a way that the final rolling temperature Twe has the desired target value of equal to or less than 880° C., in particular 850° C. The final rolling temperature Twe is defined as the temperature of the layer packet 110′ in the finishing rolling (rolling phase WP2) immediately before the last rolling pass, i.e. immediately before the last entry into the roll stand 150. The temperatures are usually measured by means of a pyrometer and in this case represent the temperatures measured on the surface. However, average temperatures arithmetically averaged over the thickness of the metal sheet can also be employed for determining the temperature Twe (and also the other temperatures mentioned here).

(28) As a result of the setting of a final rolling temperature Twe of equal to or less than 880° C., the finished product (roll-bonded clad metal sheet) has improved toughness properties. The lower the final rolling temperature Twe, the better the toughness properties which can be achieved by means of the thermomechanical cladding by roll bonding.

(29) The layer packet after the finishing rolling (WP2) is denoted by the reference symbol 110″. The finished rolled layer packet 110″ has a thickness which is decreased further compared to the prerolled layer packet 110′. Furthermore, as mentioned above, the mechanical properties of the roll-bonded clad metal sheet are set during finishing rolling (WP2).

(30) In step S6 (FIG. 1), the finished rolled layer packet 110″ can be subjected to accelerated cooling compared to cooling in air, see also FIG. 2. The accelerated cooling can, for example, be achieved by means of a cooling medium, e.g. spraying water onto the finished rolled layer packet 110″. The cooling medium is indicated by the arrows K in FIG. 1.

(31) The accelerated cooling can, for example, be carried out to a temperature of 100° C. of the finished rolled layer packet 110″. The accelerated cooling likewise has an advantageous effect on the achievable toughness properties of the roll-bonded clad metal sheet.

(32) After the accelerated cooling, further process steps such as flattening, ultrasonic testing, cutting of the edges (for example by plasma cutting), optionally separating into smaller plates, grinding and final quality monitoring, which will not be described in detail here, can take place. The physical properties of the finished product (roll-bonded clad metal sheet) are set essentially by means of the (optional) step S6 of accelerated cooling.

(33) The increase in the toughness or the improvement in the toughness properties of the roll-bonded clad metal sheets produced according to the invention is brought about mainly by the low final rolling temperature. Low final rolling temperatures in the range of the values indicated here have hitherto not been possible since these low temperatures did not make it possible for the metallurgical bond produced during preliminary deformation (i.e. prerolling in the first rolling phase WP1) to be maintained during finishing rolling (i.e. in the second rolling phase WP2). In conventional processes, finishing rolling at final rolling temperatures Twe of about 900° C. was just still possible, but at lower final rolling temperatures the previously produced metallurgical bond between the base material layer 101 and the cladding material layer 102 was torn apart again at the required degrees of deformation.

(34) The reduction in the Nb content of the cladding material now makes it possible to reduce the final rolling temperature Twe without the metallurgical bond between the layers of material 101, 102 being damaged during finishing rolling (WP2). The damage-free finishing rolling (WP2) is made possible according to the invention by the relatively large difference between the yield stress of the cladding material and the yield stress of the base material at the rolling temperatures of the second rolling phase (WP2) being decreased by the reduction in the Nb content.

(35) The higher the yield stress, the higher the deformation resistance of the material. When the yield stress is high, the material offers a high resistance to deformation and high rolling forces are required in order to be able to deform the material appropriately. When the yield stress is small, comparatively small rolling forces are sufficient to be able to carry out deformation.

(36) The reduction in the difference between the yield stresses (i.e. deformabilities) of the cladding material and the base material results in a decrease in the mechanical stresses in the bonding plane between the cladding material and the base material. Tearing apart of the metallurgical bond, which is brought about by excessively high mechanical stresses, is avoided thereby.

(37) FIGS. 3 and 4 serve to illustrate, by way of example, the yield stress behavior of base material and cladding material as a function of the temperature at different chemical compositions of the cladding material. The yield stresses of the cladding material and of the base material were measured by means of a dilatometer. For this purpose, samples of the materials used were subjected to heating and forming to simulate the rolling process, as shown in FIG. 3.

(38) Firstly, the samples were heated to a temperature of 1100° C. and maintained at this temperature for a time of 600 seconds. The heating rate was 10° C./second. The samples were subsequently cooled at a rate of 10° C./second to a deformation temperature which replicates the final rolling temperature Twe in the actual production process for the roll-bonded clad metal sheets. At this deformation temperature Twe, four rolling passes St1, St2, St3 and St4 were carried out with in each case intermediate hold times of 10 seconds. The forming rate was in each case dPhi/dt=2.0. Accelerated cooling down to 100° C. at a cooling rate of 20° C./second was subsequently carried out.

(39) The yield stresses of the samples were determined by means of a dilatometer in the first pass (St1), second pass (St2), third pass (St3) and fourth pass (St4). The experiments were carried out at different deformation temperatures Twe. The results of the experiments are shown in FIG. 4 for a base material (GW) having the designation GW8932 corresponding to API 5L grade X65, a cladding material Alloy 625 with Nb=3.5% (AW_Nb3.5) and a modified cladding material Alloy 625mod, which was identical to Alloy 625 but with Nb=2.0% and corresponding replacement of the reduced Nb content by Ni or Cr (AW_Nb2.0).

(40) It can be seen from FIG. 4 that the yield stress Kf in units of MPa of the base material (carbon steel) increases only slowly in the direction of lower deformation temperatures T (corresponds to Twe) and differs only slightly for the passes St1, St2, St3 and St4. The deformation resistance of the base material GW thus displays little temperature dependence and increases only relatively slightly between the passes. The yield stress Kf versus temperature curves of the base material in the passes St1, St2, St3, St4 are denoted by GW_St1, GW_St2, GW_St3 and GW_St4.

(41) The yield stress Kf versus temperature curves of the conventional cladding material Alloy 625 with Nb=3.5% in the passes St1, St2, St3, St4 are designated by AW_Nb3.5_St1, AW_Nb3.5_St2, AW_Nb3.5_St3 and AW_Nb3.5_St4. The cladding material Alloy 625 with Nb=3.5% displays, particularly at relatively high degrees of deformation (fourth pass St4) a significantly greater temperature dependence than the base material. As can be seen from FIG. 4, the yield stress Kf of the cladding material Alloy 625 with Nb=3.5% increases greatly when the temperature goes below about 900° C. in the fourth pass St4. This large increase leads to a rapidly increasing difference between the yield stresses of the base material and of the cladding material at higher degrees of deformation and lower temperatures, as a result of which the abovementioned destruction of the metallurgical bond between the materials occurs under these conditions.

(42) The yield stress Kf versus temperature curves of the modified cladding material Alloy 625mod with Nb=2.0% in the passes St1, St2, St3, St4 are designated by AW_Nb2.0_St1, AW_Nb2.0_St2, AW_Nb2.0_St3 and AW_Nb2.0_St4. The yield stress versus temperature curves of the modified cladding material Alloy 625mod with Nb=2.0% are in each case below the temperature curves of the cladding material Alloy 625 with Nb=3.5%. Here too, an increase in the yield stress Kf in the direction of lower deformation temperatures Twe and higher degrees of deformation (larger number of passes) can be seen. However, the difference between the yield stresses of the base material and of the modified cladding material Alloy 625mod is smaller and in particular the significant increase in the yield stress in the direction of lower temperatures occurs only at a value of significantly below 800° C. at the maximum degree of deformation (St4). This is the cause of the metallurgical bond between the cladding material and the base material remaining intact at low final rolling temperatures Twe and the required degrees of deformation in the process of the invention using a cladding material having a reduced Nb content.

(43) This difference in the yield stress behavior is shown once more in FIG. 5 in which the maximum yield stresses Kfmax (i.e. Kf in the fourth pass St4) in units of MPa of the conventional cladding material (Alloy 625) and of the modified cladding material (Alloy 625mod) are compared. The temperature window ΔT allows lower final rolling temperatures Twe and thus setting of the better toughness properties of the base material and of the roll-bonded clad metal sheet.

(44) In the actual production of roll-bonded clad metal sheets, the stack of layers can be heated to the temperature indicated here (about 1100° C.±50° C. or ±100° C.). Since the first rolling phase (WP1) has no influence on the yield stress in the last passes in the second rolling phase (WP2), the first rolling phase (WP1) did not have to be replicated in the experiments presented in FIGS. 3 and 4, i.e. the passes St1, St2, St3 and St4 correspond to passes in the second rolling phase (WP2) in the actual production of the roll-bonded clad metal sheets. However, more passes (e.g. from 10 to 20 passes) are usually employed in the second rolling phase (WP2) in the actual production of roll-bonded clad metal sheets and the periods of time between the passes can be selected differently from those in the experiment shown here.

(45) The toughness of the roll-bonded clad metal sheet is dependent both on the thickness of the metal sheet and also on the temperature in practical use. The lower the use temperature and the thicker the metal sheet, the lower the toughness (and, correspondingly, the higher the brittleness) of the metal sheet. The improved toughness properties discussed here can thus mean an increased toughness at the same use temperature and/or thickness of the metal sheet or the same toughness at lower use temperatures and/or greater thicknesses of the metal sheet.

(46) Measures of the toughness are determined by standardized measurement methods, for example by determining the notched impact strength and/or by determining the matt fracture proportion in the Battelle drop weight tear test (BDWTT). Reduction of the Nb content of the cladding material from 3.5% to, for example, 2.0% (i.e. use of Alloy 625mod instead of Alloy 625) made it possible to improve the notched impact strength from >50J at a test temperature of −60° C. and a thickness of the base material of 25 mm to a value of >50J at a test temperature of −80° C. and a thickness of the base material of 40 mm. The matt fracture proportion in the BDWTT could be improved from at least 80% at a test temperature of −10° C. and a thickness of the base material of 25 mm to at least 80% at a test temperature of −30° C. and a thickness of base material of 40 mm, i.e. the toughness values required by the customer can be guaranteed for thicker metal sheets and/or at lower use temperatures. The base material here corresponded to the abovementioned standard API 5L X65 or comparable standards.

(47) The modification of the cladding material had no adverse effects on its good corrosion protection properties. Corrosion protection properties are in industry likewise assessed by known, standardized measurement methods. At a thickness both of the conventional cladding material (Alloy 625 with material number 2.4856) and the modified cladding material (corresponding to Alloy 625mod) of 3 mm, a maximum annual loss of material of 1.2 mm/a was found in the Streicher test ASTM G 28 A and in each case no pit corrosion was found at 50° C. in the pit corrosion test ASTM G 48 A. The same results were also obtained for other materials of the standard, namely Alloy 625 with material designations UNS N06625, LC2262, etc.

(48) In order to examine the effect of the reduction in the Nb content on the corrosion, 10 kg laboratory batches were melted.

(49) Tables 1A and 1B show the analyses of the batches melted on the laboratory scale together with some industrially melted batches Alloy 625 according to the prior art employed for comparison. The batches according to the prior art are denoted by a T, and the batches according to the invention are denoted by an E. The batches melted on the laboratory scale are denoted by an L, and the industrially melted batches are denoted by a G. The industrially melted batch 135896 is a batch of Alloy 625 according to the prior art. The batch 250537 is Alloy 625 but is melted as laboratory batch and serves as reference and to ensure comparability of results on laboratory batches and industrial batches. All batches have a similar PREN, which determines the pit corrosion resistance, of from 50.07 to 51.28.

(50) The resistance to pit corrosion is given by the following empirical formula:
PREN=Cr+3.3(Mo+W)+16*N.

(51) Cr, Mo, W, N here are the contents of the elements in % by mass. High contents of Cr, Mo, W and N result in a high resistance to pit corrosion. PREN is an empirical formula apart from which there can be further influencing parameters.

(52) The blocks of the alloys melted under reduced pressure on the laboratory scale, as in Tables 1A and 1B, were heat treated in the range from 1100° C. to 1250° C. for from 0.1 to 70 hours and hot rolled by means of hot rolling and further intermediate heat treatments in the range from 1100° C. to 1250° C. for from 0.1 to 10 hours to a final thickness of 12 mm. The metal sheets were then recrystallized in the range from 950° C. to 1050° C. The samples required for the measurements were produced from these metal sheets.

(53) The industrially melted comparative batch was melted open, followed by treatment in a VOD plant and cast as continuous casting. The continuously cast blocks were heat treated in the range from 1100° C. to 1250° C. for from 0.1 minute to 70 hours, optionally under protective gas such as argon or hydrogen, followed by cooling in air and hot rolled in the moving heat treatment atmosphere or in a water bath by means of hot rolling and further intermediate heat treatment in the range from 1100° C. to 1250° C. for from 0.1 to 20 hours to a final thickness of 5 or 16 mm. The metal sheets were then recrystallized in the range from 950° C. to 1050° C. The samples required for the measurements were produced from these metal sheets.

(54) The samples required for the corrosion tests were finally ground all around the periphery and then cleaned.

(55) A corrosion test in accordance with ASTM G 28 A was carried out. This test measures the sensitivity of a material to intercrystalline corrosion. The result is shown in FIG. 6 as a plot of the rate of loss of material against the Nb content and in Table 2 by means of numerical values. It should firstly be noted that the reference laboratory batch 250537 (LB Ref in FIG. 6) displays a higher rate of loss of material than the industrial comparative batch 135896 (GT Ref in FIG. 6). This can be observed in the case of laboratory batches in some tests because of the unfavorable surface area-to-volume ratio compared to industrial batches. All laboratory batches having a comparatively low Nb content display a low rate of loss of material, so that it can be taken that the intercrystalline corrosion in accordance with ASTM G 28 A does not become worse when the Nb content is reduced to ≤2.8% of Nb.

(56) In addition, a corrosion test in accordance with ASTM G 48 C was carried out. This test measures the sensitivity of a material to pit corrosion. The test was modified slightly here since only limited amounts of sample material are available in the case of the laboratory batches, so that a fresh sample cannot be taken for each temperature. The first test was carried out at 50° C., and in the case of the lower Nb contents also at 40° C. The sample was then weighed and once again put in fresh solution but at 5° C. higher. This was repeated until significant pit corrosion occurred, which can be seen from the step increase in the loss in mass and significant pit formation. The first temperature at which this occurred is the critical pit corrosion temperature (CPT). A material is all the more insensitive to pit corrosion, the higher this temperature (the test modified in this way has a tendency to give a higher CPT than a test in which fresh samples are taken for each temperature).

(57) The result is shown in FIG. 7 as a plot of the critical pit corrosion temperature CPT in ° C. against the Nb content or in Table 2 as numerical values. It may firstly be noted that here the reference laboratory batch 250537 (LB Ref in FIG. 7) and the industrial batch 135896 (GT in FIG. 7) achieve the maximum temperature of the test without displaying pit corrosion. Likewise, all laboratory batches having an Nb content of Nb≥0.5% also achieve the maximum temperature. Only the batch without Nb displays a lower pit corrosion temperature, which was confirmed by repetition of the test. For this reason, the Nb content should not be reduced to 0 but preferably be Nb≥0.5% so that the sensitivity to pit corrosion in accordance with ASTM G 48 C is not worsened by reduction of the Nb content. As mentioned above, PREN is an empirical formula apart from which there can be further influencing parameters.

(58) Materials such as Alloy 625 are so corrosion resistant that the limits of the modified test in accordance with ASTM G 48 C are reached. For this reason, a more severe variant of this test, known as the “Green Death Test”, was employed.

(59) This test is carried out in the same way as the modified test in accordance with ASTM G 48 C with the only change being that a test solution comprising 11.5% of H.sub.2SO.sub.4+1.2% of HCl+1% of FeCl.sub.3+1% of CuCl.sub.2 is used instead of a test solution comprising 6% of FeCl.sub.3 and 1% of HCl. The result is shown in FIG. 8 as a plot of the critical pit corrosion temperature CPT against the Nb content and in Table 2 as numerical values. Here too, it may be noted that the reference laboratory batch 250537 (LB Ref in FIG. 8) and the industrial batch 135896 (GT Ref in FIG. 8) barely differ in terms of their critical pit corrosion temperature. Above about 2% of Nb, the measured critical pit corrosion temperatures are within the range of statistical scatter, while below about 1.5% of Nb a noticeable reduction can be observed. For this reason, the Nb content should preferably be Nb≤1.5% so that the sensitivity to pit corrosion in the Green Death Test is not appreciably impaired.

(60) It may be assumed that the results explained here with the aid of examples are generally valid statements which can be applied to all materials described in this disclosure.

(61) TABLE-US-00001 TABLE 1A Composition of the industrially melted batches and the laboratory batches, part 1. All concentrations are in % by mass (column S1 - T: alloy according to the prior art, E: alloy according to the invention column S2 - L: melted on the laboratory scale, G: industrially melted). Batch S1 S2 Ni Cr Fe C Mn Si Co Al Ti P Mo Nb + Ta 250537 T L 61.1 21.6 4.54 0.014 <0.01 0.15 <0.01 0.14 0.2 0.003 8.74 3.38 250530 E L 64.4 21.9 4.7 0.014 <0.01 0.11 0.01 0.05 0.17 0.007 8.61 <0.01 250532 E L 64.4 21.2 4.59 0.013 <0.01 0.15 0.01 0.1 0.18 0.007 8.86 0.49 250533 E L 63.1 21.9 4.54 0.013 <0.01 0.15 0.01 0.11 0.2 0.006 8.88 1.00 250534 E L 63.2 21.9 4.56 0.021 <0.01 0.16 0.01 0.16 0.21 0.006 8.68 1.03 250535 E L 62.7 22.0 4.54 0.012 <0.01 0.14 0.01 0.14 0.22 0.005 8.63 1.51 250536 E L 62.2 22.0 4.56 0.011 <0.01 0.15 0.01 0.13 0.22 0.005 8.64 2.05 135896 T G 61.3 21.2 4.64 0.021 0.07 0.18 0.04 0.17 0.19 0.004 8.67 3.36

(62) TABLE-US-00002 TABLE 1B Composition of the industrially melted batches and the laboratory batches, part 2. All concentrations in % by mass. Batch S Ta B Cu W V N Mg Ca Pb PREN 250537 0.002 <0.01 <0.01 <0.01 0.006 0.012 <0.001 50.56 250530 0.002 <0.01 <0.01 <0.01 0.006 0.005 <0.001 50.38 250532 0.002 <0.01 <0.01 <0.01 0.002 0.007 <0.001 50.44 250533 0.002 <0.01 <0.01 0.01 0.004 0.007 <0.001 51.28 250534 0.002 <0.01 <0.01 <0.01 0.006 0.009 <0.001 50.63 250535 0.002 <0.01 <0.01 0.01 0.006 0.011 <0.001 50.58 250536 0.002 <0.01 <0.01 <0.01 0.006 0.008 <0.001 50.56 135896 0.002 0.01 0.001 0.01 0.01 0.04 0.016 0.016 0.001 <0.001 50.07

(63) TABLE-US-00003 TABLE 2 Results of the corrosion tests in accordance with ASTM G 28 A, the modified test in accordance with ASTM G 48 C and the Green Death Test. Rate CPT CPT of loss in ° C. in ° C. of material Modified Green Death ‘in mm/a ASTM Test (modified Batch G 28 A G 48 C ASTM G 48 C) 250537 T L 0.526 75 90 80 250530 L 0.288 >85 50 250532 L 0.317 >85 60 250533 L 0.299 >85 75 250534 L 0.344 >85 60 250535 E L 0.321 >85 70 250536 E L 0.427 >85 80 135896 T T 0.362 >85 85